The present invention relates to rare earth metal compounds, particularly rare earth metal compounds having a porous structure. The present invention also includes methods of making the porous rare earth metal compounds and methods of using the compounds of the present invention. The compounds of the present invention can be used to bind or absorb metals such as arsenic, selenium, antimony and metal ions such as arsenic III+ and V+. The compounds of the present invention may therefore find use in water filters or other devices or methods to remove metals and metal ions from fluids, especially water.
The compounds of the present invention are also useful for binding or absorbing anions such as phosphate in the gastrointestinal tract of mammals. Accordingly, one use of the compounds of the present invention is to treat high serum phosphate levels in patients with end-stage renal disease undergoing kidney dialysis. In this aspect, the compounds may be provided in a filter that is fluidically connected with a kidney dialysis machine such that the phosphate content in the blood is reduced after passing through the filter.
In another aspect, the compounds can be used to deliver a lanthanum or other rare-earth metal compound that will bind phosphate present in the gut and prevent its transfer into the bloodstream. Compounds of the present invention can also be used to deliver drugs or to act as a filter or absorber in the gastrointestinal tract or in the blood stream. For example, the materials can be used to deliver inorganic chemicals in the gastrointestinal tract or elsewhere.
It has been found that the porous particle structure and the high surface area are beneficial to high absorption rates of anions. Advantageously, these properties permit the compounds of the present invention to be used to bind phosphate directly in a filtering device fluidically connected with kidney dialysis equipment.
The use of rare earth hydrated oxides, particularly hydrated oxides of La, Ce, and Y to bind phosphate is disclosed in Japanese published patent application 61-004529 (1986). Similarly, U.S. Pat. No. 5,968,976 discloses a lanthanum carbonate hydrate to remove phosphate in the gastrointestinal tract and to treat hyperphosphatemia in patients with renal failure. It also shows that hydrated lanthanum carbonates with about 3 to 6 molecules of crystal water provide the highest removal rates. U.S. Pat. No. 6,322,895 discloses a form of silicon with micron-sized or nano-sized pores that can be used to release drugs slowly in the body. U.S. Pat. No. 5,782,792 discloses a method for the treatment of rheumatic arthritis where a “protein A immunoadsorbent” is placed on silica or another inert binder in a cartridge to physically remove antibodies from the bloodstream.
It has now unexpectedly been found that the specific surface area of compounds according to the present invention as measured by the BET method, varies depending on the method of preparation, and has a significant effect on the properties of the product. As a result, the specific properties of the resulting compound can be adjusted by varying one or more parameters in the method of making the compound. In this regard, the compounds of the present invention have a BET specific surface area of at least about 5 m2/g or 10 m2/g and may have a BET specific surface area of at least about 20 m2/g and alternatively may have a BET specific surface area of at least about 35 m2/g. In one embodiment, the compounds have a BET specific surface area within the range of about 10 m2/g and about 40 m2/g.
It has also been found that modifications in the preparation method of the rare earth compounds will create different entities, e.g. different kinds of hydrated or amorphous oxycarbonates or carbonate hydroxides rather than carbonates, and that these compounds have distinct and improved properties. It has also been found that modifications of the preparation method create different porous physical structures with improved properties.
The compounds of the present invention and in particular, the lanthanum compounds and more particularly the lanthanum oxycarbonates and lanthanum carbonate hydroxides of the present invention exhibit phosphate binding or removal of at least 40% of the initial concentration of phosphate after ten minutes. Desirably, the lanthanum compounds exhibit phosphate binding or removal of at least 60% of the initial concentration of phosphate after ten minutes. In other words, the lanthanum compounds and in particular, the lanthanum compounds and more particularly the lanthanum oxycarbonates and lanthanum carbonate hydroxides of the present invention exhibit a phosphate binding capacity of at least 45 mg of phosphate per gram of lanthanum compound. Suitably, the lanthanum compounds exhibit a phosphate binding capacity of at least 50 mg PO4/g of lanthanum compound, more suitably, a phosphate binding capacity of at least 75 mg PO4/g of lanthanum compound. Desirably, the lanthanum compounds exhibit a phosphate binding capacity of at least 100 mg PO4/g of lanthanum compound, more desirably, a phosphate binding capacity of at least 110 mg PO4/g of lanthanum compound.
In accordance with the present invention, rare earth metal compounds, and in particular, rare earth metal oxychlorides, carbonate hydroxides and oxycarbonates are provided. The oxycarbonates and carbonate hydroxides may be hydrated or anhydrous. These compounds may be produced according to the present invention as particles having a porous structure. The rare earth metal compound particles of the present invention may conveniently be produced within a controllable range of surface areas with resultant variable and controllable adsorption rates of ions.
The porous particles or porous structures of the present invention are made of nano-sized to micron-sized crystals with controllable surface areas. The rare earth oxychloride is desirably lanthanum oxychloride (LaOCl). The rare earth oxycarbonate hydrate is desirably lanthanum oxycarbonate hydrate (La2O(CO3)2.xH2O where x is from and including 2 to and including 4). This compound will further be referred to in this text as La2O(CO3)2.xH2O. The anhydrous rare earth oxycarbonate is desirably lanthanum oxycarbonate La2O2CO3 or La2CO5 of which several crystalline forms exist. The lower temperature form will be identified as La2O2CO3 and the form obtained at higher temperature or after a longer calcination time will be identified as La2CO5. The rare earth carbonate hydroxide is desirably lanthanum carbonate hydroxide LaCO3OH.
One skilled in the art, however, will understand that lanthanum oxycarbonate may be present as a mixture of the hydrate and the anhydrous form. In addition, the anhydrous lanthanum oxycarbonate may be present as a mixture of La2O2CO3 and La2CO5 and may be present in more than a single crystalline form.
One method of making the rare earth metal compound particles includes making a solution of rare earth metal chloride, subjecting the solution to a substantially total evaporation process using a spray dryer or other suitable equipment to form an intermediate product, and calcining the obtained intermediate product at a temperature between about 500° and about 1200° C. The product of the calcination step may be washed, filtered, and dried to make a suitable finished product. Optionally, the intermediate product may be milled in a horizontal or vertical pressure media mill to a desired surface area and then further spray dried or dried by other means to produce a powder that may be further washed and filtered.
An alternative method of making the rare earth metal compounds, particularly rare earth metal anhydrous oxycarbonate particles includes making a solution of rare earth metal acetate, subjecting the solution to a substantially total evaporation process using a spray dryer or other suitable equipment to make an intermediate product, and calcining the obtained intermediate product at a temperature between about 400° C. and about 700° C. The product of the calcination step may be washed, filtered, and dried to make a suitable finished product. Optionally, the intermediate product may be milled in a horizontal or vertical pressure media mill to a desired surface area, spray dried or dried by other means to produce a powder that may be washed, filtered, and dried.
Yet another method of making the rare earth metal compounds includes making rare earth metal oxycarbonate hydrate or rare earth carbonate hydroxide particles. The rare earth metal oxycarbonate hydrate or rare earth carbonate hydroxide particles can be made by successively making a solution of rare earth chloride, subjecting the solution to a slow, steady feed of a sodium carbonate solution at a temperature between about 30° and about 90° C. while mixing, then filtering and washing the precipitate to form a filter cake, then drying the filter cake at a temperature of about 100° to 120° C. to produce the desired rare earth oxycarbonate hydrate or rare earth carbonate hydroxide species. Optionally, the filter cake may be sequentially dried, slurried, and milled in a horizontal or vertical pressure media mill to a desired surface area, spray dried or dried by other means to produce a powder that may be washed, filtered, and dried.
Alternatively, the process for making rare earth metal oxycarbonate hydrate particles may be modified to produce anhydrous particles. This modification includes subjecting the dried filter cake to a thermal treatment at a specified temperature between about 400° C. to about 700° C. and for a specified time between 1 h and 48 h. Optionally, the product of the thermal treatment may be slurried and milled in a horizontal or vertical pressure media mill to a desired surface area, spray dried or dried by other means to produce a powder that may be washed, filtered, and dried.
In accordance with the present invention, compounds of the present invention may be used to treat patients with hyperphosphatemia. The compounds may be made into a form that may be delivered to a mammal and that may be used to remove phosphate from the gut or decrease phosphate absorption into the blood stream. For example, the compounds may be formulated to provide an orally ingestible form such as a liquid solution or suspension, a tablet, capsule, gelcap, or other suitable and known oral form. Accordingly, the present invention contemplates a method for treating hyperphosphatemia that comprises providing an effective amount of a compound of the present invention. Compounds made under different conditions will correspond to different oxycarbonates, carbonate hydroxides or oxychlorides, will have different surface areas, and will show differences in reaction rates with phosphate and different solubilization of lanthanum or another rare-earth metal into the gut. The present invention allows one to modify these properties according to the requirements of the treatment.
In another aspect of the present invention, compounds made according to this invention as a porous structure of sufficient mechanical strength may be placed in a device fluidically connected to a dialysis machine through which the blood flows, to directly remove phosphate by reaction of the rare-earth compound with phosphate in the bloodstream. The present invention therefore contemplates a device having an inlet and an outlet with one or more compounds of the present invention disposed between the inlet and the outlet. The present invention also contemplates a method of reducing the amount of phosphate in blood that comprises contacting the blood with one or more compounds of the present invention for a time sufficient to reduce the amount of phosphate in the blood.
In yet another aspect of the present invention, the compounds of the present invention may be used as a substrate for a filter having an inlet and outlet such that the compounds of the present invention are disposed between the inlet and the outlet. A fluid containing a metal, metal ion, phosphate or other ion may be passed from the inlet to contact the compounds of the present invention and through the outlet. Accordingly, in one aspect of the present invention a method of reducing the content of a metal in a fluid, for example water, comprises flowing the fluid through a filter that contains one or more compounds of the present invention to reduce the amount of metal present in the water.
Referring now to the drawings, the process of the present invention will be described. While the description will generally refer to lanthanum compounds, the use of lanthanum is merely for ease of description and is not intended to limit the invention and claims solely to lanthanum compounds. In fact, it is contemplated that the process and the compounds described in the present specification is equally applicable to rare earth metals other than lanthanum such as Ce and Y.
Turning now to
The lanthanum chloride solution is evaporated to form an intermediate product. The evaporation 20 is conducted under conditions to achieve substantially total evaporation. Desirably, the evaporation is conducted at a temperature higher than the boiling point of the feed solution (lanthanum chloride) but lower than the temperature where significant crystal growth occurs. The resulting intermediate product may be an amorphous solid formed as a thin film or may have a spherical shape or a shape as part of a sphere.
The terms “substantially total evaporation” or “substantially complete evaporation” as used in the specification and claims refer to evaporation such that the resulting solid intermediate contains less than 15% free water, desirably less than 10% free water, and more desirably less than 1% free water. The term “free water” is understood and means water that is not chemically bound and can be removed by heating at a temperature below 150° C. After substantially total evaporation or substantially complete evaporation, the intermediate product will have no visible moisture present.
The evaporation step may be conducted in a spray dryer. In this case, the intermediate product will consist of a structure of spheres or parts of spheres. The spray dryer generally operates at a discharge temperature between about 120° C. and about 500° C.
The intermediate product may then be calcined in any suitable calcination apparatus 30 by raising the temperature to a temperature between about 500° C. to about 1200° C. for a period of time from about 2 to about 24 h and then cooling to room temperature. The cooled product may be washed 40 by immersing it in water or dilute acid, to remove any water-soluble phase that may still be present after the calcination step 30.
The temperature and the length of time of the calcination process may be varied to adjust the particle size and the reactivity of the product. The particles resulting from calcination generally have a size between 1 and 1000 μm. The calcined particles consist of individual crystals, bound together in a structure with good physical strength and a porous structure. The individual crystals forming the particles generally have a size between 20 nm and 10 μm.
In accordance with another embodiment of the present invention as shown in
The feed solution is evaporated to form an intermediate product, which in this instance is titanium dioxide (TiO2). The evaporation 120 is conducted at a temperature higher than the boiling point of the feed solution but lower than the temperature where significant crystal growth occurs and to achieve substantially total evaporation. The resulting intermediate product may desirably be an amorphous solid formed as a thin film and may have a spherical shape or a shape as part of a sphere.
The intermediate product may then be calcined in any suitable calcination apparatus 130 by raising the temperature to a temperature between about 400° C. to about 1200° C. for a period of time from about 2 to about 24 h and then cooling to room temperature (25° C.). The cooled product is then washed 140 by immersing it in water or dilute acid, to remove traces of any water-soluble phase that may still be present after the calcination step.
The method of manufacture of the intermediate product according to the present invention can be adjusted and chosen to make a structure with the required particle size and porosity. For example, the evaporation step 120 and the calcination step 130 can be adjusted for this purpose. The particle size and porosity can be adjusted to make the structure of the intermediate product suitable to be used as an inert filter in the bloodstream.
The washed TiO2 product is then suspended or slurried in a solution of an inorganic compound. A desirable inorganic compound is a rare-earth or lanthanum compound, and in particular lanthanum chloride. This suspension of TiO2 in the inorganic compound solution is again subjected to total evaporation 160 under conditions in the same range as defined in step 120 and to achieve substantially total evaporation. In this regard, the evaporation steps 120 and 160 may be conducted in a spray drier. The inorganic compound will precipitate as a salt, an oxide, or an oxy-salt. If the inorganic compound is lanthanum chloride, the precipitated product will be lanthanum oxychloride. If the original compound is lanthanum acetate, the precipitated product will be lanthanum oxide.
The product of step 160 is further calcined 170 at a temperature between 500° and 1100° C. for a period of 2 to 24 h. The temperature and the time of the calcination process influence the properties and the particle size of the product. After the second calcination step 170, the product may be washed 180.
The resulting product can be described as crystals of lanthanum oxychloride or lanthanum oxide formed on a TiO2 substrate. The resulting product may be in the form of hollow thin-film spheres or parts of spheres. The spheres will have a size of about 1 μm to 1000 μm and will consist of a structure of individual bound particles. The individual particles have a size between 20 nm and 10 μm.
When the final product consists of crystals of lanthanum oxychloride on a TiO2 substrate, these crystals may be hydrated. It has been found that this product will effectively react with phosphate and bind it as an insoluble compound. It is believed that, if this final product is released in the human stomach and gastrointestinal tract, the product will bind the phosphate that is present and decrease the transfer of phosphate from the stomach and gastrointestinal tract to the blood stream. Therefore, the product of this invention may be used to limit the phosphorous content in the bloodstream of patients on kidney dialysis.
According to another embodiment of the present invention, a process for making anhydrous lanthanum oxycarbonate or lanthanum carbonate hydroxide is shown in
The lanthanum acetate solution is evaporated to form an intermediate product. The evaporation 220 is conducted at a temperature higher than the boiling point of the lanthanum acetate solution but lower than the temperature where significant crystal growth occurs and under conditions to achieve substantially total evaporation. The resulting intermediate product may desirably be an amorphous solid formed as a thin film and may have a spherical shape or a shape as part of a sphere.
The intermediate product may then be calcined in any suitable calcination apparatus 230 by raising the temperature to a temperature between about 400° C. to about 800° C. for a period of time from about 2 to about 24 h and then cooled to room temperature. The cooled product may be washed 240 by immersing it in water or dilute acid, to remove any water-soluble phase that may still be present after the calcination step. The temperature and the length of time of the calcination process may be varied to adjust the particle size and the reactivity of the product.
The particles resulting from the calcination generally have a size between 1 and 1000 μm. The calcined particles consist of individual crystals, bound together in a structure with good physical strength and a porous structure. The individual crystals generally have a size between 20 nm and 10 μm.
The products made by methods shown in
The particles made according to the process of the present invention, have the following common properties:
a. They have low solubility in aqueous solutions, especially serum and gastrointestinal fluid, compared to non-ceramic compounds.
b. Their hollow shape gives them a low bulk density compared to solid particles. Lower density particles are less likely to cause retention in the gastro-intestinal tract.
c. They have good phosphate binding kinetics. The observed kinetics are generally better than the commercial carbonate hydrates La2(CO3)3.H2O and La2(CO3)3.4H2O. In the case of lanthanum oxychloride, the relationship between the amount of phosphate bound or absorbed and time tends to be closer to linear than for commercial hydrated lanthanum carbonates. The initial reaction rate is lower but does not significantly decrease with time over an extended period. This behavior is defined as linear or substantially linear binding kinetics. This is probably an indication of more selective phosphate binding in the presence of other anions.
d. Properties a, b, and c, above are expected to lead to less gastro-intestinal tract complications than existing products.
e. Because of their particular structure and low solubility, the products of the present invention have the potential to be used in a filtration device placed directly in the bloodstream.
Different lanthanum oxycarbonates have been prepared by different methods. It has been found that, depending on the method of preparation, lanthanum oxycarbonate compounds with widely different reaction rates are obtained.
A desirable lanthanum carbonate hydroxide is LaCO3OH. This lanthanum carbonate hydroxide is preferred because it exhibits a relatively high rate of removal of phosphate. To determine the reactivity of the lanthanum carbonate hydroxide compound with respect to phosphate, the following procedure was used. A stock solution containing 13.75 g/l of anhydrous Na2HPO4 and 8.5 g/l of HCl is prepared. The stock solution is adjusted to pH 3 by the addition of concentrated HCl. 100 ml of the stock solution is placed in a beaker with a stirring bar. A sample of lanthanum carbonate hydroxide powder is added to the solution. The amount of lanthanum carbonate hydroxide powder is such that the amount of La in suspension is 3 times the stoichiometric amount needed to react completely with the phosphate. Samples of the suspension are taken at intervals, through a filter that separated all solids from the liquid. The liquid sample is analyzed for phosphorous.
Another preferred lanthanum carbonate is the anhydrous La oxycarbonate La2O2CO3. This compound is preferred because of its particularly high binding capacity for phosphate, expressed as mg PO4 removed/g of compound.
Samples of different oxycarbonates have been made by different methods as shown in Table 1 below.
For each sample, the surface area measured by the BET method and the fraction of phosphate remaining after 10 min of reaction have been tabulated. The table also shows the rate constant k1 corresponding to the initial rate of reaction of phosphate, assuming the reaction is first order in phosphate concentration. The rate constant k1 is defined by the following equation:
d[PO4]/dt=−k1[PO4]
where [PO4] is the phosphate concentration in solution (mol/liter), t is time (min) and k1 is the first order rate constant (min−1). The table gives the rate constant for the initial reaction rate, i.e. the rate constant calculated from the experimental points for the first minute of the reaction.
Without being bound by any theory, for the oxycarbonate, it is proposed that the observed dependence on surface area and phosphate concentration may be explained by a nucleophilic attack of the phosphate ion on the La atom in the oxycarbonate, with resultant formation of lanthanum phosphate LaPO4. For example, if the oxycarbonate is La2O2CO3, the reaction will be: ½La2O2CO3+PO43−+2H2O→LaPO4+½H2CO3+3OH−
If the rate is limited by the diffusion of the PO43− ion to the surface of the oxycarbonate and the available area of oxycarbonate, the observed relationship expressed in
In general, data obtained at increasing pH show a decrease of the reaction rate. This may be explained by the decrease in concentration of the hydronium ion (H3O+), which may catalyze the reaction by facilitating the formation of the carbonic acid molecule from the oxycarbonate. Or, it may be simply explained in that the compound is more soluble at lower pHs that higher pHs, which allows it to react faster.
Turning now to
The LaCl3 solution is placed in a well-stirred tank reactor. The LaCl3 solution is then heated to 80° C. A previously prepared analytical grade sodium carbonate is steadily added over a period of 2 hours with vigorous mixing. The mass of sodium carbonate required is calculated at 6 moles of sodium carbonate per 2 moles of LaCl3. When the required mass of sodium carbonate solution is added, the resultant slurry or suspension is allowed to cure for 2 hours at 80° C. The suspension is then filtered and washed with demineralized water to produce a clear filtrate. The filter cake is placed in a convection oven at 105° C. for 2 hours or until a stable weight is observed. The initial pH of the LaCl3 solution is 2, while the final pH of the suspension after cure is 5.5. A white powder is produced. The resultant powder is a lanthanum carbonate hydroxide.
Turning now to
The LaCl3 solution is placed in a well-stirred tank reactor. The LaCl3 solution is then heated to 80° C. A previously prepared analytical grade sodium carbonate is steadily added over 2 hours with vigorous mixing. The mass of sodium carbonate required is calculated at 6 moles of sodium carbonate per 2 moles of LaCl3. When the required mass of sodium carbonate solution is added the resultant slurry or suspension is allowed to cure for 2 hours at 80° C. The suspension is then washed and filtered removing NaCl (a byproduct of the reaction) to produce a clear filtrate. The filter cake is placed in a convection oven at 105° C. for 2 hours or until a stable weight is observed. The initial pH of the LaCl3 solution is 2.2, while the final pH of the suspension after cure is 5.5. A white lanthanum carbonate hydroxide powder is produced. Next the lanthanum carbonate hydroxide is placed in an alumina tray, which is placed in a high temperature muffle furnace. The white powder is heated to 500° C. and held at that temperature for 3 hours. Anhydrous La2C2O3 is formed.
Alternatively, the anhydrous lanthanum oxycarbonate formed as indicated in the previous paragraph may be heated at 500° C. for 15 to 24 h instead of 3 h or at 600° C. instead of 500° C. The resulting product has the same chemical formula, but shows a different pattern in an X-Ray diffraction scan and exhibits a higher physical strength and a lower surface area. The product corresponding to a higher temperature or a longer calcination time is defined here as La2CO5.
Turning now to
In yet another aspect of the present invention, the device 500 may be provided in a fluid stream so that a fluid containing a metal, metal ion, phosphate or other ion may be passed from the inlet 502 through the substrate 506 to contact the compounds of the present invention and out the outlet 504. Accordingly, in one aspect of the present invention a method of reducing the content of a metal in a fluid, for example water, comprises flowing the fluid through a device 500 that contains one or more compounds of the present invention to reduce the amount of metal present in the water.
The following examples are meant to illustrate but not limit the present invention.
An aqueous solution containing 100 g/l of La as lanthanum chloride is injected in a spray dryer with an outlet temperature of 250° C. The intermediate product corresponding to the spray-drying step is recovered in a bag filter. This intermediate product is calcined at 900° C. for 4 hours.
To determine the reactivity of the lanthanum compound with respect to phosphate, the following test was conducted. A stock solution containing 13.75 g/l of anhydrous Na2HPO4 and 8.5 g/l of HCl was prepared. The stock solution was adjusted to pH 3 by the addition of concentrated HCl. An amount of 100 ml of the stock solution was placed in a beaker with a stirring bar. The lanthanum oxychloride from above was added to the solution to form a suspension. The amount of lanthanum oxychloride was such that the amount of La in suspension was 3 times the stoichiometric amount needed to react completely with the phosphate. Samples of the suspension were taken at time intervals, through a filter that separated all solids from the liquid. The liquid sample was analyzed for phosphorous.
To determine the reactivity of a commercial lanthanum with respect to phosphate, the relevant portion of Example 1 was repeated under the same conditions, except that commercial lanthanum carbonate La2(CO3)3.H2O and La2(CO3)3.4H2O was used instead of the lanthanum oxychloride of the present invention. Additional curves on
An aqueous HCl solution having a volume of 334.75 ml and containing LaCl3 (lanthanum chloride) at a concentration of 29.2 wt % as La2O3 was added to a four liter beaker and heated to 80° C. with stirring. The initial pH of the LaCl3 solution was 2.2. Two hundred and sixty five ml of an aqueous solution containing 63.59 g of sodium carbonate (Na2CO3) was metered into the heated beaker using a small pump at a steady flow rate for 2 hours. Using a Buchner filtering apparatus fitted with filter paper, the filtrate was separated from the white powder product. The filter cake was mixed four times with 2 liters of distilled water and filtered to wash away the NaCl formed during the reaction. The washed filter cake was placed into a convection oven set at 105° C. for 2 hours, or until a stable weight was observed.
To determine the reactivity of the lanthanum compound with respect to phosphate, the following test was conducted. A stock solution containing 13.75 g/l of anhydrous Na2HPO4 and 8.5 g/l of HCl was prepared. The stock solution was adjusted to pH 3 by the addition of concentrated HCl. An amount of 100 ml of the stock solution was placed in a beaker with a stirring bar. Lanthanum carbonate hydroxide powder made as described above was added to the solution. The amount of lanthanum carbonate hydroxide powder was such that the amount of La in suspension was 3 times the stoichiometric amount needed to react completely with the phosphate. Samples of the suspension were taken at time intervals through a filter that separated all solids from the liquid. The liquid sample was analyzed for phosphorous.
To determine the reactivity of a commercial lanthanum with respect to phosphate, the second part of Example 3 was repeated under the same conditions, except that commercial lanthanum carbonate La2(CO3)3.H2O and La2(CO3)3.4H2O was used instead of the lanthanum oxychloride of the present invention.
An aqueous HCl solution having a volume of 334.75 ml and containing LaCl3 (lanthanum chloride) at a concentration of 29.2 wt % as La2O3 was added to a 4 liter beaker and heated to 80° C. with stirring. The initial pH of the LaCl3 solution was 2.2. Two hundred and sixty five ml of an aqueous solution containing 63.59 g of sodium carbonate (Na2CO3) was metered into the heated beaker using a small pump at a steady flow rate for 2 hours. Using a Buchner filtering apparatus fitted with filter paper the filtrate was separated from the white powder product. The filter cake was mixed four times with 2 liters of distilled water and filtered to wash away the NaCl formed during the reaction. The washed filter cake was placed into a convection oven set at 105° C. for 2 hours until a stable weight was observed. Finally, the lanthanum carbonate hydroxide was placed in an alumina tray in a muffle furnace. The furnace temperature was ramped to 500° C. and held at that temperature for 3 hours. The resultant product was determined to be anhydrous lanthanum oxycarbonate La2O2CO3.
The process was repeated three times. In one case, the surface area of the white powder was determined to be 26.95 m2/gm. In the other two instances, the surface area and reaction rate is shown in Table 1.
To determine the reactivity of this lanthanum compound with respect to phosphate, the following test was conducted. A stock solution containing 13.75 g/l of anhydrous Na2HPO4 and 8.5 g/l of HCl was prepared. The stock solution was adjusted to pH 3 by the addition of concentrated HCl. An amount of 100 ml of the stock solution was placed in a beaker with a stirring bar. Anhydrous lanthanum oxycarbonate made as described above, was added to the solution. The amount of anhydrous lanthanum oxycarbonate was such that the amount of La in suspension was 3 times the stoichiometric amount needed to react completely with the phosphate. Samples of the suspension were taken at intervals, through a filter that separated all solids from the liquid. The liquid sample was analyzed for phosphorous.
To determine the reactivity of a commercial lanthanum with respect to phosphate, the second part of Example 5 was repeated under the same conditions, except that commercial lanthanum carbonate La2(CO3)3.H2O and La2(CO3)3.4H2O was used instead of the La2O2CO3 of the present invention.
A solution containing 100 g/l of La as lanthanum acetate is injected in a spray-drier with an outlet temperature of 250° C. The intermediate product corresponding to the spray-drying step is recovered in a bag filter. This intermediate product is calcined at 600° C. for 4 hours.
To determine the reactivity of the lanthanum compound with respect to phosphate, the following test was conducted. A stock solution containing 13.75 g/l of anhydrous Na2HPO4 and 8.5 g/l of HCl was prepared. The stock solution was adjusted to pH 3 by the addition of concentrated HCl. An amount of 100 ml of the stock solution was placed in a beaker with a stirring bar. La2CO5 powder, made as described above, was added to the solution. The amount of lanthanum oxycarbonate was such that the amount of La in suspension was 3 times the stoichiometric amount needed to react completely with the phosphate. Samples of the suspension were taken at intervals through a filter that separated all solids from the liquid. The liquid sample was analyzed for phosphorous.
To determine the reactivity of a commercial lanthanum with respect to phosphate commercial lanthanum carbonate La2(CO3)3.H2O and La2(CO3)3.4H2O was used instead of the lanthanum oxycarbonate made according to the present invention as described above.
To a solution of titanium chloride or oxychloride containing 120 g/l Ti and 450 g/l Cl is added the equivalent of 2.2 g/l of sodium phosphate Na3PO4. The solution is injected in a spray dryer with an outlet temperature of 250° C. The spray dryer product is calcined at 1050° C. for 4 h. The product is subjected to two washing steps in 2 molar HCl and to two washing steps in water.
The product of Example 9 is re-slurried into a solution of lanthanum chloride containing 100 g/l La. The slurry contains approximately 30% TiO2 by weight. The slurry is spray dried in a spray dryer with an outlet temperature of 250° C. The product of the spray drier is further calcined at 800° C. for 5 h. It consists of a porous TiO2 structure with a coating of nano-sized lanthanum oxychloride.
An aqueous HCl solution having a volume of 334.75 ml and containing LaCl3 (lanthanum chloride) at a concentration of 29.2 wt % as La2O3 was added to a 4 liter beaker and heated to 80° C. with stirring. The initial pH of the LaCl3 solution was 2.2. Two hundred and sixty five ml of an aqueous solution containing 63.59 g of sodium carbonate (Na2CO3) was metered into the heated beaker using a small pump at a steady flow rate for 2 hours. Using a Buchner filtering apparatus fitted with filter paper the filtrate was separated from the white powder product. The filter cake was mixed four times, each with 2 liters of distilled water and filtered to wash away the NaCl formed during the reaction. The washed filter cake was placed into a convection oven set at 105° C. for 2 hours or until a stable weight was observed. The X-Ray diffraction pattern of the product shows that it consists of hydrated lanthanum carbonate hydroxide LaCO3OH. The surface area of the product was determined by the BET method. The test was repeated 3 times and slightly different surface areas and different reaction rates were obtained as shown in Table 1.
Six adult beagle dogs were dosed orally with capsules of LaCO3OH (compound A) or La2O2CO3 (compound B) in a cross-over design using a dose of 2250 mg elemental lanthanum twice daily (6 hours apart). The doses were administered 30 minutes after provision of food to the animals. At least 14 days washout was allowed between the crossover arms. Plasma was obtained pre-dose and 1.5, 3, 6, 7.5, 9, 12, 24, 36, 48, 60, and 72 hours after dosing and analyzed for lanthanum using ICP-MS. Urine was collected by catheterization before and approximately 24 hours after dosing and creatinine and phosphorus concentrations measured.
The tests led to reduction of urine phosphate excretion, a marker of phosphorous binding. Values of phosphate excretion in urine are shown in Table 2 below.
Plasma lanthanum exposure: Overall plasma lanthanum exposure in the dogs is summarized in Table 3 below. The plasma concentration curves are shown in
Groups of six adult Sprague-Dawley rats underwent ⅚th nephrectomy in two stages over a period of 2 weeks and were then allowed to recover for a further two weeks prior to being randomized for treatment. The groups received vehicle (0.5% w/v carboxymethyl cellulose), or compounds A or B suspended in vehicle, once daily for 14 days by oral lavage (10 ml/kg/day). The dose delivered 314 mg elemental lanthanum/kg/day. Dosing was carried out immediately before the dark (feeding) cycle on each day. Urine samples (24 hours) were collected prior to surgery, prior to the commencement of treatment, and twice weekly during the treatment period. Volume and phosphorus concentration were measured.
Feeding—During the acclimatization and surgery period, the animals were given Teklad phosphate sufficient diet (0.5% Ca, 0.3% P; Teklad No. TD85343), ad libitum. At the beginning of the treatment period, animals were pair fed based upon the average food consumption of the vehicle-treated animals the previous week.
⅚ Nephrectomy—After one week of acclimatization, all animals were subjected to ⅚ nephrectomy surgery. The surgery was performed in two stages. First, the two lower branches of the left renal artery were ligated. One week later, a right nephrectomy was performed. Prior to each surgery, animals were anesthetized with an intra-peritoneal injection of ketamine/xylazine mixture (Ketaject a 100 mg/ml and Xylaject at 20 mg/ml) administered at 10 ml/kg. After each surgery, 0.25 mg/kg Buprenorphine was administered for relief of post-surgical pain. After surgery, animals were allowed to stabilize for 2 weeks to beginning treatment.
The results showing urine phosphorus excretion are given in
Six young adult male Sprague-Dawley rats were randomly assigned to each group. Test items were lanthanum oxycarbonates La2O2CO3 and La2CO5 (compound B and compound C), each tested at 0.3 and 0.6% of diet. There was an additional negative control group receiving Sigmacell cellulose in place of the test item.
The test items were mixed thoroughly into Teklad 7012CM diet. All groups received equivalent amounts of dietary nutrients.
Rats were maintained in the animal facility for at least five days prior to use, housed individually in stainless steel hanging cages. On the first day of testing, they were placed individually in metabolic cages along with their test diet. Every 24 hours, their output of urine and feces was measured and collected and their general health visually assessed. The study continued for 4 days. Food consumption for each day of the study was recorded. Starting and ending animal weights were recorded.
Plasma samples were collected via retro-orbital bleeding from the control (I) and high-dose oxycarbonate groups, III and V. The rats were then euthanized with CO2 in accordance with the IACUC study protocol.
Urine samples were assayed for phosphorus, calcium, and creatinine concentration in a Hitachi 912 analyzer using Roche reagents. Urinary excretion of phosphorus per day was calculated for each rat from daily urine volume and phosphorus concentration. No significant changes were seen in animal weight, urine volume or creatinine excretion between groups. Food consumption was good for all groups.
Even though lanthanum dosage was relatively low compared to the amount of phosphate in the diet, phosphate excretion for 0.3 or 0.6% La added to the diet decreased as shown in Table 5 below. Table 5 shows average levels of urinary phosphate over days 2, 3, and 4 of the test. Urine phosphorus excretion is a marker of dietary phosphorous binding.
Tests were run to determine the binding efficiency of eight different compounds for twenty-four different elements. The compounds tested are given in Table 6.
The main objective of the tests was to investigate the efficiency at which the compounds bind arsenic and selenium, in view of their use in removing those elements from drinking water. Twenty-one different anions were also included to explore further possibilities. The tests were performed as follows:
The compounds given in Table 6 were added to water and a spike and were vigorously shaken at room temperature for 18 hrs. The samples were filtered and the filtrate analyzed for a suite of elements including Sb, As, Be, Cd, Ca, Cr, Co, Cu, Fe, Pb, Mg, Mn, Mo, Ni, Se, Tl, Ti, V, Zn, Al, Ba, B, Ag, and P.
The spike solution was made as follows:
1. In a 500 ml volumetric cylinder add 400 ml of de-ionized water.
2. Add standard solutions of the elements given above to make solutions containing approximately 1 mg/l of each element.
3. Dilute to 500 mls with de-ionized water.
The tests were conducted as follows:
1. Weigh 0.50 g of each compound into its own 50 ml centrifuge tube.
2. Add 30.0 ml of the spike solution to each.
3. Cap tightly and shake vigorously for 18 hrs.
4. Filter solution from each centrifuge tube through 0.2 .mu.m syringe filter. Obtain about 6 ml of filtrate.
5. Dilute filtrates 5:10 with 2% HNO3. Final Matrix is 1% HNO3.
6. Submit for analysis.
The results of the tests are given in Table 7.
The most efficient compounds for removing both arsenic and selenium appear to be the titanium-based compounds 5 and 6. The lanthanum oxycarbonates and carbonate hydroxides made according to the process of the present invention remove at least 90% of the arsenic. Their efficiency at removing Se is in the range 70 to 80%. Commercial lanthanum carbonate (4 in Table 6) is less effective.
The tests show that the lanthanum and titanium compounds made following the process of the present invention are also effective at removing Sb, Cr, Pb, Mo from solution. They also confirm the efficient removal of phosphorus discussed in the previous examples.
While the invention has been described in conjunction with specific embodiments, it is to be understood that many alternatives, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description. Accordingly, this invention is intended to embrace all such alternatives, modifications, and variations that fall within the spirit and scope of the appended claims.
This application is a divisional of U.S. application Ser. No. 14/491,305, filed Sep. 19, 2014, which is a continuation of U.S. application Ser. No. 14/149,299, filed Jan. 7, 2014, now U.S. Pat. No. 8,852,543, which is a divisional of U.S. application Ser. No. 12/643,059, filed Dec. 21, 2009, now U.S. Pat. No. 8,715,603, which is a continuation of U.S. application Ser. No. 11/217,001, filed Aug. 31, 2005, now abandoned, which is a continuation-in-part of U.S. application Ser. No. 10/444,774, filed May 23, 2003, now abandoned, which claims the benefit of the filing dates of U.S. Provisional Application No. 60/396,989, filed May 24, 2002, U.S. Provisional Application No. 60/403,868 Aug. 14, 2002, U.S. Provisional Application No. 60/430,284, filed Dec. 2, 2002, and U.S. Provisional Application No. 60/461,175, filed Apr. 8, 2003, the entire disclosures of which applications are hereby incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3692671 | Recht | Sep 1972 | A |
| 3768989 | Goetzinger et al. | Oct 1973 | A |
| 3922331 | MacDonald et al. | Nov 1975 | A |
| 3922333 | Mazdiyasni et al. | Nov 1975 | A |
| 4240048 | Zumsteg | Dec 1980 | A |
| 4454162 | Schanze | Jun 1984 | A |
| 4462970 | Pastor et al. | Jul 1984 | A |
| 4497785 | Tilley et al. | Feb 1985 | A |
| 4919902 | Bricker et al. | Apr 1990 | A |
| 4929787 | Cameron et al. | May 1990 | A |
| 5061670 | Forquy et al. | Oct 1991 | A |
| 5407560 | Miyawaki et al. | Apr 1995 | A |
| 5539000 | Leonard | Jul 1996 | A |
| 5683953 | Mills | Nov 1997 | A |
| 5782792 | Jones et al. | Jul 1998 | A |
| 5843477 | Alexander | Dec 1998 | A |
| 5968976 | Murrer et al. | Oct 1999 | A |
| 6146539 | Mills | Nov 2000 | A |
| 6197201 | Misra et al. | Mar 2001 | B1 |
| 6312604 | Denkewicz, Jr. et al. | Nov 2001 | B1 |
| 6322895 | Canham | Nov 2001 | B1 |
| 6338800 | Kulperger et al. | Jan 2002 | B1 |
| 6376479 | Knutson et al. | Apr 2002 | B1 |
| 6403523 | Cantrell et al. | Jun 2002 | B1 |
| 6521647 | Foster | Feb 2003 | B2 |
| 6849609 | Morrison | Feb 2005 | B2 |
| 6858203 | Holmes-Farley et al. | Feb 2005 | B2 |
| 7078059 | Atherton et al. | Jul 2006 | B2 |
| 7119120 | Jozefiak et al. | Oct 2006 | B2 |
| 7381428 | Ferdinando et al. | Jun 2008 | B2 |
| 7465465 | Haslam et al. | Dec 2008 | B2 |
| 7588782 | Moerck et al. | Sep 2009 | B2 |
| 8715603 | Moerck | May 2014 | B2 |
| 8852543 | Moerck et al. | Oct 2014 | B2 |
| 20020035151 | DeLuca | Mar 2002 | A1 |
| 20020051822 | Atherton et al. | May 2002 | A1 |
| 20030133902 | Holmes-Farley et al. | Jul 2003 | A1 |
| 20030235616 | Sowden et al. | Dec 2003 | A1 |
| 20040161474 | Moerck et al. | Aug 2004 | A1 |
| 20050079135 | Haslam et al. | Apr 2005 | A1 |
| 20050131138 | Connor et al. | Jun 2005 | A1 |
| 20050247628 | Moerck et al. | Nov 2005 | A1 |
| 20060002837 | Moerck et al. | Jan 2006 | A1 |
| 20060003018 | Moerck et al. | Jan 2006 | A1 |
| 20060083791 | Moerck et al. | Apr 2006 | A1 |
| 20060134225 | Moerck et al. | Jun 2006 | A1 |
| 20060153932 | Ferdinando et al. | Jul 2006 | A1 |
| 20060252907 | Shigematsu et al. | Nov 2006 | A1 |
| 20070149405 | Spitler | Jun 2007 | A1 |
| 20070259052 | Hallenbeck et al. | Nov 2007 | A1 |
| 20080058250 | Wren et al. | Mar 2008 | A1 |
| 20080069860 | Wren et al. | Mar 2008 | A1 |
| 20080089948 | Hallenbeck et al. | Apr 2008 | A1 |
| 20080226735 | Moerck et al. | Sep 2008 | A1 |
| 20100196485 | Moerck et al. | Aug 2010 | A1 |
| 20110123628 | Moerck et al. | May 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 601998 | Sep 1990 | AU |
| 0114462 | Jul 2003 | BR |
| 1184428 | Jun 1998 | CN |
| 1557982 | Dec 2004 | CN |
| 1688511 | Oct 2005 | CN |
| 101484798 | Jul 2009 | CN |
| 0604919 | Jul 1994 | EP |
| 1698233 | Sep 2006 | EP |
| 60-206448 | Oct 1985 | JP |
| 60-226414 | Nov 1985 | JP |
| 61-004529 | Jan 1986 | JP |
| 08-010610 | Jan 1996 | JP |
| 09-315865 | Dec 1997 | JP |
| 11-047765 | Feb 1999 | JP |
| 2002-018421 | Jan 2002 | JP |
| 2004-339336 | Dec 2004 | JP |
| 2006-514600 | May 2006 | JP |
| 2007-503400 | Feb 2007 | JP |
| 2008-516971 | May 2008 | JP |
| 2009-536356 | Oct 2009 | JP |
| 9630029 | Oct 1996 | WO |
| 9915189 | Apr 1999 | WO |
| 0200227 | Jan 2002 | WO |
| 0222258 | Mar 2002 | WO |
| 02060818 | Aug 2002 | WO |
| 03088976 | Oct 2003 | WO |
| 03094933 | Nov 2003 | WO |
| 2004016553 | Feb 2004 | WO |
| 2004050558 | Sep 2004 | WO |
| 2005018651 | Mar 2005 | WO |
| 2005042617 | May 2005 | WO |
| 2005049084 | Jun 2005 | WO |
| 2006015055 | Feb 2006 | WO |
| 2006044657 | Apr 2006 | WO |
| 2006050314 | May 2006 | WO |
| 2007022466 | Feb 2007 | WO |
| 2007130721 | Nov 2007 | WO |
| Entry |
|---|
| Puppies and Dogs for Sale .com, “Beagle Dog Breed Information,” http://puppiesanddogsforsale.com/dog—breed—info/Beagle.asp, accessed Sep. 2009. |
| Puppies and Dogs for Sale .com, “Great Dane Dog Breed Information,” http://puppiesanddogsforsale.com/dog—breed—info/GreatDane.asp, accessed Sep. 2009. |
| Supplementary European Search Report, EP 06801934, dated Jul. 4, 2009. |
| Cullel-Young M et al: “Lanthanum Carbonate Treatment of Hyperphosphatemia” Drugs of the Future, Prous Science, ES, vol. 28, No. 3, Mar. 1, 2003, (Mar. 1, 2003), pp. 224-228, XP009014864 ISSN: 0377-8282. |
| European Search Report, EP 05823302, dated Dec. 1, 2009. |
| Aldigier et al., Protection of Renal Function with ACE Inhibitors, 1998, Clinical Drug Investment, vol. 16(6), pp. 463-472. |
| Supplementary European Search Report, EP 06789875, dated Sep. 2, 2008. |
| Behets Geert J et al: Does the phosphate binder lanthanum carbonate affect bone in rats with chronic renal failure? Journal of the American Society of Nephrulogy vol. 15, No. 8, Aug. 2004 (Aug. 2004), pp. 2219-2228, XP002492560. |
| Magill-Lewis J: Coping with chronic kidney disease Drug Topics 20040927 us, vol. 148, No. 18, Sep. 27, 2004 (Sep. 27, 2004), XP008095473. |
| Office Action from corresponding Canadian Application No. 2,494,992 dated Mar. 25, 2011. |
| European Search Report, EP 10151585 dated Sep. 3, 2010. |
| Han, Zhaohui; Xu, Pu; Ratinac, K. R.; Lu, G. Q. ARC Centre for Functional Nanomaterials, University of Queensland, Australia. Journal of Crystal Growth (2004), 273(1-2), 248-257. |
| Sun, J.; Kyotani, T.; Tomita, A. Chem. Res. Inst. Non-Aqueous Solut., Tohoku Univ., Sendai, Japan. Journal of Solid State Chemistry (1986), 65(1), 94-9. |
| Christensen, A. Norlund. Dep. Inorg. Chem., Univ. Aarhus, Aarhus, Den. Acta Chemica Scandinavica (1947-1973) (1973), 27(8), 2973-82. |
| Shirsat, A. N.; Ali, M.; Kaimal, K. N. G.; Bharadwaj, S. R.; Das, D. Chemical Thermodynamics Section, Applied Chemistry Division, Bhabha Atomic Research Centre, Mumbai, India. Thermochimica Acta (2003), 399(1-2), 167-170. |
| Attfield, J. Paul; Ferey, Gerard. Chem. Crystallogr. Lab., Univ. Oxford, Oxford, UK. Journal of Solid State Chemistry (1989), 82(1), 132-8. |
| Office Action from U.S. Appl. No. 13/229,157 mailed Dec. 29, 2011. |
| Office Action from U.S. Appl. No. 13/018,894 mailed Jun. 13, 2011. |
| Office Action from corresponding Canadian Application No. 2,494,992 dated Dec. 19, 2011. |
| Office Action from Israel Application No. 166803 dated Sep. 19, 2012. |
| European Examination Report for Application No. EP 10151585.6 dated Aug. 31, 2012. |
| Office Action from U.S. Appl. No. 13/229,157 mailed Jul. 31, 2012. |
| Office Action from U.S. Appl. No. 12/643,059 mailed Jun. 12, 2012. |
| Office Action from Israel Application No. 166803 dated May 23, 2011. |
| Office Action from Israel Application No. 166803 dated Feb. 1, 2010. |
| Office Action from Canada Application No. 2,494,992 dated Apr. 29, 2010. |
| Office Action from Brazil Application No. PI313737-6 dated Jun. 21, 2011. |
| Canadian Office Action for Application No. 2,494,992 dated Nov. 21, 2012. |
| Office Action from U.S. Appl. No. 13/229,157 mailed Nov. 27, 2012. |
| Office Action from U.S. Appl. No. 13/229,157 mailed May 2, 2013. |
| U.S. Office Action from U.S. Appl. No. 12/643,059 dated Feb. 1, 2013. |
| U.S. Office Action for U.S. Appl. No. 10/444,774 dated Dec. 15, 2010. |
| U.S. Office Action for U.S. Appl. No. 12/814,716 dated Oct. 27, 2010. |
| U.S. Appl. No. 12/814,716, filed Jun. 14, 2010. |
| U.S. Office Action for U.S. Appl. No. 11/181,538 dated Oct. 30, 2009. |
| U.S. Office Action for U.S. Appl. No. 11/181,650 dated Dec. 29, 2008. |
| U.S. Office Action for U.S. Appl. No. 12/051,726 dated Sep. 29, 2011. |
| U.S. Office Action for U.S. Appl. No. 11/217,001 dated Jun. 23, 2009. |
| U.S. Appl. No. 12/051,726, filed Mar. 19, 2008. |
| Fiddler, G. et al. (Apr. 2003). Lanthanum Carbonate has a Good Safety Profile Following Concomifanf Adminisfrafion wifh Mefoprolol and has No Clinically Significanf Effecf on ifs Pharmacokinetics, Poster presented at the National Kidney Foundation Clinical Meeting, Dallas, Texas, Apr. 2-6, 2003, 1 page. |
| Fiddler, G. et al. (Apr. 2003). “Lanthanum Carbonate has No Effect on the Pharmacokientics of Digoxin and Can be Adminisfered Safely in Combinafion,” Posfer presenfed af fhe Nafional Kidney Foundation Clinical Meeting, Dallas, Texas, Apr. 2-6, 2003, 1 page. |
| Finn, W. et al. (Apr. 2003). ‘Efficacy and Safety of Long-Term Treatment with Lanthanum Carbonafe—A Novel Phosphafe-Binding Agenf,’ Posfer presenfed af fhe Nafional Kidney Foundation Clinical Meeting, Dallas, Texas, Apr. 2-6, 2003, 1 page. |
| Finn, W. F. et al. (Sep. 1999). Resulfs of a Randomized Dose-Ranging, Placebo Controlled Study of Lanthanum Carbonate for Reduction of Serum Phosphate in Chronic Renal Failure Pafienfs Receiving Hemodialysis, Journal of the American Society of Nephrology, 32nd Annual Meefing and 1999 Renal Week, Nov. 1-8, 1999, Miami Beach, Florida, 10:261A, Abstract No. A1317. |
| Graff, L. et al. (Sep. 1995). A Possible Non-Aluminum Oral Phosphafe Binder? A Comparative Study on Dietary Phosphorus Absorption, Research Communications in Molecular Pathology and Pharmacology 89(3) 373-388. |
| Joy, M. S. et al., ‘Safety Profile of Lanthanum Carbonate in Hemodialysis Patients: Results from a Phase III Study,’ Journal of the American Society of Nephrology, 10:388A (1999), Abstract No. A1997. |
| Larson, E. A. et al. (1986). Phosphate Binding Gels: Balancing Phosphate Adsorption and Aluminum Toxicity, Kidney International29:1 131-11350. (Abstract only obtained from Medline, 86308884, 1 page). |
| Rudnic, E. R. et al. (1990). Oral Solid Dosage Forms, Chapter 89 In Remington: Pharmaceutical Sciences. 18th Edition, pp. 1633-1658. |
| Stewart, J. ef al. (Sep. 2002). Adminisfrafion of a Novel Phosphafe Binder, FosrenolJM, wifh Food is Associated wifh Good Tolerabilify and Low Systemic Absorption, Journal of the American Society of Nephrology, Oct. 30-Nov. 4, 2002, Philadelphia, Pennsylvania, 13:386A, Abstracf No. SA-P0601. |
| U.S. Office Action mailed May 12, 2008, for U.S. Appl. No. 11/181,650, filed Jul. 13, 2005, 10 pages. |
| U.S. Office Action mailed Dec. 4, 2007, for U.S. Appl. No. 10/444,774, filed May 23, 2003, 9 pages. |
| U.S. Office Acfion mailed Sep. 8, 2006, for U.S. Appl. No. 10/444,774, filed May 23, 2003, 8 pages. |
| Joy, M. S. et al. (Sep. 2002). FosrenolTM, a Novel, Non-Aluminum, Non-Calcium Phosphate Binder, has a Good Safety and Efficacy Profile in the Long-Term Treatment of Hyperphosphatemia in Hemodialysis Patients, Journal of the American Society of Nephrology, Oct. 30-Nov. 4, 2002, Philadelphia, Pennsylvania, 1 3:386A, Abstract No. SA-P0600. |
| Medline abstract 86308884 (1986). |
| Yamaguchi et al., Abstract for “Formation and Decomposition of Lanthanum Monoxocarbonate,” Zeitschrift fuer Anorganiche and Allgemeine Chemie, 514, 1984, pp. 205-212, obtained from Chemabs “Online”, Chemical Abstracts Service, Columbus OH; 1 pg. |
| Holsa et al., Abstract for “Preparation, Thermal Stability and Luminescence Properties of Selected Rare Earth Oxycarbonates,” Thermochimica Acta, 190(2), pp. 335-343, 1991, Chemabs “Online”, Chemical Abstracts Service, Columbus, OH; 1 pg. |
| Olafsen et al., Abstract for “Synthesis of Rare Earth Oxide Carbonates and Thermal Stability of Nd202C03 II,” Journal of Materials Chemistry, 9(10), 1999, pp. 2697-2702, obtained from Database Chemabs “Online,” Chemical Abstracts Service, Columbus,OH, 1 pg. |
| Behets et al., “An Assessment of the Effects of Lanthanum on Bone in a Chronic Renal Failure (CFR) Rat Model,” Journal of the American Society of Nephrology, Miami, FL; Nov. 1999. |
| Behets et al., “Effects of the Phosphate Binder Renagel.RTM. (Sevelamer) on Biochemical Parameters and Bone Histology in a Chronic Renal Failure (CRF) Rat Model,” Journal of the American Society of Nephrology, Miami, FL; Nov. 1999. |
| DeBroe et al., “Lanthanum Carbonate (Fosrenol.TM.), A New Agent in the Treatment of Hyperphosphatemia in End-State Renal Failure,” University Hospital of Antwerp, Belgium, 2002. |
| Shire Pharmaceutical Development Ltd., Programme for “New Directions in the Treatment of Hyperphosphatemia,” European Renal Association Conference, Jul. 14, 2002, Copenhagen, Denmark. |
| Damment et al., “Bone Mineralisation Defect with High Doses of Phosphate Binders in Uraemic Rats—An Artefact of Phosphate Depletion?,” European Renal Association Conference, Jul. 14, 2002, Copenhagen, Denmark. |
| Sack et al., “Fosrenal.TM. (Lanthanum Carbonate) is Well Tolerated in Patients Requiring Hemodialysis: Results of a Phase I Clinical Trial,” ASN 35.sup.th Annual Meeting & Scientific Exposition, Nov. 2002, Philadelphia, PA. |
| Hutchison, A.J., “The Novel, Non-Aluminum, Non-Calcium Phosphate Binder, Lanthanum Carbonate (Fosrenol.TM.), is an Effective Treatment for Hyperphosphatemia and has a Good Safety Profile,” ASN 35.sup.th Annual Meeting & Scientific Exposition, Nov. 2002, Philadelphia, PA. |
| Finn et al., “Fosrenol.TM., a Novel, Non-Calcium, Non-Aluminum Phosphate Binder, Has a Good Safety and Efficacy Profile in the Long-Term Treatment of Hyperphosphatemia in Hemodialysis Patients,” ASN 35.sup.th Annual Meeting & Scientific Exposition,Nov. 2002. |
| D'Haese et al., “The Effects of Lanthanum Carbonate (Fosrenol.TM.) and Calcium Carbonate on Renal Bone Disease in Dialysis Patients,” National Kidney Foundation Clinical Meeting, Apr. 2003, Dallas, TX. |
| Hutchison et al., “Safety and Efficacy of Lanthanum Carbonate for Treatment of Hyperphosphatemia in Haemodialysis Patients over 12 months,” National Kidney Foundation Clinical Meeting, Apr. 2003, Dallas, TX. |
| Fiddler et al., “Lanthanum Carbonate is Well Tolerated When Administered with Warfarin and Has No Effect on its Pharmacokinetics,” National Kidney Foundation Clinical Meeting, Apr. 2003, Dallas, TX. |
| Hutchinson et al., “Safety, Tolerability and Efficacy of Lanthanum Carbonate in Haemodialysis Patients: a 12-Month Study,” ERA-EDTA World Congress of Nephrology, Jun. 2003, Berlin, Germany. |
| Dictionary of Chemistry and Chemical Technology. (1999). p. 2240-2242. (English translation attached, 13 pages). |
| European Search Report mailed Aug. 16, 2006, for EP 06000002.3 filed Aug. 8, 2003, 10 pages. |
| International Preliminary Examination Report mailed Jan. 3, 2005, PCT Application No. PCT/US03/25192 filed Aug. 8, 2003, 7 pages. |
| International Search Report and Written Opinion mailed Jul. 20, 2007, for PCT Application No. PCT/US06/32415 filed Aug. 17, 2006, 8 pages. |
| International Search Report and Written Opinion mailed Jun. 3, 2008, for PCT Application No. PCT/US06/32492 filed Aug. 17, 2006, 8 pages. |
| International Search Report and Written Opinion mailed Mar. 21, 2008, for PCT Application No. PCT/US05/37015 filed Oct. 13, 2005, 16 pages. |
| International Search Report mailed Jun. 1, 2004, for PCT Application No. PCT/US03/38235 filed Dec. 2, 2003, 6 pages. |
| International Search Report mailed Jun. 7, 2004, for PCT Application No. PCT/US03/25192 filed Aug. 8, 2003, 11 pages. |
| International Written Opinion mailed Mar. 21, 2005, PCT Application No. PCT/US03/38235 filed Dec. 2, 2003, 5 pages. |
| Joy, M. S. et al. (2003). “Randomized, Double-Blind, Placebo-Controlled, Dose Titration, Phase III Study Assessing Efficacy and Tolerability of Lanthanum Carbonate: A New Phosphate Binder for the Treatment of Hyperphosphatemia,” American Journal ofKidney Diseases 42:96-107. (Abstract only obtained from Chemical Abstracts HCAplus, 2003:602063, 1 page). |
| Nagashima, K. et al. (Jan. 1973). “The Synthesis of Crystalline Rare Earth Carbonates,” Bulletin of the Chemical Society of Japan 46(1):152-156. |
| Olafsen, A. et al. (2001). “On the Crystal Structure of Ln.sub.2O.sub.2CO.sub.3 II (Ln=La and Nd),” Journal of Solid State Chemistry 158:14-24 (Abstract only obtained from Chemical Abstracts HCAplus, 2001:260955, 1 pages). |
| Partial European Search Report mailed Apr. 18, 2006, for EP 06000002.3 filed Aug. 8, 2003, 7 pages. |
| U.S. Office Action mailed Feb. 16, 2006, for U.S. Appl. No. 10/444,774, filed May 23, 2003, 7 pages. |
| U.S. Office Action mailed May 25, 2007, for U.S. Appl. No. 10/444,774, filed May 23, 2003, 10 pages. |
| U.S. Office Action mailed Sep. 17, 2008, for U.S. Appl. No. 11/181,609, filed Jul. 13, 2005, 6 pages. |
| U.S. Office Action mailed Sep. 8, 2006, for U.S. Appl. No. 10/444,774, filed May 23, 2003, 8 pages. |
| U.S. Appl. No. 11/576,785, filed Apr. 5, 2007 for Moerck et al. |
| U.S. Appl. No. 12/051,726, filed Mar. 19, 2008 for Moerck et al. |
| U.S. Appl. No. 12/197,157, filed Aug. 22, 2008 for Moerck et al. |
| Office Action from Corresponding Japanese Application No. 2005-502047, dated Oct. 19, 2009. |
| U.S. Ex part Quayle Action for U.S. Appl. No. 13/106,637 dated Sep. 6, 2013. |
| Canadian Office Action for Application No. 2,494,992 dated Aug. 26, 2013. |
| Brazilian Written Opinion and Examination Report for Application No. PI0313737-6 dated Aug. 23, 2013. |
| Taiwanese Office Action and Search Report for Application No. 100116778 dated Oct. 14, 2013. |
| U.S. Office Action for U.S. Appl. No. 13/229,157 dated Oct. 18, 2013. |
| Chinese Office Action for Application No. 201180023076.0 dated Nov. 5, 2013. |
| Olsbye et al. “A comparative study of coprecipitated BaC03/La20n(C03)m catalysts for the oxidative coupling of methane.” Catalysis Today, 13 (1992) 603-608. |
| Australian Patent Report for Application No. 2011252983 dated Mar. 6, 2014. |
| U.S. Appl. No. 14/104,663, filed Dec. 12, 2013. |
| Israeli Office Action for Application No. 166803 dated Jan. 7, 2014. |
| Notice of Allowance for Canadian Application No. 2,494,992 dated Feb. 13, 2014. |
| U.S. Notice of Allowability for U.S. Appl. No. 12/643,059 dated Oct. 9, 2013. |
| U.S. Office Action for U.S. Appl. No. 12/643,059 dated Jun. 28, 2011. |
| U.S. Office Action for U.S. Appl. No. 13/229,157 dated Apr. 4, 2014. |
| International Preliminary Report on Patentability for Application No. PCT/US2011/036317 dated Nov. 13, 2012. |
| European Communication for Application No. 11721201.9 dated Jan. 31, 2013. |
| U.S. Notice of Allowability for U.S. Appl. No. 14/149,299 dated May 29, 2014. |
| Chinese Office Action for Application No. 201180023076.0 dated Jun. 30, 2014. |
| U.S. Office Action for U.S. Appl. No. 13/106,637 dated Jun. 30, 2014. |
| Australian Notice of Acceptance for Application No. 2011252983 dated Jul. 10, 2014. |
| Liu S et al: “Synthesis and structure characterization of hydrated lanthanum carbonate”, Huanan Ligong Oaxue Xuebao—Journal of South China University of Technology, Guangzhou, CH, vol. 25, No. 10, Oct. 1, 1997 (Oct. 1, 1997), pp. 23-26, XP008116865. |
| Olafsen, Anja et al: “Synthesis of rare earth oxide carbonates and thermal stability of Nd20 2C03 II”, XP002280167, Journal of Materials Chemistry, 9(10), 2697-2702, 1999. |
| European Office Action for Application No. 10151585.6 dated Jan. 7, 2015. |
| Chinese Office Action for application 201180023076.0 dated Jan. 26, 2015. |
| Russian Office Action for Application No. 2012146818 dated Mar. 2, 2015. |
| U.S. Office Action for U.S. Appl. No. 14/491,305 dated Feb. 18, 2015. |
| Brazilian Office Action for Application No. PI0313737-6 dated Mar. 26, 2015. |
| Japanese Office Action for Application No. 2013-510310 dated Jun. 30, 2015. |
| Guilhaume et al. “Oxygen storage capacity in Perovskite-related oxides: The role of overstoichiometric oxygen in three-way catalysis.” Catalysis and Automotive Pollution Control IV, Studies in Surface Science and Catalysis, vol. 116, pp. 581-589, 1998. |
| Mzareulishvili et al.; Study of the Interaction of Lanthanum Nitrate with Alkali Metal and Ammonium Carbonates, Chemical Abstracts, Jun. 30, 1986, 81-84 (English Summary on p. 84). |
| Altair Nanotechnologies Press Release, “RenaZorb™, Phosphate Lowering Drug for Kidney Dialysis Patients, Shows Promising Laboratory Results” [retrieved on Jun. 3, 2011] Retrieved from Internet: http://www.altaimano.com/profi lesli nvestor/ResLibrary View .asp ?ResLibrary ID=2808&GoTopage=32&Category= 1951 &BzID=546 Published on Oct. 25, 2002. |
| Joy, M. S. et al., ‘Results of a Randomized, Phase III, Dose-Titration, Parallel Croup Sfudy of Lanthanum Carbonafe for Reduction and Mainfenance of Serum Phosphafe in Chronic Hemodialysis Patients,’ Journal of the American Society of Nephrology, 10; 2:388A (1999), Abstract No. A1996. |
| International Search Report and Written Opinion, PCT/US2011/036317, dated Aug. 2, 2011. |
| U.S. Appl. No. 13/106,637, filed May 12, 2011. |
| Altair Nanotechnologies Press Release, “Altair Nanotechnologies Reports Results of Testing and Likely Patient Dosing for Phosphate Binding Dialysis Drug” [retrieved on Jun. 3, 2011], Retrieved from Internet: http://www.altairnano.com/profiles/investor/ResLibraryView.asp?ResLibrary ID=7038& Topage=23&Category=1951&BzID=546, Published on Sep. 1, 2004. |
| HCAPLUS abstract 2003:602063 (2003). |
| HCAPLUS abstract 2001:260955 (2001). |
| Zhang, Youjin; Han, Kaidong; Cheng, Tao; Fang, Zhiyong. Department of Chemistry, University of Science and Technology of China, Hefei, Peop. Rep. China. Inorganic Chemistry (Washington, DC, United States) (2007), 46 (11), 4713-4717. |
| Li, Zhonghao; Zhang, Jianling; Du, Jimin; Gao, Haixiang; Gao, Yanan; Mu, Tiancheng; Han, Buxing. Center for Molecular Sciences, Institute of Chemistry, Key Lab of Photochemistry, Chinese Academy of Sciences, Beijing, Peop. Rep. China. Materials Letters (2005), 59(8-9), 963-965. |
| Number | Date | Country | |
|---|---|---|---|
| 20160008396 A1 | Jan 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60461175 | Apr 2003 | US | |
| 60430284 | Dec 2002 | US | |
| 60403868 | Aug 2002 | US | |
| 60396989 | May 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14491305 | Sep 2014 | US |
| Child | 14860023 | US | |
| Parent | 12643059 | Dec 2009 | US |
| Child | 14149299 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14149299 | Jan 2014 | US |
| Child | 14491305 | US | |
| Parent | 11217001 | Aug 2005 | US |
| Child | 12643059 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10444774 | May 2003 | US |
| Child | 11217001 | US |