The present invention relates in general to photovoltaic modules and in particular to colorized photovoltaic modules having miniaturized photovoltaic cells.
Traditional photovoltaic cells have been coated with antireflection coatings to minimize the reflectance of light incident on a cell surface. Accordingly, antireflection coatings are typically applied with an optical thickness to maximize absorption and conversion efficiency. As a result, traditional photovoltaic cells appear black or dark blue, due to the nearly complete absorption of incident light by the cells.
In an embodiment of the present invention, a photovoltaic module includes reflective photovoltaic cells that act as pixels. The reflective photovoltaic cells are arranged wherein reflections from the photovoltaic cells or pixels visually combine into an image on the photovoltaic module. Each photovoltaic cell or pixel is composed of a set of 100 to 256 base color sub-pixel reflective segments or sub-pixels. The color of each pixel is determined by the combination of base color sub-pixels forming the pixel. As a result, each pixel can have a wide variety of colors using a set of base colors, which are created, from sub-pixel segments having standard film thicknesses.
In yet another embodiment of the present invention, a photovoltaic module includes colorized reflective photovoltaic cells that act as pixels and photovoltaic cells that act as background. The reflective photovoltaic cells are arranged wherein reflections from the photovoltaic cells or pixels visually combine into an image on the photovoltaic module. Colorized photovoltaic cells or pixels are composed of a set of 100 to 256 base color sub-pixel reflective segments or sub-pixels. The color of each pixel is determined by the combination of base color sub-pixels forming the pixel. As a result, each pixel can have a wide variety of colors using a set of base colors, which are created, from sub-pixel cells having standard film thicknesses. The background cells may be approximately the same size as the pixel cells and may or may not be colorized.
In still another embodiment the present invention provides a method of arranging photovoltaic cells to visually combine reflections into an image on a photovoltaic module. A first colorized photovoltaic cell is arranged to visually combine reflections into a first predetermined color using colored reflective segments, and a second colorized photovoltaic cell is arranged to visually combine reflections into a second predetermined color using colored reflective segments.
In another embodiment of the present invention, a photovoltaic module includes adjacent electricity generating devices, and at least one film layer covering the electricity generating devices. The film layer has reflective pixel segments and the reflective pixel segments have colored sub-pixel reflective segments. The colored sub-pixel reflective segments provide sub-pixel reflections that visually combine into a first predetermined color and the reflective pixel segments provide pixel reflections that visually combine into an image.
A photovoltaic cell having a device layer with a cell surface and a film with a film surface over the cell surface is described. The film may be configured to reflect a predetermined wavelength of visible light from the film surface and the cell surface in a direction away from the device layer. The film may include an optical thickness such that rays of the visible light reflected from the film surface and from the cell surface interfere constructively. Furthermore, the optical thickness of the film may vary such that the optical thickness at a first location of the film differs from a second optical thickness at a second location of the film. As a result, rays of a second predetermined wavelength of the visible light may reflect from the film surface and from the cell surface, and interfere constructively at the second location.
A photovoltaic module having a first set of photovoltaic cells and a second set of photovoltaic cells is also described. Each photovoltaic cell in the first set may include a first cell surface under a first film and each photovoltaic cell in the second set may include a second cell surface under a second film. Furthermore, the second film may differ from the first film such that the first set of photovoltaic cells and the second set of photovoltaic cells respectively reflect a first wavelength and a different second wavelength of visible light in a direction away from the photovoltaic module. For example, the first wavelength and the second wavelength may differ by at least 10 nm. The first set of photovoltaic cells may be horizontally spaced apart from the second set of photovoltaic cells on a plane of the photovoltaic module, forming an array of cells over the plane. Alternatively, the first set of photovoltaic cells may be stacked above the second set of photovoltaic cells out of a plane of the photovoltaic module, forming one or more multi-junction cells.
The photovoltaic module includes a receiving substrate with a support surface that supports the first set of photovoltaic cells and the second set of photovoltaic cells. Respective reflections from the first set of photovoltaic cells and the second set of photovoltaic cells may be visually combined into an image on the photovoltaic module. For example, the image may be a camouflage pattern on the photovoltaic module. Furthermore, the receiving substrate may be configured to flex.
The invention may best be understood by referring to the following description and accompanying drawings that are used to illustrate embodiments of the invention. In the drawings:
Receiving substrate 104 may include a conductive material and/or may include a substantially flexible polymer. For example, receiving substrate 104 may have the structure and characteristics of a flexible circuit. That is, receiving substrate 104 may include a conductive circuit pattern affixed, coated with, and/or encapsulated within a flexible insulating polymer film. Accordingly, conductive circuitry of receiving substrate 104 may be electrically connected with one or more of photovoltaic cells 102. Alternatively, receiving substrate 104 may include a rigid material to stiffen photovoltaic module 100. Thus, receiving substrate 104 material may be selected according to the intended application of photovoltaic module 100.
Photovoltaic cells 102 may be electrically connected with the circuitry of receiving substrate 104 in numerous manners. For example, the underside of photovoltaic cells 102 may have conductive contacts such as solder bumps, conductive epoxy, or electroplated bumps comprising metal materials such as metal alloy, titanium or indium. The photovoltaic cells' conductive contacts may be bonded with electrical contacts of receiving substrate 104 circuitry using known techniques such as soldering.
Optionally, photovoltaic module 100 may further include a base substrate 106 structurally connected with receiving substrate 104. Base substrate 106 may be a flexible or rigid sheet of material, depending on the application. For example, base substrate 106 may be a thin sheet of polymer, elastomer, fabric, or any other material that is flexible and/or resilient. Alternatively, base substrate may be a structure formed from glass, metal, or any other material that is rigid and/or stiff. Base substrate 106 may provide structure to photovoltaic module 100 that compensates or complements the structure of receiving substrate 104. Thus, base substrate 106 may be sufficiently stiff to allow receiving substrate 104 to be formed solely from electrical wiring and/or elastic tape, yet still achieve acceptable overall structural integrity for the desired application. As an example, base substrate 106 may be rip-stop forming a wall of a tent, a jib of a sailboat or a poster panel for a billboard.
In the case of base substrate 106 being flexible, photovoltaic cells 102 may have a thickness of, for example, less than about 50 μm and preferably from about 5 μm to about 10 μm. As such, an overall thickness of photovoltaic module 100 remains small, for example, less than about 0.5 mm. More particularly, photovoltaic module 100 may have an overall thickness in a range of about 0.2 mm to about 0.4 mm. In addition, each of photovoltaic cells 102 may have profile dimensions of, for example, up to about 5 mm. More particularly, a lateral dimension of photovoltaic cell 102 may be about 1 mm or less. Smaller photovoltaic cell thicknesses and lateral dimensions, result in a smaller photovoltaic module bending radius.
In addition to its size, photovoltaic cell 102 may also include a shape that contributes to the overall flexibility of photovoltaic module 100. For example, photovoltaic cell 102 may include a polygonal shape (e.g. hexagonal or square) that allows for photovoltaic cells 102 to be tightly packed while maintaining spacing between them. This spacing may accommodate bending of photovoltaic module 100 in a variety of directions. For example, photovoltaic cells 102 may be arranged within photovoltaic module 100 in a side by side honeycomb like pattern such that each of the side walls of photovoltaic cells 102 may be juxtaposed with a sidewall of an adjacent photovoltaic cell as illustrated in
Although a flexible photovoltaic module 100 is described, photovoltaic module 100 may be a substantially rigid structure. For example, where photovoltaic cells 102 are attached to a rigid receiving substrate 104 or base substrate 106, photovoltaic module 100 may form a rigid module structure. Furthermore, additional stiffening structures such as ribbing or epoxy films may be used to further stiffen an originally flexible photovoltaic module.
Referring to
Referring to
In the example of
Film 204 may be applied over a cell surface 310 of device layer 202. More specifically, film 204 may be applied over an entire cell surface 310 and side wall 311 of device layer 202, or alternatively, film 204 may be applied over only a portion of cell surface 310. Film 204 may be formed over cell surface 310 using deposition techniques. For example, film 204 may be deposited by sputtering, atomic layer deposition, electron beam evaporation or chemical vapor deposition. Film 204 is deposited over cell surface 310 to a film thickness 312. Film thickness 312 may be defined by a distance between cell surface 310 and a film surface 314. Film thickness 312 may be a length orthogonally between cell surface 310 and film surface 314. Film thickness 312 may be controlled during the selected deposition process, for example, by controlling timing of deposition. Thickness of film 204 may also be measured during deposition to ensure that a desired thickness is achieved. Thus, films may be controllably applied using known processes and process controls.
Film 204 may be formed from numerous optical materials. For example, film 204 may be formed from various nitrides or oxides. Film 204 may include either silicon nitride (Si3N4) or silicon dioxide (SiO2); however, other materials may be suitable to form film 204, including a variety of transparent dielectric materials such as alumina, magnesium fluoride or diamond-like carbon. Furthermore, exotic methods such as nanostructured films, self-assembled microspheres, and organic materials, may be used to form film 204 over cell surface 310. Additionally, film 204 may also include a semiconductor material.
In an embodiment, film 204 material may be chosen based on a refractive index value of the material. In particular, a film material may be selected that has an index value between the refractive index values of the surrounding medium, for example air, and device layer 202, for example silicon. An index value in this range may provide for the reflection of light from both film surface 314 and cell surface 310. Accordingly, a refractive index of film 204 may be in a range of about 1.0 to 6.5 for the transmission of light across the visible spectrum. For example, refractive index for film 204 of silicon nitride transmitting light spanning the visible spectrum may be between about 2.01 to 2.09. Alternatively, the refractive index for film 204 of silicon dioxide transmitting light across the visible spectrum may be in a range of about 1.45 to 1.47.
As described below, film 204 may have one or more layers formed from similar or different materials. Each layer may include a similar or different optical thickness. As used here, optical thickness refers to an optical path length or optical distance of a film or a film layer. More specifically, optical thickness is a product between a refractive index of a film and a dimensional thickness of the film. For example, in the case of two films, one formed from silicon nitride and one formed from silicon dioxide, a dimensional thickness of the films to ensure that light of the same wavelength that is coherent before entering the films will also be in phase when exiting the films, is the ratio between the refractive indices of the materials. That is, the thickness of the silicon dioxide film must be about 1.4 times thicker than the thickness of the silicon nitride film to ensure that transmitted light rays of the same wavelength entering the films will remain in phase when exiting the films.
Reflection of a ray of light from a film depends on optical thickness. More particularly, for two light rays of a like wavelength to constructively interfere and reflect from film 204, the rays must be in phase as they exit film surface 314. Thus, for constructive interference between a front-surface-reflected ray and a back-surface reflected ray that are in phase when they impinge the front surface, the difference in optical thickness traversed by the respective rays must equal one or more full wavelengths. This condition is satisfied if the dimensional thickness of the film equals one or more integer numbers of (vacuum) half-wavelengths, divided by the refractive index of the film. Generally, a film thickness corresponding to a single half-wavelength will be typical. As an example, for film of silicon nitride having a refractive index of 2.09 when transmitting light with a wavelength of 380 nm, a dimensional thickness of the film will be a half wavelength (190 nm) divided by the refractive index (2.09), or about 91 nm, to ensure that the incident light constructively interferes at the film surface. From the discussion above, it is apparent that constructive interference and reflectance of light from a film depends in part on optical thickness, and optical thickness may be controlled not only through the choice of material with a particular refractive index, but also through the dimensional thickness of the film and/or film layers.
Referring to
Rays 410 and 412 schematically illustrate the possibility of combining reflections from multiple film layers. Combinations of reflected light from a single photovoltaic cell may be exploited through the addition of more and different layers of film 204, which provides for control over the types and intensities of reflected visible light wavelengths.
In reference to
Referring to
As mentioned above, the first dark fringe 502 may correspond to different film thicknesses 312 where multiple film layers are employed. For example, in a case in which device layer 202 is formed from silicon and a two-layer film 204 is employed having a silicon dioxide top film layer 404 (refractive index of about 1.46 at 535 nm) and a silicon nitride bottom film layer 402 (refractive index of about 2.04 at 535 nm), a dark fringe 502 for an incident wavelength of light of 535 nm occurs with a top film layer thickness and a bottom film layer thickness corresponding to an optical thickness of a quarter wavelength each. Accordingly, a dark fringe 502 occurs with a top film layer thickness of approximately 91 nm and a bottom film layer thickness of approximately 65 nm. With multiple layers 402 and 404, and hence two or more interfaces, there is sufficient control to create two minima. More layers may be employed to create even more dark fringes centered at different wavelengths.
As film thickness 312 increases beyond the optical thickness associated with dark fringe 502 for a given wavelength, percent power reflected for that wavelength increases. More specifically, as film thickness 312 increases so does the path length over which cell ray 320 travels, causing film ray 318 and cell ray 320 to shift back into phase until a maximum at bright fringe 504 is achieved. For the pertinent wavelength, a reflection maximum occurs at each film thickness corresponding to one of these bright fringes. At bright fringe 504, film ray 318 and cell ray 320 are in phase and combine to reflect away from device layer 202. Accordingly, energy of film ray 318 and cell ray 320 are lost as reflected visible light and the power absorption of device layer 202 decreases as compared to absorption at dark fringe 502. As an example, for a device layer 202 formed from silicon and a single layer film 204 formed from silicon nitride, bright fringe 504 may occur over the entire spectrum of visible light with film thickness 312 ranging from about 88 nm to 186 nm.
In an embodiment, for a photovoltaic cell 102 having a single layer film 204, dark fringe 502 and bright fringe 504 for a given wavelength repeat in a sinusoidal manner with intermittent maxima occurring at fringe spacing 506. More specifically, fringe spacing 506 corresponds with half of the wavelength of the impinging light ray, given that for every increase in film thickness 312 by one half wavelength, the optical path length travelled by cell ray 320 may be a full wavelength, and thus, the film ray 318 and cell ray 320 interference may repeat. Accordingly, for longer wavelength light, for example, red light, fringe spacing 506 is greater than for shorter wavelength light, for example, violet light.
Referring to
Film configuration may be manipulated in numerous ways to achieve the desired selective reflectance and photovoltaic cell color. For example, silicon device layer 202 may be covered by a silicon nitride film 204, film thickness 312 may be deposited to a thickness greater than a film thickness corresponding to dark fringe 502 for a given wavelength. More specifically, film thickness 312 may be deposited to achieve an optical thickness of at least a quarter wavelength of the selected colored light wavelength and more preferably at least three-eighths of the wavelength of the selected colored light. Further still, film thickness 312 may be varied to achieve an optical thickness of film 204 in a range between even multiples of three-eighths to five-eighths of a wavelength corresponding to the selected color. Such a range corresponds to constructive region 508 in which rays tend to mostly interfere constructively. For example, a second bright fringe 504 for a wavelength may be centered within constructive region 508 between optical thicknesses of film 204 ranging from six-eighths to ten-eighths, and more particularly between optical thicknesses ranging from seven-eighths to nine-eighths of the wavelength corresponding to the selected color. Thus, film thickness 312 may be configured to include an optical thickness within constructive region 508 in order to take advantage of second bright fringe 504, or other higher order bright fringes, and to reflect the wavelength of light in that range.
In another example, film thickness 312 is deposited to a thickness corresponding to bright fringe 504 for the desired wavelength of light. More specifically, for a photovoltaic cell 102 having silicon device layer 202 and single layer film 204 of silicon nitride, in order to reflect a green color, film 204 may be deposited to achieve an optical thickness of about half of the wavelength of the selected green colored light. For example, film 204 may be deposited to a thickness of about 130 nm to reflect green light with a wavelength of about 530 nm and thus color photovoltaic cell 102 green.
From the discussion above, it will be apparent that optimal film thickness 312 is variable, depending on the color sought, film material, number of layers, etc. However, in exemplary embodiments using a single interference film layer 204 of silicon nitride, total destructive interference is achieved for violet light at a film thickness 312 of about 75 nm, for blue at about 100 nm, for green at about 125 nm, and for yellow at about 200 nm. Hence to produce reflection at a selected one of these colors, thickness 312 should exceed the respective stated value.
In addition to a minimum film thickness 312 to achieve a photovoltaic cell 102 color, film thickness 312 may also be selected based on different power generation efficiencies centered around different bright fringes 504. More particularly, a photovoltaic cell 102 may appear of a certain color when film 204 is applied to a thickness corresponding to one of the bright fringes 504 associated with the color. For example, photovoltaic cell 102 may appear to be colored a similar shade of green when single layer film 204 includes an optical thickness of 130 nm, 260 nm, 390 nm, and so on, corresponding to each bright fringe 504 shown in
The discussion above primarily assumes a normal or perpendicular angle of incidence of a light ray entering film 204. However, in practice, this idealization may not be the case. For viewing at an oblique angle, the optical path length through the film increases by a factor of the secant of the angle of view, as taken relative to the normal. Nonetheless, one skilled in the art may adjust for oblique or non-perpendicular viewing angles through variations in film thickness 312. For example, if an onlooker is expected to view photovoltaic module 100 at an angle of 45 degrees, film thickness 312 may be expected to decrease approximately by the cosine of 45 degrees times a half wavelength of the incident light 316. That is, for a same color appearance of photovoltaic module 100, film thickness 312 may be decreased by about 30% as compared to film thickness 312 when onlooker is expected to view photovoltaic module 100 perpendicularly. These adjustments are derivable by one skilled in the art and may be exploited to ensure that the desired color is reflected in the desired direction from photovoltaic cells 102 that are placed on curved surfaces.
For example, photovoltaic cells 102 covering a curved parabolic reflector may include different film thickness 312. More particularly, film thickness 312 of photovoltaic cells 102 near the center of the reflector may be thicker than film thickness 312 of photovoltaic cells 102 near an outer edge of the reflector, when an onlooker is expected to view the center of the reflector straight on. As a result, the entire curved surface may appear to have approximately the same color to the onlooker, even though the optical thicknesses of the photovoltaic cells 102 across the photovoltaic module 100 differ for the different angles of incidence.
Referring to
For example, the first wavelength and the second wavelength may be the same, and thus, first photovoltaic cell 702 and second photovoltaic cell 704 may have a similar color appearance. However, alternatively, the first wavelength and the second wavelength may differ, resulting in differently colored photovoltaic cells. For example, the first wavelength may differ from the second wavelength by at least 10 nm, creating a perceptible change in color hue, even where the photovoltaic cells are in the same color range. In another example, the first wavelength and the second wavelength differ by more than about 30 nm.
Thus, when viewed from the same direction, photovoltaic module 100 may appear to have two differently colored pixels, that is, first photovoltaic cell 702 and second photovoltaic cell 704 arranged as pixels in a display. Wavelengths of light in incident light 316 not reflected by either of the photovoltaic cells may be absorbed by the photovoltaic cells for the creation of electricity.
Referring to
First photovoltaic cell 702 may be selectively colored by altering first film 710 to reflect away certain wavelengths of light, and similarly, it may be selectively receptive to other wavelengths of light. For example, second incident light 708 may correspond to yellow light with a wavelength of about 580 nm. Thus, in the example described above in which first photovoltaic cell 702 is manipulated to appear red, first film 710 of silicon nitride with a thickness of about 174 nm will have an optical thickness of about three-fifths of the yellow light wavelength. Accordingly, destructive film ray 808 and destructive cell ray 810 of second incident light 708 will substantially destructively interfere, and thus, most of yellow light will become absorbed light 718 within device layer 202, rather than being reflected away to alter the color of first photovoltaic cell 702.
Referring to
Second photovoltaic cell 704 may also be selectively receptive to other wavelengths of incident light 316, such as first incident light 706. In an example in which first incident light 706 is red light with a wavelength of 700 nm, second film 714 with a thickness of 198 nm will have an optical thickness of about two-fifths of the red light wavelength. Accordingly, destructive film ray 808 and destructive cell ray 810 of first incident light 706 will substantially destructively interfere, and thus, most of red light will become absorbed light 718 within device layer 202, rather than being reflected away to alter the appearance of second photovoltaic cell 704.
An optical thickness across a film may be varied to cause multiple visible reflections to emanate from the same film surface. For example, the optical thickness at a first location on a film may be greater than an optical thickness at a second location on the film. Thus, as incident light passes through the film, a first wavelength of light will constructively interfere at the first location and a second wavelength of light will constructively interfere at the second location. Accordingly, the first wavelength of light will reflect from the first location and the second wavelength of light will reflect from the second location. Therefore, the visible color of a photovoltaic cell may be altered across the cell surface by closely controlling optical thickness of a film over the cell surface. This phenomenon may be used, for example, to give a single photovoltaic cell surface an iridescent visible appearance.
In this example, a multi junction cell includes first photovoltaic cell 702 stacked above second photovoltaic cell 704. Thus, the stack of photovoltaic cells may project out of a plane of photovoltaic module 100. First photovoltaic cell 702 may include first film 710 and second photovoltaic cell 704 may include second film 714. Thus, first film 710 may be above both first photovoltaic cell 702 and second photovoltaic cell 704, while second film 714 may be sandwiched between first photovoltaic cell 702 and second photovoltaic cell 704. Optionally, second film 714 may function as a glue layer to adhere the photovoltaic cells together, or in another embodiment, a separate junction film may be applied to bond the photovoltaic cells into a stacked configuration. The cells may be nominally isolated electrically and interconnected using various interconnection architectures, as described further below.
Incident light 706 may pass through first film 710 to be partially reflected as first visible reflection 712 and partially absorbed as absorbed light 718. Absorbed light 718 may also travel through first photovoltaic cell 702 toward second photovoltaic cell 704. More specifically, absorbed light 718 is not only partially absorbed by first photovoltaic cell 702, but portions may also reflect from sandwiched second film 714 as second reflection 716, and still other portions may enter second photovoltaic cell 704 to become absorbed light 718 therein.
Unlike
Although the presence of internal reflections and the combinations of internal reflections with absorbed light may complicate the photovoltaic cell model, the design of a multi junction cell may nonetheless be performed using well known optical design techniques. For example, a structure such as this may be referred to as a multilayer dielectric stack, for which design tools exist to optimize reflections. Thus, first film 710 and second film 714 may be optimized to achieve the desired visible reflections 712 and 716 over the optical spectrum of interest. A spatial variation of first film 710 may allow a spatial dependence of reflection across the stacked photovoltaic cell 704. Furthermore, multiple stacked photovoltaic cells 704 may be arranged in-plane across photovoltaic module 100 as described above with respect to
Referring to
Photovoltaic module 100 includes a first set 1102 of one or more first photovoltaic cells 702 that are electrically connected in series with each other. For example, first set 1102 may include a plurality of first photovoltaic cells 702 that are each configured to have the same energy conversion efficiency. For example, each of first photovoltaic cells 702 may be configured to reflect the same color light in a direction, for example, red light, and therefore appear to have the same color as described above. Alternatively, each of first photovoltaic cells 702 may be differently colored or have different film configurations, but may nonetheless have approximately the same power efficiency.
For example, a first photovoltaic cell 702 in the first set 1102 may appear as a first color and reflect light at a first bright fringe for the first color, while a second photovoltaic cell 704 in the first set 1102 may appear as a second color and reflect light at a second bright fringe for the second color. Although the reflected colors may differ, the power loss for the different colors may be similar at the different selected bright fringes, and thus, differently colored photovoltaic cells 102 in the first set 1102 may have about the same conversion efficiency.
Although first set 1102 is shown with six photovoltaic cells in series, first set 1102 may include more or fewer photovoltaic cells. For example, first set 1102 may include between ten and twelve photovoltaic cells electrically connected in series. Typically, a series of photovoltaic cells are limited in efficiency by the least efficient cell in the series. However, since in this illustration every cell in first set 1102 includes the same configuration, for example, reflects the same wavelength of light, the power production efficiency of first set 1102 may not be significantly constrained by any one of the first photovoltaic cells 702 as compared to another.
Photovoltaic module 100 includes a second set 1104 of photovoltaic cells divided into subsets. For example, second set 1104 may include a first subset 1106 and a second subset 1108. As shown, second set 1104 may include six subsets. However, this is illustrative and more or fewer subsets may be included in second set 1104. Rather than being electrically connected in series, subsets of second set 1104 may be connected in parallel. For example, each subset may include one or more photovoltaic cells electrically connected in series, and the subsets may then be electrically connected in parallel. Consequentially, the efficiency of each subset will be limited by the least efficient photovoltaic cell in the subset. Nonetheless, the overall efficiency of second set 1104 may not be so limited. More particularly, voltage harvesting from each subset may be accumulated independently from parallel subsets, and thus, accumulation of voltage may not be limited by any one of the subsets. Optionally, each photovoltaic cell in a subset may be similarly configured, that is, may be similarly colored. However, similar coloring of sets may be unnecessary except to the degree it is necessary to achieve similar energy conversion efficiencies in the photovoltaic cells of first set 1102.
Photovoltaic module 100 may include numerous combinations of sets. For example, second set 1104 may be electrically connected in series with a third set 1110, which like first set 1102, may include a plurality of photovoltaic cells electrically connected in series. Furthermore, like first set 1102, the photovoltaic cells in third set 1110 may be similarly colored so as to not limit the efficiency of third set 1110 to a single low efficiency photovoltaic cell. Additional sets like second set 1104, in which subsets of serially connected photovoltaic cells are connected in parallel, may be added to build out photovoltaic module 100 further. Combinations of sets may be made in any manner, with sets connected in series, as shown, or with two or more sets of photovoltaic module 100 connected in parallel.
Referring to
As an example, photovoltaic cells 102 may be arranged to display an image 1202, such as a company logo, on a photovoltaic module 100. First set 1102 of photovoltaic cells 102 may include a film that preferentially reflects a background color and second set 1104 of photovoltaic cells 102 may include a film that preferentially reflects a logo color. As described above, second set 1104 may also include some photovoltaic cell pixels of background color electrically connected in parallel with photovoltaic cell pixels of logo color. Thus, the combination of first set 1102 and second set 1104 in an arrangement will display a logo image 1202 to an onlooker. It will be readily apparent that although a photovoltaic module 100 that reflects a logo image 1202 may be less efficient than one with a purely anti-reflective coating, the aesthetic value provided by such a photovoltaic module 100 may offset the lower energy conversion efficiency. Furthermore, color customization of photovoltaic cells 102 may invite architects, industrial designers, and marketers to integrate microscale photovoltaic cells 102 into products that presently do not use commercial photovoltaic cells 102 because of their traditional size and appearance.
In addition to providing a logo image 1202 as shown in
Additive color models may be realized through the use of multi-layered films. More specifically, multiple film layers may be tuned to cause constructive interference and reflection of multiple light wavelengths. For example, in the case of a photovoltaic cell 102 having a two-layered film with a top film layer 404 and a bottom film layer 402, the top film layer 404 may be tuned to include an optical thickness of about 240 nm, that is, a half wavelength of blue light. Furthermore, the bottom film layer 402 may be tuned to include an optical thickness of about 110 nm, and thus, the combination of the upper layer and lower layer may create a total optical thickness for the film 204 of about 350 nm, that is, a half wavelength of red light. Accordingly, constructive interference and reflection may occur for both blue light and red light, and the reflected light rays may visually combine to give the photovoltaic cell 102 a magenta color.
Alternatively, photovoltaic cells 102 adjacently positioned that respectively reflect red, green, and blue may be manipulated to cause the combination of reflected light to be recognized as a combined color, such as red brown or forest green. Manipulation to achieve this effect may be made according to the principles described above. For example, the intensity of reflected red, green, and blue light from individual photovoltaic cells may be controlled by controlling film properties such that film ray 318 and cell ray 320 constructively interfere to a greater or lesser degree. Intensity of a color will be greatest where film ray 318 and cell ray 320 have no phase shift, but lower intensities may also be achieved by shifting film ray 318 and cell ray 320 out of phase slightly. Then, by reflecting different light and light intensities from adjacent cells, the individual colors from multiple photovoltaic cells 102 may visually combine into a resultant color when viewed by a distant onlooker.
Referring to
It is also possible to use other colors as base colors, for example Cyan, Magenta, Yellow and Black may also be used as a set of base colors. In this example a film thickness of approximately 110 nm will produce a Cyan colored sub-pixel reflective segment, a film thickness of approximately 310 nm will produce a Magenta colored sub-pixel reflective segment, a film thickness of approximately 140 nm will produce a Yellow colored sub-pixel reflective segment, and a film thickness of approximately 60 nm will produce a black or dark colored sub-pixel reflective segment.
It is helpful to think of the desired color for a colorized photovoltaic cell as a particular percentage of base colors such as red, green, blue and black. The percentages of R, G, B, BK (Red, Green, Blue, Black) can be used to decide how many colored sub-pixel reflective segments within a colorized photovoltaic cell should be given a particular base color in order to provide the colorized photovoltaic cell 1502 with the desired color. It should be noted that for some desired colors a percentage for a particular base color may be zero.
In the case of a colorized photovoltaic cell having 256 colored sub-pixel reflective segments, the following colors can be created using the combinations of R, G, B and BK colored sub-pixel reflective segments shown. Tan can be created using a combination of 53, 54, 47 and 102 colored sub-pixel reflective segments having the colors R, G, B and BK, respectively. Light olive green can be created using a combination of 35, 40, 36 and 145 colored sub-pixel reflective segments having the colors R, G, B and BK, respectively. Forest green can be created using a combination of 27, 33, 30 and 166 colored sub-pixel reflective segments having the colors R, G, B and BK, respectively.
The brightness or intensity of colorized photovoltaic cell 1502 may be controlled using colorized sub-pixel reflective segments 1602 having a dark color. It is also possible to use non-reflective sub-pixel segments to provide a dark color. Increasing the number of non-reflective sub-pixel segments or dark colored sub-pixel reflective segments composing colorized photovoltaic cell 1502 decreases the color intensity of the colorized photovoltaic cell.
This application claims the benefit of the earlier filing date of U.S. Provisional Patent Application No. 62/016,823, filed Jun. 25, 2014, entitled “REFLECTIVE PHOTOVOLTAICS”. The aforementioned application is hereby incorporated by reference, in its entirety, for all purposes. This application is a Continuation-In-Part of commonly assigned, co-pending U.S. patent application Ser. No. 14/067,822, filed on Oct. 30, 2013. The aforementioned application is hereby incorporated by reference, in its entirety, for all purposes.
This invention was made with Government support under Contract No. DE-AC04-94AL85000 awarded by the U.S. Department of Energy. The Government has certain rights in the invention.
Number | Name | Date | Kind |
---|---|---|---|
8736108 | Nielson et al. | May 2014 | B1 |
20090078316 | Khazeni et al. | Mar 2009 | A1 |
20090296194 | Gally et al. | Dec 2009 | A1 |
20120247541 | Wootton | Oct 2012 | A1 |
20140261624 | Cruz-Campa et al. | Sep 2014 | A1 |
Number | Date | Country |
---|---|---|
2011-114262 | Sep 2011 | WO |
Entry |
---|
International Search Report and Written Opinion for PCT/US2014/027670 filed on Mar. 14, 2014 mailed by the International Searching Authority dated Sep. 24, 2014 pp. 1-4. |
Number | Date | Country | |
---|---|---|---|
62016823 | Jun 2014 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 14067822 | Oct 2013 | US |
Child | 14747196 | US |