Claims
- 1. A rigid, non-cellular composition having a density of at least about 1 gram/cc which is demoldable, without the application of an external source of heat, within about 5 minutes after admixture of the components of the composition which is the reaction product of a polyurethane-forming composition comprising
- A. a dihydroxyl-containing compound having a hydroxyl equivalent weight of less than about 250;
- B. an organic polyisocyanate having an NCO functionality of at least about 2.5;
- C. a liquid modifier compound having a boiling point of at least about 150.degree. C or mixture of such compounds and which moderates the reaction exotherm between components (A), (B), and (D) without substantial reaction therewith selected from the group consisting of fatty oils, fatty acids and mixtures thereof; and
- D. and organotin catalyst;
- wherein components (A) and (B) are present in quantities such that the NCO:OH ratio is from about 0.8:1 to about 1.5:1, component (C) is present in quantities of from about 10 to about 50 percent by weight of the combined weights of components (A), (B) and (C); and component (D) is present in quantities of from about 0.02 to about 5.0 percent by weight of the combined weight of components (A), (B) and (C).
- 2. The composition of claim 1 wherein component (D) is employed in quantities of from about 0.1 to about 2.0 percent by weight of the combined weight of components (A), (B) and (C) and the NCO:OH ratio is from about 0.9:1 to about 1.2:1.
- 3. The composition of claim 2 wherein component (C) is employed in a quantity of from about 20 to about 40 percent by weight of the combined weight of components (A), (B) and (C).
- 4. The composition of claim 3 wherein component (C) is selected from the group consisting of castor oil, safflower oil, tall oil, oleic acid, 2-ethyl hexanoic acid, C.sub.36 dimer acids and mixtures thereof.
- 5. The composition of claim 3 wherein component (D) is selected from the group consisting of stannous octoate, stannous naphthenate, dibutyltin dilaurate and dibutyltin diacetate.
- 6. The composition of claim 1 cast as a furniture component.
- 7. The composition of claim 1 cast as a decorative object.
- 8. The composition of claim 1 cast as a machine component.
- 9. A process for producing solid, rigid, polyurethane articles having a density of at least 1 g/cc, a percent elongation of less than 100, and which can be demolded within a period of about 5 minutes without the addition of an external source of heat which process comprises:
- 1. admixing the components of a composition comprising
- A. a dihydroxyl-containing compound having a hydroxyl equivalent weight of less than about 250;
- B. an organic polyisocyanate having an NCO functionality of at least about 2.5;
- C. a liquid modifier compound having a boiling point of at least about 150.degree. C or mixture of such compounds and which moderates the reaction exotherm between components (A), (B) and (D) without substantial reaction therewith selected from the group consisting of fatty oils, fatty acids and mixtures thereof; and
- D. an organotin catalyst;
- wherein components (A) and (B) are present in quantities such that the NCO:OH ratio is from about 0.8:1 to about 1.5:1, component (C) is present in quantities of from about 10 to about 50 percent by weight of the combined weights of components (A), (B) and (C); and component (D) is present in quantities of from about 0.02 to about 5.0 percent by weight of the combined weight of components (A), (B) and (C);
- 2. placing the admixed composition into a suitable mold wherein said composition solidifies within less than about 5 minutes to a solid having the aforesaid density and elongation; and
- 3. subsequently demolding the resultant article from the mold.
- 10. The process of claim 9 wherein component (D) is employed in quantities of from about 0.1 to about 2.0 percent by weight of the combined weight of components (A), (B) and (C) and the NCO:OH ratio is from about 0.9:1 to about 1.2:1.
- 11. The process of claim 10 wherein component (C) is a halogenated aliphatic compound and is employed in a quantity of from about 20 to about 40 percent by weight of the combined weight of components (A), (B) and (C).
- 12. The process of claim 11 wherein component (C) is selected from the group consisting of castor oil, safflower oil, tall oil, oleic acid, 2-ethyl hexanoic acid, C.sub.36 dimer acids and mixtures thereof.
- 13. The process of claim 11 wherein component (D) is selected from the group consisting of stannous octoate, stannous naphthenate, dibutyltin dilaurate and dibutyltin diacetate.
- 14. The process of claim 9 wherein said mold is that of a furniture component.
- 15. The process of claim 9 wherein said mold is that of a decorative object.
- 16. The process of claim 9 wherein said mold is that of a machine component.
Parent Case Info
This application is a continuation-in-part of application Ser. No. 358,245, filed May 7, 1973, now U.S. Pat. No. 3,801,532, which is a continuation-in-part of application Ser. No. 205,697 filed Dec. 7, 1971, now abandoned.
US Referenced Citations (7)
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
358245 |
May 1973 |
|
Parent |
205697 |
Dec 1971 |
|