Patent Application
20100313957
The disclosure relates generally to solar cells. More particularly, the disclosure relates to quantum dot solar cells and methods for manufacturing quantum dot solar cells and/or components or layers thereof.
A wide variety of solar cells have been developed for converting sunlight into electricity. Of the known solar cells, each has certain advantages and disadvantages. There is an ongoing need to provide alternative solar cells as well as alternative methods for manufacturing solar cells.
The disclosure relates generally to solar cells and methods for manufacturing solar cells and/or components or layers thereof. An example method for manufacturing a multi-bandgap quantum dot layer for use in a solar cell may include providing a first precursor compound, providing a second precursor compound, and combining a portion of the first precursor compound with a portion of the second precursor compound to form a multi-bandgap quantum dot layer that includes a plurality of quantum dots that differ in bandgap.
Another example method for manufacturing a multi-bandgap quantum dot layer for use in a solar cell may include providing a first precursor compound, providing a second precursor compound, combining a portion of the first precursor compound with a portion of the second precursor compound to form precursor quantum dots through a process in which reaction parameters can be adjusted so that the precursor quantum dots are formed with different bandgap. The multi-bandgap quantum dot layer includes a plurality of quantum dots where at least some of the quantum dots differ in size.
Another example method for manufacturing a multi-bandgap quantum dot layer for use in a solar cell may include providing a cadmium-containing compound, providing a selenium-containing compound, combining the cadmium-containing compound with the selenium-containing compound to form a precursor quantum dot, and alloying the precursor quantum dot by performing cation exchange to form a multi-bandgap quantum dot layer that includes a plurality of quantum dots where at least some of the quantum dots differ in bandgap.
An example quantum dot solar cell may include a first electrode. An electron conductor may be electrically coupled to the first electrode. A multi-bandgap quantum dot layer may be electrically coupled to the electron conductor. The multi-bandgap quantum dot layer may include a plurality of quantum dots, where at least some of the quantum dots differ in bandgap. A hole conductor may be electrically coupled to the multi-bandgap quantum dot layer. A second electrode may be electrically coupled to the hole conductor.
The above summary of some embodiments is not intended to describe each disclosed embodiment or every implementation. The Figures and Description which follow more particularly exemplify certain illustrative embodiments.
The invention may be more completely understood in consideration of the following detailed description of various embodiments of the invention in connection with the accompanying drawings, in which:
While the invention is amenable to various modifications and alternative forms, specifics thereof have been shown by way of example in the drawings and will be described in detail. It should be understood, however, that the intention is not to limit the invention to the particular embodiments described. On the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.
The following description should be read with reference to the drawings in which similar elements in different drawings are numbered the same. The drawings, which are not necessarily to scale, depict illustrative embodiments and are not intended to limit the scope of the invention.
For the following defined terms, these definitions shall be applied, unless a different definition is given in the claims or elsewhere in this specification.
All numeric values are herein assumed to be modified by the term “about,” whether or not explicitly indicated. The term “about” generally refers to a range of numbers that one of skill in the art would consider equivalent to the recited value (i.e., having the same function or result). In many instances, the terms “about” may include numbers that are rounded to the nearest significant figure.
The recitation of numerical ranges by endpoints includes all numbers within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, and 5).
As used in this specification and the appended claims, the singular forms “a”, “an”, and “the” include plural referents unless the content clearly dictates otherwise. As used in this specification and the appended claims, the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise.
In some cases, a flexible and transparent substrate 24, shown at the lower side (in the illustrated orientation) of
In the illustrative embodiment of
In some cases, the electron conductor layer 16 be a metallic and/or semiconducting material, such as TiO2 or ZnO. Alternatively, electron conductor layer 16 may be an electrically conducting polymer such as a polymer that has been doped to be electrically conducting and/or to improve its electrical conductivity. In at least some embodiments, electron conductor layer 16 may include an n-type conductor and/or form or otherwise be adjacent to the anode (negative electrode) of cell 10.
Hole conductor layer 18 may include a p-type conductor and/or form or otherwise be adjacent to the cathode (positive electrode) of cell 10. In some instances, hole conductor layer 18 may be a conductive polymer, but this is not required. The conductive polymer may, for example, be or otherwise include a functionalized polythiophene. An illustrative but non-limiting example of a suitable conductive polymer has
as a repeating unit, where R is absent or alkyl and m is an integer ranging from about 6 to about 12. The term “alkyl” refers to a straight or branched chain monovalent hydrocarbon radical having a specified number of carbon atoms. Examples of “alkyl” include, but are not limited to, methyl, ethyl, n-propyl, isopropyl, n-butyl, s-butyl, t-butyl, n-pentyl, n-hexyl, 3-methylpentyl, and the like.
Another illustrative but non-limiting example of a suitable conductive polymer has
as a repeating unit, where R is absent or alkyl.
Another illustrative but non-limiting example of a suitable conductive polymer has
as a repeating unit, where R is absent or alkyl.
Another illustrative but non-limiting example of a suitable conductive polymer has
as a repeating unit, where R is absent or alkyl.
The quantum dot layer 12 may include one quantum dot or a plurality of quantum dots. Quantum dots are typically very small semiconductors, having dimensions in the nanometer range. Because of their small size, quantum dots may exhibit quantum behavior that is distinct from what would otherwise be expected from a larger sample of the material. In some cases, quantum dots may be considered as being crystals composed of materials from Groups II-VI, III-V, or IV-VI materials. The quantum dots employed herein may be formed using any appropriate technique. Examples of specific pairs of materials for forming quantum dots include, but are not limited to, MgO, MgS, MgSe, MgTe, CaO, CaS, CaSe, CaTe, SrO, SrS, SrSe, SrTe, BaO, BaS, BaSe, BaTe, ZnO, ZnS, ZnSe, ZnTe, CdO, CdS, CdSe, CdTe, HgO, HgS, HgSe, HgTe, Al2O3, Al2S3, Al2Se3, Al2Te3, Ga2O3, Ga2S3, Ga2Se3, Ga2Te3, In2O3, In2S3, In2Se3, In2Te3, SiO2, GeO2, SnO2, SnS, SnSe, SnTe, PbO, PbO2, PbS, PbSe, PbTe, AlN, AlP, AlAs, AlSb, GaN, GaP, GaAs, GaSb, InN, InP, InAs and InSb.
In some cases, the quantum dot layer 12 may include quantum dots that are all the same size is noted, however, that the bandgap of a quantum dot is typically size dependent. Thus, a quantum dot layer 12 that includes quantum dots that are all the same may have a substantially uniform bandgap. Because of this “uniform bandgap”, such a quantum dot layer may only absorb light at or near a particular range of wavelengths of the electromagnetic spectrum. To provide absorption across a wider range of the electromagnetic spectrum, which may help increase the efficiency of the solar cell 20, it is contemplated that quantum dot layer 12 may be made to include quantum dots with a number of different bandgaps.
For example, some of the quantum dots in quantum dot layer 12 may include two elements. Some of the quantum dots may have one chemical formula (e.g, ZnSe) and some of the other quantum dots may have a different formula (e.g., CdSe). These two different quantum dots (having differing bandgaps) may allow quantum dot layer 12 with a “multi-bandgap” quantum dot layer 12.
Still other quantum dots are contemplated for quantum dot layer 12 that include three or more elements. These quantum dots, which may be known as the alloyed quantum dots, may have a variety of different bandgaps depending on the content of different elements in the quantum dots. For example, some quantum dots in quantum dot layer 12 may have the general formula of CdxZn1−xSe, where x is the fraction of Zn atoms among all Zn and Cd atoms in a quantum dot and may have a value that ranges from 0≦×≦1. If x is 0, these quantum dots may have a bandgap that more closely resembles (e.g., is the same or about the same as) a quantum dot that includes ZnSe (e.g., about 2.7 eV). As x increases to 1, these quantum dots may have a bandgap that more closely resembles (e.g., is the same or about the same as) a quantum dots that includes CdSe (e.g., about 1.7 eV).
For purposes of this disclosure, a multi-bandgap quantum dot layer may be understood as including a plurality of constituents or subcomponents that have different bandgaps. Accordingly, a multi-bandgap quantum dot layer (e.g., quantum dot layer 12) may include a number of quantum dots with a variety of different bandgaps that span a wider range of energies. This may allow the quantum dots in quantum dot layer 12 to collectively absorb light from a wider range of wavelengths of the electromagnetic spectrum, which may help improve the efficiency of solar cell 20.
As alluded to above, in order to provide quantum dot layer 12 with a multi-bandgap range, quantum dot layer 12 may include a plurality of alloyed quantum dots that differ in bandgap. For example, quantum dot layer 12 may include two, three, four, five, six, seven, eight, or more different quantum dots with a differing bandgap (e.g., due to their differences in contents or sizes).
Forming such a quantum dot layer 12 may be accomplished using any number of processes, methods and/or techniques. In one example method, differently alloyed quantum dots are formed in quantum dot layer 12. This method may include providing a first precursor compound, providing a second precursor compound, and combining a portion of the first precursor compound with a portion of the second precursor compound to form precursor quantum dots. In some embodiments, one of the precursor compounds (e.g., the first precursor compound) may include cadmium. For example, one of the precursor compounds may include a cadmium nitrilotriacetic acid, Cd(NO3)2, or any other suitable cadmium-containing compound. The other precursor compound (e.g., the second precursor compound) may include selenium. For example, one of the precursor compounds may include Na2SeSO3.
The example method for forming quantum dot layer 12 may also include combining a portion of the first precursor compound with a portion of the second precursor compound to form a number of “base” or precursor quantum dots. The combining step may include a number of different methods. For example, the combining step may include dip coating a substrate into the first precursor compound and then into the second precursor compound. In at least some embodiments, the substrate may include a glass substrate such as a low-iron glass, fluoride-doped tin oxide glass, indium tin oxide glass, any other suitable glass, an electrically conductive material, or any other suitable material as desired. In some of these and in other embodiments, the substrate may be or include an electron conductor layer 16.
Dip coating may result in a layer or shell of the appropriate precursor compound(s) being deposited or otherwise formed on the substrate. The dip coating process may be repeated a number of times (e.g., a total of two, three, four, five, six, or more) so that the desired amount of the precursor compound(s) are disposed on the substrate and form the precursor quantum dots. It can be appreciated that as the number of dip coating cycles increases, the relative amount of material formed on the substrate increases and, thus, the size of the resultant precursor quantum dots formed as part of the process. This process may be repeated, to form layers of quantum dots, where each layer has different size (and thus bandgap) quantum dots. When forming each layer, the dip coating process may be changed by, for example, having a different number of dip coating steps, a different concentration of first and second precursor compounds, different first and second precursor compounds, different dip coating conditions such as temperature, pH, light conditions, and/or other conditions, etc. This may form a gradient in the bandgap through the quantum dot layer 12.
Alternatively, or in addition, the combining step may also include a chemical bath deposition. In one example, the substrate may be exposed to one or both of the precursor compounds (e.g., formulated as or otherwise including a chemical bath deposition solution) in a chemical bath deposition process. In some embodiments, a relatively low concentration of the chemical bath deposition solution may be utilized. For example, the concentration of the chemical bath deposition solution may be about 20-30 mmol/L, or about 25-30 mmol/L, or about 26-27 mmol/L, or about 26.7 mmol/L. The pH may also be controlled for the chemical bath deposition. For example, the pH of the chemical bath deposition process may be basic, about 9-12, about 10-11, or about 10.5. Additionally, the temperature of the chemical bath deposition may be controlled. For example, the chemical bath deposition may be conducted at a temperature of about 0-80° C., or about 4-20° C., or about 8-12° C., or about 10° C.
Variations to any one or more of the chemical bath deposition parameters may alter the amount of material deposited onto the substrate as part of the chemical bath deposition process and, thus, the size of the resultant quantum dots formed. For example, the concentration of the precursor compounds utilized in the chemical bath deposition may impact the amount of material deposited onto the substrate. Likewise, changes in pH temperature, light exposure (which may be controlled using, for example, a graduated filter), electrical current, etc. may be employed. Like above, such changes may form a gradient that results in differing amounts of material being deposited and, thus, the size of the resultant precursor quantum dots formed. These differences may be utilized in processes that include chemical bath deposition and ion exchange (described below) or in processes that omit ion exchange so that quantum dots (e.g., in quantum dot layer 12) may be formed in different sizes and so as to have different bandgaps.
In some cases, the above combining step may form a multi-bandgap quantum dot layer 12 that includes a plurality of quantum dots that differ in bandgap. In some of these and in other cases, the example process for forming quantum dot layer 12 may also include alloying the quantum dots formed above as part of the combining step(s) to form a multi-bandgap quantum dot layer 12. In some cases, this may include an ion exchange reaction with an appropriate alloying material. For example, the quantum dots formed as part of the above combining steps may be alloyed in an ion exchange reaction with Zn2+. Other cations may be used such as those listed above from the pairs of materials that may be appropriate for forming quantum dots. When such cations are used, the precursor quantum dots may initially be at or near the same size.
The ion exchange reaction may include disposing the quantum dots formed as part of the combining step in the appropriate ion exchange solution (e.g., containing Zn2+ or any other suitable alloying cation). The precursor quantum dot or dots, which may be formed as a layer, layers, or film, may have a total thickness of about 1-15 μm or about 3-10 μm or so. As the ion exchange solution penetrates into the precursor quantum dots, a natural concentration gradient is formed. Thus, differing concentrations of the ion exchange solution may be available along different portions of the precursor quantum dots, resulting is differing levels of ion exchange. For example, the precursor quantum dots may generally include cadmium and selenium and different alloyed quantum dots may be formed having a general formula of ZnxCd1−xSe, where x is the fraction of Zn atoms among all Zn and Cd atoms in a quantum dot. This may result in a quantum dot layer 12 having a multi- bandgap as x ranges between 0 and 1.
Some of the methods include portions or all or some the steps and/or processes described above. One example process may include a dip coating step and a chemical bath deposition step followed by an ion exchange step. The precursor quantum dots may initially be about the same size. In this method, the concentration gradient formed in the ion exchange process may lead to the formation of quantum dots (e.g., in quantum dot layer 12) that differ in bandgap.
Other example processes may include only a chemical bath deposition step, where gradients formed in temperature, light, electrical current, combinations thereof, and the like, or any other parameters, may be varied so that quantum dots (e.g., in quantum dot layer 12) may be formed that differ in bandgap.
While the cells 10 and method for manufacturing cells 10 disclosed herein are described in terms of solar cells, it should be appreciated that this disclosure is also applicable to other thin-film devices, such as light emitting diodes (LED's ) and other devices. Consequently, to the extent applicable, this disclosure may analogously be applied to other thin film structures, as desired.
It should be understood that this disclosure is, in many respects, only illustrative. Changes may be made in details, particularly in matters of shape, size, and arrangement of steps without exceeding the scope of the invention. The invention's scope is, of course, defined in the language in which the appended claims are expressed.