Patent Application
20240209238
This application claims the benefit of priority under 35 U.S.C. 119(a) of European Patent Application No. 22216244.8, filed Dec. 22, 2022, the entire disclosure of which is incorporated herein by reference for all purposes.
The present disclosure concerns a paper-based backing layer. The backing layer comprises several layers, inter alia a paper layer, and a barrier coating layer, which may comprise polymers and inorganic fillers. The backing layer may be used in tapes, labels and related products.
Paper-based backing layers form the backbone of various tapes (closing tapes, opening tapes (e.g. tear tapes) and reinforcing tapes), labels and related products, on which prints may be applied. The paper-based backing layers often include several coatings applied in layers on a paper carrier.
As the tapes, labels and related products are attached to cardboard boxes, letters, envelopes and the like, the entire materials are subjected to recycling processes. In recycling processes the materials are fed into a pulper and treated mechanically in water having neutral to alkaline pH to achieve disintegration of paper to cellulose fibres. This is followed by several purification steps such as sieving and flotation, finally affording a slurry comprising cellulose fibres. The slurry is expected to satisfy the requirements for feeding into a paper-making machine.
During the processing of cellulose slurries derived from recycled paper on paper-making machines, interruptions and down-times of machinery occur frequently. This reduces the efficiency of the recycling process.
The interruptions are caused by so-called “stickies”, which are agglomerations or even lumps of sticky polymers, which originate from coatings applied on paper carriers and could not be removed from cellulose fibers during purification of the cellulose slurry. Stickies are noticeable as fatty spots on recycled paper sheets. They are responsible for sheets of recycled paper sticking together. Stickies attach to rollers and thereby affect the quality of a paper web during production, thereby reducing efficiency of production and increasing production costs.
A certain proportion of agglomerations and lumps of sticky polymers is separated from the slurry during purification by way of sieves, screens and filters. However, purification is incomplete. In addition, the removed agglomerations and lumps of sticky polymers are not recyclable. They end up in the waste stream to be landfilled or burned. This shall be avoided from the point of view of environmental protection.
Thus, even comprising a paper-based backing layer, conventional tapes, labels and related products can be recycled only to an unsatisfactory extent.
Recyclability may be measured as per the “Voluntary Standard For Repulping and Recycling Corrugated Fiberboard Treated to Improve Its Performance in the Presence of Water and Water Vapor” (revised Aug. 16, 2013) published by the Fibre Box Association (FBA), USA, which comprises guidelines for measuring fibre recyclability and the proportion of stickies contents of a recycled product. The Standard sets a requirement of at least 85% of fiber recyclability, based on bone dry fiber charged to a pulper; and a sticky proportion of 15 or lower.
Conventional paper-based backing layers presents values of around % of fiber recyclability and a sticky proportion of around and higher than 100. From the view point of production efficiency and environmental pollution, these values are disadvantageous.
Therefore there is a need in the art to provide a paper-based backing layer that presents improved recyclability and improved production efficiency. Such paper-based backing layer is expected to exhibit a fiber recyclability of at least 85% and a sticky proportion of lower than 15, preferably lower than 5, as determined by aforesaid Voluntary Standard.
The present disclosure concerns a paper-based backing layer.
The present disclosure provides a backing layer comprising
The present disclosure also provides an adhesive tape comprising the above backing layer.
The backing layer of the present disclosure passes the stringent criteria of the “Voluntary Standard For Repulping and Recycling Corrugated Fiberboard Treated to Improve Its Performance in the Presence of Water and Water Vapor” (revised Aug. 16, 2013) published by the Fibre Box Association (FBA), USA. The backing layer presents advantageous fibre recyclability and stickies count having a very high extent of repulpability. The backing layer shows improved production efficiency and reduced ecological footprint. As such it is advantageous and instrumental in improving production efficiency and ecological footprint of conventional tapes, labels and related products.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate several embodiments and together with the description serve to explain certain principles.
Further aspects, features and advantages of the exemplary embodiments will become apparent from the detailed description which follows.
The patents, published applications and scientific literature referred to herein establish the knowledge of those with skill in the art and are hereby incorporated by reference in their entireties to the same extent as if each was specifically and individually indicated to be incorporated by reference.
As used herein, whether in a transitional phrase or in the body of a claim, the terms “comprise(s)” and “comprising” are to be interpreted as having an open-ended meaning. That is, the terms are to be interpreted synonymously with the phrases “having at least” or “including at least”. When used in the context of a method, the term “comprising” means that the method includes at least the recited steps, but may include additional steps. When used in the context of a composition, the term “comprising” means that the composition includes at least the recited features or components, but may also include additional features or components.
The terms “consists essentially of” or “consisting essentially of” have a partially closed meaning, that is, they do not permit inclusion of steps or features or components which would substantially change the essential characteristics of a method or composition; for example, steps or features or components which would significantly interfere with the desired properties of the compounds or compositions described herein, i.e., the method or composition is limited to the specified steps or materials and those which do not materially affect the basic and novel characteristics of the method or composition. The terms “consists of” and “consists” are closed terminology and allow only for the inclusion of the recited steps or features or components.
As used herein, the singular forms “a,” “an” and “the” specifically also encompass the plural forms of the terms to which they refer, unless the content clearly dictates otherwise.
The term “dissolved” or “substantially dissolved” is used herein to mean the solubilization of a solid in a solution. It can be considered that a solid is “dissolved” or “substantially dissolved” in a solution when the resulting solution is clear or substantially clear.
As used herein, the recitation of a numerical range for a variable is intended to convey that the variable can be equal to any values within that range. Thus, for a variable which is inherently discrete, the variable can be equal to any integer value of the numerical range, including the end-points of the range. Similarly, for a variable which is inherently continuous, the variable can be equal to any real value of the numerical range, including the end-points of the range. As an example, a variable which is described as having values between 0 and 2, can be 0, 1 or 2 for variables which are inherently discrete, and can be 0.0, 0.1, 0.01, 0.001, or any other real value for variables which are inherently continuous.
In the specification and claims, the singular forms include plural referents unless the context clearly dictates otherwise.
Technical and scientific terms used herein have the meaning commonly understood by one of skill in the art to which the present description pertains, unless otherwise defined.
The present disclosure provides a backing layer. This is a stack of layers which serves as support, on which layers may be applied so that a resulting multilayer stack has certain properties and fulfils certain functions, respectively, which make the multilayer stack suitable for use in diverse fields.
The backing layer is paper-based.
The backing layer of the present disclosure comprises
The paper layer serves as a carrier layer or support layer. It may be referred to as paper carrier in the prior art. The barrier coating layer may be applied on both sides of the paper layer or only on one side of the paper layer. Preferably, it is applied on both sides of the paper layer. The barrier coating layer may be directly applied on the first layer, which is a paper layer. It is preferably applied directly on both sides of the paper layer.
The backing layer may comprise a prime coating layer applied on the second layer (i.e. the barrier coating layer). The prime coating layer functions as an intermediate layer in between the barrier coating layer and another layer, ensuring stability of a stack of layers.
In an example, the prime coating layer may be present only on one side of the backing layer. The prime coating layer may be applied directly on the barrier coating layer only on one side of the backing layer. A release coating layer may be applied on the second layer (i.e. the barrier coating layer) on the side of the backing layer opposite the prime coating layer. The release coating layer may be applied directly on said second layer. Thus the release coating layer is present only on one side of the backing layer. The release coating layer ensures that the backing layer can be rolled up during production and desired lengths of backing layer be unrolled before use.
In an example, a backing layer may comprise a first layer which is a paper layer; a second layer, which is a barrier coating layer applied directly on both sides of the paper layer; a prime coating layer applied directly on the second layer only on one side of the backing layer; and a release coating layer directly applied on the second layer on the side of the backing layer opposite the prime coating layer. In an example, a backing layer may consist of the aforesaid layer sequence and stack. The prime coating layer may receive a layer such as an adhesive layer. As the adhesive is applied only on one side, a single-sided adhesive tape may be formed.
In an example, the prime coating layer may be present on both sides of the second layer (i.e. the barrier coating layer). The prime coating layer may be applied directly on the barrier coating layer on both sides of the backing layer. Thus, in an example a backing layer may comprise a first layer which is a paper layer; a second layer, which is a barrier coating layer applied directly on both sides of the paper layer; and a prime coating layer applied directly on the second layer on both sides of the backing layer. In an example, a backing layer may consist of the aforesaid layer sequence and stack. The two prime coating layers may receive a layer such as an adhesive layer. As the adhesive is applied on both prime coating layers, a double-sided adhesive tape may be formed.
The second layer (i.e. the barrier coating layer) comprises 30 to 70% by weight of an inorganic filler. The barrier coating layer may comprise preferably 35 to 65 wt. %, more preferably 40 to 60 wt. %, and most preferably 45 to 55 wt. % of an inorganic filler.
The inorganic filler may be a hydrophilic filler. The inorganic filler may be selected from the group consisting of kaolinite, calcined kaolinite, calcium carbonate, precipitated calcium carbonate (PCC), ground calcium carbonate (GCC), talc, mica, clay, silica, precipitated silica, pyrogenic silica, titanium dioxide or their mixtures. The barrier coating layer may preferably comprise kaolinite. The hydrophilic fillers are typically not coated or chemically treated in any way. The presence of the inorganic filler in the barrier coating layer in aforesaid proportions has the advantage that repulpability and sticky count of the backing layer is significantly improved. Without wanting to be bound by theory, it is assumed that the presence of the inorganic filler, in particular a hydrophilic filler, in significant amounts in the barrier coating layer allows for the penetration of water into the layer during recycling procedures and allows for suspending the polymer components of the layer in water.
The second layer (i.e. the barrier coating layer) comprises 70 to 30% by weight of a polymer having a glass transition temperature (Tg) of −35 to +15° C. The weight percentages are calculated on the basis of all components of the barrier coating layer in dry, applied state. The barrier coating layer may comprise 65 to 35 wt. %, preferably 60 to 40 wt. %, more preferably 55 to 45 wt. % of a polymer having a glass transition temperature (Tg) of −35 to +15° C. The polymer may have a glass transition temperature (Tg) of −30 to +10° C., preferably −25 to +5° C. The glass transition temperature is measured according to DIN ISO 53765 (1994 March). Polymers having a Tg of below zero degrees Celsius and in particular well below zero degrees Celsius are considered as hard polymers which tend to be sticky. Polymers having a Tg above zero degrees Celsius tend to be non-sticky. The instant disclosure provides backing layers comprising polymers having a Tg of below zero degrees Celsius, which are sticky, but still lead to a sticky count below 5, so that they conform to the Voluntary Standard described above as tested by the Western Michigan University.
The polymer may be selected from the group consisting of carboxylated styrene-butadiene rubber, styrene butadiene-rubber, acrylate-based polymers, acrylo-nitrile butadiene rubber, natural rubber, polyvinylacetate or mixtures thereof, with carboxylated styrene-butadiene rubber being preferred. The barrier coating layer may comprise carboxylated styrene-butadiene rubber having a Tg of −27 to −23° C. at a proportion of 65 to 35 wt. %, preferably 60 to 40 wt. %, more preferably 55 to 45 wt. %. The barrier coating layer may comprise carboxylated styrene-butadiene rubber with a Tg of +3 to +7° C. at a proportion of 65 to 35 wt. %, preferably 60 to 40 wt. %, more preferably 55 to 45 wt. %.
The barrier coating layer may comprise an anti-foaming agent. The anti-foaming may be contained in 0 to 0.05 wt. %. If contained, it may be contained in up to 0.05 wt. % or 0.01 to 0.03 wt. %. The proportions are calculated on the basis of the overall weight of the barrier coating layer, so that inorganic filler, polymer and anti-foaming agent add up to 100 wt. %. The anti-foaming agent may be selected from the group consisting of a mineral oil-based, vegetable oil-based, and siloxane-oil based anti-foaming agent.
In an example, the barrier coating layer comprises the inorganic filler in weight percentages given above, the polymer in weight percentages given above and the anti-foaming agent in percentages given above. In an example, the barrier coating layer may consist of aforesaid components in the given weight percentages. The barrier coating layer may essentially consist of said components in the given percentages, whereby it is not excluded that impurities are present due to processing parameters or starting material specifications and that customary additives are present in small weight percentages not materially altering the technical properties, the intended effect described in the present disclosure and the usability of the barrier coating layer. To achieve the intended effect, the inorganic filler and the polymer are comprised in the barrier coating layer at a combined percentage of at least 93%, preferably at least 95%, even at least 97%.
The barrier coating layer may comprise customary additives such as crosslinkers, dispersants, wetting agents, thickeners, hydrophobing agents or hydrophilizing agents in customary amounts such as minimum amounts of 0.05, 0.1 or 0.25 wt. % up to 3, 4 or 5 wt. %. If additives are present, the inorganic filler and the polymer are comprised in the barrier coating layer at a combined percentage of at least 93%, preferably at least 95%, even at least 97%.
The barrier coating layer is applied at a coat weight of 1 to 10 gsm, preferably 3 to 7 gsm.
The first layer of the backing layer of the present disclosure is a paper layer. The paper layer may have an extensibility in machine direction (MD) of 3 to 10%, preferably 5 to 8%, wherein extensibility is measured as per DIN EN ISO 1924-2 (2008). The paper may have an extensibility in cross direction (CD), which is orthogonal to machine direction (VID) of 5 to 15%, preferably 8 to 12%, wherein extensibility is measured as per DIN EN ISO 1924-2 (2008). The extensibility values, in particular in machine direction, allow for use of the backing layer in adhesive tapes and related applications. The extensibility allows for the backing layer to be used in various forms of tapes used for wrapping or fixing. The extensibility is maintained even after application of layers described herein. Extensibility of the final product may even surpass aforesaid extensibility due to the application of the layers.
In addition, the paper used as paper layer may have a high density and be highly sized, so that components of the barrier coating layer do not or to a very limited extent impregnate the paper layer and repulpability is maintained. The paper layer may have a porosity measured as Air Resistance (Gurley) of 5 to 25, preferably 10 to 20 Gurleys, measured as per ISO 5636-5 (2003). The paper layer may have water absorption (Cobb60) values of 20 to 40 gsm, preferably 25 to 35 gsm, measured according to the Cobb 60 test method ISO 535 (2014). The porosity and water absorption values ensure that the components of the barrier coating layer do not or only to a very limited extent impregnate the paper layer, while the paper layer remains repulpable. The paper layer may consist of paper satisfying aforesaid requirements and carry no other coating or have been subjected to any treatment such as coatings except for treatments or coatings to arrive at aforesaid technical properties.
The paper used for the paper layer may be selected from the group consisting of bleached or brown Kraft paper, bleached or brown sack Kraft paper, semi-extensible Kraft paper, semi-extensible sack Kraft paper, preferably semi-extensible sack Kraft paper.
Said papers satisfy the air resistance (Gurley) and water absorption (Cobb60) requirements given above, so that the components of the barrier coating layer do not or only to a very limited extent impregnate the paper layer, while the paper layer remains repulpable.
These papers are not subjected to any additional treatments such as additional coatings. The papers are used as purchased.
The paper used for the paper layer may have a basis weight of 40 to 100 gsm, or 40 to 80 gsm, preferably 50 to 70 gsm.
The backing layer may comprise a prime coating layer, which may be present on one or both sides of the second layer (i.e. the barrier coating layer) as described above. The prime coating layer may comprise polymers or polymer compositions selected from the group consisting of styrene butadiene-rubber, acrylate-based polymers, acrylo-nitrile butadiene rubber, polyvinyl acetate, natural rubber, pre-vulcanised natural rubber, butyl-acrylate; natural rubber grafted with methacrylate, carboxylated styrene butadiene rubber, and polyurethane.
The prime coating layer may comprise one polymer or a mixture of two or more polymers. The prime coating layer may be a composition comprising pre-vulcanised natural rubber and, butyl-acrylate. The prime coating layer may be a composition comprising methacrylate-grafted natural rubber and carboxylated styrene-butadiene-rubber. Said composition may comprise methacrylate-grafted natural rubber and carboxylated styrene-butadiene-rubber blended at a proportion of 80:20 to 95:05. In some examples, the prime coating layer may comprise the same polymer or polymers as the barrier coating layer. The prime coating layer may be present at a coat weight of 0.1 to 3 gsm, preferably 0.5 to 2 gsm.
A release coating layer may be applied on the prime coating layer, as described above. Compositions of release coating layers are well-known in the art. For example, the release coating layer may comprise compositions comprising polymers selected from the group consisting of hydrophilic acrylic or acrylate polymers; water-based vinyl acetate copolymer latexes. The release coating layer may be applied to attain a coat weight of 0.1 to 5 gsm, preferably 0.5 to 4 gsm on the prime coating layer.
The overall thickness of the backing layer comprising the layers described herein ranges from 60 to 150 micrometer. For example, a backing layer of the present disclosure of 90 g/m2 has a thickness of 105-135 micrometer. A backing layer of 70 g/m2 has a thickness of 70-100 micrometer.
The backing layer of the instant disclosure presents a repulpability of more than 85% as per the Voluntary Standard described above and measured according to a test performed at the Western Michigan University for repulping and recycling. The backing layer of the instant disclosure also presents a sticky formation in paper making of lower than 5. The test methods indicate that a) cellulose fibers can be recycled in high yield to form sheet paper and b) in particular polymers used in the production of the backing layer can be easily separated from cellulose fibers, when used adhesive tapes or other products comprising the backing layer of the present disclosure are subjected to paper recycling processes. Therefore, the backing layer of the instant disclosure is highly recyclable and repulpable.
The backing layer is suitable for diverse applications like adhesive tapes, which are used for stabilizing and wrapping up cardboard boxes, adhesive tapes applied on the inside of flaps of envelopes, and construction industry. The backing layer is also suitable for print media, labels, bundling tapes, carry handle tape, printed packaging tape, promotional banderole, industrial packaging for light medium and heavy duty applications, paper-based adhesive foil. The backing layer is in particular suitable for adhesive tapes, which are single-sided or double-sided as indicated in
The present disclosure also provides an adhesive tape which comprises the backing layer of the instant disclosure. The adhesive tape comprises an adhesive layer on the sole prime coating layer to afford a single-sided adhesive tape. It comprises adhesive layers on both prime coating layers to afford a double-sided adhesive tape. Adhesive layers are well-known in the art. Any adhesive layer known in the art may be used in combination with the backing layer of the present disclosure. Due to the advantageous properties of the backing layer, an adhesive tape is provided which is highly recyclable and repulpable.
The backing layer of the present disclosure is produced by successively coating the layers at coat weights described above on the paper layer. Components of layers may be applied as dispersion or as solution or as dry coating using standard methods known in the art. The barrier coating layer may be applied via an impregnation device, such as a water bath comprising a polymer dispersion through which the paper layer is moved. The impregnated layer may then be introduced into a pair of rolls to remove excess coating layer from the paper. Subsequently it may be dried. Then the prime coating layer and the release layer (if necessary) may be applied by an air knife device.
Unbleached, semi-extensible sack Kraft papier; grammage 60 g/m2, tensile strength: (ID) 5.3, (CD) 4.0; porosity (air resistance, Gurley) 18 s/100 ml; water absorption (Cobb60) 31 g/m2 (60 s).
As carboxylated styrene-butadiene rubber (SBR) having a Tg of +5 degrees Celsius product “Exopal L7063”, of EOC Belgium N.V. was used, providing an aqueous colloidal dispersion of a styrene-butadiene copolymer with carboxyl groups (solids content 49-51%). As carboxylated styrene-butadiene rubber (SBR) having a Tg of −25 degrees Celsius product “Ligod I4086 Binder”, of Trinseo was used, providing an aqueous colloidal dispersion of a styrene-butadiene copolymer with carboxyl groups (solids content (48-50%).
For kaolinite the product “Capim DG slurry” was used, providing a slurry having 70, 5 (wt. %) solids content.
The product “Primal R-253 ER Emulsion” of Dow Chemical Company was used providing a hydrophilic acrylic emulsion of solids content of 40%. Alternatively the product “Orgal KR250” of Organikkimya was used (solids content of 40%).
90% methacrylate-grafted natural rubber blended with 10% carboxylated styrene-butadiene rubber.
Glass transition temperature is measured as per DIN ISO 53765 (1994 March).
Extensibility is measured according to DIN EN ISO 1924-2 (2008).
Paper porosity is measured as Air Resistance (Gurley) as per ISO 5636-5 (2003).
Paper water absorption (Cobb60) are measured according to the Cobb 60 test method ISO 535 (2014).
Repulpability and recyclability are measured according to the “Voluntary Standard For Repulping and Recycling Corrugated Fiberboard Treated to Improve Its Performance in the Presence of Water and Water Vapor” (revised Aug. 16, 2013) published by the Fibre Box Association (FBA), USA. Testing was performed at the Western Michigan University, USA, on their paper pilot plant. The test method is to evaluate the repulpability and recyclability of moisture barrier treatments or coatings applied to liners or combined corrugated board in an effort to establish a minimum threshold for moisture barrier treated or coated corrugated that is intended, and labelled, to be recyclable into new containerboard and other paper products. The test is described in the following. In this test following wordings have meanings as follows:
Preliminary Analysis: Before beginning the test protocol, determine the moisture content of the treated corrugated sample.
A 100% charge of treated corrugated is repulped in a Modified Waring Blender and a British Disintegrator in water at a pH of 7 (+0.5 pH) that is maintained at 125° F. (±10°) following the procedure outlined under Repulpability Test procedure below. The pulped material is separated in a screen with 0.010-inch or smaller slots to determine fiber recovery as a percentage of the amount of fiber charged. Fiber yield from the repulpability test must be at least 80% based on the total weight, or 85% based on the bone dry fiber charge to the pulper.
A minimum of 20% treated corrugated and the remainder of the same untreated corrugated are mixed in a laboratory-scale pulper at pH 7 (+0.5 pH) and 125° F. (+10°). This is the recyclability test sample. As a control, a charge of 100% of the same untreated corrugated is also pulped using identical conditions. Each pulped material is passed through (in succession) a pressure screen equipped with a basket with 0.062 inch holes, the same screen or a similar screen equipped with a basket with 0.010 inch slots and a reverse centrifugal separator under conditions specified in the Recyclability Test procedure below.
Handsheets (3.0 gram) are made from the final stage (cleaner) accepts. For each batch tested, the handsheets are pressed and dried with heat and tested for product performance properties. Appearance tests shall be done according to the procedure outlined in Appendix B. The final sheets shall have no more than 15 spot counts, or not exceeding 30% greater counts than the control, with an area of3 0.4 mm2 area, averaged over 3 sheets. Detailed procedures for recyclability are given in Recyclability Test procedure below.
Repulpability Test Procedure
To determine the repulpability of corrugated board. (Note that the Repulpability Test must be run at least twice on the treated corrugated board. The sample must pass two out of three tests.)
The value obtained signifies the percentage of fiber repulpability.
Note: Both the Control sample and the sample of Treated and Untreated test material must be tested at least twice and must pass two out of three tests.
Backing layers as per the present disclosure were prepared as follows:
The barrier coating layer was applied on the paper layer via a water bath comprising a polymer dispersion through which the paper layer is moved. Temperatures of the water bath are generally ambient temperatures (15 to 40 degrees Celsius). The impregnated layer may then be introduced into a pair of rolls to remove excess coating layer from the paper. Subsequently it may be dried at 50 to 220 degrees Celsius. Then the prime coating layer and the release layer (if necessary) may be applied by an air knife device at ambient temperatures.
The unbleached semi-extensible sack Kraft paper having a basis weight of 60 gsm as described above was used as paper layer. The paper layer was coated on both sides with a composition comprising 50% carboxylated styrene-butadiene rubber (SBR) having a Tg of −25 degrees Celsius and 50% kaolinite to provide the barrier coating layer. The coat weight was 5 gsm. In this example a soft SBR was used. One side of the obtained layer stack was coated with a hydrophilic acrylic dispersion (Primal R253/Orgal KR250) at a coat weight of 2 gsm to provide a release coating layer.
When subjecting the obtained backing layer to the Western Michigan University test method for repulping and recycling, a yield of fiber recyclability of 92.5% and 94.1% (two test runs) was obtained. As the values are above 85%, the sample passed the test method. Regarding the stickies test, 1 sticky per hand sheet was observed. As this is below the target of 5 stickies, the sample passed the test method.
The unbleached semi-extensible sack Kraft paper having a basis weight of 60 gsm was used as paper layer. The paper layer was coated on both sides with a composition comprising 50% carboxylated styrene-butadiene rubber (SBR) having a Tg of +5 degrees Celsius and 50% kaolinite to provide the barrier coating layer. The coat weight was 5 gsm. In this example a hard SBR was used.
One side of the obtained layer stack was coated with a hydrophilic acrylic dispersion (Primal R253/Orgal KR250) at a coat weight of 2 gsm to provide a release coating layer.
When subjecting the obtained backing layer to the Western Michigan University test method for repulping and recycling, a yield of fiber recyclability of 95.8% and 97.5% (two test runs) was obtained. As the values are above 85%, the sample passed the test method. Regarding the stickies test, 1.67 stickies per hand sheet were observed. As this is below the target of 5 stickies, the sample passed the test method.
The unbleached semi-extensible sack Kraft paper having a basis weight of 60 gsm was used as paper layer. The paper layer was coated on both sides with a composition comprising 50% carboxylated styrene-butadiene rubber (SBR) having a Tg of −25 degrees to provide a barrier coating layer. The coat weight was 5 gsm.
One side of the obtained layer stack was coated with a hydrophilic acrylic dispersion (Primal R253/Orgal KR250) at a coat weight of 2 gsm to provide a release coating layer.
The other side of the layer stack was coated with a dispersion comprising 90% methacrylate-grafted natural rubber and 10% carboxylated styrene-butadiene rubber at a coat weight of 1 gsm to provide a primer layer.
When subjecting the obtained backing layer to the Western Michigan University test method for repulping and recycling, a yield of fiber recyclability of 65.9% and 69.2% (two test runs) was obtained. As the values are below 85%, the sample failed the test method. Regarding the stickies test, more than 100 stickies per hand sheet were observed. As this is above the target of 5 stickies, the sample failed the test method.
1. A backing layer comprising
2. The backing layer according to claim 1, comprising a prime coating layer applied on the second layer, which is a barrier coating layer, wherein the prime coating layer is present only on one side of the backing layer.
3. The backing layer according to claim 1, comprising a prime coating layer applied on the second layer, which is a barrier coating layer, wherein the prime coating layer is present on both sides of the backing layer.
4. The backing layer according to claim 2, comprising a release coating layer applied on the second layer, which is a barrier coating layer, wherein the release coating layer is present only on one side of the backing layer.
5. The backing layer according to any of claims 1 to 4, characterized in that the barrier coating layer comprises 35 to 65 wt. %, preferably 40 to 60 wt. %, more preferably 45 to 55 wt. % of inorganic filler.
6. The backing layer according to any of claims 1 to 5, characterized in that the barrier coating layer comprises 65 to 35 wt. %, preferably 60 to 40 wt. %, more preferably 55 to 45 wt. % of a polymer having a glass transition temperature (Tg) of −35 to +15° C.
7. The backing layer according to any of claims 1 to 6, characterized in that the polymer has a glass transition temperature (Tg) of −30 to +10° C., preferably −25 to +5° C.
8. The backing layer according to any of claims 1 to 7, characterized in that the barrier coating layer comprises 0 to 0.05 wt. % of an anti-foaming agent.
9. The backing layer according to claim 8, characterized in that the barrier coating layer comprises 0.01 to 0.03 wt. % of an anti-foaming agent.
10. The backing layer according to claim 8 or 9, characterized in that the anti-foaming agent is selected from the group consisting of a mineral oil-based, vegetable oil-based, and siloxane-oil based anti-foaming agent.
11. The backing layer according to any of claims 1 to 10, characterized in that the first layer, which is a paper layer, has an extensibility in machine direction (MD) of 3 to 10%, preferably 5 to 8%, wherein extensibility has been measured as per DIN EN ISO 1924-2.
12. The backing layer according to any of claims 1 to 11, characterized in that the first layer, which is a paper layer, has an extensibility in cross direction (CD), which is orthogonal to machine direction (MD) of 5 to 15%, preferably 8 to 12%.
13. The backing layer according to any of claims 1 to 12, characterized in that the first layer, which is a paper layer, has a porosity measured as Air Resistance (Gurley) of 5 to 25, preferably 10 to 20 Gurleys, measured as per ISO 5636-5.
14. The backing layer according to any of claims 1 to 13, characterized in that the first layer, which is a paper layer, has water absorption (Cobb60) values of 20 to 40 gsm, preferably 25 to 35 gsm measured according to the Cobb 60 test method ISO 535.
15. The backing layer according to any of claims 1 to 14, characterized in that the first layer, which is a paper layer, comprises paper selected from the group consisting of bleached or brown Kraft paper, bleached or brown sack Kraft paper, semi-extensible Kraft paper, semi-extensible sack Kraft paper, preferably semi-extensible sack Kraft paper.
16. The backing layer according to any of claims 1 to 15, characterized in that the first layer, which is a paper layer, comprises paper having a basis weight of 40 to 80 gsm, preferably 50 to 70 gsm.
17. The backing layer according to any of claims 1 to 16, characterized in that the second layer, which is a barrier coating layer, comprises an inorganic filler selected from the group consisting of kaolinite, calcined kaolinite, calcium carbonate, precipitated calcium carbonate (PCC), ground calcium carbonate (GCC), talc, mica, clay, silica, precipitated silica, pyrogenic silica, titanium dioxide or their mixtures.
18. The backing layer according to any of claims 1 to 16, characterized in that the second layer, which is a barrier coating layer, comprises kaolinite.
19. The backing layer according to any of claims 1 to 18, characterized in that the second layer, which is a barrier coating layer, comprises a polymer selected from the group consisting of carboxylated styrene-butadiene rubber, styrene butadiene-rubber, acrylate-based polymers, acrylo-nitrile butadiene rubber, natural rubber, polyvinylacetate or mixtures thereof, with carboxylated styrene-butadiene rubber being preferred.
20. The backing layer according to any of claims 1 to 18, characterized in that the second layer, which is a barrier coating layer, comprises carboxylated styrene-butadiene rubber having a Tg of −27 to −23° C.
21. The backing layer according to any of claims 1 to 18, characterized in that the second layer, which is a barrier coating layer, comprises carboxylated styrene-butadiene rubber having a Tg of +3 to +7° C.
22. The backing layer according to any of claims 1 to 21, characterized in that the second layer, which is a barrier coating layer, is present at a coat weight of 1 to 10 gsm, preferably 3 to 7 gsm.
23. The backing layer according to any of claims 2 to 22, characterized in that the prime coating layer comprises polymers or polymer compositions selected from the group consisting of styrene butadiene-rubber, acrylate-based polymers, acrylo-nitrile butadiene rubber, polyvinylacetate, natural rubber, pre-vulcanised natural rubber, butyl-acrylate; natural rubber grafted with methacrylate, carboxylated styrene butadiene rubber, and polyurethane.
24. The backing layer according to claim 23, characterized in that the prime coating layer comprises a composition of natural rubber grafted with methacrylate and carboxylated styrene butadiene rubber at a proportion of 80:20 to 95:05.
25. The backing layer according to any of claims 2 to 14, characterized in that the prime coating layer is present at a coat weight of 0.1 to 3 gsm, preferably 0.5 to 2 gsm.
26. The backing layer according to any of claims 4 to 25, characterized in that the release coating layer comprises compositions comprising polymers selected from the group consisting of hydrophilic acrylic or acrylate polymers; water-based vinyl acetate copolymer latexes.
27. The backing layer according to any of claims 4 to 26, characterized in that the release coating layer is present at a coat weight of 0.1 to 5 gsm, preferably 0.5 to 4 gsm.
28. The backing layer according to any of claims 1 to 27, characterized in that it has a repulpability of more than 85% measured according to the Western Michigan University test method for repulping and recycling.
29. The backing layer according to any of claims 1 to 28, characterized in that it has a sticky formation in paper making of lower than 5.
30. The backing layer according to any of claims 1 to 29, characterized in that it is suitable for adhesive tapes.
31. An adhesive tape comprising the backing layer according to any of claims 1 to 30.