Patent Grant
10629343
The present disclosure relates to a rare earth permanent magnet containing neodymium, iron, and boron.
As a technique to enhance a magnet property of a rare earth permanent magnet containing neodymium (Nd), iron (Fe), and boron (B), there is a magnet in which Fe is substituted with Co (PTL 1). PTL 1 describes that a coercive force Hc, residual magnetic flux density Br, maximum energy product BHmax, and so on of permanent magnets in which Fe is substituted with other atoms were measured exhaustively, thereby showing enhancement of the magnetic property of the above-described permanent magnet.
Furthermore, PTL 2 discloses a rare earth sintered magnet that contains, by percent by weight: R (where R is at least one type of rare earth elements including Y and Nd accounts for 50 atom % or more of R): 25 to 35%; B: 0.8 to 1.5%; M (at least one type selected from Ti, Cr, Ga, Mn, Co, Ni, Cu, Zn, Nb, and Al) when necessary: 8% or less; and the remainder T (Fe or Fe and Co).
As another suggestion to enhance the magnetic property of the rare earth permanent magnet, there is a nanocomposite magnet having a two-phase composite structure in which a hard magnet phase of nanoparticles consisting of Nd, Fe, and B forms a core and a soft magnet phase of specified nanoparticles forms a shell. Regarding the above-mentioned nanocomposite magnet, particularly when the shell is formed by covering the core with a grain boundary composed of very fine particles of a soft magnetic substance whose particle size is 5 nm or less, a good exchange interaction occurs between the hard magnet phase and the soft magnet phase, that is, the core and the shell, thereby making it possible to enhance saturation magnetization.
PTL 3 discloses a nanocomposite magnet in which Nd2Fe14B compound particles form a core and Fe particles form a shell. The saturation magnetization of the nanocomposite magnet is further enhanced by using FeCo alloy nanoparticles which exhibit high saturation magnetization as a shell constituent. PTL 4 discloses a nanocomposite magnet in which a core of an NdFeB hard magnet phase is covered with a shell of an FeCo soft magnet phase.
PTL 5 discloses an anisotropy bulk nanocomposite rare earth permanent magnet regarding which a composition of a magnetically hard phase as defined by atom percentage is RxT100-x-yMy (where in this expression, R is selected from rare earths, yttrium, scandium, or a combination of these elements; T is selected from one or more types of transition metals; M is selected from elements of group IIIA, elements of group IVA, elements of group VA, or a combination of these elements; x is larger than a stoichiometric amount of R in a corresponding rare-earth transition-metal compound; and y is 0 to approximately 25) and at least one type of a magnetically-soft phase includes at least one type of a soft magnetic material containing Fe, Co, or N.
However, with the nanocomposite rare earth permanent magnet disclosed in PTL 5, a soft phase is formed by a metallurgical method. Accordingly, the particle size of particles which form the soft phase is large. So, there is a possibility that a sufficient exchange interaction may not be obtained. Furthermore, if reducing power is weak, alloy nanoparticles tend to easily become just an aggregate of single-layer nanoparticles and a desired nanocomposite structure cannot be obtained. Therefore, it is presumed that the magnetic property of the above-described nanocomposite rare earth permanent magnet may not be enhanced effectively.
NPL 1 discloses a method for manufacturing FeCo nanoparticles at a high temperature. However, a coercive force Hcj of the relevant Nd2Fe14B particles manufactured at a high temperature is not good.
However, there is a further demand for enhancement of the magnetic property of the rare earth permanent magnet. It is an object of the present disclosure to enhance the magnetic property of the rare earth permanent magnet whose main phase is a compound containing Nd, Fe, and B.
As a result of earnest examinations of constituent atoms of Nd2Fe14B particles in order to achieve the above-described object, the inventors of the present disclosure conceived the idea of enhancing a magnetic moment of neodymium atoms in the Nd2Fe14B particles, thereby enhancing the magnetic property of the permanent magnet. Specifically speaking, the inventors conceived the idea of further enhancing the magnetic moment of the above-mentioned neodymium atoms by substituting boron contained in Nd2Fe14B particles with other atoms.
In addition, a function effect of a case where other atoms which can be substituted for boron are contained in the particles was examined. As a result, they found the possibility of further enhancing the magnetic moment of the relevant particles as such other atoms are substituted for iron.
The inventors of the present disclosure advanced the examinations and found that the coercive force Hcj can be enhanced by forming a grain boundary phase in the Nd2Fe14B particles. The inventors of the present disclosure have completed the present disclosure on the basis of the above conceived ideas and findings.
The present disclosure is a rare earth permanent magnet with a compound represented by an expression (1) indicated below as a main phase. In the expression (1), M represents an element selected from any one of cobalt, beryllium, lithium, aluminum, and silicon and x is a value that satisfies 0.01≤x≤0.25, and more preferably 0.02≤x≤0.25.
[Chem. 1]
Nd2Fe14B(1-x)Mx (1)
The present disclosure includes a rare earth permanent magnet with a compound represented by an expression (2) indicated below as a main phase. In the expression (2), M and L are elements selected from any one of cobalt, beryllium, lithium, aluminum, and silicon, y is 0<y<2, x is 0.01≤x≤0.25, and x and y satisfy 0.01<(x+y)<2.25. More preferably, y is 0.1<y<1.2, x is 0.02≤x≤0.25, and x and y satisfy 0.12<(x+y)<1.45.
[Chem. 2]
Nd2Fe(14-y)LyB(1-x)Mx (2)
The present disclosure is a rare earth permanent magnet whose main phase has an Nd—Fe—B layer and an Fe layer periodically and part of boron contained in the Nd—Fe—B layer is substituted with any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon.
The above-mentioned Nd—Fe—B layer should preferably contain terbium. Furthermore, the Nd—Fe—B layer should preferably contain any one or more types of elements of praseodymium and dysprosium.
From another point of view, the present disclosure is a rare earth permanent magnet including a main phase containing neodymium, iron, and boron and further containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon. A content of neodymium is 20 to 35 wt %, a content of boron is 0.80 to 0.99 wt %, and a total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon relative to a total weight of the rare earth permanent magnet of the present disclosure.
The present disclosure includes a rare earth permanent magnet further containing terbium. In that case, it is preferable that the content of neodymium should be 20 to 35 wt %, the content of boron should be 0.80 to 0.99 wt %, the total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon should be 0.8 to 1.0 wt %, and the content of terbium should be 2.0 to 10.0 wt % relative to the total weight of the rare earth permanent magnet of the present disclosure.
The present disclosure includes a rare earth permanent magnet equipped with a main phase further containing any one or more types of elements of praseodymium and dysprosium. It is preferable that the content of neodymium should be 15 to 40 wt %, the content of praseodymium should be 5 to 20 wt %, the content of boron should be 0.80 to 0.99 wt %, the total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon should be 0.8 to 1.0 wt %, and the content of terbium should be 2.0 to 10.0 wt % relative to the total weight of the rare earth permanent magnet containing the praseodymium.
The present disclosure includes a rare earth permanent magnet including the above-described main phase and a grain boundary phase containing any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium. The grain boundary phase should preferably contain at least 0.1 to 0.4% aluminum and 0.01 to 0.1% copper by percent by weight.
According to the present disclosure, the main phase should preferably contain a crystal containing neodymium, iron, boron and containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, and a sintered particle size D50 of the crystal be 2 to 25 μm. Furthermore, a sintered density of the rare earth permanent magnet of the present disclosure should preferably be 6 to 8 g/cm3.
The present disclosure containing neodymium, iron, and boron, further containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, and containing terbium has a magnetic property that satisfies any one or more conditions of a group consisting of mc1 and mc2 mentioned below at a temperature condition of 20° C. Mc1 represents the magnetic property indicating that a residual magnetic flux density Br is 12.90 kG or more. Mc2 represents the magnetic property indicating that a coercive force Hcj is 27.90 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc3 and mc4 mentioned below at a temperature condition of 100° C. Mc3 represents the magnetic property indicating that the residual magnetic flux density Br is 11.80 kG or more. Mc4 represents the magnetic property indicating that the coercive force Hcj is 17.40 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc5 and mc6 mentioned below at a temperature condition of 160° C. Mc5 represents the magnetic property indicating that the residual magnetic flux density Br is 10.80 kG or more. Mc6 represents the magnetic property indicating that the coercive force Hcj is 10.50 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc7 and mc8 mentioned below at a temperature condition of 200° C. Mc7 represents the magnetic property indicating that the residual magnetic flux density Br is 10.10 kG or more. Mc8 represents the magnetic property indicating that the coercive force Hcj is 6.60 kOe or more.
The present disclosure containing neodymium, iron, and boron, further containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, and containing terbium, and additionally containing any one or more types of elements of praseodymium and dysprosium has a magnetic property that satisfies any one or more conditions of a group consisting of mc9 and mc10 mentioned below at a temperature condition of 20° C. Mc9 represents the magnetic property indicating that the residual magnetic flux density Br is 12.50 kG or more. Mc10 represents the magnetic property indicating that the coercive force Hcj is 21.20 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc11 and mc12 mentioned below at a temperature condition of 100° C. Mc11 represents the magnetic property indicating that the residual magnetic flux density Br is 11.60 kG or more. Mc12 represents the magnetic property indicating that the coercive force Hcj is 11.80 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc13 and mc14 mentioned below at a temperature condition of 160° C. Mc13 represents the magnetic property indicating that the residual magnetic flux density Br is 10.60 kG or more. Mc14 represents the magnetic property indicating that the coercive force Hcj is 6.20 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc15 and mc16 mentioned below at a temperature condition of 200° C. Mc15 represents the magnetic property indicating that the residual magnetic flux density Br is 9.60 kG or more. Mc16 represents the magnetic property indicating that the coercive force Hcj is 3.80 kOe or more.
The present disclosure containing the above-specified main phase and any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium has a magnetic property that satisfies any one or more conditions of a group consisting of mc17 and mc18 mentioned below at a temperature condition of 20° C. Mc17 represents the magnetic property indicating that the residual magnetic flux density Br is 11.40 kG or more. Mc18 represents the magnetic property indicating that the coercive force Hcj is 28.00 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc19 and mc20 mentioned below at a temperature condition of 100° C. Mc19 represents the magnetic property indicating that the residual magnetic flux density Br is 10.60 kG or more. Mc20 represents the magnetic property indicating that the coercive force Hcj is 17.70 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc21 and mc22 mentioned below at a temperature condition of 160° C. Mc21 represents the magnetic property indicating that the residual magnetic flux density Br is 9.80 kG or more. Mc22 represents the magnetic property indicating that the coercive force Hcj is 10.60 kOe or more.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc23 and mc24 mentioned below at a temperature condition of 200° C. Mc23 represents the magnetic property indicating that the residual magnetic flux density Br is 9.00 kG or more. Mc24 represents the magnetic property indicating that the coercive force Hcj is 6.70 kOe or more.
Tensile strength of the rare earth permanent magnet according to the present disclosure is 80 MPa or more, preferably 100 MPa or more, and more preferably 150 MPa or more.
The present disclosure includes a rare earth permanent magnet manufacturing method. Specifically speaking, the rare earth permanent magnet manufacturing method includes a heat treatment step of: retaining a raw material compound which contains neodymium, iron, and boron, contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, contains terbium, and contains any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium, at a main-phase-forming temperature and then lowering the main-phase-forming temperature to a grain-boundary-phase-forming temperature, thereby forming a main phase containing neodymium, iron, and boron, containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, and containing terbium; and further retaining the raw material compound at the grain-boundary-phase-forming temperature, thereby forming a grain boundary phase containing any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium.
The present disclosure includes the rare earth permanent magnet manufacturing method including the heat treatment step of: retaining a raw material compound which contains neodymium, praseodymium, iron, and boron, contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, contains any one or more types of elements of terbium and dysprosium, and contains any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium, at the main-phase-forming temperature and then lowering the main-phase-forming temperature to the grain-boundary-phase-forming temperature, thereby forming the main phase containing neodymium, praseodymium, iron, and boron, and further containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, and containing any one or more types of elements of terbium and dysprosium; and retaining the raw material compound at the grain-boundary-phase-forming temperature, thereby forming the grain boundary phase containing any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium.
In the heat treatment step, the raw material compound should preferably be retained at 1000 to 1200° C. for 3 to 5 hours, then retained at 880 to 920° C. for 4 to 5 hours, and then retained at 480 to 520° C. for 3 to 5 hours.
The present disclosure can enhance the magnetic moment by using a compound having the above-described specified crystal structure as a main phase. As a result, the coercive force Hcj, the residual magnetic flux density Br, and the maximum energy product BHmax of the rare earth permanent magnet of the present disclosure are enhanced.
Examinations on the crystal of the Nd2Fe14B particles by the inventors of the present disclosure will be described in order to explain the present disclosure. The inventors of the present disclosure calculated the magnetic moment of the Nd2Fe14B particles by the first-principles pseudopotential method using a plane wave basis and obtained the results illustrated in
Furthermore, the inventors of the present disclosure calculated a local electron density of states at s orbitals and p orbitals of B atoms in the Nd2Fe14B particles and obtained the results shown in
Conventionally, it is believed that the boron in the Nd2Fe14B particles is involved in stabilization of the crystal structure. However, the above-described results of
Table 1 is a table of magnetic moments calculated based on atomic locations obtained by a neutron diffraction method (O. Isnard et. al J. Appl. Phys. 78 (1995) 1892-1898). Table 1 shows that the magnetic moment of the ND atoms in the Nd2Fe14B particles is less than 4μB and the magnetic moment is small. It is presumed that one of the reasons for such reduction of the magnetic moment would be covalent bondings between the Nd atoms and the B atoms in the crystal structure of the relevant particles and donation of part of f electrons in the Nd atoms to the s orbitals of the boron atoms. As a result, it is believed that the Nd atoms in the particles lose their magnetism.
Through the above-described examinations, the inventors of the present disclosure obtained findings that the B atoms are polarized and are involved in suppression of magnetism of the Nd2Fe14B particles. Based on such findings, the inventors of the present disclosure conceived the idea of enhancing the magnetism of the particles by substituting the B atoms with other atoms in the crystal of the Nd2Fe14B particles.
The rare earth permanent magnet of the present disclosure has a compound represented by an expression (1) indicated below as a main phase. According to the present disclosure, the number of atoms in the relevant compound in a unit lattice accounts for 90 to 98 at % of the number of atoms of the entire particles. However, as long as the function effect of the present disclosure is obtained, the present disclosure permits the main phase to contain impurities which are not the above-described compound.
[Chem. 3]
Nd2Fe14B(1-x)Mx (1)
In the expression (1), M represents an element selected from any one of cobalt, beryllium, lithium, aluminum, and silicon. Furthermore, x satisfies 0.01≤x≤0.25, and more preferably 0.03≤x≤0.25.
The present disclosure is composed so that part of boron in the conventional Nd2Fe14B crystal is substituted with a specified element. Accordingly, the present disclosure can inhibit transfer of f electrons of neodymium to other atoms. Therefore, the number of unpaired electrons of neodymium can be easily maintained and the magnetic moment of the Nd atoms can be enhanced as compared to the conventional crystal. In the expression (1), in a case of x<0.01, the magnetic moment reduces. In a case of x>0.25, the crystal structure cannot be maintained, so that synthesis cannot be performed.
The present disclosure is designed so that part of boron contained in the main phase is substituted with one or more atoms selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon. Accordingly, the present disclosure inhibits reduction of unpaired electrons and enhances the magnetic property.
The present disclosure may be composed so that part of boron and part of iron in the conventional Nd2Fe14B crystal are substituted with a specified element. Such a composition can be represented by the following expression (2).
[Chem. 4]
Nd2Fe(14-y)LyB(1-x)Mx (2)
In the expression (2), M and L are elements selected from any one of cobalt, beryllium, lithium, aluminum, and silicon, y is 0<y<2, x is 0.0≤x≤0.25, and x and y satisfy 0.01<(x+y)<2.25. More preferably, y is 0.1<y<1.2, x is 0.02≤x≤0.25, and x and y satisfy 0.12<(x+y)<1.45.
Also in this case, the magnetic moment of the Nd atoms can be enhanced as compared to the conventional crystal. Furthermore, the magnetic moment of the Fe atoms can be enhanced based on conventionally-known findings. In the expression (2), in a case of the magnetic moment of the iron atoms reduces. In a case of x<0.01 or x>0.25, the magnetic moment of the neodymium atoms reduces. When x, y, and x+y are out of their respective specified ranges, the magnetic moments of the iron atoms and the neodymium atoms reduce.
Since the compound of the main phase according to the present disclosure has the composition represented by the expression (1) or the expression (2), the magnetic moment of the Nd atoms contained in that compound is larger than the magnetic moment of the Nd atoms in the Nd2Fe14B crystal. The magnetic moment of the Nd atoms according to the present disclosure is at least larger than 2.70μB and should preferably be 3.75 to 3.85μB, and more preferably 3.80 to 3.85μB.
Specifically, the present disclosure is designed to cause the magnetism of the Nd atoms to be expressed, it has a better magnetic property than magnetism derived from the Fe atoms and the Nd atoms. The magnetic property of the present disclosure can be evaluated based on the coercive force Hcj and the residual magnetic flux density Br. The magnetic property of the present disclosure is enhanced by 40 to 50% as compared to the rare earth permanent magnet composed of the conventional Nd2Fe14B crystal.
The compound constituting the main phase of the present disclosure contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon and contains neodymium, iron, and boron.
Regarding the element M, an element whose wave function fits in the relevant interstice 103 and which has a smaller atomic radius than that of boron, for example, any one cobalt, beryllium, lithium, aluminum, and silicon, is selected as appropriate. The compound for which such an element is used as a raw material constituent has a structure in which part of the B atoms is substituted with M atoms as compared to the structure of the conventionally known Nd2Fe14B crystal, and has a tetragonal crystal structure with P4/mnm and lattice constants a=8.81 Å and c=12.21 Å.
As the element M of the expression (1), any one or more elements of cobalt, beryllium, lithium, aluminum, and silicon should preferably be selected. Cobalt is more preferable.
A content ratio of constituent elements of the above-described compound on a basis of the number of atoms is neodymium (Nd):iron (Fe):boron (B):M=2:14:(1−x):x, and x should preferably satisfy 0.01≤x≤0.25 and should more preferably satisfy 0.03≤x≤0.25. Part of B can be naturally substituted with another element M by sintering an alloy of the above-described content ratio.
As the element M is contained in the relevant compound particulates by 1 to 25 at % relative to the number of neodymium atoms, electrons donated from the Nd atoms to the B atoms in the compound are reduced, thereby making it possible to enhance the magnetic moment of the Nd atoms. As a result, the present disclosure exhibits a high magnetic moment and a good magnetic property.
Since the iron of the above-described basic skeleton has a high density, any element whose atomic radius is extremely larger than that of the iron atoms can hardly be selected as the element L. However, it is presumed that if the wave functions of atoms in the elements are appropriately superimposed on each other, the relevant atoms in the elements may be easily substituted for the iron atoms in the crystal. An explanation about the element M as illustrated in
Any one or more of cobalt, beryllium, lithium, aluminum, and silicon should preferably be selected as the element M and the element L in the expression (2) which satisfies the above-described conditions. Cobalt is more preferable. Normally the same element is selected as M and L, but different elements may be selected as M and L. From the viewpoint of simplifying a manufacturing process, the same element should preferably be selected. From the viewpoint of enhancing the magnetic moment of the Fe atoms, at least the cobalt should preferably be selected as M.
A content ratio of constituent elements of the compound represented by the expression (2) on a basis of the number of atoms is neodymium (Nd):iron (Fe):L:boron (B):M=2:(14−y):y:(1−x):x. It is preferable that y should satisfy 0<y<2, and more preferably 0.1<y<1.2. It is preferable that x should satisfy 0.01≤x≤0.25, and more preferably 0.02≤x≤0.25. Furthermore, x and y should preferably satisfy 0.01<(x+y)<2.25, and more preferably 0.12<(x+y)<1.45.
As the compound represented by the expression (2) contains the element M by 1 to 25 at % relative to the number of Nd atoms in the relevant compound particulates, electrons donated from the Nd atoms to the B atoms in the compound are reduced, thereby making it possible to enhance the magnetic moment of the Nd atoms. As a result, the present disclosure exhibits a high magnetic moment and a good magnetic property.
The rare earth permanent magnet of the present disclosure has the Nd—Fe—B layer and the Fe layer periodically and part of boron contained in the Nd—Fe—B layer is substituted with any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon.
According to the present disclosure, the Nd—Fe—B layer should preferably contain terbium. Furthermore, the Nd—Fe—B layer should preferably contain any one or more types of elements of praseodymium and dysprosium. An aspect where terbium, praseodymium, and dysprosium exist at whatever sites in the Nd—Fe—B layer also falls under the crystal structure of the main phase according to the present disclosure. Specifically speaking, each one of terbium, praseodymium, and dysprosium may be substituted with Nd or Fe and may enter the interstices.
If the present disclosure explained above is summarized from the viewpoint of the constituents of the main phase according to the present disclosure described above, we can say, in other words, that the main phase contains neodymium, iron, and boron and further contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon.
The rare earth permanent magnet of the present disclosure contains iron as its main constituent more than any other constituents and the content of iron is sometimes expressed as the remainder relative to the other constituents. Regarding the other constituents relative to the total weight of the rare earth permanent magnet, the content of neodymium should preferably be 20 to 35 wt % and more preferably 22 to 33 wt %. The content of boron should preferably be 0.80 to 0.99 wt % and more preferably 0.82 to 0.98 wt %. The total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon is 0.8 to 1.0 wt %. As a result, the present disclosure can obtain a good residual magnetic flux density Br.
The present disclosure should preferably contain terbium in addition to the above-described constituents. The present disclosure can enhance the coercive force Hcj of the rare earth permanent magnet by containing terbium in addition to any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon.
The compound containing terbium can be represented by the following expression (3) or expression (4).
[Chem. 5]
Nd(2-z)TbzFe14B(1-x)Mx (3)
In the above-described expression (3), M represents an element selected from any one of cobalt, beryllium, lithium, aluminum, and silicon, x satisfies 0.01≤x≤0.25, and z satisfies 1<z<1.8. In the expression (3), in a case of x<0.01, the magnetic moment of the neodymium atoms reduces. In a case of x>0.25, the crystal structure becomes unstable. In a case of z≤1, this causes a reduction of holding force. In a case of z≥0.8, the residual magnetic flux density reduces.
[Chem. 6]
Nd(2-z)TbzFe(14-y)LyB(1-x)Mx (4)
In the above-described expression (4), each of M and L is an element selected from any one of cobalt, beryllium, lithium, aluminum, and silicon, y is 0<y<2, x is 0.01≤x≤0.25, and x and y satisfy 0.01<(x+y)<2.25. Furthermore, z is 1<z<1.8. When x, y, z, and x+y are out of the above-described ranges, the residual magnetic flux density and the coercive force decrease.
The rare earth permanent magnet of the present disclosure containing the terbium contains the iron as its main constituent more than any other constituents and the content of iron is sometimes expressed as the remainder relative to the other constituents. Regarding the other constituents relative to the total weight of the rare earth permanent magnet, the content of neodymium should preferably be 20 to 35 wt % and more preferably 22 to 33 wt %. The content of boron should preferably be 0.80 to 0.99 wt % and more preferably 0.82 to 0.98 wt %. The total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon is 0.8 to 1.0 wt %. The content of terbium is 2.0 to 10.0 wt % and more preferably 2.5 to 4.5 wt %. As a result, the present disclosure can obtain a good residual magnetic flux density Br.
When the present disclosure contains neodymium, iron, and boron and further contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon and contains terbium, it has a magnetic property that that satisfies any one or more conditions of a group consisting of mc1 and mc2 at a temperature condition of 20° C.
Mc1 represents the magnetic property indicating that the residual magnetic flux density Br is 12.90 kG or more. The residual magnetic flux density Br should more preferably be 13.00 kG or more as mc1. Mc2 represents the magnetic property indicating that the coercive force Hcj is 27.90 kOe or more. The coercive force Hcj should more preferably be 28.20 kOe or more as mc2. Incidentally, any magnetic property of the present disclosure can be measured by using a pulse-excitation-type magnetic property measurement apparatus with a specimen temperature variator which is conventionally known.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc3 and mc4 at a temperature condition of 100° C. Mc3 represents the magnetic property indicating that the residual magnetic flux density Br is 11.80 kG or more. The residual magnetic flux density Br should more preferably be 11.85 kG or more as mc3. Mc4 represents the magnetic property indicating that the coercive force Hcj is 17.40 kOe or more. The coercive force Hcj should more preferably be 18.20 kOe or more as mc4.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc5 and mc6 at a temperature condition of 160° C. Mc5 represents the magnetic property indicating that the residual magnetic flux density Br is 10.80 kG or more. The residual magnetic flux density Br should more preferably be 10.95 kG or more as mc5. Mc6 represents the magnetic property indicating that the coercive force Hcj is 10.50 kOe or more. The coercive force Hcj should more preferably be 11.00 kOe or more as mc6.
The present disclosure containing the above-mentioned elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc7 and mc8 at a temperature condition of 200° C. Mc7 represents the magnetic property indicating that the residual magnetic flux density Br is 10.10 kG or more. The residual magnetic flux density Br should more preferably be 10.14 kG or more as mc7. Mc8 represents the magnetic property indicating that the coercive force Hcj is 6.60 kOe or more. The coercive force Hcj should more preferably be 6.90 kOe or more as mc8. According to the present disclosure, both the residual magnetic flux density Br and the coercive force Hcj are good. The magnetic property of this present disclosure does not degrease even at a temperature condition higher than a room temperature.
The present disclosure may contain elements, such as praseodymium and dysprosium, that contributes to enhancement of the magnetic property. It is possible to manufacture the rare earth permanent magnet of the present disclosure, which exhibits the excellent magnetic property, at low cost by containing the praseodymium. The praseodymium contained in the present disclosure is mainly substituted with neodymium. It can also be dispersed in other areas within the crystal structure. The ratio of neodymium to praseodymium contained in the present disclosure on a basis of the number of atoms is 80:20 to 70:30.
From the viewpoint of the low cost, it is preferable that a proportion of the praseodymium should be larger and a proportion of the neodymium should be smaller; however, if the proportion of the neodymium becomes less than 70 on the basis of the above-described ratio of the number of atoms, the possibility of decrease of the residual magnetic flux density Br increases.
It is possible to enhance the magnetic property by containing dysprosium in the same manner as in the case of containing terbium. The dysprosium contained in the present disclosure is substituted for the iron. The dysprosium may be used solely as a substituent element of the iron or together with the terbium. Incidentally, besides being substituted for the iron, the elements such as terbium and praseodymium may be dispersed in other areas within the crystal structure.
The compound containing praseodymium and dysprosium can be represented by the following expression (5) or expression (6).
[Chem. 7]
Nd(2-z)R1z1R2z2Fe14B(1-z)Mx (5)
In the above-described expression (5), M represents an element selected from any one of cobalt, beryllium, lithium, aluminum, and silicon and x satisfies 0.01≤x≤0.25. R1 represents praseodymium and R2 represents any one or more types of elements of terbium and dysprosium. Z, z1, and z2 satisfy z=z1+z2, 1<z<1.8, and 0<z1<1.8. When x, z, z1, and z2 are out of the above-described ranges, the residual magnetic flux density and the coercive force decrease.
[Chem. 8]
Nd(2-z)R1z1R2z2Fe(14-y)LyB(1-x) (6)
In the above-described expression (6), M and L represent elements selected from any one of cobalt, beryllium, lithium, aluminum, and silicon, y is 0<y<2, x is, 0.01≤x≤0.25, and x and y satisfy 0.01<(x+y)<2.25. Z is 1<z<1.8. R1 represents praseodymium and R2 represents any one or more types of elements of terbium and dysprosium. Z, z1, and z2 satisfy z=z1+z2, 1<z<1.8, and 0<z1<1.8. When x, y, x+y, z, z1, and z2 are out of the above-described ranges, the crystal structure cannot be maintained.
The main phase of the present disclosure has crystals containing neodymium, iron, and boron and containing any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon. A sintered particle size D50 of the crystals should preferably be 2 to 25 μm, more preferably 3 to 15 μm, and further more preferably 3 to 11 μm. Particularly when the crystals are refined to 3 to 6 μm, the obtained particles are preferable because they exhibit a good magnetic property even if the content of terbium is reduced.
Regarding the present disclosure, D50 is a median diameter in cumulative distribution of an alloy particulate group on a volume basis. D50 can be measured by known methods using a laser-diffraction-type particle-size distribution measuring apparatus. All numerical values indicating the “powder particle size,” “sintered particle size,” and “particle size” are D50.
A raw material alloy used for the present disclosure forms crystals which become the main phase by a heat treatment step. The sintered particle size D50 of such crystals is 110 to 300%, more specifically 110 to 180%, of the powder particle size D50 of the raw material alloy. An example of a method for forming the crystals whose sintered particle size is within the above-described preferable range can include a method of molding the raw material alloy of an appropriate power particle size corresponding to the desired sintered particle size, magnetizing the raw material alloy, and applying a heat treatment to the raw material alloy. The powder particle size can be adjusted by known methods by using, for example, a ball mill or a jet mill.
According to the present disclosure, as the sintered density of the main phase becomes higher, the residual magnetic flux density becomes larger. Therefore, the sintered density should preferably be 6.0 g/cm3 or more and a larger sintered density of 7.5 g/cm3 or more is more preferable. However, the sintered density is determined based on the powder particle size of the raw material alloy, and a processing temperature, a sintering temperature, and an aging temperature in the heat treatment step. Therefore, according to the present disclosure, because of the raw material alloy which can be prepared and conditions of the heat treatment step, the sintered density is 6.0 to 8.0 g/cm3, more preferably 7.0 to 7.9 g/cm3, and further preferably 7.2 to 7.7 g/cm3. When the sintered density is less than 7.0 g/cm3, it is inappropriate for a magnet.
When the present disclosure contains neodymium, iron, and boron, further contains any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon, contains terbium, and additionally contains any one or more types of praseodymium and dysprosium, it has a magnetic property that satisfies any one or more conditions of a group consisting of mc9 and mc10 at a temperature condition of 20° C.
Mc9 represents the magnetic property indicating that the residual magnetic flux density Br is 12.50 kG or more. The residual magnetic flux density Br should more preferably be 13.20 kG or more as mc9. Mc10 represents the magnetic property indicating that the coercive force Hcj is 21.20 kOe or more. The coercive force Hcj should more preferably be 29.50 kOe or more as mc10.
The present disclosure containing the above-described elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc11 and mc12 at a temperature condition of 100° C. Mc11 represents the magnetic property indicating that the residual magnetic flux density Br is 11.60 kG or more. The residual magnetic flux density Br should more preferably be 12.30 kG or more as mc11. Mc12 represents the magnetic property indicating that the coercive force Hcj is 11.80 kOe or more. The coercive force Hcj should more preferably be 18.00 kOe or more as mc12.
The present disclosure containing the above-described elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc13 and mc14 at a temperature condition of 160° C. Mc13 represents the magnetic property indicating that the residual magnetic flux density Br is 10.60 kG or more. The residual magnetic flux density Br should more preferably be 11.20 kG or more as mc13. Mc14 represents the magnetic property indicating that the coercive force Hcj is 6.20 kOe or more. The coercive force Hcj should more preferably be 10.00 kOe or more as mc14.
The present disclosure containing the above-described elements has a magnetic property that satisfies any one or more conditions of a group consisting of mc15 and mc16 at a temperature condition of 200° C. Mc15 represents the magnetic property indicating that the residual magnetic flux density Br is 9.60 kG or more. The residual magnetic flux density Br should more preferably be 10.30 kG or more as mc15. Mc16 represents the magnetic property indicating that the coercive force Hcj is 3.80 kOe or more. The coercive force Hcj should more preferably be 6.00 kOe or more as mc16.
According to the present disclosure containing the above-described elements, both the residual magnetic flux density Br and the coercive force Hcj are good. The magnetic property of this disclosure does not decrease even at a temperature condition higher than a room temperature.
The rare earth permanent magnet of the present disclosure containing any one or more types of elements selected from a group consisting of praseodymium, terbium, dysprosium, and so on contains iron as its main constituent more than any other constituents and the content of iron is sometimes expressed as the remainder relative to the other constituents.
Regarding the other constituents relative to the total weight of the rare earth permanent magnet, the content of neodymium should preferably be 15 to 40 wt % and more preferably 20 to 35 wt %. The content of praseodymium is 5 to 20 wt % and more preferably 5 to 15 wt %. The content of boron should preferably be 0.80 to 0.99 wt % and more preferably 0.82 to 0.98 wt %. The total content of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon is 0.8 to 1.0 wt %. The content of any one or more types of elements of terbium and dysprosium is 2.0 to 10.0 wt % and more preferably 2.5 to 4.5 wt %. As a result, the present disclosure can obtain a good residual magnetic flux density Br.
In addition to the above-described specified main phase, the present disclosure should preferably include a grain boundary phase containing any one or more types of elements selected from a group consisting of aluminum, copper, niobium, zirconium, titanium, and gallium. Incidentally, the elements which form the grain boundary phase can be also dispersed in the main phase as appropriate. Since the amount of dispersion is very small, it is not reflected in the preferable content of each constituent in the above-described main phase.
Regarding a preferable content of the grain boundary phase constituents according to the present disclosure by percent by weight, the content of aluminum should be 0.1 to 0.4% and the content of copper should be 0.01 to 0.1%. More preferably, the content of aluminum should be 0.2 to 0.3% and the content of copper should be 0.02 to 0.09%. When zirconium is to be added, a preferable content of zirconium by percent by weight relative to the total weight of the rare earth permanent magnet should be 0.004 to 0.04% and more preferably 0.01 to 0.04%.
Regarding the content of each constituent for the present disclosure including the main phase and the grain boundary phase, the iron is contained as its main constituent more than any other constituents and the content of iron is sometimes expressed as the remainder relative to the other constituents. Regarding the content of other constituents relative to the total weight of the present disclosure by percent by weight, it is preferable that the content of neodymium should be 20 to 35%, the content of boron should be 0.80 to 0.99%, the total amount of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon should be 0.8 to 1.0%, and the content of terbium should be 2.0 to 10.0%; and in addition to the above constituents, the content of aluminum should be 0.1 to 0.4% and the consent of copper should be 0.01 to 0.1%.
As an example of a more preferable consent of the constituents other than the iron as described above by percent by weight, it is preferable that at least the content of neodymium should be 22 to 33%, the content of boron should be 0.82 to 0.98%, the total amount of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon should be 0.8 to 1.0%, and the content of terbium should be 2.6 to 5.4%; and in addition to the above constituents, the content of aluminum should be 0.2 to 0.3% and the content of copper should be 0.02 to 0.09%.
As another example of preferable content, it is preferable that the content of neodymium should be 15 to 40 wt %, the content of praseodymium should be 5 to 20 wt %, the content of terbium should be 2.0 to 10.0 wt %, the content of boron should be 0.80 to 0.99 wt %, and the total amount of any one or more types of elements selected from a group consisting of cobalt, beryllium, lithium, aluminum, and silicon should be 0.8 to 1.0 wt %; and in addition to the above constituents, the content of aluminum should be 0.1 to 0.4 wt % and the content of copper should be 0.01 to 0.1 wt %.
The present disclosure exhibits excellent heat resistance and has a high residual magnetic flux density Br, a high coercive force Hcj, and a large maximum energy product BHmax even under the high-temperature condition. The magnetic property of the present disclosure regarding which the sintered particle size D50 of the main phase is 3 to 11 μm is summarized below by each temperature condition. Incidentally, the magnetic property described below can be further enhanced by refining the crystal particle size of the main phase.
Regarding the magnetic property at the temperature condition 20° C., the residual magnetic flux density Br is distributed at 11.40 kG or more, preferably at 12.50 kG or more, and more preferably at 12.90 kG or more. The coercive force Hcj is distributed at 21.20 kOe or more, and preferably at 27.90 kOe or more. The maximum energy product BHmax is distributed at 31.00 MGOe or more, and more preferably at 40.10 MGOe or more.
Regarding the magnetic property at the temperature condition 100° C. according to the present disclosure, the residual magnetic flux density Br is distributed at least at approximately 10.00 to 12.00 kG. In addition, the residual magnetic flux density Br should preferably be distributed at 10.60 kG or more, and more preferably at 11.80 kG or more. The coercive force Hcj is distributed at 11.80 kOe or more and at 17.00 to 19.00 kOe. The coercive force Hcj should preferably be distributed at 17.40 kOe or more. The maximum energy product BHmax is distributed at least at 33.00 to 35.00 MGOe. In addition, the maximum energy product BHmax should preferably be distributed at 27.10 MGOe or more, more preferably at 36.80 MGOe or more.
Regarding the magnetic property at the temperature condition 160° C. according to the present disclosure, the residual magnetic flux density Br is distributed at least at approximately 9.000 to 11.00 kG. In addition, the residual magnetic flux density Br should preferably be distributed at 9.80 kG or more, and more preferably at 10.80 kG or more. The coercive force Hcj is distributed at 6.200 kOe or more and at 11.00 to 12.00 kOe. The coercive force Hcj should preferably be distributed at 10.50 kOe or more. The maximum energy product BHmax is distributed at least at 27.00 to 29.00 MGOe. In addition, the maximum energy product BHmax should preferably be distributed at 22.75 MGOe or more, more preferably at 27.80 MGOe or more.
Regarding the magnetic property at the temperature condition 200° C. according to the present disclosure, the residual magnetic flux density Br is distributed at 9.00 kG or more, preferably at 9.90 to 11.00 kG, more preferably at 9.60 kG or more, and more preferably at 10.10 kG or more. The coercive force Hcj is distributed at 3.80 kOe or more and at approximately 6.50 to 7.00 kOe. The coercive force Hcj should preferably be distributed at 6.60 kOe or more, and more preferably 15.90 kOe or more. The maximum energy product BHmax is distributed at least at 22.90 to 24.00 MGOe. In addition, the maximum energy product BHmax should preferably be distributed at 19.00 MGOe or more, more preferably at 23.70 MGOe or more.
In addition, the present disclosure has high mechanical strength. Tensile strength of the rare earth permanent magnet of the present disclosure is 80 MPa or more, preferably 100 MPa or more, and more preferably 150 MPa or more. In other words, the present disclosure has excellent machinability and can enhance mass productivity of products which use the present disclosure. It is also possible to enhance the products' life cycle. The tensile strength of the present disclosure can be measured by methods according to JIS Z2201 (tension test specimen processing method) and JIS Z2241 (tensile test measurement method).
[Rare Earth Permanent Magnet Manufacturing Method]
The method for manufacturing the rare earth permanent magnet according to the present disclosure is not particularly limited as long as the function effects of the present disclosure can be obtained. An example of a preferable manufacturing method according to the present disclosure can be a manufacturing method including a microparticulation step, a magnetization step, and a heat treatment step. The rare earth permanent magnet of the present disclosure can be manufactured by cooling a product, which is obtained as a result of each of the above-described steps, down to a room temperatures in a cooling step.
[Microparticulation Step]
In the microparticulation step, specified materials (M, L) such as Co and Fe, Nd, and B are dissolved at the stoichiometric ratio explained above, thereby obtaining a raw material alloy. When praseodymium, terbium, and aluminum as well as copper, niobium, zirconium, titanium, gallium, and so on are contained, starting materials containing these elements are added as raw materials when manufacturing the above-described raw material alloy.
The stoichiometric ratio of the composition of the raw material alloy is almost the same as the composition of the compound which becomes the main phase of the present disclosure that is a final product. Therefore, it is only necessary to combine the raw materials according to the composition of the desired compound. The obtained raw material alloy is coarsely ground by using, for example, a ball mill or a jet mill. It is also preferable that particulates of the raw material alloy which are then obtained by coarse grinding should be refined by using, for example, the ball mill or the jet mill.
The coarsely-ground raw material alloy particles are dispersed in an organic solvent and a reducing agent is added to the obtained product. As a result of reduction processing, the raw material alloy particles are atomized and its particle size becomes a powder particle size of 1.8 to 22.7 μm. When the reduction processing is executed on the microparticulated raw material alloy particles, the powder particle size becomes much smaller to 2.7 to 13.6 μm, more specifically 2.7 to 10.0 μm.
[Magnetization Step]
In the magnetization step, the obtained raw material alloy particulates are compression-molded in an oriented magnetic field. Furthermore, in the heat treatment step, the obtained molded body is heated under vacuum and then the obtained sinter is rapidly cooled to a room temperature. Subsequently, the heat treatment step is conducted under an inert gas atmosphere and then the sinter is cooled down to a room temperature.
[Heat Treatment Step]
In the heat treatment step, the main phase and the grain boundary phase are formed by conducting specified temperature management and time management. The heat treatment conditions are determined based on melting points of the constituents. Specifically speaking, all the constituents are dissolved by increasing the processing temperature to a main-phase-forming temperature and maintaining that temperature. Then, in the process of decreasing the temperature from the main-phase-forming temperature to a grain-boundary-phase-forming temperature, the main phase constituents enter a solid phase and the grain boundary phase constituents start depositing on a solid phase surface. The grain boundary phase can be formed by maintaining the grain-boundary-phase-forming temperature.
As an example of the heat treatment conditions to form the main phase, the temperature should preferably be retained at 1000 to 1200° C. for 3 to 5 hours and then further retained at 880 to 920° C. for 4 to 5 hours. More preferably, the temperature should be retained at 1010 to 1190° C. for 3 to 5 hours and then further retained at 890 to 910° C. for 3 to 5 hours.
As an example of the heat treatment conditions to form the grain boundary phase, the temperature should preferably be retained at 480 to 520° C. for 3 to 5 hours and then further retained at 490 to 510° C. for 3 to 5 hours.
The present disclosure can be manufactured by executing at least each of the above-described steps. The present disclosure can manufacture the rare earth permanent magnet by applying the conventionally-known method for manufacturing the rare earth permanent magnet only by using the alloy, in which Nd, Pr, Tb, etc. and Fe, B, Co, etc. of the specified content described earlier are dissolved, as raw materials. Furthermore, when manufacturing the rare earth permanent magnet which includes the specified main phase and grain boundary phase, the rare earth permanent magnet of the present disclosure can be manufactured easily by applying the above-explained heat treatment step.
By the method for manufacturing the rare earth permanent magnet of the present disclosure, the powder particle size of the raw material compound should preferably be 1.8 to 22.7 μm. By using the powder particle size of more preferably 2.7 to 13.6 μm, and further preferably 2.7 to 10.0 μm and retaining the raw material compound at the main-phase-forming temperature, the rare earth permanent magnet with an excellent magnetic property can be manufactured even if the content of terbium is suppressed. As a result of the heat treatment step, the sintered particle size of the raw material compound becomes 110 to 300%, or preferably 110 to 180%, of the powder particle size.
When the raw material alloy particulates of the powder particle size within the above-described preferable range are sintered, the sintered particle size becomes 2 to 25 μm, preferably 3 to 15 μm, more preferably 3 to 11 μm, and particularly preferably 3 to 6 μm. Particularly when crystals are refined to achieve the particle size of 3 to 11 μm, the rare earth permanent magnet of the present disclosure having the main phase of the crystals of the above-described sintered particle size decreases the content of terbium by 20 to 30% and has an equivalent magnetic property. In order to make the raw material alloy particles of the above-described powder particle size, such power particle size can be obtained by grinding the crystals by using the jet mill or the ball mill.
A sintered density of the alloy compound which includes the crystals of the above-described preferable sintered particle size as the main phase becomes 6 to 8 g/cm3, and more preferably 7.2 to 7.9 g/cm3. A method for measuring the sintered density will be described below. The weight used for measurement of the sintered density was measured by measuring samples with an electronic scale. Furthermore, the volume was found by the Archimedean Method or by measuring the dimensions of the samples with a ruler.
The present disclosure will be further explained by referring to examples below. However, the present disclosure is not limited to the examples described below.
Cobalt (Co), Nd, Fe, and B were arc-melted, thereby obtained a raw material alloy. The obtained 5 kg alloy was coarsely ground with the ball mill, thereby obtaining alloy particles with an average particle diameter of 16 μm. Subsequently, the alloy particles was dispersed in a solvent. An additive was introduced into the dispersed solution, which was then stirred to cause a reduction reaction to refine the alloy particles. An average particle diameter of the obtained fine alloy powder was 16 to 25 μm. The same process can be conducted on any one type of metal from among beryllium (Be), lithium (Li), aluminum (Al), and silicon (Si) besides cobalt (Co).
Respective samples of the above-described fine alloy powder were used as raw material compounds 1 to 5 and their magnetic moments were calculated by referring to atomic locations obtained by a neutron diffraction method (O. Isnard et. al J. Appl. Phys. 78 (1995) 1892-1898). Table 2 shows the magnetic moments of the raw material compounds 1 to 5. Furthermore, as a result of analysis by calculation, each crystal structure of the raw material compounds 1 to 5 was tetragonal and P43/mnm and lattice constants were a=8.81 Å and c=12.21 Å according to X-ray diffraction simulation.
A molding cavity was filled with 500 g of the raw material compound (the raw material compound 1) which used cobalt (Co), a 19 kOe magnetic field with a molding pressure of 2 t/cm2 was applied to conduct compression molding and magnetization. The obtained molded body was heated at a treatment temperature of 1090° C. for one hour under a 2×101 Torr Ar gas atmosphere. After the heat treatment terminated, the temperature was cooled down to a room temperature, and then the obtained product was removed from the cavity, thereby obtaining a rare earth permanent magnet of Example 1. Rare earth permanent magnets of Examples 2 to 5 for which any one type of metals from among beryllium (Be), lithium (Li), aluminum (Al), and silicon (Si) was used can be obtained in the same manner.
The raw material alloy containing the respective elements with the content indicated in
The molding cavity was filled with 500 g of the obtained alloy particulates 500 g and a 19 kOe magnetic field with a molding pressure of 2 t/cm2 was applied to the alloy particulates of each example to conduct compression molding and magnetization. A heat treatment was applied to each obtained molded body under a 2×101 Torr Ar gas atmosphere under the conditions indicated in
In the following explanation, each example number means that the relevant rare earth permanent magnet has a composition of the example number indicated in
In Example 7, the content in the rare earth permanent magnet was also measured in addition to the charged amounts indicated in
The residual magnetic flux density Br, the coercive force Hcj, and the maximum energy product BHmax of Example 6 to Example 14 were measured. Furthermore, the tensile strength was measured at a room temperature (25° C.). The measurement results of Example 6 to Example 14 are shown in
In Example 6 to Example 10, the crystal structure of the main phase was analyzed. A magnetic property measurement method, a tensile strength measurement method, and a crystal structure analysis method are as described below.
[Method for Measuring Residual Magnetic Flux Density Br, Coercive Force Hcj, and Maximum Energy Product BHmax]
Measurement Apparatus: apparatus equivalent to TPM-2-08S pulse-excitation-type magnetic property measurement apparatus with specimen temperature variator made by TOEI INDUSTRY, CO., LTD.
[Tensile Strength Test]
The tensile strength test was conducted by a method according to JIS Z2201 (tension test specimen processing method) and JIS Z2241 (tensile test measurement method).
[Crystal Structure Analysis by 3DAP]
A needle-like substance to be used for 3DAP analysis as a sample was processed by a method described below in order to observe the crystal structure of the main phase of the rare earth permanent magnet of the example. Specifically speaking, after the example sample was firstly set to a focused ion beam machining observation device (Focused Ion Beam [FIB]), the grooves were processed to observe a surface including an easy magnetization direction. The surface of the sample including the easily-magnetizing direction, which had appeared by processing the grooves, was irradiated with electron beams. The main phase (inside the grains) was identified by observing, with SEM, a reflection electron beams emitted from the specimen as a result of the irradiation. The sample was processed to form a needle-like shape in order to analyze the identified main phase by means of the 3DAP.
Conditions for the crystal structure analysis by means of the 3DAP are as follows.
Device Name: LEAP3000XSi (by AMETEK)
Measurement Condition: laser pulse mode (laser wavelength=532 nm)
Laser power=0.5 nJ, specimen temperature=50K
Furthermore, the 3DAP analysis of Example 6-10 shows that Co, Tb, and Al exist in the Nd—Fe—B layer.
In addition, the 3DAP analysis of Example 6-10 shows that Co exists in layers parallel to a C axis of the crystal lattice of the main phase.
The 3DAP analysis of Example 6-10 shows that Co exists in the layers parallel to the C axis of the crystal lattice of the main phase. A columnar area in a right diagram of
[Crystal Structure Analysis by Rietveld Method]
The crystal structure of Example 6-11 was analyzed by the Rietveld method. Analysis methods and analysis conditions are as described below.
[Analysis Methods]
Analysis Test Apparatus: X-ray diffractometer RAD-RRU300 made by Rigaku Corporation
Target: Co
Monochromatization: a monochrometer was used (Kα)
Target Output: 40 kV-200 mA
(Continuous Measurement) θ/2θ scanning
Slits: divergence slit: 1°; scattering slit: 1°; and light reception slit: 0.3 mm
Monochrometer Light Reception Slit: 0.6 mm
Scan Speed: 0.5°/min
Sampling Width: 0.02°
Measured Angle (2θ): 10°−110°
[Analysis Conditions]
The analysis was conducted by the Rietveld method. Analysis software RIETAN-FP was used and reference was made to F. Izumi and K. Momma, “Three-dimensional visualization in powder diffraction” Solid State Phenom., 130, 15-20 (2007). Coordinates were adopted form D. Givord, H.-S. Li and J. M. Moreau, “Magnetic properties and crystal structure of Nd2Fe14B” Solid State Communications, 50, 497-499 (1984).
The analysis results of the crystal structure by the Rietveld method are shown in the diagrams indicated below. Specifically speaking, the analysis results of Example 6-11 are shown in
The tensile strength of Example 11 was measured in Example 11-1 to Example 11-5. Furthermore, the tensile strength of Example 12 was measured in Example 12-1 to Example 12-5. The measurement method is the same as in Example 6. Table 5 shows the measurement results.
Raw material alloys containing the respective elements with the content indicated in Example 13 and Example 14 in
The molding cavity was filled with 500 g of the fine alloy powder of Example 13, or with 500 g of the fine alloy powder which was a mixture of Example 13 and Example 14, and a 19 kOe magnetic field with a molding pressure of 2 t/cm2 was applied to the fine alloy powder to conduct compression molding and magnetization. The heat treatment was applied to each obtained molded body under a 2×101 Torr Ar gas atmosphere under the conditions indicated in
The residual magnetic flux density Br, the coercive force Hcj, and the maximum energy product BHmax were measured by the same method as in Example 6. The measurement results are shown in
Each of raw material alloys containing the respective elements with the content indicated in Comparative Example 1 and Comparative Example 2 in
The molding cavity was filled with 500 g of the obtained fine alloy powder and a 30 kOe magnetic field with a molding pressure of 2 t/cm2 was applied to the alloy powder of each comparative example to conduct compression molding and magnetization. The heat treatment was applied to each obtained molded body under a 2×101 Torr Ar gas atmosphere. The heat treatment step was conducted under the heat treatment conditions indicated in
The rare earth permanent magnet of the present disclosure exhibits a high magnetic moment and has a good magnetic property. The rare earth permanent magnet contributes to downsizing, weight reduction, and cost reduction of, for example, electric motors, offshore wind power generators, and industrial motors. Since the rare earth permanent magnet exhibits an excellent magnetic property under high temperature conditions, it is suited for the use in automobiles and industrial motors.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-229783 | Nov 2013 | JP | national |
| 2013-229786 | Nov 2013 | JP | national |
| 2014-002050 | Jan 2014 | JP | national |
| 2014-002051 | Jan 2014 | JP | national |
| 2014-110669 | May 2014 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5645651 | Fujimura et al. | Jul 1997 | A |
| 5976271 | Nomura et al. | Nov 1999 | A |
| 20060005898 | Liu et al. | Jan 2006 | A1 |
| 20060016515 | Tomizawa et al. | Jan 2006 | A1 |
| 20070175544 | Hasegawa et al. | Aug 2007 | A1 |
| 20100003156 | Suzuki | Jan 2010 | A1 |
| 20100104767 | Sskuma et al. | Apr 2010 | A1 |
| 20140286815 | Ishiyama et al. | Sep 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 1462531 | Sep 2004 | EP |
| 11-008109 | Jan 1999 | JP |
| 2001-217112 | Aug 2001 | JP |
| 2002-038245 | Feb 2002 | JP |
| 2002-327255 | Nov 2002 | JP |
| 2003-217918 | Jul 2003 | JP |
| 2003-226944 | Aug 2003 | JP |
| 2005-320628 | Nov 2005 | JP |
| 2006-041507 | Feb 2006 | JP |
| 2008-505500 | Feb 2008 | JP |
| 2008-117855 | May 2008 | JP |
| 2010-074062 | Apr 2010 | JP |
| 2010-150604 | Jul 2010 | JP |
| 2013054854 | Apr 2013 | WO |
| Entry |
|---|
| Japanese Office Action dated May 1, 2018 for the Japanese Patent Application No. 2015-546639. |
| Extended European Search Report, European Patent Application No. 14860236.0, dated Jun. 30, 2017, 10 pgs. |
| Sagawa, M., et al., “ND—FE—B Permanent Magnet Materials,” Japanese Journal of Applied Physics, JP, vol. 26, No. 6, Jun. 1, 1987 (Jun. 1, 1987), pp. 785-800. |
| Japanese Office Action with English Translation, Japanese Application No. 2015-546639, dated Jul. 4, 2017, 8 pgs. |
| G.S. Chaubey et al., “Synthesis and Stabilization of FeCo Nanoparticles,” J. Am. Chem. Soc. 9 vol. 129, No. 23, 2007, pp. 7214-7215. |
| International Search Report, PCT/JP2014/079183, dated Feb. 10, 2015, 2 pgs. |
| Number | Date | Country | |
|---|---|---|---|
| 20160322135 A1 | Nov 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2014/079183 | Nov 2014 | US |
| Child | 15146932 | US |