Patent Grant
10388940
There is a need for rechargeable battery systems with enhanced safety which have a high energy density and hence are capable of storing and delivering large amounts of electrical energy per unit volume and/or weight. Such stable high energy battery systems have significant utility in a number of applications including military equipment, communication equipment, and robotics.
There is a need for rechargeable battery systems with enhanced safety which have a high energy density and hence are capable of storing and delivering large amounts of electrical energy per unit volume and/or weight. Such stable high energy battery systems have significant utility in a number of applications including military equipment, communication equipment, and robotics.
An example of a high energy density rechargeable (HEDR) battery commonly in use is the lithium-ion battery.
A lithium-ion battery is a rechargeable battery wherein lithium ions move from the negative electrode to the positive electrode during discharge and back when charging. Lithium-ion batteries can be dangerous under some conditions and can pose a safety hazard. The fire energy content (electrical+chemical) of lithium cobalt-oxide cells is about 100 to 150 kJ per A-h, most of it chemical. If overcharged or overheated, Li-ion batteries may suffer thermal runaway and cell rupture. In extreme cases this can lead to combustion. Also, short-circuiting the battery, either externally or internally, will cause the battery to overheat and possibly to catch fire.
Overcharge:
In a lithium-ion battery, useful work is performed when electrons flow through a closed external circuit. However, in order to maintain charge neutrality, for each electron that flows through the external circuit, there must be a corresponding lithium ion that is transported from one electrode to the other. The electric potential driving this transport is achieved by oxidizing a transition metal. For example, cobalt (Co), from Co3+ to Co4+ during charge and reduced from Co4+ to Co3+ during discharge. Conventionally, Li1−χCoO2 may be employed, where the coefficient χ represents the molar fraction of both the Li ion and the oxidative state of CoO2, viz., Co3+ or Co4+. Employing these conventions, the positive electrode half-reaction for the lithium cobalt battery is represented as follows:
LiCoO2↔Li1−χCoO2+χLi++χe−
The negative electrode half reaction is represented as follows:
χLi++χe−+χC6↔χLiC6
The cobalt electrode reaction is reversible limited to x<0.5, limiting the depth of discharge allowable because of cycle life considerations and the stability of LiCoO2. Overcharge leads to the synthesis of cobalt (IV) oxide, as follows:
LiCoO2↔Li++CoO2+O2+e−
LiCoO2 will decompose into CoO2 and release a large amount of heat and oxygen. The released oxygen will then oxidize the electrolyte, which will lead to thermal runaway. This process is irreversible. Therefore, what is needed is some device or design that can decompose below or before positive decomposition. This device will protect the cell from thermal runaway.
Thermal Runaway:
If the heat generated by a lithium ion battery exceeds its heat dissipation capacity, the battery can become susceptible to thermal runaway, resulting in overheating and, under some circumstances, to destructive results such as fire or violent explosion. Thermal runaway is a positive feedback loop wherein an increase in temperature changes the system so as to cause further increases in temperature. The excess heat can result from battery mismanagement, battery defect, accident, or other causes. However, the excess heat generation often results from increased joule heating due to excessive internal current or from exothermic reactions between the positive and negative electrodes. Excessive internal current can result from a variety of causes, but a lowering of the internal resistance due to separator short circuit caused by the factors such as conductive particles spearing through the separator is one possible cause. Heat resulting from a separator short circuit can cause a further breach within the separator, leading to a mixing of the reagents of the negative and positive electrodes and the generation of further heat due to the resultant exothermic reaction.
Internal Short Circuit:
Lithium ion batteries employ a separator between the negative and positive electrodes to electrically separate the two electrodes from one another while allowing lithium ions to pass through. When the battery performs work by passing electrons through an external circuit, the permeability of the separator to lithium ions enables the battery to close the circuit. Short circuiting the separator by providing a conductive path across it allows the battery to discharge rapidly. A short circuit across the separator can result from improper charging and discharging or cell manufacturing defects such as metal impurities and metal shard formation during electrode production. More particularly, improper charging can lead to the deposition of metallic lithium dendrites on the surface of the negative electrode and grow to penetrate the separator through the nanopores so as to provide a conductive path for electrons from one electrode to the other. In addition, improper discharge at or below 1.5V will cause copper dissolution which can ultimately lead to the formation of metallic copper dendrites on the surface of the negative electrode which can also grow to penetrate the separator through the nanopore. The lower resistance of these conductive paths allows for rapid discharge and the generation of significant joule heat. Overheating and thermal runaway can result.
What was needed was a combination internal current limiter and current interrupter that could, at first, limit the rate of internal discharge resulting from an internal short circuit so as to reduce the generation of Joule heat, if the rate of internal discharge is insufficiently limited, could also interrupt the internal short circuit to further curtail the rate of internal discharge, regardless of the temperature increase, so as to avert fire and/or explosion.
A first aspect of the disclosure is directed to an improved high energy density rechargeable (HEDR) battery of a type including two electrodes of opposite polarity (12 and 14). Each electrode is characterized by its resistivity, by its safe operating temperature range, and its safe charging voltage. The HEDR is further of a type having a separator 2 for separating the two electrodes (12 and 14) and preventing internal discharge there between and at least one electrode (12 or 14) employing a current collector 4 for transferring electrons. The separator 2 is subject to a risk of forming a short circuit. The short circuit can potentially allow a rapid internal discharge between the two electrodes (12 and 14), potentially allowing a rapid production of joule heat therefrom, the rapid production of joule heat potentially allowing a thermal runaway. The two electrodes (12 and 14) are subject to a risk of overcharge above the safe charging voltage and the formation of the short circuit therefrom. The two electrodes (12 and 14) are subject to a risk of thermal runaway above the safe operating temperature range.
The improvement for this first aspect of the disclosure is employable for slowing the rate of internal discharge resulting from the short circuit, for slowing the production of joule heat therefrom, and for reducing the risk of thermal runaway.
The improvement comprises the addition to the HEDR battery of a current limiter 6 combined with a current interrupter 8.
The current limiter 6 forms an electrical coupling between one of the electrodes (12 or 14) and its corresponding current collector 4. The current limiter 6 has a resistivity for resistively impeding current therethrough and, in the event the separator 2 forms the short circuit, for diverting current from the electrode current collector 4 to which it is coupled, and for reducing the rate of the internal discharge between the two electrodes (12 and 14).
The current interrupter 8 has an engaged configuration, a disengaged configuration, and a gas generating component for transitioning said current interrupter 8 from the engaged to the unengaged configuration. The gas generating component also has a trigger for generating a gas. The trigger is selected from the group consisting of temperature triggers and voltage triggers.
The temperature triggers is activatable above the safe operating temperature range.
The voltage triggers is activatable above the safe charging voltage.
In its engaged configuration, the current interrupter 8 electrically couples one of the electrodes (12 or 14) and its corresponding current collector 4 with a laminated connection.
In disengaged configuration, the laminated connection becomes delaminated and the current interrupter 8 forms a nonconductive gap for interrupting the electrical coupling between the electrode (12 or 14) and its corresponding current collector 4.
The current interrupter 8 transitions from its engaged configuration to its disengaged configuration by triggering the gas generating component responsive to the trigger. The resulting generated gas delaminates the laminated connection for interrupting the electrical coupling between the electrode (12 or 14) and its corresponding current collector 4.
In this first aspect of the disclosure, the current limiter 6 and the current interrupter 8, in combination, diminishes the risk of thermal runaway resulting from separator short circuit, electrode overcharge, and electrode overheating.
In one embodiment of this first aspect of the disclosure, the current limiter 6 and the current interrupter 8 are simultaneously incorporated into a protective layer interposed by lamination between the same electrode (12 or 14) and current collector 4.
In another embodiment of this first aspect of the disclosure, the battery is of a type having two current collectors 4, including a first current collector 4 and a second current collector 4. The two electrodes (12 and 14) include a first electrode and a second electrode. The first electrode includes a first portion and a second portion. The second portion of the first electrode is interposed between the first portion of the first electrode and the first current collector 4. The improvement of this embodiment of the disclosure is further characterized by the current limiter 6 being layered between the first portion of the first electrode and the second portion of the first electrode; and the current interrupter 8 being layered between the second portion of the first electrode and the first current collector 4. In a sub-embodiment of this first aspect of the disclosure, the current limiter 6 is layered between the second portion of the first electrode and the first current collector 4, and the current interrupter 8 is layered between the first portion of the first electrode and the second portion of the first electrode.
In another embodiment of this first aspect of the disclosure, the battery is of a type having two current 4, including a first current collector 4 and a second current collector 4 and the two electrodes (12 and 14) including a first electrode and a second electrode, the improvement further characterized wherein. In this embodiment, the current limiter 6 is layered between the first electrode and the first current collector 4; and the current interrupter 8 being layered between the second electrode and the second current collector 4.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 or 14) has a temperature range for safe operation and an internal resistivity therein. In this embodiment, the current limiter 6 has a resistivity greater than the internal resistivity of the electrode (12 or 14) with which said current limiter 6 is layered within the temperature range for safe operation.
In another embodiment of this first aspect of the disclosure, the improvement is further characterized by the current limiter 6 lacking a resistivity transition switch at temperatures within the temperature range for safe operation.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has a temperature range for standard operation. In this embodiment, the current limiter 6 has a resistivity transition with a resistivity less than the internal resistivity of the electrode (12 and/or 14) within the temperature range for standard operation and a resistivity greater than the internal resistivity of the electrode (12 and/or 14) above the temperature range for standard operation.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has a temperature range for standard operation. In this embodiment, the current interrupter 8 is activated by temperature above the temperature range for standard operation.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has a temperature range for standard operation and a temperature range for safe operation. In this embodiment, the current interrupter 8 is activated by temperature above the temperature range for standard operation and within the temperature range for safe operation.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has an internal resistivity within the temperature range for safe operation. In this embodiment, the current limiter 6 has a resistivity greater than the internal resistivity of the electrode (12 or 14) with which said current limiter 6 is layered within the temperature range for safe operation. In an alternative to this embodiment, the current limiter 6 and said current interrupter 8 are simultaneously incorporated into a protective layer interposed by lamination between the same electrode (12 or 14) and current collector 4.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has a voltage range for standard operation. In this embodiment, the current interrupter 8 is activated by voltage above the voltage range for standard operation.
In another embodiment of this first aspect of the disclosure, the battery is of a type wherein each electrode (12 and 14) has a voltage range for standard operation and a voltage range for safe operation. In this embodiment, the current interrupter 8 is activated by voltage above the temperature range for standard operation and within the voltage range for safe operation. In an alternative of this embodiment, the current limiter 6 and current interrupter 8 are simultaneously incorporated into a protective layer interposed by lamination between the same electrode (12 or 14) and current collector 4.
A second aspect of the disclosure is directed to another improved high energy density rechargeable battery of a type including two electrodes (12 and 14) of opposite polarity, a separator 2 separating the two electrodes (12 and 14), and at least one current collector 4 electrically coupled to one of the electrodes (12 or 14). The separator 2 prevents internal discharge between the two electrodes (12 and 14). Failure of the separator 2 potentially causes an internal discharge between the two electrodes (12 and 14). The internal discharge causes the generation of joule heat of potential danger.
The improvement for this second aspect of the disclosure comprises a thermally activatable current interrupter 8 and a voltage activatable current interrupter 8.
The thermally activatable current interrupter 8 is layered by lamination between one of the current collectors 4 and one of the electrodes (12 or 14). The thermally activatable current interrupter 8, when unactivated, electrically couples the current collector 4 to the electrode (12 or 14) with which it is layered, said current interrupter 8. When activated, the thermally activatable current interrupter 8 delaminates from the current collector 4 for forming a nonconductive gap for electrically decoupling the current collector 4 from the electrode (12 or 14) with which it had been layered. The electrical decoupling serves to slow the rate of internal discharge between the two electrodes (12 and 14) in the event of separator failure.
The voltage activatable current interrupter 8 is layered by lamination between one of the current collectors 4 and one of the electrodes (12 or 14). The voltage activatable current interrupter 8, when unactivated, electrically couples the current collector 4 to the electrode (12 or 14) with which it is layered. The current interrupter 8, when activated, delaminates from the current collector 4 by forming a nonconductive gap for electrically decoupling the current collector 4 from the electrode (12 or 14) with which it had been layered. The resultant electrical decoupling serves to slow the rate of internal discharge between the two electrodes (12 and 14) in the event of separator failure. In this second aspect of the disclosure, activation of either the thermally activated current interrupter 8 or the voltage activated current interrupter 8 in the event of separator failure, slows the generation joule heat for diminishing the potential danger.
A second aspect of the disclosure is directed to a process for avoiding thermal runaway within a high energy density rechargeable battery undergoing internal discharge due to separator failure. The process comprises the step of delaminating an electrode (12 or 14) within the battery from its current collector 4 by generating a gas from a heat sensitive gas generating material within an interrupt layer interposed between the electrode (12 or 14) and current collector 4. The delamination electrically decouples the electrode (12 or 14) from its current collector 4 for slowing the rate of internal discharge.
A third aspect of the disclosure is directed to a process for avoiding thermal runaway within a high energy density rechargeable battery at risk of suffering from separator failure due to voltage overcharge. The process comprises the step of delaminating an electrode (12 or 14) within the battery from its current collector 4 by generating a gas from a voltage sensitive gas generating material within an interrupt layer interposed between the electrode (12 or 14) and current collector 4. The delamination electrically decouples the electrode (12 or 14) from its current collector 4 for interrupting the voltage overcharge.
A fourth aspect of the disclosure is directed to a process for avoiding thermal runaway within a high energy density rechargeable battery at risk of suffering from separator failure due to voltage overcharge. The process comprises the step of delaminating an electrode (12 or 14) within the battery from its current collector 4 by generating a gas from a voltage or temperature sensitive material that will form the gas indirectly through its decomposition compound (at the high voltage) that will react with the battery components such as electrolyte and electrodes (12 and 14). This voltage or temperature sensitive material will be still called as gas generator, and can be within an interrupt layer interposed between the electrode (12 or 14) and current collector 4. The delamination electrically decouples the electrode (12 or 14) from its current collector 4 for interrupting the voltage overcharge.
The present disclosure is described more fully herein with reference to the accompanying drawings, in which some exemplary embodiments of the present disclosure are shown. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present disclosure. Accordingly, the drawings and description are to be regarded as illustrative in nature and not restrictive. In the drawings, the thicknesses of layers and regions may be exaggerated for clarity.
The terminology used herein is for the purpose of describing some particular exemplary embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
It will be understood that, although the terms “first,” “second,” etc. may be used herein to describe various members, elements, regions, layers and/or parts, these members, elements, regions, layers and/or parts should not be limited by these terms. These terms may be used merely to distinguish one member, element, region, layer and/or part from another member, element, region, layer and/or part. Thus, for example, a first member, element, region, layer and/or part discussed below could be termed a second member, element, region, layer and/or part without departing from the teachings of the present disclosure.
Current Limiter
A first aspect of the disclosure is directed to an improved HEDR battery of a type including an anode energy layer 12, a cathode energy layer 14, a separator 2 between the anode energy layer 12 and the cathode energy layer 14 for preventing internal discharge thereof, and at least one current collector 4 for transferring electrons to and from either the anode or cathode energy layer. The anode and cathode energy layers each have an internal resistivity. The HEDR battery has a preferred temperature range for discharging electric current and an upper temperature safety limit. The improvement is employable, in the event of separator failure, for limiting the rate of internal discharge through the failed separator and the generation of joule heat resulting therefrom. More particularly, the improvement comprises a resistive layer 6 interposed between the separator and one of the current collectors 4 for limiting the rate of internal discharge through the failed separator in the event of separator failure. The resistive layer 6 has a fixed resistivity at temperatures between the preferred temperature range and the upper temperature safety limit. The fixed resistivity of the resistive layer 6 is greater than the internal resistivity of either energy layer. The resistive layer 6 helps the battery avoid temperatures in excess of the upper temperature safety limit in the event of separator failure.
Some embodiments of the present disclosure include an improved high energy density rechargeable battery are of a type including:
In some embodiments, the current interrupter is triggered by temperature.
In some embodiments, the current interrupter includes a layer containing a single gas generating component triggered by temperature.
In some embodiments, the current interrupter is triggered by voltage.
In some embodiments, the current interrupter includes a layer containing a single gas generating component triggered by voltage.
In some embodiments, the current interrupter is triggered by temperature and voltage.
In some embodiments, the current interrupter includes a layer containing a single gas generating component triggered by temperature and voltage.
In some embodiments, the current interrupter includes a layer containing two gas generating components, one triggered by temperature and the other triggered by voltage.
In some embodiments, the current interrupter may include a layer containing one or more inorganic gas generating compounds that generate gas at a specific temperature or voltage.
In some embodiments, the inorganic gas generating compounds are selected from the group consisting of CaCO3, La2(CO3)3, Na2SO3, ZnCO3Zn(OH)2, CuCO3Cu(OH)2, and Cu(NO3)2 as disclosed in
In some embodiments, the current interrupter may include a layer containing one or more organic gas generating compounds that generate gas at a specific temperature or voltage.
In some embodiments, the organic gas generating compounds are selected from the group consisting of Carbopol, Torlon® AI-50, CMC, and PVDF as disclosed in
In some embodiments, the current interrupter may include a layer containing a combination of inorganic and organic gas generating compounds that generate gas at a specific temperature or voltage.
In some embodiments of the improved high energy density rechargeable battery, said current limiter and said current interrupter are simultaneously incorporated into a protective layer interposed by lamination between the same electrode and current collector, as disclosed in
In some embodiments of the improved high energy density rechargeable battery, said current limiter and said current interrupter triggered by both temperature and voltage are simultaneously incorporated into a protective layer interposed by lamination between the same electrode and current collector, as disclosed in
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the first electrode including a first portion and a second portion, the second portion of the first electrode interposed between the first portion of the first electrode and the first current collector, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the first electrode including a first portion and a second portion, the second portion of the first electrode interposed between the first portion of the first electrode and the first current collector, the improvement further characterized, wherein said current limiter and said current interrupter are simultaneously incorporated into a protective layer interposed by lamination between the first portion and the second portion of the first electrode, as disclosed in
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the first electrode including a first portion and a second portion, the second portion of the first electrode interposed between the first portion of the first electrode and the first current collector, the improvement further characterized, wherein said current limiter and said current interrupter triggered by both temperature and voltage are simultaneously incorporated into a protective layer interposed by lamination between the first portion and the second portion of the first electrode, as disclosed in
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the second electrode including a first portion and a second portion, the first portion of the second electrode interposed between the second portion of the second electrode and the second current collector, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the second electrode including a first portion and a second portion, the first portion of the second electrode interposed between the second portion of the second electrode and the second current collector, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the first electrode including a first portion and a second portion, the first portion of the second electrode interposed between the second portion of the second electrode and the second current collector, the improvement further characterized, wherein said current limiter and said current interrupter are simultaneously incorporated into a protective layer interposed by lamination between the first portion and the second portion of the second electrode, as disclosed in
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector, the two electrodes including a first electrode and a second electrode, and the first electrode including a first portion and a second portion, the second portion of the first electrode interposed between the first portion of the first electrode and the first current collector, the improvement further characterized wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type having two current collectors, including a first current collector and a second current collector and the two electrodes including a first electrode and a second electrode, the improvement further characterized, wherein:
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a temperature range for safe operation and an internal resistivity therein, the improvement further characterized wherein said current limiter having a resistivity greater than the internal resistivity of the electrode with which said current limiter is layered within the temperature range for safe operation.
In some embodiments of the improved high energy density rechargeable battery, the improvement further characterized, wherein said current limiter lacking a resistivity transition switch at temperatures within the temperature range for safe operation.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a temperature range for standard operation, the improvement further characterized, wherein said current limiter having a resistivity transition with a resistivity less than the internal resistivity of the electrode within the temperature range for standard operation and a resistivity greater than the internal resistivity of the electrode above the temperature range for standard operation.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a temperature range for standard operation, the improvement further characterized, wherein said current interrupter is activated by temperature above the temperature range for standard operation.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a temperature range for standard operation and a temperature range for safe operation, the improvement further characterized, wherein said current interrupter is activated by temperature above the temperature range for standard operation and within the temperature range for safe operation.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has an internal resistivity within the temperature range for safe operation, the improvement further characterized, wherein said current limiter having a resistivity greater than the internal resistivity of the electrode with which said current limiter is layered within the temperature range for safe operation.
In some embodiments of the improved high energy density rechargeable battery, the improvement further characterized, wherein said current limiter and said current interrupter are simultaneously incorporated into a protective layer interposed by lamination between the same electrode and current collector.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a voltage range for standard operation, the improvement further characterized, wherein said current interrupter is activated by voltage above the voltage range for standard operation.
In some embodiments, the improved high energy density rechargeable battery is of a type, wherein each electrode has a voltage range for standard operation and a voltage range for safe operation, the improvement further characterized, wherein said current interrupter is activated by voltage above the temperature range for standard operation and within the voltage range for safe operation.
In some embodiments of the improved high energy density rechargeable battery, the improvement further characterized, wherein said current limiter and said current interrupter are simultaneously incorporated into a protective layer interposed by lamination between the same electrode and current collector.
Other embodiments of the present disclosure include an improved high energy density rechargeable battery of a type including two electrodes of opposite polarity, a separator separating the two electrodes, and at least one current collector electrically coupled to one of the electrodes, the separator preventing internal discharge between the two electrodes, failure of the separator potentially causing an internal discharge between the two electrodes (as illustrated in
Some embodiments of the present disclosure include a process for avoiding thermal runaway within a high energy density rechargeable battery undergoing internal discharge due to separator failure, the process comprising delaminating an electrode within the battery from its current collector by generating a gas from a heat sensitive gas generating material within an interrupt layer interposed between the electrode and current collector, said delaminating electrically decoupling the electrode from its current collector for slowing the rate of internal discharge.
Some embodiments of the present disclosure include a process for avoiding thermal runaway within a high energy density rechargeable battery at risk of suffering from separator failure due to voltage overcharge (as illustrated in
Definitions
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as is commonly understood by one of ordinary skill in the art to which this disclosure belongs. In the event that there is a plurality of definitions for a term herein, those in this section prevail unless stated otherwise.
As used herein, “high energy density rechargeable (HEDR) battery” means a battery capable of storing relatively large amounts of electrical energy per unit weight on the order of about 50 W-hr/kg or greater and is designed for reuse, and is capable of being recharged after repeated uses. Non-limiting examples of HEDR batteries include metal-ion batteries and metallic batteries.
As used herein, “metal-ion batteries” means any rechargeable battery types in which metal ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of metal-ion batteries include lithium-ion, aluminum-ion, potassium-ion, sodium-ion, magnesium-ion, and others.
As used herein, “metallic batteries” means any rechargeable battery types in which the anode is a metal or metal alloy. The anode can be solid or liquid. Metal ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of metallic batteries include M-S, M-NiCl2, M-V2O5, M-Ag2VP2O8, M-TiS2, M-TiO2, M-MnO2, M-Mo3S4, M-MoS6Se2, M-MoS2, M-MgCoSiO4, M-Mg1.03Mn0.97SiO4, and others, where M=Li, Na, K, Mg, Al, or Zn.
As used herein, “lithium-ion battery” means any rechargeable battery types in which lithium ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of lithium-ion batteries include lithium cobalt oxide (LiCoO2), lithium iron phosphate (LiFePO4), lithium cobalt phosphate (LiCoPO4), lithium excess layered oxides such as (LiMnO3)x(LiMO2) (M=Ni, Co, Mn), olivines, LiMSiO4 (M=iron, Cobalt, Nickel and Vanadium); lithium manganese oxide (LiMn2O4), lithium nickel oxide (LiNiO2), lithium nickel manganese cobalt oxide (LiNiMnCoO2), lithium nickel cobalt aluminum oxide (LiNiCoAlO2), lithium titanate (Li4Ti5O12), lithium titanium dioxide, lithium/graphene, lithium/graphene oxide coated sulfur, lithium-sulfur, lithium-purpurin, and others. Lithium-ion batteries can also come with a variety of anodes including silicon-carbon nanocomposite anodes and others. Lithium-ion batteries can be in various shapes including small cylindrical (solid body without terminals), large cylindrical (solid body with large threaded terminals), prismatic (semi-hard plastic case with large threaded terminals), and pouch (soft, flat body). Lithium polymer batteries can be in a soft package or pouch. The electrolytes in these batteries can be a liquid electrolyte (such as carbonate based or ionic), a solid electrolyte, a polymer based electrolyte or a mixture of these electrolytes.
As used herein, “aluminum-ion battery” means any rechargeable battery types in which aluminum ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of aluminum-ion batteries include AlnM2 (XO4)3, wherein X═Si, P, S, Mo, As, and others; and M=Fe, Ca, Mg, V, Cr and others; aluminum transition-metal oxides (AlxMO2 wherein M=Fe, Mn, Ni, Mo, Co, Cr, Ti, V and others) such as Alx (V4O8), AlxNiS2, AlxFeS2, AlxVS2 and AlxWS2 and others.
As used herein, “potassium-ion battery” means any rechargeable battery types in which potassium ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of potassium-ion batteries include KnM2(XO4)3, wherein X═Si, P, S, Mo, As, and others; and M=Fe, Ca, Mg, V, Cr and others; potassium transition-metal oxides (KMO2 wherein M=Fe, Mn, Ni, Mo, Co, Cr, Ti, V and others), and others.
As used herein, “sodium-ion battery” means any rechargeable battery types in which sodium ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of sodium-ion batteries include NanM2(XO4)3, wherein X═Si, P, S, Mo, As, and others; and M=Fe, Ca, Mg, V, Cr and others; NaV1−xCrxPO4F, NaVPO4F, Na4Fe3(PO4)2(P2O7), Na2FePO4F, Na2FeP2O7, Na2/3[Fe1/2Mn1/2]O2, Na(Ni1/3Fe1/3Mn1/3)O2, NaTiS2, NaFeF3; Sodium Transition-Metal Oxides (NaMO2 wherein M=Fe, Mn, Ni, Mo, Co, Cr, Ti, V and others) such as Na2/3[Fe1/2Mn1/2]O2, Na(Ni1/3Fe1/3Mn1/3)O2, NaxMo2O4, NaFeO2, Na0.7CoO2, NaCrO2, NaMnO2, Na0.44MnO2, Na0.7MnO2, Na0.7MnO2.25, Na2/3Mn2/3Ni1/3O2, Na0.61Ti0.48Mn0.52O2; Vanadium Oxides such as Na1+xV3O8, NaxV2O5, and NaxVO2 (x=0.7, 1); and others.
As used herein, “magnesium-ion battery” means any rechargeable battery types in which magnesium ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of magnesium-ion batteries include MgnM2(XO4)3, wherein X═Si, P, S, Mo, As, and others; and M=Fe, Ca, Mg, V, Cr and others; magnesium Transition-Metal Oxides (MgMO2 wherein M=Fe, Mn, Ni, Mo, Co, Cr, Ti, V and others), and others.
As used herein, “silicon-ion battery” means any rechargeable battery types in which silicon ions move from the negative electrode to the positive electrode during discharge and back when charging. Non-limiting examples of silicon-ion batteries include SinM2(XO4)3, wherein X═Si, P, S, Mo, As, and others; and M=Fe, Ca, Mg, V, Cr and others; Silicon Transition-Metal Oxides (SiMO2 wherein M=Fe, Mn, Ni, Mo, Co, Cr, Ti, V and others), and others.
As used herein, “binder” means any material that provides mechanical adhesion and ductility with inexhaustible tolerance of large volume change. Non-limiting examples of binders include styrene butadiene rubber (SBR)-based binders, polyvinylidene fluoride (PVDF)-based binders, carboxymethyl cellulose (CMC)-based binders, poly(acrylic acid) (PAA)-based binders, polyvinyl acids (PVA)-based binders, poly(vinylpyrrolidone) (PVP)-based binders, and others.
As used herein, “conductive additive” means any substance that increases the conductivity of the material. Non-limiting examples of conductive additives include carbon black additives, graphite nonaqueous ultrafine carbon (UFC) suspensions, carbon nanotube composite (CNT) additives (single and multi-wall), carbon nano-onion (CNO) additives, graphene-based additives, reduced graphene oxide (rGO), conductive acetylene black (AB), conductive poly(3-methylthiophene) (PMT), filamentary nickel powder additives, aluminum powder, and others.
As used herein, “metal foil” means any metal foil that under high voltage is stable. Non-limiting examples of metal foils include aluminum foil, copper foil, titanium foil, steel foil, nano-carbon paper, graphene paper, carbon fiber sheet, and others.
As used herein, “ceramic powder” means any electrical insulator or electrical conductor that hasn't been fired. Non-limiting examples of ceramic powder materials include barium titanate (BaTiO3), zirconium barium titanate, strontium titanate (SrTiO3), calcium titanate (CaTiO3), magnesium titanate (MgTiO3), calcium magnesium titanate, zinc titanate (ZnTiO3), lanthanum titanate (LaTiO3), and neodymium titanate (Nd2Ti2O7), barium zirconate (BaZrO3), calcium zirconate (CaZrO3), lead magnesium niobate, lead zinc niobate, lithium niobate (LiNbO3), barium stannate (BaSnO3), calcium stannate (CaSnO3), magnesium aluminum silicate, sodium silicate (NaSiO3), magnesium silicate (MgSiO3), barium tantalate (BaTa2O6), niobium oxide, zirconium tin titanate, silicon dioxide (SiO2), aluminum oxide (Al2O3), titanium dioxide (TiO2), and others.
As used herein, “gas generator material” means any material which will decompose at the high temperature or high voltage to produce a gas either directing from the gas generator material or indirectly from reaction of the decomposition products produced from the gas generator material with other materials contained within the battery (e.g. the electrolyte and electrodes). Non-limiting examples of gas generator materials include inorganic carbonates such as Mn(CO3)m, Mn(SO3)m, Mn(NO3)m, 1Mn2Mn(CO3)m, NaSiO3*H2O, CuCO3CU(OH)2, and others and organic carbonates such as polymethacrylic [—CH2—C(CH3)(COOM)-]p and polyacrylate salts [—CH2—CH(COOM)-]p, and others wherein M, 1M, 2M are independently selected from the group consisting of Ba, Ca, Cd, Co, Cu, Fe, K, Li, Mg, Mn, Na, Ni, Pb, Sr, and Zn; n is 1-3 and m is 1-4. In some embodiments, M is independently selected from the group consisting of an ammonium ion, pyridinium ion and a quaternary ammonium ion. In some embodiments, the gas generator material may decompose to produce a liquid (e.g. water). The liquid may react with other materials contained within the battery to form a gas and this gas will delaminate the electrode. (E.g. water reacting with the electrolyte [LiFP6] to form gaseous HF and lithium in the negative to form hydrogen gas (H2). If the temperature of the cell exceeds the vaporization temperature of the liquid, the liquid may also undergo a phase transition to form a gas and this gas will also delaminate the electrode.
Layers were coated onto metal foils by an automatic coating machine (compact coater, model number 3R250W-2D) produced by Thank-Metal Co., Ltd. Layers are then compressed to the desired thickness using a calender machine (model number X15-300-1-DZ) produced by Beijing Sevenstar Huachuang Electronics Co., Ltd.
The disclosure will be described more in detail below using examples, but the disclosure is not limited to the examples shown below.
The following abbreviations have the indicated meanings:
Resistance layer and electrode active layer preparation and cell assembly.
Generic example of a resistance layer preparation steps (first layer):
Generic example of the electrode preparation (on the top of the first layer):
Cell assembly:
ix. Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr.
Impact test (See
Overcharge test.
Resistance (Thermal) Measurement Test.
Cycle Life procedure.
Discharge test at 1 A, 3 A, 6 A, 10 A.
The cell was tested in a chamber with a temperature control to 50° C.
Preparation of baseline electrodes, positive and negative electrodes, and the completed Cell #1 for the evaluation in the resistance measurement, discharge capability tests at 50° C., impact test, and cycle life test.
A) Preparation of POS1A as an Example of the Positive Electrode Preparation.
i) Dissolve PVDF (21.6 g) into NMP (250 g); ii) Add carbon black (18 g) and mix for 15 minutes at 6500 rpm; iii) Add LiNi0.5Mn0.3Co0.2O2 (NMC) (560.4 g) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Some NMP may be added for the viscosity adjustment; v) Coat this slurry onto 15□ Coat this slurry onto 15 the viscosity adjustment; e slurry; pability tests at 50eted Cell ° C. and the second heat zone to about 130° C. to evaporate off the NMP. The final dried solid loading is about 15.55 mg/cm2. The positive layer was then compressed to a thickness of about 117 μm. The electrode made here is called as zero voltage against graphite electrode and is ready for the impedance measurement at 0 V in relation to the temperature, and the dry for the cell assembly.
B) Preparation of NEG2A as an Example of the Negative Electrode Preparation
i) Dissolve CMC (5.2 g) into deionized water (˜300 g); ii) Add carbon black (8.4 g) and mix for 15 minutes at 6500 rpm; iii) Add negative active graphite (JFE Chemical Corporation; Graphitized Mesophase Carbon Micro Bead (MCMB) and Synthetic Graphite (TIMCAL) (378.4 g in total) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Add SBR (solid content 50% suspended in water) (16.8 g) to the slurry formed in Step iii and mix at 6500 rpm for 5 min; v) Adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9□ Coat this slurry onto 9 a smooth coating; r) (16.8 g) to the slurry formed in Step Bead (MCM° C. and the second heat zone to about 100° C. to evaporate off the water. The final dried solid loading is about 9.14 mg/cm2. The negative electrode layer was then compressed to a thickness of about 117 μm. The negative made is ready for the dry for the cell assembly.
C) Preparation of Cell for the Evaluation
i) Punch the electrodes into the pieces with the electrode tab; ii) Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr; iii) Laminate the positive and negative electrodes with the separator as the middle layer; iv) Put the flat jelly-roll made in the Step iii. into the Aluminium composite bag; v) Dry the bag from Step iv. in a 70° C. vacuum oven; vi) Fill the bag from Step v with the LiPF6 containing organic carbonate based electrolyte; vii) Seal the bag from Step vi; viii) Rest for 16 hours; viiii) Charge the cell to 4.2V at C/20 rate for 5 hours and then to 4.2V at 0.5C rate for 2 hours, then rest for 20 minutes, then discharge to 2.8V at 0.5C rate. Under vacuum, puncture the cell to release any gases and then reseal the cell. The cell made here is ready for grading and other tests such as discharging capability test at 50° C., impact test, cycle life test and so on.
Preparation of CaCO3 based gas generator and resistive layer, positive and negative electrodes, and the completed Cell #3 for the evaluation in the resistance measurement, discharge capability tests at 50° C., impact test, over charge, and cycle life test
A) Positive POS3B as an Example of a Gas Generator and Resistive Layer (1st Layer) Preparation.
i) Dissolve Torlon®4000TF (0.8 g) into NMP (10 g); ii) Dissolve PVDF (4.8 g) into NMP (˜70 g); iii) Mix solution prepared in Step i and ii, and then add carbon black (0.32 g) and mix for 10 minutes at 6500 rpm; iv) Add nano CaCO3 powder (34.08 g) to the solution from Step iii and mix for 20 minutes at 6500 rpm to form a flowable slurry; v) Coat this slurry onto 15□ Coat this slurry onto 15 6500 rpm to form a flowable slurry; 6500 rpm; sts at 50 completed Cell #° C. and the second heat zone to about 165° C. to evaporate off the NMP. The final dried solid loading is about 1 mg/cm2.
B) Preparation of POS3A as an Example of the Positive Electrode Preparation (2nd Layer).
i) Dissolve PVDF (21.6 g) into NMP (250 g); ii) Add carbon black (18 g) and mix for 15 minutes at 6500 rpm; iii) Add LiNi1/3Co1/3Mn1/3O2 (NMC) (560.4 g) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Some NMP may be added for the viscosity adjustment; v) Coat this slurry onto POS3B (Example 2A) using an automatic coating machine with the first heat zone set to about 85° and the second heat zone to about 135° C. to evaporate off the NMP. The final dried solid loading is about 19.4 mg/cm2. The positive layer was then compressed to a thickness of about 153 μm. The electrode made here is called as zero voltage against graphite electrode and is ready for the impedance measurement at 0 V in relation to the temperature.
C) Preparation of NEG3A as an Example of the Negative Electrode Preparation
i) Dissolve CMC (13 g) into deionized water (˜1000 g); ii) Add carbon black (20 g) and mix for 15 minutes at the rate of about 6500 rpm; iii) Add negative active graphite (JFE Chemical Corporation; Graphitized Mesophase Carbon Micro Bead (MCMB) and Synthetic Graphite (TIMCAL) (945.92 g in total) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Add SBR (solid content 50% suspended in water) (42 g) to the slurry formed in Step iii and mix at 6500 rpm for 5 min; v) Adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9□ Coat this slurry onto 9 a smooth coating; er) (42 g) to the slurry formed in Step act=8&sqi=2&v° C. and the second heat zone to about 130° C. to evaporate off the water. The final dried solid loading is about 11.8 mg/cm2. The negative electrode layer was then compressed to a thickness of about 159 μm. The negative made is ready for the dry for the cell assembly.
D) Preparation of Cell for the Evaluation
i) Punch the electrodes into the pieces with the electrode tab; ii) Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr; iii) Laminate the positive and negative electrodes with the separator as the middle layer; iv) Put the flat jelly-roll made in the Step iii. into the Aluminium composite bag; v) Dry the bag from Step iv. in a 70° C. vacuum oven; vi) Fill the bag from Step v with the LiPF6 containing organic carbonate based electrolyte; vii) Seal the bag from Step vi; viii) Rest for 16 hours; viiii) Charge the cell to 4.2V at C/50 rate for 8 hours and then to 4.2V at 0.5C rate for 2 hours, then rest for 20 minutes, then discharge to 2.8V at 0.5C rate. Under vacuum, puncture the cell to release any gases and then reseal the cell. The cell made here is ready for grading and other tests such as discharging capability test at 50° C., impact test, cycle life test and so on.
Preparation of 50% Al2O3 and 50% CaCO3 based gas generator and resistive layer, positive and negative electrodes, and the completed Cell #4 for the evaluation in the resistance measurement, discharge capability tests at 50° C., impact test, over charge and cycle life tests:
A) Positive POS4B as an Example of a Gas Generator and Resistive Layer (1st Layer) Preparation.
i) Dissolve Torlon®4000TF (0.8 g) into NMP (10 g); ii) Dissolve PVDF (4.8 g) into NMP (˜70 g); iii) Mix solution prepared in Step i and ii, and then add carbon black (0.32 g) and mix for 10 minutes at 6500 rpm; iv) Add nano CaCO3 powder (17.04 g) and Al2O3 powder (17.04 g) to the solution from Step iii and mix for 20 minutes at 6500 rpm to form a flowable slurry; v) Coat this slurry onto 15□ Coat this slurry onto 15 6500 rpm to form a flowable slurry; 6500 rpm; sts at 50 completed Cell #° C. and the second heat zone to about 165° C. to evaporate off the NMP. The final dried solid loading is about 1 mg/cm2.
B) Preparation of POS4A as an Example of the Positive Electrode Preparation (2nd Layer).
i) Dissolve PVDF (21.6 g) into NMP (250 g); ii) Add carbon black (18 g) and mix for 15 minutes at the rate of about 6500 rpm; iii) Add LiNi1/3Co1/3Mn1/3O2 (NMC) (560.4 g) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Some NMP may be added for the viscosity adjustment; v) Coat this slurry onto POS4B (Example 3A) using an automatic coating machine with the first heat zone set to about 85° C. and the second heat zone to about 135° to evaporate off the NMP. The final dried solid loading is about 19.4 mg/cm2. The positive layer was then compressed to a thickness of about 153 μm. The electrode made here is called as zero voltage against graphite electrode and is ready for the impedance measurement at 0 V in relation to the temperature.
C) Preparation of NEG4A as an Example of the Negative Electrode Preparation
i) Dissolve CMC (13 g) into deionized water (˜1000 g); ii) Add carbon black (20 g) and mix for 15 minutes at 6500 rpm; iii) Add negative active graphite (JFE Chemical Corporation; Graphitized Mesophase Carbon Micro Bead (MCMB) and Synthetic Graphite (TIMCAL) (945.92 g in total) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Add SBR (solid content 50% suspended in water) (42 g) to the slurry formed in Step iii and mix at about 6500 rpm for 5 min; v) Adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9□ m thick Copper foil using an automatic coating machine with the first heat zone set to about 100° C. and the second heat zone to about 130° C. to evaporate off the water. The final dried solid loading is about 11.8 mg/cm2. The negative electrode layer was then compressed to a thickness of about 159 μm. The negative made is ready for the dry for the cell assembly.
D) Preparation of Cell for the Evaluation
i) Punch the electrodes into the pieces with the electrode tab; ii) Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr; iii) Laminate the positive and negative electrodes with the separator as the middle layer; iv) Put the flat jelly-roll made in the Step iii. into the Aluminium composite bag; v) Dry the bag from Step iv. in a 70° C. vacuum oven; vi) Fill the bag from Step v with the LiPF6 containing organic carbonate based electrolyte; vii) Seal the bag from Step vi; viii) Rest for 16 hours; viiii) Charge the cell to 4.2V at C/50 rate for 8 hours and then to 4.2V at 0.5C rate for 2 hours, then rest for 20 minutes, then discharge to 2.8V at 0.5C rate. Under vacuum, puncture the cell to release any gases and then reseal the cell. The cell made here is ready for grading and other tests such as discharging capability test at 50° C., impact test, cycle life test (
Preparation of Al2O3 and Sodium trisilicate (NaSiO3) mixed based gas generator and resistive layer, positive and negative electrodes, and the completed Cell #5 for the evaluation in the resistance measurement, discharge capability tests at 50° C., impact test, over charge, and cycle life tests:
A) Positive POS5B as an Example of a Gas Generator and Resistive Layer (1st Layer) Preparation.
i) Dissolve Torlon®4000TF (0.8 g) into NMP (˜10 g); ii) Dissolve PVDF (4.8 g) into NMP (60 g); iii) Mix solution prepared in Step i and ii, and then add carbon black (0.32 g) and mix for 10 minutes at 6500 rpm; iv) Add nano Al2O3 powder (17.04 g) and NaSiO3 (17.04 g) to the solution from Step iii and mix for 20 minutes at 6500 rpm to form a flowable slurry; v) Coat this slurry onto 15□ Coat this slurry onto 15 6500 rpm to form a flowable slurry; 6500 rpm; sts at 50 and the completed° C. and the second heat zone to about 165° C. to evaporate off the NMP. The final dried solid loading is about 0.7 mg/cm2.
B) Preparation of POS5A as an Example of the Positive Electrode Preparation (2nd Layer).
i) Dissolve PVDF (21.6 g) into NMP (270 g); ii) Add carbon black (18 g) and mix for 15 minutes at the rate of about 6500 rpm; iii) Add LiNi1/3Co1/3Mn1/3O2 (NMC) (560.4 g) to the slurry from Step ii and mix for 30 minutes at the rate of about 6500 rpm to form a flowable slurry; iv) Some NMP may be added for the viscosity adjustment; v) Coat this slurry onto POS5B (Example 4A) using an automatic coating machine with the first heat zone set to about 85° C. and the second heat zone to about 135° C. to evaporate off the NMP. The final dried solid loading is about 19.4 mg/cm2. The positive layer was then compressed to a thickness of about 153 μm. The electrode made here is called as zero voltage against graphite electrode and is ready for the impedance measurement at 0 V in relation to the temperature.
C) Preparation of NEG5A as an Example of the Negative Electrode Preparation
i) Dissolve CMC (13 g) into deionized water (˜1000 g); ii) Add carbon black (20 g) and mix for 15 minutes at the rate of about 6500 rpm; iii) Add negative active graphite (JFE Chemical Corporation; Graphitized Mesophase Carbon Micro Bead (MCMB) and Synthetic Graphite (TIMCAL) (945.92 g in total) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Add SBR (solid content 50% suspended in water) (42 g) to the slurry formed in Step iii and mix at 6500 rpm for 5 min; v) Adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9□ Coat this slurry onto 9 a smooth coating; er) (42 g) to the slurry formed in Step ro Bead (MCMB° C. and the second heat zone to about 130° C. to evaporate off the water. The final dried solid loading is about 11.8 mg/cm2. The negative electrode layer was then compressed to a thickness of about 159 μm. The negative made is ready for the dry for the cell assembly.
D) Preparation of Cell for the Evaluation
i) Punch the electrodes into the pieces with the electrode tab; ii) Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr; iii) Laminate the positive and negative electrodes with the separator as the middle layer; iv) Put the flat jelly-roll made in the Step iii. into the Aluminium composite bag; v) Dry the bag from Step iv. in a 70° C. vacuum oven; vi) Fill the bag from Step v with the LiPF6 containing organic carbonate based electrolyte; vii) Seal the bag from Step vi; viii) Rest for 16 hours; viiii) Charge the cell to 4.2V at C/50 rate for 8 hours and then to 4.2V at 0.5C rate for 2 hours, then rest for 20 minutes, then discharge to 2.8V at 0.5C rate. Under vacuum, puncture the cell to release any gases and then reseal the cell. The cell made here is ready for grading and other tests such as discharging capability test at 50° C., impact test, cycle life test (
Preparation of 52% CaCO3 and 48% PVDF based gas generator and resistive layer, positive and negative electrodes, and the completed Cell #6 for the evaluation in the resistance measurement, discharge capability tests at 50° C., impact test, over charge, and cycle life tests:
A) Positive POS6B as an Example of a Gas Generator and Resistive Layer (1st Layer) Preparation.
i) Dissolve PVDF (23.25 g) into NMP (˜250 g); ii) Mix solution prepared in Step i, and then add carbon black (1.85 g) and mix for 10 minutes at the rate of about 6500 rpm; iv) Add nano CaCO3 powder (24.9 g) to the solution from Step iii and mix for 20 minutes at 6500 rpm to form a flowable slurry; v) Coat this slurry onto 15□ Coat this slurry onto 15 6500 rpm to form a flowable slurry; the rate of about 6500 rpm; the com° C. and the second heat zone to about 165° C. to evaporate off the NMP. The final dried solid loading is about 1 mg/cm2.
B) Preparation of POS6A as an Example of the Positive Electrode Preparation (2nd Layer).
i) Dissolve PVDF (24 g) into NMP (300 g); ii) Add carbon black (12 g) and mix for 15 minutes at 6500 rpm; iii) Add LiNi0.4Co0.3Mn0.4Co0.3O2 (NMC) (558 g) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Some NMP may be added for the viscosity adjustment; v) Coat this slurry onto POS6B (Example 5A) using an automatic coating machine with the first heat zone set to about 85° C. and the second heat zone to about 135° C. to evaporate off the NMP. The final dried solid loading is about 22 mg/cm2. The positive layer was then compressed to a thickness of about 167 μm. The electrode made here is called as zero voltage against graphite electrode and is ready for the impedance measurement at 0 V in relation to the temperature.
C) Preparation of NEG6A as an Example of the Negative Electrode Preparation.
i) Dissolve CMC (9 g) into deionized water (˜530 g); ii) Add carbon black (12 g) and mix for 15 minutes at 6500 rpm; iii) Add negative active graphite (JFE Chemical Corporation; Graphitized Mesophase Carbon Micro Bead (MCMB) (564 g) to the slurry from Step ii and mix for 30 minutes at 6500 rpm to form a flowable slurry; iv) Add SBR (solid content 50% suspended in water) (30 g) to the slurry formed in Step iii and mix at about 6500 rpm for 5 min; v) Add some water to adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9□ Add some water to adjust the viscosity for a smooth coating; vi) Coat this slurry onto 9 d (MCM° C. and the second heat zone to about 125° C. to evaporate off the water. The final dried solid loading is about 12 mg/cm2. The negative electrode layer was then compressed to a thickness of about 170 μm. The negative made is ready for the dry for the cell assembly.
D) Preparation of Cell for the Evaluation.
i) Punch the electrodes into the pieces with the electrode tab; ii) Dry the positive electrode at 125° C. for 10 hr and negative electrode at 140° C. for 10 hr; iii) Laminate the positive and negative electrodes with the separator as the middle layer; iv) Put the flat jelly-roll made in the Step iii. into the Aluminium composite bag; v) Dry the bag from Step iv. in a 70° C. vacuum oven; vi) Fill the bag from Step v with the LiPF6 containing organic carbonate based electrolyte; vii) Seal the bag from Step vi; viii) Rest for 16 hours; viiii) Charge the cell to 4.2V at C/50 rate for 8 hours and then to 4.2V at 0.5C rate for 2 hours, then rest for 20 minutes, then discharge to 2.8V at 0.5C rate. Under vacuum, puncture the cell to release any gases and then reseal the cell. The cell made here is ready for grading and other tests such as discharging capability test at 50° C., impact test, cycle life test and so on.
Preparation of positive electrodes for chemical decomposition voltage measurements:
POS7B: (i) Mix deionized water (˜300 g) into Carbopol®-934 (19.64 g); (ii) Add Super-P® (160 mg) and LiOH (200 mg) into the slurry made in Step (i) and mix them for 30 minutes at 5000 rpm; (iii) Add an appropriate amount of deionized water to adjust the slurry to form a coatable slurry. (iv) Coat the slurry onto a 15 μm Aluminum foil with the automatic coating machine with the drying temperatures set to 135° C. for zone 1 and 165° C. for zone 2. The final dried solid loading is about 0.7 mg/cm2.
POS8B: (i) Mix deionized water (˜100 g) into AI-50 (19.85 g); (ii) Add Super-P® (160 mg) into the slurry made in Step (i) and mixing them for 30 minutes at 5000 rpm; (iii) Add an appropriate amount of deionized water to adjust the slurry to form a coatable slurry. (iv) Coating the slurry onto 15 μm Aluminum foil with automatic coating machine with the drying temperatures set to 135 for zone 1 and 165° C. for zone 2. The final dried solid loading is about 0.7 mg/cm2.
POS9B: (i) Mix deionized water (˜322 g) into 19.85 g CMC-DN-800H; (ii) Add Super-P® (160 mg) into the slurry made in Step (i) and mixing them for 30 minutes at 5000 rpm; (iii) Add an appropriate amount of deionized water to adjust the slurry to form a coatable slurry. (iv) Coating the slurry onto 15 μm Aluminum foil with automatic coating machine with the drying temperatures set to 135 for zone 1 and 165° C. for zone 2. The final dried solid loading is about 0.7 mg/cm2.
POS13B: (i) Dissolve Torlon® 4000TF (400 mg) into NMP (4 g). (ii) Dissolve PVDF-A (2.4 g) into NMP (30 g). (iii) Mix above two solution and add Super-P® (160 mg), then mix them for 30 minutes at 5000 rpm. (iv) Add La2(CO3)3 (17.04 g) or the salts listed in
Electrochemical test for the gas generator layers on the Aluminum foil:
The decomposition voltages of all resistive layers were measured with three electrodes configuration (resistive layer as the working electrode, and lithium metal as both reference electrode and count electrode) by Linear Sweep Voltammetry technology using VMP2 multichannel potentiostat instrument at the room temperature. A 0.3 cm×2.0 cm piece of the resistive layer as the working electrode, and 0.3 cm×2.0 cm piece of lithium metal as both reference electrode and count electrode were put into a glass containing LiPF6 ethylene carbonate based electrolyte (5 g). The scan rate is 5 mV/second in the voltage range from 0 to 6V.
While the present disclosure has been described in connection with certain exemplary embodiments, it is to be understood that the disclosure is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims, and equivalents thereof.
This application is a continuation under 35 U.S.C. § 120 of patent application Ser. No. 15/055,576 filed on Feb. 27, 2016, now U.S. Pat. No. 9,904,836, issued on Feb. 27, 2018, which is a continuation under 35 U.S.C. § 120 of patent application Ser. No. 14/714,160 filed on May 15, 2015, allowed, which claims priority under 35 U.S.C. § 119(e) to U.S. provisional application No. 62/084,454 filed Nov. 25, 2014, and also to U.S. provisional application No. 62/114,508 filed Feb. 10, 2015, the disclosures of which are incorporated herein by reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4075400 | Fritts | Feb 1978 | A |
| 4541735 | Abu-Isa | Sep 1985 | A |
| 5504128 | Mizutani et al. | Apr 1996 | A |
| 5507842 | Fiorino | Apr 1996 | A |
| 6387570 | Nakamura et al. | May 2002 | B1 |
| 6576373 | Iwamoto et al. | Jun 2003 | B1 |
| 6780544 | Noh | Aug 2004 | B2 |
| 7203049 | Chu et al. | Apr 2007 | B2 |
| 7390589 | Shin et al. | Jun 2008 | B2 |
| 8021788 | Kim et al. | Sep 2011 | B2 |
| 8841011 | Jang | Sep 2014 | B2 |
| 9627722 | Fan et al. | Apr 2017 | B1 |
| 9806382 | Fan et al. | Oct 2017 | B1 |
| 20050079422 | Ko et al. | Apr 2005 | A1 |
| 20060099506 | Krause et al. | May 2006 | A1 |
| 20070166609 | Lee et al. | Jul 2007 | A1 |
| 20070269718 | Krause et al. | Nov 2007 | A1 |
| 20080116423 | Fan et al. | May 2008 | A1 |
| 20080241684 | Muraoka et al. | Oct 2008 | A1 |
| 20080254343 | Kaplin et al. | Oct 2008 | A1 |
| 20080292939 | Xie | Nov 2008 | A1 |
| 20100047674 | Ryu et al. | Feb 2010 | A1 |
| 20100099022 | Nishida et al. | Apr 2010 | A1 |
| 20100167107 | Byun et al. | Jul 2010 | A1 |
| 20110045321 | Park et al. | Feb 2011 | A1 |
| 20110052950 | Yoo | Mar 2011 | A1 |
| 20110117403 | Hermann et al. | May 2011 | A1 |
| 20110151293 | Kim et al. | Jun 2011 | A1 |
| 20110157755 | Honkura | Jun 2011 | A1 |
| 20110273807 | Kim et al. | Nov 2011 | A1 |
| 20110273809 | Falsett et al. | Nov 2011 | A1 |
| 20120056709 | Kajino et al. | Mar 2012 | A1 |
| 20120068127 | Kawase et al. | Mar 2012 | A1 |
| 20120121974 | Tikhonov et al. | May 2012 | A1 |
| 20120189881 | Geoffroy et al. | Jul 2012 | A1 |
| 20130101869 | Farmer | Apr 2013 | A1 |
| 20130130075 | Kim et al. | May 2013 | A1 |
| 20130216867 | Schaefer | Aug 2013 | A1 |
| 20140072851 | Oh et al. | Mar 2014 | A1 |
| 20140168845 | Charles | Jun 2014 | A1 |
| 20160149196 | Fan et al. | May 2016 | A1 |
| 20160149199 | Fan | May 2016 | A1 |
| 20160149268 | Fan et al. | May 2016 | A1 |
| 20160149269 | Fan et al. | May 2016 | A1 |
| 20160164065 | Liu et al. | Jun 2016 | A1 |
| 20160181590 | Fan et al. | Jun 2016 | A1 |
| 20160380307 | Akita et al. | Dec 2016 | A1 |
| 20170365840 | Fan et al. | Dec 2017 | A1 |
| 20180019505 | Fan et al. | Jan 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 0450549 | Oct 1991 | EP |
| 0776058 | May 1997 | EP |
| 1246280 | Oct 2002 | EP |
| 7220755 | Aug 1995 | JP |
| H09 320568 | Dec 1997 | JP |
| 20130123492 | Nov 2013 | KR |
| WO-2004049494 | Jun 2004 | WO |
| WO-2015060175 | Apr 2015 | WO |
| WO-2016086184 | Jun 2016 | WO |
| Entry |
|---|
| Eichstadt, Amy E., et al. “Structure-Property Relationships for a Series of Amorphous Partially Aliphatic Polyimides.” Journal of Polymer Science Part B: Polymer Physics 40.14 (2002): 1503-1512. |
| Fang, Xingzhong, et al. “Synthesis and properties of polyimides derived from cis-and trans-1, 2, 3, 4-cyclohexanetetracarboxylic dianhydrides.” Polymer 45.8 (2004): 2539-2549. |
| International Search Report and Written Opinion issued in International Application No. PCT/2015/062767, dated Feb. 12, 2016. 14 pages. |
| Jeon, Jong-Young, and Tae-Moon Tak. “Synthesis of Aliphatic-Aromatic Polyimides by Two-Step Polymerization of Aliphatic Dianhydride and Aromatic Diamine.” Journal of Applied Polymer Science 60.11 (1996): 1921-1926. |
| Loncrini, D. F., and J. M. Witzel. “Polyaryleneimides of meso-and dl-1, 2, 3, 4-Butanetetracarboxylic Acid Dianhydrides.” Journal of Polymer Science Part A—1: Polymer Chemistry 7.8 (1969): 2185-2193. |
| Matsumoto, Toshihiko. “Aliphatic polyimides derived from polyalicyclic monomers.” High Performance Polymers 13.2 (2001): S85-S92. |
| Schab-Balcerzak, E., et al. “Synthesis and characterization of organosoluble aliphatic-aromatic copolyimides based on cycloaliphatic dianhydride.” European Polymer Journal 38.3 (2002): 423-430. |
| Seino, Hiroshi, Amane Mochizuki, and Mitsuru Ueda. “Synthesis of Aliphatic Polyimides Containing Adamantyl Units.” Journal of Polymer Science Part A Polymer Chemistry 37.18 (1999): 3584-3590. |
| Seino, Hiroshi, et al. “Synthesis of fully aliphatic polyimides.” High Performance Polymers 11.3 (1999): 255-262. |
| Spotnitz, R., and J. Franklin. “Abuse behavior of high-power, lithium-ion cells.” Journal of Power Sources 113.1 (2003): 81-100. |
| Number | Date | Country | |
|---|---|---|---|
| 20180190967 A1 | Jul 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62114508 | Feb 2015 | US | |
| 62084454 | Nov 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15055576 | Feb 2016 | US |
| Child | 15900726 | US | |
| Parent | 14714160 | May 2015 | US |
| Child | 15055576 | US |