REFRACTORY WITH A HIGH ZIRCONIA CONTENT AND A HIGH SILICA CONTENT

Abstract

The invention provides a novel fused cast refractory product with a high zirconia content having improved electrical resistivity. Said refractory product comprises, as a percentage by weight based on the oxides and for a total of more than 98.5%: ZrO2+Hf2O: >85%;SiO2: >10% to 12%;Al2O3: 0.1% to 2.4%;B2O3: <1.5%; anda dopant selected from the group formed by V2O5, CrO3, Nb2O5, MoO3, Ta2O5, WO3, and mixtures thereof, in a weighted quantity as expressed below:

Description

The invention relates to a fused cast refractory product with a high zirconia content. Refractory products include fused cast products, which are well known in the construction of glass-melting furnaces, and sintered products.

In contrast to sintered products such as those described, for example, in United States patent U.S. Pat. No. 4,507,394, fused cast products usually include an intergranular vitreous phase connecting together the crystalline grains. The problems posed by sintered products and by fused cast products, and the technical solutions adopted to overcome them thus generally differ. A composition that has been developed for the production of a sintered product is thus not, a priori, of use per se in producing a fused cast product, and vice versa.

Fused cast products, often termed electrofused products, are obtained by melting a mixture of appropriate starting materials in an electric arc furnace or by using any other technique that is suitable for such products. The molten liquid is then cast into a mold and the product obtained undergoes a controlled cooling cycle to bring it to ambient temperature without fracturing. This operation is termed “annealing” in the art.

Fused cast products include electrofused products with a high zirconia content, i.e. comprising more than 85% by weight of zirconia (ZrO₂); they are well known for their very good resistance to corrosion without coloring the glass produced and without generating defects.

Conventionally, fused cast products with a high zirconia content also include sodium oxide (Na₂O) to prevent the formation of zircon from the zirconia and silica present in the product. Zircon formation is in fact deleterious, since it is accompanied by a reduction in volume of the order of 20%, thus creating mechanical stresses that are the source of cracks.

The product ER-1195 produced and marketed by the Société Européenne des Produits Réfractaires and protected by European patent EP-B-0 403 387, is currently widely used in glass-melting furnaces. Its chemical composition comprises approximately 94% of zirconia, 4% to 5% of silica, approximately 1% of alumina, 0.3% of sodium oxide and less than 0.05% by weight of P₂O₅. It is typical of products with a high zirconia content that are used in glass furnaces.

French patent FR-A-2 701 022 describes fused cast products with a high zirconia content that contain 0.05% to 1.0% by weight of P₂O₅ and 0.05% to 1.0% by weight of boron oxide, B₂O₃. Said products have a high electrical resistivity. This can advantageously stabilize the consumption of electricity during electric melting of the glass and above all, this can overcome any problems with short circuiting in refractories, causing their rapid degradation. During electric melting of glass, some of the electric current passes through the refractory products. Thus, increasing the resistivity of said refractory products can reduce the quantity of electric current that passes through them.

International patent document WO-A-2005/068393 describes fused cast products with a high zirconia content with a high electrical resistivity while minimizing the quantities of BaO, SrO, MgO, CaO, P₂O₅, Na₂O, and K₂O. Said products contain 0.1% to 1.2% by weight of B₂O₃.

Japanese patent document JP 2000 302 560 describes fused cast products that do not contain Nb₂O₅ or Ta₂O₅.

The current trend for very high quality glass, in particular glass for LCD type flat screens, is increasing the demand for refractory products from glass-melting furnaces. In particular, there is a need for refractory products with further improved electrical resistivity while retaining good resistance to corrosion by the molten glass.

The aim of the present invention is to satisfy this need.

More particularly, it provides a fused cast refractory product with a high zirconia content comprising, as a percentage by weight based on the oxides and for a total of more than 98.5%, preferably more than 99% and more preferably more than 99.5%:

• • ZrO₂+Hf₂O: >85%;
  • SiO₂: >10% to 12%;
  • Al₂O₃: 0.1% to 2.4%;
  • B₂O₃: <1.5%; and
  • a dopant selected from the group formed by V₂O₅, CrO₃, Nb₂O₅, MoO₃, Ta₂O₅, WO₃, and mixtures thereof, in a weighted quantity as expressed in formula (1) below: 2.43V₂O₅+4.42CrO₃+1.66Nb₂O₅+3.07MoO₃+Ta₂O₅+1.91WO₃≧0.2%.

As can be seen below, surprisingly, the refractory product of the invention has a remarkable electrical resistivity while retaining good resistance to corrosion by molten glass.

Preferably, the refractory product of the invention also has one or, as is preferable, more of the following optional characteristics:

• • the weighted quantity of dopant is 0.5% or more, preferably 0.6% or more, more preferably 1.2% or more, and/or 3% or less, preferably 2.5% or less, more preferably 1.4% or less;
  • the total quantity of dopant is 0.05% or more, preferably 0.1% or more and/or 0.5% or less, preferably 0.4% or less, as a molar percentage based on the oxides;
  • the dopant is selected from V₂O₅, Nb₂O₅, Ta₂O₅, WO₃, and mixtures thereof, preferably from Nb₂O₅, Ta₂O₅ and mixtures thereof;
  • in one embodiment, the dopant is Nb₂O₅.

Preferably, the quantity by weight of Nb₂O₅ is more than 0.1%;

• • in a further embodiment, the dopant is a mixture of Nb₂O₅ and Ta₂O₅, the quantity of Nb₂O₅ being more than 0.1% and the quantity of Ta₂O₅ being more than 0.1%, as a percentage by weight based on the oxides;
  • the quantity of B₂O₃ is more than 0.05%, preferably more than 0.1%, more preferably more than 0.25%;
  • the quantity by weight of boron oxide B₂O₃ is 1.0% or less, preferably 0.8% or less;
  • the quantity of yttrium oxide Y₂O₃ is 1% or less, preferably 0.5% or less, more preferably 0.2% or less;
  • the quantity of alumina Al₂O₃ is 0.4% or more, preferably 0.5% or more, more preferably 0.6% or more and/or 1.5% or less, preferably 1% or less, more preferably 0.85% or less;
  • the quantity by weight of barium oxide, HaO, is 0.6% or less, preferably less than 0.5%;
  • the species other than ZrO₂+HfO₂, SiO₂, B₂O₃, Al₂O₃, Y₂O₃, BaO, and dopant (constituting the complement to 100%) represent, by weight, less than 1.5%, preferably less than 1%, and more preferably less than 0.5%;
  • the species other than ZrO₂+HfO₂, SiO₂, B₂O₃. Al₂O₃, Y₂O₃, and dopant (constituting the complement to 100%) represent, by weight, less than 1.5%, preferably less than 1%, and more preferably less than 0.5%;
  • the complement by weight to 100% is constituted by impurities;
  • the quantity of impurities (essentially oxides of iron, titanium, phosphorus, sodium, and calcium) is less than 0.6%, preferably less than 0.3%;
  • the quantity by weight of sodium oxide Na₂O is 0.1% or less, preferably 0.05% or less, more preferably 0.03% or less.

Advantageously, these characteristics can further improve the electrical resistivity and the corrosion resistance of the product of the invention.

The refractory product of the invention preferably has an electrical resistivity of 400 Ω.cm [ohm.centimeter] or more, more preferably 500 Ω.cm or more, still more preferably 600 Ω.cm or more at 1500° C. at a frequency of 100 Hz [hertz].

The invention also provides a glass-melting furnace including a refractory product in accordance with the invention or a refractory product that is produced or that may be produced using a method in accordance with the invention, in particular in regions intended to come into contact with molten glass. In the furnace of the invention, the refractory product may advantageously form part of a tank for the preparation of glass by melting, especially by electrical melting, where it is susceptible of coming into contact with molten glass at a temperature of more than 1200° C.

The refractory product of the invention is not intended to be brought into contact with molten glass at temperatures of less than 1100° C.

Finally, the invention provides a method of producing a refractory product in accordance with the invention, comprising the following steps in succession:

a) mixing starting materials, with the introduction of a dopant, to form a starting charge;

b) melting said starting charge until a molten liquid is obtained;

c) casting and solidifying said molten liquid by controlled cooling to obtain a refractory product;

said method being remarkable in that said starting materials are selected such that said refractory product is in accordance with the invention.

The “weighted” content or quantity of dopant designates here the quantity:

2.43V₂O₅+4.42CrO₃+1.66Nb₂O₅+3.07MoO₃+Ta₂O₅+1.91WO₃

in which the quantities of oxides are expressed as a percentage by weight.

Unless otherwise mentioned, all of the percentages in the present description are percentages by weight based on the oxides.

In the fused cast products of the invention, the high zirconia content, i.e. ZrO₂>7 85%, means that it can satisfy the demands for high corrosion-resistance without coloring the glass produced and without generating defects that are deleterious to the quality of said glass.

Hafnium oxide, HfO₂, present in the product of the invention is the hafnium oxide naturally present in sources of zirconia. Its quantity by weight in the product of the invention is thus 5% or less, generally 2% or less.

The presence of silica is necessary for the formation of an intergranular vitreous phase that can effectively accommodate variations in the volume of the zirconia during its reversible allotropic transformation, i.e. during passage from the monoclinic phase to the tetragonal phase. The silica content may be more than 10.1%, or even more than 10.5%.

The presence of alumina is necessary for the formation of a stable vitreous phase and for good castability of products into the mold. An excessive amount causes instability of the vitreous phase (crystal formation).

Yttrium oxide, Y₂O₃, has an unfavorable effect on electrical resistivity, but its presence can be accepted in a quantity of less than 1%, preferably less than 0.5%, more preferably less than 0.2%.

The presence of dopant in the products of the invention is necessary in order to improve the electrical resistivity. However, the total weighted content of said oxides must preferably not exceed 4% so that the percentage of zirconia is kept at a sufficiently high level to ensure excellent resistance to corrosion by the molten glass and to retain good stability in the vitreous phase.

The inventors have established that all the pentavalent dopants have a substantially identical effect at identical molar quantities. This is also true for all the hexavalent dopants. Furthermore, the inventors have observed that the molar efficiency of the hexavalent dopants M⁶⁺ is almost twice as great as that of the pentavalent dopants M⁵⁺. Without wishing to be bound by any particular theory, the inventors explain this difference by the role of dopants as regards oxygen voids in the zirconia. Hexavalent dopants M⁶⁺ would in fact compensate for two oxygen voids, as opposed to just one for pentavalent dopants M⁵⁺. One mole of an oxide of a pentavalent dopant M₂O₅ would thus have an identical effect to one mole of an oxide of a hexavalent dopant MoO₃.

Regarding the weighted quantity of dopant, the differences between the molar masses of the dopants should also be taken into account. Thus, 1.66 g [gram] of Ta₂O₅ has an equivalent effect to 1 g of Nb₂O₅.

The complement to 100% in the composition of the product of the invention is constituted by other species. The term “other species” means species that are not particularly desired, but that are generally present in the starting materials as impurities.

Examples that may be mentioned are alkaline oxides, in particular sodium oxide Na₂O and potassium oxide K₂O, which can be accepted but preferably must not exceed 0.5%, more preferably 0.1%, and more preferably be present in trace amounts only Otherwise, electrical resistivity would be degraded because of the increased conductivity of the vitreous phase. Oxides of iron, titanium, and phosphorus are known to be harmful, and their contents must be limited to traces introduced with the starting materials as impurities. Preferably, the quantity of Fe₂O₃+TiO₂ is less than 0.55%, and that of P₂O₅ is less than 0.05%.

A product of the invention may be produced by following steps a) to c) described below:

a) mixing starting materials, with the introduction of a dopant, to form a starting charge;

b) melting said starting charge until a molten liquid is obtained;

c) solidifying said molten liquid by controlled cooling to obtain a refractory product in accordance with the invention.

In step a), the dopant is added in a manner that guarantees the quantity of dopant in the finished product of the invention.

In step b), melting is preferably carried out by the combined action of a fairly long electric arc that does not cause reduction and stirring, favoring re-oxidation of the products. Melting is carried out at a temperature of more than 2300° C., preferably in the range 2400° C. to 2500° C.

To minimize the formation of nodules with a metallic appearance and to prevent the formation of apertures or crazing in the finished product, it is preferable to carry out melting under oxidizing conditions.

Preferably, a long arc fusion method is used as described in French patent FR-A-1 208 577 and its patents of addition, numbers 75893 and 82310.

That method consists in using an electric arc furnace the arc of which arcs between the charge and at least one electrode that is separated from said charge, and adjusting the length of the arc so that its reducing action is reduced to a minimum, while maintaining an oxidizing atmosphere above the melt and stirring said melt either by the action of the arc itself or by bubbling an oxidizing gas (air or oxygen, for example) into the melt or by adding to the melt substances which release oxygen, such as peroxides.

In step c), cooling is preferably carried out at a rate of less than 20° C. per hour, preferably at a rate of about 10° C. per hour.

Any conventional method of producing fused products based on zirconia intended for applications in glass-melting furnaces may be employed, provided that the composition of the starting charge allows products to be produced with a composition that is in accordance with that of the product of the invention.

As an example, the use of a continuous induction melting and solidification furnace, as described in FR-A-1 430 962, is possible and allows products to be produced that have a particularly homogeneous zirconia content.

The product of the invention is constituted by grains of zirconia more than 80%, more than 90%, more than 99% or substantially 100% of which are unstabilized monoclinic zirconia, surrounded by a vitreous phase that is more than 50%, more than 70%, or even more than 90% or substantially 100% constituted by silica, as a percentage by weight.

The products of the invention may advantageously be used in any other application which requires a refractory product with a high electrical resistivity.

Clearly, the present invention is not limited to the implementations described and represented by way of illustrative, non-limiting example.

The following non-limiting examples are given with the aim of illustrating the invention.

In these examples, the following starting materials were used:

• • zirconia principally containing, as a mean percentage by weight, 98.5% of ZrO₂+HfO₂, 0.2% of SiO₂ and 0.02% of Na₂O;
  • zircon sand containing 33% silica;
  • type AC44 alumina sold by Pechiney and containing a mean of 99.4% of alumina Al₂O₃;
  • oxides of barium, boron, yttrium, tantalum, Ta₂O₅, and niobium, Nb₂O₅, with a purity of more than 99%.

The examples were prepared using the conventional arc furnace melting method then cast to obtain blocks with a 220×450×150 mm [millimeter] format.

The chemical analysis of the products obtained is given in Table 1; it is a mean chemical analysis given as a percentage by weight with the exception of the column indicating the molar percentage of the sum of the oxides Ta₂O₅ and Nb₂O₅.

In this table, a blank entry corresponds to a quantity of 0.05% by weight or less.

The Na₂O content is not indicated; it was always less than 0.05% by weight.

In the various examples of blocks that were produced, cylindrical bars of the product that were 30 mm in diameter and 30 mm in height were subjected to a potential difference of 1 volt at a frequency of 100 Hz at 1500° C. to carry out the measurements of electrical resistivity R.

	TABLE 1
								Ta2O5 +
								Nb2O5	R
	ZrO2	SiO2	B2O3	Al2O3	Nb2O5	Y2O3	BaO	(mol %)	(Ω · cm)
1	87.6	10.2	0.53	0.53	0.80	0.19	0.10	0.33	813
2	87.4	10.8	0.89	0.54	0.20	0.18	0.03	0.08	1348
3	87.3	11.2	0.60	0.54	0.16	0.17	0.02	0.07	1165

Claims

1. A fused cast refractory product with a high zirconia content comprising, as a percentage by weight based on the oxides and for a total of more than 98.5%: ZrO2+Hf2O: >85%;SiO2: >10% to 12%;Al2O3: 0.1% to 2.4%;B2O3: <1.5%; anda dopant selected from the group formed by V2O5, CrO3, Nb2O5, MoO3, Ta2O5, WO3, and mixtures thereof, in a weighted quantity as expressed below: 2.43V2O5+4.42CrO3+1.66Nb2O5+3.07MoO3+Ta2O5+1.91WO3≧0.2%.

2. A refractory product according to claim 1, in which the weighted quantity of dopant is 0.5% or more and/or 3% or less.

3. A refractory product according to claim 1, in which the weighted quantity of dopant is 0.6% or more and/or 1.4% or less.

4. A refractory product according to claim 1, in which the dopant is selected from Nb2O5, Ta2O5, WO3, and mixtures thereof.

5. A refractory product according to claim 1, in which the dopant is selected from Nb2O5, Ta2O5 and mixtures thereof.

6. A refractory product according to claim 1, in which the quantity of B2O3 is more than 0.05% and/or less than 1%.

7. A refractory product according to claim 1, in which the quantity of B2O3 is more than 0.1%.

8. A refractory product according to claim 1, further including Y2O3, the quantity of Y2O3 being 1% or less.

9. A refractory product according to claim 1, in which the quantity of dopant is 0.05% or more and 0.4% or less, as a percentage by weight based on the oxides.

10. A refractory product according to claim 1, in which the silica content is more than 10.5%, as a percentage by weight based on the oxides.

11. A refractory product according to claim 1, in which the Y2O3 content is less than 0.5%, as a percentage by weight based on the oxides.

12. A refractory product according to claim 1, in which the alumina content (Al2O3) is 1% or less, as a percentage by weight based on the oxides.

13. A refractory product according to claim 1, in which the alumina (Al2O3) content is 0.85% or less, as a percentage by weight based on the oxides.

14. A refractory product according to claim 1, in which the alumina (Al2O3) content is 0.4% or more, as a percentage by weight based on the oxides.

15. A refractory product according to claim 1, further including Na2O, the Na2O content being less than 0.1%.

16. A refractory product according to claim 1, in which the Na2O content is 0.03% or less.

17. A method of producing a refractory product comprising the following steps in succession: a) mixing starting materials to form a starting charge;b) melting said starting charge until a molten liquid is obtained;c) casting and solidifying said molten liquid by controlled cooling, to obtain a refractory product;wherein said starting materials are selected such that said refractory product is in accordance with claim 1.

18. A method according to claim 17, in which melting is carried out under oxidizing conditions.

19. A method according to claim 17, in which melting is carried out using an induction furnace or using a long arc.

20. A method according to claim 17 in which, in step c), cooling is carried out at a rate of less than 20° C. per hour.

21. A glass-melting furnace, including a refractory product according to claim 1.

22. A furnace according to claim 21, said refractory product forming part of a tank for preparing glass by electrical melting, where it is susceptible of coming into contact with molten glass at a temperature of more than 1200° C.