The present invention relates to a rare earth-doped core optical fiber, and to a manufacturing method thereof. The rare earth-doped core optical fiber according to the present invention is used as a fiber for optical amplification of an optical fiber laser, an optical amplifier, etc. and is particularly suitable for the constitution of an optical fiber laser.
Recently, it has been reported that a single-mode optical fiber laser or optical amplifier, which employs as a laser active material an optical fiber doped with a rare earth element such as neodymium (Nd), erbium (Er), praseodymium (Pr), and ytterbium (Yb), (hereinafter referred to as a rare earth element-doped optical fiber,) has a high number of possible applications in wide fields such as optical sensors or optical communication, and their applicability has been expected. One example of applications thereof is an Yb-doped core optical fiber laser employing an optical fiber in which a core is doped with Yb (which is hereinafter referred to as a Yb-doped core optical fiber), which is examined for the use in marker, repairing, soldering, cutting/drilling, welding or the like, and then commercialized. Conventionally, the laser used in such processing applications has been mainly a YAG laser, but recently the requirements for the processing performance have become more stringent, and as a result, the needs of laser performance have increased. For example,
1. a smaller spot size is required in order to achieve high precision processing;
2. a higher output is required; and
3. a reduction in down time for maintenance, etc. of a laser (MTBF, MTBM) is required.
For these requirements, the Yb-doped core optical fiber laser is characterized in that it has
1. a spot size in a μm-order;
2. a several W through several kW output; and
3. an expected life span of 30,000 or more implementations, and the Yb-doped core optical fiber laser has a greater advantage when compared to a conventional YAG laser.
As the rare earth-doped core optical fiber, there is generally known an optical fiber obtained by using a rare earth element-doped glass, as described in Patent Documents 1 and 2. The rare earth element-doped glass is doped with a rare earth element, aluminum, and fluorine in a host glass having a SiO2-based composition, and the rare earth-doped core optical fiber includes the glass as a core. Accordingly, the core part is doped with a rare earth element, aluminum, and fluorine.
If a SiO2 glass or a GeO2—SiO2-based glass, used for common optical fibers, is doped with about 0.1% by mass or more of a rare earth element, there occurs a problem of a so-called concentration quenching. This is a phenomenon where rare earth ions are aggregated (clustered) with each other in the glass, whereby the energy of excited electrons is likely to be lost in a non-radial process, leading to a reduction of life span of the emitted light or of efficiency. Patent Document 1 describes that by doping both of the rare earth element and Al, a high concentration of the rare earth element can be doped without causing deterioration of the light emitting characteristics, and even with a lower function length with the exciting light, a sufficient amplification benefit is attained, thereby making it possible to realize a small-sized laser or optical amplifier.
Patent Document 2 describes a method for manufacturing a rare earth-doped core optical fiber, and in particular a rare earth element-doped glass. In this method, a parent metal of a silica porous glass having an open pore connected therewith is immersed in a solution containing a rare earth element ion and an aluminum ion, and the rare earth element and the aluminum are impregnated in the parent metal. Thereafter, a drying process is carried out, in which the parent metal is dried, the salts of the rare earth element and the aluminum are deposited in the pores of the parent metal, and the deposited salt is oxidized and stabilized. Then, the parent metal after the drying process is sintered for vitrification. Further, at a time between the completion of the drying process and the completion of the sintering process, the parent metal is subject to heat treatment under an atmosphere containing fluorine to dope the fluorine.
A rare earth element-doped optical fiber is obtained by synthesizing glass, as a clad portion, around the obtained rare earth element-doped glass to obtain a glass parent metal for manufacturing of an optical fiber; and then fiber-drawing the parent metal. Herein, in order to obtain an optical fiber that is used for an Yb-doped core optical fiber laser, ytterbium (Yb) may be used as a rare earth element in the manufacturing process for the rare earth element-doped glass.
One representative example of other methods for manufacturing an Yb-doped core optical fiber is a combination of a MCVD process and an immersion process, as described in Non-Patent Document 1. In this method, SiCl4, GeCl4, O2 gases, etc. are firstly flowed through a silica glass tube which is to be served as a clad glass, and a heat source such as an oxyhydrogen burner disposed outside the silica glass tube is used to oxidize SiCl4 and GeCl4 and to produce SiO2 and GeO2 glass particulates, which are then deposited inside the silica glass tube. At this time, the temperature upon deposition is lowered to not give a completely transparent glass, thus obtaining a glass in a porous state. Next, a solution containing Yb ions is introduced into the inside of the silica glass tube having the prepared porous glass layer therein, and penetrated into the porous portion. After the sufficient penetration with the solution, the solution is withdrawn from the silica glass tube, and the tube is dried to remove water under a chlorine atmosphere. Then, the porous portion is made transparent, and core solidification is performed to prepare a parent metal for a Yb-doped core optical fiber. If necessary, the Yb-doped core optical fiber is obtained by synthesizing a glass, as a clad portion, around the prepared parent metal, thereby giving a transparent glass parent metal for preparation of an optical fiber; and then fiber-drawing the parent metal. Further, the obtained optical fiber can be used to constitute an Yb-doped core optical fiber laser.
[Patent Document 1] Japanese Unexamined patent Application, First Publication No. 11-314935
[Patent Document 2] Japanese Unexamined Patent Application, First Publication No. 3-265537
[Non-Patent Document 1] Edited by Shoichi SUDO, Erbium-doped optical fiber amplifier, The Optronics Co., Ltd.
[Non-Patent Document 2] Laser Focus World Japan 2005. 8, p.p. 51-53, published by Co., Ltd. E-express
[Non-Patent Document 3] Z. Burshtein, et. al., “Impurity Local Phonon Nonradiative Quenching of Yb3+ Fluorescence in Ytterbium-Doped Silicate Glasses”, IEEE Journal of Quantum Electronics, vol. 36, No. 8, August 2000, pp. 1000-1007
The present inventors have observed that when a conventional manufacturing method was used to prepare a Yb-doped core optical fiber to constitute the Yb-doped core optical fiber laser as shown in
The photodarkening phenomenon is one that clearly differs from the above-described concentration quenching. The concentration quenching is a phenomenon in which rare earth ions are aggregated (clustered) with each other in the glass, whereby the energy of excited electrons is likely to be lost in a non-radial process. Since there is usually no change in the aggregation state of the rare earth ions during the laser oscillation, the laser oscillation, even carried out over a long period of time, does not cause the change in the degree of concentration quenching and decrease in the output of the laser oscillation over time, Patent Documents 1 and 2 in prior art may solve the problems on an optical fiber obtained by employing a rare earth element-doped glass, but they cannot solve the problems on the decrease in the output of the laser oscillation caused from a photodarkening phenomenon.
Under these circumstances, the present invention has been made, and an object of which is to provide a rare earth-doped core optical fiber that can be used to prepare an optical fiber laser capable of maintaining a sufficient output of laser oscillation, even carried out over a long period of time, and a manufacturing method thereof.
In order to accomplish the object, the present invention provides a rare earth-doped core optical fiber, which includes a core comprising a silica glass containing at least aluminum and ytterbium, and a clad provided around the core and comprising a silica glass having a lower refraction index than that of the core, wherein aluminum and ytterbium are doped into the core such that a loss increment by photodarkening, TPD, satisfies the following inequation (A):
T
PD≧10{−0.655*(D
[in equation (A), TPD represents a desired loss increment by photodarkening at a wavelength of 810 nm (unit: dB), DAl represents the concentration of aluminum contained in the core (unit: % by mass), and AYb represents the peak light absorption rate of the light absorption band which appears around a wavelength of 976 nm in the light absorption band by ytterbium contained in the core (unit: dB/m)].
Furthermore, the present invention provides a rare earth-doped core optical fiber, which comprises a core comprising a silica glass containing aluminum and ytterbium, and a clad provided around the core and comprising a silica glass having a lower refraction index than that of the core, wherein the core has an aluminum concentration of 2% by mass or more, and ytterbium is doped into the core at such a concentration that the light absorption band of ytterbium doped into the core, which appears around a wavelength of 976 nm, shows a peak light absorption rate of 800 dB/m or less.
In the rare earth-doped core optical fiber of the present invention, it is preferable that the core also contains fluorine.
In the rare earth-doped core optical fiber of the present invention, it is preferable that a polymer layer having a lower refraction index than that of the clad is provided in the periphery of the clad.
In the rare earth-doped core optical fiber, it is preferable that the clad is composed of an inner clad positioned in the vicinity of the core, and an outer clad positioned outside the inner clad, and that the refractive index n1 of the core, the refractive index n2 of the inner clad, the refractive index n3 of the outer clad, and the refractive index n4 of the polymer layer satisfy the relationship of n1>n2>n3>n4.
In the rare earth-doped core optical fiber of the present invention, hollow pores may be present in a part of the clad glass.
Furthermore, the present invention provides a manufacturing method of a rare earth-doped core optical fiber. The method includes a deposition step which includes introducing raw material gases composed of various kinds of a halide gas and an oxygen gas from a first cross-section of the glass tube having silica as a main component into a hollow portion of the glass tube, heating the glass tube by a heating means, subjecting the halide gas to oxidization to form a soot-like oxide, depositing the soot-like oxide on the inner surface of the glass tube, and sintering deposited soot-like oxide to deposit the porous glass layer; a doping step which includes doping an additive into the porous glass layer of the inner surface of the glass tube after the deposition step; a transparentization step which includes heating the glass pipe to subject the porous glass layer to transparent vitrification after the doping step; a core solidification step which includes collapsing a hollow portion of the glass tube for core solidification to form a preform after the transparentization step; and a fiber-drawing step which includes fiber-drawing the optical fiber parent metal including the preform to obtain a rare earth-doped core optical fiber after the core solidification step, wherein the halide gas contains at least SiCl4 and AlCl3, the additive contains at least a rare earth element, and in either or both of the deposition step and the transparentization step, a fluoride gas is introduced from a first cross-section of the glass tube to a hollow portion of the glass tube.
In the manufacturing method of the present invention, it is preferable that the rare earth element used as the additive at least contains ytterbium.
In the manufacturing method of the present invention, it is preferable that the core of the obtained rare earth-doped core optical fiber has an aluminum concentration of 2% by mass or more, and ytterbium is doped into the core at such a concentration that the light absorption band of ytterbium doped into the core which appears around a wavelength of 976 nm shows a peak light absorption rate of 800 dB/m or less.
In the manufacturing method of the present invention, it is preferable that the method further comprises a step for forming a polymer layer having a lower refraction index than that of the clad in the periphery of the clad of the optical fiber in the fiber-drawing step.
In the manufacturing method of the present invention, it is preferable that the clad of the obtained rare earth-doped core optical fiber is composed of an inner clad positioned in the vicinity of the core, and an outer clad positioned outside the inner clad, and the refractive index n1 of the core, the refractive index n2 of the inner clad, the refractive index n3 of the outer clad, and the refractive index n4 of the polymer layer satisfy the relationship of n1>n2>n3>n4.
As for the rare earth-doped core optical fiber of the present invention, when the rare earth-doped core optical fiber of the present invention is used for an optical fiber laser having ytterbium as a laser active material, the laser oscillation, even carried out over a long period of time, only slightly decreases the output of the light at a laser oscillation wavelength, and enables to manufacture an optical fiber laser capable of maintaining a sufficient output of laser oscillation even with use over a long period of time.
By using the manufacturing method of the rare earth-doped core optical fiber of the present invention, a rare earth-doped core optical fiber that is capable of manufacturing an optical fiber laser capable of maintaining a sufficient output of laser oscillation even with use over a long period of time can be efficiently manufactured.
According to Patent Documents 1 and 2, a rare earth element-doped glass having a rare earth element, aluminum, and fluorine doped in a host glass having SiO2-based composition, and a manufacturing method thereof are disclosed, wherein ytterbium (Yb) is used as a rare earth element, and further the Yb-doped glass is used in the core portion to make an Yb-doped core optical fiber, which can be also applied in prior art. However, Patent Documents 1 and 2 have a detailed description that erbium (Er) is chosen as a rare earth element, but have no description of ytterbium being chosen as a rare earth element. Furthermore, the technology as described in Patent Documents 1 and 2 is a means for solving a problem on concentration quenching of a rare earth element, and thus it cannot be applied to solve the problem of the decrease in the output of the laser oscillation light over time by using an Yb-doped core optical fiber in prior art. That is, it is known that since the energy level that participates in the laser oscillation of the ytterbium ion (Yb3+) in the Yb-doped core optical fiber is only in two kinds of states, that is, a 2F7/2 ground state and a 2F5/2 excited state, very little concentration quenching occurs. Further, Non-Patent Document 3 describes that the ytterbium concentration upon generation of concentration quenching in the glass having neither aluminum nor fluorine doped thereinto is 5×1020 cm−3. The Yb-doped core optical fiber used in the optical fiber laser generally has such an ytterbium concentration that the light absorption band which appears around a wavelength of 976 nm shows the peak absorption rate in a range of from 100 to 2000 dB/m. The ytterbium concentration, as determined through conversion using the value, 0.11×1020 cm−3 to 2.2×1020 cm−3, which is smaller than that upon generation of concentration quenching as described in Non-Patent Document 3. Therefore, it is believed that aluminum is not needed to inhibit the concentration quenching of ytterbium.
On the other hand, a method of doping aluminum into the Yb-doped core optical fiber, as described later, can be a means for solving the problem on the decrease in the output of the laser oscillation light, but the amount of aluminum doped is even more than that required to inhibit concentration quenching. For example, the concentration quenching was not observed in the Yb-doped core optical fiber, in which the core has a fluorine concentration of 0.6% by mass and an aluminum concentration of 0.1% by mass, and ytterbium is doped at a concentration such that the light absorption band which appears around a wavelength of 976 nm in the light absorption band by ytterbium contained in the core shows the peak light absorption rate of 1000 dB/m, but remarkable increase in the photodarkening loss was observed. Further, the fluorescence life span was measured on several other Yb-doped core optical fibers, in which the core has a fluorine concentration of 0.6% by mass and an aluminum concentration of 0.1% by mass, and the Yb light absorption rate is in a range of from 200 dB/m to 1900 dB/m. The results are shown in Table 1.
Regardless of the Yb light absorption rate, the fluorescence life span is a constant value, and accordingly, even if the Yb light absorption rate is in a range of from 200 dB/m to 1900 dB/m, the concentration quenching does not occur.
Patent Documents 1 and 2 as prior arts do not describe appropriate concentrations of ytterbium, aluminum, and fluorine, and thus it is difficult to solve a problem on the decrease in the output of the laser oscillation light even using the Yb-doped core optical fiber in prior art.
On the other hand, in order to solve a problem on the decrease in the output of the laser oscillation light, the rare earth-doped core optical fiber of the present invention is a rare earth-doped core optical fiber, which comprises a core comprising a silica glass containing aluminum and ytterbium, and a clad provided around the core and comprising a silica glass having a lower refraction index than that of the core, wherein a concentration of aluminum contained in the core, and the peak light absorption rate of the light absorption band which appears around a wavelength of 976 nm in the light absorption band by ytterbium contained in the core, are adjusted, respectively, so as to obtain a desired loss increment by photodarkening.
A first example of the first embodiment of the rare earth-doped core optical fiber according to the present invention is described with reference to
The rare earth-doped core optical fiber 10B shown in
If an optical fiber laser is constituted by using a rare earth-doped core optical fiber having Yb doped into the core, an optical fiber laser providing an output of a light as a laser oscillation wavelength of 1060 nm is obtained. However, an optical fiber laser using a conventional Yb-doped core optical fiber has a phenomenon that the output of a light as a laser oscillation wavelength of 1060 nm is decreased over time, and as a result, laser oscillation stops.
On the other hand, for the optical fiber laser constituted by using the rare earth-doped core optical fiber of the present invention, the decrease rate of the output of the light at a laser oscillation wavelength of 1060 nm can be significantly reduced even when laser oscillation is carried out over a long period of time. As the core has a higher Al concentration, the optical fiber laser has a lower decrease rate in the output of the laser oscillation. Further, as the core has a higher Yb concentration, the optical fiber laser has a higher decrease rate in the output of laser oscillation. As a result, by making the Al concentration of the core and the light absorption rate by Yb equal to those of the rare earth-doped core optical fiber of the present invention, the decrease rate in the output in the optical fiber laser can be significantly reduced.
The second example of the present embodiment of the rare earth-doped core optical fiber is described by way of specific examples. The rare earth-doped core optical fiber of the present example has substantially the same basic structure as that of the rare earth-doped core optical fiber shown in
In the inequation (A), TPD is a desired loss increment by photodarkening at a wavelength of 810 nm in the Yb-doped core optical fiber, expressed in a unit of dB. The TPD is a value as determined when an optical fiber laser is designed using the Yb-doped core optical fiber of the present invention, and is a valued determined in consideration of various factors such as an acceptable value of the decrease rate of the output of the optical fiber laser, a use environment, an intensity of the exciting light source input to the Yb-doped core optical fiber, and a desired output of laser oscillation. If TPD is set at a certain value, the loss increment by photodarkening of the Yb-doped core optical fiber of no more than TPD provides the optical fiber laser using the Yb-doped core optical fiber with good characteristics. To the contrary, the loss increment by photodarkening of the Yb-doped core optical fiber of more than TPD leads to unexpectedly higher decrease in the output of the laser oscillation in the optical fiber laser using the Yb-doped core, and as a result, laser oscillation cannot be carried out over a long period of time.
From the right hand side of the inequation (A), by using two parameters: the concentration of aluminum contained in the core DAl, (unit: % by mass) and the peak light absorption rate of the light absorption band which appears around a wavelength of 976 nm in the light absorption band by ytterbium contained in the core AYb (unit: dB/m), the loss increment by photodarkening of the Yb-doped core optical fiber can be presumed. However, the inequation (A) is an empirical equation obtained from the data of the aluminum concentration, the Yb light absorption rate, and the loss increment by photodarkening of a variety of the manufactured Yb-doped core optical fibers. A process for deriving the empirical equation will be described later.
As in the present invention, as long as the rare earth-doped core optical fiber has the concentration of aluminum contained in the core and the peak light absorption rate of the light absorption band which appears around a wavelength of 976 nm in the light absorption band by ytterbium contained in the core, which are each adjusted so as to obtain a desired loss increment by photodarkening, the optical fiber laser using the rare earth-doped core optical fiber of the present invention, even with the ytterbium concentration varying in the Yb-doped core optical fiber, has good characteristics. Particularly,
even when laser oscillation is carried out over a long period of time, most of the output of the light at a laser oscillation wavelength is not decreased, and thus it is capable of maintaining a sufficient output of laser oscillation even with use over a long period of time;
even when the ytterbium concentration in the Yb-doped core optical fiber is high, decrease in the output of the light at a laser oscillation wavelength can be maintained small;
since the ytterbium concentration in the Yb-doped core optical fiber can be set high, the length of the fiber required for laser oscillation may be shorter, and by this, reduction in cost, inhibition of generation of noise light by a non-linear optical phenomenon, and the like can be attained; and
other effects can be attained.
In the manufacturing method of the present invention, first, a deposition step as follows is carried out. Specifically, a silica glass tube 20 having a suitable outer diameter and a suitable thickness is first prepared, and as shown in
Further, in the deposition step as shown in
In the deposition step as shown in
The reciprocation movement of the oxyhydrogen burner 22 is repeatedly carried out once or several times, to form a porous glass layer 21 containing SiO2 and Al2O3.
Next, a doping step as follows is carried out. Specifically, a raw material gas is supplied, and the oxyhydrogen burner 22 is stopped and stood to cool. Then, a plug 24 is positioned on one side of the silica glass tube 20 having the porous glass layer 21 formed on its inner surface, and the tube is stood with the plug 24 down side, and as shown in
The aqueous solution containing the rare earth element is selected according to the rare earth element doped into the core to the solution. In the manufacturing of the Yb-doped core optical fiber, it is preferable that the solute of the aqueous solution containing the rare earth element is YbCl3, and the solvent is H2O. In this case, the YbCl3 concentration in the aqueous solution 23 is, for example, 0.1 to 5% by mass, and the solution concentration for obtaining a desired Yb concentration is empirically determined.
The porous glass layer 21 of the inner surface of the silica glass tube 20 is immersed in the aqueous solution containing the rare earth element compound for a suitable time, such as about 3 hours, and the plug 24 is detached. Then, the aqueous solution 23 is withdrawn from the tube, and as shown in
In order to remove the remaining moisture, while Cl2, O2, and He gases are transported into the silica glass tube 20, the periphery of the silica glass tube 20 is heated by the oxyhydrogen burner 22 to sufficiently remove the moisture (
Thereafter, while SiF4, He, and O2 are transported into the silica glass tube 20, and the fire power of the oxyhydrogen burner 22 is raised to perform the process to make the porous glass layer 21 transparent (
Next, a core solidification step in which the fire power of the oxyhydrogen burner 22 is increased to carry out core solidification of the silica glass tube 20, to prepare a rod-like preform 28 is carried out (
The silica tube that is an outer portion of the clad glass layer is covered on the outside of the prepared preform 28, and a jacket process for heating integration is carried out to prepare an optical fiber parent metal. The parent metal is fiber-drawn to obtain a rare earth-doped core optical fiber.
Further, a method for forming a clad glass layer is not limited to a method by the jacket process, and it may be an outside vapor phase deposition method.
By the above-described manufacturing method, Al can be uniformly contained in the porous glass layer 21 deposited on the inner surface of the silica glass tube 20. The present inventors have found out that when the prepared porous glass layer 21 is immersed in the aqueous solution 23 containing the rare earth element, the decrease in the output of the optical fiber laser is reduced, as compared to the case where Al is not contained in the production of a porous glass layer, but in the doping step. Particularly, the present inventors have found out that in the case where the rare earth element is Yb, the optical fiber laser, constituted using the Yb-doped core optical fiber obtained by fiber-drawing the parent metal obtained by the manufacturing method of the present invention, does not decrease the output of the light at a laser oscillation wavelength of 1060 nm, even when laser oscillation is carried out over a long period of time. Accordingly, the manufacturing method of the present invention, and the Yb-doped core optical fiber obtained by the manufacturing method of the Yb-doped core optical fiber, can be used to obtain an optical fiber laser capable of maintaining sufficient output of laser oscillation even when used over a long period of time.
By using such a structure, the rare earth-doped core optical fiber of the present invention can be a double-clad fiber, and thus by inserting a higher power of the exciting light, a higher output of laser oscillation can be obtained. In a conventional rare earth-doped core optical fiber, a higher power of the exciting light leads to more remarkable deterioration in the output of the laser oscillation, and it cannot be used as the double-clad fiber. On the other hand, the rare earth-doped core optical fiber of the present invention has a core having the same composition as described above, and if it is a double-clad fiber having the polymer layer 13 in the periphery of the clad 12D as shown in the present embodiment, it is possible to carry out laser oscillation over a long period of time.
By using such a structure, the difference in the refractive indices between the core 11E and the inner clad 14, nA (=n1−n2), can be smaller than the difference in the refractive indices between the core 11E and the outer clad 15, nB (=n1−n3). Accordingly, the effective cross-sectional Aeff can be larger of the light at a laser oscillation wavelength of 1060 nm, and thus generation of the noise light by a non-linear optical phenomenon such as Stimulated Raman Scattering, Stimulated Brillouin Scattering, and Four Wave Mixing can be reduced. In order to increase the effective cross-sectional Aeff by a conventional optical fiber, it is necessary to decrease the difference in the refractive indices between the core and the clad. Thus, the dopant such as Al and germanium should be reduced, but if the Al concentration is small, the decrease rate of the output in the optical fiber laser is increased. The rare earth-doped core optical fiber 10E of the present embodiment can have the core 11E doped with a sufficient amount of Al, and the effective cross-sectional Aeff can be further increased. Further, the optical fiber laser using the rare earth-doped core optical fiber 10E of the present embodiment can have higher performance and higher quality.
In the rare earth-doped core optical fiber according to the present invention, even when hollow pores are provided in a part of the clad, a double-clad fiber can be obtained, in which laser oscillation is carried out over a long period of time. Furthermore, by optimization of the positions of the hollow pores, a higher NA, a reduced skew light, or the like can be attained.
Using the Yb-doped core optical fiber having a structure as shown in
Evaluation of the characteristics of decrease in the power of the laser oscillation light of the prepared Yb-doped core optical fiber was conducted with reference to “Measurement System of Photodarkening” in Non-Patent Document 2. As described above, it is thought that the decreased in the power of the laser oscillation light is caused from the loss in the power by photodarkening. When the exciting light at a wavelength of 976 nm is entered with a high power onto the Yb-doped core optical fiber, photodarkening occurs, thereby leading to loss. By measuring the loss amount at a certain wavelength after the exciting light at a wavelength of 976 nm was entered for a certain period of time, the magnitude of the increase in the loss by photodarkening loss in the optical fiber to be measured can be measured, and it is related to the decrease rate of the light at a laser oscillation wavelength of 1060 nm. Accordingly, the characteristics of decrease in the power of laser oscillation light of the Yb-doped core optical fiber can be evaluated.
The prepared Yb-doped core optical fiber was set in a device for measuring the loss increment by photodarkening as shown in
As shown in
Next, an optical fiber laser was constituted by using the Yb-doped core optical fiber, and subject to laser oscillation over a long period of time, and then the output power of the light at a laser oscillation wavelength of 1060 nm was observed. The optical fiber laser constituted by using the Yb-doped core optical fiber having a loss increment by photodarkening at a wavelength of 810 nm of 0.5 dB or less, the output of the light at a laser oscillation wavelength of 1060 nm was not substantially reduced even when laser oscillation was carried out over a long period of time. On the other hand, the optical fiber laser constituted by using the Yb-doped core optical fiber having a loss increment by photodarkening at a wavelength of 810 nm of more than 0.5 dB, the output of the light at a laser oscillation wavelength of 1060 nm was observed to be decreased over time. Furthermore, as the loss increment by photodarkening was higher, the decrease rate of the output of the light at a laser oscillation wavelength of 1060 nm was higher.
As clearly shown from
Using the Yb-doped core optical fiber having a structure as shown in
On the other hand, in Reference Example, using the Yb-doped core optical fiber having a structure as shown in
In a similar manner to Example 1, the loss increment by photodarkening at a wavelength of 810 nm was measured. The results are shown in
On the other hand, since the specific refractive index A of the core with respect to any optical fiber was about 0.12%, the optical characteristics such as the mode field diameter and the cut-off wavelength were the same. Accordingly, by constituting the Yb-doped core optical fiber such that the core had an Al concentration of 2% by mass or more, Yb was contained at such a concentration that a light absorption band which appeared around a wavelength of 976 nm showed a peak light absorption rate of 800 dB/m or less in the light absorption band by Yb contained in the core, and fluorine was contained in the core, an Yb-doped core optical fiber having a loss increment by photodarkening at a wavelength of 810 nm of 0.5 dB or less can be obtained, with a small difference Δ in the specific refractive indices of the core.
According to the manufacturing method of the rare earth-doped core optical fiber according to the present invention, a Yb-doped core optical fiber was prepared. The prepared optical fiber was a Yb-doped core optical fiber having a structure as shown in
On the other hand, in Reference Example, a Yb-doped core optical fiber was prepared in the same manner as in Example 3, except that Al doping for a preform was performed in the doping step in
In a similar manner to Example 1, the loss increment by photodarkening at a wavelength of 810 nm was measured. The results are shown in
In any of the optical fibers, the Al concentration in the core was 2% by mass, and the loss increment by photodarkening at a wavelength of 810 nm was sufficiently small, but there were differences according to the manufacturing methods. The optical fiber Example 3 in which the Al doping was performed in the deposition step as shown in
Here, the method for deriving the inequation (A) is described.
For the measurement results of the loss increment by photodarkening the Yb-doped core optical fiber in Example 1, we tried to express the relationship between the Yb light absorption rate and the concentration of aluminum contained in the core by an empirical equation. The data in
log(LPD)=C0−C1*exp{−C2*(AYb)} (1)
wherein LPD is a loss increment by photodarkening at a wavelength of 810 nm (unit: dB), and AYb is an Yb light absorption rate per unit length (unit: dB/m). C0, C1, and C2 are fit factors. For the data of each Al concentration in
As shown in Table 2, it is found that the fit factors C1 and C2 give almost the same values even under different Al concentrations, whereas the fit factor C0 varies depending on the Al concentration. Since the fit factors C1 and C2 are substantially not changed depending on the Al concentrations, the average values of C1 and C2 obtained from each Al concentration, C1=4.304 and C2=0.00343 were substituted into the empirical equation (1), thereby obtain the following empirical equation (2).
log(LPD)=C0−4.304*exp{−0.00343*(AYb)} (2)
It is expected that the fit factor C0 is variable depending on the Al concentration.
Next, in the data shown in
log(LPD)=−0.655*(DAl)+0.997 (3)
wherein DAl is an Al concentration in the core (unit: % by mass).
Since the empirical equation (3) is an equation derived only from the data in a case where the Yb light absorption rate per unit length is 800 dB/m, 800 dB/m is substituted into AYb in the empirical equation (2), thereby obtaining the following equation (4).
log(LPD)=C0−0.277 (4)
By substituting the equation (4) into the equation (3), the following equation (5) was obtained.
C
0=−0.655*(DAl)+1.274 (5)
By substituting the equation (5) into the equation (2), the following equation (6) was obtained.
log(LPD)=−0.655*(DAl)−4.304*exp{−0.00343*(AYb)}+1.274 (6)
By modifying the equation (6), the following equation (7) was obtained.
L
PD=10{−0.655*(D
Therefore, the equation (7) is an empirical equation showing the relationship between the Yb light absorption rates and the aluminum concentrations contained in the core, for the measurement results of the loss increment by photodarkening. If a measured value of the loss increment by photodarkening, LPD, is no more than a desired loss increment by photodarkening, TPD, as described above, that is, in the case of the following equation (8):
TPD≧LPD (8)
the optical fiber laser obtained using this Yb-doped core optical fiber would have good characteristics.
From the equations (7) and (8), the inequation (A) is derived.
T
PD≧10{−0.655*(D
As shown in Examples 1 and 2, the optical fiber laser constituted by using the Yb-doped core optical fiber having a loss increment by photodarkening of 0.5 dB or less, the output of the light at a laser oscillation wavelength of 1060 nm was substantially reduced, even when laser oscillation was carried out over a long period of time. In order to obtain such the Yb-doped core optical fiber, by using the equation (B) obtained by setting a desired loss increment by photodarkening in the inequation (A) to TPD=0.5 dB, the Yb light absorption rates and the aluminum concentrations should satisfy the relationship in this equation.
0.5≧10{−0.655*(D
To confirm the effect of the inequation (B), using the Yb-doped core optical fiber having a structure as shown in
For the samples, A, B, and C, the Yb light absorption rates are all 600 dB/m, but the Al concentrations are different from each other. For the samples, D, E, and F, the Yb light absorption rates are all 800 dB/m, but the Al concentrations are different from each other. For the samples, G, H, and I, the Yb light absorption rates are all 1000 dB/m, but the Al concentrations are different from each other. In Comparative Examples, if the Yb light absorption rate and the Al concentration of each of the samples, A, D, G are substituted into the inequation (B), the right hand side of the inequation (B) is more than 0.5 in any of the fibers, and accordingly it does not satisfy the condition of the inequation (B). On the other hand, the samples, B, C, E, F, H, and I, that are the optical fibers of the present invention, all satisfy the condition of the inequation (B).
In a similar manner to Example 1, for the Yb-doped core optical fibers of the samples A through I, the loss increment by photodarkening at a wavelength of 810 nm was measured. The results are shown in Table 3. As seen from Table 3, the samples, B, C, E, F, H, and I, that are the optical fibers of the present invention, all have a loss increment by photodarkening of 0.5 dB or less. On the other hand, the samples, A, D, and G in Comparative Examples, all had a loss increment by photodarkening of more than 0.5 dB.
As clearly seen from Table 2, by doping aluminum and ytterbium in the core such that the concentration of aluminum contained in the core, and the peak light absorption rate of the light absorption band which appears at a wavelength of 976 nm in the light absorption band by ytterbium contained in the core satisfy the inequation (B), it is possible to obtain an Yb-doped core optical fiber having a loss increment by photodarkening at a wavelength of 810 nm of 0.5 dB or less.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2005-311002 | Oct 2005 | JP | national |
This application is a continuation application based on a PCT Patent Application No. PCT/JP2006/321385, filed Oct. 26, 2006, whose priority is claimed on Japanese Patent Application No. 2005-311002, filed on Oct. 26, 2005. The contents of both the PCT Application and the Japanese Application are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2006/321385 | Oct 2006 | US |
| Child | 12109612 | US |