This invention relates to razor blades for use in wet shave razors, to compositions for making razor blades, and methods for use with these compositions to produce razor blades for wet shave razors having improved corrosion resistance and a high hardness.
Razor blades for wet shave razors are commonly produced from steel containing about 0.7% carbon by weight and about 12% chromium by weight. A conventional process for producing these razor blades is to hot roll and then cold roll a starting material to the desired razor blade thickness, which is usually between about 0.003 inches and 0.005 inches. This rolled material is then heat-treated to convert the as-rolled microstructure to an austenite microstructure. Following heat treatment the material is quenched to at least partially convert the austenite to a martensitic microstructure. The martensitic microstructure is too hard and brittle for use in razor blade applications, so the material is further heat treated at an intermediate tempering temperature to partially transform the martensite thereby obtaining a tougher, softer microstructure. In this conventional material the increased hardness and toughness which results from the heat treatment process is a consequence of the formation and modification of carbon-containing phases in the material. Most of the carbon-containing phases formed in this steel contain chromium, and typically about 4 wt. % chromium is in the form of carbides, leaving about 8 wt. % chromium remaining for corrosion reduction. This amount of chromium reduces but does not eliminate corrosion resulting from shaving conditions.
The above-described chromium carbon steel material has historically been used in the manufacture of razor blades and has exhibited a proclivity towards corrosion. Corrosion is unappealing to the user and degrades razor performance. Consequently, there have been many efforts made to provide a hard, tough material suitable for razor blade applications which is corrosion resistant.
Attempts to improve the corrosion resistance of razor blade steel through additions of more chromium have been largely unsuccessful due to the fact that when sufficient chromium to eliminate corrosion is added, the steel cannot be heat treated to a sufficient hardness for use in razor blade applications.
Precipitation hardening stainless steels have been developed which do not rely on carbon-containing phases for mechanical properties. Such steels are described in patents U.S. RE 36,389, U.S. Pat. No. 5,632,826, U.S. Pat. Nos. 5,759,308, and 6,475,307 which are expressly incorporated herein by reference.
Many attempts have been made to modify the surface of carbon steel razor blades by the application of coatings to retard corrosion and/or to reduce friction. Coatings such as chromium, precious metals, alloys based on chromium, and mixtures thereof, ceramics, diamond-like carbon, amorphous diamond, and polymers such as Teflon™ Krytox 1000™, and Dryfilm LXE™ have been used (Teflon, Krytox 1000, and Dryflim LXE are products of the DuPont Corporation).
There remains a need and desire in the industry to provide razor blades which are hard and inherently corrosion resistant.
Based on the foregoing, it is the general object of the present invention to provide a material useful for the production of razor blades that overcomes the problems and drawbacks associated with the prior art.
The present invention resides in one aspect in a low carbon (less than about 0.1%) precipitation hardening stainless steel useful for making razor blades for wet shave razors, containing substantial amounts of chromium and nickel for corrosion resistance and containing at least one element selected from the group consisting of titanium, aluminum, copper, silicon, and molybdenum provided as a starting material. Elements of a second group (titanium, aluminum, copper, silicon and molybdenum) are present as strengthening precipitates which replace and perform the functions of the carbon-containing precipitates that provide strengthening and hardness in conventional chromium-containing carbon steels.
The above-described starting material also displays transformation-induced plasticity which means that if the starting material is heat treated so that it exhibits an austenite structure, it can be deformed, for example, by cold rolling, to at least partially convert the austenite structure to the harder, tougher, martensite structure. Following the transformation of the austenite to martensite, the material can be heat treated to cause the formation of a strengthening dispersion of precipitates which contain one or more of the materials titanium, aluminum, copper, silicon and molybdenum. This precipitation hardening stainless steel in combination with appropriate process steps can be used to produce a razor blade material having a hardness in excess of 600 HV, and preferably in excess of 800 HV (measured at an applied load of 1 Kg) in combination with a high resistance to corrosion in shaving applications.
One advantage of the present invention over the prior art resides in the composition having improved corrosion resistance. Improved corrosion resistance results from the presence of an increased amount of non-carbide chromium. Because less chromium is bound in a carbide structure, more chromium is available to provide resistance to the formation of oxides that form the basis for corrosion.
The present invention relates to razor blades and to compositions and processes for producing razor blades for wet shave razors. The resultant razor blades have a particular composition and are produced using a particular processing sequence.
Table I presents broad and preferred compositions for use in manufacturing razor blades of the invention. The percentage values in Table I are in weight percent (wt. %) as are all other percent values in this application unless otherwise expressly indicated.
(values shown in wt. %)
In a razor blade of the present invention having a composition as indicated in Table I, the carbon content is limited so that it is well below that used in conventional razor blade steels. In one embodiment, the carbon content is less than about 0.015% and preferably less than about 0.010%. Because in a carbide compound the effectiveness of the carbon is limited in its ability to precipitate to provide a strengthening effect, the term “carbon content” as used herein is exclusive of the carbon contents of any carbides present. By limiting the carbon content as such, the use of carbide compounds to provide the carbon content is precluded or at least substantially limited.
In the preferred composition, neither silicon nor manganese is required. However, if either silicon or manganese is present in the composition, they may contribute to the formation of certain strengthening precipitates. As used herein, the term “strengthening precipitate” indicates a metal-containing phase that precipitates from a supersaturated solution of an alloy in which the precipitation occurs during the slow cooling of the alloy because. the solubility of the metal of the metal-containing phase decreases with decreasing temperature. In the present invention, the contribution of silicon or manganese to the formation of strengthening precipitates is effected by the homogenous nucleation of metal atoms to form aggregates having no well-defined crystral structure of their own and containing high concentrations of individual silicon or manganese atoms. The precipitates increase the strength of the alloy by developing coherency strains at the interface between the matrix and the growing aggregates.
Strengthening precipitates may also result from the presence of the elements molybdenum, titanium, copper, aluminum, or combinations thereof. Additionally, chromium, nickel, iron, and combinations thereof may also be found in the strengthening precipitates.
Chromium and nickel are added to promote corrosion resistance. Chromium is a strong ferrite stabilizer and is utilized to convert the composition to an austenite microstructure at a moderately low temperatures. At lower concentrations, nickel provides for the formation of the austenite microstructure at the temperature at which the composition is annealed. At higher concentrations, nickel also facilitates the transformation of the austenite structure to martensite when the composition is quenched or cold worked.
Cobalt is optional but may be employed to enhance the formation of precipitates. Tantalum, niobium, vanadium, and tungsten are limited to less than about 0.1% each. The balance is iron, and customary impurities in amounts up to about 0.5% total. In the broad range, iron will be present in an amount of at least 50% and in the preferred range in an amount of at least 65%.
The above-described material is melted and solidified according to conventional steel making techniques taking care that the resultant material is homogenous and free from porosity and inclusions. The starting material is then processed, preferably by hot rolling, to an intermediate thickness which is selected so that the subsequent required amount of cold rolling produces a sheet or strip having a thickness appropriate for use in razor blades.
Because the above-identified material is originally processed by hot working in the austenite range and is then cooled, some of the precipitate forming materials (titanium, aluminum, copper, silicon, manganese, and molybdenum) will be in a non-equilibrium-supersaturated condition. There is a thermodynamic driving force which tends to move the supersaturated elements in the direction of equilibrium by causing the nucleation and growth of particles which provide increased strength and hardness. But the nucleation and growth processes which produce the particles are extremely slow at temperatures below about 300 degrees C.
Following the cold rolling step, strengthening precipitates are formed by heat treatment at temperatures between 300 degrees C. and 650 degrees C. for a time of between 1 minute and 20 hours. Preferably, the temperature range is between about 420 degrees C. and 500 degrees C. and the time is between about 2 minutes and 10 hours. The resultant microstructure comprises a matrix having a largely martensitic structure containing strengthening particles based on at least one of Ti, Al, Cu, Si, or Mo.
In addition, the resultant material will have a thickness appropriate for use in razor blade applications, and a hardness in excess of about 600 HV (measured at 1 Kg) and preferably between about 620 HV and 800 HV (measured at 1 Kg), and will have substantial corrosion resistance as the result of the presence of a substantial amount of chromium (preferably more than about 9%) and nickel in the matrix.
The ultimate hardness of the material is dependant upon, among other things, the extent of the cold reduction, the heat treat temperature for any post cold reduction heat treatment, and the amount of time during which the material is held at the heat treat temperature. Referring now to
Referring now to
A sharpened edge may be produced on the razor blade made from the above-described material by using conventional grinding techniques. The sharpened edge may be coated with one or more layers of conventional coatings including, but not limited to chromium and alloys based on chromium, various precious metals (including, but not limited to, platinum, rhodium, iridium, and osmium), alloys based on chromium and precious metals and mixtures thereof, ceramics, diamond-like carbon, amorphous diamond, and polymers such as Teflon™, Krytox 1000™, and Dryfilm LXE™.
Although this invention has been shown and described with respect to the detailed embodiments thereof, it will be understood by those of skill in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiments disclosed in the above detailed description, but that the invention will include all embodiments falling within the scope of the above description.
This application claims the benefits of U.S. Provisional Patent Application Ser. No. 60/685,714, filed on May 27, 2005, the contents of which are incorporated herein by reference in their entirety.
Number | Date | Country | |
---|---|---|---|
60685714 | May 2005 | US |