Patent Application
20200325299
This disclosure relates generally to Reduced Density Thermoplastics structures produced through solid state foaming.
Plastics are widely used in both durable and non-durable applications. The majority of non-durable plastics are used in initial packaging of goods and food service packaging, often in single use applications.
The disposal of plastic products results in huge amounts of waste. Recyclable plastic products must be cleaned before recycling, which consumes additional energy. Due to incomplete cleaning and degradation of the polymers during processing they are often unable to be recycled into similar quality goods.
Foam plastic products produced through conventional means utilizing a chemical blowing agent solve some of the problems of solid plastic products by adding insulation and cushioning to their benefits, but often create new problems. Foamed plastic may become friable, and form small pellets nearly impossible to separate from a waste stream. The surface of foamed plastics is often cellular and unattractive to consumers.
The chemical blowing agents, fluorocarbons and chlorofluorocarbons, used in producing many foams have negative environmental effects, and the contamination of plastics from these blowing agents may render them non-recyclable.
Solid state foaming utilizing carbon dioxide, or other high pressure gas, as a foaming agent has been explored as a resolution to some of the above problems. Semi-continuous foaming is a method of interleaving a saturated roll of polymer with a gas-channeling means, which allows saturation of polymers prior to thermoforming. Semi-continuous production is a labor intensive process which consumes an interleaving layer and requires a large amount of plastic. Plastic loses gas during processing, and a large roll of plastic may take a long time to process, so the properties at the start of a foam roll may differ from those of the end of a roll.
The problems concerning the utilization of plastics in packaging, in both foam and solid form, extend to durable goods as well. A particular area of plastic usage for durable goods is composites, in which multiple phase separated materials are bonded together to create a single part with better properties. The center section of these parts are often foam. Most foams produced for these applications cannot be recycled after bonding, and are not biodegradable.
The instant application discloses, among other things, reduced density thermoplastics. A rapid foaming process which may create a polymer product which may include an integral solid skin by saturating thermoplastic sheet or preforms, heating, and then forming into final shape, is described. This method may be utilized with any thermoplastic. The material handling, saturation methods, and end products are unique and also described. Utilizing these methods with compostable Polylactic Acid (PLA) or a blend may result in low density, high strength compostable structures.
A more particular description of certain embodiments of Reduced Density Thermoplastics may be had by references to the embodiments described below, and those shown in the drawings that form a part of this specification, in which like numerals represent like objects.
In one embodiment, a set of plastic blanks may be created by either cutting from a roll of plastic or by injection molding of the shapes. Each blank may be shaped in such a manner that it provides the material for a small number of parts, such as one to 100. The blanks, which may be of any shape or size, may then be loaded into a rack for ease of saturation. The rack may then be loaded into a pressure vessel for saturation. The plastic may be allowed to saturate partially or fully, possibly resulting in a high gas concentration at the surface of the blanks. The blanks may then be removed, and the plastic may be transferred into a heating rack. The heating rack may be fed through a conventional thermoformer, where the blanks may be heated and stretched into shape. During heating and stretching, a solid state foam structure may be created.
A variation of the above embodiment is to injection mold blanks instead of extruding them. Injection molded parts may be formed of varying thickness, allowing different levels of saturation and the parts may be shaped in such a manner as to require little post-forming after heating. The injection molded parts may also be directly molded into a pressure vessel and allowed to cool, eliminating the need for saturation time.
Mask 120 may have an opening 150, and Mask 140 may have an Opening 160, which may allow portions of Plastic Blank 110 covered by Mask 120 and Mask 140 to be exposed to a gas foaming agent, while protecting other portions of Plastic Blank 110 from the gas foaming agent.
One having skill in the art will recognize that various ways of masking plastic blanks may be used, and that masks may have different sizes and shapes. Mask device may also be configured to hold several plastic blanks at the same time.
Mask Device 170 may have sufficient thermal shielding to prevent masked portions of Plastic Blank 110 from becoming heated enough to foam if Mask Device 170 is used during heating.
In another embodiment, sheet may be extruded directly into a pressure vessel. The extruded sheet may be allowed to cool into the pressure vessel, and loaded into racks. This variation eliminates the need for saturation time.
In yet another embodiment, gate-style valves and pressure locks may be used at the inlet and exit to all pressure vessels, and a conveyance system may be configured within the pressure vessel. The pressure locks may allow sheet, blanks, or preforms to enter a pressure vessel which contains other plastic. A material conveyance system within the pressure vessel may move items through the pressure vessel. All materials in this arrangement may receive precisely the same amount of time in the pressure vessel.
Various parameters such as temperature, pressure, gas foaming agent, and timing, may be adjusted to provide various characteristics of resulting foamed plastic. Saturation time and desorption time variations have been shown to be able to produce novel structures within the polymer. Higher gas concentration can lead to increases in crystallinity, and also to increases in bubble nucleation rates. Lower gas concentrations can lead to increases in density reduction. Combining these two elements can result in parts with high density exteriors and low density interiors, a structure that leads to optimal mechanical properties for a given part weight.
It may be desirable to add a solvent to the pressure vessel during the saturation process. When saturating PLA, it has been found that water induces a change in the surface of the sheet, creating a uniform white surface during heating. When saturating PET, it has been found that acetone will induce crystallization on the surface of the part.
Controlled heating of the plastic may be used to induce specific properties in foam parts. Heating a single side of the plastic sheet may cause an asymmetric density and foam cell distribution. Asymmetric density may optimize mechanical properties, such as creating a cup that is resistant to external crushing forces while bending outward easily for removal from a stack. Colorant usage may be optimized by creating a colored, high density exterior (colorants are dispersed by reducing density) while minimizing density in the remainder of the part.
It may be advantageous to partially distort the plastic blanks, or plastic exposed in holes during heating. This may be done to increase the uniformity of heating, or begin stretching into shape before beginning final shape stretching into a mold. This may be performed by increasing air pressure on one side of the sheets, decreasing air pressures on one side of the sheets, utilizing high pressure air jets, or by inducing stretching by direct mechanical force through the use of temperature controlled plugs.
Upon completion of the foaming operation, Rack 310 may be removed from Pressure Vessel, and Mask Device 170 may be extracted.
Plastic Blank 110 may then be heated through a thermoforming machine. Plastic Blank 110 may be held by rack or chain rails until heated. Portions of Plastic Blank 110 exposed by the mask may become foamed while portions protected by the mask may remain unfoamed.
For some products, Plastic Blank 110 may be pushed into a mold using, for example, a mechanical plug. Plastic Blank may be formed into a final desired shape using vacuum (reduced pressure), positive pressure, mechanical coercion, or combinations of these techniques.
For example, Plastic Blank 110 may be moved via a material conveyance system until it is over a mold to form a drinking cup. A clamp ring which may aid in the forming of a lip may hold Plastic Blank 110 in the proper position as an upper portion of a mold lowers to hold Plastic Blank 110 in place. Positive pressure may be applied from the top, while vacuum may pull Plastic Blank 110 into the mold. The mold may allow a lip to be formed where the top and bottom of the mold hold Plastic Blank 110 securely in place.
The following conditions have been used to produce a drinking cup. A sheet of Natureworks 4032D, 0.024 inches in thickness, may be saturated in a CO2 pressure vessel for 10 minutes, at a pressure of 600 pounds per square inch (PSI), with water vapor introduced during the fill cycle of the pressure vessel. The sheet was allowed to lose gas for 5 minutes prior (desorption time) to heating and stretching, and then heated while constrained within 0.2 inches of the cup perimeter until reaching approximately 90 degrees Celsius. The sheet may then be forced into a cup mold using an aluminum plug at 7 degrees Celsius, and set against a cup mold at 110 degrees Celsius for 15 seconds.
Pressure ranges from 400-1000 PSI for PLA and saturation times of 5 to 45 minutes may be useful for producing products. Desorption times of 5 to 30 minutes may be used to produce products. Plug temperatures may be varied from −5 C to 90 Celsius, and different materials may result in different cup wall thickness distributions. Cooler mold temperatures down to 0 Celsius may allow more rapid processing, although less foaming will be induced.
While the detailed description above has been expressed in terms of specific examples, those skilled in the art will appreciate that many other configurations could be used.
Accordingly, it will be appreciated that various equivalent modifications of the above-described embodiments may be made without departing from the spirit and scope of the invention.
The foregoing description of various embodiments of the invention has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. It is intended that the scope of the invention be limited not by this detailed description, but rather by the claims appended hereto. The above specification, examples and data provide a complete description of the manufacture and use of the invention. Since many embodiments of the invention can be made without departing from the spirit and scope of the invention, the invention resides in the claims hereinafter appended.
| Number | Date | Country | |
|---|---|---|---|
| 61837110 | Jun 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14308959 | Jun 2014 | US |
| Child | 16673368 | US |