The invention relates to fuel cells and, more particularly, to electrolyte-supported solid oxide fuel cells.
Direct conversion of chemical energy into electric energy, through use of fuel cells, is an important area of energy conversion technology. Among various types of fuel cells, the solid oxide fuel cell (SOFC) is of particular interest because operation of such fuel cells at high temperature allows direct use of natural gas as a fuel.
Fuel cells, including solid oxide fuel cells, have an electrolyte positioned between an anode and a cathode, and such a structure generates electric energy from fuel and oxidant as desired. In an electrolyte-supported SOFC, the electrolyte is the structure providing the mechanical integrity to the cell and the electrodes are held together structurally by the electrolyte.
The layers of a solid oxide fuel cell, that is, the electrolyte, anode and cathode, are typically quite thin. Thin electrolyte-supported cells, however, are subject to cracking during handling, assembly and operation because they have poor mechanical strength. While very thin electrolyte-supported cells (thickness <50 μm) may exhibit some amount of overall flexibility, local constraints (as with seals or ends) or during assembly and handling procedures can cause electrolyte fracture due to the poor strain tolerance of the ceramic electrolyte.
In addition, in an electrolyte-supported cell, electrodes are disposed and supported on the electrolyte, and these electrodes are also subject to cracking during operation.
Still further, strip-cell configuration involves positioning of via holes through the electrolyte so that communication can be established between adjacent elements of the assembly. These via holes can also experience cracking during operation.
Although these problems might dictate the use of a thicker electrolyte, this approach causes problems since the electrolyte thickness should be as small as possible in order to avoid high resistance to ion migration during electrochemical operation. The other option to decrease the resistance to ion migration is increasing the operating temperature which becomes impractical with metallic interconnects and current collectors.
Based upon the foregoing, it is clear that the need remains for improved electrolyte-supported solid oxide fuel cell structures.
It is therefore the primary object of the present invention to provide such structures.
Other objects and advantages of the present invention will appear hereinbelow.
In accordance with the present invention, the foregoing objects and advantages have been readily attained.
According to the invention, an electrode assembly for solid oxide fuel cells is provided which comprises an electrolyte member defining a cathode side and an anode side and having an active area and an edge portion; a cathode disposed on said cathode side; an anode disposed on said anode side; and at least one electrolyte support member positioned adjacent to said edge portion of said electrolyte and having an opening positioned over at least a portion of said active area.
The support member can advantageously be a frame on the edge portion of electrolyte material or other thermal expansion matched materials which can be laminated or bonded to the electrolyte.
In addition, ribs can advantageously be positioned extending between the outer frame portion of the support member, along via lines on the electrolyte, to further support the electrolyte without affecting the active area of same. These ribs can also be provided of electrolyte material or other thermal expansion matched materials, or can be either laminated, bonded or otherwise secured relative to the electrolyte as desired.
In accordance with a further aspect of the present invention, the ribs of the support member can be provided as a grid, which extends between the side edges of the frame of the support member, also along non-active portions of the electrolyte. In such cases, the coverage of the active area is optimized to provide adequate support with minimal loss in active area.
In accordance with a further aspect of the invention, the electrolyte member can advantageously be provided as a plurality of discrete electrolyte segments, and the frame can be positioned to define a plurality of openings wherein each electrolyte segment is positioned within a respective opening.
The electrode assembly in accordance with the present invention advantageously strengthens the electrolyte and associated structures so as to substantially reduce the risk of damage during handling and to increase resistance to damage during operation.
A detailed description of preferred embodiments of the present invention follows, with reference to the attached drawings, wherein:
The invention relates to solid oxide fuel cells and, more particularly, to reinforcing structures for solid oxide fuel cells which enhance the strength and resistance of the electrolyte and electrolyte-supported electrodes to damage during handling, operation and the like.
In accordance with the present invention, it has been found that reinforcement structures can be positioned on non-active portions of the electrolyte or with minimal loss of active area, so as to provide the electrolyte with enhanced resistance to damage while nevertheless maintaining efficiency of operation of the electrolyte at relatively low temperatures.
Referring also to
Electrolyte 12 can be provided of any material suitable for use as an electrolyte in a solid oxide fuel cell, which materials are well known to a person of ordinary skill in the art. In accordance with the present invention, it is preferred that electrolyte 12 be maintained as thin as possible, preferably having a thickness of less than about 150 microns, more preferably less than about 50 microns, and ideally about 20 microns. An electrolyte having such thicknesses can be operated at temperatures which are relatively low, for example less than about 800° C., without sacrificing efficiency due to increased resistance of the electrolyte.
Support member 32 in this embodiment is provided as an outside edge or frame defined by side members 34 which define an opening 36 through which active area 24 of electrolyte 12 is exposed. Support member 32 can advantageously be provided having a thickness of less than about 10 mm, preferably less than about 5 mm, and ideally about 1 mm, and such thickness advantageously serves to increase strength of edge portion 26 of electrolyte 12 as desired.
Support member 32 can advantageously be provided of electrolyte material, and may be laminated or otherwise secured to electrolyte 12 as desired. Thus, support member 32 can advantageously be provided of the same or at least similar material to electrolyte 12.
Alternatively, and as further discussed below, support member 32 can be provided from a different material and bonded or otherwise secured to electrolyte 12, so long as the material is preferably selected to have substantially similar coefficient of thermal expansion (CTE) as electrolyte 12. Other materials for this embodiment of the present invention include ferritic stainless steels, barium titanates, chromium-based alloys as well as combinations of metals and ceramics that produce similar CTE as the electrolyte.
In accordance with a further aspect of the present invention, and referring to
Another problem which exists when utilizing relatively thin electrolytes in solid oxide fuel cells is that operation of the fuel cell at the desired parameter can generate a relatively large pressure difference across the electrolyte. Although the side reinforcement aspect of support member 32 as described above can enhance resistance of the electrolyte to edge cracking and the like, it may be desirable to provide further reinforcement to electrolyte 12.
As set forth above, electrolyte 12 typically has via lines 22 which serve to provide for proper functioning of a strip cell configuration as is well known to a person of ordinary skill in the art. These via lines are not a part of the active area of the electrolyte, and can be reinforced without reducing the active area of the cell. Thus, in accordance with the embodiment of the present invention as illustrated in
Ribs 42 add more stiffness to the electrolyte, further improving durability and handleability, and such configuration does not reduce cell active area because ribs 42 are positioned on via lines. In addition, reinforcing via lines decreases permeability of the vias and also increase integrity of the vias themselves.
It should be appreciated that support member 32 as illustrated in the drawings of the present application is shown being positioned on both sides of electrolyte 12. It may be desirable to utilize a single support member 32, positioned only on one side of electrolyte 12, and such a configuration falls completely within the broad scope of the present invention.
In accordance with a still further aspect of the present invention, support for a central portion of electrolyte 12 can be provided as a grid member such as is illustrated in
The grid members may provide reinforcement on one side or both sides of the cell and may be made of CTE matched materials preferably having insulating properties, or coated with insulating materials. The grid can be advantageously provided with grid openings from 0.01 mm to 50 mm and grid thicknesses from 0.001 mm to 5 mm.
The grids may be made of materials such as wire weaves or mesh with symmetric or non-symmetric openings or of foams with random openings.
One preferred example is the use of ferritic stainless steels with alumina forming compositions or alumina coated ferritic stainless steel as a material to make the wire weave or foams. Another preferred material is zirconia foam.
In these examples a small amount of active surface area is lost for significant durability improvements.
It should readily be appreciated that the present invention has provided reinforcement structures for electrolytes of thin electrolyte-supported solid oxide fuel cell assemblies, and these reinforcement structures greatly reduce the possibility of damage or cracking of edges, via lines and the like during handling and use of the electrode assembly. The present invention is well suited for use with reinforcement members provided of substantially the same material as the electrolyte, or alternatively in connection with use of reinforcement members provided from a substantially CTE-matched materials. Further, the invention is particularly well suited to materials which can be laminated to the electrolyte, or bonded to the electrolyte, or formed into the electrolyte, or which can be provided using other methods.
It is to be understood that the invention is not limited to the illustrations described and shown herein, which are deemed to be merely illustrative of the best modes of carrying out the invention, and which are susceptible of modification of form, size, arrangement of parts and details of operation. The invention rather is intended to encompass all such modifications which are within its spirit and scope as defined by the claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5856035 | Khandkar et al. | Jan 1999 | A |
| 6224993 | Hartvigsen et al. | May 2001 | B1 |
| 20040028975 | Badding et al. | Feb 2004 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20050191536 A1 | Sep 2005 | US |