Reformed crosslinked polyethylene articles

Information

  • Patent Grant
  • 6361842
  • Patent Number
    6,361,842
  • Date Filed
    Thursday, December 23, 1999
    25 years ago
  • Date Issued
    Tuesday, March 26, 2002
    22 years ago
Abstract
A method of producing reformed crosslinked polymer articles provides reformed crosslinked articles free of visible and objectionable folds, seams and interfaces on reformed surfaces thereof. In a preferred embodiment, a product is produced by a method including the steps of extruding a silane-grafted polyethylene tube, heating an end of the tube, reforming the end of the tube to produce a radially enlarged sealing surface thereon, cooling the reformed tube, and curing the reformed tube to produce an increase in the degree of crosslinking of the polyethylene material.
Description




BACKGROUND OF THE INVENTION




The present invention relates generally to methods of forming articles made of polyolefin materials and, in a preferred embodiment thereof, more particularly provides a product produced by a method of reforming crosslinked polyethylene articles.




It is well known in the art to crosslink polyolefins. Such crosslinking is known to enhance certain physical and chemical properties of polyolefin materials. In particular, crosslinking has been shown to increase maximum useful temperature, reduce creep, improve chemical resistance, increase abrasion resistance, improve memory characteristics, improve impact resistance, increase resistance to oxidative degradation, and improve environmental stress crack resistance of polyolefin materials.




It is also well known in the art to subject polyethylene (PE) to a variety of crosslinking processes to produce crosslinked polyethylene (PEX). These PE crosslinking processes include addition of peroxide, addition of Azo compounds, electron beam irradiation, and addition of silane. The last of these utilizes silane to produce a grafted polymer.




Crosslinking of silane-grafted PE is described in a paper entitled “Polymer Crosslinking with Union Carbide(R) Organofunctional Silane A-171” published by Union Carbide Chemicals and Plastics Company, Inc. of Danbury, Connecticut, and in a paper entitled “Advances in Silane Crosslinking of Polyethylene” by L. M. Panzer of Union Carbide Chemicals and Plastics Company, Inc., Tarrytown, New York, both of which are hereby incorporated by reference.




In one silane crosslinking process known as Sioplas, a PE resin is melted and silane is added to the melted PE along with a peroxide initiator. Crosslinking sites are thereby formed on PE polymer chains and crosslinking begins to occur. The grafted resin is pelletized and stored for later use in foil-lined bags. As crosslinking of the grafted resin occurs in the presence of moisture, it is important that the grafted resin not be exposed to moisture until substantial crosslinking is desired. However, since this method of crosslinking of PE is self-perpetuating, the crosslinking reaction producing moisture as a byproduct, it is not practical to completely prevent crosslinking in the pelletized grafted PE resin and so it has a shelf life of only approximately 6-9 months.




A catalyst masterbatch is prepared for the grafted resin. The catalyst masterbatch typically includes a quantity Of PE, a catalyst, an antioxidant, a stabilizer, and an internal lubricant. The catalyst masterbatch is typically pelletized for ease of mixing with the grafted resin in a conventional extruder.




The grafted resin and catalyst masterbatch are usually combined in a specific ratio, melted and mixed together, and extruded. When the grafted PE resin and catalyst masterbatch are mixed together, crosslinking of the PE at the silane graft sites accelerates. The material exits the extruder and is typically cooled in water.




In another silane crosslinking process known as Monosil, instead of preparing separate grafted PE resin and catalyst masterbatch, the PE resin, silane, peroxide initiator, catalyst, antioxidant, stabilizer, and internal lubricant are combined in one step. The materials are melted and mixed together, typically in the extruder, and extruded. A method of making crosslinked extruded products is described in U.S. Pat. No. 4,117,195, the disclosure of which is hereby incorporated by reference. AS with the Sioplas method, in the Monosil process the material exits the extruder and is cooled in water.




To complete the crosslinking process, the extruded material from either the Sioplas or Monosil process is generally exposed to moisture at an elevated temperature. A sauna-like environment or hot water immersion will produce the desired level of crosslinking in a relatively short period of time. When this curing stage is finished, the PE may be approximately 65-89% crosslinked.




PEX has been utilized for diverse applications, including wire and cable insulation, and pipe. Where pipe is made of PEX, the crosslinking process enhances its ability to contain fluid at elevated temperature and pressure. For this reason, commercial success has been achieved in utilizing PEX pipe in hot water heating applications and in potable hot water plumbing applications.




A disadvantage of PEX pipe, however, is that it is not suitable for forming sealing surfaces thereon. For example, riser tubes may not be conveniently formed from PEX pipe by heating the PEX pipe and forming the heated pipe between mating dies as described in U.S. patent application Ser. No. 08/622,061 entitled “Automated Tube Reforming Apparatus and Associated Methods of Manufacturing”, the disclosure of which is hereby incorporated by reference. Since the material is substantially crosslinked, such reforming of the PEX pipe typically produces visible and objectionable interfaces, seams, and folds, which provide leak paths across the sealing surface formed thereon.




From the foregoing, it can be seen that it would be quite desirable to provide a product produced by a method of reforming crosslinked PE articles which does not produce visible and objectionable interfaces, seams, and folds on sealing surfaces of the articles, but which articles may be subsequently utilized in sealing applications, such as containment of pressurized hot water. It is accordingly an object of the present invention to provide such a product.




SUMMARY OF THE INVENTION




In carrying out the principles of the present invention, in accordance with an embodiment thereof, a method is provided which permits grafted polyolefin articles to be reformed with sealing surfaces thereon and subsequently crosslinked. The articles thus produced have the superior properties associated with crosslinked polyolefins, in combination with a desired functional shape, such as a hot water riser tube in plumbing applications having a radially enlarged sealing surface formed thereon.




In broad terms, a method of reforming a polymer material having a first shape as extruded from an extruder is provided. The method includes the steps of forming the extruded material so that the extruded material has a second shape, and then curing the extruded material. The polymer material may be a polyolefin, a silane-grafted polyolefin, and may be a silane-grafted polyethylene material.




In one aspect of the present invention, the forming step includes the steps of gauging a volume of the polymer material to be formed, heating the gauged volume of polymer material, forming the gauged volume of polymer material, and cooling the formed polymer material. The polymer material may be generally tubular-shaped prior to the forming step.




In another aspect of the present invention, the curing step includes subjecting the formed polymer material to moisture for a predetermined period of time. The formed material may also be heated while it is subjected to the moisture.




Also provided is a method of reforming and crosslinking a silane-grafted polyolefin article. The method includes the steps of heating the polyolefin article when it is approximately 1-60% crosslinked, reforming the heated polyolefin article between a pair of mating dies so that the heated polyolefin article is at least partially reshaped, cooling the reformed polyolefin article, and curing the reformed polyolefin article. The polyolefin article may be a tube made of silane-grafted polyethylene.




In one aspect of the present invention, the curing step includes subjecting the reformed polyolefin article to moisture until it is approximately 65-89% crosslinked. The curing step may be accomplished by placing the reformed polyolefin article in a steam chamber for a predetermined period of time.




Yet another method is provided by the present invention—a method of forming a radially enlarged sealing surface on a tube made of a silane-grafted polyethylene material. The method includes the steps of gauging a volume of the tube to be formed, heating the volume of the tube to be formed, forming the heated volume of the tube into the radially enlarged sealing surface when the tube is approximately 1-60% crosslinked or, more preferably, approximately 1-40% crosslinked, cooling the formed volume of the tube, and further crosslinking the tube.




In one aspect of the present invention, the further crosslinking step includes exposing the tube to water until the tube is approximately 65-89% crosslinked. The tube may be further crosslinked by disposing the tube in an enclosure and introducing steam into the enclosure.




The present invention also provides products produced by the above methods.




The use of the disclosed method enables convenient reforming of articles made of polymer materials. Significantly, the method permits tubes made of silane-grafted polyethylene to be reformed so that radially enlarged sealing surfaces are formed thereon, without also causing visible and objectionable folds, seams, or interfaces to be formed on the sealing surfaces. Thereafter, the tubes may be cured so that they may be used in applications requiring a relatively large percentage of crosslinking.











BRIEF DESCRIPTION OF THE DRAWING





FIG. 1

is a cross-sectional view of a riser tube manufactured according to a method embodying principles of the present invention.











DETAILED DESCRIPTION




In a method embodying principles of the present invention, a polymer material is extruded from an extruder. The extruded polymer material is then reformed by gauging a volume of the extruded polymer material to be reformed, heating the gauged volume of extruded polymer material, reforming the gauged volume of extruded polymer material, cooling the reformed polymer material, and then curing the reformed polymer material.




Applicant has successfully utilized the method to produce articles, such as riser tubes, having sealing surfaces thereon. The sealing surfaces are formed on PE tubes substantially continuously extruded from an extruder. Applicant's method of producing reformed crosslinked riser tubes is described more fully hereinbelow, but it is to be understood that other articles may be produced without departing from the principles of the present invention.




Applicant procures repelletized PE resin in which the PE resin has been subjected to a silane grafting reaction. Thus, the PE resin has previously been melted, had silane and a free radical generator, such as a peroxide initiator, added thereto, and the silane has formed crosslinking sites on the PE polymer chains. The result is a grafted base PE resin which is repelletized. Note that, as soon as the PE resin has silane grafted thereto, some crosslinking may occur.




Applicant also procures a catalyst masterbatch. The catalyst masterbatch comprises a quantity of PE, a catalyst, an antioxidant, and a stabilizer. The catalyst masterbatch may also include an internal lubricant. Different formulations of catalyst masterbatch may be desired, for example, the internal lubricant may be considered optional. The catalyst masterbatch is also provided in pelletized form.




Applicant procures the grafted base PE resin and catalyst masterbatch from Padanaplast USA, located in Sheboygan, Wisconsin. The grafted base PE resin is sold under the tradename PEXIDAN A/T. The catalyst masterbatch is sold under the tradename CAT 002 UV.




The grafted base PE resin and catalyst masterbatch are introduced into a conventional extruder. The proportions are approximately 95% grafted base PE resin and 5% catalyst masterbatch, by weight. This mixture is then melted and mixed thoroughly in the extruder. Applicant prefers to use the above proportions, but it is to be understood that other proportions may be used without departing from the principles of the present invention, for example, if the grafted base PE resin and/or catalyst masterbatch are procured from different sources, different proportions of these components may be desirable.




The mixture is extruded by the extruder in tubing form, the tubing having approximate desired inside and outside diameters, and wall thickness. As the tubing exits the extruder, it is cooled by, for example, immersion in a liquid, such as water. As the tubing cools, it is sized to its desired dimensions.




When the tubing has been fully cooled, it is cut into pieces. Each of the pieces has a desired length appropriate for a riser tube, generally between 6 and 72 inches. Note that, when a volume of each tube piece is reformed as more fully described hereinbelow, the overall length of each tube piece will be somewhat shortened thereby, thus, this shortening of the tube pieces should be compensated for when the tube pieces are cut to length. Such tube pieces are suitable for loading into an automated tube reforming apparatus, such as that disclosed in U.S. patent application Ser. No. 08/622,061. It is to be understood that other tube reforming apparatus may be utilized in the method of the present invention without departing from the principles thereof.




At this point, the PE material of which each of the tubing pieces has been fabricated is approximately 1-60% crosslinked. Applicant prefers that the material be approximately 1-40% crosslinked for ease of forming. However, further crosslinking is required in order for the tubing pieces to meet the performance requirements of ASTM Standard F876-93 entitled “Standard Specification for Crosslinked Polyethylene (PEX) Tubing”, which is hereby incorporated by reference. To meet those performance requirements, the tubing pieces as reformed must be crosslinked approximately 65-89%. Applicant utilizes ASTM Standard D2765 entitled “Test Methods for Determination of Gel Content and Swell Ratio of Crosslinked Ethylene Plastics”, which is hereby incorporated by reference, to determine degree of crosslinking.




As will be readily apparent to one of ordinary skill in the art, a conventional unitary (i.e., one-piece) riser tube generally includes at least one radially enlarged sealing surface formed on an end thereof. If the sealing surface were formed on one of the tubing pieces after the PE material had been crosslinked approximately 65-89%, visible and objectionable folds, interfaces, or seams would be produced on the sealing surface. For this reason, applicant prefers that the tubing pieces be loaded into the automated tube reforming apparatus when the tubing pieces material has been crosslinked approximately 1-60%, and more preferably is approximately 1-40%.




After the tubing pieces have been loaded into the automated tube reforming apparatus, the apparatus gauges the volume of material to be reformed for each tubing piece, clamps the tubing pieces in the apparatus, heats each gauged volume of material, reforms each heated volume of material between a pair of mating dies, cools each reformed volume of material, and releases the reformed tubing pieces for removal from the apparatus. When the heated volumes of material are reformed between the pairs of mating dies, the radially enlarged sealing surfaces are formed on the tubing pieces. Since the tubing pieces material is not fully crosslinked, the sealing surfaces are smooth and free of visible and objectionable folds, seams, and interfaces.




To more fully crosslink the tubing pieces material, and to ensure compliance with the ASTM Standard F876-93, after the tubing pieces are reformed by the automated tube reforming apparatus, they are subjected to a subsequent deliberate crosslinking step in which the reformed tubing pieces are loaded into a steam chamber. The steam chamber is an enclosure into which steam is introduced at atmospheric pressure.




Since crosslinking of the tube pieces material occurs in the presence of moisture and the rate of crosslinking is at least somewhat dependent on temperature, the amount of moisture and the temperature within the steam chamber may be adjusted to produce a desired rate of crosslinking in the tube pieces material. Applicant prefers that the tubing pieces be cured in the steam chamber for a period of 24 hours at 100% relative humidity and at 180-210 degrees F.




A sample of each group of reformed tubing pieces loaded into the steam chamber is tested thereafter (utilizing ASTM Standard D2765) to verify that the desired degree of crosslinking has been achieved (i.e., the material is fully crosslinked). For potable pressurized hot water applications, the reformed and cured tubing pieces should also be tested for conformance with ASTM Standard F877-93 entitled “Standard Specification for Crosslinked Polyethylene (PEX) Plastic Hot- and Cold-Water Distribution Systems”, which is hereby incorporated by reference.




It is to be understood that other curing means may be utilized in the method. For example, the reformed tubing pieces may be immersed in water at an elevated temperature, such as 90 degrees Celsius, or the water may be directed to flow through the interior of each tubing piece. As another example, the reformed tubing pieces may be left to cure by exposure to humidity in ambient air. As used herein, the term “cure” means a process step that produces a deliberate increase in the degree of crosslinking of a polymer material to a desired level.




Thus has been described a method of producing formed crosslinked polyolefin articles. The method permits extruded material to be cooled and then reformed before it is more fully crosslinked. In a preferred embodiment of the method, grafted base PE resin is melted and mixed with a catalyst masterbatch, and then extruded into tubing and cooled. The extruded tubing is then reformed by heating it and forming it between mating dies. The reformed tubing is then more fully crosslinked by exposure to steam within a chamber.




Representatively illustrated in

FIG. 1

is a riser tube


100


manufactured according to the method described hereinabove. Riser tubes similar to the riser tube


100


shown in

FIG. 1

are frequently used to connect plumbing fixtures, such as faucets, to hot and cold water distribution systems in buildings. It is to be understood that other products may be produced by the method described hereinabove without departing from the principles is of the present invention.




When it is extruded from an extruder (not shown), the riser tube


100


has a continuous elongated tubular shape. A tubular body portion


102


of the riser tube


100


retains the tubular shape. After being cut to length and having an end portion


104


thereof reformed in the automated tube reforming apparatus, a radially enlarged sealing surface


106


is present on the end portion of the riser tube


100


.




The riser tube


100


is then cured in a steam chamber until it is fully crosslinked. Applicant has successfully reformed and fully crosslinked riser tubes, similar to the riser tube


100


, for hot water distribution systems in compliance with the ASTM Specification F877-93.




It is to be understood that other crosslinking processes, such as irradiation and addition of Azo compounds, may be utilized to cure a reformed PE article without departing from the principles of the present invention. For example, a reformed PE article may be exposed to beta radiation in order to cure the PE material.




The foregoing detailed description is to be clearly understood as being given by way of illustration and example only, the spirit and scope of the present invention being limited solely by the appended claims.



Claims
  • 1. A product consisting entirely of a single cross-linkable polymer material and produced by a method of reforming the polymer material from a first shape as extruded from an extruder, the method comprising the steps of:partially crosslinking the extruded material while it has a first shape, the partially crosslinked extruded material being crosslinked to within the crosslinking range of from about 1% to about 60%; reforming the partially crosslinked extruded material so that it has a second shape, said second shape having a smooth surface portion substantially devoid of visible folds, seams or interfaces; and then further crosslinking the partially crosslinked extruded material, to within a crosslinking range of from about 65% to about 89%, to form said product with said smooth surface portion thereon.
  • 2. The product according to claim 1 wherein in the method the partially crosslinking step is performed in a manner such that the partially crosslinked extruded material is crosslinked to within the crosslinking range of from about 1% to about 40%.
  • 3. The product according to claim 1 wherein in the method the polymer material is a silane-grafted polyolefin material.
  • 4. The product according to claim 3 wherein in the method the polyolefin material is polyethylene.
  • 5. The product according to claim 1 wherein in the method said reforming step comprises the steps of:gauging a volume of the polymer material to be reformed; heating the gauged volume of polymer material; forming the gauged volume of polymer material; and cooling the reformed polymer material.
  • 6. The product according to claim 1 wherein in the method said further crosslinking step comprises subjecting the reformed polymer material to moisture for a predetermined period of time.
  • 7. The product according to claim 6 wherein in the method said further crosslinking step further comprises heating the reformed polymer material while the reformed polymer material is subjected to said moisture.
  • 8. The product according to claim 1 wherein in the method the first shape is generally tubular, and wherein said smooth surface portion is a radially enlarged sealing surface.
  • 9. A product produced by a method of reforming and crosslinking an article formed entirely from a single silane-grafted polyolefin material, the method comprising the steps of:heating the polyolefin article when it is crosslinked to within a crosslinking range of from about 1% to about 60%; reforming the heated polyolefin article between a pair of mating dies so that the heated polyolefin article is at least partially reshaped to have a smooth surface portion substantially devoid of visible folds, seams or interfaces; cooling the reformed polyolefin article; and further crosslinking the reformed polyolefin article, to within a crosslinking range of from about 65% to about 89%, to form said product with said smooth surface portion thereon.
  • 10. The product according to claim 9 wherein in the method said heating step is performed when the polyolefin article is crosslinked to within a crosslinking range of from about 1% to about 40%.
  • 11. The product according to claim 9 wherein in the method said further crosslinking step comprises subjecting the reformed polyolefin article to moisture until the reformed polyolefin article is approximately 65-89% crosslinked.
  • 12. The product according to claim 11 wherein in the method said further crosslinking step further comprises placing the reformed polyolefin article in a steam chamber for a predetermined period of time.
  • 13. The product according to claim 9 wherein in the method the polyolefin article is a tube made of silane-grafted polyethylene.
  • 14. A product consisting entirely of a single cross-linkable silane-grafted polyethylene material produced by a method of forming a radially enlarged sealing surface on a tube formed from said single cross-linkable silane-grafted polyethylene material, the method comprising the steps of:gauging a volume of the tube to be formed; heating the volume of the tube to be formed; forming the heating volume of the tube into the radially enlarged sealing surface when the tube is crosslinked to within a crosslinking range of from about 1% to about 60%; cooling the formed volume of the tube; and further crosslinking the tube to within a crosslinking range of from about 65% to about 89%.
  • 15. A product according to claim 14 wherein in the method the forming step is performed when the tube is crosslinked to within a crosslinking range of from about 1% to about 40%.
  • 16. The product according to claim 14 wherein in the method said further crosslinking step comprises exposing the tube to water until the tube is approximately 65-89% crosslinked.
  • 17. The product according to claim 16 wherein in the method said further crosslinking step is performed after said cooling step.
  • 18. The product according to claim 16 wherein in the method said further crosslinking step further comprises disposing the tube in an enclosure and introducing steam into the enclosure.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. application Ser. No. 09/023,157 filed on Feb. 12, 1998, now abandoned which was a division of U.S. application Ser. No. 08/655,459 filed on May 30, 1996, now U.S. Pat. No. 5,756,023.

US Referenced Citations (106)
Number Name Date Kind
213581 Mattson Mar 1879 A
1128156 Lamb Feb 1915 A
1731988 Skillman Oct 1929 A
2699575 Haury Jan 1955 A
2793970 Jeppson May 1957 A
2897092 Miller Jul 1959 A
2948665 Rubens et al. Aug 1960 A
2974367 Doering et al. Mar 1961 A
3047910 Downs Aug 1962 A
3054142 Hinderer Sep 1962 A
3102303 Lainson Sep 1963 A
3137745 Johnstone Jun 1964 A
3205289 Carpenter Sep 1965 A
3254147 Nakada May 1966 A
3270117 Hobson Aug 1966 A
3295870 Seablom Jan 1967 A
3304357 Langecker Feb 1967 A
3360826 Lorang Jan 1968 A
3370118 Lowe Feb 1968 A
3418409 Hess et al. Dec 1968 A
3429954 Atkins et al. Feb 1969 A
3448182 Derbyshire et al. Jun 1969 A
3448491 Sosnowski, Jr. et al. Jun 1969 A
3495301 Stephens et al. Feb 1970 A
3509252 Baehr Apr 1970 A
3509599 Driza et al. May 1970 A
3548190 Sclar et al. Dec 1970 A
3557278 Kuhlemann Jan 1971 A
3563973 Arditti et al. Feb 1971 A
3599287 Buck Aug 1971 A
3601852 Bjahme Aug 1971 A
3672804 Dalik Jun 1972 A
3734995 Thomas May 1973 A
3755524 McKay Aug 1973 A
3806301 Osterhagen et al. Apr 1974 A
3823216 Petzetakis Jul 1974 A
3831983 Stickler Aug 1974 A
3843300 McFarlane Oct 1974 A
3899565 de Putter et al. Aug 1975 A
3910744 Ronden et al. Oct 1975 A
3923947 Cook Dec 1975 A
3923949 Kane et al. Dec 1975 A
3929943 Klimaszewski, Jr. Dec 1975 A
3929960 Findlay et al. Dec 1975 A
3982871 Moddel Sep 1976 A
3986810 La Branche et al. Oct 1976 A
4028037 Dawson Jun 1977 A
4059379 Korff et al. Nov 1977 A
4065243 Acda et al. Dec 1977 A
4065541 Eckstein et al. Dec 1977 A
4083918 Ronden et al. Apr 1978 A
4102623 Mathison Jul 1978 A
4107249 Murai et al. Aug 1978 A
4113813 Wilson Sep 1978 A
4117195 Swarbrick et al. Sep 1978 A
4122137 Bohm et al. Oct 1978 A
4126661 Fulconis et al. Nov 1978 A
4131407 de Putter et al. Dec 1978 A
4134949 McGregor Jan 1979 A
4140739 Cotten Feb 1979 A
4150087 de Putter et al. Apr 1979 A
4167388 Keelor et al. Sep 1979 A
4177237 Ueno et al. Dec 1979 A
4191158 Curran Mar 1980 A
4219525 Greenspan Aug 1980 A
4264661 Brandolf Apr 1981 A
4269801 Klasena et al. May 1981 A
4271218 Heckel et al. Jun 1981 A
4276010 Shartzer Jun 1981 A
4279853 Ohta et al. Jul 1981 A
4289716 Voigt Sep 1981 A
4316870 Rowley Feb 1982 A
4323337 Korff et al. Apr 1982 A
4332767 Kitanaka et al. Jun 1982 A
4333898 Schmidtchen Jun 1982 A
4345956 Cox et al. Aug 1982 A
4379115 Seach et al. Apr 1983 A
4383966 Svetlik May 1983 A
4394343 Acda et al. Jul 1983 A
4404159 McFarlane Sep 1983 A
4406852 Riegel Sep 1983 A
4426497 Kent Jan 1984 A
4428900 Riley et al. Jan 1984 A
4446084 Rowley May 1984 A
4446283 Doi et al. May 1984 A
4457886 Acda et al. Jul 1984 A
4525136 Rowley Jun 1985 A
4525319 Kaspe Jun 1985 A
4664423 Rowley May 1987 A
4803033 Rowley Feb 1989 A
4857250 Gale et al. Aug 1989 A
4891173 Saitoh et al. Jan 1990 A
4902460 Yagi et al. Feb 1990 A
4927184 Bourjot et al. May 1990 A
5055251 Lebarbier et al. Oct 1991 A
5139710 Smith Aug 1992 A
5188787 King et al. Feb 1993 A
5244622 Rumberger Sep 1993 A
5505900 Suwanda et al. Apr 1996 A
5514312 Hardy et al. May 1996 A
5573822 Nishikawa Nov 1996 A
5622670 Rowley Apr 1997 A
5756023 Stachowiak May 1998 A
5792532 Pfleger Aug 1998 A
5861200 Rowley Jan 1999 A
5879723 Stachowiak Mar 1999 A
Foreign Referenced Citations (22)
Number Date Country
2205586 Aug 1973 DE
2248471 Apr 1974 DE
2733643 Feb 1979 DE
2836798 Mar 1980 DE
2921036 Nov 1980 DE
2940719 Apr 1981 DE
4135017 Apr 1983 DE
3929326 Mar 1991 DE
733643 Mar 1993 DE
4423372 Jan 1996 DE
877735 Feb 1959 GB
1336869 Dec 1970 GB
53006369 Jan 1978 JP
5356241 May 1978 JP
5312678 Nov 1978 JP
55148143 Nov 1980 JP
6150511 Nov 1981 JP
7008110 Jan 1982 JP
58008609 Jan 1983 JP
35806113 Mar 1983 JP
4198201 Jul 1992 JP
5156032 Jun 1993 JP
Non-Patent Literature Citations (10)
Entry
“Standard Specification for Crosslinked Polyethylene (PEX) Tubing” by American Society of Testing and Materials, Designation: F 876-93. pp. 942-946.
“Polymer Crosslinking with Union Carbside Organofunctional Silan A-171” by Union Carbide (1992), SC-1702.
“Advances in Silane Crosslinking of Polyethylene”, by L. M. Panzer.
Methods and Benefits of Crosslinking Polydefins for Industrial Applications by Colin Beveridge and Andrew Sabiston.
Standing Specification for Crosslinked Polyethylene (PEX) Plastic Hot-and Cold Water Distribution Systems by ASTM Committee F-17.
Examination of Cross Linked Polyethylene for Heating Systems.
“Water and Pipes”, pp. 31-33.
“H/S 311 Schiebehulse”, pp. 3-44, Technische Information.
“System Components JRG Samplex Pipes Planning and Installation Guide” Handbook 88-1.
“Pipes for Floor Heating and Domestic Hot Water Supply” Plan Plastic Products.
Continuation in Parts (1)
Number Date Country
Parent 09/023157 Feb 1998 US
Child 09/471311 US