Patent Application
20200115629
The present application relates to the field of photoelectron material preparation technology, and in particular, to a quantum dots preparation method and quantum dots.
Quantum dot technology was recognized by the market and rapidly developed due to its excellent thermal stability, high quantum efficiency, narrow peak width at half height, and high color gamut characteristics.
However, existing quantum dots, as shown in
The present application provides a quantum dots preparation method and the quantum dot to solve the technical problem that the luminescence spectrum has a narrow wavelength range.
To solve the above problems, the technical solution provided by the present application is as follows:
An embodiment of the present application provides a method for preparing quantum dot, which includes the following steps:
step 1, mixing a first lead halide with a surfactant, a cosolvent, and a non-polar solution to obtain a first mixture, and heating the first mixture to obtain a first lead halide solution;
step 2, mixing a cesium salt with an octadecene and a cosolvent to obtain a second mixture, and heating the second mixture to obtain a cerium oleate solution;
step 3, mixing the first lead halide solution with a manganese halide to obtain a third mixture and heating the third mixture to a first preset temperature, adding the cesium oleate solution to the third mixture, after a predetermined period of time, quenching the third mixture to a second preset temperature, and thereafter centrifuging and precipitating the third mixture until intermediate quantum dots are dispersed in the non-polar solution, thereby to obtain an intermediate quantum dot non-polar solution; and
step 4, adding a second lead halide to the intermediate quantum dot non-polar solution to obtain the target quantum dots, wherein halonium ions contained in the second lead halide are different from halonium ions contained in the first lead halide.
In the quantum dots preparing method of the present application, the target quantum dots include at least one of Mn:CsPbX3, Mn:CsPb2X5, and Mn:Cs4PbX6, wherein X is at least one of chlorine element, bromine element, and iodine element.
In the quantum dots preparation method of the present application, the halonium ions of the manganese halide are the same as halonium ions of the first lead halide.
In the quantum dots preparation method of the present application, the cesium salt includes at least one of cesium acetate, cesium carbonate, cesium nitrate, and cesium sulfate.
In the quantum dots preparation method of the present application, the surfactant includes at least one of oleylamine, laurylamine, octylamine, and hexylamine.
In the quantum dots preparation method of the present application, the cosolvent includes at least one of oleic acid, lauric acid, caprylic acid, caproic acid, acetic acid or methacrylic acid.
In the quantum dots preparation method of the present application, the non-polar solution includes at least one of dodecane and octadecene.
In the quantum dots preparation method of the present application, the step 2 and step 3 are performed under a vacuum condition.
In the quantum dots preparation method of the present application, the first preset temperature is 180° C., the predetermined period of time is 5 seconds, and the second preset temperature is room temperature.
In the quantum dots preparation method of the present application, the first lead halide in step 1 is in a form of a solution.
In the quantum dots preparation method of the present application, the manganese halide in step 3 is in a form of a solid.
In the quantum dots preparation method of the present application, the second lead halide in step 4 is in a form of a solution.
In the quantum dots preparation method of the present application, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is PbBr2.
In the quantum dots preparation method of the present application, the first lead halide is PbBr2, the manganese halide is MnBr2, and the second lead halide is PbCl2.
In the quantum dots preparation method of the present application, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is PbI2.
In the quantum dots preparation method of the present application, the first lead halide is PbI2, the manganese halide is MnI2, and the second lead halide is PbCl2.
In the quantum dots preparation method of the present application, the first lead halide is PbBr2, the manganese halide is MnBr2, and the second lead halide is PbI2.
In the quantum dots preparation method of the present application, the first lead halide is PbI2, the manganese halide is MnI2, and the second lead halide is PbBr2.
In the quantum dots preparation method of the present application, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is a mixed solution of PbBr2 and PbI2.
Meanwhile, the embodiment of the present application provides a quantum dot, the quantum is a target quantum dot obtained by the quantum dots preparation method provided by the present application.
The beneficial effects of the application are:
the present application provides a new quantum dot and a corresponding quantum dots preparation method. The quantum dots are doped with manganese ions and various kinds of halide ions such that when the quantum dots emit light, they will have a dual luminescence system, one is intrinsic luminescence of a perovskite quantum dot and the other is doping luminescence of manganese ion.
The ratio of amounts of the different substances based on various halide ions allows the perovskite intrinsic luminescence adjustable from 410 nm to 520 nm, it solves the technical problem that the conventional quantum dot has a narrow wavelength range of the luminescence spectrum, and it increases the wavelength range of the quantum dot luminescence spectrum so that the application scenario of the quantum dot is wider.
In order to more clearly illustrate the technical solutions in the embodiments of the present invention, the following figures described in the embodiments will be briefly introduced. It is obvious that the drawings described below are merely some embodiments of the present invention, other drawings can also be obtained by the person ordinary skilled in the field based on these drawings without doing any creative activity.
The following description of the various embodiments is provided to illustrate the specific embodiments of the invention. The directional terms mentioned in the present invention, such as “on,” “below”, “front”, “behind”, “left”, “right”, “inside”, “outside”, “side”, etc., are merely references of the direction in the drawings. Therefore, the directional terminology used is for the purpose of illustration and understanding of the invention rather than limiting the invention. In the drawings, the structurally similar elements are denoted by the same reference numerals.
The present application can solve the technical problem that the existing quantum dots having a narrow wavelength range of a luminescence spectrum. (as shown in
The present application provides a dual luminescence system of a manganese doped perovskite quantum dot by an ion doping method, one is intrinsic luminescence of perovskite quantum dots and the other is doping luminescence of manganese ions. We added a PbBr2 or PbI2 solution to a synthesized Mn:CsPbCl3, and successfully prepared Mn:CsPbBr3 or Mn:CsPbI3 particles by an ion exchange. By the ion exchange, we achieved intrinsic luminescence of perovskite adjustable from 410 to 480 nm, while the doping luminescence of manganese ion is maintained at 585 nm. By changing the amounts of the manganese ions added, a change in intensity of manganese ion doped luminescence can be achieved.
As shown in
step 1, mixing a first lead halide with a surfactant, a cosolvent, and a non-polar solution to obtain a first mixture, and heating the first mixture to obtain a first lead halide solution;
step 2, mixing cesium salt with octadecene and a cosolvent to obtain a second mixture, and heating the second mixture to obtain a cerium oleate solution;
step 3, mixing the first lead halide solution with a manganese halide to obtain a third mixture and heating the third mixture to a first preset temperature, adding a cesium oleate solution to the third mixture, after a predetermined period of time, quenching the third mixture to a second preset temperature, and thereafter centrifuging and precipitating the third mixture until intermediate quantum dots are dispersed in the non-polar solution, thereby to obtain an intermediate quantum dot non-polar solution; and
step 4, adding a second lead halide to the intermediate quantum dot non-polar solution to obtain target quantum dots, wherein halonium ions contained in the second lead halide are different from the halonium ions contained in the first lead halide.
In one embodiment, the target quantum dot includes at least one of Mn:CsPbX3, Mn:CsPb2X5, and Mn:Cs4PbX6, and X is at least one of a chlorine element, a bromine element, and an iodine element.
In one embodiment, halonium ions of the manganese halide are the same as the halonium ions of the first lead halide.
In one embodiment, the onium salt includes at least one of cesium acetate, cesium carbonate, cesium nitrate, and cesium sulfate.
In one embodiment, the surfactant includes at least one of oleylamine, laurylamine, octylamine, and hexylamine.
In one embodiment, the cosolvent includes at least one of oleic acid, lauric acid, caprylic acid, caproic acid, acetic acid or methacrylic acid.
In one embodiment, a non-polar solution includes at least one of dodecane and octadecene.
In one embodiment, steps 2 and 3 are performed under a vacuum condition to ensure that the liquid does not volatilize into the air under a high temperature conditions and thus does not contaminate the air.
In one embodiment, the first preset temperature is 180° C., the predetermined period of time is 5 seconds, and the second preset temperature is room temperature.
In one embodiment, the first lead halide in step 1 is in the form of a solution.
In one embodiment, the manganese halide in step 3 is in a form of a solid.
In one embodiment, the second lead halide in step 4 is in the form of a solution.
In one embodiment, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is PbBr2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of a PbCl2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.) until the solids are all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of an octadecene (ODE) solution to mix under a vacuum condition, and heating them at 120-150° C. until the solids are completely dissolved, and finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbCl2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnCl2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnCl2 solids are completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated, and finally obtaining square Mn:CsPbCl3 particles of about 10 nm. As shown in
Under a normal temperature and pressure, a PbBr2 solution is added dropwise to the synthesized Mn:CsPbCl3 particles non-polar solution, and finally Mn:CsPbCl3 particles and Mn:CsPbBr3 particles can be obtained.
As shown in
By an ion exchange, the present application can obtain a series of a dual luminescence system composed of various wavelengths.
Specifically, when the molar ratio of Mn:CsPbBr3 particles to Mn:CsPbCl3 particles (Br/Cl) fixed at 0.05, different doping concentrations of the manganese ions will result in different doping luminescence intensity peaks.
As shown in
As shown in
As shown in
Specifically, when the doping concentration of the manganese ions fixed at 20%, the molar ratio of Mn:CsPbBr3 particles to Mn:CsPbCl3 particles (Br/Cl) varies, the luminescence intensity peak of the intrinsic luminescence of perovskite varies accordingly.
As shown in
As shown in
As shown in
As shown in
As shown in
As shown in
As shown in
In one embodiment, the first lead halide is PbBr2, the manganese halide is MnBr2, and the second lead halide is PbCl2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of PbBr2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids were all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halides different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of the octadecene (ODE) solution to mix under vacuum condition, and heating the solution at 120-150° C. until the solids were completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbBr2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnBr2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnBr2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbBr3 particles of about 10 nm.
Under a normal temperature and pressure, the PbCl2 solution is added dropwise to the synthesized Mn:CsPbBr3 particles non-polar solution, and finally Mn:CsPbCl3 particles and Mn:CsPbBr3 particles can be obtained.
In one embodiment, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is PbI2.
In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of the PbCl2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids are all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halides different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of the octadecene (ODE) solution to mix under vacuum condition, and heating the solution at 120-150° C. until the solids are completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbCl2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnCl2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnCl2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbCl3 particles of about 10 nm.
Under a normal temperature and pressure, a PbI2 solution is added dropwise to the synthesized Mn:CsPbCl3 particles non-polar solution, and finally Mn:CsPbCl3 particles and Mn:CsPbI3 particles can be obtained.
In one embodiment, the first lead halide is PbI2, the manganese halide is MnI2, and the second lead halide is PbCl2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of PbI2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids were all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halides different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of the octadecene (ODE) solution to mix under vacuum condition, and heating the solution at 120-150° C. until the solids are completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbI2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnI2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnI2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbI3 particles of about 10 nm.
Under a normal temperature and pressure, a PbCl2 solution is added dropwise to the synthesized Mn:CsPbI3 particles non-polar solution, and finally Mn:CsPbCl3 particles and Mn:CsPbI3 particles can be obtained.
In one embodiment, the first lead halide is PbBr2, the manganese halide is MnBr2, and the second lead halide is PbI2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of a PbBr2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids were all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halides different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of the octadecene (ODE) solution to mix under a vacuum condition, and heating the solution at 120-150° C. until the solids are completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbCl2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnBr2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnBr2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbBr3 particles of about 10 nm.
Under a normal temperature and pressure, a PbI2 solution is added dropwise to the synthesized Mn:CsPbBr3 particles non-polar solution, and finally Mn:CsPbBr3 particles and Mn:CsPbI3 particles can be obtained.
In one embodiment, the first lead halide is PbI2, the manganese halide is MnI2, and the second lead halide is PbBr2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of the PbI2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids were all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halides different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA), and 18 ml of the octadecene (ODE) solution to mix under a vacuum condition, and heating the solution at 120-150° C. until the solids are completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbI2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnBr2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnI2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbI3 particles of about 10 nm.
Under a normal temperature and pressure, the PbBr2 solution is added dropwise to the synthesized Mn:CsPbI3 particles non-polar solution, and finally Mn:CsPbBr3 particles and Mn:CsPbI3 particles can be obtained.
In one embodiment, the first lead halide is PbCl2, the manganese halide is MnCl2, and the second lead halide is a mixed solution of PbBr2 and PbI2. In the above condition, the quantum dots preparation method provided by the present application is:
Mixing a certain amount (0.2 mmol) of the PbCl2 solution with 0.5 ml of oleic acid, 0.5 ml of oleylamine, and 3 ml of a non-polar alkyl solution (such as dodecane, octadecene, etc.), following heating the solution until the solids were all dissolved, and finally obtaining a backup oleylamine/oleic acid coordination solution having lead halide different from above. The concentration of lead halide is adjustable.
Taking 0.65 g of Cs2CO3, 2.5 ml of oleic acid (OA) and 18 ml of the octadecene (ODE) solution to mix under a vacuum condition, and heating the solution at 120-150° C. until the solids are completely dissolved, finally obtaining a cesium oleate solution. The concentration of cesium oleate and the heating temperature are adjustable.
Taking the PbCl2 solution prepared above, adding a certain amount (such as 0.08 mmol) of MnCl2 solid thereto. Heating and stirring the solution under a vacuum condition until the MnCl2 solids were completely solved, next the solution is heated to 180° C. and adding 0.2 ml of the cesium oleate solution thereto, and after 5 seconds, the solution is quenched to room temperature, following the solution is centrifuged and separated and finally obtaining square Mn:CsPbCl3 particles of about 10 nm.
Under a normal temperature and pressure, the PbBr2 and PbI2 solutions were added dropwise to the synthesized Mn:CsPbCl3 particles non-polar solution, and finally Mn:CsPbCl3 particles, Mn:CsPbBr3 particles and Mn:CsPM3 particles can be obtained.
Meanwhile, the embodiment of the present application provides a plurality of quantum dots, the quantum dots is at least one of the target quantum dots obtained by the method of preparing the quantum dots according to the present application.
The quantum dots are doped with manganese ions and various kinds of halogen ions such that when the quantum dots emit light, they will have a dual luminescence system, one is intrinsic luminescence of perovskite quantum dots and the other is doping luminescence of manganese ions.
The intrinsic luminescence of perovskite is adjustable from 410 nm to 520 nm based on the ratio of the amounts of different substances having various halide ions.
Meanwhile, the embodiment of the present application provides a display device, such as a light-emitting diode (LED) device or the like, which uses the quantum dots obtained by the invention.
Meanwhile, in order to enhance the stability of quantum dot luminescence, the present application includes the following steps when preparing a quantum dots device:
Step 5, mixing the target quantum dots solution obtained in step 4 with a polydimethylsiloxane (PDMS) solution, and stirring to obtain a uniformly mixed solution. The volume ratio of the target quantum dots solution to the PDMS solution is preferably 1: (1-2). The concentration of the target quantum dots solution is preferably 25 mg/ml. The concentration of the PDMS solution is preferably 10 mg/ml.
Step 6, the mixed solution obtained in step 5 is applied onto a silicon substrate, dried naturally in the air, or placed in an oven at 50° C. for 30 minutes to form a film. The film is placed in a vacuum apparatus for continuous variable temperature heat treatment and conventional annealing heat treatment to obtain a heat-treated sample, and the heat-treated sample is subjected to a luminescence heat stability test.
The temperature range in the variable temperature heat treatment is preferably from 20° C. to 140° C. The treatment time is preferably from 10 min to 2 h.
The annealing heat treatment temperature can be selected to be 60° C., 80° C., and 100° C., and the treatment time is for 10 minutes respectively. The vacuum apparatus is preferably a cryogenic storage Dewar.
The present invention effectively improves the thermal stability of the quantum dots by embedding the quantum dots in the PDMS.
The doping of the manganese ions increases the stability of the crystal, and besides, the use of a PDMS coating agent can significantly inhibit a surface ligand of quantum dots from shedding and inhibit the agglomeration and growth of quantum dots.
Specifically, the organic chain of PDMS interacts with the ligand on a surface of the quantum dots to isolate the quantum dots and prevent the polymerization and growth of quantum dots at higher temperatures, meanwhile, the interaction between them can also protect the surface ligand, prevent it from falling off, reduce the surface defect state, and its luminescence stability will be enhanced, thereby improving its luminescent thermal stability.
According to the above embodiment, it can be known that the present application provides the quantum dots preparation method and the quantum dots, the quantum dots are doped with the manganese ions and various kinds of the halogen ions such that when the quantum dots emit light, they will have the dual luminescence system, one is intrinsic luminescence of the perovskite quantum dots and the other one is doping luminescence of the manganese ions. The intrinsic luminescence of perovskite is adjustable from 410 nm to 520 nm based on the ratio of the amounts of different substances having various halide ions, which increases the wavelength range of the quantum dots luminescence spectrum so that the application scenario of the quantum dots is wider.
The description of the above exemplary embodiments is only for the purpose of understanding the invention. It is to be understood that the present invention is not limited to the disclosed exemplary embodiments. It is obvious to those skilled in the art that the above exemplary embodiments may be modified without departing from the scope and spirit of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201811196378.8 | Oct 2018 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2019/072109 | 1/17/2019 | WO | 00 |