The present disclosure relates generally to the repair of pipes and more particularly to methods and systems for pipe repair in which holes in the pipe are patched.
Over time or because of a particular event or condition (e.g., seismic activity, exposure to excessive or uneven loads or moments, exposure to micro-organisms, poor compaction, crown corrosion, corrosive soil, etc.), the structural integrity or capacity of force mains, other pipes and other structures may diminish. For example, such items may crack, corrode, deteriorate and the like. Different methods of repairing or otherwise strengthening damaged pipes and other items are well-known. For example, liners or sheets made of fiber reinforced polymers can be attached to one or more portions of a pipe interior. Among other ways, liners of this type can be formed in a tubular shape and dragged in or everted into the pipe to be repaired. Still further, in larger diameter pipes, the lining may be formed by manually adhering sheets of repair material to the walls of the pipe.
Repair of buried or underground pipes in the manner described is hindered by groundwater infiltration. In many instances repair cannot proceed until groundwater infiltration is halted, at least temporarily. The conventional solution for metal pipes was to use welding to block holes or openings in the pipe (e.g., cracks or voids in the pipe side wall) that were allowing groundwater infiltration. However, this process is very time consuming and expensive. Other methods, such as simply stuffing material (e.g. pieces of wood, grout, gels or adhesives without any reinforcement) into pipe openings are unreliable.
In one aspect, a method of repairing a section of a pipe including a breach in the pipe comprises preparing a surface of a wall of the pipe generally around the breach. A piece of conformable material of the type capable of carrying a curable polymer is sized in relation to a size of the breach. The sized piece of conformable material is applied to the prepared surface so that the breach is covered by the piece of conformable material. The piece of conformable material is impregnated with a curable polymer. The curable polymer is cured within the piece of conformable material thereby to seal the breach against egress of groundwater into the pipe.
In another aspect, a repaired pipe having a breach in the side wall closed by the repair comprises a conditioned surface around the breach. Adhesive is applied to the conditioned surface. A piece of fiber reinforced polymer material is cured over the breach and joined to the side wall of the pipe at least in part by the adhesive. The piece of fiber reinforced polymer material seals the breach against egress of groundwater into the pipe. The piece of reinforced polymer material is sized to cover the breach.
Other aspects and features will also be apparent in view of the included drawings, description, and claims.
Corresponding reference characters indicate corresponding parts throughout the several views of the drawings.
Referring now to the drawings, a pipe 1 in need of repair shown schematically in
Repair of the opening 3 in the pipe 1 may be temporary until a more universal repair of the pipe is accomplished, or could be a longer term repair. According to a process of the present invention, a portion of the internal wall of the pipe 1 around the opening 3 is prepared for bonding in a suitable manner. For example, the internal wall portion is conditioned to facilitate bonding of a material to the wall with an epoxy or other suitable adhesive. Other portions of the pipe near the opening 3 are not required to be finished. In one embodiment, the internal wall portion is brought to a near white finish. This may be accomplished by abrasive blasting, mechanical grinding, hand sanding or by other suitable processes or combination of processes. The materials used to accomplish the finish of the internal wall portion may be broadly referred to as “abraders.” The internal wall portion is then roughened and then cleaned. Surface roughening can be carried out by hand or with other mechanical assistance. For example, roughening can be achieved using high pressure water blasting, sand blasting, with a grinding wheel, wire brush or by other suitable techniques. Surface cleaning can be as simple as wiping with rags, vacuuming or broom cleaning In other embodiments, solvents may be used or other special chemicals when, for example, reduction of chlorides or other contaminants is needed. Prior to conditioning the internal wall portion surrounding the opening 3, a stopgap seal of the opening may be employed. For example conformable materials may be forced by hand into the opening to achieve a momentary stoppage of infiltration.
After the internal wall portion surrounding the opening 3 is cleaned and dry, a prime coat of adhesive is applied to the internal wall portion. For example an epoxy may be used. Preferably, the epoxy should be one that forms a liquid barrier at least in any interstices of a fabric to which is it applied for use in forming an unbroken liquid barrier. The epoxy also needs to prevent liquid from moving laterally across the fabric, which could result in leakage around the fabric. One example of a suitable epoxy is Tyfo® S epoxy available from Fyfe Co. LLC of San Diego, Calif. However, it will be understood that other suitable materials could be used within the scope of the present invention.
A first piece of fabric 5 capable of holding a hardening or curable material is sized in relation to the size of the opening 3 to cover the opening, but is not sized for lining the entire pipe. In most cases, that means the first piece of fabric 5 is sized much smaller than the circumference of the pipe at the location of the opening 3. After the prime coat is applied, the first fabric piece 5 is applied over the opening 3 and against the internal wall portion next to the opening on the prime coat. Preferably the application occurs while the prime coat is still tacky. In one embodiment, the fabric is a fiber ladened woven fabric or chopped strand mat of glass fibers or other suitable fibrous materials (e.g., carbon fibers, basalt fibers, aramid fibers, ultra-high molecular weight polyethylene fibers, or other, preferably non-conductive fibers, etc.). A suitable multi-axial fabric comprises a woven fabric. In one or more embodiments, the woven fabric is a bi-directional woven fabric with warp and weft fibers generally oriented perpendicular to one another (e.g., 0°/90°, 45°/−45°, etc.). A suitable bi-directional fabric material may include more or stronger fibers oriented in one direction (e.g., the warp direction) than the other direction (e.g., the weft direction). For purposes of the present application the direction including more and/or stronger fibers, whether warp, weft or any other orientation within the fabric material, may be referred to as the “strong direction” of the fabric material. Other bi-directional materials include substantially the same amount of fibers in the warp and weft directions without departing from the scope of the invention. In a preferred embodiment of a woven multi-axial fabric, the fabric sheet 5 has a satin or twill weave. For example, a suitable weave is one in which the weft floats or skips over as many as 12 warps before being woven in to the weave. The next pick repeats the float, but on a different set of warps. Generally the material will be at least minimally conformable to the surface (e.g., the interior of a pipe) to which it is applied. However, “conformable” includes semi-rigid materials. Preferably, the material is configured to hold at least some hardenable material in such a fashion that the hardenable material (e.g., epoxy) can fill in any void spaces in the fabric. The fabric can be treated with a sizing to improve the bond of the glass fiber to the epoxy. One example of a suitable material is Tyfo® WEB reinforcing fabric available from Fyfe Co. LLC of San Diego, Calif. Tyfo® WEB reinforcing fabric is a satin woven glass fabric in which each weft bundle of glass fibers floats over three adjacent warp bundles of glass fibers. Materials of this construction have good resistance to penetration by liquids.
The first fabric piece 5 is impregnated (e.g., saturated) with a hardenable polymer or other hardenable material to form a fiber reinforced composite. Preferably, the fabric 5 is impregnated such that the hardenable material fills substantially all of the void spaces in the fabric. In a preferred embodiment, the first fabric piece 5 is impregnated prior to being placed against the internal wall portion surrounding the opening 3. However, the fabric piece 5 could be placed against the primer coat on the internal wall portion dry and then impregnated within the scope of the present invention. In a still further embodiment, the fabric piece 5 may not be impregnated with resin at any point in the process. One example of a suitable hardenable polymer is an epoxy. One such epoxy is Tyfo® S epoxy available from Fyfe Co. LLC of San Diego Calif. Use of Tyfo® S epoxy as both the primer coat and the hardenable polymer has been found effective. However, it will be appreciated by those of ordinary skill in the art that different materials may be used for the primer coat and for the hardenable polymer within the scope of the present invention.
As illustrated in
The impregnated fabric pieces 5, 7 can be allowed to cure in the air or more rapidly cured using heat, UV or other curing stimulant. As cured, the epoxy and fabric pieces 5, 7 provide a strong and liquid tight covering for the opening 3, preventing further infiltration of groundwater into the pipe 1. This allows a more universal repair of the pipe 1 to be carried out in optimum (e.g., dry) conditions conducive to the best overall repair result. For example, other pieces of curable materials (not shown) may be applied to the internal or external walls of the pipe 1 in such a manner as to completely line the interior of the pipe. An example of a suitable system for overall repair of the pipe is shown in U.S. Pat. No. 5,931,198. This material can be applied over the fabric pieces 5, 7. It is also possible to form material into a tube and drag or evert the tube into the pipe 1. The tube of material can be impregnated with a hardenable polymer and cured in the pipe in manner well known to those of ordinary skill in the art.
Referring to
Each test system 100 includes a generally square steel plate 110, which is designed to function like the wall of the pipe 1. The plate 110 has a length and width of about 12 inches (about 30.48 cm), respectively, and a thickness of about 0.375 inches (about 0.953 cm). A test slot 112, which is configured to function like a relatively large void in the wall of the pipe 1, extends through the thickness of the plate 110. The slot 112 has a length of about 6 inches (about 15.24 cm) and a width of about 0.75 inches (about 1.905 cm). The plate 110 is secured by a liquid tight connection to one end of a cylinder 114 so that the slot 112 is fluidly coupled to the interior of the cylinder. The cylinder has in interior diameter of about 6 inches (about 15.24 cm) and is arranged relative the plate 110 so that the slot 112 is centered diametrically at one end of the cylinder interior. The cylinder 114 is adapted to be at least partially filled with water and includes a compressed air fitting 116 opposite the plate 110.
Having described the structure of the illustrated test system 100, the steps testing technicians performed to construct suitable coverings over the slots 112 of six test systems 100 and to test the liquid tightness of the coverings will now be briefly described. Before placing the covering over each of the slots 112, the technicians prepared the surfaces of the plates 110 opposite the cylinders 114 and applied prime coats of Tyfo® S epoxy. For each of the six test systems 100, the technicians cut a first rectangular shaped piece 5 of Tyfo® Web fabric to a length of about 12 inches (about 30.48 cm) and a width of about 6 inches (about 15.24 cm). While the prime coat was still tacky, the technicians impregnated the first pieces of fabric 5 with Tyfo® S epoxy and applied each to a respective plate 110 in a centered position in which the longitudinal ends of the sheet were substantially aligned with opposite sides of the plate and the length of the fabric sheet was oriented substantially parallel to the length of the slot 112. In this position, the fabric sheet 5 completely covered the slot 112. The fibers in the piece of fabric 5 are arranged so as to intersect the sides of the sheet at an angle of about 90°. The piece of fabric 5 is applied over the slot 112 so that the fibers make an angle of 90° with respect to a longitudinal axis of the slot. The technicians also cut a second, substantially square sheet fabric sheet of Tyfo® Web fabric 7 measuring about 12 inches (about 30.48 cm) between opposite corners. The technicians impregnated the second pieces with Tyfo® S epoxy and subsequently applied each to a respective plate 110 in a centered position in which the corners of the sheet were substantially aligned with the sides of the plate. As applied to the plates 110, the second pieces of fabric 7 substantially covered the slots 112. The fibers of the second piece of fabric 7 are oriented at right angles with respect to the edges of the piece of fabric. As applied to the plate 110, the bidirectional fibers of the fabric 7 make angles of ±45° with respect to the longitudinal axis of the slot 112. The piece of fabric 7 was applied so that the direction in which the fibers are strongest is oriented at 45° with respect to the direction in which the fibers are strongest in the piece of fabric 5. After applying the first and second pieces of fabric 5, 7 to each plate, the epoxy was allowed to cure at ambient conditions for a minimum of 72 hours. Once the epoxy cured, the pieces of fabric 5, 7 formed an exemplary liquid tight covering over the slot 112.
After the coverings were applied over the slots 112 of each of the six test systems 100, the liquid tightness of the coverings was tested. The cylinders 114 of each of the test samples were partially filled with deionized water. The fluid inside four of the ten cylinders 114 was pressurized to an internal pressure of about 50 psi (about 345 kPa), and the fluid inside the other two cylinders was pressurized to an internal pressure of 100 psi (about 689 kPa). The technicians placed each of the test systems 110 in a holding facility for a period of 7 days. A temperature monitoring system continuously monitored the environmental temperature throughout the seven-day period, and a humidity monitoring system provided daily recordings of the humidity in the holding facility. During the seven day holding period, the patches of both the 50 psi test systems and the 100 psi test systems showed no signs of leakage. Due to environmental changes over the seven day period, the internal pressures of each of the 50 psi cylinders decreased by about 2-3 psi (about 13.79-20.68 kPa) per day and the internal pressures of each of the 100 psi cylinders decreased by about 5-7 psi (about 34.47-48.26 kPa) per day. To maintain substantially constant fluid pressures throughout the seven-day holding period, the technicians added pressure to each of the cylinders 114 on a daily basis. The results of the seven day holding period testing indicated that the coverings were substantially liquid tight at fluid pressures of about 50 psi (about 345 kPa) for a period of seven days. Likewise, the results of the seven day holding period testing indicated that the coverings were substantially liquid tight at fluid pressures of about 100 psi (about 689 kPa) for a period of seven days.
Once the seven day holding period ended, the technicians performed burst testing on each of the six test systems 100. During burst testing, the fluid pressure in each of the cylinders 114 was slowly increased until the covering over the slots 112 failed and the water contained in the cylinders escaped through the slots. The pressure at which the coverings ruptured was recorded as the burst pressure for the sample. As shown in Table 1 below, the patches provided by the first and second fabric sheets 5, 7 remained watertight up to a fluid pressure of at least about 290 psi (about 2000 kPa).
The systems, apparatuses, devices and/or other articles disclosed herein may be formed through any suitable means. The various methods and techniques described above provide a number of ways to carry out the inventions. Of course, it is to be understood that not necessarily all objectives or advantages described may be achieved in accordance with any particular embodiment described herein. Thus, for example, those skilled in the art will recognize that the methods may be performed in a manner that achieves or optimizes one advantage or group of advantages as taught herein without necessarily achieving other objectives or advantages as may be taught or suggested herein.
Furthermore, the skilled artisan will recognize the interchangeability of various features from different embodiments disclosed herein. Similarly, the various features and steps discussed above, as well as other known equivalents for each such feature or step, can be mixed and matched by one of ordinary skill in this art to perform methods in accordance with principles described herein. Additionally, the methods which are described and illustrated herein are not limited to the exact sequence of acts described, nor are they necessarily limited to the practice of all of the acts set forth. Other sequences of events or acts, or less than all of the events, or simultaneous occurrence of the events, may be utilized in practicing the embodiments of the invention.
Although the inventions have been disclosed in the context of certain embodiments and examples, it will be understood by those skilled in the art that the inventions extend beyond the specifically disclosed embodiments to other alternative embodiments and/or uses and obvious modifications and equivalents thereof. Accordingly, it is not intended that the inventions be limited, except as by the appended claims.
The present application claims priority to U.S. Provisional Patent Application Ser. No. 62/012,762, entitled REPAIR OF PIPES, which is hereby incorporated by reference into the present disclosure.