Patent Application
20170320776
The present invention relates to concrete materials, and particularly to a synthetic recycled plastic aggregate for use in concrete.
Concrete is one of the most important and frequently used materials in civil engineering, such as in high-low buildings, bridges, infrastructure and environmental protection facilities. Concrete is a composition of an aggregate and a binder substance. The binder substance and the aggregate are combined by a moistening agent to allow the binder substance to link with aggregate particles and form a solid block. Generally the aggregate or aggregates make up about 60% to 75% of the total concrete volume. Therefore, the type and proportion of the aggregate used in concrete can significantly impact the weight, strength, durability, and elastic properties, of the concrete. However, as a result of environmental concerns, there has been a growing trend for the use of secondary, industrial, granular and recycled plastic wastes as recycled and/or artificial aggregate instead of natural aggregate in the production of concrete as a direct replacement of coarse/fine natural aggregate. For example, air-cooled, blast furnace, and steel furnace slag have been used to replace coarse aggregate materials and fly ash and furnace bottom ash have been used to replace fine aggregate materials. Furthermore, by product materials, such as silica fume and rice husk ash have been used as supplementary cementing materials as a partial replacement of cement.
Over the last 30 years, worldwide production of plastic grew by more than 500%. Current annual global production is estimated at over 100 million tons and is expected to increase by 3% a year. In the U.K., 7% of plastics are recycled each year, which is a small quantity when compared to the 275 million tons of natural aggregate used in concrete applications. About 80% of the plastic wastes are either left in stockpiles, as landfill material, or is illegally dumped. Most importantly, much of the non-decaying wastes will remain in the environment for hundreds, perhaps thousands of years. The non decaying waste will not only cause a waste disposal crisis, but also contribute to significant environmental problems.
Use of synthetic aggregate in concrete has been limited; however, because synthetic aggregates do not provide the same physical, chemical, or mechanical properties as natural aggregates.
Thus, a synthetic aggregate solving the aforementioned problems is desired.
The synthetic recycled plastic aggregate (RPA) for use in concrete is a composite material of recycled plastic having a filler encapsulated in the plastic. The recycled plastic includes polyethylene terephthalate (PET). The RPA includes between about 30% and 50% by weight recycled plastic, the balance being filler. For example, the RPA can include between about 30% and 50% by weight polyethylene terephthalate (PET), the balance being filler. The filler can include dune sand, fly ash, and quarry fines. The synthetic RPA is best used to make concrete with a water-to-cement ratio of at least 0.5.
A method of making synthetic RPA includes the steps of shredding and grinding recycled plastic, mixing the ground plastic with a filler to form a homogenized mixture, compressing the homogenized mixture in a mold, melting the plastic in the homogenized mixture to form a composite sheet or slab, and shredding the composite sheet or slab to form either coarse or fine aggregates for use in making concrete. The recycled plastic includes polyethylene terephthalate (PET) and the filler includes a granular waste, such as dune sand, fly ash, and/or quarry fines.
These and other features of the present invention will become readily apparent upon further review of the following specification and drawings.
Similar reference characters denote corresponding features consistently throughout the attached drawings.
Referring to
A method of making concrete having the synthetic RPA includes the steps of shredding and grinding plastic, wherein the plastic includes polyethylene terephthalate (PET), mixing the shredded plastic with filler to form a homogenized mixture, compressing the homogenized mixture in a mold, melting the plastic in the homogenized mixture to form a composite sheet or slab, and crushing the composite sheet or slab to form either coarse or fine aggregates for use in making concrete. The filler can be granular waste such as dune sand, fly ash, and quarry fines.
In order to test the use of the synthetic RPA as an aggregate in concrete, different samples of the synthetic RPA were prepared. The synthetic RPA includes filler and plastic as described above. The filler used in the synthetic RPA is granular waste, such as dune sand, fly ash, or quarry fines. The particles of the filler, such as dune sand particles, preferably have a particle size less than or equal to 0.15 mm, for example. One manner in which this can be accomplished is by passing the filler, such as dune sand, through a sieve. After obtaining the particles of the desired size, the filler can be dried at room temperature. Preferably, the filler is free from any contamination.
The recycled plastic used in the samples of synthetic RPA tested was polyethylene terephthalate (PET). The plastic-filler percentages were adjusted to reach the optimal percentage, as illustrated in Table 1. Table 1 shows six different synthetic RPA compositions according to the present teachings, including two different percentages of recycled PET mixed with three different kinds of filler.
Once the filler, such as dune sand, is sieved and the fraction with the desired particle size (such as less than or equal to 0.15 mm) is selected, it is dried at room temperature.
The recycled plastic is collected and either sorted into different polymer groups, such as PET, or used “as is” in a mixed stream. Regardless of the type of plastic used, the recycled plastic stream should be separated from non-polymer products (such as wood, glass, or metal) and then shredded and processed by grinding to obtain particles with a maximum size of 2.36 mm. After the plastic and the filler are dried, they are mixed together within a mixing machine to produce a homogenized mixture. The homogenized mixture is then preheated for approximately one hour at a temperature of from about 110° C.±5° C.
The homogenized mixture is then poured into a flat mold. After it is poured into the flat mold, the homogenized mixture is compressed. To compress the homogenized mixture, the mold containing the polymer-filler mixture is placed between two heated plates in a compression molding press machine. The compression molding machine is heated to a temperature of about 300° C., and the polymer-filler mixture is compressed with about twenty-five tons of force for about fifteen minutes. After fully melting the polymer and the subsequent encapsulation of filler, the resulting slab is slowly cooled in the mold through an automatic cooling system in the machine and later removed from the compression molding machine, to be cooled slowly in air at room temperature for about thirty minutes. Utilizing a screen created to meet certain specifications, the polymer-filler solid slab is crushed in a normal crusher machine to form either coarse aggregate and/or fine aggregate at the desired gradation. As illustrated in
As discussed herein, the properties of the materials used in concrete have a great role in determining the quality of the concrete. As such, it is important to determine the physical, chemical and mechanical properties of the materials used. For illustration purposes only, tests were conducted comparing the various properties of ordinary concrete (NC), conventional lightweight concrete (LWC), and concrete comprising the inventive synthetic RPA prepared as described above. A conventional lightweight concrete (LWC) is produced as a control using a local conventional lightweight aggregate, which is a type of volcanic rock collected from the western region of the Arabian Peninsula. The properties of this conventional lightweight aggregate are tabulated in Table 2.
In the same manner for comparison purposes, natural crushed stone was used to produce normal concrete (NC). The properties of this natural aggregate are illustrated in Table 3.
Synthetic recycled plastic was used to replace natural/conventional lightweight coarse aggregates at 100% replacement for making the inventive specimens of concrete including a synthetic RPA. These synthetic RPAs were manufactured in different sizes (as shown in
For those mixes containing synthetic RPA and/or conventional lightweight aggregate, the quantity of the coarse aggregate is calculated by using the specific gravity of the synthetic RPA and/or conventional lightweight aggregate as a replacement for the specific gravity of natural coarse aggregates. The resultant mix proportions are illustrated in Table 5. In Table 5, the sample designation “NC” means normal concrete made using natural crushed stone, the designation “LWC” means concrete made with the conventional volcanic lightweight aggregate described above. Reference can be made to Table 1 for the compositions of the synthetic RPA designations used in Table 5. For example, the designation “RP3F1C” means synthetic RPA concrete with recycled plastic 3 (50% recycled PET) and filler 1 (50% dune sand).
The results of the tests discussed below illustrate the effect that a specific aggregate can have on certain concrete properties. Specifically, the results illustrate the relation between slump, unit weight, compressive strength, splitting tensile strength, flexural strength, and chloride permeability for all of the synthetic RPA specimens having a water-to-cement ratio of 0.5.
Continuing with reference to
The percentage decrease in compressive strength of RP3F1C, RP3F2C, RP3F3C, RP4F1C, RP4F2C, and RP4F3C was 27%, 27%, 15%, 40%, 24%, and 28%, respectively, after seven (7) days, 28%, 26%, 18%, 45%, 37%, and 30%, respectively, at fourteen (14) days, and 18%, 24%, 11%, 41%, 41%, and 27%, respectively, at twenty eight (28) days as compared to normal concrete. Among the RPA concrete the results showed that the compressive strength is decreased as the percentage of filler, such as dune sand, fly ash, and quarry fines, is increased from 50% to 70%. As demonstrated by the results described herein, RPA concrete satisfy the ASTM C330 requirement for compressive strength. Therefore, it can be used for such structural applications.
The reduction in compression strength of the RPA compared to the normal concrete was expected due to the weakness of the aggregate compared to natural crushed stone and the weakness in the bonding between cement mortar and synthetic RPA particles. This weakness is due to differences in surface texture and size of synthetic plastic aggregate particles.
The splitting tensile strength of concrete was calculated using the compression machine test. Cylinder specimens were made to be tested at six, fourteen, and twenty-eight days using cylinder having a diameter of 50 mm and a depth of 100 mm.
Comparison of splitting tensile strengths for the concrete mixes made with RPA having a water-to-cement ratio of 0,5 are presented in
The splitting tensile strength of RPA concrete increased initially compared to the splitting tensile strength of conventional lightweight concrete, but tended to decrease after fourteen and twenty-eight days, respectively. At seven days, for example, the percentage increase in splitting tensile strength of RP3F1C, RP3F2C, RP3F3C, RP4F1C, RP4F2C, and RP4F3C was 20%, 5%, 29%, 4%, 32%, and 27%, respectively, as compared to conventional lightweight concrete. Whereas, at fourteen and twenty-eight days the percentage decrease was 14%, 21%, 3%, 29%, 28%, 3%, respectively, and 18%, 17%, 11%, 31%, 30%, and 13%, respectively as compared to conventional lightweight concrete.
The general trend observed for the splitting tensile strength of RPA concrete compared to normal concrete was a decrease at all stages, When compared to normal concrete, the percentage decrease in splitting tensile strength of RP3F1C, RP3F2C, RP3F3C, RP4F1C, RP4F2C, and RP4F3C was 29%, 41%, 21%, 46%, 17%, and 23%, respectively, at seven days, 47%, 51%, 41%, 56%, 56%, and 37%, respectively, at fourteen days, and 48%, 48%, 44%, 56%, 56%, and 45%, respectively at twenty-eight days. Among the RPA concrete, the results showed that the splitting tensile strength increased as the percentage of filler (dune sand, fly ash and quarry fines) increased from 50% to 70%, As demonstrated by the results described herein, RPA concrete satisfy the ASTM C330 requirement for splitting tensile strength. Therefore, it can be used for such structural applications.
It is to be noted that the factors causing reduction in the splitting tensile strength in concrete containing synthetic RPA are the same as that which cause reduction in the compressive strength, as stated previously.
Using a simple beam (Prism) with one point loading, the flexural strength specimens were prepared by casting the fresh concrete in two layers in steel prism beam molds with dimension 160×40×40 mm, in which each layer was subjected to vibration for three (3) seconds, After twenty-four (24) hours, the beam specimens were demolded, and cured in water at a temperature of 20° C. 2° C. for seven, fourteen, and twenty-eight days, After the curing process, the beams were tested by flexural strength machine to measure the flexural load and strength at which the beams will fail.
In
The flexural strength of RPA concrete increased as compared to conventional lightweight concrete but reduced as compared to normal concrete, The percentage increase in flexural strength of RP3F1C, RP3F2C, RP3F3C, RP4FIC, RP4F2C and RP4F3C was 5%, 14%, 16%, 21, 12%, and 14%, respectively at seven days, 24%, 8%, 7%, 42%, 22%, and 12%, respectively, at fourteen days, and 26%, 34%, 23%, 41%, 43%, and 23%, respectively, at twenty-eight days as compared to conventional lightweight concrete. On the other hand the percentage decrease in flexural strength of RP3F1C, RP3F2C, RP3F3C, RP4F1C, RP4F2C and RP4F3C was 39%, 33%, 31%, 52%, 35%, and 33%, respectively, at seven days, 49%, 39%, 38%, 61%, 48%, and 41%, respectively, at fourteen days, and 39%, 46%, 36%, 51%, 52%, and 36%, respectively, at twenty-eight days as compared to normal concrete. Among the RPA concrete, the results showed that the flexural strength increased as the percentage of filler (dune sand, fly ash and quarry fines) increased from 50% to 70%.
The reason behind this reduction is the same as that for compressive strength reduction, as mentioned earlier. Moreover, there are two main reasons for reduction in flexural strength of such concrete. One is a decrease in the amount of solid material carrying load, which was replaced by RPA. The second reason is concentration of stresses around the boundaries of recycled plastic aggregates.
This means that the resistance of concrete containing synthetic RPA to chloride ion penetrability increases with the incorporation of RPA. This may he because recycled plastic aggregate particles block or distract the transferof chloride ions.
The synthetic RPA can be used as a total replacement of the natural/conventional lightweight aggregates in concrete. Use of plastic aggregate in concrete has certain advantages associated with its strength, light weight, durability, and elastic properties, As it is acknowledged that aggregate occupies nearly 70% to 75% of concrete volume, use of higher amounts of low weight materials (such as plastic) can contribute significantly to lightweight concrete. Lightweight concrete is useful in applications requiring concrete with a low density, such as pavement, floating structures, and shock absorbing structures. Moreover, the elastic properties of plastic will improve the elasticity of concrete and allow it to resist deformation.
Further, the presence of synthetic RPA in the concrete can make it more ductile and, as such, can significantly increase its deformation before dramatic failure. The concrete containing this property is more durable and can be utilized in applications that are exposed to severe chemical attack., such as chloride ion penetrability.
It is to be understood that the present invention is not limited to the embodiments described above, but encompasses any and all embodiments within the scope of the following claims.
This application is a divisional application of U.S. patent application Ser. No. 14/872,099, tiled on Sep. 30, 2015, presently pending.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14872099 | Sep 2015 | US |
| Child | 15656066 | US |