The present invention relates generally to current collectors. More particularly, the invention relates to activating a sulfur cathode to near its equilibrium potential by adding a small aromatic molecule in the electrolyte as a redox mediator (RM).
Lithium-sulfur (Li—S) batteries are a sustainable and cost-effective solution for next generation energy storage to support renewable energy integration due to the natural abundance of sulfur. Li—S batteries can theoretically store an energy density of 2500 Wh kg−1, a five-fold increase compared to traditional lithium ion batteries (LIBs). Such exceptionally high energy density is enabled by the reversible conversion reaction between sulfur and lithium sulfide (Li2S) via a series of lithium polysulfides intermediates (LiPSs, Li2Sn, 2≤n≤8). However, significant challenges remain in order to build practical Li—S batteries, which are mainly attributed to the solubility of LiPSs in the electrolytes and the insulating nature of both sulfur and Li2S. For examples, when charging a Li2S electrode, a significant portion of each particle is electrically isolated and can be oxidized at the localized interface between the electrode/electrolyte with sufficient charge transfer; therefore, the Li2S exhibits a large overpotential and a limited reversible capacity that is substantially lower than the theoretical value. Furthermore, the dissolution-precipitation process yields insulating deposits of S and Li2S, which passivate the active interface for the redox reaction. Such evolution of the electrode architecture recurring over cycling is thus considered one of the primary causes of capacity fading in Li—S batteries together with internal polysulfides shuttling. Consequently, Li—S cells have been shown to have insufficient practical energy density, poor rate capability, and limited cycle life, collectively restricting commercial success of this system.
To address the aforementioned issues, considerable efforts have focused on incorporating nanostructured conductors, such as transition metals (Fe, Cu, Co), metal oxides, metal sulfides, metal nitrides, metal carbides, carbon nanomaterials, and conductive polymers. The electrochemically active area in the electrode significantly improved through these approaches, and LiPSs diffusion was further suppressed when appropriate physical confinement was attained. However, this improvement was often accomplished at the expense of the tap density with low active material loadings and would require costly production processes. Also, this approach does not necessarily prevent detachment of active particles from a conductive support and passivation of redox active sites upon long-term cycling during the solid-liquid-solid transition. Employing chemical interactions between LiPSs and hosts can better trap the sulfur species, but this effect is specific to the host surfaces, raising concerns about practical viability of requiring an ultrahigh-surface-area matrix. Therefore, breakthroughs are still needed to develop a low cost, scalable and reliable method to improve the practical performance of Li—S batteries.
Introducing redox mediators (RMs) to the electrolyte solution represents another effective strategy to address the limited performance of Li—S batteries. This approach relies on electrochemical oxidation of RMs in solution which can in turn chemically oxidize the active material on the entire surface of the particle. This additional charge transfer route beyond the localized interface enables homogeneous and complete oxidation of the electrode with a reduced overpotential. This approach has been primarily explored in lithium-oxygen (Li—O2) batteries, which suffer from the poor electronic conductivity of Li2O2. Properly designed RMs have been shown to reduce the charge overpotential of Li2O2 by less than 0.1 V and protect both the electrolyte and carbon electrodes from degradation, significantly improving the energy efficiency and cycling stability of Li—O2 cells. In contrast, the research in utilizing RMs in Li—S batteries is still in its infancy. Soluble LiPSs are known to serve as an internal RM if available, but their transient nature renders LiPSs unreliable in the cell at fully discharged or charged states. So far, only metallocene has been confirmed to shuttle electrons during Li2S oxidation, which can reduce the initial charge potential of Li2S electrodes to 2.9 V. Lithium iodide (LiI) was also reported to reduce the polarization, but later it was found that it actually modified Li2S surfaces; regardless, the charging occurs at 2.8 V, which still deviates from the Li2S equilibrium potential. Hence, the lack of proper redox chemistry has hindered the potential of employing RMs in Li—S batteries when compared to Li—O2 batteries.
What is needed is a quinone redox chemistry to enable a new RM for fast and stable cycling of Li—S batteries.
To address the needs in the art, a battery electrolyte solution that includes an organic electrolyte solution, a lithium-sulfur (Li2S) compound, soluble lithium polysulfide (Li2Sx) microparticles, and a redox mediator comprising a soluble quinone derivative.
In one aspect of the invention, the quinone derivative includes 1,5-bis(2-(2-(2-methoxyethoxy)ethoxy)ethoxy)anthra-9,10-quinon (AQT).
In another aspect of the invention, the soluble polysulfide Li2Sx is a compound that includes Li2S2, Li2S4, Li2S6, Li2S8, and Li2Sx—S, where x={2, 4, 6, 8}.
According to a further aspect of the invention, a reduction energy level of the redox mediator is higher than an oxidation energy level of the battery electrode active material.
In yet another aspect of the invention, a reduction potential of the redox mediator is higher than an oxidation potential of the battery electrode active material.
According to one aspect of the invention, a reduction energy level of the redox mediator is higher than an oxidation energy level of the redox mediator. In one aspect, a reduction energy level of the redox mediator is higher than an oxidation energy level of the Li2S compound. In another aspect, the reduction energy level is in a range of 2.15 V to 2.3 V. In a further aspect, an oxidation energy level of the redox mediator is higher than and proximal to an oxidation energy level of the Li2S compound.
According to one aspect, the reduction energy level is in a range of 2.15 V to 2.3 V.
In one aspect of the invention, a redox potential of the quinone derivative ranges from 1.7 V to 3.2 V.
According to one embodiment the invention includes a Li—S battery having an anode, a cathode, an organic electrolyte solution, a current collector, a lithium-sulfur (Li2S) compound a soluble lithium polysulfide (Li2Sx) microparticles, and a redox mediator comprising a soluble quinone derivative.
In one aspect of the current invention, the quinone derivative includes 1,5-bis(2-(2-(2-methoxyethoxy)ethoxy)ethoxy)anthra-9,10-quinon (AQT).
In another aspect of the invention, the soluble polysulfide Li2Sx includes a compound selected from the group consisting of Li2S2, Li2S4, Li2S6, Li2S8, and Li2Sx—S, where x={2, 4, 6, 8}.
According to a further aspect of the invention, a reduction energy level of the redox mediator is higher than an oxidation energy level of the redox mediator.
In yet another aspect of the invention, a reduction energy level of the redox mediator is higher than an oxidation energy level of the Li2S compound. In one aspect, the reduction energy level is in a range of 2.15 V to 2.3 V. In a further aspect, an oxidation energy level of the redox mediator is higher than and proximal to an oxidation energy level of the Li2S compound. Here, the reduction energy level is in a range of 2.15 V to 2.3 V.
According to one aspect of the invention, a redox potential of the quinone derivative ranges from 1.7 V to 3.2 V.
The development of Li2S electrodes is a crucial step toward the industrial manufacturing of Li—S batteries, a promising alternative to Li-ion batteries due to their projected two times higher specific capacity. However, the high voltages needed to activate Li2S electrodes, and the consequent electrolyte solution degradation, represent the main challenge. Hence, the discovery of effective catalyst is an important step to solving this problem. According to the current invention, a series of organic RM candidates are selected as a model system to identify the key factor in determining the catalytic activities and in Li—S cells. It is revealed that the level of oxidation potential, ability to oxidize Li2S and solubility play an important role for activating Li2S electrode. It is demonstrated that they are critical in reducing the overpotential of the Li2S electrode. Accordingly, the current invention provides a general principle for designing feasible catalyst and report a RM, AQT, with a remarkably low overpotential. The discovery leads to high rate cycle stability (1 C) can be achieved in 700 cycles with an only decay rate of 0.034% per cycle.
The current invention provides an effective strategy to activate a sulfur cathode near its equilibrium potential by adding a small aromatic molecule in the electrolyte as a redox mediator (RM).
The insulating nature of Li2S particles hinder the charge transfer process and require intimate contact with current collectors to become activated. This stringent limitation leads to large first charge cycle polarization and decay of charge capacity. To address these issues, a redox mediator (RM) can be used to completely re-route charge transfer process between Li2S particles and current collectors. RM can chemically oxidize Li2S particles (Step 1 chemical reactions: RM become RM2−), diffuse to current collectors and unload the electrons (Step 2 electrochemical reactions: RM2− become RM). Since RM can be continuously regenerated, small quantities of RM can catalytically shuttle electrons for entire cathodes efficiently. Notably, RM can patrol the cathode compartment by free diffusion to identify and react with Li2S particles, not in proper contact with current collectors. Hence, RM fundamentally resolves issues imposed by insulating Li2S particles. Spontaneous chemical oxidation of Li2S particles by RM necessitates the reduction potential of RM higher than Li2S oxidation potential (2.15V). Further, since RM is responsible for the release of electrons to current collectors, the cathode oxidation potential is now determined by oxidation potential of RM (the potential from RM2− to RM). Therefore, selecting RM with oxidation potential close to 2.15 V can substantially reduce the first charge overpotential (˜3.5V). Moreover, by introducing two triethylene glycol monomethyl ether groups on the RM core, the resulting molecule (denoted as AQT) shows substantial improvement in the solubility, resulting in outstanding charge potential improvement and cycle stability.
Applications:
Because most research is focused on producing the nanoparticle Li2S or creating an encapsulating structure with conductive materials to solve the insulating nature of sulfur materials, the synthesis is too complicated. In one aspect of the invention, the mediator approach is less complex—just dissolve the RM in the electrolyte without any synthetic procedure of electrode materials.
According to the current invention, the approach is universal for Li—S batteries that does not change either the electrolytes or the electrode of the battery system. In essence, the current invention provides an effective, simple and universal approach that can easily implant any method that has been provided in the Li—S battery field.
Many strategies have been proposed to improve first charge cycling performance. First, many efforts have been dedicated to improving contact of Li2S particles with conducting materials by blending or encapsulating Li2S with high-surface-area conductive material. Common conductive materials include transition metal (Fe, Cu, Co), transition metal oxide or carbide, carbon materials (e.g., graphene and carbon nanofibers) and conductive polymers. However, the first charge overpotential is still limited to above 2.8 V.
Second, incorporation of RM is another promising approach. However, all literature reported RMLi2S cathodes still show first charge overpotential above 3V. According to the current invention, AQT disclosed herein is the only RM that can significantly reduce overpotential down to 2.4V up to 0.5 C charge rate, and outperforms current literature reported counterparts. An enhanced cycle stability is also demonstrated by AQTLi2S electrode. The cycle retention has improved from 60% to 81% in 350 cycles compared to the bare Li2S electrode. Moreover, only a few studies successfully display high rate 1 C cycle stability over 1000 cycles, and electrode encapsulation is needed. Nevertheless, provided herein the cycle retention of 76% over 700 cycles can be successfully maintained. Furthermore, AQT could successfully resolve first charge overpotential in high mass loading Li2S cathodes (3-6 mg/cm2) and maintain high cycling stability up to 100 cycles (900 mAh/gs).
According to the current invention, a rational design principle has been created for the sulfur cathode, including potential selection rule, solubility effect for different functional group tuning. This leads to finding a chemical structure that is the most suitable RM for sulfur battery cathode.
Due to the insulating nature of Li2S, hinders the charge transfer process between Li2S and current collector, causing large polarization in the first cycle, accumulation of unreacted Li2S during cycles. The thick and inhomogeneous Li2S would eventually block the cathode and cause a death cell. Besides, because of repeated dissolution-deposition process of polysulfide, Li2S loses intimate contact with current collector and therefore becomes inactive (isolated Li2S) in the subsequent cycling. But with adding small molecule (RM) to the electrolyte that reversibly accept and donate electrons at known potential, it can completely re-route the electron transfer process between Li2S and current collector by shuttling electrons between Li2S and current collector continuously, facilitating charge transfer kinetics throughout the electrode and making the isolated Li2S active through cycling.
Turning now to a more specific discussion, lithium-sulfur (Li—S) batteries charge by oxidizing solid lithium sulfide (Li2S) into sulfur (S8) through soluble lithium polysulfide intermediates (Li2Sx), enabling a high theoretical specific capacity of 1675 mAh gs−1. However, the insulating nature of sulfur and Li2S results in large polarization and low sulfur utilization while the soluble polysulfides lead to internal shuttle upon charge and discharge. Furthermore, the redox reaction via the dissolution-precipitation route destroys the electrode architecture by passivating the active interface responsible for the redox reaction, and thus the performance of Li—S batteries deteriorates with cycling. Disclosed herein is the redox chemistry of a quinone derivative to realize efficient, fast, and stable operation of Li—S batteries using Li2S microparticles. By adding a quinone derivative with tailored properties (e.g. oxidation potential, solubility, and electrochemical stability in the electrolyte) to an electrolyte as a redox mediator, initial charging of Li2S electrodes occurs below 2.5 V at a 0.5 C rate, and the subsequent discharge capacity is as high as 1300 mAh gs−1. Moreover, deposition of dead Li2S, which was the primary cause of increasing polarization and decreasing reversible capacity of Li—S batteries upon cycling, is effectively prevented with the addition of the redox mediator.
Here, quinone redox chemistry is used to design a new RM for fast and stable cycling of Li—S batteries. Through rational tuning of the redox potential, stability, and solubility of quinones by molecular engineering, it is successfully demonstrated that the quinone redox can facilitate the initial oxidation of Li2S below 2.5 V at a fast rate of 0.5 C. The continuing effectiveness of the quinone-based RM beyond the first cycle was confirmed with observation of the minimal polarization and improved capacity retention of Li—S cells over prolonged cycles. Importantly, when cycled with the RM, the Li2S electrode maintained its original morphology over 250 cycles, suggesting a unique mechanism that enables controlled deposition of Li2S and sulfur instead of random deposition. Thus, minimal overpotential and high capacity continued over prolonged cycling. Because of these collective attributes, a high mass loading electrode of 6 mg cm−2 Li2S was used to successfully demonstrate charging below 2.5 V with a reversible capacity of 952 mAh gs−1. This effective strategy of using tailored RMs in sulfur redox chemistry to improve both reaction kinetics and stability is the key to obtaining high practical power and energy density over prolonged cycling for the practical implementation of Li—S batteries.
Turning now to a discussion of large overpotentials for Li2S cathodes, due to poor electronic conductivity, Li2S electrodes are difficult to activate. The oxidation reaction only occurs at the localized regions of the active particles directly interfacing electron and ion transfer channels. This mechanism thus requires a large overpotential, and the cell exhibits a specific capacity much lower than the theoretical value.
Effective RMs solubilized in the electrolyte shuttle electrons between current collectors and the surfaces of isolated Li2S particles, which would have otherwise remained inactive (see
Anthraquinone-2-carboxylic acid (AQC) and 2,5-dichloro-1,4-benzoquinone (DCBQ) are selected as RMs to examine electrochemical properties.
The first cycle voltage profiles of Li2S electrodes with different RMs at 0.3 C are shown in
From the energy efficiency and discharge capacity of the various RMs, it is determined that low polarization and high Coulombic efficiency lead to high energy efficiency. According to the current invention, the Li2S cell with AQT showed the highest discharge capacity (1402 mAh gs−1), lowest average charge potential (<2.5 V) and highest Coulombic efficiency (87%), thus exhibiting the highest energy efficiency among all tested RMs. Taken together, AQT with the desired redox potential, high solubility in the electrolyte and superior cycling stability is the most effective in promoting charge transport of Li2S cathodes among all the tested systems.
In one example, with 10 mM of AQT in the electrolyte, where the molar ratio between Li2S and AQT is 80 to 1, the overpotential during the first charging cycle can be effectively reduced. Nevertheless, as the AQT concentration increases, the reversible capacity and Coulombic efficiency increase. Thus, either 80 mM or 160 mM of AQT depending on the electrode mass loading in the following study to assure improved performance. When the electrolyte amount was also decreased from 20 μl to 10 μl, which corresponds to the electrolyte/Li2S of 14 μl mg−1, the Li2S electrode can be still charged at 2.5V. Note that redox cycling of quinone is also effective in oxidizing ball-milled commercial Li2S with a more heterogeneous size distribution than the μ-Li2S.
Notably, AQT performs better than Li2S8, the internal RM spontaneously formed during conventional sulfur redox processes. When adding 80 mM Li2S8 as a RM to the DOL/DME electrolyte, the charge capacity obtained below 2.5 V is less than 400 mAh gs−1 at 0.3 C, which is three-fold less than AQT. This result confirmed the need for a RM better than Li2S8 to minimize polarization during charging.
Next, the maximum C rate achieved was compared with various reported strategies using Li2S electrodes and the corresponding first average charging voltage. Methods such as mixing Li2S with nanostructured conductors like carbon, metals sulfides, and polymers still exhibited oxidation potentials of 2.8 V, 3.3 V, and 3.5 V, respectively, even at a slow rate (<0.1 C), simultaneously suffering from process complexity and lower active material loadings. Likewise, the previous best performing additives LiI and FC exhibited first charge potentials of 2.8 V at 0.05 C and 2.9 V at 0.2 C, respectively, which are far above the equilibrium potential of Li2S. In comparison, AQT can facilitate Li2S oxidation at voltages as low as 2.45 V even at a high current density of 0.5 C, which demonstrated that this system has exceptionally fast charge transfer kinetics. The performance comparison is more reasonable when the critical cell parameters including areal mass loading, active content, and electrolyte/active ratio are considered in parallel. Note that the charge overpotential and the subsequent discharge capacity in this example study is remarkable despite using large particles, a high active content, and a comparable electrolyte to Li2S ratio.
Turning now to the chemical reaction between AQT and Li2S, the voltage profiles of half cells using 80 mM AQT in DOL/DME electrolyte (20 μl) with and without a Li2S electrode, exhibit capacities of 0.612 mAh and 0.059 mAh, respectively. Given that the charge voltage of the Li2S electrode overlaps with the voltage range of AQT at 2.4 V, the charge process should involve the direct electrochemical oxidation of AQT. In the galvanotactic discharge and charge of AQT (as a catholyte), it is confirmed that there exists stable reduction and oxidation of AQT with 80% capacity retention over 200 cycles and negligible redox shuttling of AQT with Coulombic efficiency higher than 98% throughout cycling. This result validates that AQT can continuously be reduced and oxidized in the presence of a lithium metal anode without significant degradation of the RM on the Li metal surface.
The spontaneous chemical reaction of Li2S oxidation by AQT was investigated by X-ray photoelectron spectroscopy (XPS). To probe changes in the oxidation state of Li2S when mixed with AQT in its oxidized state, the S2p binding energy of the Li2S and AQT mixture (5:1 molar ratio) in the DOL/DME solvent were measured. The result was compared to that of blank Li2S and chemically synthesized Li2S4. The S2p spectrum of Li2S4 shows two pairs of doublets at 161.20/162.4 eV and 162.8/163.9 eV, which corresponds to the terminal (ST−1) and bridge (SB0) S atoms, respectively, in addition to minor contributions from the unreacted Li2S at 159.67.20/160.85 eV. Similarly, the mixture of Li2S and AQT exhibited significant contribution at higher S2p binding energies than pristine Li2S. This arises from the oxidation of Li2S by AQT, and thus proves the spontaneous charge transfer between Li2S and AQT.
The spontaneous chemical reaction of Li2S oxidation by AQT is better understood by analyzing the reaction product. Since the reaction product simultaneously forms when we mix the Li2S electrode and the AQT-containing electrolyte to fabricate the half cell, the product is thus able to be electrochemically analyze by directly discharging the half cell. The discharge profile of the half cell with a mixture of Li2S and 160 mM AQT was compared with the cell without Li2S and only having 160 mM AQT. Note that no discharge capacity would be exhibited when directly discharging pristine Li2S. From the mixture, on the other hand, it is observed that a plateau exists at 2.25 V corresponding to the electrochemical reduction of the AQT−, followed by a plateau at 2.1 V corresponding to the electrochemical reduction of Li2Sx. Since the profile does not show the first reduction plateau of AQT at 2.45 V, it is confirmed that all of the AQT has been chemically converted into AQT− when mixed with Li2S. Simultaneously, chemical oxidation of Li2S into Li2Sx should occur. The discharge capacity is identical to that of pure AQT, indicating that the total amount of charge is retained and no side reaction occurs other than this process.
Further evidence of the charge transfer process between AQT and Li2S was obtained with cyclic voltammetry. A cathodic sweep was conducted followed by an anodic sweep of AQT in DOL/DME electrolyte while gradually adding Li2S4. The second oxidation peak at 2.6 V (O2) showed significant current responses upon addition of Li2S4, while the first oxidation peak (O1) showed negligible changes. This result indicates that the concentration of AQT− to be oxidized at 2.6 V increases as the polysulfide concentration in the electrolyte increases due to the chemical regeneration of AQT− from AQT. It is hypothesize that the chemical regeneration of AQ− from AQ is promoted by Li2Sx (x<4), which can be formed during the previous cathodic sweep by reducing Li2S4. (for details, see Supplementary Note 1).
Turning now to the universal improvement in sulfur electrochemistry by AQT, the effectiveness of AQT to improve the Li—S battery operation beyond the first cycle was confirmed over continued cycling. During 10 cycles at 0.1 C, the blank Li2S electrode showed repeated overshooting in the initial stage of charging and the capacity continuously decreased to 400 mAh gs−1. In contrast, with AQT, no voltage overshoot was observed during charging, and 96% of the capacity at the second cycle was retained in the 10th cycle. In the study, enlarged dQ/dV curves displayed two consistent reduction peaks from AQT over 10 cycles which were not observed in the pristine Li2S cell, showing continuous redox activity of AQT over prolonged cycling.
To validate the effect of AQT to promote the sulfur electrochemistry generally, cells using a Li2S8 catholyte instead of a Li2S electrode were fabricated. The cells were first discharged to reduce Li2S8 to Li2S and comparable capacities were obtained regardless of the AQT presence because pristine AQT does not participate in the reduction of Li2S8. Then, the cell charging with AQT showed a slightly lower overpotential when compared to the blank cell, and the subsequent discharge capacity was much higher in the presence of AQT. Note that the increased capacity (307 mAh gs−1) in the second cycle cannot be fully accounted for the capacity contribution from AQT indicating more Li2S can be activated with AQT in the Li2S8 catholyte cells as well. Upon prolonged cycling, the effect of AQT became prominent. Am average charge and discharge voltage of the Li2S8 catholyte cells with AQT at rates of 0.1 C, 0.3 C and 0.5 C were compared to the blank Li2S8 cell at 0.1 C. The reduced polarization by AQT remarkably persisted over 200 cycles, demonstrating consistent charge transport kinetics over many cycles, outperforming the blank cells.
For improving cycling stability of Li—S batters by AQT, it is found that adding AQT significantly enhances the cycling stability of Li—S batteries. At a current density of 1 C, the capacity of 850 mAh gs−1 was retained after 500 cycles in the presence of AQT, whereas the capacity of the bare Li2S cell decayed drastically to 225 mAh gs−1 within 10 cycles. At a lower rate of 0.5 C, the capacity retention was still considerably better with AQT. This cycling stability is exceptional because it was achieved without specialized processing such as confinement or encapsulation of the sulfur species. The energy efficiency and Coulombic efficiency is also improved by adding AQT. It is also important to note that AQT does not accelerate the self-discharge discharge of Li—S batteries; but it prevents the capacity decrease due to the sulfur loss in later cycles, suggesting that shuttling of RM to the Li metal anode is negligible.
The capacity decay of Li—S batteries is attributed to the loss of active material due to the soluble intermediates and the propagation of electrochemically inactive portion by pulverisation and random deposition of insulating species during cycling. Therefore, to understand the origin of the improved cycle life with AQT, the effects of AQT on both polysulfide dissolution and Li2S morphology evolution were explored.
Examined first was the solubility of representative LIPS species (Li2S4 and Li2S8) in DOL/DME upon AQT introduction. Polysulfide solutions (20 mM) were prepared as references, and an equivalent molar amount of AQT was added to the polysulfide solutions to prepare the mixtures. After filtering the solution to remove any particles, inductively coupled plasma optical emission spectrometry (ICP-OES) was used to quantify the total concentration of sulfur and lithium in the liquid phase. The Li2S4 and AQT mixture contained only 25% of the expected sulfur content from the original pristine Li2S4 solution, and the Li2S8 and AQT mixture also contained less than 55% of the sulfur content from the pristine Li2S8 solution. Therefore, introducing AQT decreased the amount of soluble sulfur species in the electrolyte. The decreased LiPSs solubility is attributed to the binding interaction between AQT and LiPSs.
Next, the morphology evolution of Li2S electrodes over many cycles was monitored. The Li2S electrodes tested with and without AQT were retrieved after the first and 250th cycles, respectively, and examined by scanning electron microscopy (SEM). In accordance with the previous study under the conventional condition suffering from the recurring solid-liquid-solid transition, randomly deposited sulfur species that are different from the initial morphology were observed in the blank Li2S electrode regardless of the cycle number and state of the charge. Such uneven accumulation of thick sulfur/Li2S layers observed in SEM would block the charge transfer across the electrode/electrolyte interfaces and thus cause poor reaction kinetics and capacity decay. Nevertheless, in the presence of AQT, the original morphology of Li2S particles was virtually unchanged over 250 cycles (
It is hypothesized that AQT can potentially alter LiPS-solvent interactions and determine sulfur speciation, as evidenced by the reduced solubility of LIPS with AQT, which in turn induces preferred deposition of Li2S and S on the surfaces of active particles.
Further conducted was ex situ X-ray spectromicroscopy with the Li2S electrodes in the charged state that had been cycled over 200 times. The maps were collected at multiple spots on each sample (as indicated with area #1 and #2) at energies of 2470.8, 2472.6, 2473.6, and 2476.4 eV, in order to differentiate between Li2S, polysulfide, and elemental sulfur species. After cycling for 200 times in the presence of AQT, the fully charged electrode showed a homogeneous sulfur distribution and a trace of Li2S throughout the electrode. In sharp contrast, when cycled without AQT, the Li2S electrode displayed a localized region of sulfur with exceptionally high intensity (6-40 times higher than other regions) in the elemental sulfur map while also showing significant intensities from unreacted Li2S in the Li2S map. This is consistent with our SEM result showing heterogeneous conversion of sulfur during cycling. In sharp contrast, Thus, the results verify homogenous and complete conversion of sulfur over the entire electrode in the presence of AQT, which is highly desirable for improved energy density and cycle life. Due to the complex nature of sulfur speciation, further studies are needed to specify the sulfur redox mechanism with AQT by real-time monitoring of chemical and structural evolution of the electrode.
The above results suggest that AQT may effectively resolve poor charge transfer and heterogeneity in high mass loading electrodes. Thick Li2S electrodes were tested with areal Li2S loading of 4 and 6 mg cm−2 in the presence of AQT. The first charge plateau remained below 2.6 V at 0.05 C throughout the charging process, and more than 950 mAh gs−1 of discharge capacity was obtained in both electrodes. This supports the hypothesis that the redox mediating function of AQT effectively facilitates Li2S oxidation even in thick electrodes with an electrolyte to Li2S ratio of 12.5 μl mg−1. When cycled at 0.1 C over 100 cycles, the 4 mg cm−2 electrode still exhibited a discharge capacity of 863 mAh gs−1 with an average Coulombic efficiency of 93.7% and the 6 mg cm−2 electrode exhibited 606 mAh gs−1 with an average Coulombic efficiency of 92.8%. Notably, the above results were obtained by using μ-Li2S (70 wt % of active content) without adopting any nanostructuring or hosts for the first time. This highlights the viability of using AQT as a practical strategy to dramatically improve the performance of Li2S electrodes for Li—S batteries. Nevertheless, when combined with optimized electrode architectures, further improvements in the performance and cell parameters (e.g. mass loading and electrolyte amount) would be feasible and would truly translate our fundamental discovery to real applications.
Also confirmed was the charge transfer kinetics in the Li2S cathode cycled with AQT is superior to that of the Li2S8 catholyte. A comparison of multiple charge profiles were taken over prolonged cycling of the Li2S cathode with AQT against Li2S8 catholyte having the equivalent sulfur loading of 3 mg cm−2 and the active content of 70%. Surprisingly, it was found that voltage profiles significantly evolved over time in the catholyte system whereas the profiles of the AQT-added Li2S cathode remained unchanged for more than 100 cycles. When comparing the average voltage of charge and discharge curves over cycling for those two conditions, the results were reliably consistent and lower polarization was observed in the Li2S electrode with AQT, highlighting stable and efficient sulfur redox cycling enabled by AQT.
The present invention has now been described in accordance with several exemplary embodiments, which are intended to be illustrative in all aspects, rather than restrictive. Thus, the present invention is capable of many variations in detailed implementation, which may be derived from the description contained herein by a person of ordinary skill in the art. All such variations are considered to be within the scope and spirit of the present invention as defined by the following claims and their legal equivalents.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/016899 | 2/6/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/157088 | 8/15/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20160006039 | Cosnier | Jan 2016 | A1 |
| 20170222226 | Helms | Aug 2017 | A1 |
| 20170279122 | Helms | Sep 2017 | A1 |
| 20230223651 | Fan | Jul 2023 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20210050624 A1 | Feb 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62627458 | Feb 2018 | US | |
| 62626936 | Feb 2018 | US |