Claims
- 1. In a method for regenerating a spent HDS catalyst having an alumina support by removing contaminating nickel and vanadium compounds therefrom while increasing the BET surface area and the pore diameter thereof to attain a porosity effective to allow the regenerated HDS catalyst to be reused as HDS catalyst, the steps of:
- (a) sulfiding the spend HDS catalyst by passing a total amount of hydrogen sulfide of at least about 60 cm.sup.3 per gram of spent HDS catalyst through the spent catalyst under elevated temperature selected in the range of about 400.degree. C. to about 700.degree. C. to obtain, after leaching, the increased BET surface area;
- (b) leaching the spent HDS catalyst obtained from step (a) in an acidic aqueous ferric ion containing solution at a temperature and for a time sufficient to remove an effective amount of the vanadium and nickel therefrom while increasing the pore diameter of the HDS catalyst; and
- (c) recovering regenerated catalyst from step (b) having porosity effective to allow the regenerated HDS catalyst to be reused.
- 2. In the method as defined in claim 1 wherein said spent HDS catalyst is a nickel/tungsten catalyst.
- 3. In the method as defined in claim 1 wherein said spent HDS catalyst is a cobalt/molybdenum catalyst.
- 4. In the method as defined in claim 1 wherein said spent HDS catalyst is a nickel/molybdenum catalyst.
- 5. In the method as defined in claim 1 wherein the spent HDS catalyst is washed with a solvent such as toluene, sieved and dried prior to step (a).
- 6. In the method as defined in claim 1 wherein the elevated temperature of step (a) is about 400.degree. C.
- 7. In the method as defined in claim 1 wherein the elevated temperture of step (a) is about 556.degree. C.
- 8. In the method as defined in claim 1 wherein the temperature and time of step (b) are about 100.degree. C. and about 20 minutes respectively.
- 9. The method of regenerating HDS catalysts having an alumina substrate and containing molybdenum oxide and an oxide of a metal selected from the group consisting of cobalt, tungsten and nickel as active catalytic components thereof, which HDS catalyst has become deactivated by contamination with vanadium and nickel compounds with consequent reduction in the BET surface area of the spent HDS catalyst, which includes the steps of:
- (a) sulfiding the deactivated HDS catalyst at elevated temperature in preparation for leaching contaminating nickel and vanadium therefrom to regenerate the spent HDS catalyst;
- (b) leaching the sulfided deactivated HDS catalyst of step (a) in an acidic aqueous leaching solution containing ferric ions to solubilize the contaminating nickel and vanadium compounds which have become sulfided in step (a);
- (c) recovering regenerated HDS catalyst from the leaching solution of step (b); and wherein
- step (a) is controlled to increase the BET surface area of the regenerated catalyst recovered in step (c) substantially as compared with the BET surface area of the deactivated HDS catalyst by controlling the temperature of step (a) to a temperature within the range of about 400.degree. C. to not more than about 700.degree. C.
- 10. The method as defined in claim 9 including the step of calcining the deactivated HDS catalyst at a temperature of about 400.degree. C. prior to the sulfiding of step (a).
- 11. The method as defined in claim 10 wherein the temperature of step (a) is controlled at about 556.degree. C.
- 12. The method as defined in claim 10 including the step of washing the deactivated HDS catalyst to remove oil therefrom prior to calcining.
- 13. The method as defined in claim 12 wherein the temperature of step (a) is controlled at about 556.degree. C.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of our copending application of Ser. No. 517,027, filed July 25, 1983, now U.S. Pat. No.4,559,313, issued Dec. 17, 1985 and which was itself a continuation-in-part of application Ser. No. 313,458 filed Oct. 21, 1981, now abandoned.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4559313 |
Myerson et al. |
Dec 1985 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
517027 |
Jul 1983 |
|
Parent |
313458 |
Oct 1981 |
|