Recording sheets for ink jet printing

Information

  • Patent Application
  • 20040146665
  • Publication Number
    20040146665
  • Date Filed
    January 09, 2004
    20 years ago
  • Date Published
    July 29, 2004
    20 years ago
Abstract
A recording sheet for ink jet printing is described, which consists of a support having coated thereon at least one ink-receiving layer consisting of binders, a nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide, wherein the nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide has been treated with aluminium chlorohydrate. Nanocrystalline, nanoporous aluminium oxides or aluminium oxide/hydroxides prepared in the absence of acids are preferred.
Description


FIELD OF THE INVENTION

[0001] The present invention relates to recording sheets used in ink jet printing containing nanocrystalline, nanoporous aluminium oxides or aluminium oxide/hydroxides, wherein the surface of these oxides or oxide/hydroxides has been treated with aluminium chlorohydrate, and to coating compositions for the preparation of such recording sheets.



BACKGROUND OF THE INVENTION

[0002] Ink jet printing processes are mainly of two types: continuous stream and drop-on-demand.


[0003] In continuous stream ink jet printing systems, a continuous ink stream is emitted under pressure through a nozzle. The stream breaks up into droplets at a certain distance from the nozzle. If a specific location on the recording sheet has to be printed the individual droplets are directed to the recording sheet, otherwise they are directed to a collecting vessel. This is done for example by charging unnecessary droplets in accordance with digital data signals and passing them through an electric static field which adjusts the trajectory of these droplets in order to direct them to the collecting vessel. The inverse procedure may also be used wherein uncharged droplets are directed to the collecting vessel.


[0004] In the non-continuous process, or the so-called “drop-on-demand” systems, a droplet is generated and expelled from the nozzle in accordance with digital data signals only if a specific location on the recording sheet has to be printed.


[0005] The printing speed of modern ink jet printers is always increasing for economical reasons. Recording sheets suitable for these printers therefore need to absorb the inks very quickly. Especially suitable are recording sheets containing nanocrystalline, nanoporous inorganic oxides, preferably aluminum oxides or aluminum oxide/hydroxides.


[0006] Such recording sheets available today do not meet all of the required demands. In particular, the light stability and the storage stability of images printed on these recording sheets have to be improved. These images are not particularly stable when they are in contact with ambient air, which normally contains sulfur dioxide and, especially in summer, photochemically generated impurities such as ozone or nitrogen oxides. The images are strongly altered or even destroyed in a short time when they are in contact with ambient air. These phenomena are described for example in “Ozone Problem with Epson Photo Paper”, Hardcopy Supplies Journal 6 (7), 35-36 (2000).


[0007] In patent application EP 0'373'573 derivatives of polyhydroxybenzenes are proposed as stabilizers for recording sheets for ink jet printing.


[0008] Patent application EP 0'534'634 describes the deposition of salt solutions containing at least one bivalent metal cation onto recording sheets for ink jet printing in order to improve the water fastness of the printed images. The copper salts CuCl2, CuBr2, Cu(NO3)2, Cu(ClO3)2 and Cu(C2H3O2)2 are mentioned explicitly.


[0009] Patent application JP 1-301′359 describes the addition of organic sulfonates or organic sulfates in combination with copper or nickel salts of monocarboxylic acids to recording sheets for ink jet printing in order to improve the light stability of the printed images. The copper salts copper formiate and copper acetate are mentioned explicitly.


[0010] In patent application GB 2'088'777 derivatives of phenols and bisphenols are proposed in order to improve the stability of recording sheets containing nanoporous inorganic oxides or oxide/hydroxides.


[0011] In patent application EP 0'685'345 the addition of dithiocarbamates, thiocyanates, thiurams or sterically hindered amines to recording sheets containing nanoporous inorganic oxides or oxide/hydroxides is proposed in order to improve their stability.


[0012] Patent application WO 00/37'574 describes the addition of bivalent salts of carboxylic acids with at least 4 carbon atoms of copper, nickel, cobalt or manganese to inks as well as to recording sheets for ink jet printing in order to improve the light stability of the printed images. It is mentioned that the bivalent copper salts may be replaced by monovalent copper salts.


[0013] Patent application EP 1'197'345 describes the addition of unsubstituted or substituted 1,3-cyclohexanedione to recording sheets for ink jet printing containing nanoporous inorganic oxides or oxide/hydroxides in order to increase the stability of printed images when these are in contact with contaminated ambient air.


[0014] Patent application EP 1'231'071 proposes the addition of the salts copper(I) chloride, copper(I) bromide or copper(I) sulfite monohydrate of monovalent copper to recording sheets for ink jet printing containing nanoporous inorganic oxides or oxide/hydroxides in order to increase the stability of printed images when these are in contact with contaminated ambient air.


[0015] All these proposed additives however do not sufficiently increase the stability of printed images on recording sheets for ink jet printing containing nanocrystalline, nanoporous inorganic oxides or oxide/hydroxides when these are in contact with contaminated ambient air. In particular, all reducing additives are quickly oxidized by oxygen or the impurities contained in the ambient air and therefore rapidly loose their stabilizing behavior. Some of the proposed additives may also be transformed into colored compounds when they are in contact with ambient air, leading to an unwanted degradation of the brightness of the recording sheets or of the images printed thereon.


[0016] The colloidal, nanoporous aluminium oxide/hydroxide that is very often used in recording sheets is normally prepared in a sol-gel process, as described in the book by C. F. Brinker, G. W. Scherrer, “Sol-Gel Science”, Academic Press, 1990, ISBN 0-12-134970-5, pages 59-78. The addition of an aqueous acid, for example nitric acid, acetic acid or lactic acid, is always a step during the preparation process, either during or after hydrolysis of aluminium isopropoxide.


[0017] Patent DE 3′823′895 describes a process for the preparation of colloidal aluminium oxide/hydroxide, wherein the whole sol-gel preparation process takes place in the absence of acids.


[0018] Preferably the colloidal aluminium oxide/hydroxide contains one or more elements of the rare earth metal series of the periodic system of the elements as described in patent application EP 0'875'394.


[0019] The treatment of colloidal aluminium oxide or aluminium oxide/hydroxide prepared in the presence of acids with aluminium chlorohydrate is described by M. P. B. van Bruggen in “Liquid Crystal Formation and Diffusion in Dispersions of Colloidal Rods”, 1998, ISBN 90-393-1987-1, pages 58-79. The aluminium chlorohydrate is added as a solid to the dispersion of aluminium oxide or aluminium oxide/hydroxide.


[0020] There is therefore still a need to improve, in addition to the ink absorption capacity, the image quality, the water fastness, the light stability etc., in particular the storage stability of recording sheets containing nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide when they are in contact with ambient air containing impurities such as ozone, nitrogen oxides or sulfur dioxide.



SUMMARY OF THE INVENTION

[0021] An objective of the invention is to provide recording sheets containing nanoporous nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide with improved storage stability when they are in contact with ambient air, where images recorded thereon can be observed by both reflected and transmitted light, and consist of a support having coated thereon at least one ink-receiving layer.


[0022] We have found that the storage stability of such recording sheets for ink jet printing when they are in contact with contaminated ambient air is significantly improved when the aluminium oxide or aluminium oxide/hydroxide that is used is treated at the surface with aluminium chlorohydrate. Images printed onto such recording sheets according to the invention show considerably less change of colors and/or dye losses when they are in contact with ambient air containing impurities such as ozone, nitrogen oxides or sulfur dioxide in comparison to images printed onto recording sheets containing untreated aluminium oxide or aluminium oxide/hydroxide.


[0023] The recording sheets for ink jet printing according to the invention contain in the coated layers, besides the nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide treated with aluminium chlorohydrate one or more binders.







DETAILED DESCRIPTION OF THE INVENTION

[0024] We have found that the storage stability of such recording sheets for ink jet printing when they are in contact with contaminated ambient air is significantly improved when the aluminium oxide or aluminium oxide/hydroxide that is used is treated at the surface with aluminium chlorohydrate.


[0025] The amount of aluminium chlorohydrate of formula Al2(OH)5Cl.2.5 H2O is from 0.1 to 7 mole percent relative to Al2O3, preferably from 0.5 to 4 mole percent relative to Al2O3.


[0026] The aluminium chlorohydrate may be added to the aqueous dispersions of aluminium oxide or aluminium oxide/hydroxide as a solid or as an aqueous solution.


[0027] The addition in the form of an aqueous solution, which has been aged for a prolonged period, preferably from 2 hours to 168 hours at a temperature between 25° C. and 100° C., is preferred. Especially preferred aging conditions are 24 hours at a temperature of 50° C. or 2 hours at a temperature of 90° C.


[0028] The aluminium chlorohydrate is preferably added to the aqueous dispersion of aluminium oxide or aluminium oxide/hydroxide as a solid or as an aqueous solution. The other ingredients, such as binders, surfactants etc., are added afterwards.


[0029] Nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide prepared in the complete absence of acids are preferred.


[0030] Preferred as nanocrystalline, nanoporous aluminium oxide is y-Al2O3 and as nanocrystalline, nanoporous AlOOH an AlOOH reacted with salts of the rare earth metal series as described in patent application EP 0′875′394. This nanocrystalline, nanoporous aluminium oxide/hydroxide contains one or more elements of the rare earth metal series of the periodic system of the elements with atomic numbers 57 to 71, preferably in a quantity from 0.2 to 2.5 mole percent relative to Al2O3. Especially preferred as nanocrystalline, nanoporous aluminium oxide/hydroxide is pseudo-boehmite, an agglomerate of aluminium oxide/hydroxide of formula Al2O3.n H2O where n is from 1 to 1.5, or pseudo-boehmite reacted with the salts of the rare earth metal series as also described in patent application EP 0'875'394. This nanocrystalline, nanoporous pseudo-boehmite contains one or more elements of the rare earth metal series of the periodic system of the elements with atomic numbers 57 to 71, preferably in a quantity from 0.2 to 2.5 mole percent relative to Al2O3.


[0031] It has been found that only the addition of nanoporous substances having a pore volume of μ20 ml/100 g, as determined by the BET isotherm method, to the ink receiving layers considerably increases the absorption rate and the absorption capacity for aqueous inks. Only such inorganic oxides or oxide/hydroxides should be considered as being “nanoporous”.


[0032] The recording sheet may contain, in addition to the nanocrystalline, nanoporous aluminium oxides or aluminium oxide/hydroxides, other inorganic oxides or oxide/ hydroxides not being considered to be nanoporous according to the preceding definition.


[0033] In a preferred embodiment of the invention the recording sheet contains, in addition to the treated nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide, salts of monovalent copper such as copper(I) chloride, copper(l) bromide or copper(l) sulfite monohydrate as described in patent application EP 1'231'071.


[0034] It is especially preferred if, in addition to the treated nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide and the salts of monovalent copper, compounds of formulas Ia (diketo form) and Ib (enol form), as described in patent application EP 1'197'345, are incorporated into the recording sheet,
1


[0035] wherein in formulas Ia and Ib


[0036] M represents a hydrogen cation, a metal cation such as Li, Na or K, a triethanolamine cation or an ammonium cation optionally substituted by one or more alkyl or substituted alkyl groups each having from 1 to 18 C atoms;


[0037] R1 represents hydrogen, alkyl with 1 to 12 C atoms or substituted alkyl with 2 to 6 C atoms, wherein the substituents are selected from the group consisting of CN, COOH, OH and COOR4, where R4 represents alkyl with 1 to 12 C atoms


[0038] and


[0039] R2, R3 independently represent hydrogen, alkyl with 1 to 6 C atoms or substituted alkyl with 2 to 6 C atoms, wherein the substituents are selected from the group consisting of CN, COOH, OH and COOR5, where R5 represents alkyl with 1 to 12 C atoms.


[0040] In a further preferred embodiment of the invention, the recording sheet contains, in addition to the treated nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide, organic sulfur compounds as for example thiodiethylene glycol.


[0041] The binders are in most cases water-soluble polymers. Especially preferred are film forming polymers.


[0042] The water-soluble polymers include for example natural polymers or modified products thereof such as albumin, gelatin, casein, starch, gum arabicum, sodium or potassium alginate, hydroxyethyl cellulose, carboxymethyl cellulose, α-, β-, or γ-cyclodextrine and the like. In the case where one of the water-soluble polymers is gelatin, all known types of gelatin may be used as for example acid pigskin or limed bone gelatin, acid or base hydrolyzed gelatin, but also derivatised gelatins like for instance phthalaoylated, acetylated or carbamoylated gelatin or gelatin derivatised with the anhydride of trimellitic acid.


[0043] A preferred natural binder is gelatin.


[0044] Synthetic binders may also be used and include for example polyvinyl alcohol, polyvinyl pyrrolidone, completely or partially saponified products of copolymers of vinyl acetate and other monomers; homopolymers or copolymers of unsaturated carboxylic acids such as (meth)acrylic acid, maleic acid, crotonic acid and the like; homopolymers or copolymers of sulfonated vinyl monomers such as vinylsulfonic acid, styrene sulfonic acid and the like. Furthermore homopolymers or copolymers of vinyl monomers of (meth)acrylamide; homopolymers or copolymers of other monomers with ethylene oxide; polyurethanes; polyacrylamides; water-soluble nylon type polymers; polyesters; polyvinyl lactams; acrylamide polymers; substituted polyvinyl alcohol; polyvinyl acetals; polymers of alkyl and sulfoalkyl acrylates and methacrylates; hydrolyzed polyvinyl acetates; polyamides; polyvinyl pyridines; polyacrylic acid; copolymers with maleic anhydride; polyalkylene oxides; methacrylamide copolymers and maleic acid copolymers may be used. All these polymers may also be used as mixtures.


[0045] Preferred synthetic binders are polyvinyl alcohol and polyvinyl pyrrolidone or mixtures thereof.


[0046] These polymers may be blended with water insoluble natural or synthetic high molecular weight compounds, particularly with acrylate latices or with styrene acrylate latices.


[0047] Although not specifically claimed in this invention water insoluble polymers are nevertheless considered to be part of the system.


[0048] The polymers mentioned above having groups with the possibility to react with a cross-linking agent may be cross-linked or hardened to form essentially water insoluble layers. Such cross-linking bonds may be either covalent or ionic. Cross-linking or hardening of the layers allows for the modification of the physical properties of the layers, like for instance their water absorption capacity or the resistance against layer damage.


[0049] The cross-linking agents or hardeners are selected depending on the type of the water-soluble polymers to be cross-linked.


[0050] Organic cross-linking agents and hardeners include for example aldehydes (such as formaldehyde, glyoxal or glutaraldehyde), N-methylol compounds (such as dimethylol urea or methylol dimethylhydantoin), dioxanes (such as 2,3-dihydroxydioxane), reactive vinyl compounds (such as 1,3,5-trisacrylolyl hexahydro-s-triazine or bis-(vinylsulfonyl)methyl ether), reactive halogen compounds (such as 2,4-dichloro-6-hydroxy-s-triazine); epoxides; aziridines; carbamoyl pyridinium compounds or mixtures of two or more of the above mentioned cross-linking agents.


[0051] Inorganic cross-linking agents or hardeners include for example chromium alum, aluminium alum or boric acid.


[0052] The layers may also contain reactive substances that cross-link the layers under the influence of ultraviolet light, electron beams, X-rays or heat.


[0053] The layers may further be modified by the addition of fillers. Possible fillers are for instance kaolin, Ca- or Ba-carbonates, silicium dioxide, titanium dioxide, bentonites, zeolites, aluminium silicate, calcium silicate or colloidal silicium dioxide. Organic inert particles such as polymer beads may also be used. These beads may consist of polyacrylates, polyacrylamides, polystyrene or different copolymers of acrylates and styrene. The fillers are selected according to the intended use of the printed images. Some of these compounds cannot be used if the printed images are to be used as transparencies. However they are of interest in cases where the printed images are be to used as remission pictures. Very often, the introduction of such fillers causes a wanted matte surface.


[0054] The recording sheets may also contain water-soluble metal salts, as for example salts of the alkaline earth metals or salts of the rare earth metal series.


[0055] The recording sheets according to the invention comprise a support having coated thereon at least one ink-receiving layer, and, optionally, auxiliary layers.


[0056] A wide variety of supports are known and commonly used in the art. They include all those supports used in the manufacture of photographic materials. This includes clear films made from cellulose esters such as cellulose triacetate, cellulose acetate, cellulose propionate or cellulose acetate/butyrate, polyesters such as polyethylene terephthalate or polyethylene naphthalate, polyamides, polycarbonates, polyimides, polyolefins, polyvinyl acetals, polyethers, polyvinyl chloride and polyvinylsulfones. Polyester film supports, and especially polyethylene terephthalate or polyethylene naphthalate are preferred because of their excellent dimensional stability characteristics. The usual supports used in the manufacture of opaque photographic materials may be used including for example baryta paper, polyolefin coated papers, voided polyester as for instance Melinex® manufactured by DuPont. Especially preferred are polyolefin coated papers or voided polyester.


[0057] When such support materials, in particular polyester, are used, a subbing layer is advantageously coated first to improve the bonding of the ink receiving layers to the support. Useful subbing layers for this purpose are well known in the photographic industry and include for example terpolymers of vinylidene chloride, acrylonitrile and acrylic acid or of vinylidene chloride, methyl acrylate and itaconic acid.


[0058] Also used as supports are uncoated papers, comprising all different types of papers varying widely in their composition and in their properties. Pigmented papers and cast-coated papers may also be used, as well as metal foils, such as foils made from aluminium.


[0059] The layers may also be coated onto textile fiber materials consisting for example of polyamides, polyesters, cotton, viscose and wool.


[0060] The ink-receiving layers according to the invention are in general coated from aqueous solutions or dispersions containing all necessary ingredients. In many cases, surfactants are added to those coating solutions in order to improve the coating behavior and the evenness of the layers. Besides being necessary for coating purposes, these compounds may have an influence on the image quality and may therefore be selected with this specific objective in mind. Although not specifically claimed in this invention surfactants nevertheless form an important part of the invention.


[0061] In addition to the above mentioned ingredients, recording sheets according to the invention may contain additional compounds aimed at further improving their performance, as for example brightening agents to improve the whiteness, such as stilbenes, coumarines, triazines, oxazoles or others compounds known to someone skilled in the art.


[0062] Light stability may be improved by adding UV absorbers such as 2-hydroxy-benzotriazoles, 2-hydroxybenzophenones, derivatives of triazine or derivatives of cinnamic acid. The amount of UV absorber may vary from 200 mg/m2 to 2000 mg/m2, preferably from 400 mg/m2 to 1000 mg/m2. The UV absorber may be added to any of the layers of the recording sheet according to the invention. It is preferred that, however, if it is added, it should be added to the topmost layer.


[0063] It is further known that images produced by ink jet printing may be protected from degradation by the addition of radical scavengers, stabilizers, reducing agents and antioxidants. Examples of such compounds are sterically hindered phenols, sterically hindered amines, chromanols, ascorbic acid, phosphinic acids and their derivatives, sulfur containing compounds such as sulfides, mercaptans, thiocyanates, thioamides or thioureas.


[0064] The above-mentioned compounds may be added to the coating solutions as aqueous solutions. In the case where these compounds are not sufficiently water-soluble, they may be incorporated into the coating solutions by other common techniques known in the art. The compounds may for example be dissolved in a water miscible solvent such as lower alcohols, glycols, ketones, esters, or amides. Alternatively, the compounds may be added to the coating solutions as fine dispersions, as oil emulsions, as cyclodextrine inclusion compounds or incorporated into latex particles.


[0065] Typically, the recording sheet according to the invention has a thickness in the range of 0.5 μm to 100 μm dry thickness, preferably in the range of 5 μm to 50 μm dry thickness.


[0066] The coating solutions may be coated onto the support by any number of suitable procedures. Usual coating methods include for example extrusion coating, air knife coating, doctor blade coating, cascade coating and curtain coating. The coating solutions may also be applied using spray techniques. The ink receiving layers may be built up from several single layers that can be coated one after the other or simultaneously. It is likewise possible to coat a support on both sides with ink-receiving layers. It is also possible to coat an antistatic layer or an anticurl layer on the backside. The selected coating method however is not to be considered limiting for the present invention.


[0067] Inks for ink jet printing consist in essence of a liquid vehicle and a dye or pigment dissolved or suspended therein. The liquid vehicle for ink jet inks consists in general of water or a mixture of water and a water miscible organic solvent such as ethylene glycol, higher molecular weight glycols, glycerol, dipropylene glycol, polyethylene glycol, amides, polyvinyl pyrrolidone, N-methylpyrrolidone, cyclohexyl pyrrolidone, carboxylic acids and their esters, ethers, alcohols, organic sulfoxides, sulfolane, dimethylformamide, dimethylsulfoxide, cellosolve, polyurethanes, acrylates and the like.


[0068] The non-aqueous parts of the ink generally serve as humefactants, co-solvents, viscosity regulating agents, ink penetration additives or drying agents. The organic compounds have in most cases a boiling point, which is higher than that of water. In addition, aqueous inks used for printers of the continuous stream type may contain inorganic or organic salts to increase their conductivity. Examples of such salts are nitrates, chlorides, phosphates and salts of water-soluble organic acids such as acetates, oxalates and citrates. The dyes and pigments suitable for the preparation of inks useable with the recording sheets according to the invention cover practically all classes of known coloring compounds. Dyes or pigments typically used for this purpose are described in patent application EP 0′559′324. The recording sheets according to the invention are meant to be used in conjunction with most of the inks representing the state of the art.


[0069] Other additives present in inks are for instance surfactants, optical brighteners, UV absorbers, light stabilizers, biocides, precipitating agents such as multi-valent metal compounds and polymeric additives.


[0070] This description of inks is for illustration only and is not to be considered as limiting for the purpose of the invention.


[0071] The present invention will be illustrated in more detail by the following examples without limiting the scope of the invention in any way.



Experimental Coatings

[0072] 140 g/m2 of the coating solutions described in the following examples were coated at a temperature of 40° C. onto a polyethylene coated paper support. The coated support was then dried for 60 minutes at a temperature of 30° C. 1 m2 of the coated support contains, in addition to the other coating ingredients, 21.1 g of nanocrystalline, nanoporous aluminium oxide/hydroxide, calculated as Al2O3, and 2.39 g of polyvinyl alcohol.



Test Methods

[0073] The following methods were used to determine the stability of the recording sheets described in the following examples when they are in contact with ambient air and their light stability:


[0074] 1. Stability in Contact with Ambient Air


[0075] Patches of the colors cyan, magenta, yellow and 3 K black (mixture of cyan, magenta and yellow) with densities between 0.7 and 1.6 were printed onto the recording sheets according to the invention with an ink jet printer EPSON 890 using original inks. The ink quantity was the same for all patches.


[0076] The printed samples were exposed for 7 days in a closed cupboard to ambient air under moderate circulation at a temperature between 20° C. and 25° C. and relative humidity between 35% and 70%.


[0077] The density losses of the printed patches were measured with an X-Rite® densitometer. They are expressed as per cent loss of initial density of the color patches and as per cent loss of initial density of the individual colors of 3 K black.


[0078] 2. Light Stability


[0079] Patches of the colors cyan, magenta, yellow and 3 K black with an approximate density of 1.60 were printed onto the recording sheets according to the invention with an ink jet printer EPSON 890 using original inks.


[0080] The printed samples were irradiated in an ATLAS Ci35A Weather-O-Meter® with a 6500 W Xenon lamp until a total illumination of 10 Mluxh was reached.


[0081] The densities of the color patches were measured with an X-Rite® densitometer before and after irradiation. The density losses are expressed as percent losses of initial density.


[0082] 3. Combined Stability in Contact with Ambient Air and Exposure to Light


[0083] Patches of the colors cyan, magenta, yellow and 3K black with densities between 0.7 and 1.6 were printed onto the recording sheets according to the invention with an ink jet printer EPSON 750 using original inks. The ink quantity was the same for all patches.


[0084] The printed samples were exposed unsealed to ambient air for 244 days under subdued room light.


[0085] These conditions correspond to normally encountered conditions where the printed images are deteriorated at the same time by exposure to light as well as to air impurities.



EXAMPLES


Examples 1a-1c


Comparative Example C-1

[0086] Coating Solutions


[0087] 38.0 g of aluminium oxide/hydroxide of formula AlOOH, prepared in the absence of acid according to the method of Example 1 of patent application DE 3′823′895, were dispersed under vigorous mechanical stirring at a temperature of 40° C. in 104 g of aqueous lactic acid (1.7%). Afterwards aqueous aged solutions of aluminium chlorohydrate of formula Al2(OH)5Cl·2.5 H2O (Locron®, available from Clariant AG, Muttenz, Switzerland) (50%) were added. The amounts (in mole percent relative to Al2O3) and the aging conditions are indicated in Table 1. Vigorous mechanical stirring was continued for a further 2 hours. Afterwards, 11.4 g of a solution of polyvinyl alcohol with a hydrolysis degree of 88% (10%, molecular weight 72'000, available as Moviol 2688 from Clariant AG, Muttenz, Switzerland) and 25.4 g of a solution of polyvinyl alcohol with a hydrolysis degree of 98% (10%, molecular weight 195'000, available as Moviol 5698 from Clariant AG, Muttenz, Switzerland) were added. The total weight of the coating solution was adjusted to 200 g with deionised water and the solution was exposed to ultrasound for 30 seconds.
1TABLE 1Aging conditionsQuantity of aluminiumof the solution ofExamplechlorohydrate (mole percent)aluminium chlorohydrate1a2 5 minutes at 20° C.1b2 24 hours at 20° C.1c2168 hours at 20° C.1d2 24 hours at 50° C.C-10



Example 2


Comparative Example C-2

[0088] Preparation of Aluminium Oxide/Hydroxide Doped with La (0.2 Mole Percent Relative to Al2O3)


[0089] 50 g of aluminium oxide/hydroxide of formula AlOOH, prepared in the complete absence of acids according to the method of Example 1 of patent application DE 3′823′895, were dispersed at a temperature of 20° C. for 15 minutes under vigorous mechanical stirring in 948 g of doubly distilled water. Afterwards, temperature was increased to 90° C. and stirring was continued for 15 minutes at this temperature. 0.186 g of LaCl3 (available from Fluka Chemie AG, Buchs, Switzerland) were added as a solid and stirring was continued for 120 minutes. The solid was filtered off, washed three times with doubly distilled water and dried at a temperature of 110° C. The lanthanum content is 0.2 mole percent relative to Al2O3.


[0090] Coating Solutions


[0091] The aluminium oxide/hydroxide, prepared in the absence of acid according to the method of example 1 of patent application DE 3'823'895, used in the preparation of the coating solutions of Examples 1a-1d and comparative example C-1, is replaced by aluminium oxide/hydroxide doped with La (0.2 mole percent), also prepared in the absence of acid, as described above. The amount of aluminium chlorohydrate (in mole percent relative to Al2O3) and the aging conditions of the solution of aluminium chlorohydrate are indicated in Table 2.
2TABLE 2Aging conditionsQuantity of aluminiumof the solution ofExamplechlorohydrate (mole percent)aluminium chlorohydrate222 hours at 20° C.C-20



Examples 3a-3c


Comparative Example C-3

[0092] Coating solutions


[0093] The aluminium oxide/hydroxide, prepared in the absence of acid according to the method of example 1 of patent application DE 3′823′895, used in the preparation of the coating solutions of examples 1a-1d and Comparative Example C-1, is replaced by aluminium oxide/hydroxide Disperal HP14/4 (available from SASOL Germany GmbH, Hamburg, Germany). The amount of aluminium chlorohydrate (in mole percent relative to Al2O3) and the aging conditions of the solution of aluminium chlorohydrate are indicated in Table 3.
3TABLE 3Aging conditionsQuantity of aluminiumof the solution ofExamplechlorohydrate (mole percent)aluminium chlorohydrate3a1 5 minutes at 25° C.3b2 5 minutes at 25° C.3c124 h hours at 50° C.3d224 h hours at 50° C.C-30



Example 4


Comparative Example C-4

[0094] Coating solutions


[0095] In example 4, 340 mg of thiodiethylene glycol were added to the prepared coating solution of example 1a.


[0096] In comparative example C-4, no thiodiethylene glycol was added to the prepared coating solution of example 1a.


[0097] The dried coating of example 4 contains, in addition to the other ingredients, 242 g/m2 of thiodiethylene glycol.



Results

[0098] The density losses obtained during exposure to ambient air under the indicated testing conditions are listed in Table 4 for recording sheets according to the invention containing nanocrystalline, nanoporous aluminium oxide/hydroxide treated with aluminium chlorohydrate, as well as the density losses during exposure to ambient air for comparative recording sheets containing untreated nanocrystalline, nanoporous aluminium oxide/hydroxide.
4TABLE 4Dye density loss in %CyanMagentaYellowExampleCyanMagentaYellow(3K)(3K)(3K)1a42114140C-120101221703a201143b7613c181133d451C-326143480121140C-4122121140


[0099] A comparison of the results of experimental series 1 in Table 4 immediately shows that the recording sheet for ink jet printing containing nanocrystalline, nanoporous aluminum oxide/hydroxide, prepared in the absence of acid and treated with aluminium chlorohydrate (Example 1a), shows much lower density losses of the cyan and magenta dye in the pure color patches as well as in the 3K patches in comparison to a corresponding recording sheet containing unmodified nanocrystalline, nanoporous aluminum oxide/hydroxide (Comparative example C-1).


[0100] A comparison of the results of experimental series 3 in Table 4 immediately shows that the recording sheets for ink jet printing containing nanocrystalline, nanoporous aluminum oxide/hydroxide, prepared in the presence of acid and treated with aluminium chlorohydrate (Examples 3a-3d), show lower density losses of the cyan, magenta and yellow dye in the pure color patches in comparison to a corresponding recording sheet containing untreated nanocrystalline, nanoporous aluminum oxide/hydroxide (Comparative Example C-3). The density losses are considerably lower with an amount of aluminium chlorohydrate of 2 mole percent (Examples 3a and 3c) than with an amount of aluminium chlorohydrate of 1 mole percent (Examples 3b and 3d). The aging of the solution of aluminium chlorohydrate for prolonged periods at higher temperatures further reduces the dye losses (Examples 3a versus 3c and 3b versus 3d).


[0101] A comparison of the results of experimental series 1 and 3 in Table 4 further shows that the density losses are smaller when a nanocrystalline, nanoporous aluminum oxide/hydroxide is used that has been prepared in the absence of acids.


[0102] A comparison of the results of examples 4 and comparative example C-4 in Table 4 immediately shows that the cyan and magenta density losses are even smaller when the recording sheet additionally contains thiodiethylene glycol.


[0103] The density losses obtained during exposure to light are listed in Table 5 for recording sheets according to the invention containing nanocrystalline, nanoporous aluminium oxide/hydroxide treated with aluminium chlorohydrate, as well as the density losses during exposure to light for comparative recording sheets containing untreated nanocrystalline, nanoporous aluminium oxide/hydroxide.
5TABLE 5(Printer EPSON 890)Dye Density Loss in %CyanMagentaYellowExampleCyanMagentaYellow(3K)(3K)(3K)1a1246206220C-12746288170


[0104] A comparison of the results in Table 5 immediately shows that the recording sheet for ink jet printing containing nanocrystalline, nanoporous aluminum oxide/hydroxide, prepared in the absence of acid and treated with aluminium chlorohydrate (Example 1a), shows lower density losses of the cyan and yellow in comparison to a corresponding recording sheet containing untreated nanocrystalline, nanoporous aluminum oxide/hydroxide (Comparative example C-1).


[0105] The density losses obtained during exposure to light are listed in Table 6 for recording sheets according to the invention containing nanocrystalline, nanoporous aluminium oxide/hydroxide treated with aluminium chlorohydrate, as well as the density losses during exposure to light for comparative recording sheets containing untreated nanocrystalline, nanoporous aluminium oxide/hydroxide.
6TABLE 6(Printer EPSON 750)Dye Density Loss in %CyanMagentaYellowExampleCyanMagentaYellow(3K)(3K)(3K)2403314483421C-2604619604633


[0106] A comparison of the results in Table 6 immediately shows that the recording sheet for ink jet printing containing nanocrystalline, nanoporous aluminum oxide/hydroxide doped with lanthanum, prepared in the absence of acid and treated with aluminium chlorohydrate (Example 2), shows lower density losses of all dyes in comparison to a corresponding recording sheet containing untreated nanocrystalline, nanoporous aluminum oxide/hydroxide doped with lanthanum (Comparative Example C-2).


[0107] The density losses obtained during the combined exposure to ambient air and light under the indicated testing conditions are listed in Table 7 for recording sheets according to the invention containing nanocrystalline, nanoporous aluminium oxide/hydroxide treated with aluminium chlorohydrate, as well as the density losses obtained during the combined exposure to ambient air and light for comparative recording sheets containing untreated nanocrystalline, nanoporous aluminium oxide/hydroxide.
7TABLE 7Dye Density Loss in %ExampleCyanMagentaYellow3K through neutral density filter1b465019451c43502141C-36371462


[0108] A comparison of the results in Table 7 immediately shows that the recording sheets for ink jet printing containing nanocrystalline, nanoporous aluminum oxide/hydroxide, prepared in the absence of acid and treated with aluminium chlorohydrate (Examples 1a and 1b), show much lower density losses of the cyan, magenta and yellow dye in comparison to a corresponding recording sheet containing untreated nanocrystalline, nanoporous aluminum oxide/hydroxide prepared in the presence of acids (Comparative Example C-3).


[0109] Finally, variations from the examples given herein are possible in view of the above disclosure. Therefore, although the invention has been described with reference to certain preferred embodiments, it will be appreciated that other binders may be devised, which are nevertheless within the scope and spirit of the invention as defined in the claims appended hereto.


[0110] The foregoing description of various and preferred embodiments of the present invention has been provided for purposes of illustration only, and it is understood that numerous modifications, variations and alterations may be made without departing from the scope and spirit of the invention as set forth in the following claims.


Claims
  • 1. Recording sheet for ink jet printing having coated onto a support at least one ink-receiving layer containing binders and at least one nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide, wherein the nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide in said recording sheet has been treated with aluminium chlorohydrate.
  • 2. Recording sheet according to claim 1, wherein the nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide has been prepared in the absence of acids.
  • 3. Recording sheet according to claim 1, wherein the quantity of aluminium chlorohydrate is from 0.1 to 7. 0 mole percent relative to Al2O3.
  • 4. Recording sheet according to claim 1, wherein the quantity of aluminium chlorohydrate is from 0.5 to 4. 0 mole percent relative to Al2O3.
  • 5. Recording sheet according to claim 1, wherein the aluminium chlorohydrate is added to the aqueous dispersions of aluminium oxide or aluminium oxide/hydroxide as a solid.
  • 6. Recording sheet according to claim 1, wherein the aluminium chlorohydrate is added to the aqueous dispersions of aluminium oxide or aluminium oxide/hydroxide as an aqueous solution that has been aged for a period of 2 hours to 168 hours at a temperature between 25° C. and 100° C.
  • 7. Recording sheet according to claim 1, wherein the recording sheet additionally contains thiodiethylene glycol.
  • 8. Recording sheet according to claim 1, wherein the nanocrystalline, nanoporous aluminium oxide or aluminium oxide/hydroxide is AlOOH or pseudo-boehmite comprising one or more of the elements of the rare earth metal series of the periodic system of the elements with atomic numbers 57 to 71 in an amount of from 0.2 to 2.5 mole percent relative to Al2O3.
  • 9. Recording sheet according to claim 1, wherein the support is selected from the group consisting of coated or uncoated paper, transparent or opaque polyester or fibrous textile materials.
  • 10. Coating compositions for the preparation of ink-receiving layers for recording sheets for ink jet printing according to claim 1.