Reflective or Semi-Reflective Metal Alloy Coatings

Abstract
A silver-based alloy composition for use as a reflective or semi-reflective coatings or layer(s) for use in optical data storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors, or other reflective or semi-reflective applications. The alloy composition comprises silver with copper and/or zinc and silicon and/or tin.
Description
BACKGROUND OF THE INVENTION

1. Field of the Invention (Technical Field)


The present invention relates to silver-based alloy compositions for use as reflective or semi-reflective layers or coatings for use in optical data storage media, low emissivity glass, transparent conductive displays, electro-chromic mirrors, or other reflective or semi-reflective applications.


2. Background Art


Note that the following discussion refers to a number of publications by author(s) and year of publication, and that due to recent publication dates certain publications are not to be considered as prior art vis-à-vis the present invention. Discussion of such publications herein is given for more complete background and is not to be construed as an admission that such publications are prior art for patentability determination purposes. Each of the publications is incorporated herein by reference.


There are several specialty applications in the industry that require reflective or semi-reflective coatings or layers. These include optical storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors. The present invention provides useful alloy coating compositions for such applications.


Optical discs are commonly used for recording data, video, audio, etc. The discs are usually constructed in four layers (conventional, prerecorded, optical discs). The first layer is typically constructed from optical grade, polycarbonate resin, and manufactured by techniques well-known in the art, usually by injection or compression molding the resin into a disc. The surface of such a disc is molded or stamped with precisely located pits and lands having a predetermined size which store information on the disc.


After stamping (or molding), an optically reflective layer is disposed on the information pits and lands, which is usually between about 40 to about 100 nanometers (nm) thick. Deposition techniques such as sputtering or thermal evaporation are well-known in the art. Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd ed. Vol. 10, pp. 247 to 283, gives a detailed explanation of deposition techniques such as sputtering, thermal evaporation, flow discharge, ion plating, and chemical vapor deposition.


Next, a solvent-based or a UV (ultraviolet) curing-type resin is applied over the reflective layer. This third layer protects the reflective layer from handling and the ambient environment. An optional label identifies the particular information that is stored on the disc, and sometimes, may include artwork.


The information pits, found between the polycarbonate resin and the reflective layer usually form a continuous spiral. The spiral typically begins at an inside radius and ends at an outside radius. The distance between any 2 spirals is called the “track pitch” and is usually about 1.6 microns. The length of a pit or land is from about 0.9 to about 3.3 microns. (All of these specifications were first proposed by Philips NV of Holland and Sony of Japan as standards for the industry.)


Reading of the disc is accomplished by pointing a laser beam through the optical grade polycarbonate and onto the reflective layer with sufficiently small resolution to focus on the information pits. The pits have a depth of about ¼ of the wavelength of the laser light, which has a wavelength in the range of about 780 to 820 nanometers. Destructive (dark) or constructive (bright) interference of the laser light is then produced as the laser travels along the spiral track, focusing on an alternating stream of pits and lands in its path.


This change of light intensity from dark to bright or from bright to dark forms the basis of a digital data stream of one's and zeros. When there is no light intensity change in a fixed time interval, the digital signal is “0,” and when there is a light intensity change from either dark to bright or bright to dark, the digital signal is “1.” The continuous stream of ones and zeros is then electronically decoded into a meaningful format, such as music.


As a result, it is important to have a highly reflective coating on the disc to reflect the laser light from the disc and onto a detector in order to read the presence of an intensity change. Typically, a reflective layer is copper, silver, aluminum, or gold, all of which have a high optical reflectivity of generally more than 80 percent. Aluminum and aluminum alloys are most commonly used given their easy placement onto a polycarbonate disc, lower cost, and corrosion resistance.


Organic dye is the key to a CD-R disc. The dye is made from solvent and organic compounds from the cyanine, phthalocyanine or azo family. It is normally applied by spin coating onto the disc. A reflective layer is then applied over the dye. Because the dye may contain halogen ions or other chemicals that can corrode the reflective layer, many commonly used reflective layer materials (e.g., aluminum) may not be suitable for use on a CD-R disc. As a result, gold is often used as the reflective layer; however it is a very expensive solution.


Another type of optical disc is a prerecorded digital video disc, “DVD.” This disc is comprised of two halves, each made of polycarbonate resin and coated with a reflective layer, as described above. The halves are then bonded with a UV curing resin or a hot melt adhesive to form the whole disc. The disc can then be played from both sides. The size of a DVD is about the same as a CD, but the information density is higher, having a track pitch of about 0.7 micron with the length of the pits and lands from approximately 0.3 to 1.4 microns.


One variation of the DVD family of discs is the DVD-dual layer disc which has two information layers. On this disc, the highly reflectivity layer is usually the same as others, but a second layer is only semi-reflective with a reflectivity in the range of approximately 18 to 30 percent. This second layer must also allow a substantial amount of light to pass through, so that the laser beam can reach the highly reflective layer underneath and then reflect back through the semi-reflective layer to the signal detector.


Details regarding the manufacture and construction of DVD discs can be found in U.S. Pat. No. 5,640,382, entitled “Dual Layer Optical Medium Having Partially Reflecting Metal Alloy Layer,” to Florezak et al., issued Jun. 17, 1997.


Additional manufacturing and operating details of an optically readable storage system can be found in U.S. Pat. Nos. 4,998,239, entitled “Optical Information Recording Medium Containing a Metal Allow as a Reflective Material,” to Strandjord et al., issued Mar. 5, 1991 and U.S. Pat. No. 4,709,363, entitled “Optically Readable Information Disc Having a Reflection layer Formed From a Metal Alloy,” to Dirks et al., issued Nov. 24, 1987.


Another disc in the compact disc family that has become popular is the recordable compact disc or “CD-R.” This disc is similar to the CD described earlier, with a few minor changes. The recordable compact disc begins with a continuous spiral groove instead of a continuous spiral of pits and has a layer of organic dye between the polycarbonate substrate and the reflective layer. The disc is recorded by periodically focusing a laser beam into the grooves as the laser travels along the spiral track. The laser heats the dye to a high temperature, which in turn places pits in the groove that coincide with an input data stream of ones and zeros by periodically deforming and decomposing the dye. Additional details can be found in U.S. Pat. No. 5,325,351, entitled “Optical Recording Medium Having a Reflective Layer Made of Cu-Ag or Cu-Au Alloy,” to Uchiyama et al., issued Jun. 28, 1994; U.S. Pat. No. 5,391,462 issued Feb. 21,1995, U.S. Pat. No. 5,414,914 issued May 16,1995 and U.S. Pat. No. 5,419,939 issued May 39, 1995, entitled “Optical Recording Disk,” to Arioka et al.; and U.S. Pat. No. 5,620,767, entitled “Light Reflecting and Heat Dissipating Material and Optical Information Recording Medium Using the Same,” to Harigaya et al., issued Apr. 15, 1997.


The typical choice of a semi-reflective layer is gold or silicon in the thickness range of 5 to 70 nanometers, as discussed in U.S. Pat. No. 5,171,392, to Lida et al. Gold, when sufficiently thin, will both reflect and transmit light, has outstanding corrosion resistance, is relatively easy to sputter into a coating of uniform thickness, and is more expensive than other metals. Silicon is a reasonable alternative to gold, but because it is a semiconductor, its sputtering yield and sputtering rate is significantly lower than gold. Silicon also has a tendency to react with oxygen and nitrogen during sputtering. Nevertheless, silicon is useful as an optional component in the alloy of the present invention.


Generally, for aesthetic reasons, a gold or copper based alloy is used to offer the consumer a “gold” colored disc. Although gold naturally offers this rich color and satisfies all the functional requirements of a highly reflective layer, it is more expensive than aluminum. Examples of patents disclosing such gold alloys are: U.S. Pat. No. 5,093,174, entitled “Optical Recording Medium,” to Suzuki et al., issued Mar. 3, 1992, which discloses a metal reflecting layer of an aluminum or silver alloy containing gold for optical recording media; U.S. Pat. No. 6,292,457 B1, entitled “Recordable Optical Media With A Silver-Gold Reflective Layer,” to Preuss et al., issued Sep. 18, 2001, which discloses an optical recording media having a transparent substrate and a reflective layer containing gold; U.S. Pat. No. 6,007,889, issued Dec. 28, 1998; U.S. Pat. No. 6,280,881, issued Aug. 28, 2001; U.S. Pat. No. 6,541,402, issued Sep. 17, 2002; and U.S. Pat. No. 6,544,616 issued Apr. 8, 2003; and U.S. Patent Application Nos. US2002/0034603 filed Apr. 13, 2001 and US2002/0122913 filed Sep. 5, 2002, entitled “Metal Alloys for the Reflective or Semi-Reflective Layer of An Optical Storage Medium,” to Nee, which disclose a silver-based or copper-based alloy thin film for a coating layer for optical discs. The Nee additions to the silver alloy are gold, palladium, copper, rhodium, ruthenium, osmium, iridium, platinum, zinc, aluminum, zinc plus aluminum, manganese, and germanium. The Nee additions to the copper alloy are manganese, silver, cadmium, gold, magnesium, aluminum, beryllium, zirconium and nickel. These patents and applications do not disclose the alloy coatings of the present invention.


Other expensive materials, such as palladium have also been used in the art to produce optical storage media, such as disclosed in: U.S. Pat. No. 6,228,457 B1, entitled “Optical Data Storage Medium,” to Ueno et al., issued May 8, 2001, which discloses an optical data storage medium with a silver-palladium-copper alloy or silver-palladium-titanium alloy; and U.S. Pat. No. 6,242,068, entitled “Recordable Optical Media with a Silver-Palladium Reflective Layer,” to Preuss, issued Jun. 3, 2001, which discloses a reflective layer made of silver and palladium. The patents do not disclose the alloy coatings of the present invention.


A copper-based alloy that contains aluminum, zinc or tin is sometimes used to produce a “gold” looking layer. However, alloys of copper corrode more easily than aluminum.


U.S. Pat. No. 6,351,446, issued Feb. 26, 2003 and U.S. Patent Application No. US2002/0054973, filed Nov. 26, 2001, entitled “Optical Data Storage Disk,” to Weinzerl, disclose an optical data storage disk with at least two interfaces. The inner layer is the reflection layer and the other layer is a partially reflecting/partially transmitting layer. The inner layer is made of one type of alloy and the other layer is made of another alloy. The Weinzerl patent and application do not disclose the alloy coatings of the present invention.


Several silver-based alloys have been developed to improve tarnish resistance in multi-layer stacks. Although silver-based alloys are commonly used in the casting industry (e.g. for jewelry making), they have not heretofore been utilized as reflective or semi-reflective coatings for specialty applications, such as optical storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors. As indicated above, these silver-based alloys have typically included gold or palladium, very expensive components. These alloys traditionally have had 80% to 95% silver and employed gold or platinum group metals as alloying elements to stabilize the properties of the silver when exposed to moisture or mildly acidic environments.


The present invention is a new, lower cost alloy coating, specifically useful for optical storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors that represents a favorable balance between cost and performance. The preferred alloy of the present invention is more complex than the standard binary or ternary alloys presently known in the art, however, it can be produced using readily available production equipment.


BRIEF SUMMARY OF THE INVENTION

The present invention relates to a reflective (including highly reflective) or semi-reflective coating for optical storage media, low emissivity glass, transparent conductive displays, electro-chromic mirrors, and other reflective or semi-reflective coating applications. The preferred alloy coating comprises silver, copper and/or zinc and may have silicon and/or tin, or any combination thereof.


The preferred alloy coating is made of between approximately 45% by weight and approximately 99.9% by weight of silver, between approximately 0.01% by weight and approximately 55% by weight copper, between approximately 0.01% by weight and approximately 55% by weight zinc, between approximately 0.01% by weight and approximately 30% by weight tin, and between approximately 0.01% by weight and approximately 30% by weight silicon. More preferably, the alloy coating comprises between approximately 55% by weight and approximately 95% by weight silver, between approximately 0.01% by weight and approximately 10% by weight copper, between approximately 0.01% by weight and approximately 10% by weight zinc, between approximately 0.01% by weight and approximately 10% by weight tin, and between approximately 0.01% by weight and approximately 10% by weight silicon. Most preferably, the composition of the alloy coating comprises between approximately 90% by weight and approximately 95% by weight silver, between approximately 0.25% by weight and approximately 5% by weight copper, between approximately 0.25% by weight and approximately 5% by weight zinc, between approximately 0.01% by weight and approximately 2% by weight tin, and between approximately 0.01% by weight and approximately 1% by weight silicon.


The present invention also relates to a method for physical deposition of the reflective or semi-reflective alloy coating, onto a substrate. This method comprises providing a coating alloy comprising silver, zinc and copper and/or silicon and/or tin; and physically depositing the coating on the substrate. The method of physically depositing utilizes at least one known deposition technique including, but not limited to, sputtering, thermal evaporation, physical vapor deposition, electrolytic plating, and electroless plating.


A primary object of the present invention is to provide a silver-based alloy that is readily available in the purities required and provides technical benefits in passivation or inertness to the operating environment.


A primary advantage of the present invention is improved performance, lower cost, ease in manufacturing, and increased flexibility in application of reflective and semi-reflective coatings for specialty applications, such as optical storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors.


Another advantage is that the alloy coatings of the present invention is suitable for both fully reflective and semi-transparent layers.


Other objects, advantages and novel features, and further scope of applicability of the present invention will be set forth in part in the detailed description to follow, and in part will become apparent to those skilled in the art upon examination of the following, or may be learned by practice of the invention. The objects and advantages of the invention may be realized and attained by means of the instrumentalities and combinations particularly pointed out in the appended claims.







DESCRIPTION OF THE PREFERRED EMBODIMENTS
Best Modes for Carrying Out the INVENTION)

The present invention comprises a silver-based alloy thin film or coating for use in a reflective, highly reflective, or semi-reflective application, including optical storage media, low emissivity glass, transparent conductive displays, and electro-chromic mirrors (e.g. architectural glass, automotive glass, mirrors, display, electrochromics, and the like). The alloy coating of the present invention preferably additionally comprises silicon and/or tin, and further preferably comprises copper and/or zinc. The silver-based alloys of the invention have moderate to high reflectivity properties and are reasonably corrosion-resistant in a typical ambient environment. The term “reflective,” as used throughout the specification and claims, is intended to include both reflective and highly reflective properties. The coatings may be a single layer or multiple layers.


In a preferred embodiment of the present invention, silver is alloyed with zinc or copper, and may have tin and/or silicon in any and all combinations. The alloy coating preferably comprises between approximately 45% by weight and approximately 99.9% by weight silver, between approximately 0.01% by weight and approximately 55.0% by weight copper, between approximately 0.01% by weight and approximately 55.0% by weight zinc, between approximately 0.01% by weight and approximately 30.0% by weight tin, and between approximately 0.01% by weight and approximately 30.0% by weight silicon. More preferably, the alloy comprises between 55% by weight and approximately 95% by weight silver, between approximately 0.01% by weight and approximately 10.0% by weight copper, between approximately 0.01% by weight and approximately 10.0% by weight zinc, between approximately 0.01% by weight and approximately 10.0% by weight tin, and between approximately 0.01% by weight and approximately 10.0% by weight silicon. Most preferably, however, the alloy comprises between approximately 90% by weight and approximately 95% by weight silver, between approximately 0.25% by weight and approximately 5% by weight copper, between approximately 0.25% by weight and approximately 5% by weight zinc, between approximately 0.01% by weight and approximately 1% by weight silicon, and between approximately 0.01% by weight and approximately 2% by weight tin.


The above-described embodiments may be further modified by adding any other suitable material(s) having an intrinsic reflectivity of approximately greater than 80 percent.


Having presented the preceding compositions for the starting materials, it is important to recognize that both the manufacturing process of the sputtering target and the process to deposit the target into a thin film play important roles in determining the final properties of the film.


The alloy of the present invention can be produced using traditional casting/rolling and annealing techniques using current equipment.


The following is a description of the manufacture of optical discs or targets upon which the alloy coatings of the present invention are disposed. In general, vacuum melting and casting of the substrate or target material or alloys or melting and casting under protective atmosphere, are preferred to minimize the introduction of other unwanted impurities.


Afterwards, the as-cast ingot should undergo a cold working process to break down the segregation and the nonuniform as-cast microstructure. One preferred method is cold forging or cold uniaxial compression with more than 50 percent of size reduction, followed by annealing to recrystallize the deformed material into fine equi-axed grain structure with a preferred texture of <1, 1, 0> orientation. This texture promotes directional sputtering in a sputtering apparatus so that more of the atoms from the sputtering target are deposited onto the disc substrates for more efficient use of the target material.


Alternatively, a cold multi-directional rolling process of more than 50 percent size reduction can be employed, followed by annealing to promote a random oriented microstructure in the target and finally by machining to the final shape and size suitable for a given sputtering apparatus. This target with random crystal orientation leads to a more random ejection of atoms from the target during sputtering and a more uniform thickness distribution in the disc substrate.


Depending on different discs' optical and other system requirements, either a cold forging or a cold multi-directional rolling process can be employed in the target manufacturing process to optimize the optical and other performance requirements of the thin film for a given application.


Sputtering, thermal evaporation or physical vapor deposition, and possibly electrolytic or electroless plating processes are useful in accordance with the present invention. Depending on the method of application, the alloy thin film's reflectivity can vary. Any application method that adds impurities to or changes the surface morphology of the thin film layer on the disc can lower the reflectivity of the layer. The reflectivity of the thin film layer on the optical disc is primarily determined by the starting material of the sputtering target, evaporation source material, or the purity and composition of the electrolytic and electroless plating chemicals.


The reflective layer of the coating of the present invention can also be used for optical discs that use a reading laser of a shorter wavelength, for example, when the reading laser's wavelength is shorter than 650 nanometers.


If the reflective film is reduced to a thickness of approximately 5 to 20 nanometers, a semi-reflective film layer can be formed from the alloy coatings of the present invention that have sufficient light transmittance for use in DVD dual-layer applications.


The alloy coatings of the present invention are particularly useful as a semi-transparent layer. The reflectivity approaches gold in the infrared spectrum making the alloy of the present invention suitable for replacement as gold (but at a lower cost), as a replacement for silver alloys (but with improved corrosion resistance), and as a replacement for indium tin oxide (due to improved sputter rate). In the visible spectrum, the alloy of the present invention is useful as a replacement for gold and higher cost silver alloys (due to a lower cost). The chemical stability, and high reflectivity are comparable, and cost effectiveness is superior to prior art alloys that utilize higher cost materials and/or processes (e.g. use of an additional “overcoat” layer to protect the silver).


The preferred alloy coating of the present invention has a uniform fine grain, preferably <50 microns.


INDUSTRIAL APPLICABILITY

The invention is further illustrated by the following non-limiting examples.


EXAMPLE 1

An alloy coating for an optical disc media was made having the composition: 92.70% silver, 4.50% copper, 2.15% zinc, 0.50% tin, and 0.15% silicon. This alloy coating was found to have superior reflective and semi-reflective qualities over other alloys, at a lower cost.


EXAMPLE 2

The above described alloy coating was compared in sputter tests, reflectance, and resistivity against existing alloys.


Optical Properties—Reflectivity


The principle application of the alloy of the present invention is useful as a replacement for silver and/or gold and their alloys in visible or infrared reflecting thin films. Therefore the focus was to compare the reflectivity against these materials. Table 1 shows the reflectivity properties of the alloys tested against both silver and gold standards. The sputtering tests were carried out on standard quartz medical slides and on web plastic. The coatings were made in a 27″ wide web coater using a 10 kW power supply. The slides were placed upon the cooling drum and sputtered in a static position. Reflectivity in the ultraviolet, visible and near infrared ranges was measured with a spectrophotometer. Far infrared testing was conducted using a infrared spectrophotometer. All measurements made were in reference to aluminum standards.

TABLE 1Comparison of ReflectivityPercent - Comparedto AluminumAlloy of the99.95%99.95%Wavelength (nm)Present InventionPure AgPure Au85%Ag—15%Au93%Ag—7%Pd3049.9410424048010542969350497108641041016041021101021071067041071121091101118041141171161151179041071101101061081004103106104102104110410210410310110312041011031021001021304101103102100102140410110210199102150410010210199102160410010210199102170410010210199101180410010210199101190410010110199101200410010110199101210410010110199101219410010110199101


Optical Properties—Absorptance & Emittance


Each of the sputtered films were evaluated for absorptance and emittance properties for comparison versus pure silver and pure gold. Pure silver and pure gold are employed in architectural, aerospace and automotive glass applications, so these properties were of interest. The tests were conducted using standard ASTM tests on unprotected films in the as-sputtered and after environmental testing. The results are shown in Tables 2 and 3. The following standards were used:

Solar absorptance measurements:E903Emittance measurements:E408Environmental aging tests:D1735Adhesion tests:D3359









TABLE 2










Absorptance, Emittance & Adhesion












Metal/Alloy
Solar





(weight %)
Absorptance
Emittance
Adhesion







Alloy of the
.10
.04
Good very



Present


slight



Invention


removal



85%Ag—15%Au
.07
.04
Good



93%Ag—7%Pd
.06
.05
Good



Pure Au
.19
.06
Good



99.95%



Pure Ag
.03
.03
OK



99.95%

















TABLE 3










Absorptance, Emittance & Adhesion After Aging












Metal/Alloy
Solar





(weight %)
Absorptance
Emittance
Adhesion







Alloy of the
.11
.05
Good very



Present


slight



Invention


removal



85%Ag—15%Au
.06
.04
Good



93%Ag—7%Pd
.09
.05
Good



Pure Au
.20
.06
Good



99.95%



Pure Ag
.05
.03
OK



99.95%











Electrical Properties


Sputter Rate and Sheet Resistance


Silver alloys are employed in transparent conductive films due to their excellent conductivity. Typically the silver layers are part of an oxide-metal-oxide film stack to optimize the optical properties and isolate the metal film. Table 4 provides the sheet resistance values for each of alloys tested and compared to gold and silver standards. The targets were sputtered with a 4 kW power supply that provided an average power density of 44 W/in2. All materials were sputtered in an argon atmosphere with a flow rate of 250 sccm at a sputtering pressure of 1.0×10−3 torr. Note that the films were thick; on the order of 1500 Å. This was done to provide good average sputter rates and also to eliminate substrate effect for sheet resistance measurements. A thicker coating would also provide more interfacial stress in the film and make the adhesion test more relevant.

TABLE 4Sputter Rate and Sheet ResistanceNominalSputterSheetMetal/AlloyThicknessRateResistance(weight %)(Å)(Å/sec.)(Ω/□)Alloy of the1425194.55PresentInvention85%Ag—15%Au1454215.6093%Ag—7%Pd1533233.45Pure Au1584174.6099.95%Pure Ag1344232.3299.95%


The results show that the alloy coating of the present invention replaces more expensive or less corrosion resistant materials in some applications. The properties for the alloy of the present invention in several key areas of interest to the thin film engineer show good concurrence with the ranges of the more expensive materials.


The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.


Although the invention has been described in detail with particular reference to these preferred embodiments, other embodiments can achieve the same results. Variations and modifications of the present invention will be obvious to those skilled in the art and it is intended to cover all such modifications and equivalents. The entire disclosures of all references, applications, patents, and publications cited above, and of the corresponding application(s), are hereby incorporated by reference.

Claims
  • 1. An optical storage medium having a reflective or semi-reflective coating, said coating comprising an alloy, said alloy comprising: (a) silver in an amount of between approximately 45% by weight and approximately 99.9% by weight; (b) copper in an amount of between approximately 0.01% by weight and approximately 55% by weight; (c) zinc in an amount of between approximately 0.01% by weight and approximately 55% by weight, and (d) tin in an amount of between approximately 0.01% by weight and approximately 30% by weight; and wherein said copper is present in said alloy in an amount greater than about 5.0 atomic percent.
  • 2. The optical storage medium of claim 1, wherein said amount of said copper is between approximately 0.01% by weight and approximately 10% by weight.
  • 3. The optical storage medium of claim 1, wherein said amount of said copper is between approximately 0.25% by weight and approximately 5% by weight.
  • 4. An optical storage medium having a reflective or semi-reflective coating, said coating comprising an alloy, said alloy comprising: (a) silver in an amount of between approximately 45% by weight and approximately 99.9% by weight; (b) copper in an amount of between approximately 0.01% by weight and approximately 55% by weight; (c) zinc in an amount of between approximately 0.01% by weight and approximately 55% by weight, and (d) silicon in an amount of between approximately 0.01% by weight and approximately 30% by weight; and wherein said copper is present in said alloy in an amount greater than about 5.0 atomic percent.
  • 5. The optical storage medium of claim 4, wherein said amount of said copper is between approximately 0.01% by weight and approximately 10% by weight.
  • 6. The optical storage medium of claim 4, wherein said amount of said copper is between approximately 0.25% by weight and approximately 5% by weight.
  • 7. An optical storage medium having a reflective or semi-reflective coating, said coating comprising an alloy, said alloy comprising: (a) silver in an amount of between approximately 45% by weight and approximately 99.9% by weight; (b) copper in an amount of between approximately 0.01% by weight and approximately 55% by weight; and (c) at least one metal selected from the group consisting of silicon and tin in an amount of between approximately 0.01% by weight and 30% by weight; and wherein said copper is present in said alloy in an amount greater than about 5.0 atomic percent.
  • 8. The optical storage medium of claim 7, wherein said amount of said copper is between approximately 0.01% by weight and approximately 10% by weight.
  • 9. The optical storage medium of claim 7, wherein said amount of said copper is between approximately 0.25% by weight and approximately 5% by weight.
Parent Case Info

This application is a divisional application of U.S. patent application Ser. No. 10/616,478, entitled “Reflective or Semi-Reflective Metal Alloy Coatings”, filed on Jul. 8, 2003, which application claims the benefit of the filing of U.S. Provisional Patent Application Ser. No. 60/394,587, entitled “Metal Alloys with Reflective or Semi-Reflective Layers”, filed on Jul. 8, 2002, and the specifications and claims thereof are incorporated herein by reference.

Provisional Applications (1)
Number Date Country
60394587 Jul 2002 US
Divisions (1)
Number Date Country
Parent 10616478 Jul 2003 US
Child 11620025 Jan 2007 US