Patent Application
20120281428
1. Field of the Invention
This is invention is related to device and apparatus and methods for producing white light from luminescent particle excitation and emission.
2. Description of the Related Art
The choice of general illumination sources for commercial and residential lighting is generally governed by a balance of energy efficiency and the ability to faithfully produce colors as measured by the color rendering index (CRI). Existing fluorescent lighting is known to be economical from an energy consumption point of view. However, many users complain that the light produced by the existing fluorescent lighting is of poor spectral quality and produces eye strain and other adverse health effects. Incandescent light is also widely used and is recognized as having excellent spectral quality and the ability to accurately render colors. This high spectral quality is derived from the hot filament, which serves as a blackbody radiator and emits light over many wavelengths, similar to the sun. However, incandescent lighting suffers from very low energy efficiency. Thus, there is a long felt need to produce light sources that use less energy and have a light composition similar to the composition of the sun light.
Solid-state lighting (SSL) is an alternative general illumination and lighting technology that promises the energy efficiency of fluorescent lights and the excellent spectral qualities of incandescent lighting. Typically, commercially available SSL lamps consists of a light emitting diode (LED) surrounded by a phosphor composed of large particles usually larger than 2 μm. The light emitted from the LED is of sufficient energy to cause the phosphor to fluoresce and emit one or more colors of visible light. The most common example of commercial SSL products consists of a blue LED (typically 460 nm) surrounded by a yellow phosphor, such as cerium-doped yttrium aluminum garnet (YAG:Ce), that emits lights in a broad band centered at 550 nm. The combination of nominally yellow light emission from the phosphor and blue light from the LED produces a light source that has a generally white appearance. Alternatively, an LED that emits in the ultraviolet (<400 nm) can be used to excite a blend of red, green, and blue phosphors.
In addition, while the light intensity from lamps used in current solid-state lighting products is sufficient for applications such as flashlights, it is considered too low and the emission cone is considered too narrow for use in general illumination applications such as room lighting. Hence, there is a need for solid-state light sources that are capable of providing high intensity white light emissions over a large enough area for use in general illumination.
One approach proposed to improve the performance of SSL devices has been to use nanoparticles such as quantum dots as secondary converters to produce white light. “Quantum Dots Lend New Approach to Solid-State Lighting,” Sandia National Laboratory press release Jul. 24, 2003. This approach incorporates quantum dots into a polymer used to encapsulate the light emitting diode (LED) and essentially creates a three-dimensional dome of quantum dots around the LED die. While this method has been successful in producing white light, the three-dimensional dome structure places large quantities of quantum dots in non-optimal positions around the LED and creates potential quantum dot agglomeration issues.
Previously, polymer/quantum dot compound nanofibers have been obtained from electrospinning of the polymer/quantum dot composite solutions, as disclosed in Schlecht et. al., Chem. Mater. 2005, 17, 809-814. However, the nanofibers produced by Schlecht et al. were on the order of 10-20 nm in diameter, in order to produce quantum confinement effects. The size range of the nanoparticles and nanofibers disclosed therein is not advantageous for conversion of a primary light into secondary light emission across the white light spectrum.
Lu. et. al., Nanotechnology, 2005, 16, 2233, also reported the making of Ag2S nanoparticles embedded in polymer fiber matrices by electrospinning. Once again, the size range of the nanoparticles and nanofibers shown therein is not advantageous for conversion of a primary light into secondary light emission across the white light spectrum.
As described in U.S. application Ser. No. 11/559,260, filed on Nov. 13, 2006, entitled “LUMINESCENT DEVICE,” referenced above, highly-efficient, light-producing sheets have been developed based on a combination of photoluminescent particles and polymer nanofibers. These luminescent sheets can be used in a white-light solid-state lighting device in which the sheets are illuminated by a blue light-emitting diode (LED) light source and the sheets will transform the incident blue light into, for example, yellow light. An appropriate mixture of yellow and blue light will produce the appearance of white light.
One particular advantage of these light-producing sheets is that photoluminescent particles are suspended in air on the nanofibers instead of being contained in a bulk material with a relatively high index of refraction. This arrangement prevents light from being trapped by total internal reflection, as occurs when the particles are encapsulated within bulk materials.
Other work (listed below and incorporated herein in their entirety by reference) has studied nanofibers in optical configurations where the unique nano-scale optical properties of the nanofibers were observed.
1. P. Vukusic, B. Hallam, and J. Noyes, Science 315, 348 (2007);
2. J. L. Davis, A. L. Andrady, D. S. Ensor, L. Han, H. J. Walls, U.S. patent application U.S. 20080113214 (submitted November 2006); H. J. Walls, J. L. Davis, and D. S. Ensor, PCT Patent Application WO2009/032378 (submitted June 2007); and J. L. Davis, H. J. Walls, L. Han, T. A. Walker, L A. Tufts, A. Andrady, D. S. Ensor, in Seventh International Conference on Solid State Lighting, edited by I. T. Ferguson, N. Narendan, T. Taguchi, and I. E. Ashdown, (SPIE Proceedings 6669) pp. 666916-1-666916-9;
3. J. Yip. S.-P. Ng, and K.-H. Wong, Textile Research Journal 79, 771 (2009);
4. U.S. Pat. No. 5,892,621, “Light reflectant surface for luminaires”
5. U.S. Pat. No. 6,015,610 “Very thin highly light reflectant surface and method for making and using the same”
In one embodiment of the invention, there is provided a fiber-based reflective lighting device which includes a source configured to generate a primary light, a mat of reflective fibers which diffusely reflects light upon illumination with at least the primary light, and a light exit configured to emanate the reflected light.
In another embodiment of the invention, there is provided a lighting device which includes a housing, a source configured to generate primary light and direct the primary light into the housing, a reflective mat of fibers disposed inside the housing at a position to reflect the primary light, and a light exit in the housing configured to emanate the reflected light from the housing.
In another embodiment of the invention, there is provided a lighting device insert which includes a reflective mat of fibers for insertion in a lighting device at a position and configured to diffusively reflect at least 70% of incident light.
It is to be understood that both the foregoing general description of the invention and the following detailed description are exemplary, but are not restrictive of the invention.
A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
Lighting devices for general illumination can be fabricated by combining a pump wavelength (e.g., blue emission in the 440-470 nm range; violet emission in the 380-440 nm range; or ultraviolet emission in the 330-380 nm range) with one or more photoluminescent materials that emit at wavelengths longer than the pump light. The photoluminescent material may be of multiple chemistries and particle sizes including phosphors, nanophosphors, and quantum dots. The luminescent material is often brittle and requires a binder or support matrix in order to be incorporated into practical devices.
In one embodiment of the invention, a lighting device includes luminescent particles combined with a polymeric material that provides mechanical strength and imparts desirable optical properties to the resulting photoluminescent layer. For example, it is desirable in some lighting applications to have a photoluminescent layer that includes a blend of light transmission and light reflection properties, which can be achieved through the judicious choice of materials for the composite. Alternatively, in some embodiments of the invention, it is desirable to have a photoluminescent layer that provides a high degree of light reflection. Alternatively, in some embodiments of the invention, it is desirable to have a fiber mat layer separate from the photoluminescent layer that provides a high degree of light reflection.
One way to control the transmission and reflection properties of the photoluminescent layer is by controlling the index of refraction of the photoluminescent layer. For example, a photoluminescent layer that is index matched with its surrounding medium will display a large light transmission, while a material that is not index matching will display a mixture of light transmission and light reflection. The extent of light reflection in such a media is determined by the difference in the index of refraction of the photoluminescence layer to the surrounding media through the Fresnel equations.
One alternative way to control the transmission and reflection properties of the photoluminescent layer is to introduce features with dimensions on the order of the wavelength of light. Such features, typically 100 nm to 800 nm in size, will promote scattering of the light beam, which increases the reflection coefficient. The features may be of a different refractive index than their surroundings which will impart transmission and reflection properties governed by the Fresnel equations. Examples of materials which can be incorporated into the photoluminescent layer include such materials as polymeric nanofibers, natural and synthetic papers such as PolyArt®, and etched glasses and plastics.
Light scattering occurring in the photoluminescent layer may also be used to increase the ability of the material to diffuse light or spread its intensity over a larger area. In the extreme, light scattering can be used to produce a Lambertian scatterer in which the intensity of the object appears the same regardless of the viewing angle.
The photoluminescent layer can be created in one embodiment by adding a range of photoluminescent materials to a polymeric or ceramic material that imparts the ability to control the transmission and reflection of light. Such photoluminescent materials include phosphors, nanophosphors, and quantum dots.
Phosphors are a general class of materials that emit radiation when exposed to radiation of a different wavelength. In one embodiment of the invention, such phosphors are generally exposed to either a blue, violet, or ultraviolet light source (i.e., pump) and will absorb photons from the incident light source creating an excited electronic state. This excited state can emit a photon at a wavelength that is generally longer than the pump wavelength through the process of fluorescence or more specifically photoluminescence. Phosphors are generally made from a suitable host material (e.g., aluminum garnet, metal oxides, metal nitrides, and metal sulfides) to which an activator (e.g., copper, silver, europium, cerium and other rare earths) is added. Typically, the phosphor particle size is often 1 μm or larger. Recently, phosphors have been developed that are characterized by particles sizes below 100 nm. These nanophosphors often have similar chemistries as larger particle sizes but scatter light to a lesser degree due to their small size.
Particles having a size less than 50 nm often can be classified as quantum dots. Quantum dots are nanoparticles whose dimensions have an order of magnitude equivalent to or smaller than the size of an electron at room temperature (deBroglie wavelength). When the size of the quantum dot is roughly the same or smaller than the deBroglie wavelength of an electron, then a potential well is created that artificially confines the electron. The size of this potential well determines the quantized energy levels available to the electron, as described in the “particle-in-a-box” solution of basic quantum mechanics. Since the energy levels determine the fluorescent wavelengths of the quantum dot, merely changing the size of the quantum dot changes, to a first approximation, the color at which the quantum dot radiates visible light. Thus, the quantum confinement effects of the quantum dots directly influence the light emitted from the respective quantum dot, and a broad spectrum of colors may be achieved by assembling quantum dots of different sizes.
A typical quantum dot includes a nanocrystalline core that may be surrounded by a shell of an inorganic material with a higher band gap. This structure is capped with an external organic layer that ensures compatibility with various solvents. In this context, the entire assembly (i.e., nanocrystalline core, shell of higher band gap material, and organic capping layer) is referred to collectively as a quantum dot. A representative example of such quantum dots includes a cadmium selenide nanocrystalline core surrounded by a zinc sulfide shell and capped with organic ligands such as trioctylphosphine oxide or a long-chain amine such as hexadecylamine. Such core shell structures are sold by Evident Technologies of Troy, N.Y.
The nanocrystalline core of quantum dots may be fabricated from a variety of materials including but not limited to at least one of silicon, germanium, indium gallium phosphide, indium phosphide, cadmium sulfide, cadmium selenide, lead sulfide, copper oxide, copper selenide, gallium phosphide, mercury sulfide, mercury selenide, zirconium oxide, zinc oxide, zinc sulfide, zinc selenide, zinc silicate, titanium sulfide, titanium oxide, and tin oxide, etc. Of particular utility to the invention are quantum dots having a core of at least one of CdSe, InGaP, InP, GaP, and ZnSe The optical properties of quantum dots are produced by this nanocrystalline core.
Quantum dots are commercially available as colloidal dispersions in low dielectric constant (low-K) organic solvents such as toluene. However, quantum dots experience mutual attraction and can agglomerate, which may disrupt their quantum behavior and change their performance characteristics. For example, agglomeration is known to reduce the light emission efficiency of quantum dots and is known to cause red-shifts in emission frequency due to energy transfer to larger dots formed as a result of agglomeration. See J. Rodriguez-Viejo, K. F. Jensen, H. Mattoussi, J. Michel, B. O. Dabbousi and M. G. Bawendi, Applied Physics Letters, vol. 70 (1997), no. 16, page 21, the entire contents of which are incorporated herein by reference. Due to the sensitivity of the human eye to slight color variations, particle agglomeration can have a significant impact on the quality of light from an illumination source. In the extreme, agglomeration can lead to quenching of photoluminescence from quantum dots.
Nanofibers are a solid structure that has one dimension (diameter) in the 10-2000 nm range, and the other dimension (length) can be quite long in the meters range. Nanofibers suitable for the invention can be made from a variety of materials, including polymers, ceramics, and glasses, sol gels, and blends of materials can also be readily fabricated. One feature of nanofibers is their small diameter and consequently high surface area. Nanofiber diameters on the order of visible light (˜500 nm) or even smaller can be readily produced creating very large surface areas.
Nanofiber Enhanced Reflectance:
As described in U.S. Application Ser. No. 61/169,468, filed on Apr. 15, 2009, entitled “STIMULATED LIGHTING DEVICE,” denoted above, nanofibers can be used in various lighting applications where the nanofibers are combined with luminescent particles such that primary light obliquely incident onto a luminescent sheet made of the nanofibers and the luminescent particles will emanate secondary light. In PCT Patent Application 2009/032378, the entire contents of which are incorporated herein by reference, nanofibers were shown to be reflective below a certain cut-off wavelength and transmittive above that wavelength.
Through experimentation, the present inventors have determined that thick nanofiber substrates can exhibit excellent broad spectrum reflectance in the visible spectrum. The value of the reflectance is dependent upon several parameters including fiber diameter, fiber surface morphology, substrate thickness and density. For example, thinner less dense fiber substrates typically possesses lower reflectance than thicker denser materials.
Referring now to the drawings, wherein like reference numerals designate identical or corresponding parts throughout the several views, in various embodiments of the invention,
Accordingly, in one embodiment of the invention, the reflective nanofibers are diffuse reflectors. Diffuse reflectance is the process by which a light beam at a given incidence angle and luminous intensity is reflected from a material over a wide range of angles spreading the luminous intensity over these angles. In the ideal case, diffuse reflectance will produce a material that reflects light with equal luminance in all directions.
The polymer nanofiber reflective substrate base can be used in either an undoped form or doped with luminescent materials. The nanofiber reflective substrate base can display a variety of optical properties by varying the transmittance and reflectance of the material, which can be tailored and controlled during the fabrication process. For simplicity, a nanofiber material exhibiting the ability to exhibit high diffuse reflectance across the visible spectrum is termed a nanofiber reflector (NFR).
Doping of nanofibers to create PLNs is typically performed using a coating process that concentrates the luminescent material at one surface of the substrate (as described in detail below). The phosphors or quantum dots (QD) can be loaded onto nanofibers with a sufficient loading to achieve virtually any desired lighting color. Phosphors are typically coated using either solvent-(e.g., spray coating) or aerosol-based (e.g., dry coating) methods, whereas QDs are typically applied using ink-jet printing methods.
While compatible with any phosphor chemistry, doped-silicate and selenide phosphors have been demonstrated to be working examples, using for example cadmium selenide cores with zinc sulfide shells. The photostability of these quantum dots (QD) is size dependent, with the larger particles (i.e., orange/red) exhibiting the highest photostability. In one embodiment, a doped-silicate phosphor provides broad emissions centered in the green (˜540 nm) and orange QDs are added to provide a narrow emission around 615 nm. The combination in one embodiment, when excited with a blue LED, produces white light (CCT: 2,700 to 5,000 K) with high color rendering indices.
In operation of a typical device, blue light emitted by a LED is directed at the PLN, and a portion of the blue light is converted into green and red emissions that are diffusely reflected away from the PLN. Unconverted portions of the incident blue radiation are also diffusely reflected by the nanofiber base of the PLN. The diffusely emitted light is confined and directed by a second nanofiber material (i.e., NFR layer) that is designed to exhibit high diffuse reflectance (R˜95%). In various embodiment of the invention, diffuse reflectance values range from 70% to 80%. In various embodiment of the invention, diffuse reflectance values range from 80% to 90%. In various embodiment of the invention, diffuse reflectance values range from 90% to 95%. In various embodiment of the invention, diffuse reflectance values are greater than 95%. The high reflectance of the NFR material minimizes light absorption and also serves to mix the red, green, and blue colors produced by the device. Light produced emerges from the device well mixed with good homogeneity.
In
A typical spectrum obtained using a Cree XRE LED (Part No. CREROY-L1-00001-00801) operated at 200 mA is shown in
The device has been tested at drive currents of up to 800 mA. No significant changes in CCT, CRI, or chromaticity coordinate were found. The measured properties of the device at an operational current of 200 mA were:
Duv is a measure of how far a given set of chromaticity coordinates lie from the Planckian locus (i.e., the blackbody radiator point for a give CCT). Low Duv values are preferred. CQS stands for color quality scale.
The introduction of the nanofiber liner increased the optical power output from this device by 49.8%. This increase is believed to be due to reduced absorption of the light in the down light configuration due to the presence of the reflective nanofiber material. Since the nanofibers used in this embodiment exhibit high reflectance (typically greater than 90%), the use of the material as a liner significantly reduces absorption by luminaire materials.
While not being limited to a particular phenomenological explanation, it is believed that the high reflectance of this material is due to Mie scattering arising from the nanoscale manipulation of the optical properties of the nanofiber. The contrast in index of refraction between the nanofiber (n˜1.5) and air creates sites for Mie scattering of light. The intensity of the reflected light (i.e., backscattering) will be proportional to the angular scattering distribution and the number of scattering sites. In smooth nanofibers, the scattering sites are provided by the nanofibers themselves and the areas between adjacent nanofibers. Since the probability for backscattering (i.e., reflection) is optimal for visible radiation when this spacing is on the order of the wavelength of light, increasing substrate density (i.e., decreasing void volume) would improve reflection intensity to a point. On porous nanofibers, the introduction of surface pores increases the number of scattering sites and increases backscattering efficiency as a function of thickness. In addition, surface pores of diameter 100-250 nm can be shown to possess a high probability for backscattering of visible radiation. Hence, the properly designed porous nanofibers of the invention can also be shown to be efficient reflectors of visible radiation.
In one embodiment of the invention, an additional mechanism to impart a discontinuity in the index of refraction is provided by the introduction of nanomaterials into the nanofiber. Typically, these nanomaterials will have diameters between 50 nm and 400 nm, and be composed of materials that are known to exhibit low absorbance in the visible spectrum. Examples of such materials include BaSO4, Teflon, TiO2, and Al2O3. Such additives would be chosen to have an index of refraction different from that of the polymer used to make the nanofiber.
In one embodiment of the invention, the reflection characteristics of the nanofiber can be altered. Typically, nanofiber substrates will exhibit diffuse reflection approaching Lambertian behavior. However, a certain amount of gloss (i.e., specular reflection) can be introduced into the substrate either by intentionally electrospinning in a manner that produces occasional larger features or by adding specular reflective material such as Al flake.
The average pore size obtained using this approach was seen to depend on the weight fraction of the additive in the spinning solution. This effect was demonstrated for the range of 2% and 20% (by weight) of N- methylformamide. At levels exceeding 20%, the pores were found to be too large to maintain the cylindrical shape of the nanofibers. Under these conditions, the porous fiber tended to collapse and fold into a ribbon, as shown in
It is apparent that the addition of high dielectric constant compound, such as N-methylformamide, make the resultant nanofibers porous, and eventually into a ribbon shape, as compared with round, cylinder shape for smooth nanofiber prepared with a single solvent system. For nanofibers prepared with lower concentration of N-methylformamide, such as 2% -5%, instead of a perfect sphere or circular shape on the nanofiber surface, the pore structures tends to become slightly more elongated, especially along the longitudinal direction of the resultant nanofiber. When the concentration of the N-methylformamide increases 10%-20%, the round pore tends to become even more elongated along the longitudinal direction of the resultant nanofiber. When the N-methylformamide concentration reach to 20%, the pores started to merger into each other and form very rough surface features on nanofiber surface. These features can be characterized as round pores at certain experimental conditions and the existence of the threshold is clearly observed between 5% and 10% weight ratio N-methylformamide, where the pore size significantly increases and the shape becomes more elongated.
It is observed that the pores on the nanofibers range in shape from slightly elongated shapes to oval shapes and have an aspect ratio in the range of 1.1:1 to 10:1. The pores are partially embedded into the surface of the nanofiber and in some instances have an estimated depth of 5-100 nm, although smaller pore depths may not be readily detectable. The pores have an estimated length from 5-100 nm, although smaller pore lengths may not be readily detectable. The pores thus expose an interior surface of the nanofiber, providing for an increased surface area, as compared to a similar diameter nanofiber without pores. Adjacent pores can be totally separated from each other by a nanofiber wall material in between, or adjacent pores can partially overlap forming larger cavities in the nanofibers.
Examples of other high dielectric constant compounds suitable for the invention include, but are not limited to: N-Methylformamide, N-Methylacetamide, N-Methylpropanamide, N-Ethylacetamide, N-Propylpropanamide, Formamide, N-Butylacetamide, N-Ethylformamide. Their compatible solvents include but not limited to toluene, dimethylformamide, chloroform, dichloromethane, dimethylacetamide, and acetone. The polymers include but not limited to are Poly(methyl methacrylate), Poly(butyl methacrylate), Poly(Benzyl methacrylate), Poly(caprolactone), Poly(vinyl alcohol), Poly(Acrylonitrile), Poly(carbonate), and blends thereof.
The following table provides a listing of the reflectance of common materials. In one embodiment of the invention, materials of this optical type are introduced for the specular reflective material. Such materials for example can include Al, Au, Ag, TiO2, ZnO, BaSO4, and Zn in particle or flake form.
In one embodiment of the invention, the addition of a nanofiber material designed to provide high reflectance can be used to increase the energy efficiency of lighting devices. The nanofiber can be used as a liner in downlights and for lighting troffers.
Thus, the reflective nanofiber mat or substrate of the invention in general provides the following embodiments:
1. Nanofiber materials lining the walls of a luminaire such as a downlight, light troffer, or other lighting device.
2. A nanofiber fiber mat or substrate including smooth, randomly oriented nanofibers with dimensions comparable to the wavelength of visible light or flat, ribbon-shaped fibers with surface pores with diameters comparable to the wavelength of light that impart of textured surface morphology.
3. A nanofiber material functioning as a diffuse (i.e., Lambertian) reflector or including features or additives that impart a gloss characteristic to the substrate. Such a substrate may exhibit both specular and diffuse reflection with the ratio of the two controlled by the relative composition of diffuse reflection sites and specular reflection sites. This structure can be fabricated in an electrospinning chamber such as shown in
One illustrative set of parameters for use in
4. A nanofiber fiber mat or substrate including additives such as high dielectric constant materials (e.g., ZnO, BaSO4,TiO2, Al2O3, etc.) which provide additional scattering sites and increase reflectance. These additives can be dispersed into the electrospinning solution and a composite of the nanofiber and high dielectric constant material is provided directly by electrospinning operation. In one embodiment of the invention, random, textured (i.e., porous) nanofibers are the most effective for use as optical filters and wavelength selective reflectors, as discussed above. In contrast, thin layers of smooth round nanofibers have been found to be poor scatterers of lights and are not as effective for either use. Typical % T data observed from thin layers of smooth nanofibers are given in
More specifically, the nanofiber substrate can be coated with the high dielectric constant material using methods described in U.S. Patent Application 2008/0113214, herein incorporated by reference. In one embodiment of the invention, as discussed above, high dielectric constant materials such as for example ZnO, BaSO4,TiO2, Al2O3, etc can be applied to the fiber mats after electrospinning. This embodiment is illustrated in
5. Photoactive fillers such as TiO2 can be added to the nanofiber to provide continual cleaning of the nanofiber under the blue irradiation of the pump LED used in a solid-state lighting device. TiO2 is a known photocatalyst and when excited by wavelengths of sufficient energy will oxidze organic compounds. The badgap of TiO2 can be adjusted using known techniques such that the excitation wavelengths provided in solid-state lighting (i.e., 350 to 470 nm) are sufficient to initiate the photo-oxidation reaction. TiO2 and similar photocatalytic additives can be dispersed into the electrospinning solution and a composite of the nanofiber and the photocatalytic material is provided directly by electrospinning operation. Alternatively, the nanofiber substrate can be coated with the photocatalytic material using methods described in U.S. Patent Application 2008/0113214, herein incorporated by reference.
Photoluminescent Fibers:
Hence, in various embodiments of the invention to be explained in greater detail below, there is provided a device including the fiber substrate shown for example in
As discussed later in greater detail, the average fiber diameter is in a range between 100 to 5000 nm, or more suitably between 100 nm to 2000 nm, or more suitably between 100 nm to 1000 nm. The wavelength λ is in a range between 100 and 2000 nanometers, or more suitably between 100 and 500 nanometers. The fiber substrate 6 has a thickness in a range between 0.1 and 2,000 microns, or more suitably in a range between 1 to 500 microns.
In various embodiments of the invention, the stimulatable particles 4 include for example besides or in addition to the quantum dot materials listed above phosphors, including nano-phosphors. Phosphors such as for example in the list below and others are suitable for the invention. Examples of suitable phosphors include, but are not limited to:
1. Rare-Earth doped metal oxide such as Y2O3:Tb, Y2O3:Eu3+, Lu2O3:Eu3+, CaTiO3:Pr3+, CaO:Er3+, (GdZn)O:Eu3+; Sr4Al14O25:Eu3+, GdMgB3O10:Ce3+:Tb3+, CeMgAl11O19:Ce3+:Tb3+, Y2O3:Eu3+;
2. Metal sulfides such as CaS:Eu2+, SrGa2S4:Eu and CawSrxGay(S,Se)z:Eu
3. Rare-Earth doped yttrium aluminum garnet (YAG) such as YAG:Ce3+;
4. Metal silicates including Ca3(Sc,Mg)2Si3O12:Ce and (Ba,Sr)2SiO4:Eu;
5. Rare-Earth doped zirconium oxide such as ZrO2:Sm3+, ZrO2:Er3+;
6. Rare-Earth doped vanadate (YVO4:Eu) and phosphate (La,Ce,Tb)PO4;
7. Doped materials consisting of a host matrix (e.g., Gd2O3, GdO2S, PbO, ZnO, ZnS, ZnSe, Silicate) and a dopant (Eu, Tb, Tm, Cu, Al and Mn); and
8. Metal-doped forms of zinc sulfide and zinc selenide (e.g., ZnS:Mn2+, ZnS:Cu+, Zn0.25Cd0.75S:AgCl).
Other examples of phosphors for use with this invention may be found in W. M. Yen, S. Shionoya, and H. Yamamoto, Phosphor Handbook, Second Edition the entire contents of which are incorporated here by reference. Of particular utility to the invention are nanophosphors including at least one of rare-Earth doped YAG, doped metal sulfides including doped ZnS and doped SrGa2S4, doped silicates, and doped ZnSe.
Further, as discussed in more detail later, the stimulatable particles 4 can include a plurality of color-distinctive light emitters (i.e., a distribution of different sized quantum dots or a distribution of phosphors) or a combination of quantum dots and phosphors which produce respective secondary light emissions from the primary light and thereby form a resultant white light having a color rendering index greater than 70, or greater than 80.
In one embodiment of the invention, by dispersing the stimulatable particles 4 on a high surface area medium such as for example a fiber substrate of nanofibers, the emission efficiency of a fiber substrate 6 containing the nanofibers 2 and the stimulatable particles 4 (e.g., the quantum dots or phosphor) is increased above that achieved with planar packing of the luminescent particles are dispersed in a film. As a result, in one embodiment of the invention, such a nanofiber substrate structure can capture, with a higher efficiency than if the quantum dots were dispersed in a film, photons emitted by an LED and re-radiate at visible wavelengths with higher intensities than would be possible with planar packed luminescent particles.
While not limited to any particular theory, light scattered from the fibers 2 depends on the fiber diameter, light wavelength, orientation of the fiber to the light and the refractive index of the fibers. Polymers of the fibers have real refractive indices in the range between 1.3 to 1.6. Examples of the light scattering efficiency curves for long fibers of slightly absorbing materials (and which may act in a similar manner as the nanofiber structures of the invention) have been detailed previously by Van de Hulst, in Light Scattering by Small particles, Dover, 1957. In that earlier work, for an incident light of 300 nm, the maximum light scattering has a size parameter (π times fiber diameter/wavelength) of 3.14 and a scattering efficiency (Q) of Q1=4.2. For incident light at 600 nm, the size parameter is 1.6 and Q1=2. Therefore, the shorter wavelength light (expected to be used frequently in the invention) is twice more likely of being trapped in the substrate of fibers than the longer wavelength light. An alternative explanation of this phenomenon is that, on average, the optical path length (OPL) of light at 400 nm through an appropriately designed nanofiber material is longer than the OPL of 600 nm light. The implications of this phenomenon as applied to the invention are that an enhancement of light emission may be obtained from the light scattering characteristics of the fibers in the fiber substrate (i.e., each fiber acting as a scattering center, and the substrate of fibers acting as a medium to more effectively confine the excitation light in the fiber substrate medium permitting a higher probability that the excitation light would interact with a light emitter during its residence in the fiber substrate.
For example, in the invention a typical excitation wavelength is blue light at 450 nm. In order to produce white light, the structure will need to emit radiation over a broad range of frequencies from 450 nm to 700 nm. By fabricating a nanofiber structure in which the average diameter of the nanofibers 4 in the substrate 6 is roughly the same as that of the excitation source (i.e., 450 nm), the excitation frequency can be effectively trapped in the nanofiber structure by light scattering (i.e., OPL of the excitation source is long). This increases the likelihood that the excitation source will initiate fluorescence and produce white light. In contrast, the longer wavelength emissions produced by fluorescence of the luminescent compound will be scattered less effectively by the nanofibers in the fiber substrate, and are more likely to emerge from the fiber substrate structure with minimal scattering. Under these conditions, the light scattering/photonic properties as a function of wavelength and fiber diameter are improved.
In one embodiment of the invention, the fiber substrate 6 includes a number of nanofibers layers (as shown in
Fabrication Procedures
Formation of the reflective and light stimulatable structures in the invention can occur through a number of methods. The formation methods typically involve the formation of nanofibers 2 of a controlled diameter and the application of the stimulatable particles 4 (e.g., quantum dots or phosphors) to the nanofibers 2, for stimulatable structures only. Reflective materials are fabricated by electrospinning the nanofibers and using them without the addition of other materials such as stimulatable particles. Stimulatable structures may be formed by several methods. In one method, stimulatable particles 4 can be applied to the electrospun fibers as the fibers are coalescing into a resultant fiber substrate. In one method, stimulatable particles 4 can be included in the electrospray medium. In one method, stimulatable particles 4 can be applied to the resultant fiber substrate after the substrate has been formed without any stimulatable particles. Likewise, nanofiber substrates containing high diectric constant and/or photocatalytic materials can be made by several methods. In one method, high dielectric constant and/or photocatalytic particles 4 can be applied to the electrospun fibers as the fibers are coalescing into a resultant fiber substrate. In one method, high dielectric constant and/or photocatalytic particles 4 can be included in the electrospray medium. In one method, high dielectric constant and/or photocatalytic particles 4 can be applied to the resultant fiber substrate after the substrate has been formed without any particles.
In
The electrospinning element 24 communicates with a reservoir supply 30 containing the electrospray medium such as for example the above-noted polymer solution. The electrospray medium of the invention includes polymer solutions and/or melts known in the art for the extrusion of fibers including extrusions of nanofiber materials. Indeed, polymers and solvents suitable for the invention include for example polystyrene in dimethylformamide or toluene, polycaprolactone in dimethylformamide/methylene chloride mixture, poly(ethyleneoxide) in distilled water, poly(acrylic acid) in distilled water, poly(methyl methacrylate) PMMA in acetone, PMMA in dimethyl formamide (DMF), PMMA in N-methyl formamide (NMF), cellulose acetate in acetone, polyacrylonitrile in dimethylformamide, polylactide in dichloromethane or dimethylformamide, nylon in formic acid, nylon in acetic acid, and poly(vinyl alcohol) in distilled water and combinations thereof. In general, suitable solvents for the invention include both organic and inorganic solvents in which polymers can be dissolved. The polymer materials when formed are preferably organic materials to provide reflective substrates, although the polymers may be spun with additives that act as color filters for the luminescent compounds (as discussed in more detail later), high dielectric constant additives to increase reflectance, or photocatalytic additives to provide a measure of self-cleaning.
A high voltage source 34 is provided to maintain the electrospinning element 24 at a high voltage. The collector 28 is placed preferably 1 to 100 cm away from the tip of the electrospinning element 24. The collector 28 can be a plate or a screen. Typically, an electric field strength between 2,000 and 400,000 V/m is established by the high voltage source 34. Typically, the collector 28 is grounded, and the fibers 26 produced by electrospinning from the electrospinning elements 24 are directed by the electric field 32 toward the collector 28. The electric field 32 pulls the substance from which the fiber is to be composed as a filament or liquid jet 42 of fluid from the tip of the electrospinning element 24. A supply of the substance to each electrospinning element 24 is preferably balanced with the electric field strength responsible for extracting the substance from which the fibers are to be composed so that a droplet shape exiting the electrospinning element 24 is maintained constant. In the polymer solutions (or alternatively introduced onto the fibers after or during the electrospinning process) are either luminescent compounds, high dielectric constant materials, or photocatalytic materials. The fibers deposited in the one embodiment of the invention may range from 50 nm to several microns in diameter.
As in the related application, U.S. Ser. No. 11/130,269, previously incorporated by reference, the invention can use different electrospinning elements to generate a fiber substrate of mixed fibers of different sized fibers. The fiber substrate can have for example one side of the substrate with a larger average fiber diameter than another side of the fiber substrate.
The fibers used in the nanofibers of the invention include, but are not limited to, acrylonitrile/butadiene copolymer, cellulose, cellulose acetate, chitosan, collagen, DNA, fibrinogen, fibronectin, nylon, poly(acrylic acid), poly(chloro styrene), poly(dimethyl siloxane), poly(ether imide), poly(ether sulfone), poly(ethyl acrylate), poly(ethyl vinyl acetate), poly(ethyl-co-vinyl acetate), poly(ethylene oxide), poly(ethylene terephthalate), poly(lactic acid-co-glycolic acid), poly(methacrylic acid) salt, poly(methyl methacrylate), poly(butyl methacrylate), poly(benyl methacrylate), poly(lauryl methacrylate), polyacrylates, poly(methyl styrene), poly(styrene sulfonic acid) salt, poly(styrene sulfonyl fluoride), poly(styrene-co-acrylonitrile), poly(styrene-co-butadiene), poly(styrene-co-divinyl benzene), poly(vinyl acetate), poly(vinyl alcohol), poly(vinyl chloride), poly(vinylidene fluoride), polyacrylamide, polyacrylonitrile, polyamide, polyaniline, polybenzimidazole, polycaprolactone, polycarbonate, poly(dimethylsiloxane-co-polyethyleneoxide), poly(etheretherketone), polyethylene, polyethyleneimine, polyimide, polyisoprene, polylactide, polypropylene, polystyrene, polysulfone, polyurethane, poly(vinylpyrrolidone), proteins, SEBS copolymer, silk, and styrene/isoprene copolymer.
Additionally, nanofibers containing polymer blends can also be produced as long as the two or more polymers are soluble in a common solvent. A few examples would be: poly(vinylidene fluoride)-blend-poly(methyl methacrylate), polystyrene-blend-poly(vinylmethylether), poly(methyl methacrylate)-blend-poly(ethyleneoxide), poly(methyl methacrylate)-blend-poly(butyl methacrylate), poly(hydroxypropyl methacrylate)-blend poly(vinylpyrrolidone), poly(hydroxybutyrate) -blend-poly(ethylene oxide), poly(methyl methacrylate)-blend-poly(lauryl methacrylate), protein blend-polyethyleneoxide, polylactide-blend-polyvinylpyrrolidone, polystyrene-blend-polyester, polyester-blend-poly(hyroxyethyl methacrylate), poly(ethylene oxide)-blend poly(methyl methacrylate), poly(hydroxystyrene)-blend-poly(ethylene oxide).
Reflective Nanofiber Substrate Formation
In general,
Particles can be added to the forming or collected nanofibers to alter the physical properties of the nanofibers. The particles may be either light stimulable, made from high dielectric constant materials, or photocatalytic. At 500, a polymer solution including particles is electrospun using conditions described above. At 510, from the electrospun solution, nanofibers are formed having a diameter between 100 and 5000 nm and including the stimulatable particles. At 520, the nanofibers are collected to form a fiber substrate. The process at 500 reflects the general techniques described above for electrospinning nanofibers preferably under controlled conditions. At 500, care is taken to sonicate the particle compounds in solvent prior to mixing with the polymer in the reservoir 30 to ensure adequate dispersion. Adequate dispersion results in a uniform distribution of the particles throughout the resultant fiber substrate. Normally, a sonication time greater than 12 hours is sufficient to obtain a uniform compound suspension in the solution. The ratio of polymer to particle compound in the solution will typically range from 1:50 to 100:1
Further, according to one embodiment of the invention, a local concentration of the stimulatable particles in the polymer solution that is too high can result in deleterious agglomeration of these compounds.
In one embodiment of the invention, agglomeration is undesirable since it results in non-uniformity in the dispersion of the luminescent compound in the resultant fibers. Agglomeration can change the color uniformity of the resultant light emissions. In addition, agglomeration also degrades the optical properties of the luminescent compound by causing a red-shifting of the emission frequency and a reduction of emission intensity due to self-absorption.
The size distribution of the particles can be controlled by managing a number of parameters such as for example: changing an organic phase of a solvent system, changing a temperature at which the nanoparticles are formed, alternating reactant concentrations used to form the nanoparticles, changing the capping molecule chemistry, adding surfactants to control a coagulation of the material from which the nanoparticles are to be formed, applying an electrical or magnetic field during particle nucleation, applying acoustical energy during the formation of the nanoparticles, etc.
The capping molecule chemistry can include for example forming a shell around the nanoparticle (i.e., the quantum dot) to chemically stabilize the nanoparticle. The surfactants (e.g., organic ligands) can be included around and attached to the outside of the shells to promote solution and prevent agglomeration. Such surfactants help prevent agglomeration of particles when the particles are created or used in a dry state. Alternatively, a separation method such as electrophoretic separation can be used after the particle nucleation to achieve a desired particle distribution.
At 500, the electrospinning solution can include additives such as for example organic luminescent materials (dye), ceramics, organo-metallic, carbon, and or metal. For example, the index of refraction of the nanofibers can be increased by adding a material with a high dielectric constant, such as a ceramic like Al2O3. The additives are incorporated into a polymer to impart desired physical, chemical, or mechanical properties. The additives are usually mixed with the polymer prior to electrospinning and do not generally form strong chemical bonds with the polymer. Examples of common additives found in polymers suitable for the invention include pigments (e.g., Al2O3, BaSO4), conductive or reflective materials (e.g., metallic flakes), photocatalytic materials for self-cleaning (e.g., TiO2), UV stabilizers, and glass reinforcements.
At 510, the conditions in the electrospinning environment are controlled. U.S. Ser. No. 10/819,945 entitled “Electrospinning in a Controlled Gaseous Environment” describes techniques applicable to the invention for controlling the electrospraying environment. Additionally, refinements of the electrospinning process are described in U.S. application Ser. No. 10/819,916, entitled “Filter Incorporating Nanofibers,” previously incorporated herein by reference. The practices described therein can be used in the invention to produce small diameter nanofibers whose large surface to volume ratio can enhance the brightness of the light emitted from the resultant fiber substrate and whose average fiber diameter size is appropriately sized to match the incident light source wavelength.
At 520, techniques in U.S. application Ser. No. 10/819,916, entitled “Electrospinning of Fibers using a Rotatable Spray Head” to obtain aligned fibers or techniques in U.S. application Ser. No. 10/819,916, entitled “Filter Incorporating Nanofibers” can be used to improve fiber mat density and uniformity.
Light Emitter Incorporation onto Nanofibers during Electrospinning
In one embodiment of the invention, as discussed above, stimulatable particles 4 can be applied to the electrospun fibers 2 as the fibers are coalescing into a resultant fiber substrate 6.
Low agglomeration of stimulatable particles 4 can be achieved by separating the nanofiber formation and light stimulatable particle attachment steps. This can be achieved in one embodiment of the invention by introducing for example stimulatable particles 4 (such as from an electrospray solution) into a region where an emerging nanofiber is drying. In an electrospray introduction technique, submicron droplets of the stimulatable particle suspensions are generated by electrostatically disrupting a droplet of a solvent (such as for example toluene) containing the stimulatable particles. The electrosprayed droplets are highly charged (usually positively charged) and do not aggregate due to repulsion of similar charges during their passage to the surface of the polymer nanofiber 6 that, in one embodiment, can be carrying an opposing electrical charge.
Since the nanofiber is drying during ejection from the needle, in one embodiment of the invention, the location of the electrospray controls the penetration of the stimulatable particles 4 into the nanofiber 2. For example, if the electrospray beam is moved closely to the electrospraying tip, the nanofibers will likely be softer since they will contain more solvent and the stimulatable particles 4 will embed deeper into the fiber. Alternatively, if the electrospray beam is moved away from the electrospraying tip and closer to the collector, the nanofibers will be drier and the stimulatable particles will be restricted to the surface. Other parameters such as the solvent used to disperse the stimulatable particles may also influence the penetration depth of the electrosprayed stimulatable particles.
At 710, the processes described in U.S. Ser. No. 10/819,945 entitled “Electrospinning in a Controlled Gaseous Environment” for controlling the electrospraying environment to influence (retard) the drying rate of the electrospun fibers are applicable. At 710, the processes described in U.S. Ser. No. 11/130,269 entitled “Nanofiber Mats and Production Methods Thereof” with regard to the delivery and incorporation of particles into fibers are applicable to the invention.
The process at 720 is similar to the processes described above at 520.
Particle Incorporation onto Nanofibers after Electrospinning
In one embodiment of the invention, as discussed above, particles such as light stimulatable particles (e.g. example quantum dots or phosphors) can be applied to the fiber substrates after electrospinning. Other examples of particle coatings include high dielectric constant materials and photocatalytic materials such as TiO2. This embodiment is illustrated in
During the coating process, the polymer nanofibers may swell due to the solvent. This expansion of the fibers in the network also expands the spaces between the fibers, thus opening the network spaces to allow the particles to move in between. Thus, the particles may move to the fiber surface due to the Brownian motion. The fiber substrate 6 may be coated in the solution for a period of 1 minute to 72 hours and may be rinsed with a solvent for 0-60 seconds to ensure the removal of any loosely attached surface particles. The fiber substrate 6 may then be placed onto a support and allowed to completely dry under room temperature before use. The coating solution may contain additives such as polymers or tackifiers to increase the adhesion of the particles to the nanofiber.
The surface density of the particles on the polymer nanofibers made according to the method of the invention described in
While particle incorporation into a matrix such as a fiber or fiber substrate described in the invention, this aspect of the invention is not so limited to electrospinning and fibers. A variety of processes, including the above-noted electrospinning, and other conventional techniques such as spray coating, drop coating, spin coating, transfer printing, thermal printing, ink-jet printing, aerosol handling, electrostatic method, extrusion of filled polymers, self-assembled monolayers, etc. can be used according to the invention to form a matrix having a predetermined distribution of luminescent or light stimulatable compounds. In those examples, the matrix need not be electrospun fibers and provides a host upon which exposure to a solvent containing a dispersion of the light emitting particles will result in the application of the particle (i.e., quantum dots, phosphors, nononphosphors, or electroluminescent particles) to the matrix. The matrix material is preferably organic-based but could include sol-gel materials containing inorganic bases.
Relative Light Emitter Distribution
In one embodiment of the invention, the luminescent compounds used to make the light stimulatable devices of the invention are particles forming for example either quantum dots, phosphors, or nano-phosphors. Quantum dots (i.e., the stimulatable particles 4) emit electromagnetic waves at wavelengths that depend, to a first approximation, on the diameter of the nanoparticles. For example, CdSe nanoparticles of 2.8 nm nominal diameter emit green light at roughly 530 nm, whereas CdSe nanoparticles of 5.0 nm nominal diameter emit red light at roughly 625 nm. The mixing of specific particles (each having a characteristic wavelength emission) can be used in the invention to produce “white light” similar to the mixing techniques used in the mixing of phosphors for fluorescent lights.
In one embodiment of the invention, the nominal sizes disclosed for the stimulatable particles can have a variance in size distribution or surface structure that results in broad-band (as compared to discrete or line emissions). For example, quantum dots of a narrow size distribution that do not contain an inorganic shell layer may exhibit broadband emission due to excitation of surface defects and traps. An example of such materials is found in Bowers et al. Journal of the American Chemical Society vol. 127 (2005) pages 15378-15379 the entire contents of which are incorporated here by reference. Likewise, broad size distributions of core shell quantum dots can be produced by controlling the parameters of the reaction used to synthesize them. The broad band emissions emulate black body radiation sources. Luminescent devices of the invention exhibiting broad band emissions have a higher color rendering index.
In one embodiment of the invention, because nanoparticles emit light having a wavelength depending on the diameter of the nanoparticles, white light may be generated from a fiber substrate having different diameter particles dispersed throughout. For example, particles having a first diameter may produce an electromagnetic wave having a first wavelength, particles having a second diameter may produce an electromagnetic wave having a second wavelength, and so on until the plurality of particles produce all the wavelengths necessary to produce a desired spectrum such as that of a blackbody radiator having a CRI approaching 100. The particles used to produce such white light may be from the same chemistry (e.g., CdSe/ZnS quantum dots) or may be from different chemistrys (e.g., combination of doped-silicate or doped-selenide phosphors with CdSe/ZnS quantum dots). In some instances, it may be necessary to physically separate the different particles in order to avoid undesired absorption of secondary emissions. This can be accomplished in one embodiment of the invention by using a substrate, such as the nanofibers described above, having strong light scattering properties for select wavelengths.
Below are examples of such mixtures determined with regard to various excitation sources:
Luminescent compound: a single variety of CdSe/ZnS core shell quantum dots with particle diameter 2.6-3.2 nm (configured for yellow emission and commercially available from Evident Technologies)
Such yellow emitting quantum dots in this example are incorporated into and onto the fibers at weight percentages between 0.1% and 30% (weight quantum dots/weight fiber) with a more suitable range of weight percentage between 1% and 10% depending upon desired light output.
When packaged with the blue LED emitting at 450-460 nm, the blue light from the LED and the yellow emission from the photoluminescent fiber in this example blend to produce white light.
Luminescent compound: Two different sizes of CdSe/ZnSe core shell quantum dots with the particle diameter of the first size being 2.4 nm (green emission) and the particle diameter of second size being 5.2 nm (red emission) (purchased from Evident Technologies).
These two sizes of luminescent quantum dots are incorporated into and onto the fibers at weight percentages between 0.1% and 30% (total weight quantum dots/weight fiber) with a more suitable range of weight percentage between 1% and 10%. The ratio of green particles to red particles incorporated into and on the fibers varies between 1:1 to 20:1 depending upon desired light output. In order to prevent undesired absorption of secondary emissions, it may be preferable to physically separate the two sizes of luminescent quantum dots. This can be achieved in one embodiment of the invention by locating the quantum dots on separate sides of the fiber substrate or by placing the quantum dots in different zones or pixels on the same side of the fiber substrate.
When packaged with a blue LED emitting at 450-460 nm, the blue light from the LED and the green and yellow emission from the photoluminescent fiber in this example blend to produce white light.
Luminescent compound: Three different sizes of CdSe/ZnSe core shell quantum dots with the particle diameter of the first size being 1.9 nm (blue emission), the particle diameter of the second size being 2.4 nm (green emission), and the particle diameter of third size being 5.2 nm (red emission) (purchased from Evident Technologies).
These three sizes of luminescent quantum dots are incorporated into and onto the fibers at weight percentages between 0.1% and 100% (total weight quantum dots/weight fiber) with a more suitable range of weight percentage between 1% and 50%. The ratio of blue particles to green particles to red particles incorporated into and on the fibers is chosen to produce light emissions with relative intensities between 1:2:3 (for “warm white” color) to 2.5:1.5:1 (for “cool white” color) depending upon desired light output. In order to prevent undesired absorption of secondary emissions, it may be preferable to physically separate the three sizes of luminescent quantum dots. This can be achieved by locating the quantum dots on separate sides of the fiber substrate or by placing the quantum dots in different zones or pixels on the same side of the fiber substrate.
When packaged with a violet emitting LED at 408 nm, white light is produced in this example by blending the emission of blue, red, and green colors by the photoluminescent nanofiber. Little to no visible radiation from the LED contributes directly to the white light product.
Luminescent compound: Three different sizes of CdSe/ZnSe core shell quantum dots with the particle diameter of the first size being 1.9 nm (blue emission), the particle diameter of the second size being 2.4 nm (green emission), and the particle diameter of third size being 5.2 nm (red emission) (purchased from Evident Technologies,45 Ferry Street Troy, N.Y. 12180).
These three sizes of luminescent quantum dots are incorporated into and onto the fibers at weight percentages between 0.1% and 100% (total weight quantum dots/weight fiber) with a more suitable range of weight percentage between 1% and 50%. The ratio of blue particles to green particles to red particles incorporated into and on the fibers is chosen to produce light emissions with relative intensities between 1:2:3 (for “warm white” color) to 2.5:1.5:1 (for “cool white” color). In order to prevent undesired absorption of secondary emissions, it may be preferable to physically separate the three sizes of luminescent quantum dots. This can be achieved in one embodiment of the invention by locating the quantum dots of different sizes on separate sides of the fiber substrate or by placing these quantum dots in different zones or pixels on the same side of the fiber substrate.
When packaged with a UV emitting LED at 350-370 nm, white light is produced by the blending of emissions of the blue, red, and green colors by the photoluminescent nanofiber.
Luminescent compound: Green phosphors such as the sulfoselenide compositions sold by PhosphorTech [Lithia Springs, Ga.] can be applied to an uncoated nanofiber using the coating processes of drop coating, ink-jet printing, spray coating, dip coating, or similar methods. Added to this composite were red emitting quantum dots using processes such as ink-jet printing, spray coating, dip coating, or drop coating. When this construct is packaged with a blue emitting LED at 450 to 470 nm, white light is produced in this example by blending the emissions of the green phosphor, red quantum dot, and blue LED.
Luminescent compound: Green phosphors such as the doped silicate compositions sold by Intematix [Freemon, Calif.] can be applied to an uncoated nanofiber using the coating processes of drop coating, ink-jet printing, spray coating, dip coating, or similar methods. When this construct is packaged with a blue emitting LED at 450 to 470 nm and a red-orange emitting LED at 610 nm, white light is produced in this example by blending the emissions of the green phosphor, red-orange LED, and blue LED.
Luminescent compound: Green phosphors such as the doped silicate compositions sold by Intematix [Freemon, Calif.] can be applied to an uncoated nanofiber using the coating processes of drop coating, ink-jet printing, spray coating, dip coating, or similar methods. Added to this composite were red emitting quantum dots using processes such as ink-jet printing, spray coating, dip coating, drop coating, or similar methods. When this construct is packaged with a blue emitting LED at 450 to 470 nm, white light is produced in this example by blending the emissions of the green phosphor, red quantum dot, and blue LED.
Luminescent compound: Red-orange emitting quantum dots of diameter of approximately 5.2 nm (purchased from Evident Technologies,45 Ferry Street Troy, N.Y. 12180) can be applied to an uncoated nanofiber using the coating processes of drop coating, ink-jet printing, spray coating, dip coating, or similar methods. When this construct is packaged with a cool white emitting LED (CCT>4,500 K) radiating at 450 to 750 nm, warm white light (CCT<3,300 K) with improved color rendering index is produced in this example by blending the emissions of the cool white LED and red quantum dots.
Luminescent Devices
In one embodiment of the invention, a polymeric substrate such as an electrospun fiber substrate including luminescent materials is included in an encapsulant such as for example an epoxy matrix.
In other examples, a higher concentration of red emitters than blue emitters may be chosen for other non-white light applications. Thus, the invention permits both monochromatic and color-distinctive luminescent structures to be made by the respective placement of the appropriate luminescent particle in respective areas of the luminescent structure. Prefabricated polymer substrates including nanofiber substrates of respective emission colors (i.e., white, red, blue, green, or a color combination) can be cut and placed in the respective areas, such that a common light source coupled for example through a fiber optic cable would produce different light from the respective areas.
According to another embodiment of the invention, the substrate may be directly placed on the surface of the LED 50 before the encapsulation with epoxy. This placement may reduce energy losses from absorption of some wavelengths (e.g., blue or UV) in the epoxy. Stimulatable particles 4 such as the quantum dots may be concentrated near the LED for a maximum absorbing effect. Further as part of the bonding of the nanofiber substrate to the LED, interstices in the fibers may be filled with a low refractive index polymer, such as silicone, to optimize the scattering effects required to trap the UV light.
Some advantages of the various embodiments of the invention as compared to the traditional technology include: 1) providing a luminescent material with broad spectral emission can be created by incorporating a distribution of particles into the light stimulatable devices of the invention; 2) creating such a structure requires less solvent than the casting or electrophoretic methods currently in use for phosphors; 3) allows emission, transmission, and scattering properties of the luminescent material to be controlled separately through a choice of the particle (i.e., particle density, size, composition, etc.) and nanofiber geometry (i.e., length, diameter, etc.); 4) allows for more efficient operation of the photoluminescent converter due to higher surface area and control of the fiber geometry; and 5) provides a more convenient process to handle and process nanoparticles in finished devices than alternative approaches.
Lighting Devices
A lighting device of the invention includes a reflector (e.g., a mat of reflective fibers as discussed above) and a source of primary radiation. This lighting device can be used by itself as a luminaire (i.e., lighting fixture) or in some cases can be used as a lamp that is contained in a luminaire. The reflector configuration including the mechanism for providing primary radiation and the mechanism for supporting reflective nanofiber sheets provides for efficiently directing the light emanating from the lighting device. The reflective nanofiber material used in this device is configured to provide a structure that takes advantage of the light scatter from the thick nanofiber substrate to provide a high (>0.80) reflectance as described above. The nanofiber substrate can be made from a variety of polymers including but not limited to polyamides, polyacrylates, poly(methyl methacrylate), and poly(butyl methacrylate). The appropriate level of reflection is produced by providing a material containing discontinuities in the dielectric constant produced by either 1) a large macropore structure created by the void volume between adjacent fibers, 2) a macropore structure created by the introduction of pores onto the surface of the nanofiber, and/or 3) the addition of high dielectric constant materials to the nanofiber.
In an additional embodiment, the source of primary radiation impinging upon a reflective nanofiber is provided by a photoluminescent nanofiber made by combining luminescent particles and nanofibers. In this embodiment, there exists a mechanism for excitation illumination, and a mechanism for supporting luminescent sheets (formed from the luminescent particle/fiber composites described above). This lighting device can be used by itself as a luminaire (i.e., lighting fixture) or in some cases can be used as a lamp that is contained in a luminaire. The reflector configuration including the mechanism for exciting illumination and the mechanism for supporting luminescent sheets provides for efficient light conversion and emission from the luminescent particle/polymer composites described above. The reflector configuration of the invention is configured to accommodate the light-conversion material in a structure taking advantage of the light scatter from the nanoparticle/nanofiber composites described above. Light produced by the luminescent sheets strikes the reflective nanofibers and to directed toward the output of the lighting device. The high reflectance of the reflective nanofibers results in a high optical power emanating from the device than would occur in the absence of the reflective nanofiber.
As described above, the luminescent particle/polymer fiber composites include luminescent nanoparticles supported by organic nanofibers. The aspect of the invention permits the luminescent nanoparticles to effectively be suspended in air by the nanofibers. Most light-conversion phosphors in conventional white-light LEDs (light emitting diodes) are held within a solid material having a significant index of refraction, and various strategies are used with these materials to overcome total internal reflection and to extract the light efficiently from the solid material. The luminescent particle/polymer composites, including nanoparticle/nanofiber composites, (hereinafter referred to as “the luminescent sheet”) described above do not suffer from total internal reflection.
In one embodiment of the invention, light conversion is to accept short-wavelength light and to convert the short-wavelength light to longer wavelengths. The combination of an LED producing short-wavelength light (for example, blue light) and an appropriate light-conversion mechanism (for example, one producing yellow light) provides an efficient way of producing white light for general illumination. In one embodiment of the invention, a range of incident (excitation) wavelengths are used which provide excitation (for example, light ranging from blue to ultraviolet). In one embodiment of the invention, the light-conversion mechanism of the particles emits a single color in response to the excitation light. In one embodiment of the invention, the light-conversion mechanism of the particles emits a broad band of wavelengths representing a wide range of colors (for example, from blue to red).
In one embodiment of the invention, the light-conversion material is relatively thick or reflective, so that the excitation light will not pass through the luminescent sheet in a significant amount, but is instead reflected to a high degree. A value of less than 70% transmittance in general would make the light-conversion material an optically thick material. Such an optically thick material is provided by a nanofiber substrate with a thickness in excess of 50 μm. Under this condition, the luminaire in this embodiment of the invention is arranged so that both sides of the luminescent sheet are illuminated by the excitation light, and emitted light is collected from both sides of the luminescent sheet for emanating from the luminaire.
In one embodiment of the invention, illumination from the excitation light source does not directly escape the luminaire. Accordingly, any light escaping the luminaire in this embodiment includes both 1) a component of the excitation light has been scattered from a matrix of the luminescent sheets without a change in wavelength (for example, blue light) and 2) emitted light produced by active luminescent particles (for example light having a longer wavelength than the excitation light such as yellow light).
As shown in
Light sources 110 (e.g., light emitting diodes LEDs or other light sources) produce excitation light 112 which is directed to the luminescent sheets 102. In other embodiments, one or more separate (or integrated) excitation light sources 110 can be provided for each side of the luminescent sheet 102. Luminescent particles in the luminescent sheets 102 upon interaction with the primary light (i.e., excitation light 112) emit secondary light at a wide range of wavelengths, as discussed above in the “Relative Light Emitter Distribution” section. A reflector 120 containing reflective nanofiber made as described above reflects light back toward the luminescent sheet 102. The reflector 120 also reflects some light out of the luminaire 100. Excitation light 112 (for example, blue light) thus impinges on the luminescent sheet(s) 102 from multiple angles and impinges on the luminescent sheet(s) 102 on both sides. Some of the excitation light 112 scatters from the luminescent sheet 102 and exits the luminaire 100 at the bottom of the luminaire either directly or by reflection from the reflector 120. Emitted light 114 (for example, yellow light) created in the luminescent sheet can also exit the luminaire 100 at the bottom of the luminaire and can mix with the scattered excitation light 112.
Accordingly, in one or more embodiments of the invention, luminare 100 includes a source of excitation light (for example, blue LEDs), a luminescent sheet (for example, one that converts blue light to yellow light), and a nanofiber reflector that directs the scattered light. Light can be directed from the excitation sources obliquely toward the luminescent sheet. The angle between the excitation source and the luminescent sheet is set to a value having the greatest efficiency. Efficiency in this context also referring to the ratio of the amount of light produced by the luminaire (integrated over all directions, for example in an integrating sphere) to the power used to operate the luminaire. The luminescent sheet 102 shown in
In an alternative embodiment to that shown in
One example of another luminaire 150 according to the invention is shown in
In an alternative embodiment to that shown in
Light emitted by the primary light source strikes the nanofiber reflector and is directed to the exist of the lighting device by the highly reflective nature of the nanofiber reflector.
More specifically,
In this embodiment, the outline of the top view of structure 300 is a full circle, and the light source 310 is not located at its center. In this configuration, some light is still scattered back toward the light-conversion material 302 and the opposite reflector surface 306. In the perpendicular plane (
A model of reflector 300 is shown in
Remote Phosphor Reflector Block:
A remote phosphor reflector block (RPRB) embodiment of the invention provides another mechanism for incorporating the light conversion materials discussed above.
In the RPRB embodiment, light-conversion material 502 is relatively thick or otherwise substantially diffusely reflective. Such a reflective conversion material does not permit substantial light to be transmitted through light-conversion material 502. Therefore, this material provides a mechanism to separate light of different colors in different compartments. Separation of colors of light is a benefit when mixed light converters are to be used. For example, light emitting structure 500 can include both a green converter layer 550 and a red converter layer 560 which both can interact with blue excitation light. Mixed converters 550, 560 (e.g., green and red) can be arranged to provide a wider color gamut or better color rendering quality than a single converter layer (such as for example a single yellow layer). In this regard, mixed converters can be advantageous. However, with mixed converters, it may happen that blue light is intercepted by a green converter, which emits green light, and the emitted green light can in turn be intercepted by a red converter which emits red light. Multiple conversions like this reduce the efficiency of light production. Efficiency in this context also referring to the ratio of the amount of light produced by the luminaire (integrated over all directions, for example in an integrating sphere) to the power used to operate the luminaire. It should be noted that, for the same power input to the structure 500, multiple conversions of light colors produce less total light than single conversions To address this inefficiency, this embodiment of the invention segregates areas of different color conversion layers into different regions using reflective barriers 570.
As before, for a balance of white light, illumination from the excitation light source should not directly escape the RPRB luminaire structure. Light escaping the luminaire structure should include excitation light scattered from the matrix of the light-conversion material without a change in wavelength (for example, blue light) combined with emitted light produced by the active luminescent particles that has a longer wavelength than the excitation light (for e.g., example, red and green light).
In the RPRB embodiment, a concave reflector made from reflective nanofibers holds an array of converting and reflective layers in a position parallel to the axis of the reflector. The converting layers (e.g., 550 and 560) are located in a position that divides the volume of the reflector into two volumes. The structure 500 includes two light sources (e.g., two LEDs or other light sources) to supply respectively excitation light (in this example, blue light) to the converting layers 550 and 560. The central layer in
More specifically, in the configuration of
By combining blue light from the emission source (i.e., the primary light) and emissions from red to green PLNs (i.e., the secondary light), white light is produced. Such white light can be used as is or optically mixed to eliminate any vestiges of the separate R, G, or B lights by using devices such as an integrating sphere or high transmittance diffuser polymeric film such as those available from Brightview Technologies. Alternatively, the diffuse reflection properties of the reflective nanofiber material serves to optically mix the separate R, G, B light. This is an important advantage of the nanofiber reflector material which optically mixes the separate R, G, B lights to produce white light emanating from the structure.
In the various embodiments described above, the light sources can be LEDs used to excite the PLNs (or color conversion layers) which may emit one primary wavelength or emit different primary wavelengths. For example, one LED could emit at 460 nm and the second could emit at 410 nm.
One advantage of the nanofiber base of the PLNs is that it represents a diffuse Lambertian reflector under certain circumstances. Thus, light incident on a diffuse reflecting nanofiber will not be specularly reflected but rather will be scattered at all angles with a cosine θ dependence with respect to the surface normal (i.e., following Lambert's emission law).
An alternative to having separate green and red PLNs, each pumped by a blue light, is to have a green PLN excited by a blue LED and in the second compartment have a red LED impinging on an undoped nanofiber substrate. This design could still be configured to emit blue, green and red light in the proper proportionality to generate white light, and the reflective layer may not be required. This approach represents a solution to the so-called “green gap” of low performing LEDs. Alternatively, green or red phosphors could be used in place of quantum dots. Alternatively, blue and red LEDs could be aimed at a green PLN to produce white light. Multiple blue or red LEDs can be added to the reflector block to impart greater control over the light produced.
In addition to the embodiments listed above, there are several additional embodiments of this invention. These embodiments include:
Presently, the RPRB embodiment has yielded the following color rendering indexes (CRI) and correlated color temperatures (CCT). By comparison, measured values for commercial white LEDs have a range of CCT values depending upon the color of the lamp. “Cool white” lamps have CCTS between 5,000 K and 10,000K, “neutral white” lamps have CCTs between 3,700 K and 5,000 K, and “warm white” lamps have CCTs between 2,600 K and 3,700 K. The typical CRI of these lamps is approximately 83. Higher CCTs correspond to a bluish appearance of the light source whereas lower CCTs correspond to a more reddish appearance. CRI refers to the ability to reproduce colors accurately and values above 80 are acceptable for general illumination.
Working Examples:
Numerous modifications and variations of the invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.
This application is related to and claims priority from U.S. Application Ser. No. 61/266,323 filed Dec. 3, 2009, the entire contents of which are incorporated herein by reference. This application is related to U.S. application Ser. No. 10/819,916, filed on Apr. 8, 2004, entitled “Electrospinning of Polymer Nanofibers Using a Rotating Spray Head,” Attorney Docket No. 241015US-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is also related to U.S. application Ser. No. 10/819,942, filed on Apr. 8, 2004, entitled “Electrospray/electrospinning Apparatus and Method,” Attorney Docket No. 241013US-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to U.S. application Ser. No. 10/819,945, filed Apr. 8, 2004, entitled “Electrospinning in a Controlled Gaseous Environment,” Attorney Docket No. 245016US-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to U.S. Ser. No. 11/130,269, filed May 17, 2005 entitled “Nanofiber Mats and Production Methods Thereof,” Attorney Docket No.256964US-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to U.S. application Ser. No. 11/559,260, filed on Nov. 13, 2006, entitled “LUMINESCENT DEVICE,” Attorney Docket No. 289033US20 -2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to U.S. Ser. No. 60/929,077, filed Jun. 12, 2007 entitled “Long-Pass Optical Filter Made from Nanofibers,” Attorney Docket No. 310469US-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to PCT/US2008/066620, filed Jun. 12, 2008 entitled “Long-Pass Optical Filter Made from Nanofibers ,” Attorney Docket No. 310469WO-2025-2025-20, the entire contents of which are incorporated herein by reference. This application is related to PCT/US2009/043784, filed May 13, 2008 entitled “POROUS AND NON-POROUS NANOSTRUCTURES AND APPLICATION THEREOF,” Attorney Docket No. 326008WO. This application is related to U.S. Application Ser. No. 61/169,468, filed on Apr. 15, 2009, entitled “STIMULATED LIGHTING DEVICE,” Attorney Docket No. 340555US20 -2025-2025-20, the entire contents of which are incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US10/57007 | 11/17/2010 | WO | 00 | 7/23/2012 |