This invention is related to the recovery processing of hard alloy by electro-dissolution, which is used for separating the waste hard alloy into hard powders and metal ion solution in the acid solution.
It is known that typical electro-dissolution process is just suitable for the hard alloy whose binder content is over 15%, because when the binder content is low, the acid has to react with metal binder through the WC layer. For hard alloy whose binder content below 15%, the reaction speed is quite slow, the reaction depth could only be 2 mm˜3 mm, after that the reaction will stop because the acid is very hard to reach the metal binder with the obstruction of WC layer and oxidation bed.
Moreover, the quality of recovered WC powders is far lower than original powders', as there is always residual metal binder inside, and the impurity ions (Co, Ni, Cr, Ti, Na, Cl, etc) can't be cleaned thoroughly, the particle size will also be easily changed by the grinding process. Thus, typical recovered WC powders can only be used for low grade production, and also be sold at a low price.
The present invention makes substantial and significant inroads against the above problems by a method of flowing electrolyte of the electro-dissolution process for a low binder content hard alloy transversely of rather than longitudinally through dissolution cells, preferably augmented by supersonic wave induction in the electrolyte and that is preferably induced uniformly or nearly so in each cell or over the span of an array of cells. The hard alloy is generally used as a cell electrode—generally as anode portion of bipolar electrodes in a cell array (but also usable as end anode). Conductive cores or substrates (e.g. copper, aluminum or titanium foils or screens) are incorporated into or attached to the hard alloy electrodes. The electro-dissolution is substantially enhanced and produces the original particle components liberated from metal binder, generally as a porous flake form. The solid materials are rinsed and dried and separate using known per se methods and equipment, e.g. magnetic separator. The particles (flakes) are then milled (e.g. in a wet ball miller with alcohol carrier/lubricant) to specification powder size ranges and morphology and the liquid carrier is recovered. Conditions of drying do not cause significant rebonding by product powders. In addition to more thorough binder removal at high speeds, the process minimizes impurities in recovered hard alloy powders and the recovered particles are equivalent to virgin particles for subsequent reuse.
As used herein “hard alloy” includes compounds and alloyed mixtures such as refractory metal carbides, nitrides, borides, and silicides. Binders are generally metals, but could be other materials used in diverse applications of the hard alloy materials to effect consolidation that hold up under conditions of usage complementing self bonding of hard alloy particles. “Low” binder content means such low content of binder (and inversely, such high consolidated hard alloy content) that chemical or electrochemical dissolution is limited to thin surface layers of consolidated powder metallurgy articles.
Other objects, features and advantages of the invention will be apparent from the following detailed description of preferred embodiments taken in connection with the accompanying drawing, in which:
According to the invention, the longitudinal acid flow of typical electro-dissolution process is replaced by a transversal flow (shown in
The longitudinal acid flow is replaced by a transversal flow to progress the running quality of electrolyte, so that the concentration polarization of the acid can be decreased, furthermore, with the assistance of the supersonic wave, the acid can rapidly get through the WC layer, and react with metal binder, it can also prevent the oxidation bed from forming. For the hard alloy of 10% by weight of binder content, 5% by weight of tungsten carbide (WC) powders can only be made by the typical electro-dissolution process within one circulate, and according to the invention, with the transversal flow, the WC powders increased to 15%. With the assistance of supersonic wave, the number could reach 20%.
A supersonic wave cleaner is used for cleaning the WC flakes and unreacted hard alloy blocks.
It is known that the electrolyte is HCl solution, and the chlorine (CL—) ions can be quite harmful to the hard alloy, i.e. corrode the binder. Other impurities as Co, Ni, Cr, Ti, Na, etc. will decrease the grade of the WC powders, thus, it's necessary to get a better way for cleaning the WC flakes. Without the assistance of the supersonic wave cleaner, after cleaning the flakes for 3 times by pure water, the Cl content is about 700 ppm. After cleaning for 20 minutes by supersonic wave cleaner, the Cl content could get below 5 ppm.
A hot-air blast dryer is used fto drying the WC flakes. The hot-air blast dryer has a high efficiency for drying all kinds of materials. With adjusting the most suitable situation of temperature and time, WC flakes could be dried thoroughly within 3 hours, and also keep low oxidation content.
A roll-type magnetic separator is used fto separate the flakes with unreacted metal binder inside from the WC flakes. The roll-type magnetic separator has a high efficiency for separating relatively big size materials (below 3 mm diameter). With the magnetic separating by the separator, most of the big size WC flakes with unreacted metal binder is separated and sent back to the electrolytic tank.
The wet ball miller is used for grinding the WC flakes into WC powders which are almost the same particle shape and size distribution as original WC powders. Alcohol is used for the ball miller's mediator. Comparing to the dry ball miller, wet ball miller has an average power for crashing the WC flake, so that the size distribution of WC powders could be narrow. With adjusting the ball miller's parameters into the suitable situation for WC flake grinding, the particle shape and size distribution of recovered WC powders can reach the same grade of original WC powders.
A vacuum vibration dryer is used to evaporate the alcohol and recover it. After being drying by the vacuum vibration dryer thoroughly, the WC powders won't change the shape and it's also hard to make secondary bonding.
The thus recovered WC powders can be used in later consolidation or other manufacturing operations as if virgin WC powders.
Similar processing can be used and similar benefits realized in using the invention for recovery of other powers including metal carbides, borides, nitrides and silicides.
It will now be apparent to those skilled in the art that other embodiments, improvements, details, and uses can be made consistent with the letter and spirit of the foregoing disclosure and within the scope of this patent, which is limited only by the following claims, construed in accordance with the patent law, including the doctrine of equivalents.
This application claims priority from U.S. provisional application Ser. No. 61/236,564 filed Aug. 25, 2009.