Patent Grant
11015018
The present application is based on, and claims priority from, Taiwan Application Serial Number 107100633, filed on Jan. 8, 2018, the disclosure of which is hereby incorporated by reference herein in its entirety.
The technical field relates to a thermally conductive material.
Electronic products are increasingly being designed to be thinner than previous models, as well as to use high power so that they may operate in 5th generation wireless systems and internet of things (IoT) applications. To these ends, thermal interface materials play a critical role in integrated module design. Such thermal interface materials should have thermal conductivity so that they can efficiently increase the heat transfer between devices and heat sinks.
The main resin compositions used in conventional thermal interface materials are siloxane resin. A high thermally conductive filler (e.g. a ceramic filler such as alumina or boron oxide) is added to the siloxane resin to increase heat transfer efficiency, and the mixture is then shaped into a sheet, a pad, a belt, or a film. The amount of thermally conductive filler introduced into the siloxane resin is often greater than 85 wt % of the total weight for a higher heat transfer efficiency of the thermal interface material. More thermally conductive filler results in higher heat transfer efficiency. However, the properties of the resin composition are difficult to appear due to the high filler amount. For example, the conventional thermal interface materials have problems such as poor electrical insulation, insufficient softness, insufficient mechanical strength, and insufficient thermal resistance. The main problem limiting their application is that the thermal interface materials cannot be roll coated, which is only processed by hot pressing to greatly limit their application.
A thermally conductive, electrically insulating, and coatable resin composition is called to overcome the problems of the thermally conductive filler those are overly added (e.g. low electrical insulation and mechanical strength of the thermal interface material).
One embodiment of the disclosure provides a resin composition, including: 1 part by mole of (a) aromatic epoxy resin monomer; 0.25 to 1 part by mole of (b) cycloaliphatic epoxy resin monomer; and 1 to 9 parts by mole of (c) aliphatic epoxy resin monomer.
One embodiment of the disclosure provides a method for manufacturing a thermally conductive material, including: mixing 1 part by mole of (a) aromatic epoxy resin monomer, 0.25 to 1 part by mole of (b) cycloaliphatic epoxy resin monomer; and 1 to 9 parts by mole of (c) aliphatic epoxy resin monomer to form a resin composition; and heating and curing the resin composition to form a thermally conductive material.
A detailed description is given in the following embodiments.
In the following detailed description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. It will be apparent, however, that one or more embodiments may be practiced without these specific details.
One embodiment of the disclosure provides a resin composition, which includes 1 part by mole of (a) aromatic epoxy resin monomer, 0.25 to 1 part by mole of (b) cycloaliphatic epoxy resin monomer, and 1 to 9 parts by mole of (c) aliphatic epoxy resin monomer. The amount of (b) cycloaliphatic epoxy resin monomer that is too high results in a poor heat transfer coefficient of the cured resin composition. The amount of (b) cycloaliphatic epoxy resin monomer that is too low may reduce the compatibility of the resin composition. The amount of (c) aliphatic epoxy resin monomer that is too high may degrade the mechanical properties and lower the heat transfer coefficient of the cured resin composition. The amount of (c) aliphatic epoxy resin monomer that is too low may reduce the softness of the resin composition.
In one embodiment, (a) aromatic epoxy resin monomer has a chemical structure of
wherein Ar is
R1 is —CH2—, —C(CH3)2—, —CH═CH—, —CH═C(CH3)—, —O—, —C≡C—, —C═CH—CO—, —COO—, —CONH—, or —CO—. Each of R2 is independently H, halogen, or C1-8 alkyl group. In one embodiment, (a) aromatic epoxy resin monomer has a structure of
In one embodiment, (b) cycloaliphatic epoxy resin monomer has a chemical structure of
Cy is
R3 is —CH2—, —C(CH3)2—, —CH═CH—, —CH═C(CH3)—, —O—, —C≡C—, —C═CH—CO—, —COO—, —CONH—, or —CO—. Each of R4 is independently H, halogen, or C1-8 alkyl group. In some embodiments, (b) cycloaliphatic epoxy resin monomer has a chemical structure of
In some embodiments, (c) aliphatic epoxy resin monomer has a chemical structure of
R is C1-6 linear alkylene group substituted by hydrogen or C1-8 alkyl group. In some embodiments, (c) aliphatic epoxy resin monomer has a chemical structure of
In some embodiments, the resin composition further includes (d) amine curing agent. Epoxy groups of (a) aromatic epoxy resin monomer, (b) cycloaliphatic epoxy resin monomer, and (c) aliphatic epoxy resin monomer and amino groups of (d) amine curing agent have a molar ratio of 1:1 to 2:1.
In some embodiments, the amine curing agent has a chemical structure of H2N—R5—NH2 or H2N—Ar′—O—R6—O—Ar′—NH2. R5 is
in which is C1-6 alkylene group, and n′=1 to 10. R7 is single bond, —O—, —SO2—, —CH2—, —(CH2)2—, or —C(CF3)2—. Each of R8 is independently H, halogen, or C1-8 alkyl group. R6 is
R9 is single bond, —O—, —SO2—, or —C(CF3)2—. Each of R10 is independently H, halogen, or C1-8 alkyl group. n is an integer of 3 to 12. Ar′ is
(d) Amine curing agent may include cycloaliphatic amine curing agent, aromatic amine curing agent, and aliphatic amine curing agent. In one embodiment, the amine curing agent includes a combination of the cycloaliphatic amine curing agent and the aromatic amine curing agent, which may further enhance the heat transfer coefficient of the cured resin composition.
In some embodiments, the resin composition further includes (e) thermally conductive filler. The total weight of (a) aromatic epoxy resin monomer, (b) cycloaliphatic epoxy resin monomer, and (c) aliphatic epoxy resin monomer and the weight of (e) thermally conductive filler may have a ratio of 70:30 to 5:95. The ratio of (e) thermally conductive filler that is too high may negatively affect the physical properties of the cured resin composition (i.e. flexibility and electrical insulation). (e) Thermally conductive filler can be metal, metal oxide, metal nitride, ceramic, carbon material, or a combination thereof. For example, (e) thermally conductive filler can be copper, gold, nickel, aluminum, or an alloy thereof, alumina, magnesium oxide, zinc oxide, beryllium oxide, boron nitride, aluminum nitride, silicon carbide, tungsten carbide, diamond, graphite, carbon fiber, carbon nanotube, or a combination thereof. In one embodiment, (e) thermally conductive filler is alumina.
One embodiment of the disclosure provides a method for manufacturing a thermally conductive material, which includes mixing 1 part by mole of (a) aromatic epoxy resin monomer, 0.25 to 1 part by mole of (b) cycloaliphatic epoxy resin monomer, and 1 to 9 parts by mole of (c) aliphatic epoxy resin monomer to form a resin composition. The method also heats and cures the resin composition to form a thermally conductive material. In some embodiments, the resin composition further includes (d) amine curing agent. Epoxy groups of (a) aromatic epoxy resin monomer, (b) cycloaliphatic epoxy resin monomer, and (c) aliphatic epoxy resin monomer and amino groups of (d) amine curing agent have a molar ratio of 1:1 to 2:1. In some embodiments, (d) amine curing agent includes a combination of the cycloaliphatic amine curing agent and the aromatic amine curing agent. In some embodiments, the resin composition further includes (e) thermally conductive filler. The total weight of (a) aromatic epoxy resin monomer, (b) cycloaliphatic epoxy resin monomer, and (c) aliphatic epoxy resin monomer and the weight of (e) thermally conductive filler may have a ratio of 70:30 to 5:95.
Below, exemplary embodiments will be described in detail so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.
The abbreviations, names, and structures of epoxy resin monomers and amine curing agents used in following Examples are listed in Table 1.
The heat transfer coefficients of the thermally conductive materials prepared in the following Examples were measured using the standard ASTM-E1461. The volume resistivities of the thermally conductive materials prepared in the following Examples was measured using the standard ASTM-D257. The breakdown voltages of the thermally conductive materials prepared in the following Examples was measured using the standard ASTM-D149.
5 g of the aliphatic epoxy resin monomer NEO and 4.264 g of the cycloaliphatic amine curing agent JER-113 were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
Example 2 was similar to Example 1, and the difference in Example 2 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=8:2). The curing agent type and amount and the curing condition in Example 2 were similar to those in Example 1.
Example 3 was similar to Example 1, and the difference in Example 3 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=6:4). The curing agent type and amount and the curing condition in Example 3 were similar to those in Example 1.
Example 3 was similar to Example 1, and the difference in Example 3 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=5:5). The curing agent type and amount and the curing condition in Example 4 were similar to those in Example 1.
As shown in Table 2, the thermally conductive materials from the combinations of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer epalloy 5000 had higher heat transfer coefficients and higher breakdown voltages than those of the thermally conductive material from only the aliphatic epoxy resin monomer NEO.
Example 5 was similar to Example 1, and the difference in Example 5 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=8:2). The curing agent type and amount and the curing condition in Example 5 were similar to those in Example 1.
Example 6 was similar to Example 1, and the difference in Example 6 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=7:3). The curing agent type and amount and the curing condition in Example 6 were similar to those in Example 1.
Example 7 was similar to Example 1, and the difference in Example 7 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=6:4). The curing agent type and amount and the curing condition in Example 7 were similar to those in Example 1.
Example 8 was similar to Example 1, and the difference in Example 8 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=5:5). The curing agent type and amount and the curing condition in Example 8 were similar to those in Example 1.
As shown in Table 3, the thermally conductive material from the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000 with a molar ratio of 6:4 (in the combination of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000) had a higher heat transfer coefficient, a higher volume resistivity, and a higher breakdown voltage.
Example 9 was similar to Example 1, and the difference in Example 9 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=7:2:1). The curing agent type and amount and the curing condition in Example 9 were similar to those in Example 1.
Example 10 was similar to Example 1, and the difference in Example 10 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=6:1:3). The curing agent type and amount and the curing condition in Example 10 were similar to those in Example 1.
Example 11 was similar to Example 1, and the difference in Example 11 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4). The curing agent type and amount and the curing condition in Example 11 were similar to those in Example 1.
Example 12 was similar to Example 1, and the difference in Example 12 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:2:3). The curing agent type and amount and the curing condition in Example 12 were similar to those in Example 1.
As shown in Tables 2 and 4, the thermally conductive materials from the combinations of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 had higher heat transfer coefficients than those of the thermally conductive materials from the combinations of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer epalloy 5000.
Example 13 was similar to Example 1, and the difference in Example 13 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=7:2:1). The curing agent type and amount and the curing condition in Example 13 were similar to those in Example 1.
Example 14 was similar to Example 1, and the difference in Example 14 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=6:1:3). The curing agent type and amount and the curing condition in Example 14 were similar to those in Example 1.
Example 15 was similar to Example 1, and the difference in Example 15 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4). The curing agent type and amount and the curing condition in Example 15 were similar to those in Example 1.
Example 16 was similar to Example 1, and the difference in Example 16 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:2:3). The curing agent type and amount and the curing condition in Example 16 were similar to those in Example 1.
As shown in Tables 3 and 5, the thermally conductive materials from the combinations of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 had higher heat transfer coefficients than those of the thermally conductive materials from the combinations of the aliphatic epoxy resin monomer NEO and the cycloaliphatic epoxy resin monomer YX8000.
5 g of a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4), and 1.148 g of a combination of the cycloaliphatic amine curing agent JER-113 and 0.954 g of the aromatic amine curing agent DDM (molar ratio=1:1) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
Example 18 was similar to Example 17, and the difference in Example 18 was the amine curing agent being replaced with 1.148 g of a combination of the cycloaliphatic amine curing agent JER-113 and 1.022 g the aromatic amine curing agent DDE (molar ratio=1:1). The other curing conditions in Example 18 were similar to those in Example 17.
Example 19 was similar to Example 17, and the difference in Example 19 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.359 g of the aromatic amine curing agent CUAHARD-MED (molar ratio=1:1). The other curing conditions in Example 19 were similar to those in Example 17.
Example 20 was similar to Example 17, and the difference in Example 20 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.089 g of the aromatic amine curing agent MDA (molar ratio=1:1). The other curing conditions in Example 20 were similar to those in Example 17.
As shown in the comparison of Example 15 in Table 5 and Table 6, the combinations of the cycloaliphatic amine curing agent JER-113 and the aromatic amine curing agents could increase the heat transfer coefficients of the thermally conductive materials.
Example 21 was similar to Example 17, and the difference in Example 21 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.195 g of the aromatic amine curing agent DDS (molar ratio=1:1). The other curing conditions in Example 21 were similar to those in Example 17.
Example 22 was similar to Example 17, and the difference in Example 22 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.407 g of the aromatic amine curing agent TPE-Q (molar ratio=1:1). The other curing conditions in Example 22 were similar to those in Example 17.
Example 23 was similar to Example 17, and the difference in Example 23 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.771 g of the aromatic amine curing agent BAPB (molar ratio=1:1). The other curing conditions in Example 23 were similar to those in Example 17.
Example 24 was similar to Example 17, and the difference in Example 24 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.022 g of the aromatic amine curing agent m-Tolidine (molar ratio=1:1). The other curing conditions in Example 24 were similar to those in Example 17.
1013
1013
1011
1012
As shown in the comparison of Example 15 in Table 5 and Table 7, the combinations of the cycloaliphatic amine curing agent JER-113 and the aromatic amine curing agents could increase the heat transfer coefficients or the breakdown voltages of the thermally conductive materials.
Example 25 was similar to Example 17, and the difference in Example 25 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 0.550 g of the cycloaliphatic amine curing agent CHQ (molar ratio=1:1). The other curing conditions in Example 25 were similar to those in Example 17.
Example 26 was similar to Example 17, and the difference in Example 26 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.013 g of the cycloaliphatic amine curing agent DACH (molar ratio=1:1). The other curing conditions in Example 26 were similar to those in Example 17.
Example 27 was similar to Example 17, and the difference in Example 27 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.718 g of the aromatic amine curing agent CUA-4 (molar ratio=1:1). The other curing conditions in Example 27 were similar to those in Example 17.
Example 28 was similar to Example 17, and the difference in Example 28 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 2.349 g of the aromatic amine curing agent ELASMER 250P (molar ratio=1:1).
The other curing conditions in Example 28 were similar to those in Example 17.
1013
1012
1012
1011
As shown in the comparison of Example 15 in Table 5 and Table 8, the combinations of the cycloaliphatic amine curing agent JER-113 and the aromatic amine curing agents could increase the heat transfer coefficients of the thermally conductive materials.
5 g of the aliphatic epoxy resin monomer BUT and 3.870 g of the cycloaliphatic amine curing agent JER-113 were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
Example 30 was similar to Example 29, and the difference in Example 30 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=8:2). The curing agent type and amount and the curing condition in Example 30 were similar to those in Example 29.
Example 31 was similar to Example 29, and the difference in Example 31 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=6:4). The curing agent type and amount and the curing condition in Example 31 were similar to those in Example 29.
Example 32 was similar to Example 29, and the difference in Example 32 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer epalloy 5000 (molar ratio=5:5). The curing agent type and amount and the curing condition in Example 32 were similar to those in Example 29.
1014
1012
1012
1012
As shown in Table 9, the thermally conductive materials made from the combinations of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer epalloy 5000 had higher heat transfer coefficients and breakdown voltages than those of the thermally conductive material made from only the aliphatic epoxy resin BUT.
Example 33 was similar to Example 29, and the difference in Example 33 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=8:2). The curing agent type and amount and the curing condition in Example 33 were similar to those in Example 29.
Example 34 was similar to Example 29, and the difference in Example 34 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=7:3). The curing agent type and amount and the curing condition in Example 34 were similar to those in Example 29.
Example 35 was similar to Example 29, and the difference in Example 35 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=6:4). The curing agent type and amount and the curing condition in Example 35 were similar to those in Example 29.
Example 36 was similar to Example 29, and the difference in Example 36 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000 (molar ratio=5:5). The curing agent type and amount and the curing condition in Example 36 were similar to those in Example 29.
1013
1013
1014
1012
As shown in Table 10, the thermally conductive materials made from the combination of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000 with a higher molar ratio of the cycloaliphatic epoxy resin monomer YX8000 had higher heat transfer coefficients and higher breakdown voltages.
Example 37 was similar to Example 29, and the difference in Example 37 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=7:2:1). The curing agent type and amount and the curing condition in Example 37 were similar to those in Example 29.
Example 38 was similar to Example 29, and the difference in Example 38 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=6:1:3). The curing agent type and amount and the curing condition in Example 38 were similar to those in Example 29.
Example 39 was similar to Example 29, and the difference in Example 39 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin epalloy monomer 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4). The curing agent type and amount and the curing condition in Example 39 were similar to those in Example 29.
Example 40 was similar to Example 29, and the difference in Example 40 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:2:3). The curing agent type and amount and the curing condition in Example 40 were similar to those in Example 29.
1012
1013
1013
1014
As shown in Tables 9 and 11, the thermally conductive materials made from the combinations of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer epalloy 5000, and the aromatic epoxy resin monomer YX4000 had higher heat transfer coefficients than those of the thermally conductive materials made from the combinations of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer epalloy 5000.
Example 41 was similar to Example 29, and the difference in Example 41 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=7:2:1). The curing agent type and amount and the curing condition in Example 41 were similar to those in Example 29.
Example 42 was similar to Example 29, and the difference in Example 42 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=6:1:3). The curing agent type and amount and the curing condition in Example 42 were similar to those in Example 29.
Example 43 was similar to Example 29, and the difference in Example 43 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4). The curing agent type and amount and the curing condition in Example 43 were similar to those in Example 29.
Example 44 was similar to Example 29, and the difference in Example 44 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:2:3). The curing agent type and amount and the curing condition in Example 44 were similar to those in Example 29.
1013
1013
1014
1013
As shown in Tables 10 and 12, the thermally conductive materials made from the combinations of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 had higher heat transfer coefficients than those of the thermally conductive materials made from the combinations of the aliphatic epoxy resin monomer BUT and the cycloaliphatic epoxy resin monomer YX8000.
5 g of a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4), and 1.117 g of a combination of the cycloaliphatic amine curing agent JER-113 and 0.929 g of the aromatic amine curing agent DDM (molar ratio=1:1) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
Example 46 was similar to Example 45, and the difference in Example 46 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 0.995 g the aromatic amine curing agent DDE (molar ratio=1:1). The other curing conditions in Example 46 were similar to those in Example 45.
Example 47 was similar to Example 45, and the difference in Example 47 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.323 g the aromatic amine curing agent CUAHARD-MED (molar ratio=1:1). The other curing conditions in Example 47 were similar to those in Example 45.
Example 48 was similar to Example 45, and the difference in Example 48 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.060 g the aromatic amine curing agent MDA (molar ratio=1:1). The other curing conditions in Example 48 were similar to those in Example 45.
1012
1011
1011
1012
As shown in the comparison of Example 43 in Table 12 and Table 13, the combinations of the cycloaliphatic amine curing agent JER-113 and the some aromatic amine curing agents (e.g. DDE and CUAHARD-MED) could increase the heat transfer coefficients of the thermally conductive materials.
Example 49 was similar to Example 45, and the difference in Example 49 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.163 g the aromatic amine curing agent DDS (molar ratio=1:1). The other curing conditions in Example 49 were similar to those in Example 45.
Example 50 was similar to Example 45, and the difference in Example 50 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.370 g the aromatic amine curing agent TPE-Q (molar ratio=1:1). The other curing conditions in Example 50 were similar to those in Example 45.
Example 51 was similar to Example 45, and the difference in Example 51 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.724 g the aromatic amine curing agent BAPB (molar ratio=1:1). The other curing conditions in Example 51 were similar to those in Example 45.
Example 52 was similar to Example 45, and the difference in Example 52 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 0.995 g the aromatic amine curing agent m-Tolidine (molar ratio=1:1). The other curing conditions in Example 52 were similar to those in Example 45.
1013
1012
1012
1013
As shown in the comparison of Example 43 in Table 12 and Table 14, the combination of the cycloaliphatic amine curing agent JER-113 and the some aromatic amine curing agents (e.g. BAPB) could increase the heat transfer coefficient of the thermally conductive material.
Example 53 was similar to Example 45, and the difference in Example 53 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 0.535 g the cycloaliphatic amine curing agent CHD (molar ratio=1:1). The other curing conditions in Example 53 were similar to those in Example 45.
Example 54 was similar to Example 45, and the difference in Example 54 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 0.986 g the cycloaliphatic amine curing agent DACH (molar ratio=1:1). The other curing conditions in Example 54 were similar to those in Example 45.
Example 55 was similar to Example 45, and the difference in Example 55 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.673 g the aromatic amine curing agent CUA-4 (molar ratio=1:1). The other curing conditions in Example 55 were similar to those in Example 45.
Example 56 was similar to Example 45, and the difference in Example 56 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 2.286 g the aromatic amine curing agent ELASMER 250P (molar ratio=1:1). The other curing conditions in Example 56 were similar to those in Example 45.
1013
1013
1012
1011
As shown in the comparison of Example 43 in Table 12 and Table 15, the combinations of the two amine curing agent could increase the heat transfer coefficients of the thermally conductive materials.
5 g of the aromatic epoxy resin monomer 828 and 1.642 g of the aromatic amine curing agent DDS were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
5 g of the aliphatic epoxy resin monomer NEO and 4.264 g of the cycloaliphatic amine curing agent JER-113 were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
5 g of the aliphatic epoxy resin monomer BUT and 3.870 g of the cycloaliphatic amine curing agent JER-113 were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining a thermally conductive material.
1016
1013
1014
As shown in Table 16, the thermally conductive material from the only one epoxy resin and the only one amine curing agent had low heat transfer coefficients.
5 g of a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4), 2.295 g of the cycloaliphatic amine curing agent JER-113, and 29.19 g of the high thermally conductive filler Al2O3 (occupying 80 wt % of the thermally conductive material) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining the thermally conductive material.
Example 58 was similar to Example 57, and the difference in Example 58 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 1.771 g the aromatic amine curing agent BAPB (molar ratio=1:1). The other curing conditions in Example 58 were similar to those in Example 57.
Example 59 was similar to Example 57, and the difference in Example 59 was the amine curing agent being replaced with 1.148 g of the cycloaliphatic amine curing agent JER-113 and 2.349 g the aromatic amine curing agent ELASMER 250P (molar ratio=1:1). The other curing conditions in Example 59 were similar to those in Example 57.
1011
1011
1011
As shown in Table 17, the high thermally conductive filler could increase the heat transfer coefficients of the thermally conductive materials. On the other hand, the combinations of the cycloaliphatic amine curing agent and the aromatic amine curing agent could further increase the heat transfer coefficients of the thermally conductive materials.
5 g of a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4), 2.234 g of the cycloaliphatic amine curing agent JER-113, and 28.936 g of the high thermally conductive filler Al2O3 (occupying 80 wt % of the thermally conductive material) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining the thermally conductive material.
Example 61 was similar to Example 60, and the difference in Example 61 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 1.724 g the aromatic amine curing agent BAPB (molar ratio=1:1). The other curing conditions in Example 61 were similar to those in Example 60.
Example 62 was similar to Example 60, and the difference in Example 62 was the amine curing agent being replaced with 1.117 g of the cycloaliphatic amine curing agent JER-113 and 2.286 g the aromatic amine curing agent ELASMER 250P (molar ratio=1:1). The other curing conditions in Example 62 were similar to those in Example 60.
1011
1011
1011
As shown in Table 18, the high thermally conductive filler could increase the heat transfer coefficients of the thermally conductive materials. On the other hand, the combinations of the cycloaliphatic amine curing agent and the aromatic amine curing agent could further increase the heat transfer coefficients of the thermally conductive materials.
5 g of a combination of the aliphatic epoxy resin monomer NEO, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=5:1:4), 1.148 g of the cycloaliphatic amine curing agent JER-113 and 2.349 g of the aromatic amine curing agent ELASMER 250P, and 56.865 g of the high thermally conductive filler Al2O3 (occupying 87 wt % of the thermally conductive material) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining the thermally conductive material.
Example 64 was similar to Example 63, and the difference in Example 64 was the amount high thermally conductive filler Al2O3 being increased to 112.89 g (93 wt %). The other curing conditions in Example 64 were similar to those in Example 63.
Example 65 was similar to Example 63, and the difference in Example 65 was the amount high thermally conductive filler Al2O3 being increased to 161.443 g (95 wt %). The other curing conditions in Example 65 were similar to those in Example 63.
1012
1010
1010
As shown in Table 19, increasing the amounts of the high thermally conductive filler could increase the heat transfer coefficients of the thermally conductive materials.
5 g of the aromatic epoxy resin monomer 828, 1.642 g of the aromatic amine curing agent DDS, and 26.568 g of the high thermally conductive filler Al2O3 (occupying 80 wt % of the thermally conductive material) were evenly mixed, and then put into an oven at 150° C. for 1 hour to be cured for obtaining the thermally conductive material.
108
Comparative Example 5 was similar to Example 29, and the difference in Comparative Example 5 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=8.9:0.1:1). The amine curing agent type and amount in Comparative Example 5 were similar to those in Example 29. Because the resin composition had an incompatible problem (e.g. phase separation), which was not further cured.
Comparative Example 6 was similar to Example 29, and the difference in Comparative Example 6 was 5 g of the epoxy resin monomer being replaced with a combination of the aliphatic epoxy resin monomer BUT, the cycloaliphatic epoxy resin monomer YX8000, and the aromatic epoxy resin monomer YX4000 (molar ratio=0.5:1:1). The amine curing agent type and amount and the curing conditions in Comparative Example 6 were similar to those in Example 29. The cured resin composition was rigid, hard, brittle, and cracked, and its properties could not be measured.
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples be considered as exemplary only, with the true scope of the disclosure being indicated by the following claims and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 107100633 | Jan 2018 | TW | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4283521 | Jones | Aug 1981 | A |
| 6060539 | Hermansen et al. | May 2000 | A |
| 7022410 | Tonapi et al. | Apr 2006 | B2 |
| 7109288 | Akatsuka et al. | Sep 2006 | B2 |
| 7297399 | Zhang et al. | Nov 2007 | B2 |
| 7405246 | Rubinsztajn | Jul 2008 | B2 |
| 7550097 | Tonapi et al. | Jun 2009 | B2 |
| 7662307 | Chiou et al. | Feb 2010 | B2 |
| 7797808 | Zhang et al. | Sep 2010 | B2 |
| 8530566 | Lin et al. | Sep 2013 | B2 |
| 9296916 | Peters et al. | Mar 2016 | B2 |
| 9371233 | Lin et al. | Jun 2016 | B2 |
| 9441069 | Arita et al. | Sep 2016 | B2 |
| 9643221 | Eda et al. | May 2017 | B2 |
| 20040224163 | Tobita et al. | Nov 2004 | A1 |
| 20050049352 | Rubinsztajn et al. | Mar 2005 | A1 |
| 20050170188 | Campbell et al. | Aug 2005 | A1 |
| 20060275608 | Tonapi et al. | Dec 2006 | A1 |
| 20060293172 | Rubinsztajn et al. | Dec 2006 | A1 |
| 20170096577 | Abrami et al. | Apr 2017 | A1 |
| 20170145247 | Ho et al. | May 2017 | A1 |
| 20170158932 | Liu et al. | Jun 2017 | A1 |
| 20170158934 | Liu et al. | Jun 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 102858837 | Jan 2013 | CN |
| S62-89720 | Apr 1987 | JP |
| H3-72522 | Mar 1991 | JP |
| H4-185630 | Jul 1992 | JP |
| 2003-147046 | May 2003 | JP |
| 2004-27005 | Jan 2004 | JP |
| 2004-111501 | Apr 2004 | JP |
| 2017-101237 | Jun 2017 | JP |
| 200533714 | Oct 2005 | TW |
| 201431900 | Aug 2014 | TW |
| I475103 | Mar 2015 | TW |
| WO 2015005211 | Jan 2015 | WO |
| WO 2017191801 | Nov 2017 | WO |
| Entry |
|---|
| Office Action issued in Taiwan Patent Application No. 107127273 dated Mar. 6, 2018. |
| Japanese Office Action for Application No. 2019-000418 dated Mar. 3, 2020 w/ English translation. |
| Number | Date | Country | |
|---|---|---|---|
| 20190211138 A1 | Jul 2019 | US |