In various embodiments, the present invention relates to support structures for high-temperature processing.
While high-temperature metal fabrication and joining processes are used in many different industries and to generate a host of different metallic parts, the extreme temperatures of such processes place many demands on the processing spaces and support structures utilized during processing. The joining of metal parts via high-temperature brazing (i.e., the joining of materials via a joint composed of a brazing material) is one such example, as the support structure on which the parts rest during processing must be able to tolerate vacuum or reducing ambients and extreme temperatures (e.g., greater than 1000° C.) without deformation or failure.
Conventional support structures for brazing processes include rack-like structures fastened together via welding or riveting, but such structures are typically unsuited for the extreme environments utilized in high-temperature brazing processes. Specifically, the materials of which such structures are composed may deform or fail when supporting heavy loads (i.e., the parts being brazed, which may weigh hundreds of kilograms or more) at extreme temperatures. Conventional support structures may deform under such conditions by, e.g., creep, and disturb the parts being brazed or even fail entirely, resulting in economic loss and reduced productivity. Thus, there is a need for improved structures capable of supporting heavy loads during high-temperature processes without deformation, failure, or reaction with processing ambients or metallic parts being processed.
In accordance with various embodiments of the present invention, support racks for high-temperature processing (e.g., brazing, dewaxing, or the like) are formed of a series of plates (or “shelves”) supported and separated from each other by threaded posts incorporating support collars for improved stability. In various embodiments, the bottom end of the post is threaded and engages with a complementarily threaded hole in the shelf below, while the top end of the post includes a support collar for supporting the shelf above. In various other embodiments, the upper end of the post is threaded and incorporates a support collar. In such embodiments, the upper threaded end engages with a complementarily threaded nut featuring a tapered recess defined by the upper surface thereof. This recess receives the lower end of the post, which is tapered to snugly fit within the nut recess. Since in some embodiments a set of posts is only threadingly fastened to one shelf (either the shelf above or below the posts), one or more of the shelves may include one or more (and preferably two or more, e.g., four) “lift hooks” enabling the modularized movement, assembly, or disassembly of the full rack one module (i.e., a shelf with all associated posts) at a time, depending upon the demands of a particular high-temperature process. In various embodiments, the rack may also incorporate one or more support layers on which the various shelves and posts are disposed. The support layer(s) may include or consist essentially of a series of bars or braces that support the weight of the rack while reducing the amount of areal contact between the bottom surface of the rack and the high-temperature furnace (or other processing equipment) compared to an embodiment in which one of the shelves themselves were to rest directly upon the furnace surface.
One or more of the parts of the racks include, consist essentially of, or consist of one or more refractory materials (e.g., refractory metals) having melting points higher than the temperatures utilized for high-temperature brazing processes (e.g., 1000° C.-1100° C.). In various embodiments, one or more of the rack parts include, consist essentially of, or consist of one or more TZM alloys (i.e., alloys of titanium (Ti), zirconium (Zr), and molybdenum (Mo), with optional additions of carbon (C)), as such alloys exhibit superior resistance to creep when supporting heavy loads at extreme temperatures (e.g., 1000° C.-1400° C.) and thus resist deformation (and resulting failure) at such temperatures. In various other embodiments, one or more of the rack parts include, consist essentially of, or consist of one or more refractory metals, e.g., niobium (Nb), tantalum (Ta), rhenium (Re), tungsten (W), and/or Mo. In various embodiments, one or more of the rack parts incorporate one or more alloying elements, for example lanthanum (La), at concentrations of, e.g., approximately 0.01% to approximately 1%.
In various embodiments of the invention, the shelves of the rack are perforated (i.e., a series of apertures is defined therethrough) in order to allow gas to flow through the shelves during processing. Such gases may include, for example, the by-products of out-gassing of the parts or the brazing material during processing, or process gases (e.g., hydrogen and/or another appropriate process gas) utilized to generate a desired processing atmosphere (e.g., a reducing atmosphere), i.e., the processing “ambient.” While racks in accordance with embodiments of the present invention may include any number of shelves, typical implementations include two, three, or even more shelves with the aforementioned threaded posts disposed therebetween and supporting the layered shelves. In various embodiments, the support post upon which the top shelf rests is configured to penetrate through the top shelf. This protruding section of the upper support post may define a lateral aperture through which a locking pin may be disposed to lock the upper shelf in place. In various embodiments, the locking pin is held in place by one or more retaining wires. Alternatively, a threaded cap or nut may also be used to lock the upper shelf in place.
In an aspect, embodiments of the invention feature an apparatus for receiving and supporting one or more components during processing thereof at a process temperature greater than approximately 1000° C. The apparatus includes or consists essentially of a first shelf, a plurality of first support posts, and a second shelf. The first shelf includes, consists essentially of, or consists of a first refractory metal having a melting point greater than the process temperature. The first shelf defines therein or therethrough a plurality of apertures, each aperture being threaded through at least a portion of its thickness. One or more of the first support posts includes, consists essentially of, or consists of a second refractory metal having a melting point greater than the process temperature. One or more of the first support posts has a threaded lower end for engagement with a threaded aperture of the first shelf. One or more of the first support posts defines a support collar proximate an upper end opposite the threaded lower end. A lateral dimension (e.g., a width or diameter) of the first support post above the support collar is smaller than a lateral dimension (e.g., a width or diameter) of the first support post below the support collar. The second shelf includes, consists essentially of, or consists of a third refractory metal having a melting point greater than the process temperature. The second shelf defines therein or therethrough a plurality of apertures. One or more apertures of the second shelf receives and/or is configured to receive the upper end of one of the lower support posts such that a portion of the second shelf proximate each aperture thereof rests upon the support collar of the first support post received in the aperture.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. One or more of the components may be a metallic part. The apparatus may resist creep deformation at the process temperature. The first, second, and/or third refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The first, second, and/or third refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first shelf and/or the second shelf may define a plurality of perforations therethrough. The threaded lower end of each of the first support posts may include a support shoulder defined therein. The apparatus may include a third shelf and a plurality of second support posts. The third shelf may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. The third shelf may define therein or therethrough a plurality of apertures. One or more of the second support posts may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. One or more of the second support posts may have a threaded lower end for engagement with a threaded aperture. One or more of the second support posts may define a support collar proximate an upper end opposite the threaded lower end. A lateral dimension (e.g., a width or diameter) of the second support post above the support collar may be smaller than a lateral dimension (e.g., a width or diameter) of the second support post below the support collar. One or more of the second support posts may define a dowel pin mount through the upper end thereof above the support collar. The upper end of one or more of the second support posts is receivable and/or received within an aperture of the third shelf such that (i) a portion of the third shelf proximate each aperture thereof rests upon the support collar of the second support post received in the aperture, and (ii) the dowel pin mount of the second support post is disposed above a top surface of the third shelf. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo.
The threaded lower end of one or more of the second support posts may include a support shoulder defined therein. The third shelf may define a plurality of perforations therethrough. The apparatus may include a plurality of locking pins. One or more of the locking pins may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. One or more of the locking pins may be receivable and/or received within a dowel pin mount of a second support post, thereby preventing disengagement of the second support posts from the third shelf. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. One or more of the locking pins may define one or more apertures therethrough.
The apparatus may include a plurality of retaining wires. One or more of the retaining wires may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. One or more of the retaining wires may be receivable and/or received within an aperture of a locking pin, thereby preventing disengagement of the locking pin from the second support post in which it is received or receivable. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys). The threaded lower end of each second support post may be engaged with and/or receivable within a threaded aperture in the second shelf. The apparatus may include one or more additional shelves disposed between the second shelf and the third shelf. One or more of the additional shelves may define a plurality of perforations therethrough.
The first shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a shelf support disposed below the first shelf. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. The apparatus may include a first support tube. The first support tube may have a lower end for extending through the central aperture of the first shelf. The lower end of the first support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the cross braces of the shelf support. The first support tube may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first support tube may have an upper end opposite the lower end. The upper end of the first support tube may define therein a plurality of notches. The apparatus may include a first support brace including or consisting essentially of a plurality of appendages for supporting the second shelf thereon. One or more of the appendages may be configured for receipt into one of the notches of the upper end of the first support tube. The appendages of the support brace may define a cross shape. The second shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a second support tube. The second support tube may have a lower end for extending through the central aperture of the second shelf. The lower end of the second support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the appendages of the support brace. The second support tube may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The second support tube may have an upper end opposite the lower end. The upper end of the second support tube may define therein a plurality of notches. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a base disposed beneath the shelf support. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features.
The apparatus may include a base disposed beneath the first shelf. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. One or more of the cross bars may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. One or more of the through rods may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a shelf support disposed below the first shelf and/or disposed above the base. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces metals may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo.
In another aspect, embodiments of the invention feature a method of high-temperature brazing at a process temperature greater than approximately 1000° C. An apparatus is disposed within a furnace chamber. The apparatus includes or consists essentially of a first shelf, a plurality of first support posts, and a second shelf. The first shelf includes, consists essentially of, or consists of a first refractory metal having a melting point greater than the process temperature. The first shelf defines therein or therethrough a plurality of apertures, each aperture being threaded through at least a portion of its thickness. One or more of the first support posts includes, consists essentially of, or consists of a second refractory metal having a melting point greater than the process temperature. One or more of the first support posts has a threaded lower end for engagement with a threaded aperture of the first shelf. One or more of the first support posts defines a support collar proximate an upper end opposite the threaded lower end. A lateral dimension (e.g., a width or diameter) of the first support post above the support collar is smaller than a lateral dimension (e.g., a width or diameter) of the first support post below the support collar. The second shelf includes, consists essentially of, or consists of a third refractory metal having a melting point greater than the process temperature. The second shelf defines therein or therethrough a plurality of apertures. One or more apertures of the second shelf receives and/or is configured to receive the upper end of one of the lower support posts such that a portion of the second shelf proximate each aperture thereof rests upon the support collar of the first support post received in the aperture. On the first shelf and/or the second shelf of the apparatus are disposed (i) a first component, (ii) a second component, and (iii) a brazing material disposed between the first and second components. The brazing material may be in direct contact with the first and second components. A processing ambient is introduced within the furnace chamber. The process temperature is applied within the furnace chamber, thereby melting the brazing material and joining the first and second components at a brazed joint therebetween.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. The first and/or second components may include, consist essentially of, or consist of a metallic part. The apparatus may resist creep deformation at the process temperature. Introducing the processing ambient may include or consist essentially of at least partially evacuating the furnace chamber (i.e., introducing a vacuum therein). Introducing the processing ambient may include or consist essentially of introducing a process gas within the furnace chamber. The process gas may include, consist essentially of, or consist of hydrogen.
The first, second, and/or third refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The first, second, and/or third refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first shelf and/or the second shelf may define a plurality of perforations therethrough. The threaded lower end of each of the first support posts may include a support shoulder defined therein. The apparatus may include a third shelf and a plurality of second support posts. The third shelf may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. The third shelf may define therein or therethrough a plurality of apertures. One or more of the second support posts may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. One or more of the second support posts may have a threaded lower end for engagement with a threaded aperture. One or more of the second support posts may define a support collar proximate an upper end opposite the threaded lower end. A lateral dimension (e.g., a width or diameter) of the second support post above the support collar may be smaller than a lateral dimension (e.g., a width or diameter) of the second support post below the support collar. One or more of the second support posts may define a dowel pin mount through the upper end thereof above the support collar. The upper end of one or more of the second support posts is receivable and/or received within an aperture of the third shelf such that (i) a portion of the third shelf proximate each aperture thereof rests upon the support collar of the second support post received in the aperture, and (ii) the dowel pin mount of the second support post is disposed above a top surface of the third shelf. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo.
The threaded lower end of one or more of the second support posts may include a support shoulder defined therein. The third shelf may define a plurality of perforations therethrough. The apparatus may include a plurality of locking pins. One or more of the locking pins may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. One or more of the locking pins may be receivable and/or received within a dowel pin mount of a second support post, thereby preventing disengagement of the second support posts from the third shelf. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. One or more of the locking pins may define one or more apertures therethrough.
The apparatus may include a plurality of retaining wires. One or more of the retaining wires may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. One or more of the retaining wires may be receivable and/or received within an aperture of a locking pin, thereby preventing disengagement of the locking pin from the second support post in which it is received or receivable. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys). The threaded lower end of each second support post may be engaged with and/or receivable within a threaded aperture in the second shelf. The apparatus may include one or more additional shelves disposed between the second shelf and the third shelf. One or more of the additional shelves may define a plurality of perforations therethrough.
The first shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a shelf support disposed below the first shelf. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. The apparatus may include a first support tube. The first support tube may have a lower end for extending through the central aperture of the first shelf. The lower end of the first support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the cross braces of the shelf support. The first support tube may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first support tube may have an upper end opposite the lower end. The upper end of the first support tube may define therein a plurality of notches. The apparatus may include a first support brace including or consisting essentially of a plurality of appendages for supporting the second shelf thereon. One or more of the appendages may be configured for receipt into one of the notches of the upper end of the first support tube. The appendages of the support brace may define a cross shape. The second shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a second support tube. The second support tube may have a lower end for extending through the central aperture of the second shelf. The lower end of the second support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the appendages of the support brace. The second support tube may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The second support tube may have an upper end opposite the lower end. The upper end of the second support tube may define therein a plurality of notches. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a base disposed beneath the shelf support. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features.
The apparatus may include a base disposed beneath the first shelf. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. One or more of the cross bars may include, consist essentially of, or consist of a fourth refractory metal having a melting point greater than the process temperature. One or more of the through rods may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fourth and/or fifth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a shelf support disposed below the first shelf and/or disposed above the base. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces metals may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features. The sixth refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The sixth refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo.
In yet another aspect, embodiments of the invention feature an apparatus for receiving and supporting one or more components during processing thereof at a process temperature greater than approximately 1000° C. The apparatus includes or consists essentially of a first shelf, a second shelf disposed over the first shelf, a plurality of first support posts, and a plurality of first nuts. The first shelf includes, consists essentially of, or consists of a first refractory metal having a melting point greater than the process temperature. The first shelf defines therein or therethrough a plurality of apertures. The second shelf includes, consists essentially of, or consists of a second refractory metal having a melting point greater than the process temperature. The second shelf defines therein or therethrough a plurality of apertures. The second shelf includes one or more first lift hooks extending therefrom. The one or more first lift hooks may extend from a top surface and/or a perimeter of the second shelf. The first shelf may include one or more lift hooks extending therefrom. One or more of the first support posts includes, consists essentially of, or consists of a third refractory metal having a melting point greater than the process temperature. One or more of the first support posts has a tapered lower end for engagement with an aperture of the first shelf. One or more of the first support posts has a threaded upper end opposite the lower end. One or more of the first support posts defines a support collar proximate the upper end. A lateral dimension (e.g., a width or diameter) of the first support post above the support collar is smaller than a lateral dimension (e.g., a width or diameter) of the first support post below the support collar. When an upper end of a first support post is received in an aperture of the second shelf, a portion of the second shelf proximate the aperture rests upon the support collar of the first support post received in the aperture. When an upper end of a first support post is received in an aperture of the second shelf, at least a portion of the upper end of the first support post may extend above a top surface of the second shelf. One or more of the first nuts includes, consists essentially of, or consists of a fourth refractory metal having a melting point greater than the process temperature. One or more of the first nuts defines therein a lower aperture. At least a portion of the lower aperture may be threaded for engagement with an upper end of a first support post. One or more of the first nuts defines therein an upper aperture. At least a portion of the upper aperture may be tapered. The lower aperture and the upper aperture of at least one of the first nuts may be connected to form an aperture extending through an entire thickness thereof. The lower aperture and the upper aperture of at least one of the first nuts may be isolated from each other (i.e., separated from each other by a portion of the first nut therebetween). The second shelf, the first support posts, and the first nuts may be collectively separable, as a modular unit, from the first shelf via a lifting force applied via the one or more first lift hooks.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. One or more of the components may be a metallic part. The apparatus may resist creep deformation at the process temperature. The first, second, third, and/or fourth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The first, second, third, and/or fourth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first shelf and/or the second shelf may define a plurality of perforations therethrough.
The apparatus may include a third shelf disposed over the second shelf, a plurality of second support posts, and a plurality of second nuts. The third shelf may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The third shelf may define therethrough a plurality of apertures. The third shelf may include one or more second lift hooks extending therefrom. The one or more second lift hooks may extend from a top surface and/or a perimeter of the third shelf. The third shelf may define a plurality of perforations therethrough. One or more of the second support posts may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. One or more of the second support posts may have a tapered lower end for engagement with an upper aperture of a first nut. One or more of the second support posts may have a threaded upper end opposite the tapered lower end. One or more of the second support posts may define a support collar proximate the upper end. A lateral dimension (e.g., a width or diameter) of the second support post above the support collar being smaller than a lateral dimension (e.g., a width or diameter) of the second support post below the support collar. When an upper end of a second support post is received in an aperture of the third shelf, a portion of the third shelf proximate the aperture may rest upon the support collar of the second support post received in the aperture. When an upper end of a second support post is received in an aperture of the third shelf, at least a portion of the upper end of the second support post may extend above a top surface of the third shelf. One or more of the second nuts may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. One or more of the second nuts may define therein a lower aperture. At least a portion of the lower aperture may be threaded for engagement with an upper end of a second support post. The third shelf, the second support posts, and the second nuts may be collectively separable, as a modular unit, from the second shelf and the first shelf via a lifting force applied via the one or more second lift hooks. One or more of the second nuts may define therein an upper aperture. At least a portion of the upper aperture may be tapered. The lower aperture and the upper aperture of at least one of the second nuts may be connected to form an aperture extending through an entire thickness thereof. The lower aperture and the upper aperture of at least one of the second nuts may be isolated from each other (i.e., separated from each other by a portion of the second nut therebetween). The fifth, sixth, and/or seventh refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth, sixth, and/or seventh refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys).
The first shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a shelf support disposed below the first shelf. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The apparatus may include a first support tube. The first support tube may have a lower end for extending through the central aperture of the first shelf. The lower end of the first support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the cross braces of the shelf support. The first support tube may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first support tube may have an upper end opposite the lower end. The upper end of the first support tube may define therein a plurality of notches. The apparatus may include a first support brace including or consisting essentially of a plurality of appendages for supporting the second shelf thereon. One or more of the appendages may be configured for receipt into one of the notches of the upper end of the first support tube. The appendages of the support brace may define a cross shape. The second shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a second support tube. The second support tube may have a lower end for extending through the central aperture of the second shelf. The lower end of the second support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the appendages of the support brace. The second support tube may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. The second support tube may have an upper end opposite the lower end. The upper end of the second support tube may define therein a plurality of notches. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys). The apparatus may include a base disposed beneath the shelf support. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features.
The apparatus may include a base disposed beneath the first shelf. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. One or more of the cross bars may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. One or more of the through rods may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a shelf support disposed below the first shelf and/or disposed above the base. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces metals may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys).
In another aspect, embodiments of the invention feature a method of high-temperature brazing at a process temperature greater than approximately 1000° C. An apparatus is disposed within a furnace chamber. The apparatus includes or consists essentially of a first shelf, a second shelf disposed over the first shelf, a plurality of first support posts, and a plurality of first nuts. The first shelf includes, consists essentially of, or consists of a first refractory metal having a melting point greater than the process temperature. The first shelf defines therein or therethrough a plurality of apertures. The second shelf includes, consists essentially of, or consists of a second refractory metal having a melting point greater than the process temperature. The second shelf defines therein or therethrough a plurality of apertures. The second shelf includes one or more first lift hooks extending therefrom. The one or more first lift hooks may extend from a top surface and/or a perimeter of the second shelf. The first shelf may include one or more lift hooks extending therefrom. One or more of the first support posts includes, consists essentially of, or consists of a third refractory metal having a melting point greater than the process temperature. One or more of the first support posts has a tapered lower end for engagement with an aperture of the first shelf. One or more of the first support posts has a threaded upper end opposite the lower end. One or more of the first support posts defines a support collar proximate the upper end. A lateral dimension (e.g., a width or diameter) of the first support post above the support collar is smaller than a lateral dimension (e.g., a width or diameter) of the first support post below the support collar. When an upper end of a first support post is received in an aperture of the second shelf, a portion of the second shelf proximate the aperture rests upon the support collar of the first support post received in the aperture. When an upper end of a first support post is received in an aperture of the second shelf, at least a portion of the upper end of the first support post may extend above a top surface of the second shelf. One or more of the first nuts includes, consists essentially of, or consists of a fourth refractory metal having a melting point greater than the process temperature. One or more of the first nuts defines therein a lower aperture. At least a portion of the lower aperture may be threaded for engagement with an upper end of a first support post. One or more of the first nuts defines therein an upper aperture. At least a portion of the upper aperture may be tapered. The lower aperture and the upper aperture of at least one of the first nuts may be connected to form an aperture extending through an entire thickness thereof. The lower aperture and the upper aperture of at least one of the first nuts may be isolated from each other (i.e., separated from each other by a portion of the first nut therebetween). The second shelf, the first support posts, and the first nuts may be collectively separable, as a modular unit, from the first shelf via a lifting force applied via the one or more first lift hooks. On the first shelf and/or the second shelf of the apparatus are disposed (i) a first component, (ii) a second component, and (iii) a brazing material disposed between the first and second components. The brazing material may be in direct contact with the first and second components. A processing ambient is introduced within the furnace chamber. The process temperature is applied within the furnace chamber, thereby melting the brazing material and joining the first and second components at a brazed joint therebetween.
Embodiments of the invention may include one or more of the following in any of a variety of combinations. The first and/or second components may include, consist essentially of, or consist of a metallic part. The apparatus may resist creep deformation at the process temperature. Introducing the processing ambient may include or consist essentially of at least partially evacuating the furnace chamber (i.e., introducing a vacuum therein). Introducing the processing ambient may include or consist essentially of introducing a process gas within the furnace chamber. The process gas may include, consist essentially of, or consist of hydrogen.
The first, second, third, and/or fourth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The first, second, third, and/or fourth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first shelf and/or the second shelf may define a plurality of perforations therethrough.
The apparatus may include a third shelf disposed over the second shelf, a plurality of second support posts, and a plurality of second nuts. The third shelf may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The third shelf may define therethrough a plurality of apertures. The third shelf may include one or more second lift hooks extending therefrom. The one or more second lift hooks may extend from a top surface and/or a perimeter of the third shelf. The third shelf may define a plurality of perforations therethrough. One or more of the second support posts may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. One or more of the second support posts may have a tapered lower end for engagement with an upper aperture of a first nut. One or more of the second support posts may have a threaded upper end opposite the tapered lower end. One or more of the second support posts may define a support collar proximate the upper end. A lateral dimension (e.g., a width or diameter) of the second support post above the support collar being smaller than a lateral dimension (e.g., a width or diameter) of the second support post below the support collar. When an upper end of a second support post is received in an aperture of the third shelf, a portion of the third shelf proximate the aperture may rest upon the support collar of the second support post received in the aperture. When an upper end of a second support post is received in an aperture of the third shelf, at least a portion of the upper end of the second support post may extend above a top surface of the third shelf. One or more of the second nuts may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. One or more of the second nuts may define therein a lower aperture. At least a portion of the lower aperture may be threaded for engagement with an upper end of a second support post. The third shelf, the second support posts, and the second nuts may be collectively separable, as a modular unit, from the second shelf and the first shelf via a lifting force applied via the one or more second lift hooks. One or more of the second nuts may define therein an upper aperture. At least a portion of the upper aperture may be tapered. The lower aperture and the upper aperture of at least one of the second nuts may be connected to form an aperture extending through an entire thickness thereof. The lower aperture and the upper aperture of at least one of the second nuts may be isolated from each other (i.e., separated from each other by a portion of the second nut therebetween). The fifth, sixth, and/or seventh refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth, sixth, and/or seventh refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys).
The first shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a shelf support disposed below the first shelf. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. The apparatus may include a first support tube. The first support tube may have a lower end for extending through the central aperture of the first shelf. The lower end of the first support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the cross braces of the shelf support. The first support tube may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The first support tube may have an upper end opposite the lower end. The upper end of the first support tube may define therein a plurality of notches. The apparatus may include a first support brace including or consisting essentially of a plurality of appendages for supporting the second shelf thereon. One or more of the appendages may be configured for receipt into one of the notches of the upper end of the first support tube. The appendages of the support brace may define a cross shape. The second shelf may define a central aperture therethrough. The central aperture may have the shape of a square, rectangle, or circle. The apparatus may include a second support tube. The second support tube may have a lower end for extending through the central aperture of the second shelf. The lower end of the second support tube may define a plurality of notches. One or more of the notches may be configured to receive therein one of the appendages of the support brace. The second support tube may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. The second support tube may have an upper end opposite the lower end. The upper end of the second support tube may define therein a plurality of notches. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys). The apparatus may include a base disposed beneath the shelf support. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features.
The apparatus may include a base disposed beneath the first shelf. The base may include or consist essentially of (i) a plurality of spaced-apart cross bars each defining a plurality of apertures therethrough, and (ii) a plurality of spaced-apart through rods each extending through the apertures of multiple ones of the cross bars. One or more of the cross bars may include, consist essentially of, or consist of a fifth refractory metal having a melting point greater than the process temperature. One or more of the through rods may include, consist essentially of, or consist of a sixth refractory metal having a melting point greater than the process temperature. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The fifth and/or sixth refractory metals may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. The apparatus may include a shelf support disposed below the first shelf and/or disposed above the base. The shelf support may include or consist essentially of a plurality of interconnected cross braces. One or more of the cross braces metals may include, consist essentially of, or consist of a seventh refractory metal having a melting point greater than the process temperature. The base may include one or more alignment features (e.g., posts, brackets, plates, etc.) extending upward therefrom. The shelf support may include one or more brackets each for receiving one of the one or more alignment features. The seventh refractory metal may include, consist essentially of, or consist of a TZM alloy. The TZM alloy may include, consist essentially of, or consist of approximately 0.40-approximately 0.55 weight percent Ti, approximately 0.06-approximately 0.12 weight percent Zr, and the balance Mo. The TZM alloy may include, consist essentially of, or consist of approximately 0.50 weight percent Ti, approximately 0.08 weight percent Zr, and the balance Mo. The seventh refractory metal may include, consist essentially of, or consist of Nb, Ta, Re, W, and/or Mo. Two or more (in any combination), or even all, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of the same material (e.g., metal or metal alloy). Two or more (in any combination), or even each, of the first, second, third, fourth, fifth, sixth, and seventh refractory metals may include, consist essentially of, or consist of different materials (e.g., metals or metal alloys).
These and other objects, along with advantages and features of the present invention herein disclosed, will become more apparent through reference to the following description, the accompanying drawings, and the claims. Furthermore, it is to be understood that the features of the various embodiments described herein are not mutually exclusive and may exist in various combinations and permutations. As used herein, the terms “approximately” and “substantially” mean±10%, and in some embodiments, ±5%. The term “consists essentially of” means excluding other materials that contribute to function, unless otherwise defined herein. Nonetheless, such other materials may be present, collectively or individually, in trace amounts. For example, a structure consisting essentially of multiple metals will generally include only those metals and only unintentional impurities (which may be metallic or non-metallic) that may be detectable via chemical analysis but do not contribute to function. As used herein, “consisting essentially of at least one metal” refers to a metal or a mixture of two or more metals but not compounds between a metal and a non-metallic element or chemical species such as oxygen, silicon, or nitrogen (e.g., metal nitrides, metal silicides, or metal oxides); such non-metallic elements or chemical species may be present, collectively or individually, in trace amounts, e.g., as impurities. Herein, in a part “defining an aperture therethrough,” the aperture extends through the thickness of the part unless otherwise indicated; in a part “defining an aperture therein,” the aperture may extend through only a portion of the thickness of the part, or the aperture may extend through the entire thickness.
In the drawings, like reference characters generally refer to the same parts throughout the different views. Also, the drawings are not necessarily to scale, emphasis instead generally being placed upon illustrating the principles of the invention. In the following description, various embodiments of the present invention are described with reference to the following drawings, in which:
While the rack 100 is depicted in
In order to maintain a consistent spacing between various ones of the cross bars 1100, a series of hollow spacers 1120 may be disposed between the cross bars 1100, and the through rods 1105 may extend through the spacers 1120. The spacers 1120 may have diameters (or other lateral dimensions) larger than those of the apertures defined by cross bars 1100 through which the through rods 1105 extend, thereby preventing movement of the spacers 1120 through the apertures and alteration of spacings between various cross bars 1100. As shown in
In various embodiments, one or more of the components of base 900 (e.g., cross bars 1100, through rods 1105, spacers 1120, nuts 1125, washers 1130, alignment brackets 1135, and/or rivets 1140) include, consist essentially of, or consist of one or more TZM alloys. In other embodiments, one or more of the components of base 900 include, consist essentially of, or consist of one or more refractory metals, e.g., Nb, Ta, Re, W, and/or Mo. In various embodiments, one or more of the components of base 900 incorporate one or more alloying elements, for example La, at concentrations of, e.g., approximately 0.01% to approximately 1%.
As mentioned above, a shelf support 1000 may be disposed between base 900 and shelf 110. The shelf support 1000 may, for example, provide additional support to shelf 110 and all of the other parts of the apparatus thereover. The shelf support 1000 may even provide additional space between base 900 and shelf 110 for the flow of process gas through the apparatus.
In various embodiments, one or more of the components of shelf support 1000 (e.g., shelf ring 1200, cross braces 1205, joining strips 1210, rivets 1215, brackets 1220, rivets 1225, retaining wires 1230, studs 1235, and/or nuts 1240) include, consist essentially of, or consist of one or more TZM alloys. In other embodiments, one or more of the components of shelf support 1000 include, consist essentially of, or consist of one or more refractory metals, e.g., Nb, Ta, Re, W, and/or Mo. In various embodiments, one or more of the components of shelf support 1000 incorporate one or more alloying elements, for example La, at concentrations of, e.g., approximately 0.01% to approximately 1%.
In various embodiments, one or more of the components of rack 1300 (e.g., shelves 105, 110, base 900, shelf support 1000, rods 1305, support tubes 1310, 1315, support brackets 1320, lift hooks 1325, nuts 1340, and/or rivets 1375, 1395, 1399) include, consist essentially of, or consist of one or more TZM alloys. In other embodiments, one or more of the components of rack 1300 include, consist essentially of, or consist of one or more refractory metals, e.g., Nb, Ta, Re, W, and/or Mo. In various embodiments, one or more of the components of rack 1300 incorporate one or more alloying elements, for example La, at concentrations of, e.g., approximately 0.01% to approximately 1%.
As mentioned above, racks 100, 1300 in accordance with embodiments of the present invention may be utilized to receive and support parts (or “components”) during high-temperature processes such as brazing. For example, multiple heavy metallic parts may be placed on each shelf 105, 110 with a brazing material placed at locations between the parts where brazed joints are desired. For example, a first component including, consisting essentially of, or consisting of steel (e.g., stainless steel) may be joined to a second component including, consisting essentially of, or consisting of Ti with a brazing material including, consisting essentially of, or consisting of, for example, silver or an alloy of nickel and chromium. The rack 100, 1300 may be disposed within a furnace chamber configured to heat the parts and the rack 100, 1300 to elevated processing temperatures of greater than 1000° C., e.g., between approximately 1100° C. and approximately 1500° C. or even approximately 2000° C. with appropriate refractory metal selection. The furnace chamber may be sealable to enable the evacuation thereof for processing parts under vacuum (for example, to prevent exposure to oxygen at high temperatures and resulting deleterious oxidation) or for the introduction of one or more process gases, e.g., hydrogen gas if a reducing atmosphere is desired. The parts are heated within the furnace chamber at the desired processing temperature and under the desired ambient conditions until the brazing material melts and forms the brazed joint(s) between the parts. The parts may then be cooled down and removed from the rack 100, 1300 and the furnace chamber for further processing. The design features of rack 100, 1300 described herein advantageously enable the high-temperature batch processing of multiple joined parts and repeated use without deformation or failure of rack 100, 1300.
Thus, as shown in
The terms and expressions employed herein are used as terms and expressions of description and not of limitation, and there is no intention, in the use of such terms and expressions, of excluding any equivalents of the features shown and described or portions thereof. In addition, having described certain embodiments of the invention, it will be apparent to those of ordinary skill in the art that other embodiments incorporating the concepts disclosed herein may be used without departing from the spirit and scope of the invention. Accordingly, the described embodiments are to be considered in all respects as only illustrative and not restrictive.
This application claims the benefit of and priority to U.S. Provisional Patent Application No. 62/117,192, filed Feb. 17, 2015, the entire disclosure of which is hereby incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62117192 | Feb 2015 | US |