Patent Grant
11491748
The current method of manufacturing composites having complex shapes is by forming a reinforcement fiber preform of a particular shape, placing the preform in a vacuum bag or mold, infusing the preform with liquid resin, and then heating the impregnated preform to cure it into the final composite part. During the preparation of some preforms, it is common to encounter a void space or cavity at various junctions formed between different layups of fiber plies. Fillers have been conventionally used to fill such a cavity.
The present disclosure relates to radius fillers useful in aerospace applications such as aircraft structural components. The radius filler is a deformable, coated structure comprising a continuous or elongated fibrous structure and a tacky, resin surface coating formed by pulling a dry, continuous or elongated fibrous structure through a heated resin bath, wherein the coated radius filler has an inner portion that is substantially free of resin and the resin surface coating has a substantially uniform thickness.
For composite parts made out of prepreg materials, the common practice has been to use the same material used in the joining section, and to roll it to form a filler. This approach is time consuming, inefficient and has the particular disadvantage of manufacturing fillers of limited length. To alleviate this short coming, some solutions involve manufactured prepreg fillers made of continuous tows where several tows are prepregged either individually or bunched up together. In some cases, these tows can be run through a die to pre-shape the filler to a desired cross section profile, mimicking the cavity profile they will fill. One or more fillers are used per cavity, depending on the size of the cavity, the size and shape of the filler, the ability of the filler(s) to fill the cavity, the desired mechanical performance of the part and some other constraints such as handling of the filler(s), placement in the cavity, material inventory management, etc. In another approach, a machine is provided to take several prepreg tapes and produce a filler of a continuous length, and pre-shaped to a desired profile. Such prepreg radius fillers have in common a large amount of resin typically 30% to 40% by weight of the product. The resin distribution is such that it has generally wet out the vast majority of the fibers that form the filler. Prepreg fillers usually have some level of tack that can be enhanced during the lay down process by heating the filler with a heat gun for instance. Handling, flexibility and malleability of prepreg fillers is usually poor, rendered difficult by the resin that prevents free motion of the filler fibrous structure, even when the filler is warmed up with a heat gun. Finally in the case of composite parts made of prepreg materials, adhesive resin fillers were also developed as an alternative to prepreg fillers. In this case, the filler is 90% to 100% made of resin, with on occasion, a light scrim embedded into the resin filler to provide higher handling characteristics.
In recent years, the number of composite parts manufactured via a Resin Infusion (RI) process has considerably increased. RI is not only used to manufacture small complex parts but it is also now used to manufacture the entire wings, or other very large parts of aircraft. Although in some cases, the forming of the parts via a textile preforming process may eliminate the need for a filler—in the case of π preforms for instance—the large majority of RI parts, especially large parts, still rely on tackified broadgoods or textiles that are folded to form the desired shape, which creates cavities that need to be filled with fillers. The tackified broadgoods can be rolled into a noodle filler. This method can only produce short-length fillers and is by far the least cost effective approach. Other approaches rely on partially impregnating individual or multiple tows or ropes or braids with a tackifier. The purpose of the tackifier is to provide some level of tackiness to the filler in order to position it in the cavity while the preform is being assembled. Unfortunately, most tackifiers must be heat activated to provide their tackiness characteristic. This requires warming up the filler with a heat gun, for instance, during its lay down. In some cases, the tackifier may be a sprayable, solvent-based resin, which requires full solvent removal, thereby presenting safety and laminate void content issues. This may at times be a difficult task, requiring more than one operator, and can even become questionable from a safety hazard stand point and possible material degradation. Attempts to use prepreg fillers or solid fillers in a cavity of a part to be processed via RI have not been very successful as the integration between the RI part and the prepreg filler, due to cure cycle differences, does not exist, and compatibility between the materials is poor, resulting in mechanical issues.
Finally, pre-shaped fillers have been found to be difficult to handle and position within the cavity to be infused with resin. Cavities of structural parts may have complex profiles, thus, it is important to match the shape of the pre-shaped filler to the profile of the cavity. This matching requirement burdens unnecessarily the manufacturing operators. In some applications, the profile of the cavity even changes with the location in the part. It is thus extremely difficult to manufacture a filler with a varying cross section to suit the cavity profile. Furthermore, the associated cost of such filler would be far beyond the need and performance of its function. Moreover, many conventional pre-shaped fillers are very stiff and cannot be bent, risking damaging their profile, and as such can only be made of a discrete length for handling and shipping reasons, this limiting their attractiveness. For those fillers that are somewhat less stiff, and can be wound onto very large diameter cores, e.g. 20 inches and up, special grooved cores are necessary in order to maintain the shape of the filler and avoid its twisting. Furthermore, the amount of filler deposited on this type of core is usually limited by the groove spacing and size of the core (diameter and length). These packaging requirements increase the overall cost of such a product and reduce its attractiveness.
This present disclosure relates to coated fillers for use in composite preforms that are subjected to a resin infusion (RI) process. More specifically, the coated fillers take the form of continuous or elongated fillers for filling in a cavity of a three-dimensional composite preform structure. The coated fillers are deformable and malleable so that they can conform to various cavity geometries. In one embodiment, the continuous or elongated filler to be coated is in the form of a dry, continuous, braided structure, for example, a fiber braid made of a plurality of individual fiber strands intertwined in a braided pattern.
The term “tacky” or “tackiness” as used herein refers to the ability of the coated fillers to stick to a surface for a period of time.
Resin infusion (RI) is a generic term which covers processing techniques such as resin transfer molding, liquid resin infusion, vacuum assisted resin transfer molding, resin infusion with flexible tooling, vacuum assisted resin infusion, resin film infusion, controlled atmospheric pressure resin infusion, vacuum assisted process and single line injection. Resin infusion may be used in the fabrication process of a structural part, in which liquid resin is drawn into a dry fibrous preform which is kept under vacuum. The dry fibrous preform may take the form of a plurality of layers or plies of dry reinforcement fibers assembled in a stack or layup. Then the preform is placed in a mold or vacuum bag, and injected or infused directly in-situ with the matrix resin. The coated radius fillers of the present disclosure may be used to fill cavities formed within the dry fibrous preform.
In one embodiment, the fillers to be coated are made of uniquely designed braids which confer a tailorable deformability to fit various cavity profiles. In particular, the deformability of the filler is due to the high ratio of axial fibers over bias fibers that form the envelope of the braid. Braids may be made of 3 or more intertwined yarns, described as bias yarns that form a hollow flexible and highly deformable tube. In some cases, axial yarns are also intertwined with the bias yarns to form a hollow flexible tube with a higher cohesion, i.e. the braid is more stable or less deformable. This type of braid structure is called a “triaxial” braid because the yarns (i.e. fiber strands) are going in three different directions, contrary to the so-called “biaxial” braid because yarns are disposed in two different directions only. In other cases, the hollow section of the braid, biaxial or triaxial, can be filled with longitudinal yarns. The longitudinal yarns are defined as the core of the braid while the biaxial or triaxial structure of the braid is defined as the outer layer or shell or envelope. When braids are used, the percentage by weight of axial fibers either as fibers placed in the core of the braid or/and within the bias fibers is of at least 50%, preferably above 65%, based on the total weight of the braid. The resin coating is uniformly deposited on the outer surface of the braid, leaving the inner portion of the braid substantially resin-free. This in turn allows the core of the braid to be infused during the RI cycle. The resin remains on and within the outer surface of the braid created by the bias yarns because of a combination of a tight layer structure and a low-flowing resin at room temperature.
Specific braid architectures are the function of the braid filling purpose and the radius filler size. In general coarser braids, the ones with a diameter over 0.150 inch are used to fill the maximum volume of the cavity and are designed with a core wrapped by a biaxial sleeve while finer braids are used in the apexes of the cavity and have a triaxial design. However, other braid designs can be developed for other applications. In the case of the core and envelope construction for the coarser braids, the core and the biaxial envelope are independent of each other and allow for free independent motion relative to each other. Furthermore, the core contains the vast majority of the fibers, at least 50%, of the filler and is made of independent parallel yarns that allow for a free motion without much constraint. This favors a good packing of the filler in the cavity. The outer envelope is independent of the core with its fibers at a long angle relative to the braid longitudinal direction, e.g., less than 35°. This further favors the good handling of the radius filler. The outer layer has a good cover factor which helps to contain the resin on the braid within the shell of the filler or its surface.
In the case of triaxial braid filler, high deformability of the filler is desired to fill the cavity apexes. As such the braid structure is preferably collapsible. As such, a hollow braid structure is best suited for this purpose. The axial yarns representing about 50% by weight of the braid filler will provide a good longitudinal stability that is particularly needed during the resin coating process, and consistency in the deformability and the collapsibility of the product. Similarly to the core-shell braid, the coverage of the triaxial braid is high to help contain the resin within the outer shell or on its surface.
The resin coating of the radius filler is controlled by the resin viscosity, the coating process and the characteristics of the uncoated fibrous structure. For a given radius filler, the desired deposited amount of resin is controlled by processing conditions such as resin temperature which affects resin viscosity, line speed which affects residency time of the uncoated filler in the resin, diameter of the grommet through which the filler exits the resin bath, which affects how much resin is squeezed out of the coated filler. The internal diameter of the hole in the grommet is controlled and works with other control factors to provide the desired coating resin content. The major control factors include:
(a) Grommet aperture dimension (ID dimension)
(b) Resin temperature (which affects resin viscosity during coating)
(c) Resin level in the resin bath
(d) Resin age
(e) Line speed
The contact time of the continuous filler with resin bath is determined by the resin level and line speed. The viscosity of the resin bath during the coating process is controlled via heating so as to enable relatively smooth and uniform surface coating, and may be in the range of 0.50 Poise-1000 Poise (0.05 Pa·s-100 Pa·s) depending on the filler surface to be coated (e.g. coarseness, texture of the braid weave). The temperature of the heated resin bath during surface coating may be in the range of 100° F.-300° F. (37.78° C.-148.89° C.), depending on the type of resin being used. Any conventional heating means may be used for heating the resin bath, for example, strip heaters around a metallic vessel to provide the heat source. The line speed may vary from 10 to 150 feet per minute (fpm) (5.08 cm/s to 76.25 cm/s), preferably 30 fpm to 60 fpm (15.25 cm/s to 30.5 cm/s). The resin level within the coating bath directly affects the resin content of the coated filler by increasing the dwell time of the uncoated filler in the resin, thus, it may be varied to achieve the desired resin content for the coated filler. The surface tension of the resin also acts to draw the resin level down prior to the entering the grommet.
The grommet is fabricated from a deformable material and is sized to be the same or slightly below the solid diameter of the continuous filler/braid to be coated. For example, a 0.125 in (3.175 mm) ID grommet may be used for coating a braid with 0.148 in (3.76 mm) outer diameter (OD), and a 0.08 in (2.03 mm) ID grommet may be used for coating a braid with 0.08 in (2.03 mm) OD. In some embodiments, in order to increase the resin content of the coated filler, the grommet inner diameter may be increased so that it is slightly larger than the diameter of the continuous filler/braid to be coated. Rubber grommets have been found to be suitable for the coating system of the present disclosure. It should be understood, however, that other elastomeric material may be used for making the grommet.
The resulting coated filler produced by the coating method depicted in
The amount of resin deposited onto the uncoated filler may range from 5% to 50%, preferably 10%-30%, more preferably about 15%-20%, by weight based on the total weight of the coated filler and is tailored to meet the requirements of the intended application. The resin content and surface coating substantially prevent the coated filler from restricting the resin flow during RI process when the structural part is fabricated. The developed coating method disclosed herein is very robust and stable, and allows consistent deposition of a desired amount of resin onto the filler.
The resin coated radius fillers can be economically produced in a diameter range of about 0.010 in to 1.5 in (0.254 mm to 38.1 mm) for most purposes, and may be in the range of 0.04 in to 0.4 in (1.02 mm to 10.16 mm) for certain intended purposes.
The continuous or elongated fibrous structure to be coated may be made of organic or inorganic fibers including fibers made of polymer, carbon, graphite, glass, quartz, aramid (e.g. Kevlar), PBO, polyethylene, inorganic oxide, carbide, ceramic, metal, or combinations thereof.
The coating resin may be a coating formulation containing one or more thermosetting resins that include, but are not limited to members of the group consisting of epoxy resin, addition-polymerisation resin, bis-maleimide resin, cyanate ester resin, phenolic resin, polyester resins, vinyl ester resins, and combinations thereof.
Furthermore, the resin may be a hot-melt resin, which means that the resin is a solvent-free resin that is liquid at temperatures greater than room temperature and a solid or semisolid at room temperature. Hot melt coating processes rely on controlling the viscosity of the resin polymer with temperature. When hot melt epoxy resin is used, the resin may be preheated in an oven (e.g., at 100° F.-250° F. or 37.78° C.-121.11° C.) prior to the start of the coating process to allow the resin to be poured into the process vessel.
Examples of epoxy-based resins suitable for the coating formulation includes Cycom® 890® resin and Cycom® 823® resin from Cytec Industries Inc. (both are liquid epoxy resins designed for Resin Transfer Moulding). Other possible epoxy-based resins that can be used include an epoxy resin selected from N,N,N′N′-tetraglycidyl diamino diphenylmethane (e.g. “MY 9663”, “MY 720” or “MY 721” sold by Ciba-Geigy) viscosity 10-20 Pa·s at 50° C.; (MY 721 is a lower viscosity version of MY 720 and is designed for higher use temperatures); N,N,N′,N-tetraglycidyl-bis(4-aminophenyl)-1,4-diisopropylbenzene (e.g. Epon 1071 sold by Shell Chemical Co.) viscosity 18-22 Poise (1.8-2.2 Pa·s) at 110° C.; N,N,N′,N′-tetraglycidyl-bis(4-amino-3,5-dimethylphenyl)-1-,4-diisopropylbenzene, (e.g. Epon 1072 sold by Shell Chemical Co.) viscosity 30-40 Poise (3-4 Pa·s) at 110° C.; triglycidyl ethers of p-aminophenol (e.g. “MY 0510” sold by Ciba-Geigy), viscosity 0.55-0.85 Pa·s at 25° C.; preferably of viscosity 8-20 Pa·s at 25° C.; preferably this constitutes at least 25% of the epoxy components used; diglycidyl ethers of bisphenol A based materials such as 2,2-bis(4,4′-dihydroxy phenyl) propane (e.g. “DER 661” sold by Dow, or “Epikote 828” sold by Shell), and Novolak resins preferably of viscosity 8-20 Pa·s at 25° C.; glycidyl ethers of phenol Novolak resins (e.g. “DEN 431” or “DEN 438” sold by Dow); diglycidyl 1,2-phthalate, e.g. GLYCEL A-100; diglycidyl derivative of dihydroxy diphenyl methane (Bisphenol F) (e.g. “PY 306” sold by Ciba Geigy) which is in the low viscosity class. Other epoxy resin precursors include cycloaliphatics such as 3′,4′-epoxycyclohexyl-3,-4-epoxycyclohexane carboxylate (e.g. “CY 179” sold by Ciba Geigy) and those in the “Bakelite” range of Union Carbide Corporation.
Examples of addition-polymerisation resins are acrylics, vinyls, bis-maleimides, and unsaturated polyesters.
Suitable bismaleimide resins are heat-curable resins containing the maleimido group as the reactive functionality. The term bismaleimide as used herein includes mono-, bis-, tris-, tetrakis-, and higher functional maleimides and their mixtures as well, unless otherwise noted. Bismaleimide resins with an average functionality of about two are preferred. Bismaleimide resins as thus defined are prepared by the reaction of maleic anhydride or a substituted maleic anhydride such as methylmaleic anhydride, with an aromatic or aliphatic di- or polyaniine. The closely related nadicimide resins, prepared analogously from a di- or polyamine but wherein the maleic anhydride is substituted by a Diels-Alder reaction product of maleic anhydride or a substituted maleic anhydride with a diene such as cyclopentadiene, are also useful. As used herein, the term bismaleimide shall include the nadicimide resins. Also useful are bismaleimide “eutectic” resin mixtures containing several bismaleimides. Such mixtures generally have melting points which are considerably lower than the individual bismaleimides.
In one embodiment, the resin used for surface coating is an epoxy-based resin that has been modified with a viscosity modifier such that process and performance compatibility is retained but that the ambient viscosity is such that it produces a surface tackiness for positioning purposes and low-flow behavior. The viscosity modifier may be selected from thermoplastic polymers and rubbers. Such modified resin is a modified low-flow version of the resin used in resin infusion process, which is usually a high-flow, low-viscosity resin that satisfies the requirements of the RI process. The low-flow resin formulation is achieved by adding a high-viscosity thermoplastic polymer or rubber to the base low-viscosity epoxy resin in a quantity ranging from 5% to 20% based on the total weight of the resin formulation, preferably 10 to 15%, depending on the epoxy type, the curing agent type and the desired resin flow. Furthermore, the resin surface coating is formulated so as to be compatible with the infusion process resin with respect to tack and rheology behavior during the manufacturing of composite structures.
The thermoplastic viscosity modifier may be selected from, but not limited to, a group consisting of cellulose derivatives, polyester, polyamide, polyimide, polycarbonate, polyurethane, poly(methyl methacrylate), polystyrene, polyaromatics; polyesteramide, polyamideimide, polyetherimide, polyaramide, polyarylate, polyacrylate, poly(ester) carbonate, poly(methyl methacrylate/butyl acrylate), polysulphone, polyethersulphone, polyetherethersulphone polyethersulphone-etherketone, and copolymers thereof, polyetheretherketone (PEEK), polyetherketoneketone (PEKK), nylon, and combinations thereof. As an example, a commercially available thermoplastic viscosity modifier that may be used is Cytec KM® 180 (co-polymer of polyethersulfphone (PES) and polyetherethersulphone (PEES) available from Cytec Industries).
As one example, the low-flow resin coating formulation may be comprised of a liquid epoxy-based resin, e.g., Cycom® 890® or Cycom® 823®, that has been modified by adding a PES-PEES copolymer, e.g. Cytec KM® 180, as viscosity modifier.
The surface coating resin formulation may further comprise conventional additives such as a curing agent and/or a catalyst. Additional flow modifiers such as silica particles (e.g. Cabosil from Cabot Corp.) may also be added to the resin coating formulation to further fine tune the resin viscosity. It should be understood that resin viscosity influences the coating process, the tack-out time of the coated filler, and the reaction of the filler to the RI process. The “tack-out time” refers the time of exposure to ambient conditions during which the product is able to provide positioning tack as measured in hours or days.
The coated radius filler produced by the coating method disclosed herein may be used to fill the radial cavity created in composite structural parts. This concept can also be used in other applications where cavities created by the joining of fabric plies to form a specific section that must be filled. Further, the coated radius filler is to be used in applications where composite parts are manufactured via RI process.
An example of the application for the coated radius fillers will be described with reference to
The characteristics of the radius fillers manufactured in the manner described above include:
Coated radius fillers designed and manufactured according to the present disclosure are affordable and further reduce the overall composite part manufacturing cost by simplifying the part manufacturing process. The resin coating process to manufacture such a product is simple, elegant yet robust as well as being very efficient and results in an end product with very little variation.
The coating method and coated filler of the present disclosure may be illustrated by the following non-limiting examples.
Using the coating system illustrated by
Using the coating system illustrated by
The instant application is a divisional application of U.S. application Ser. No. 13/454,761 filed on Apr. 24, 2012, which claims the benefit of U.S. Provisional Patent Application No. 61/493,277 filed on Jun. 3, 2011, both of which are incorporated by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6333064 | Gan | Dec 2001 | B1 |
| Number | Date | Country |
|---|---|---|
| 07052268 | Feb 1995 | JP |
| Entry |
|---|
| Machine Translation JP 07052268 A (Year: 1995). |
| Number | Date | Country | |
|---|---|---|---|
| 20190210307 A1 | Jul 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13454761 | Apr 2012 | US |
| Child | 16353566 | US |