Patent Application
20190202954
Photo-polymerization is a process in which a monomer is converted to a polymer; the process is initiated by the absorption of visible or ultraviolet light. The light may be absorbed either directly by the reactant monomer (direct photo-polymerization) or by a photosensitizer that absorbs the light and then transfers energy to the monomer. The monomers then form a long chain or crosslinked network.
Some current dental restorative compositions rely on photo-copolymerization of resin monomers to form a stable, solid mass in an oral environment. However, to be practically useful, the polymerization must occur in a relatively short time frame. This need for rapid polymerization precludes the use of many materials and compositions that could perform well in an oral environment. As an example, styrene derivatives may perform satisfactorily in an oral environment, but current styrene derivative compositions require many tens of minutes or hours to polymerize, making such compositions unsuitable for dental restorative applications. Furthermore, current methacrylate derivative-based compositions, and their accompanying use instructions, may not produce satisfactory durability and esthetics over time. In addition to a short average service life, these compositions are subject to leaching of unreacted monomers and system degradation by hydrolysis of acids, bases, or enzymes.
In addition, although the polymerization rate of styrene may be improved through copolymerization with methacrylate monomers, the resulting composition may experience a significant composition shift as the conversion of monomers increases. Vinyl ether resins (VER), as an example, are copolymers of styrene and dimethacrylate monomers. At a high monomer conversion, more styrene is converted into polymer due to diffusion limitations. That is, the dimethacrylate monomers are more viscous than styrene, and thus diffuse more slowly than styrene to reach radicals as the polymerization progresses. This diffusion limitation becomes more obvious for VERs when styrene derivatives have two double bonds on a single monomer. The composition shift of copolymers at different monomer conversions may generate inconsistent physical and mechanical properties in the resulting polymers.
Disclosed are compositions for enzymatically and hydrolytically stable dental applications, and methods for producing such compositions that can yield highly cross-linked, strong and durable polymers that form rapidly when exposed to light. The compositions may be used in restorative dentistry and can withstand the challenging conditions of the oral environment; however, the compositions may be useful in additional applications such as in medical devices, as coating and packing materials, as adhesives, as filters, and in 3D printing.
In an aspect, disclosed are new and non-obvious compositions of resin monomers that enhance the polymerization rate of styrene derivatives over that achievable with current compositions and associated methods by the addition of acrylate derivatives, and photo-initiators. Furthermore, with the herein disclosed compositions and methods, the fractions of styrene derivatives and acrylate derivatives in the monomer state can be retained in the polymeric state, and these fractions can be maintained throughout the process of polymerization regardless of the speed of polymerization. Furthermore, the viscosities of the monomers will not cause composition drift in the polymer. Finally, the diffusion limitation of copolymerization is overcome by using monomers containing carbamate functional groups.
In an embodiment, the novel and non-obvious compositions of matter include two or more vinyl-containing monomer(s) and one or more initiators. The two or more vinyl-containing monomers undergo vinyl conversion to form a composition-controlled resin.
In an aspect, the two or more vinyl-containing monomer(s) are chosen from a group consisting of mixtures of methacrylate derivatives and styrene derivatives, and mixtures of acrylate derivatives and styrene derivatives; and the methacrylate and styrene moieties or the acrylate and styrene moieties are in a same monomer or different monomers.
In another aspect, one or more of the vinyl-containing monomer(s) have functional groups selected from a group consisting of one or more carbamate groups and/or derivatives; one or more urethane groups and/or derivatives; and one or more amine groups and/or derivatives.
In yet another aspect, the initiators are selected from a group consisting of photo-initiator(s) including camphorquinone or derivatives; a combination of camphorquinone or derivatives and amine(s), including ethyl-4-N, N-dimethyl-aminobenzonate; Phenylpropanedione or derivatives, including 1-phenyl-1,2-propanedione; and Bisacrylphosphine oxide or derivatives including bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (Irgacure 819), bis(2,6-dimethoxy benzoyl)-trimethylpentyl phosphine oxide and 1-hydroxycyclohexyl phenyl ketone. The photo-initiators may be used with/without diaryl iodonium derivatives, and with/without boryl radicals including tert-butylamine borane complex.
In still another aspect, the composition is used to achieve composition control of a forming polymer, wherein the mole fraction of acrylate/methacrylate moieties and styrene moieties in the forming polymer is determined preferably by the chemistry and composition of the feeding monomers rather than the viscosity of the feeding monomers,
The detailed description refers to the following figures in which like numerals and symbols refer to like items, and in which:
With current compositions and associated methods, photo-polymerization of styrene derivatives occurs too slowly to be practically useful in dental applications. Disclosed herein are precursor compositions (resin monomer compositions) that include styrene derivatives and that reach satisfactory vinyl conversion within a time frame that is suitable for dental applications such as dental preventive and restorative applications, laminate veneers, dentures, denture repairing materials, inlays and onlays, fixed bridges, implants, resin reinforced cements, placement of ceramic restorations, and sealants. Also disclosed are methods for producing satisfactory resins for such dental applications.
With an ever-growing impetus to produce new, advanced functional materials, many synthetic approaches and conceptual designs have been developed, and opportunities have opened. A clinically implementable system that makes high performance functional polymeric materials on site, especially those with well-defined chemical structures, is appealing for various applications, including medical devices, coatings, packaging, electronic devices, solar cells, and the automobile industry. Photo-polymerization also may be used as a photographic or printing process, because polymerization only occurs in regions that have been exposed to light. Unreacted monomers can be removed from unexposed regions, leaving a relief polymeric image. Several forms of 3D printing, including layer-by-layer stereo lithography and two-photon absorption 3D photo-polymerization, also may use photo-copolymerization.
In an aspect, the precursor compositions include a styrene derivative to which is added a small amount of methacrylate (MA) or acrylate derivatives. The methacrylate or acrylate derivatives may contain urethane groups, carbamate groups, amide, and/or amine groups, preferably urethane groups as shown in
In an aspect, the precursor composition may be comprised of a fraction of methacrylate derivatives, up to 80 percent by weight (80 wt %), preferably 50 wt %. As can be seen in the example of
The precursor composition may be cured by light irradiation, and preferably by visible light, or by heating. The polymerization may occur after the precursor composition infiltrates into pores of porous objects, wherein the porous objects include metal oxide, ceramic, chitosan, polysaccharide particles, metal, and wood.
Finally, the above monomers may be mixed with or without solvents or with or without fillers such as silica particles, metal oxide particles, ceramic particles, chitosan, polysaccharide particles, and the particles are in nano-scale and micro-scale size.
By co-polymerizing with the methacrylate derivatives, the styrene derivatives may reach about a 60 percent or more degree of vinyl conversion (DC) within about one minute of light irradiation.
Further, the copolymerization of the precursor composition may follow an alternating copolymerization kinetics, and the precursor composition may have an azeotropic composition at the equimolar of styrene derivatives and methacrylate derivatives. Azeotropic composition means the mole ratio of styrene and methacrylate in the monomers is the same as that in the copolymer and is independent of the polymerization rate. This monomer reactivity-controlled process depends on the monomer and initiator used in the polymerization process. As a consequence, the repeating unit of copolymers is styrene-alt-methacrylate, and the reactivity is controllable through the feeding monomers, particularly when equimolar styrene derivative monomers and methacrylate derivative monomers are used. By selective control of the chemical structure of the feeding monomers, the desired performance of the light-cured dental resin is achieved; in particular, the feeding monomers are controlled to produce a dental resin having the desired polymerization shrinkage, hydrophilicity, hydrophobicity, and hydrogen bonding.
Furthermore, the dental resin formed using the monomers of
Still further, for MA derivatives containing urethane groups, carbamate groups, amide groups, and amine functional groups, preferable urethane groups serve an additional function as co-initiators, thereby reducing the amount of leachable photo-initiators needed in the precursor composition. Thus, the forming polymer is more biocompatible and safer for use in dental applications.
Finally, with certain of the herein disclosed precursor compositions, viscosity does not cause a deviation in the co-polymer composition (i.e., composition drift) as may happen in DMA-based co-polymer compositions.
Following are examples of compositions and methods related to rapid azeotropic photo-copolymerization. In these examples, the commercial monomers UDMA and ethoxylated bisphenol dimethacrylate (EBPADMA) were supplied by Esstech (Essington, Pa., USA) and were used as received. TEG-DVBE was synthesized and fully characterized by the applicant. The resin formations in the examples were activated either by 0.2 weight percent (wt %) of camphorquinone (CQ, Aldrich, Saint Louis, Mo., USA) and 0.8 wt % of ethyl 4-N,N-dimethylaminobenzoate (amine, Aldrich, Saint Louis, Mo., USA) or Irgacure 1819 for visible light photo-polymerization.
This example involves the use of FTIR spectroscopy, real-time Raman micro-spectroscopy, and one-hour (1H) NMR spectroscopy to evaluate the composition of monomer mixtures and their copolymers. The absorbance or scattering of vinyl groups on TEG-DVBE (a styrene-derivative) and UDMA (a methacrylate-derivative) were identified, separated, and quantified using FTIR spectroscopy and Raman spectroscopy. The vinyl groups on TEG-DVBE formed a stronger conjugation with their benzene rings than the vinyl groups on UDMA did with carboxyl groups. In addition, the di-substitution (methyl and carboxyl) of the β-carbon of methacrylates may cause the C═C stretching to shift to a lower energy. As a result, the vinyl groups on TEG-DVBE and UDMA exhibited peaks at approximately 1629 cm−1 and 1638 cm−1, respectively, in both FTIR and Raman spectra. The separation and quantification of the C═C peaks of these two monomers was realized through peak-fitting using mathematical models developed for FTIR and Raman spectroscopy. In the wave number ranging from 1580 cm−1 and 1660 cm−1, four peaks were identified. Besides the absorption of C═C stretching of vinyl groups, the C═C stretching of the benzene ring from TEG-DVBE (1612 cm−1) and N—H bending from UDMA (1623 cm−1) were observed, respectively.
The mixture of TEG-DVBE and UDMA monomers at an azeotropic composition (i.e., 1/1 mole ratio) had higher reactivity toward free-radical photo-polymerization than ethoxylated bisphenol A dimethacrylate (EBPADMA) and approximately the same reactivity as that of UDMA. For the degree of vinyl conversion (DC) of EBPADMA, UDMA and UDMA/TEG-DVBE mixtures immediately after light irradiation (20 seconds, 40 seconds, or 60 seconds, using Smartlite® Max at 1600 mW/cm2), mixtures of CQ and 4E (0.2 wt % and 0.8 wt %, respectively) were used as an initiator. Using the same initiators and curing light, the DC of monomer mixtures (UDMA/TEG-DVBE/=1/3) reached 79% immediately after 40 seconds of light irradiation. Increasing the amount of UDMA makes the polymerization rate even faster. At a 1/1 mole ratio, UDMA/TEG-DVBE initiated by CQ/4E was found to be the fastest system among the three systems evaluated with different initiators and monomer mixtures.
As noted herein, and as described in this example 3, azeotropic composition in copolymers means that the fractions (mole ratio) of the starting monomers are the same as their fractions in the copolymers, and this mole ratio is constant throughout the copolymerization process. As an example, alternating copolymers of styrene and methyl methacrylate (MMA) have an azeotropic composition, 1/1 by mole. Three methods, FTIR-ATR, confocal Raman micro-spectroscopy, and NMR were used to confirm that equimolar UDMA/TEG-DVBE was an azeotropic composition when CQ/4E was used as an initiator, but not when Irgacure 819 was used as an initiator. The vinyl groups on TEG-DVBE (peak at 1630 cm−1) and UDMA (peak at 1639 cm−1) were identified and separated by both FTIR and Raman spectroscopy, and the intensity ratio of these peaks was proportional to the mole ratio of the two corresponding monomers. Kinetic studies using confocal Raman micro-spectroscopy confirmed that the ratio of peak intensity of UDMA/TEG-DVBE did not change, no matter how fast the photo-copolymerization was, nor how high the DC was. The polymerization rate was controlled through the intensity of irradiation light to obtain fast (150 mW/cm2 for 20 seconds) and slow (4 mW/cm2 for 5 seconds) reactions. In addition, NMR also confirmed that the mole ratio of monomers was constant (1/1) at different DCs, from 5% to 60%. Using the same NMR method, UDMA (viscosity 7000 cP (centipoise)) was found to have a reduced fraction at high DC in copolymers with TEGDMA, due to viscosity effects. Even though TEG-DVBE had a similarly low viscosity (29 cP) as TEGDMA (12 cP), applicant did not observe any viscosity effects throughout all of the reaction conditions that were evaluated.
Diffusion limitations lead to less monomer conversion (lower DC) of high viscosity monomers when no carbamate functional groups are in the monomers. The copolymerization of a mixture of EBPADMA with TEG-DVBE, 1/1 by mole, initiated by camphor quinone and amine showed that more TEG-DVBE was converted into polymer, and the mole fraction of TEG-DVBE-polymer was higher than polymerized EBPADMA at high monomer conversion. The mixture of monomers and initiators was irradiated for 20 seconds with a curing gun at 400 mW/cm2. The DC of each monomer during copolymerization was monitored by real-time FTIR.
Diffusion limitations lead to less monomer conversion of high viscosity monomers when no carbamate functional groups are in the monomer. The copolymerization of mixture of EBPADMA with TEG-DVBE, 1/1 by mole, initiated by 1819 showed that more TEG-DVBE was converted into polymer, and the mole fraction of TEG-DVBE-polymer was higher than polymerized EBPADMA at a high monomer conversion. The mixture of monomer and initiators was irradiated for 20 seconds with a curing gun at 400 mW/cm2. The DC of each monomer during copolymerization was monitored by real-time FTIR.
Diffusion limitations lead to more monomer conversion of high viscosity monomer when carbamate functional groups are in the high viscosity monomer. The copolymerization of a mixture of UDMA with TEG-DVBE, 1/1 by mole, initiated by 1819 showed that more UDMA was converted into polymer, and the mole fraction of UDMA-polymer was higher than polymerized TEG-DVBE at high monomer conversion. The mixture of monomer and initiators were irradiated for 20 seconds with a curing gun at 400 mW/cm2.
The copolymer of UDMA/TEG-DVBE generated less stress than the copolymer of Bis-GMA/TEGDMA at the same DC when initiated by CQ/amine.
A composite was made by resin (25% by mass) and silica particles as fillers (75% by mass). The resin was a mixture of UDMA/TEG-DVBE 3/1 (by mole) and CQ/4E. The mixture was cured by light irradiation, and the cured composite had the same rigidity as composites made of Bis-GMA/TEGDMA but had significantly high flexural strength and toughness.
The degree of vinyl conversion (DC) of the mixture of UDMA/TEG-DVBE (1/1 by mole) with CQ/amine as initiator was approximately 86% after 1 minute of light irradiation. The DC was further increased by heat. The DC was approximately 96% after 24 hours at 60 degrees centigrade; and the DC reached >99% after 0.5 hours at 200 degrees centigrade.
This example describes photo-polymerization methods. Monomer mixtures were sandwiched between two Mylar films (10 μL, for FTIR-ATR measurement) or sealed in capillary glass tubes (Vitrocom, Mt. Lks. N.J., USA; 0.40×4.0 I.D., for real-time Raman micro-spectroscopy evaluation) and photo-cured using a handheld dental curing light (SmartLite max LED curing light, model: 644050, Dentsply International, Milford, Del., USA). The intensity of light irradiation was adjusted through the distance of light to samples.
This example determined the degree of vinyl conversion (DC) using FTIR-ATR and peak fitting methods. DC was evaluated immediately after curing using a Thermo Nicolet Nexus 670 FT-IR spectrometer (Thermo Scientific, Madison, Wis., USA) with a KBr beamsplitter, an MCT/A detector and an attenuated total reflectance (ATR) accessory. The areas of absorption peaks of the vinyl group of TEG-DVBE at 1629 cm−1, and the methacrylate groups of UDMA at 1638 cm−1 were integrated, and the DC was calculated using the aromatic group of TEG-DVBE at 1612 cm−1 or the amide group of UDMA at 1537 cm−1 as an internal standard. Peaks were resolved with the assistance of the curve fitting program Fityk (version 0.9.8). In order to correct potential discrepancies, a standard curve was produced by plotting varied resin composition ratio values analyzed by NMR spectroscopy against the values obtained through FTIR peak fitting. The phenyl absorbance at 1612 cm−1 was the internal standard for TEG-DVBE homo-polymers. DC was calculated according to the following equation: DC=(A1/A0−A1′/A0′)/(A1/A0) 100%, where A1/A0 and A1′/A0′ stand for the peak-area-ratio of vinyl-of-interest and internal standard before and after polymerization, respectively. The vinyl-of-interest may be vinyl groups from TEG-DVBE, UDMA, or both.
Sol-gel experiment. Resin specimens were placed in a stainless steel mold (13 mm in diameter and 1 mm in thickness) and then cured for different time scales (10 seconds, 20 seconds and 60 seconds) with a Triad 2000 visible light curing unit (Dentsply, York, Pa., USA) fitted with a tungsten halogen light bulb (75 W and 120 V, 43 mW/cm2). The samples were then weighed and their DCs were determined by FITR-ATR immediately after the curing. In a pre-weighed vial, each sample was extracted twice using 5 mL deuterated methylene chloride (CDCl3) containing 0.01 wt % butylated hydroxytoluene (Aldrich, Saint Louis, Mo., USA) via continuous shaking for 48 hours. The solution (sol) fractions from these two extractions were combined and concentrated via rotary evaporation under reduced pressure until no further changes in weight were observed. 1H NMR (Bruker 600 MHz) was conducted for each sol fraction sample to determine the monomer ratio. The remaining gel fraction was collected and dried via in-house vacuum to yield a constant weight, and the DC was measured by FTIR-ATR.
Real-time Raman micro-spectroscopy: method description, peak fitting method, and real-time DC evaluation. Raman spectra were acquired from dried residues using a Renishaw S1000 micro-Raman spectrometer (Renishaw, Gloucestershire, UK) consisting of a Leica DMLM microscope coupled to a 250 mm focal length imaging spectrograph with a proprietary deep depletion, thermoelectrically cooled (70 degrees centigrade) charge-coupled device. For this work, a 632.8 nm helium-neon laser (Model 1144P, JDS Uniphase, Milpitas, Calif.), holographically ruled 1800 grooves mm−1 grating, and 20× objective (Leica N PLAN) were used. The excitation laser was focused to a line approximately 50 μm long at the sample position and aligned to the spectrograph entrance slit to maximize throughput. The line focus was utilized to reduce laser power density at the sample. Laser power measured at the sample position was approximately 12 mW. Depending on the desired spectral range, data was acquired using a static grating position covering the Raman shift range from 1275 cm−1 to 1790 cm−1 (577 data points) or a grating step scan mode covering the Raman shift range from 500 cm−1 to 1800 cm−1 (1369 data points). Integrations time was typically 1 second/pixel. Spectral resolution was approximately 3 cm−1. To further minimize any unintended impacts of laser illumination on the photo-polymerization the samples used in the kinetic studies were slowly translated laterally throughout data acquisition. This was done using the motorized microscope translation stage and Raman mapping capabilities in the spectrometer control software (WiRE 3.1, Renishaw, Gloucestershire, UK).
Estimation of the degree of conversion of the monomers was accomplished using a direct classical least squares (CLS) multivariate regression approach. Pure spectra of each monomer were acquired by placing the neat materials in the same vessels as used for the photo-polymerization kinetic studies and collecting spectra with equivalent excitation laser power and integration time to provide spectra that were quantitative relative to one another. The spectral range was restricted to a narrow spectral range from 1625 cm−1 to 1660 cm−1, which corresponds to the stretching modes of the terminal vinyl groups on each monomer. This narrow range was necessary because of band intensity changes and small band shifts observed for many of the vibrational modes as a consequence of the polymerization. Blending of the monomers appeared to introduce small peak shifts (≤0.5 cm−1) in the vinyl stretching modes that were correlated with the mixture composition. The pure spectra were shifted slightly prior to application of the CLS method in order to minimize the fit residuals. In addition to the two monomer pure spectra, a constant offset was fit in the CLS model in order to correct for baseline variations that arose during the experiments. A simple constant was deemed adequate because the CLS models were fit over a very narrow region of 35 cm−1, which corresponds to a spectral band of only 1.75 nm, and fluorescent background interferences generally have much broader spectral profiles. The CLS scores are the contribution of each component of a linear combination of the pure spectrum in a least squares fit of the sample spectra. This is essentially a rigid peak fitting using an arbitrary experimentally measured peak function with a single parameter that corresponds to intensity. The pure spectra were acquired under identical instrumental conditions and thus the CLS scores were assumed to correspond directly to the relative composition of the monomer mixture before and during the polymerization. To estimate degree of conversion of each monomer, the CLS scores for each polymerization data set were normalized by the average score for the given component from an initial data set (typically ten or more spectra) acquired prior to photo initiation.
Rapid Photo-polymerization: One of the synergetic effects of the model monomers is the significant improvement of polymerization rate of the styrene-derivative, TEG-DVBE, by adding UDMA. Free radical homo-polymerization of styrene is relatively slow in comparison with methacrylate due to stabilization of free radicals through resonance with styrene's benzene ring. Without modifying the chemical structure of the monomer or inventing new initiators, copolymerization is one of the most efficient ways to accelerate polymer chain propagation because the rate of copolymerization is strongly affected by the competition of monomer reactivity ratios (r1 and r2), which overcomes the drawback of free-radical stabilization in homo-polymerization of TEG-DVBE. Although substantial work has been done to improve the polymerization rate of styrenic monomer in vinyl ester resins (VERs) (Rey et al. Macromolecules 2000, 33, 6780, and Scott et al. Macromolecules 2003, 36, 6066), the polymerization rate and low degree of vinyl conversion are still limiting factors for VERs to be used clinically in dental adhesives and dental composites. This experiment demonstrates the viability of using model monomers in dental clinics by reaching DC above 70% with 20 seconds of light irradiation. The DCs of TEG-DVBE, UDMA, and the equimolar mixture of TEG-DVBE and UDMA immediately after light irradiation (light intensity at 1600 mW/cm2) for 20 seconds, 40 seconds, and 60 seconds were determined. The resulting low DC indicates that camphorquinone/ethyl 4-N, N-dimethylaminobenzoate (CQ/amine) are not efficient initiators for TEG-DVBE homo-polymerization. This initiator combination is however very effective on UDMA homo-polymer and the copolymer: their DCs reaching approximately 90% in 20 seconds.
Another noteworthy feature is the azeotropic composition at equimolar TEG-DVBE and UDMA when CQ/amine are used as initiators. Azeotropic compositions in copolymers mean that the mole fractions of the feed monomers are retained in the polymer and are constant throughout the polymerization process. FTIR also revealed that the DC of TEG-DVBE and UDMA in the above equimolar copolymers was the same, approximately 90%. The composition of copolymers was further evaluated by the sol-gel experiment. To extract enough leachable materials, the light intensity was reduced to mW/cm2, and low DC copolymers were obtained. The progress of photo-polymerization was controlled by varying the time of light irradiation. Based on the peak-area analysis of the absorbance of C═C stretching in FTIR spectra and integration of 1H NMR signals associated with protons on C═C, the styrene-vinyl groups and methacrylate-vinyl groups had the same mole fraction in both gels and solubles. This suggests that the equimolar composition of the feed monomers was maintained in these three polymerization stages from DC=5% to DC=62%.
The azeotropic composition confirmed by real-time Raman spectroscopy: Real-time Raman micro-spectroscopy further confirmed that the equimolar composition was constant over time during photo-polymerization and was independent of the polymerization rate, which was controlled through light intensity and irradiation time. To achieve a step-wise polymerization, specimens were exposed to light at 4 mW/cm2 for 5 seconds up to a total of four exposures. The multivariate CLS method standardized using pure monomer spectra was used to estimate unpolymerized monomer composition in the samples using the C═C stretching bands of TEG-DVBE and UDMA. CLS scores for each specimen were normalized to 100 for the pre-polymerized monomer mixtures. As the vinyl groups converted to polymers, the associated C═C band intensity decreased, and the DC increased accordingly. At each light irradiation, the intensity dropped immediately, which was followed by further decrease at a much slower rate, until the next irradiation. During the full time range (10 minutes) of this set of experiments, DC reached approximately 20%, and the mole ratio of TEG-DVBE/UDMA remained 1/1. A faster photo-polymerization took place when the sample was irradiated at 150 mW/cm2 for 20 seconds. The DC of this specimen achieved approximately 55% immediately after light irradiation; after 1 hour, the DC was approximately 65%; after 1 day, it was approximately 72%. During the course of this set of experiments, the mole ratio of TEG-DVBE and UDMA was always 1/1.
The azeotropic composition predicted by monomer reactivity ratios: Monomer reactivity ratios were evaluated to understand the kinetics behind the azeotropic composition at equimolar composition. The polymer composition (F) was determined by Raman micro-spectroscopy according to the CLS score ratios of TEG-DVBE and UDMA at low DCs (1-3%). A classic instantaneous copolymerization equation for non-cross-linking polymers was used to compare F with the monomer feed composition (f, mole fraction) based on an assumption that at such low DCs, the two vinyl groups in one molecule act independently without interfering with each other.
The feed ratios of monomers may not always determine the compositions of the final material. Feeds with a molar ratio UDMA/TEG-DVBE >0.5 are expected to produce resin networks depleted in their UDMA content relative to the feeds, and UDMA/TEG-DVBE <0.5 produce networks enriched in UDMA. The composition data were fit to an equation with a nonlinear least-squares (NLLS) optimization after van Herk. The monomer reactivity ratios, rUDMA and rTEG-DVBE, are 0.64±0.11 and 0.55±0.12, respectively. They are slightly, but statistically significantly higher than the reactivity ratios of styrene and methyl methacrylate, r1≈r2≈0.5. These reactivity ratios suggest a polymerization mechanism somewhat biased towards cross-propagation and alternating sequences, characteristic of styrenic-methacrylic copolymer systems.
The effects of viscosity and monomer chemistry on composition control: Both of the sol-gel experiments and kinetic studies suggest the copolymerization of TEG-DVBE and UDMA is a monomer-chemistry-controlled process. The viscosity of monomer played no consequential role during the polymer chain propagation, considering that the viscosity of UDMA (6.631±0.100 Pas (Pascal seconds)) is approximately 240 times higher than that of TEG-DVBE (0.029±0.001 Pas). In contrast, copolymerization of UDMA and triethylene glycol dimethacrylate (viscosity=0.050 Pas) showed significant composition drift when DC was above 20% because the low viscosity monomers diffused faster in resin networks than the base monomers and reached the propagating chain quicker, thus more of them were converted into polymers at high DCs. Although the exact mechanism that leads to such rapid photo-polymerization and well-controlled azeotropic composition is yet to be defined, UDMA has dual roles: monomer and co-initiator when initiated by CQ/amine. The carbamate functional group in UDMA may form a free radical on a methylene group adjacent to its N—H groups. This may be achieved via electron transfer from the light-excited CQ. Experimentally, the photo-polymerization rate of UDMA initiated by CQ alone was similar to that by CQ/amine, and the photo-bleaching rate of CQ in UDMA also showed minimal differences with/without amine.
This application is a continuation of U.S. patent application Ser. No. 15/276,821, filed Sep. 27, 2016, and entitled RAPID AZEOTROPIC PHOTO-COPOLYMERIZATION OF STYRENE AND METHACRYLATE DERIVATIVES AND USES THEREOF, which claims the benefit of provisional patent application 62/234,088 filed Sep. 29, 2015 and entitled RAPID AZEOTROPIC PHOTO-COPOLYMERIZATION OF STYRENE AND METHACRYALTE DERIVATIVES FOR DENTAL APPLICATIONS. The disclosures of these two applications are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15276821 | Sep 2016 | US |
| Child | 16294531 | US |