Abstract

A reactive disazo dye of the formula (I) D1—Y—D2 wherein each of D1 and D2 is a chromophore of the formula (II) in which X is fluorine, chlorine or optionally substituted pyridinium, an SO3H is present in the 5-or 6-position of the naphthalene nucleus, n is 0 or 1, and Y is a bridging group or a sulphonic acid salt of the dye of formula (I). The dyes may be used for dyeing, printing or ink-jet printing, for example, of textile materials and paper and are particularly valuable for coloring cellulosic textile materials.

Description

This invention relates to reactive dyes having a bridging group between triazinylamino groups each attached to a chromophore.

GB-A-1283771 and EP-A-0625551 disclose respective general ranges of reactive dyes of the formula (A)

where D is a chromophore (which in the case of GB-A-1283771 is specifically a naphthylazo-phenylene or -naphthalene containing at least 3 sulphonic acid groups and in the case of EP-A-0625551 is any of a wide range of chromophores), R is H or an optionally substituted C 1-4 alkyl group and X specifically a linking group which, in the case of GB-A-1283771, is an aromatic group selected from phenylene, diphenylene and naphthalene nuclei, and in the case of EP-A-0625551 is an aliphatic linking group, the group —NHXNH— forming a bridging group between receptive triazine nuclei. The dyes of GB-A-1283771 offer a degree of fixation over a wide range of liquor to goods ratios and provide shades of very good light fastness, while those of EP-A-0625551 show good fastness and build up properties.

JP-A-62-172062 discloses a wide range of dyestuffs in which chromophores are linked by the specific group

wherein Y is hydrogen, halogen or alkyl and Z is the reactive group —CH═CH 2 or —CH 2 CH 2 OSO 3 H.

One of many examples of dyes disclosed has the following formula

In our WO-A-99/05224, we describe a range of dyes in which the bridging group is derived from an aminoalkyl piperazine, which dyes have the formula (B)

wherein:

each of R 1 , R 2 , R 3 and R 4 , independently, is H or an optionally substituted alkyl group;

each of X 1 and X 2 , independently, is a labile atom or group;

each of x and y, independently, is 0 or 1 and at least one of x and y is 1;

each of a and b, independently, is 2 to 5;

z is zero or is 1 to 4; and

when each of x and y is 1, a>b;

the or each R 5 , independently, is alkyl; and

each of D 1 and D 2 , independently, is a monoazo or polyazo chromophore, or a metallized derivative thereof.

We have found surprisingly that if, in dyes of the above formula (A), the chromophore D is a particular disazo dye, defined below, then such dyes, especially when used for exhaust dyeing of cellulosic materials, can exhibit excellent all-round fastness properties and build-up and compatibility with other dyes whose preferred exhaust temperature is 80° C. or, more preferably, above.

Thus, according to one aspect, the invention provides a dye of the formula (I)

D 1 —Y—D 2   (I)

wherein each of D 1 and D 2 independently is a chromophore of the formula

in which

X is fluorine, chlorine or optionally substituted pyridinium;

an SO 3 H is present in the 5- or 6-position (preferably the 6-position) of the naphthalene nucleus;

n is zero or 1 (preferably 1); and

in which

Z is a C 5-12 aliphatic or aromatic cyclic hydrocarbon group, optionally additionally containing at least one hetero atom selected from N, O and S and optionally substituted by at least one of C 1-4 alkyl and SO 3 H (or a salt thereof); or

at least two said cyclic hydrocarbon groups linked together; or

a C 1-15 alkylene or C 2-15 alkenylene chain, which said chain

(a) optionally additionally contains, so as to be interrupted or terminated by, at least one of (1) at least one hetero atom selected from N, O and S and (2) at least one C 5-12 aliphatic or aromatic cyclic hydrocarbon group, which said cyclic hydrocarbon group optionally additionally contains at least one hetero atom selected from N, O and S and is optionally substituted by at least one of C 1-4 alkyl and SO 3 H (or a salt thereof); and

(b) is optionally substituted by C 1-4 alkyl, hydroxy-C 1-4 alkyl, amino-C 1-4 alkyl, hydroxyl, carboxyl or amino, which amino group or moiety is optionally substituted by one or two C 1-4 alkyl groups, or by a substituent group which, together with (i) one of R 1 , R 2 and R 3 (each defined below), (ii) the nitrogen atom to which R 1 , R 2 or R 3 is attached and (iii) a chain length of Z between the said nitrogen and the substituent group, forms a heterocyclic group; and

each of R 1 , R 2 and R 3 , independently, is hydrogen, a C 1-4 alkyl, hydroxy-C 1-4 alkyl or amino-C 1-4 alkyl group or each of R 1 and R 2 , together with the respective nitrogen atoms to which they are attached and the chain Z therebetween, forms a heterocyclic group or (as defined above) one of R 1 , R 2 and R 3 , together with (i) the nitrogen atom to which it is attached, (ii) the said substituent group on the chain Z and (iii) the said chain length between the said nitrogen atom and the said substituent group, forms a heterocyclic group; and

Y is other than

 (and preferably contains no reactive group); or a sulphonic acid salt of the said dye of the formula (I).

When X is a substituted pyridinium, preferred substituents are 3-carboxyl, 3-carbonamido and 4-carboxyl.

In one preferred range of dyes, Z is a C 1-10 alkylene chain optionally substituted by at least one group selected from C 1-4 alkyl, hydroxy and carboxyl. Such chains may be free from any hetero atom or may contain additionally at least one hetero atom selected from O and N. More preferably, the chain is a C 2-8 -alkylene chain which is unsubstituted or substituted by at least one group selected from methyl, hydroxy and carboxyl. Still more preferably the chain is of the formula

[CH 2 ] x

wherein x is 2 or 3, which alkylene chain is unsubstituted or substituted by one or two methyl groups or a hydroxy or carboxyl group and each of R 1 , R 2 and R 3 independently is selected from hydrogen, C 1-4 alkyl and hydroxyethyl.

Examples of the group Y in which Z is a C 1-10 alkylene chain optionally substituted by at least one of C 1-4 alkyl, hydroxy and carboxyl are HNC 2 H 4 NH; HNC 3 H 6 NH; HNC 4 H 8 NH; HNC 5 H 10 NH; HNC 6 H 12 NH; HNC 8 H 16 NH; HNC 2 H 4 N(CH 3 ); HNC 3 H 6 N(CH 3 ); HNC 2 H 4 N(C 2 H 4 OH); HNC 2 H 4 N(C 3 H 6 OH); HNC 3 H 6 N(C 2 H 4 OH); HNC 2 H 4 N(C 2 H 5 ); HNC 2 H 4 N(n-C 3 H 7 ); HNC 3 H 6 N(C 2 H 5 ); HNC 3 H 6 N(n-C 3 H 7 ); (H 3 C)NC 2 H 4 N(CH 3 ); (H 3 C)NC 3 H 6 N(CH 3 ); (H 3 C)NC 2 H 4 N(C 2 H 5 ); HNC 2 H 4 NH[CH(CH 3 ) 2 ]; (H 5 C 2 )NC 2 H 4 N(C 2 H 5 ); HNC 2 H 4 NH[CH(CH 3 ) (C 2 H 5 )]; HNC 2 H 4 N(n-C 4 H 9 ); HNC 2 H 4 N[CH 2 CH(CH 3 ) (OH)]; HNCH(CH 3 )CH 2 NH; HNC(CH 3 ) 2 CH 2 NH; HNCH 2 CH(OH)CH 2 NH; HNCH 2 C(CH 3 ) 2 CH 2 NH; HNCH(C 2 H 5 )CH 2 NH; HNCH 2 CH(CH 3 )C 3 H 6 NH; HNCH 2 CH(CH 3 )N [CH(CH 3 ) 2 ]; NHCH 2 C(CH 3 ) 2 CH[CH(CH 3 ) 2 ]NH; HNC 2 H 4 S and HNCH(CO 2 H)CH 2 S.

Examples of the group Y in which Z is a C 1-10 alkylene chain additionally containing a hetero atom are HNC 3 H 6 N(CH 3 )C 3 H 6 NH; HNC 2 H 4 OC 2 H 4 OC 2 H 4 NH; and HNC 2 H 4 OC 2 H 4 NH.

The C 1-10 alkylene chain of Z may additionally contain an aliphatic or aromatic ring structure and examples of the group Y in which Z is such a chain are:

where n is 2 or 3, which is an example of the group Y in which Z is C 1-10 alkylene chain interrupted by an aliphatic ring containing at least one hetero atom. Of these groups,

are especially preferred.

Especially preferred examples of the group Y in which Z is a C 1-10 alkylene chain are NHC 2 H 4 NH; NHC 3 H 6 NH; NHCH(CH 3 )CH 2 NH; NHC 2 H 4 N(CH 3 ); NHC 3 H 6 N(CH 3 ); NHCH 2 CH(OH)CH 2 NH; NHC 2 H 4 N(C 2 H 4 OH); NHC(CH 3 ) 2 CH 2 NH; NHC 3 H 6 N(C 2 H 4 OH); NHC 2 H 4 S; NHC 2 H 4 N(C 2 H 5), N(CH 3 )C 2 H 4 N(CH 3 ); NHC 3 H 6 N(C 3 H 7 ); N(C 2 H 4 OH)C 2 H 4 N(C 2 H 4 OH); HNCH(CO 2 H)CH 2 S; N[CH(CH 3 ) 2 ]CH(CH 3 )CH 2 NH; HNC 6 H 12 NH; HNC 3 H 6 N(CH 3 )C 3 H 6 NH; HNC 2 H 4 OC 2 H 4 NH; and HNC 2 H 4 OC 2 H 4 OC 2 H 4 NH.

In another preferred range of dyes, Z is a phenylene group, optionally substituted by a sulphonic acid group or one or more methyl group(s). Examples of the group Y in which Z is a phenylene group are:

or mixtures thereof, for example, a mixture of

In yet another preferred range of dyes Z is a C 1-15 alkylene chain and is substituted by a substituent group, preferably a C 1-10 alkylene group, which, together with (i) one of R 1 , R 2 and R 3 , (ii) the nitrogen atom to which R 1 , R 2 or R 3 is attached and (iii) a chain length of Z between the said nitrogen atom and the substituent group, forms a heterocyclic group. More preferably, the C 1-15 alkylene chain is interrupted by a nitrogen atom which carries the substituent group, for example, in the case where Y is an imino-C 14 alkylpiperazinyl group. Examples of Y in which the group Z includes a heterocyclic ring formed in this manner are:

In another preferred range of dyes, each of R 1 and R 2 , together with the respective nitrogen atoms to which they are attached and the chain Z therebetween, form a heterocyclic group, more preferably a piperazine group.

A dye of the formula (I), given and defined above, can be prepared by a method aspect of the invention, which method comprises allowing at least one reactive disazo dye of the formula (II)

wherein X and n are as defined above and X 1 is a fluorine, chlorine or optionally substituted pyridinium group, to react with a diamine or thioamine of the formula

wherein each of R 1 , R 2 , R 3 and Z is as defined above, at a pH of from 7 to 10, in a proportional amount of two moles of reactive disazo dye (II) per mole of diamine or thioamine (III) or (IV). The reaction may take from 1-12 hours.

The reactive disazo dye of the above formula (II) can be prepared by reacting a disazo dye of the formula (V)

with a triazine of the formula

wherein each of X X 1 and X 2 independently is chlorine, fluorine or optionally substituted pyridinium.

The disazo dye of the formula (V) may be prepared by firstly diazotising 4-acetylamino-2-aminobenzene sulphonic acid and coupling in acid conditions (pH of 2) onto a hydroxynaphthylamine of the formula

and secondly diazotising 2-aminonaphthalene-1,5-disulphonic acid and coupling in neutral conditions (pH of 7) onto the hydroxynaphthylamine. Thereafter, removal of the acetyl protecting group of the amino group meta to the azo linkage yields the disazo dye of the formula (V).

Although dye formulae have been shown in the form of their free acid in this specification, the invention also includes dyes and processes using dyes in the salt form, particularly their salts with alkali metals such as the potassium, sodium, lithium or mixed sodium/lithium salt.

The dyes may be used for dyeing, printing or ink-jet printing, for example, of textile materials and paper.

The process for colouration is preferably performed at a pH of 7.1 to 13, more preferably 10 to 12. pH levels above 7 can be achieved by performing the process for colouration in the presence of an acid-binding agent.

The substrate may be any of a textile material, leather, paper, hair or film, but is preferably a natural or artificial textile material containing amino or hydroxyl groups, for example textile material such as wool, silk, polyamides and modified polyacrylonitrile fibres, and more preferably a cellulosic textile material, especially cotton, viscose and regenerated cellulose, for example, that commercially available as Tencel. For this purpose the dyes can be applied to the textile materials at a pH above 7 by, for example, exhaust dyeing, padding or printing. Textile materials are coloured bright shades and possess good fastness to light and wet treatments such as washing.

The new dyes are particularly valuable for colouring cellulosic textile materials. For this purpose, the dyes are preferably applied to the cellulosic textile material at a pH above 7 in conjunction with a treatment with an acid-binding agent.

Preferred acid-binding agents include alkali metal carbonates, bicarbonates, hydroxides, metasilicates and mixtures thereof, for example, sodium bicarbonate, sodium carbonate, sodium metasilicate, sodium hydroxide and the corresponding potassium salts. The dyes benefit from excellent build-up and high fixation.

At least for cellulosic materials, dyeing may be carried out at a temperature of from 80 to 105° C., preferably 85 to 95° C., still more preferably at about 90° C., a somewhat higher temperature as compared with dyeing carried out with conventional monochlorotriazine exhaust dyes which are generally dyed at temperatures of about 80° C. By operating at this temperature, particularly improved migration is obtained.

The new dyes can be applied to textile materials containing amine groups, such as wool and polyamide textile materials, from a neutral to mildly alkaline dyebath. The dyeing process can be carried out at a constant or substantially constant pH, that is to say the pH of the dyebath remains constant or substantially constant during the dyeing process, or if desired the pH of the dyebath can be altered at any stage of the dyeing process.

The dyes may be in liquid or solid form, for example in granular or powdered form.

We find surprisingly that such dyes provide the following advantageous properties:

a) good all-round fastness;

b) exceptionally good build-up, especially at a dyeing temperature of 90° C.;

c) very strong dyeing;

d) exceptionally good robustness to changes in dyeing conditions, especially temperature, pH and, in particular, dyebath liquor to substrate ratio, leading to overall excellent shade reproducibility;

e) good wash off;

f) good fixation;

g) good aqueous solubility; and

h) good compatibility with other dyes of this type.

Especially preferred embodiments of the invention will now be described in more detail with reference to the following Examples in which all parts and percentages are by weight unless otherwise stated. Although preparation and dyeing with any single dye is exemplified, particular advantages can be seen when dyeing with mixtures of dyes.

EXAMPLE 1

An aqueous solution of sodium 4-acetylamino-2-aminobenzenesulphonate (0.75 mole) and sodium nitrite (390 ml 2N) was added to stirred ice (1 kg) containing concentrated hydrochloric acid (150 ml) over 30 minutes maintaining the temperature below 5° C. Excess nitrite was decomposed with 10% sulphamic acid solution. An aqueous solution of the sodium salt of H-acid (0.5 mole in 600 ml) was added slowly to the well-stirred diazonium salt solution over 45 mins below 5° C. at pH 2. The mixture was stirred below 5° C. for 2 h, and then allowed to warm to room temperature overnight. The intermediate (A) was screened off and dried to a damp paste at 40° C.

An aqueous solution of sodium 2-aminonaphthalene-1,5-disulphonate (0.12 mole in 200 ml water) and sodium nitrite (60 ml 2N) was added to stirred ice (200 g) containing concentrated hydrochloric acid (30 ml) over 30 minutes maintaining the temperature below 5° C. Stirring was continued for a further 30 mins when excess nitrite was decomposed with 10% sulphamic acid solution. Intermediate (A) (ca 0.1 mole) in water (800 ml) was treated with sufficient concentrated NaOH solution to ensure solution and cooled to below 5° C. This was added in a steady stream to the diazonium solution below 5° C. whilst the pH gradually rose to 4 when coupling commenced. After 2 h at pH 4 below 5° C. the pH was raised to 7 and the solution stirred overnight whilst warming to room temperature. The solution was filtered, the filtrate concentrated, and treated with methylated spirit to precipitate intermediate (B). This could be purified by redissolving in water and re-precipitating.

The protecting acetyl group was removed from intermediate (3) (0.1 mole) by hydrolysis with KOH (112 g) in aqueous solution at 55° C. for 2.5 h. The alkaline solution was neutralised with hydrochloric acid and concentrated to give successive crops of deacetylated intermediate (C). This (0.0262 mole) was dissolved in water (600 ml) and cooled to below 5° C. and then treated with excess cyanuric chloride (5.08 g; 0.0275 mole) dissolved in acetone. The well-stirred mixture was maintained at pH 6-6.5 for 2 h, after which insolubles were filtered off. The filtrate (containing 0.0131 mole dye (D)) was stirred with ethylenediamine (0.4 g; 0.00655 mole) overnight at pH 10. The pH was then adjusted to 7 and the reaction mixture concentrated. Addition of methylated spirit precipitated the product (1; below) as a blue powder, which could be purified by dialysis. As can be seen from Table 1, this had λ max =616 nm, ε max =86500, ½-band width (HBW)=117nm, and dyed cotton a greenish-navy shade with excellent all-round fastness properties.

EXAMPLES 2-30

By replacing the ethylenediamine of Example 1 by an alternative diamine or mercaptoalkylamine, LH 2 , analogues of (1) differing in the nature of the linking group, L, have also been prepared, as listed in Table 1.

TABLE 1
Exam-		Shade
ple		on	λ max		HBW
number	L in structure (1)	cotton	nm	ε max	nm
1	NHC 2 H 4 NH	greenish	616	86,500	117
		navy
2	1,3-NHC 6 H 4 NH	greenish	616	83,200	123
		navy
3		greenish navy	613	91,000	117
4	NHC 3 H 6 NH	greenish	617	91,100	116
		navy
5	NHCH(Me)CH 2 NH	greenish	615	88,900	114
		navy
6	NHC 2 H 4 N(Me)	greenish	616	82,700	117
		navy
7	NHC 3 H 6 N(Me)	greenish	616	100,200	112
		navy
8	NHCH 2 CH(OH)CH 2 NH	greenish	616	91,500	114
		navy
9	1,4-NHC 6 H 4 N(Me)	greenish
		navy
10	1,4-NHC 6 H 4 CH 2 NH	greenish	616	88,200	109
		navy
11		greenish navy	616	83,900	117
12	NHC 2 H 4 N(C 2 H 4 OH)	greenish	616	89,900	116
		navy
13	NHC(Me) 2 CH 2 NH	greenish
		navy
14	NHC 3 H 6 N(C 2 H 4 OH)	greenish	616	89,600	113
		navy
15	NHC 2 H 4 S	greenish	615	90,100	123
		navy
16	1,3-NHC 6 H 4 CH 2 N(Me)	greenish
		navy
17	NHC 6 H 12 NH	greenish
		navy
18	NHC 2 H 4 N(C 2 H 5 )	greenish
		navy
19	NHC 3 H 6 N(Me)C 3 H 6 NH	greenish	622	108,400	110
		navy
20		greenish navy
21	1,4-NHC 6 H 4 NH	greenish
		navy
22	N(Me)C 2 H 4 N(Me)	greenish
		navy
23	NHC 2 H 4 OC 2 H 4 NH	greenish
		navy
24		greenish navy
25	NHC 3 H 6 N(C 3 H 7 )	greenish
		navy
26	N(C 2 H 4 OH)C 2 H 4 N(C 2 H 4 OH)	greenish
		navy
27	NHC 2 H 4 (OC 2 H 4 ) 2 NH	greenish
		navy
28		greenish navy
29	HNCH(CO 2 H)CH 2 S	greenish
		navy
30	N(i-Pr)CH(Me)CH 2 NH	greenish
		navy
31	(Et)NC 2 H 4 N(Me)	greenish	616	104,700	113
		navy
32	HNC 2 H 4 N(C 3 H 7 )	greenish	616	99,900	113
		navy

EXAMPLES 33-62

Each of the dyes prepared in Examples 1-32 was applied to cotton by exhaust dyeing at 90° C. at a liquor :goods ratio of 10:1 and in the presence of salt and soda ash. In each case, the dye was found to have excellent build-up, extremely high fixation efficiency and good all round fastness properties.

Claims

1. A dye of the formula (I):D1—Y—D2 wherein each of D1 and D2 independently is a chromophore of the formula (II) in which X is fluorine, chlorine or optionally substituted pyridinium;an SO3H is present in the 5- or 6- position of the naphthalene nucleus; n is zero or 1; and Y is the group  or a sulphonic acid salt of the dye of formula (I).

2. The dye according to claim 1, having the formula:

3. A method of preparing a dye of the formula (I) of claim 1, or a sulphonic acid salt thereof, which method comprises allowing at least one reactive disazo dye of the formula (VI): wherein X and n are as defined in claim 1 and X1 is a fluorine, chlorine or optionally substituted pyridinium group, to react with a diamine of the formula (III′): at a pH of from 7 to 10, in a proportional amount of two moles of reactive disazo dye (VI) per mole of diamine (III′).

4. The method according to claim 3, which includes the preliminary step of preparing the reactive disazo dye of the formula (VI) by reacting a disazo dye of the formula (V): wherein n is zero or 1, with a triazine of the formula: wherein each of X, X1 and X2 independently is chlorine, fluorine or optionally substituted pyridinium.

5. The method according to claim 3, wherein the product is a dye of the formula

6. A process for the coloration of a substrate, which process comprises applying to the substrate, at a pH above 7, a dye according to claim 1.

7. The process according to claim 6, wherein the dye is applied to the substrate by exhaust dyeing, padding or printing.

8. The process according to claim 7, wherein the dye is applied to the substrate by exhaust dyeing at a temperature of from 80 to 105° C.

9. The process according to claim 8, wherein the exhaust dyeing is carried out at a temperature of 85° C. to 95° C.