TREA

R-Tl-Sr-Ca-Cu-O superconductors

Follow

Information

  • Patent Grant
  • 5036044
  • Patent Number
    5,036,044
  • Date Filed
    Thursday, September 29, 1988
    36 years ago
  • Date Issued
    Tuesday, July 30, 1991
    33 years ago
Information
Abstract
A high temperature superconductor system is provided having the following formula: M-A-B-C-D-E, wherein, M is a metallic element, A is an element in Group 3A, B is an element in Group 2A, C is another element in Group 2A, D is an element in Group 1B, and E is an element in Group 6A. In an embodiment, the high temperature superconductor has the following formula: R-Tl-Sr-Ca-Cu-O (wherein R is chosen from the group consisting of La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y). Processes for making these high temperature superconductors are also disclosed.
Description

BACKGROUND OF THE INVENTION
The present invention relates generally to high temperature superconductors. More specifically, the present invention relates to a new high temperature superconductor system and processes for making same.
A variety of superconducting systems are known. The inventors of the present patent application have filed the following patent applications that disclose superconductors and/or methods of making same.
U.S. patent application Ser. No. 144,114 discloses a high temperature superconductor having the composition Tl-R-X-Y wherein: R is an element chosen from Group 2A; X is an element chosen from Group IB; and Y is an element chosen from Group 6A.
U.S. patent application Ser. No. 155,247 discloses a high temperature superconductor having the composition: Tl-R-Ba- Cu-O wherein R is a Group 2A element excluding barium; Tl-Sr-Cu-O. In an embodiment, R is either strontium or calcium.
U.S. Patent application Ser. No. 082,222 discloses a high temperature superconductor having the composition: Tb-R-Ba-Cu-O wherein R is chosen from the group of rare earth metals excluding: praseodymium; cerium; and terbium.
U.S. patent application Ser. No. 089,067 discloses a high temperature superconductor having the composition: R-Ba-Cu-O wherein R is chosen from the group of rare earth metals excluding: praseodymium; terbium; and cerium.
U.S. patent application Ser. No. 236,502 discloses a process for making Tl-Ba-Ca-Cu-O superconductors
Applicants have also filed, on the same day as the instant patent application, a patent application entitled: "Tl-Sr-Ca-Cu-O SUPERCONDUCTORS AND PROCESSES FOR MAKING SAME". The patent application discloses a high temperature superconductor having the formula Tl-Sr-Ca-Cu-O and processes for making same.
A new superconductor would be desirable for many reasons. Such a superconductor would: (1) facilitate the discovery of the correct theory on oxide superconductivity; (2) provide a framework for the search for higher temperature, even room temperature superconductors; (3) allow superconducting components to operate with lower cost; and (4) provide low cost processing and manufacturability. Furthermore, in superconducting systems including Tl, there is a drawback in that Tl is toxic. Therefore, a superconducting system with a reduced amount of Tl would be desirable.
Accordingly, there is a need for new high temperature superconductors.
SUMMARY OF THE INVENTION
The present invention provides a new superconductor system that yields a number of new high temperature superconductors with transition temperatures above liquid nitrogen temperature that are unique to date among all high temperature superconductors
The present invention comprise a system containing six elements:
M-A-B-C-D-E
wherein:
M, A, B, C, and D are metallic elements; and
E is a non-metallic element.
Preferably, M is a metallic element, A is an element in Group 3A, B, and C are elements in Group 2A, D is an element in Group 1B, and E is an element in Group 6A.
In a preferred embodiment, M is a rare earth, including La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y; A is thallium (Tl); B is strontium (Sr); C is calcium (Ca); D is copper (Cu); and E is oxygen (0).
In an embodiment, the superconductor of the present invention has the following formula:
Pr-Tl-Sr-Ca-Cu-O.
In an embodiment, the superconductor of the present invention has the following formula:
Tb-Tl-Sr-Ca-Cu-O.
In an embodiment, the superconductor of the present invention has the following approximate stoichiometry:
RTl.sub.x Sr.sub.y Ca.sub.z Cu.sub.u O.sub.v
wherein:
x is greater than 0.1 and less than 10;
Y is greater than or equal to 0 and less than or equal to 10;
z is greater than or equal to 0 and less than or equal to 10;
y+z is greater than 0.1 and less than 20;
u is greater than 0.1 and less than 20;
v is greater than x+y+z+u and less than 5+x+y+z+u; and
R is a rare earth metal.
Methods for producing the high temperature superconductors of the present invention are also provided. The methods allow the superconductors to be prepared at temperatures of approximately 850 to about 1OOO.degree. CC in flowing oxygen.
Accordingly, an advantage of the present invention is to provide a number of new superconducting systems having high transition temperatures.
A further advantage of the present invention is to provide a number of material systems that may produce higher temperature, even room temperature superconductors.
A still further advantage of the present invention is that it provides a number of new high temperature superconductors that can be rapidly fabricated.
Furthermore, an advantage of the present invention is that it provides processes for making new high temperature superconductors.
Still another advantage of the present invention is that it provides processes for rapidly making high temperature superconductors.
Additional features and advantages of the present invention will be apparent from the detailed description of the presently preferred embodiments and from the drawings





BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 illustrates graphically ac (5 Khz) resistance versus temperature for nominal RTl.sub.2 Sr.sub.2 Ca.sub.3 Cu.sub.3 O.sub.12 samples with R=La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y.
FIG. 2 illustrates graphically dc resistance versus temperature for La-Tl-Sr-Ca-Cu-O, Pr-Tl-Sr-Ca-Cu-O, and Tb-Tl-Sr-Ca-Cu-O samples.
FIG. 3 illustrates graphically ac (5 Khz) susceptibility versus temperature dependences for a Pr-Tl-Sr-Ca-Cu-O sample and a Tb-Tl-Sr-Ca-Cu-O sample.





DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS
The present invention provides a new superconductor system that provides a number of new superconductors with phases whose transition temperatures are above liquid nitrogen temperature. The present invention also provides a number of new material systems that may produce higher temperature, even room temperature superconductors by further elemental substitution and variation of preparation procedures. In addition, the present invention provides processes for making these new high temperature superconductors.
The present invention comprises a superconducting system containing six elements:
M-A-B-C-D-E
wherein:
M, A, B, C, and D are metallic elements; and
E is a non-metallic element.
Preferably, M is a metallic element, A is an element in Group 3A, B and C are elements in Group 2A, D is an element in Group 1B, and E is an element in Group 6A.
In a preferred embodiment, M is a rare earth (including La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y), A is thallium, B is strontium (Sr), C is calcium (Ca), D is copper (Cu), and E is oxygen (0).
In a preferred embodiment, the superconductor of the present invention has the following formula:
R-Tl-Sr-Ca-Cu-O
wherein:
R=La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y.
The inventors of the present invention have found that superconductors having this formula are superconducting above liquid nitrogen temperature. To date, the following above-liquid-nitrogen-temperature superconducting systems are known: rare earth-Ba-Cu-O (90K); Tl-Ba-Cu-O (90K); Bi-Sr-Ca-Cu-O (110K); and Tl-Ba-Ca-Cu-O (120K). The R-Tl-Sr-Ca-Cu-O systems of the present invention are the fifth above-liquid-nitrogen-temperature superconducting systems.
The present invention provides a number of new superconductors that can be operated at higher temperature with lower cost. Furthermore, the new high temperature superconductors of the present invention can be rapidly produced.
In a preferred embodiment, the superconductors in the new superconductive systems having the following approximate stoichiometry:
RTl.sub.x Sr.sub.y Ca.sub.z Cu.sub.u O.sub.v
wherein:
x is greater than 0 and less than 10;
Y is greater than or equal to 0 and less than or equal to 10;
z is greater than or equal to 0 and less than or equal to 10;
Y+z is greater than 0.1 and less than 20;
u is greater than 0.1 and less than 20;
v is greater than x+y+z+u and less than 5+x+y+z+u; and
R is a rare earth metal.
By way of example and not limitation, examples of methods for making the new high temperature R-Tl-Sr-Ca-Cu-O superconductors will now be given.
EXAMPLE 1
A. The following reagents were utilized:
1. La.sub.2 O.sub.3
2. Tl.sub.2 O.sub.3
3. SrCO.sub.3
4. CaCO.sub.3
5. CuO
B. The following procedure was followed:
A mixture of SrCO.sub.3, CaCO.sub.3, and CuO with a molar ratio of 2:2:3 was completely ground.
2. The mixture was heated at 950.degree. C. in air for at least 24 hours with several intermediate grindings.
3. The heated mixture was cooled and ground, so that a powder with a nominal composition of Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 was obtained.
4. A mixture of La.sub.2 O.sub.3, Tl.sub.2 O.sub.3, and Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 with a molar ratio of 1:2:2:2:3 (La:Tl:Sr:Ca:Cu) was ground and pressed into a pellet.
5. A tube furnace was heated to 900.degree. C. in flowing oxygen.
6. The pellet was put in a platinum boat, and the boat was placed in the tube furnace, maintaining the temperature and oxygen flow for 3 minutes.
7. The pellet was then furnace-cooled to room temperature.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is shown in FIG. 1 (curve La) and FIG. 2 (curve Lal). This sample reached zero resistance at liquid nitrogen temperature.
EXAMPLE 2
The procedure was the same as that set forth Example 1 except that La.sub.2 O.sub.3 was replaced by Pr.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Pr) and FIG. 2 (curve Pr3). This sample reached zero resistance at liquid nitrogen temperature. FIG. 3 illustrates ac susceptibility-temperature dependence for this sample (curve Pr12223 in FIG. 3).
EXAMPLE 3
The same procedure as that used in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Nd.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Nd).
EXAMPLE 4
The same procedure as that set forth in Example 1 was used except that La.sub.2 O.sub.3 was replaced by Sm.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The ac resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Sm).
EXAMPLE 5
The same procedure as that set forth in Example 1 was used except that La.sub.2 O.sub.3 was replaced by Eu.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Eu).
EXAMPLE 6
The same procedure as that set forth in Example 1 was used except that La.sub.2 O.sub.3 was replaced by Gd.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Gd).
EXAMPLE 7
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Tb.sub.4 O.sub.7.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Tb). The ac susceptibility-temperature dependence for the sample is illustrated in FIG. 3 (curve Tb12223).
EXAMPLE 8
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Dy.sub.2 O.sub.3.
The sample prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Dy).
EXAMPLE 9
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Ho.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Ho).
EXAMPLE 10
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Er.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Er).
EXAMPLE 11
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Tm.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Tm).
EXAMPLE 12
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Yb.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Yb).
EXAMPLE 13
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Lu.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Lu).
EXAMPLE 14
The same procedure as that set forth in Example 1 was followed except that La.sub.2 O.sub.3 was replaced by Y.sub.2 O.sub.3.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 1 (curve Y).
EXAMPLE 15
A. The following reagents were utilized:
1. La.sub.2 O.sub.3
2. Tl.sub.2 O.sub.3
3. SrCO.sub.3
4. CaCO.sub.3
5. CuO
B. The following procedure was followed:
A mixture of SrCO.sub.3, CaCO.sub.3, and CuO with a molar ratio of 2:2:3 was completely ground.
2. The mixture was heated at 950.degree. C. in air for at least 24 hours with several intermediate grindings.
The heated mixture was cooled and ground, so that a powder with a nominal composition of Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 was obtained.
4. A mixture of La.sub.2 O.sub.3 and Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 with an atomic molar ratio of 1:2:2:3 (La:Sr:Ca:Cu) was ground and pressed into a pellet.
5. The pellet was heated at 950.degree. C. in air or flowing oxygen for 3-10 minutes.
6. A tube furnace was heated to 900.degree. C. in flowing oxygen.
7. 0.1 to about 0.2 gram of Tl.sub.2 O.sub.3 was put in a platinum boat which was put in a quartz boat, and the heated pellet was put over the platinum boat.
8. The quartz boat and its contents was placed in the tube furnace, maintaining the temperature and oxygen flow for 2 to about 5 minutes.
9. The quartz boat with its contents was then furnace-cooled to room temperature.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature.
EXAMPLE 16
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Pr.sub.2 O.sub.3.
EXAMPLE 17
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Nd.sub.2 O.sub.3.
EXAMPLE 18
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Sm.sub.2 O.sub.3.
EXAMPLE 19
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Eu.sub.2 O.sub.3.
EXAMPLE 20
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Gd.sub.2 O.sub.3.
EXAMPLE 21
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Tb.sub.4 O.sub.7.
EXAMPLE 22
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Dy.sub.2 O.sub.3.
EXAMPLE 23
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Ho.sub.2 O.sub.3.
EXAMPLE 24
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Er.sub.2 O.sub.3.
EXAMPLE 25
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Tm.sub.2 O.sub.3.
EXAMPLE 26
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Yb.sub.2 O.sub.3.
EXAMPLE 27
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Lu.sub.2 O.sub.3.
EXAMPLE 28
The same procedure as that set forth in Example 15 was followed except La.sub.2 O.sub.3 was replaced by Y.sub.2 O.sub.3.
EXAMPLE 29
A. The following reagents were utilized:
1. Pr.sub.2 O.sub.3
2. Tl.sub.2 O.sub.3
3. SrCO.sub.3
4. CaCO.sub.3
5. CuO
B. The following procedure was followed:
A mixture of SrCO.sub.3, CaCO.sub.3, and CuO with a molar ratio of 2:2:3 was completely ground.
2. The mixture was heated at 950.degree. C. in air for at least 24 hours with several intermediate grindings.
3. The heated mixture was cooled and ground, so that a powder with a nominal composition of Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 was obtained.
4. A mixture of Pr.sub.2 O.sub.3, Tl.sub.2 O.sub.3, and Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7 with an atomic molar ratio of 1:2:2:2:3 (Pr:Tl:Sr:Ca:Cu) was ground and pressed into a pellet.
5. A tube furnace was heated to 950.degree. C. in flowing oxygen.
6. The pellet was put in a platinum boat, and the boat was placed in the tube furnace, maintaining the temperature and oxygen flow for 2 minutes.
7. The platinum boat with the pellet was then furnace-cooled to room temperature
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The dc resistance-temperature dependence for a sample prepared pursuant to this example is illustrated in FIG. 2 (curve Pr2). This sample reached zero resistance at liquid nitrogen temperature.
EXAMPLE 30
A. The following reagents were utilized:
1. Pr.sub.2 O.sub.3
2. Tl.sub.2 O.sub.3
3. SrCO.sub.3
4. CaCO.sub.3
5. CuO
B. The following procedure was followed:
A mixture of SrCO.sub.3, CaCO.sub.3, and CuO with a molar ratio of 2:4:5 was completely ground.
2. The mixture was heated at 950.degree. C. in air for at least 24 hours with several intermediate grindings.
3. The heated mixture was cooled and ground, so that a powder with a nominal composition of Sr.sub.2 Ca.sub.4 Cu.sub.5 O.sub.11 was obtained.
4. A mixture of Pr.sub.2 O.sub.3, Tl.sub.2 O.sub.3, and Sr.sub.2 Ca.sub.4 Cu.sub.5 O.sub.11 with an atomic molar ratio of 1:1:2:4:5 (Pr:Tl:Sr:Ca:Cu) was ground and pressed into a pellet.
5. A tube furnace was heated to 900.degree. C. in flowing oxygen.
6. The pellet was put in a platinum boat, and the boat was placed in the tube furnace, maintaining the temperature and oxygen flow for 3 minutes.
7. The pellet was annealed at 710.degree. C. in flowing oxygen for 10 hours, followed by furnace-cooling to room temperature.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The dc resistance-temperature dependence for a sample prepared pursuant to the method of this example is illustrated in FIG. 2 (curve Pr1).
EXAMPLE 31
The same procedure as that set forth in Example 30 was followed except that Pr.sub.2 O.sub.3 was replaced by Tb.sub.4 O.sub.7.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The dc resistance-temperature dependence for a sample prepared pursuant to the method of this example is illustrated in FIG. 2 (curve Tb2).
EXAMPLE 32
A. The following reagents were utilized:
1. Tb.sub.4 O.sub.7
2. Tl.sub.2 O.sub.3
3. SrCO.sub.3
4. CaCO.sub.3
5. CuO
B. The following procedure was followed:
1. A mixture of SrCO.sub.3, CaCO.sub.3, and CuO with a molar ratio of 2:4:5 was completely ground.
2. The mixture was heated at 950.degree. C. in air for at least 24 hours with several intermediate grindings.
3. The heated mixture was cooled and ground, so that a powder with a nominal composition of Sr.sub.2 Ca.sub.4 Cu.sub.5 O.sub.11 was obtained.
4. A mixture of Tb.sub.4 O.sub.7, Tl.sub.2 O.sub.3, and Sr.sub.2 Ca.sub.4 Cu.sub.5 O.sub.11 with an atomic molar ratio of 1:1:2:4:5 (Tb:Tl:Sr:Ca:Cu) was ground and pressed into a pellet.
5. A tube furnace was heated to 950.degree. C. in flowing oxygen.
6. The pellet was put in a platinum boat, and the boat was placed in the tube furnace, maintaining the temperature and oxygen flow for 3 minutes.
7. The pellet was then quenched in air to room temperature.
The samples prepared by this procedure were found to be superconducting above liquid nitrogen temperature. The dc resistance-temperature dependence for a sample prepared pursuant to this method is illustrated in FIG. 2 (curve Tbl).
It should be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the spirit and scope of the present invention and without diminishing its attendant advantages. It is therefore intended that such changes and modifications be covered by the appended claims.
Claims
  • 1. A composition having superconductive properties the composition comprising a melt produced complex having the nominal formula:
  • R-Tl-Sr-Ca-Cu-O
  • wherein R is a rare earth metal, and the atomic molar ratio of R:Tl:Sr:Ca:CU is 1:2:2:2:3.
  • 2. A composition having superconductive comprising a melt produced complex having the following nominal formula:
  • Pr-Tl-Sr-Ca-Cu-O
  • wherein the atomic molar ratio of Pr:Tl:Sr:Ca:Cu is 1:2:2:2:3.
  • 3. A composition having superconductive properties comprising a melt produced complex having the nominal formula:
  • Tb-Tl-Sr-Ca-Cu-O
  • wherein the atomic molar ratio of Tb-Tl-Sr-Ca-Cu is 1:2:2:2:3.
  • 4. A composition having superconductive properties comprising a melt produced complex having the following nominal approximate stoichiometry:
  • RTl.sub.2 Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7
  • wherein R is chosen from the group consisting of La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and Y.
  • 5. A composition having superconductive properties comprising a melt produced complex having the following nominal approximate stoichiometry:
  • PrTl.sub.2 Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7.
  • 6. A composition having superconductive properties comprising a melt produced complex having the following nominal approximately stoichiometry:
  • TbTl.sub.2 Sr.sub.2 Ca.sub.2 Cu.sub.3 O.sub.7.
US Referenced Citations (1)
Number Name Date Kind
4880773 Itozaki et al. Nov 1989
Foreign Referenced Citations (3)
Number Date Country
0292340 Mar 1988 JPX
0301952 Jul 1988 JPX
0301958 Jul 1988 JPX
Non-Patent Literature Citations (20)
Entry
Nagashimo "Superconductivity in Tl.sub.1.5 Sr Ca Cu.sub.2 O.sub.x " Jap. Jnl of Appld. Phys. vol. 27, No. 6 pp. L1077-L1079, Jun. 1988.
Saito "High-Tc Superconducting Properties in (Y.sub.1-x Tl) Ba.sub.2 Cu.sub.3 O.sub.7 ", Physica 148B 1987 pp. 336-338.
Ishida "Compositional Variation of High T.sub.c in Yb.sub.x Er.sub.1-x Ba.sub.2 Cu.sub.3 O.sub.6+y" Jap. Jnl. Appld. Phys. vol. 26, No. 8, Aug. 1987, pp. L1294-L1295.
Ihara "Possibility of Superconductivity at 65.degree. C. in Sr-Ba+Y-Cu-O" Jap. Jnl. of Appld. Phys. vol. 26, No. 8 Aug. 1987, pp. L1413-L1415.
Bhattacharya "High-Temp. Superconducting Properties in Y.sub.1-x A.sub.x Ba.sub.2 Cu.sub.3 O.sub.7-x . . . " Physica C 152 Jun. 1, 1988, pp. 283-285.
Hasegawa, T., High T.sub.c Superconductivity of (La.sub.1-x Sr.sub.x).sub.2 CuO.sub.4 -Effect of Substitution of Foreign Ions for Cu and La on Superconductivity, Japan Journal Applied Physics, vol. 26, No. 4, Apr. 20, 1987, L337-L338.
Kishio, K., Effect of Lanthanide Ion Substitutions for Lanthanum Sites on Superconductivity of (La.sub.1-x Sr.sub.x).sub.2 Cuo.sub.4-.alpha. Japan Journal of Applied Physics, vol. 26, No. 4, Apr. 20, 1987, L391-L393.
Ohshima, S., Superconducting and Structural Properties of the New Ba.sub.1-x Ln.sub.x CuO.sub.3-y Compound System (Ln.dbd.La, Ce, Pr, Nd, Sm, Eu, Gd, TB, Dy, Ho, Er and Yb), Japan Journal of Applies Physics, vol. 26, No. 5, May 20, 1987, L815-L817.
Tsurumi, S., High T.sub.c Superconductivities of A.sub.2 Ba.sub.4 Cu.sub.6 O.sub.14+Y, Japan Journal of Applied Physics, vol. 26, No. 5, May, 1987, L856-L857.
Superconductivity News, vol. 1, No. 2, Aug. 1987, pp. 1, 2, and 6-8.
Yang, K. N., High Temperature Superconductivity in Rare-Earth (R)-Barium Copper Oxides (RBa.sub.2)Cu.sub.3 O.sub.9.alpha. Solid State Communications, vol. 63, No. 6, 1987, pp. 515-519.
Tarascon, J. M., Oxygen and Rare-Earth Doping of the 90-K Superconducting Perovskite YBa.sub.2 Cu.sub.3 O.sub.7-x, The American Physical Society, vol. 36, No. 1, 1987, pp. 226-234.
Hor, P. H., Superconductivity Above 90 K in the Square-Planar Compound System ABa.sub.2 Cu.sub.3 O.sub.6+x with A=Y, La, Nd, Sm, Eu, Gd, Ho, Er, and Lu, The American Physical Society, vol. 58, No. 18, 1987, pp. 1891-1894.
Khurana, A., Superconductivity Seen Above the Boiling Point of Nitrogen, Physics Today, Apr. 1987, pp. 17-23.
Cava, R. J., Bulk Superconductivity at 91 K in Single-Phase Oxygen-Deficient Perovskite Ba.sub.2 YCu.sub.3 O.sub.9-s, The American Physical Society, vol. 58, No. 16, 1987.
Nagashima, T., et al., Superconductivity in Tl.sub.1.5 SrCaCu.sub.2 O.sub.x, Japanese Journal of Applied Physics, vol. 27, No. 6 Jun., 1988, L1077-L1079.
Kondoh, S., et al., Superconductivity in Tl-Ba-Cu-O System, Solid State Communications, vol. 65, No. 11, 1988, 1329-1331.
Sera, M., et al, On the Structure of High-T.sub.c Oxide System Tl-Ba-Cu-O.
Kijima, T., et al, Superconductivity in the Bi-Sr-La-Cu-O system, Japanese Journal of Applied Physics, vol. 27, No. 6, Jun., 1988, L1035-L1037.
Richert, B. et al., Atomic Substitution in YBa.sub.2 Cu.sub.3 O.sub.7 : Modification of the Electronic Structure, American Institute of Physics COnference Proceeding No. 165 (Thin Film Processing and Characterization of High-Temperature Superconductors), Nov. 6, 1987, 227-283.