Patent Application
20080121225
The invention described and claimed herein below is also described in German Patent Application 10 2006 056 536.3 filed Nov. 27, 2006 in Germany, which provides the basis for a claim of priority under 35 U.S.C. 119 (a)-(d).
1. The Field of the Invention
The present invention relates to a radiation selective absorber coating, especially for an absorber pipe of a parabolic trough collector, with an infrared-range reflective layer, an absorption layer arranged over the infrared-range reflective layer, and an antireflection layer arranged over the absorption layer.
2. The Description of the Related Art
Conventional absorber coatings applied to a substrate, especially a metal pipe, comprise an infrared-range reflective layer, a cermet layer, which provides a high absorptivity in a region of the solar spectrum, and a cover layer applied to the cermet layer, which is called an antireflective layer and is provided on the cermet layer to reduce the surface reflection because of the high refractive index of the cermet layer.
Striving to attain the highest possible energy yield is basic. The energy yield depends, among other things, on the coefficients of the absorptivity α and emissivity ε. A high absorptivity (α>95%) and a low emissivity (ε<10%) of the absorber coating are always the goals of further improvements in the absorber coating.
Furthermore the temperature at which the parabolic trough collector operates determines the efficiency. From this standpoint the highest possible operating temperature is desired. However the service life of the layer system of the absorber coating is reduced at elevated operating temperatures because of aging and/or diffusion processes, whereby for example the absorption properties of the cermet layer and the reflectivity properties of the infrared-range reflective layer can be greatly impaired.
DE 101 50 738 C1 thus describes a radiation selective absorber coating, which exhibits no relevant color changes and thus no aging. This is achieved by providing a certain oxygen volume flow rate during applying of a third layer comprising aluminum and aluminum oxide. A final layer of Al2O3 is applied on this layer.
An absorber coating, in which several cermet layers with different metal content and thus different indices of refraction are included, is disclosed in U.S. Pat. No. 5,523,132. Since they have several different absorption maxima at different wavelengths, an improved fit to the solar spectrum should be achievable. Antidiffusion layers could be provided between the cermet layer and the IR-range reflective layer or between the cermet layer and the antireflection layer. No disclosure was made however regarding material and layer thicknesses.
A special absorber coating is disclosed in “Solar selective absorber coating for high service temperatures, produced by plasma sputtering” by Michael Lanxner and Zvi Elgat, in SPIE, Vol. 1272, Optical Materials Technology for Energy Efficiency and Solar Energy Conversion IX (1990), pp. 240 to 249. The absorber coating is applied to a steel substrate and comprises an antireflection layer made of SiO2, a cermet layer made from an Mo/Al2O3 composition and an infrared-range reflective layer made from molybdenum, in which a diffusion barrier made from Al2O3 is arranged between the infrared-range reflective layer and the substrate.
DE 10 2004 010 689 B3 discloses an absorber component with a radiation selective absorber coating, which comprises a metal substrate, a diffusion barrier, a metallic reflection layer, a cermet layer and an antireflection layer. The diffusion barrier is an oxide layer, which comprises oxide components of the metal substrate.
Molybdenum is usually used for the infrared-range reflective layer. Generally the reflection properties of a molybdenum layer are not optimal so that it is desirable to use better reflecting materials.
The operating temperature of the known absorber pipe is in a range from 300° C. to 400° C. in vacuum. For the previously stated reasons it is desirable to increase the operating temperature however without for example impairing the absorption properties of the cermet layer and the reflection properties of the infrared-range reflective layer.
These endeavors are summarized in C. E. Kennedy, “Review of Mid- to High-Temperature Solar Selective Absorber Materials”, a Technical Report of the National Renewable Energy Laboratory, Report, of July 2002. From that a layer structure comprising an absorption layer composed of ZrOxNy or ZrCxNy and an IR-range reflective layer made from Ag or Al, is known, which has improved temperature stability in air because of the introduction of an Al2O3-diffusion barrier. Furthermore it was established that the temperature stability of the IR-range reflective layer in vacuum is improved by the insertion of the diffusion barrier under this layer. The suggested layer materials for the diffusion barrier are Cr2O3, Al2O3, or SiO2. Because of this diffusion barrier the temperature at which the silver reflective layer is stable was increased to 500° C.
However the possibilities for further improvements in both absorption and emission properties for stable coating layers have not been exhausted.
It is the object of the present invention to provide a radiation selective absorber coating, absorber pipes with this sort of radiation selective absorber coating and parabolic trough collectors, in which absorber pipes with this sort of absorber coating are used, which are operated economically with a long-lasting service life.
This object and others, which will be made more apparent hereinafter, are attained when the infrared-range reflective layer is arranged on at least two barrier layers.
It has been surprisingly shown that the shielding of the IR-range reflective layer from the substrate by a two-layer barrier effectively prevents the thermally dependent diffusion of the substrate material, especially of iron from steel absorber pipes, into the IR-range reflective layer and thus increases the long-time temperature stability of the coating.
This is especially successful when the two-layer barrier comprises a first barrier layer made by thermal oxidation advantageously of the substrate and a second barrier layer comprising AlxOy compounds. The preferred AlxOy compounds are AlO, AlO2, and Al2O3. Al2O3 is particularly preferred.
In a preferred embodiment an additional barrier layer is arranged between an absorption layer comprising a cermet material and an IR-range reflective layer, which are applied over the two-layer barrier. The additional barrier layer preferably comprises another AlxOy layer, in which x=1 or 2 and y=1, 2, or 3.
The embedding of the infrared-range reflective layer between two aluminum oxide layers and the formation of a sandwich structure in connection with it has the advantage that no material from the infrared-range reflective layer can diffuse into the absorption layer above it and in this way impair the absorption properties of the absorption layer. The comprehensive prevention of diffusion within the layer system, especially in or from the infrared-range reflective layer and in the cermet absorption layer can thus be guaranteed.
For the first time in this way a high absorption with α>95.5% and a low emissivity with ε<9% is obtained for an operating time of 250 hours at an operating temperature of 550° C. in vacuum. Because of that the efficiency of a collector with an absorber pipe provided with this coating may be improved in a two-fold manner: the improved selectivity ratio α/ε>0.95/0.1 means a higher yield for the radiation energy and an increased operating temperature permits an efficient conversion into electrical energy. The long service life of this sort of coating guarantees the efficient operation of an appropriate parabolic trough collector with this sort of absorber pipe coating.
The high temperature resistance of the absorber coating permits the use of an economical heat-carrying medium. Up until the present invention expensive special oils were used as heat-carrying media, which are only stable up to about 400° C. The high temperature stability of the absorber coating now allows operating temperatures for the absorber pipe of >450° C. to 550° C.
In preferred embodiments a heat-carrying medium can be used with a boiling point <110° C. Water is particularly preferred as the heat-carrying medium. The steam, which arises at the high operating temperatures, can be directly conducted into a steam turbine. Additional heat exchangers for heat transfer from the oils previously used as heat-carrying media to water are no longer required so that from this standpoint a parabolic trough collector with an absorber pipe with the absorber coating according to the invention can be operated more economically than the current parabolic trough collectors.
An additional advantage is that the flow rate of the heat-carrying medium through the absorber pipe can be lowered, since a higher operating temperature is permissible for the absorber pipe coating without any disadvantages. In this way some of the energy used for operation of the pumps of a parabolic trough collector can be saved.
Preferably the thickness of the aluminum oxide layers is between 20 and 100 nm. At thicknesses of less than 20 nm the barrier action of the aluminum oxide layer is no longer satisfactory according to the composition of the adjacent layer. At thicknesses of more than 100 nm thermal stresses occur, which could lead under certain circumstances to loosening of the layer.
The thicknesses of both aluminum oxide layers can be different. The thickness of the lower aluminum oxide layer is preferably greater than the thickness of the upper aluminum oxide layer. Preferably the layer thickness of the aluminum oxide layer, which is arranged between the substrate and the IR-range reflective layer, is from 20 to 100 nm, preferably 50 to 70 nm. The layer thickness of the aluminum oxide layer, which is arranged between the IR-range reflective layer and the absorption layer, is preferably 0 nm to 50 nm, and preferably from 30 nm to 40 nm or also from 5 nm to 15 nm according to the composition of the layers.
The embedding of the IR-range reflective layer between the two aluminum oxide layers has the additional advantage that materials, such as silver, copper, platinum or gold, can be used for this layer, which has the advantage of course that diffusion of molybdenum is reduced but also the decisive advantage that reflectivity in the IR-range is clearly improved so that an emissivity ε<10% is attainable.
The thickness of the infrared-range reflective coating is from 50 nm to 150 nm according to the type of the material used. A layer thickness of 100 nm to 120 nm is preferred when copper or silver is used. A layer thickness in a range of from 90 nm to 130 nm is preferred when using silver. In other cases the layer thickness of 50 to 100 nm, especially of 50 to 80 nm, is preferred.
These lower layer thicknesses of the infrared-range reflective layer are thus allowed because the materials of the layer, namely gold, silver, platinum and copper, have a clearly higher reflectivity, cannot diffuse across the layer into other layers because the layer is packed between two aluminum oxide layers and other interfering elements do not impair their positive properties by diffusion.
The high prices of the noble metals, Au, Ag and Pt, can be compensated by the clearly lower layer thickness in comparison to known layer thicknesses for the infrared-range reflecting layer, partially even over-compensated.
The thickness of the absorption layer is preferably from 60 to 140 nm. The absorption layer is preferably a cermet layer of aluminum oxide with molybdenum or zirconium oxide with molybdenum. Instead of a uniform absorption layer several absorption layers of different composition can be provided, especially with decreasing metal content, or a gradually changing absorption layer. Preferably the cermet layer is a gradient layer, which means a layer in which the metal content within the layer increases or decreases continuously, but in practice also stepwise.
The layer thickness of the antireflection layer arranged on the absorption layer is preferably from 60 to 120 nm. This layer preferably comprises silicon oxide or aluminum oxide.
An absorber pipe according to the invention, especially for a parabolic trough collection, comprises a steel pipe, on whose outer side at least an IR-range reflective layer, an absorption layer, especially made of cermet material, and an antireflective layer, which is applied to the cermet layer, is characterized in that the infrared-range reflective layer is arranged between two AlxOy layers, in which x=1 or 2 and y=1, 2, or 3.
A method according to the invention for operating a parabolic trough collector with an absorber pipe, through which a heat-carrying medium is conducted and which has a radiation selective absorber coating, which comprises at least an infrared-range reflective layer, an absorption layer, especially made of cermet material, and an antireflective layer, in which the infrared-range reflective layer is arranged between two AlxOy layers, in which x=1 or 2 and y=1, 2, or 3, comprises conducting a heat-carrying liquid with a boiling point of less than 110° C. through the absorber pipe.
In a preferred embodiment of this method water is used as the heat-carrying liquid.
According to a preferred embodiment the method of operating the parabolic trough collector is conducted so that the operating temperature of the absorber pipe is set at 450° C. to 550° C., especially to 480° C. to 520° C.
The objects, features and advantages of the invention will now be described in more detail with the aid of the following description of the preferred embodiments, with reference to the accompanying figures in which:
A parabolic trough collector, which has a longitudinally extending parabolic reflector 11 with a parabola-shaped cross-section, is shown in
The absorber coating 20 comprises, from the innermost layer applied to the steel pipe 1 to the outermost, a first barrier or diffusion-blocking layer 24a of iron-chromium oxide produced by thermal oxidation; a second preferably aluminum oxide barrier layer 24b; an infrared-range reflective layer 21 made of gold, silver, platinum, or copper; a third preferably aluminum oxide barrier layer 24c; a cermet layer 22 applied on the third barrier layer; and finally an antireflection layer 23 applied over the cermet layer 22.
The process described herein below produces the absorber pipe with the absorber coating 20 according to the embodiment shown in
The steel pipe 1, preferably a stainless steel pipe, is polished and subsequently cleaned. Preferably it is polished until the surface roughness Ra is less than 0.2 μm. Subsequently the stainless steel pipe is thermally oxidized at a temperature greater than 400° C. for about a half an hour to 2 hours, especially for about an hour at 500° C. An oxide layer with a thickness of from 15 nm to 50 nm, preferably from 30 nm±10 nm, is produced by the thermal oxidation. This oxide layer is the first barrier layer 24a.
Subsequently the steel pipe 1 is placed in a vacuum coating unit and the unit is evacuated. After achieving a pressure of less than 5×10−4 mbar, preferably 1×10−4 mbar, the following layers are applied by means of gas-phase physical deposition (PVD), especially by means of cathodic sputtering. Moreover the rotating steel pipe is guided past the sputtering source, i.e. the target comprising the coating substance, for example Al, Ag, and Mo.
The second barrier coating 24b is applied in the form of an AlxOy layer in a first deposition step, in which the aluminum deposited by evaporation or sputtering is reacted with oxygen. The oxygen pressure during this step is between 10−2 mbar and 10−3 mbar, preferably 4 to 7×10−3 mbar. The preferred layer thickness of this second barrier layer is between 30 nm and 65 nm, and especially 50 nm±10 nm.
The infrared-range reflective layer 21 is applied in a second deposition step, in which gold, silver, platinum, or copper, preferably silver, is deposited with a thickness of 90 nm to 130 nm, preferably of 110 nm±10 nm, on the second barrier layer 24b.
The third barrier layer 24c is applied over the infrared-range reflective layer 21 in a following second deposition step, in which aluminum is evaporated as in the case of the second barrier layer and reacted with oxygen. The preferred coating thickness of this third barrier layer is at most 50 nm, especially preferably 10 nm±5 nm. However this barrier layer can be completely omitted, since it has been shown that with suitable composition the absorption layer 22 applied on the reflective layer 21 must block diffusion, not blocked by the additional barrier layer.
The absorption layer 22, or more precisely the cermet layer, is applied by simultaneous evaporation/sputtering of aluminum and molybdenum from a common crucible or from two separate targets in a fourth deposition step. Preferably oxygen is simultaneously conducted into the evaporation/sputtering region, in order to deposit (reactively) aluminum oxide besides aluminum and molybdenum.
The composition of the layer deposited in the fourth deposition step can be varied even in the course of the coating process so that it is variably adjusted by suitable selection of the operating parameters, such as the evaporation/sputtering rates and the oxygen amount or flow rate. Especially using separate targets the fraction of the molybdenum deposited can be varied in relation to the fraction of the aluminum or the fraction of the aluminum oxide deposited in the absorption layer 22. In other words, a gradient of the molybdenum concentration is produced in the absorption layer 22; preferably the molybdenum fraction is decreased during the formation of the absorption layer 22. Preferably the amount of molybdenum in the absorption layer 22 is from 25 vol. % to 70 vol. %, especially preferably 40±15 vol. %, and decreases toward the outside of the absorber pipe to 10 vol. % to 30 vol. %, especially preferably 20±vol. %.
Oxygen is preferably provided in amounts that are below the stoichiometric amount in relation to the fraction of the aluminum deposited, so that a certain fraction of the aluminum deposited in the absorption layer 22 remains as metallic aluminum, which is not oxidized. This fraction of metallic aluminum is thus available as a potential redox agent or oxygen getter, so that molybdenum oxide is not formed. The not oxidized aluminum fraction should amount to preferably under 10 vol. %, especially preferably between 0 and 5 vol. %, in relation to the total composition of the absorption layer 22. The not oxidized aluminum fraction can similarly be varied within the absorption layer by changing the operating parameters, namely the evaporation rate and the oxygen flow rate.
The absorption coating 22 is applied preferably with a thickness of 70 nm to 140 nm, especially preferably 100±10 nm.
The antireflection layer 23 is applied in the form of an SiO2 layer in a fifth deposition step, in which silicon is deposited in a gas-phase physical deposition while oxygen is supplied. The preferred antireflection layer 23 deposited in this manner has a thickness of 70 nm to 110 nm, especially preferably 90±10 nm.
An absorber pipe produced in this way was heated in a vacuum heating unit at 550° C. for 250 h. The pressure in the vacuum chamber was less than 1×10−4 during this heating process. After cooling the sample to 100° C. the vacuum chamber was aerated and the sample was removed. The sample was subsequently tested spectrophotometrically. It had an integrated solar absorptivity of 95.5±0.5% for a solar spectrum 1.5 AM direct and a wavelength range of 350 to 2500 nm. The thermal emissivity was 8%±2% for a substrate temperature of 400° C. The thermal emissivity calculated from the spectral measurement was subsequently tested by a heat loss measurement, in which the coated absorber pipe was equipped with an evacuated tubular jacket and heated from the inside. The calculated emissivity could be reported with a precision of ±1% by the heat loss measurement.
While the invention has been illustrated and described as embodied in a radiation selective absorber coating for an absorber pipe, absorber pipe with said coating, and method of making same, it is not intended to be limited to the details shown, since various modifications and changes may be made without departing in any way from the spirit of the present invention.
Without further analysis, the foregoing will so fully reveal the gist of the present invention that others can, by applying current knowledge, readily adapt it for various applications without omitting features that, from the standpoint of prior art, fairly constitute essential characteristics of the generic or specific aspects of this invention.
What is claimed is new and is set forth in the following appended claims.