Claims
- 1. A method for producing a self-supporting ceramic composite structure comprising a ceramic matrix obtained by an oxidation reaction of at least a first parent metal with an oxidant to form a polycrystalline material which comprises an oxidation reaction product of said first parent metal and said oxidant and a filler infiltrated by said matrix, the method comprising:
- (a) orienting a source comprising said first parent metal and a permeable mass of filler relative to each other so that formation of an oxidation reaction product will occur in a direction towards and into said mass of filler, wherein the quantity of said source of first parent metal provided is insufficient to embed substantially completely said permeable mass;
- (b) communicating a reservoir comprising a second metal having a chemical composition which is different from said source of first parent metal with said source of first parent metal;
- (c) heating said source of first parent metal to a temperature which is above the melting points of the first parent metal and the second metal, but below the melting point of said oxidation reaction product of said first parent metal to form a source comprising molten first parent metal and reacting said source of molten first parent metal with an oxidant to form said oxidation reaction product by maintaining at least a portion of said oxidation reaction product in contact with and extending between said source of molten first parent metal and said oxidant to progressively draw molten parent metal through the oxidation reaction product towards the oxidant and into said mass of filler so that fresh oxidation reaction product continues to form within said mass of filler at an interface between said oxidant and previously formed oxidation reaction product; and
- (d) at said temperature, replenishing said source of first parent metal with said second metal in said reservoir as said oxidation reaction continues such that said permeable mass is substantially completely embedded, to permit the formation of said self-supporting ceramic composite structure.
- 2. The method of claim 1, wherein said reservoir of second metal communicates with said parent metal by gravity flow.
- 3. The method of claim 1 or claim 2, wherein said mass of filler comprises at least one shaped preform.
- 4. The method of claim 1 or claim 2, wherein said ceramic composite structure comprises an interconnected metallic component.
- 5. The method of claim 3, wherein said ceramic composite structure comprises an interconnected metallic component.
- 6. The method of claim 1 or claim 2, wherein said reservoir of a second metal is maintained at a temperature less than a temperature utilized for the growth of oxidation reaction product.
- 7. The method of claim 3, wherein said reservoir of a second metal is maintained at a temperature less than a temperature utilized for the growth of oxidation reaction product.
- 8. The method of claim 1 or claim 2, wherein said first source of parent metal comprises a solid ingot of parent metal having a pattern formed thereon, and said mass of filler material comprises a filler which is in conforming engagement with said pattern, whereby after said reacting is completed by infiltrating the filler material to a desired amount to form said self-supporting ceramic composite structure, any excess parent metal which did not form oxidation reaction product is removed from said filler material and said self-supporting ceramic composite structure contains an inversely replicated geometry of said pattern therein.
- 9. The method of claim 3, wherein at least a portion of a surface of said at least one preform is defined by a barrier means.
- 10. The method of claim 1 or claim 2, further comprising a barrier means at least partially spaced from said first source of parent metal for establishing at least one surface of said mass of filler material, whereby said reacting occurs until said oxidation reaction product confronts said barrier means, thereby producing a ceramic composite structure having an exterior surface established by said barrier means.
- 11. The method of claim 1 or claim 2, further comprising maintaining said reservoir source of molten parent metal at an elevation at or above the highest elevation of said body of molten parent metal from said first source to maintain a static pressure head on said body of molten parent metal from said first source.
- 12. The method of claim 3, further comprising maintaining said reservoir source of molten parent metal at an elevation at or above the highest elevation of said body of molten parent metal from said first source to maintain a static pressure head on said body of molten parent metal from said first source.
- 13. The method of claim 1 or claim 2, wherein said mass of filler material comprises a plurality of masses of filler material each of said plurality of masses of filler material contacting said molten parent metal.
- 14. The method of claim 3, wherein said at least one preform comprises a plurality of preforms each of said plurality of preforms contacting said molten parent metal.
- 15. The method of claim 1 or claim 2, further comprising maintaining molten parent metal in contact with said mass of filler material and after said reacting is completed, permitting unreacted metal to solidify in contact with said self-supporting ceramic composite structure so as to provide a metal substrate integrally formed therewith.
- 16. The method of claim 3, further comprising maintaining molten parent metal in contact with said at least one shaped preform and after said reacting is completed, permitting unreacted metal to solidify in contact with said self-supporting ceramic composite structure so as to provide a metal substrate integrally formed therewith.
- 17. The method of claim 1 or claim 2, wherein said parent metal comprises at least one metal selected from the group consisting of aluminum, titanium, silicon, zirconium, hafnium and tin.
- 18. The method of claim 9, wherein said barrier means comprises at least one material selected from the group consisting of stainless steel, plaster of paris, calcium silicate, calcium sulfate, wollastonite and portland cement.
- 19. The method of claim 10, wherein said barrier means comprises at least one material selected from the group consisting of stainless steel, plaster of paris, calcium silicate, calcium sulfate, wollastonite and portand cement.
- 20. A method for producing a self-supporting ceramic composite structure comprising a ceramic matrix obtained by an oxidation reaction of at least a first parent metal with an oxidant to form a polycrystalline material which comprises an oxidation reaction product of said first parent metal and said oxidant and a filler infiltrated by said matrix, the method comprising:
- (a) orienting at least a source comprising a first parent metal and a permeable mass of filler relative to each other so that formation of an oxidation reaction product will occur in a direction towards and into said mass of filler, wherein the quantity of said source of first parent metal provided is insufficient to embed substantially completely said permeable mass;
- (b) communicating a reservoir comprising a second metal which is maintained at a temperature which is less than a temperature of said first source of parent metal with said first source of parent metal;
- (c) heating said source of first parent metal to a temperature which is above the melting points of the first parent metal and the second metal, but below the melting point of said oxidation reaction product of said parent metal to form a source comprising first molten parent metal and reacting said molten first parent metal with an oxidant to form said oxidation reaction product by maintaining at least a portion of said oxidation reaction product in contact with and extending between said source of first molten parent metal and said oxidant to progressively draw molten parent metal through the oxidation reaction product towards the oxidant and into said mass of filler so that fresh oxidation reaction product continues to form within said mass of filler at an interface between said oxidant and previously formed oxidation reaction product; and
- (d) at said temperature, replenishing said source of first parent metal with said second metal in said reservoir as said oxidation reaction continues such that said permeable mass is substantially completely embedded, to permit the formation of said self-supporting ceramic composite structure.
- 21. The method of claim 20, wherein said heating of said first source of parent metal occurs within a furnace.
- 22. The method of claim 21, wherein at least a portion of said second metal is located, at least initially, external to said furnace.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of Commonly Owned and Copending U.S. patent application Ser. No. 908,067, filed Sept. 16, 1986, in the names of Marc S. Newkirk, H. Daniel Lesher, Ratnesh K. Dwivedi and Robert C. Kantner, entitled "Reservoir Feed Method of Making Ceramic Composite Structures and Structures Made Thereby".
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
3709096 |
Church et al. |
Jan 1974 |
|
4824008 |
Luszoz et al. |
Apr 1989 |
|
4833110 |
Newkirk et al. |
May 1989 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
908067 |
Sep 1986 |
|