Removal of acetaldehyde from hydrocarbons

Abstract

Acetaldehyde is removed from C.sub.3 -C.sub.15 hydrocarbons by contacting the hydrocarbon or a hydrocarbon mixture in liquid phase with a zeolite whose pores have a width which is greater than 0.3 nm and up to 0.75 nm.

Description

The present invention relates to a process for removing acetaldehyde from C.sub.3 -C.sub.15 hydrocarbons.

The thermal or thermal/catalytic cracking of natural gas, refinery gas or certain petroleum fractions, as is carried out, for example, in steam crackers, results, after workup of the products, in, among other things, mixtures of butadiene, butanes, 1- and 2-butenes and isobutene, which are generally called C.sub.4 cuts (Weissermel, Arpe, Industrielle Organische Chemie, Verlag Chemie 1988, p. 68 ).

These C.sub.4 cuts contain traces of acetaidehyde. Extraction of butadiene from the C.sub.4 cut also removes acetaldehyde from the remaining hydrocarbons, called the raffinate. If, however, the C.sub.4 cut is further processed by, for example, selective hydrogenation of butadiene to butene, the acetaldehyde is not removed. Acetaldehyde is in principle unwanted in hydrocarbons, being capable, among other things, of inactivating the catalysts used in the further processing of C.sub.4 cuts.

SU-A 1011624 discloses a process for removing carbonyl impurities from gaseous isobutene streams by adsorption onto a magnesium A zeolite (Mg A zeolite).

The adsorption of pure gaseous acetaidehyde onto a sodium A zeolite is described in J. Chem. Soc. Faraday Trans. 86 (1990) 205 in connection with infrared investigations.

It is an object of the present invention to provide a process which separates acetaldehyde from hydrocarbons with maximum selectivity and economy.

We have found that this object is achieved by a process for removing acetaldehyde from C.sub.3 -C.sub.4 hydrocarbons, which comprises contacting the hydrocarbon or a hydrocarbon mixture in liquid phase with a zeolite whose pores have a width which is greater than 0.3 nm and up to 0.75 nm.

The acetaldehyde is adsorbed onto zeolites. Zeolites are also called molecular sieves and are crystalline aluminosilicates which have a highly ordered structure with a rigid three-dimensional network of SiO.sub.4 and AlO.sub.4 tetrahedra which are linked by shared oxygen atoms. The charge on the aluminum-containing tetrahedra is balanced by inclusion of cations in the crystal, e.g. alkali metal or hydrogen ions. Cation exchange is possible. The zeolites may also contain in place of aluminum in the lattice other elements such as B, Ga, Fe, Cr, V, As, Sb, Bi or Be or mixtures thereof, and the silicon may also be replaced by another tetravalent element such as Ge, Ti, Zr or Hr.

Suitable zeolites for the process according to the invention have pores with a width which is greater than 0.3 and up to 0.75 nm. This width is determined by the crystal structure and can be determined, for example, from X-ray data. The diffusion of acetaldehyde into zeolites with smaller pores is, because of its size, only poor, and thus it cannot be satisfactorily adsorbed. Zeolites of the A, L, X and Y types are preferred, and those of the A and X types are particularly preferred. Sodium zeolites are very particularly preferred.

Na A zeolites with pores 0.4 nm wide are particularly suitable for removing acetaldehyde from mixtures of propene, butane, 2-butene and butadiene. If the acetaldehyde is mixed only with branched hydrocarbons such as isobutane or isobutene, it is particularly advantageous to use an Na A zeolite or to replace the Na A zeolite partly or entirely by alkaline earth metal A zeolites such as Ca A zeolites.

The zeolites are prepared by conventional methods (eg. Ullmanns Encyclopadie d. Techn. Chemie, 4th edition, Vol. 17, (1983) pp. 9-17). The zeolites can, after removal of trapped water by calcining, be shaped to strands or tablets with binders. Suitable binders are aluminas, silica, mixtures of highly disperse SiO.sub.2 with Al.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 or clay.

The process according to the invention makes it possible to remove acetaldehyde from hydrocarbons which have from 3 to 15 carbon atoms. Smaller hydrocarbons are so similar in size to acetaldehyde that they compete for adsorption in the zeolite. The hydrocarbons comprise alkanes such as propane, n-butane, isobutane, n-pentane, 2-methylbutane, 3-methylbutane, alkenes such as propene, 1-butene, 2-butene, 1-pentene, cyclohexene as well as 1,3-butadiene, alkynes and aromatic compounds such as benzene, toluene, o-xylene, m-xylene and p-xylene. The process is particularly important for treating C.sub.4 cuts, from which butadiene can have already been removed, and for isobutene.

The process according to the invention is particularly advantageous for removing acetaldehyde in amounts of from 10 to 500 ppm, as are present in C.sub.4 cuts, for example. However, it is also able to reduce higher acetaldehyde concentrations in the range up to 50,000 ppm (5% by weight).

The process according to the invention is, as a rule, carried out at from -10 to 60.degree. C., preferably from 15 to 35.degree. C. Lower temperatures are too costly for large streams, while at higher temperatures the adsorption capacity of the zeolites decreases markedly.

The pressure is chosen so that the hydrocarbons to be purified are liquid. The pressure is generally from 1 to 70, preferably from 5 to 35, bar. It is advantageous to use the pressure under which the hydrocarbon is liquid on production, e.g. by petroleura cracking.

It has proven advantageous in the treatment of large product streams to employ the zeolite in the form of a fixed bed in an adsorption column, through which the hydrocarbon is passed. The hydrocarbon to be treated is passed through the column in an ascending or descending manner. The height of the bed is preferably from 2 to 15 times the diameter of the bed. It is recommended that the linear velocity of the liquid cross-section, calculated from the ratio of the volume flow to the cross-section of the adsorber bed, is from 0.5 to 35 cm/min, preferably from 1 to 15 cm/min and, in particular, from 1.5 to 10 cm/min.

Once the zeolite is saturated it can be regenerated by passing over an inert gas such as nitrogen under atmospheric pressure and at from 150 to 250.degree. C, which takes about 4-12 hours.

For continuous operation, it is expedient to provide two adsorption columns, one for adsorption and the other for desorption (regeneration). It is also possible for a plurality of adsorption columns to be arranged in parallel on this principle.

The process according to the invention makes it possible to remove acetaldehyde from C.sub.3 -C.sub.4 hydrocarbons down to a residual content of less than 1 ppm. Such a content does not, as a rule, interfere with the use the further processing of the hydrocarbons. The zeolite used for this purpose is easy to regenerate. Furthermore, traces of water can also be removed from the hydrocarbons by adsorption.

EXAMPLES

Hydrocarbons with particular acetaldehyde concentrations were passed over zeolites. The acetaldehyde concentration was measured at various times after adsorption. Details are to be found in the following Table.

TABLE__________________________________________________________________________ Pore width Amount of zeolite Bed length/Example Zeolite [nm] [kg] diameter Hydrocarbon__________________________________________________________________________1 Na A 0.4 196 3.6 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene2 Na A 0.4 521 5 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene3 Na A 0.4 0.039 14 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene4 Ca A 0.5 0.038 14 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene5 Ca X 0.75 0.035 14 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene6 Na A 0.4 52 2.5 isobuteneComparative K A 0.3 252 3.6 8.6% by weight n-butane 4.1% by weight isobutane 26.0% by weight isobutene 33.0% by weight 1-butene 28.3% by weight 2-butene__________________________________________________________________________ __________________________________________________________________________ Acetaldehyde content Temperature T Pressure p Linear velocity before adsorption after adsorptionExample [.degree.C.] [bar] [cm/min] [ppm] [ppm]__________________________________________________________________________1 25 19 6.9 260 after 1 h: <1 after 3 h: 1.3 after 6.5 h: 4.22 27 18 4.1 195 after 2 h: 1.1 after 9 h: 0.14 after 17 h: 0.283 35 5 1.7 40,000 after 3.5 h: <14 35 5 1.7 40,000 after 3.5 h: <15 35 5 1.7 40,000 after 2 h: <1 after 3 h: <1 after 3.5 h: 9.16 23 14 2.7 270 after 255 h: <2 (water: 47 ppm) (<5)Comparative 27 18 6.9 250 after 0.5 h: 3 after 3.5 h: 59 after 12 h: 129 after 26 h: 164__________________________________________________________________________

Claims

1. A process for removing acetaldehyde from C.sub.3 -C.sub.15 hydrocarbons, which comprises contacting the C.sub.3 -C.sub.15 or a hydrocarbon mixture of C.sub.3 -C.sub.15 hydrocarbon in liquid phase with a zeolite whose pores have a width which is greater than 0.3 nm and up to 0.75 nm.

2. A process as defined in claim 1, wherein the zeolite is an A or X zeolite.

3. A process as defined in claim 1, wherein an acetaldehyde-containing mixture of butanes, 1- and 2-butenes and isobutene is contacted with the zeolite.

4. A process as defined in claim 2, wherein an acetaldehyde-containing mixture of butanes, 1- and 2-butenes and isobutene is contacted with the zeolite.

5. A process as defined in claim 1, wherein acetaldehyde-containing isobutene is contacted with the zeolite.

6. A process as defined in claim 2, wherein acetaldehyde-containing isobutene is contacted with the zeolite.

7. A process as defined in claim 1, wherein the zeolite is an Na A zeolite with pores about 0.4 nm wide.