Claims
- 1. A ready-to-use microalloyed steel wire, the steel comprising:
- a) from 0.2% by weight to 0.6% by weight of carbon; and
- b) from 0.08% to 0.5% by weight of an alloying element selected from the group consisting of vanadium, molybdenum, chromium, and mixtures thereof;
- wherein the microalloyed steel consists essentially of cold-hammered annealed martensite; the diameter of the steel wire is from 0.10 mm to 0.50 mm; and the tensile strength of the steel wire is greater than or equal to 2800 MPa.
- 2. The wire according to claim 1, further comprising a metallic alloy coating other than steel that is deposited onto the microalloyed steel.
- 3. The wire according to claim 2, wherein the metallic alloy coating is brass.
- 4. The metal wire according to claim 1, wherein the microalloyed steel comprises from 0.3% to 0.5% by weight of carbon.
- 5. The wire according to claim 1, wherein the microalloyed steel comprises approximately 0.4% by weight of carbon.
- 6. The wire according to claim 1, wherein the microalloyed steel comprises: 0.3%.ltoreq.Mn.ltoreq.0.6% by weight; 0.1%.ltoreq.Si.ltoreq.0.3% by weight; P.ltoreq.0.02% by weight; and S.ltoreq.0.02% by weight.
- 7. The wire according to claim 1, wherein the microalloyed steel comprises less than or equal to 0.3% by weight of the alloying element.
- 8. The wire according to claim 1, wherein the alloying element is vanadium.
- 9. The wire according to claim 1, wherein the microalloyed steel comprises greater than or equal to 0.2% by weight of a chromium alloying element.
- 10. The wire according to claim 1, wherein the tensile strength of the wire is greater than or equal to 2900 MPa.
- 11. The wire according to claim 1, wherein the diameter of the wire is from 0.15 mm to 0.40 mm.
- 12. A process for producing a ready-to-use microalloyed steel wire, the process comprising the steps of:
- a) deforming a microalloyed steel wire rod to a diameter of less than 3 mm, wherein the steel comprises from 0.2% by weight to 0.6% by weight of carbon, and from 0.08% by weight to 0.5% by weight of an alloying element selected from the group consisting of vanadium, molybdenum, chromium, and mixtures thereof;
- b) heating the deformed wire above the point of transformation AC3 to give it a homogeneous austenitic structure;
- c) cooling the wire at least almost to the end point of martensitic transformation M.sub.F at a cooling rate of greater than or equal to 60.degree. C./s in order to obtain a structure consisting essentially of martensite;
- d) heating the wire to an annealing temperature in the range of 250.degree. C. and 700.degree. C. in order to cause the formation for the steel of a precipitation of at least one carbonitride and/or carbide of the alloying element and the formation of a structure consisting essentially of annealed martensite;
- e) cooling the wire to a temperature under 250.degree. C.; and
- f) deforming the wire at a deformation rate .epsilon. of not less than 1.
- 13. The process according to claim 12, further comprising, after step c), the step of depositing at least two metals onto the microalloyed steel wire, said metals being capable of forming by diffusion an alloy other than steel onto the wire.
- 14. The process according to claim 13, wherein the deposited metals are copper and zinc, which provide a brass alloy in step d).
- 15. The process according to claim 12, wherein the microalloyed steel comprises from 0.3% to 0.5% by weight of carbon.
- 16. The process according to claim 12, wherein the microalloyed steel comprises about 0.4% by weight of carbon.
- 17. The process according to claim 12, wherein the microalloyed steel comprises 0.3%.ltoreq.Mn.ltoreq.0.6% by weight; 0.1%.ltoreq.Si.ltoreq.0.3% by weight; P.ltoreq.0.02% by weight; and S.ltoreq.0.02% by weight.
- 18. The process according to claim 12, wherein the microalloyed steel comprises less than or equal to 0.3% by weight of the alloying element.
- 19. The process according to claim 12, wherein the alloying element is vanadium.
- 20. The process according to claim 12, wherein the microalloyed steel comprises 0.2% by weight of a chromium alloying element.
- 21. The process according to claim 12, wherein the cooling rate in step c) is less than 150.degree. C./second.
- 22. The process according to claim 12, wherein the annealing temperature is from 400.degree. C. to 650.degree. C.
- 23. The process according to claim 12, wherein the wire is cooled to room temperature in step e).
- 24. The process according to claim 12, wherein the deformation rate .epsilon. greater than or equal to 3.
- 25. A reinforcing assembly comprising at least one wire according to claim 1.
- 26. An article of manufacture that is reinforced in part by wires according to claim 1.
- 27. A pneumatic tire that is reinforced in part by wires according to claim 1.
- 28. A pneumatic tire comprising a reinforcing assembly according to claim 25.
Priority Claims (1)
Number |
Date |
Country |
Kind |
96 00406 |
Jan 1999 |
FRX |
|
Parent Case Info
This application is a 371 of PCT/FR97/00028 filed Jan. 8, 1997.
PCT Information
Filing Document |
Filing Date |
Country |
Kind |
102e Date |
371c Date |
PCT/FR97/00028 |
1/8/1997 |
|
|
5/3/1999 |
5/3/1999 |
Publishing Document |
Publishing Date |
Country |
Kind |
WO97/26379 |
7/24/1997 |
|
|
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
5167727 |
Kim et al. |
Dec 1992 |
|
5261974 |
Hyodo et al. |
Nov 1993 |
|
5503688 |
Arnaud et al. |
Apr 1996 |
|
Foreign Referenced Citations (4)
Number |
Date |
Country |
0330752 |
Sep 1989 |
EPX |
6336648 |
Dec 1994 |
JPX |
2088257 |
Jun 1982 |
GBX |
WO8402354 |
Jun 1984 |
WOX |