The present invention relates to a heat exchanger, and, more particularly, to a resin heat exchanger unit, in which a pipe and fins for increasing heat exchange efficiency are integrally molded, and a heat exchanger using the resin heat exchanger unit.
In the prior art, there has been used a heat exchanger in which metal fins are joined with a metal tube or pipe by welding or the like, and the joined fins and metal tube or pipe are integrated with a header tank by caulking or the like. Recently, in order to reduce the impact on the global environment, there is a growing need for improvement of fuel efficiency owing to lightening of a vehicle, such as an automobile. Also in the fields of household appliances and OA, the reduction in size and weight is strongly desired. In response to those needs, there have been intensified tendencies to substitute materials or optimize shapes for the prior art heat exchanger. Specifically, there has been proposed an all-resin heat exchanger in which all components are resinified. The resinified components can realize the extension of the degree of freedom of the shape, and it is considered that if the heat exchange efficiency can be ensured, it is very advantageous in terms of reduction of weight and size of the entire apparatus.
As an example of a resin heat exchanger, Patent Document 1 discloses a technique that a plurality of resin tubes having a single refrigerant circulation hole are individually set in a mold so as to penetrate through a cavity, and the tubes set in the mold are injection-molded, whereby the resin tubes and a seat plate are connected to each other. Patent document 2 discloses a technique that a plurality of flat perforated tubes having a plurality of refrigerant circulation holes are each set in a mold in the same manner as for Patent Document 1, and a resin material is injected, whereby the tubes and a seat plate are integrally molded.
Patent Document 3 discloses a technique that grooved sheets formed of a resin are joined so as to face each other, whereby a tube having a refrigerant passage is formed, and, at the same time, tanks are formed at the both ends.
The resin heat exchanger disclosed in Patent Document 4 has components each formed of a resin material, and plates (headers of tubes) formed by double injection are provided at the both front ends of the tubes, and a header tank is joined with the plate.
However, in the methods disclosed in Patent Documents 1 and 2, previously prepared straight tubes or sets of a plurality of tubes are inserted in different molds to be joined by thermal fusion bonding. However, the process is complex and lack of reliability.
In the method disclosed in Patent Document 3, two sheets are previously molded, and they are joined with each other. However, since they are joined with an adhesive, the process is complex, and, at the same time, the joint lacks the reliability. In the method disclosed in Patent Document 4, a molded body including straight tubes and fins is previously molded, and the molded body is joined with the headers of tubes by thermal fusion bonding. However, the process is complex, and the joint lacks reliability. In Patent Document 4, although the fins are also provided at the tube, the fin serves as a joint between the two straight tubes, and therefore, the heat exchange efficiency of the heat exchanger is not satisfactorily effective.
As a metal heat exchanger, there has been well-known one in which a plurality of fins are provided at a pipe or a tube having integrated straight portions and curved portions. However, also in this metal heat exchanger, the fins and the pipe or tube are joined by a separate process, for example, by welding.
Regardless of the material, there has not been known so far a heat exchanger in which a large number of fins, straight portions, and curved portions are integrally constituted as a heat exchanger unit.
Thus, it is an object of the present invention to provide a resin heat exchanger unit, in which a resin pipe having straight portions and curved portions and resin fins are integrally molded and there can be realized high reliability, high heat exchange efficiency, and a simple manufacturing process, and a heat exchanger using the resin heat exchanger unit.
The resin heat exchanger unit of the present invention is characterized by including a resin pipe and a plurality of resin fins integrally injection-molded together, the resin pipe having straight portions and curved portions provided alternatively and continuously, and the resin fins being connected to the pipe.
The heat exchanger of the invention is characterized in that a plurality of the resin heat exchanger units are joined through a header tank.
A method for manufacturing a resin heat exchanger unit, according to the invention is characterized by including injecting a molten resin into a pipe cavity of a mold, the pipe cavity having on its one end a pressure port provided with a floating core and on its other end an outlet, pressure-injecting a pressurized fluid through the pressure port after the injection of the molten resin, and moving the floating core to the outlet side, and, at the same time, extruding the molten resin from the outlet.
The present invention can provide at low cost a resin heat exchanger unit, which is highly reliable and has high heat exchange efficiency, and a heat exchanger using the resin heat exchanger unit.
Hereinafter, the present invention will be described in detail with reference to the drawings.
The resin heat exchanger unit shown in
The resin heat exchanger unit shown in
The average thickness of the fin 4 is preferably not less than Tp/20 (Tp is the average thickness of the pipe 1) in terms of intensity, and it is preferably not more than Tp in terms of heat exchange efficiency and ensuring the smoothness of the inner surface of the pipe. When the average thickness of the fin 4 is less than Tp/20, there may occur intensity problems that, for example, the fin 4 is easily broken. Meanwhile, when the average thickness of the fin 4 is more than Tp, the heat exchange efficiency may be reduced, or the effect of weight reduction due to resinification may be reduced. When the portion of the fin 4 in contact with the pipe 1 has a thickness of more than Tp, the inner surface of the pipe 1 may be rendered uneven by shrinkage of resin upon molding, whereby there may occur problems that, for example, the unevenness disturbs the flow of a fluid used as a heat exchange medium and passing through the pipe 1 or causes noises.
The thickness of the front end of the fin 4 is preferably not less than Tr/10 and not more than Tr (Tr is the thickness of the portion of the fin 4 in contact with the pipe 1). When the thickness of the front end of the fin 4 is less than Tr/10, there may cause intensity problems that, for example, the front end of the fin 4 is easily chipped. Meanwhile, when the thickness of the front end of the fin 4 is more than Tr, the moldability may be reduced such as deterioration of separation performance from a mold upon injection-molding, whereby the heat exchange efficiency may be reduced.
The greater the number of the fins 4, the better in terms of the heat exchange efficiency. However, the number of the fins 4 is preferably approximately 2 to 30 fins per 1 cm length of the pipe 1, and particularly approximately 3 to 20 fins. When the number of the fins 4 is less than 2, the expected heat exchange efficiency may not be obtained. Meanwhile, when the number of the fins 4 is more than 30, there may occur an inconvenience in the separation performance from a mold in the injection-molding, a molten resin may not be satisfactorily filled in the fins 4 due to the significant reduction of the thickness of the fins 4, or the intensity of the fin 40 may be reduced.
The fin 4 is not limited to the one perpendicular to the axial direction of the straight portion 2 of the pipe 1, and the fins 4 may be provided in parallel or diagonally relative to the axial direction of the straight portion 2 of the pipe 1. However, in terms of the heat exchange efficiency and the injection moldability, it is preferable that the fin 4 is perpendicular to the axial direction of the straight portion 2 of the pipe 1. The shape of the fin 4 is not limited to a disk shape, and may be suitably set according to the design conditions of a heat exchanger. Specifically, the fins as shown in
The example shown in
Although the resin used in the present invention includes any thermoplastic resin and thermosetting resin that enable injection-molding of a hollow body, the thermoplastic resin is preferably used in terms of hollow moldability in the injection-molding. The thermoplastic resin includes various resins, for example, polystyrene, a polystyrene-based resin such as AS and ABS, a polyolefin-based resin such as polypropylene and polyethylene, a polyamide-based resin such as nylon 66 or nylon 6, a polyester-based resin such as PET and PBT, POM, polycarbonate, PPS, modified PPE, a PMMA resin, and a polyvinyl chloride resin. Further, there may be used those thermoplastic resins containing a reinforcing material, such as glass fiber, talc, calcium carbonate, or kaolin, or an inorganic filler. If the thermosetting resin is an injection moldable resin that is known as BCM such as unsaturated polyester resin and phenol resin, it can be used in the present invention.
The resin heat exchanger unit of the present invention can be used alone; however, as shown in
In the heat exchanger of the present invention, hot water is flowed from one side of a pipe, and cold air is sent to fins by a fan or the like, whereby the temperature of the hot water can be lowered. The heat exchange efficiency can be arbitrarily designed by, for example, the number of the resin materials and the fins used in the heat exchanger, the thickness of the fin, the diameter of the pipe or the length from the pipe to the fin, and the number of the resin heat exchanger units. Further, the heat exchanger of the invention has advantages, for example, that compared with the conventional metal heat exchanger, the weight and cost can be further reduced, and, at the same time, a space area can be reduced due to the degree of freedom of the design. Furthermore, relative to the conventional resin heat exchanger, the heat exchanger of the present invention uses the units with integrally molded components important for a heat exchanger, such as a pipe and fins, and therefore, a post-process such as welding or deposition is not required. Thus, the present invention can realize a resin heat exchanger with high reliability, high heat exchange efficiency, and low manufacturing cost.
Next, a method for manufacturing a resin heat exchanger unit of the present invention will be described.
The resin heat exchanger unit of the present invention is manufactured by, for example, gas-assist injection molding (for example, Japanese Patent Application Publication No. 57-14968), water-assist injection molding (for example, plastic age (September 2007, page 106)), and a method using a floating core (for example, Japanese Patent Application Publication No. 7-20646). In order to maintain uniformity of the inside diameter of the pipe over the entire area of the pipe, the injection-molding method using a floating core is preferably used. A more preferable injection-molding method includes injecting a molten resin into a pipe cavity of a mold, the pipe cavity having on its one end a pressure port provided with a floating core and on its other end an outlet, pressure-injecting a pressurized fluid through the pressure port after the injection of the molten resin, and moving the floating core to the outlet side, and, at the same time, extruding the molten resin from the outlet.
Hereinafter, a method for manufacturing the resin heat exchanger unit of
As shown in
An end 7 which is one end of the cavity is provided with a floating core 5 and a pressure port 6. The floating core 5 has a diameter corresponding to the inside diameter of the pipe. A pressurized fluid for pressing and moving the floating core 5 to the other end 8 of the cavity is pressure-injected through the pressure port 6.
The floating core 5 is provided in the cavity so that its back faces the pressure port 6, whereby the floating core 5 can be pressed by the pressurized fluid pressure-injected through the pressure port 6. The floating core 5 can be formed of a metal, such as copper, iron, aluminum, stainless, and steel, or can be formed of a resin. The shape of the floating core 5 is not limited to a spherical shape shown in
The pressure port 6 is connected to a pressurized fluid system (not shown) for pressure-injecting/discharging a pressurized fluid. The pressure port 6 applies the pressurized fluid, supplied from the pressurized fluid system, to the back surface of the floating core 5 and presses and moves the floating core 5 to the other end 8 of the cavity. The pressurized fluid is pressure-injected through the pressure port 6 after the inside of the cavity is filled with a resin. A resin gate (not shown) is provided slightly away from the floating core 5 so that in the injection of the molten resin through the resin gate, while the floating core 5 is pressed against the pressure port 6 without floating, the inside of the cavity can be filled with the molten resin.
A communicating port 9 is provided on the other end 8 side of the cavity, and an excess resin storage cavity 10 is communicated with the cavity 1′ through the communicating port 9. Although the communicating port 9 has a size allowing the passage of the floating core 5, it is preferable that the floating core 5 has a slightly constricted shape for the sake of ease of the following process such as cutting process. When the pressurized fluid is pressure-injected through the pressure port 6 in such a state that the cavity 1′ is filled with a resin, an excess resin is extruded from the cavity 1′ by moving the floating core 5. The excess resin storage cavity 10 has a capacity capable of satisfactorily storing the excess resin and the floating core 5.
Although the means that opens and closes the communicating port 9 is not limited especially, there is means that opens and closes the communicating port 9 by moving a receiving shaft forward and backward by means of, for example, hydraulic pressure. Specifically, the receiving shaft passes through substantially the central portion of the excess resin storage cavity 10 to be retractably inserted toward the communicating port 9. When the receiving shaft advances, the peripheral edge of the front end is in press contact with the peripheral wall of the communicating port 9 to close the communicating port 9. The receiving shaft advances and retracts, whereby the communicating port 9 is opened and closed. Alternatively, the communicating port can be opened and closed by, for example, oil pressure, using a simply slidably opening/closing bar or the like.
Next, a specific procedure of injection-molding using the mold shown in
As shown in
Then, as shown in
As the pressurized fluid, there is used a gas or liquid that does not react with or is not compatible with the resin to be used under injection-molding temperature and pressure conditions. Specifically, nitrogen gas, carbon dioxide gas, air, glycerin, liquid paraffin, and so on can be used; however, an inert gas including nitrogen gas is preferably used. In the pressure-injection of the pressurized fluid, for example when a gas such as nitrogen gas is used as the pressurized fluid, a pressurized gas as the pressurized fluid, whose pressure is raised by a compressor, is previously stored in an accumulator (not shown), and the pressurized gas is introduced into the pressure port 6 through a pipe, whereby the pressurized gas can be pressure-injected. Alternatively, the pressurized gas whose pressure is raised by a compressor is directly supplied to the pressure port 6, whereby the pressurized gas can be pressure-injected. Although the pressure of the pressurized gas supplied to the pressure port 6 is different depending on the kind of a resin to be used and the size of the floating core 5, it is usually approximately 4.90 to 29.42 MPa (50 to 300 kg/cm2G).
Subsequently, preferably, the resin is cooled while maintaining the inner pressure in a mold, and the pressurized fluid in the hollow 11 is then discharged; thereafter, a molded product is removed. When a gas is used as the pressurized fluid, the pressurized fluid can be discharged by opening the pressure port 6 to the atmosphere. The pressurized fluid may be recovered into a recovery tank (not shown) for circulation utilization.
A secondary molded product (not shown) molded in the excess resin storage cavity 10 is separated from the removed molded product, whereby the resin heat exchanger unit of the present invention can be obtained. Although the secondary molded product can be easily separated by, for example, being cut near the communicating port, the communicating port 9 is previously formed into a constricted shape, whereby the secondary molded product can be more easily cut off to be separated.
A resin heat exchanger unit of the following size shown in
[Pipe]
Outer diameter: 10 mm
Inner diameter: 7 mm
Average thickness: 1.5 mm
Length of straight portion: 105 mm, 70 mm
Curved portion: R15 mm
[Fin]
Disk shape of 20 mmφ
Average thickness: 0.85 mm
Thickness of root: 1 mm
Thickness of front end: 0.65 mm
Number: 58 (4 fins/1 cm length of the pipe)
As the floating core, a steel ball with a diameter of 7 mm is used, and a gas generator for gas hollow injection-molding (“air mold” from Asahi Engineering CO., LTD) is used for the supply of a pressurized fluid. As the pressurized fluid, nitrogen gas is used. As a resin, a polyamide 66 resin (“LEONA 1300G from Asahi Kasei Chemicals Corporation) containing 33% by weight of glass fiber is used.
As shown in
When hot water is flowed from one side of the pipe of the obtained heat exchanger unit to be discharged from the other side, the temperature of the discharged hot water is lowered by 1.5° C. (ΔT=1.5° C.), and thus the obtained heat exchanger unit satisfactorily serves as a heat exchanger. When the durability is tested under such conditions that the hot water at 80° C. is flowed for 1000 hours while being subjected to the inner pressure of 0.15 MPa (1.5 Kg/cm2), the heat exchanger unit is highly durable as a heat exchanger without causing the increase of the resistance to flow, the occurrence of cracks, and so on.
When three resin heat exchanger units are joined through a header tank, ΔT=5° C., excellent performances as a heat exchanger are exhibited.
A resin heat exchanger unit (similar to one shown in
A resin heat exchanger unit is obtained in the same manner as for Example 1, except that each of the fins has a rectangular plate-like shape, and the adjacent fins are continuously connected to each other (this resin heat exchanger unit is similar to one shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-132990 | May 2008 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2009/054878 | 3/13/2009 | WO | 00 | 5/7/2010 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2009/142055 | 11/26/2009 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4132264 | Furlong | Jan 1979 | A |
| 4926933 | Gray | May 1990 | A |
| 5948343 | Hiroki et al. | Sep 1999 | A |
| 20020088526 | Lee | Jul 2002 | A1 |
| 20030024120 | Adams et al. | Feb 2003 | A1 |
| 20040058030 | Romanski et al. | Mar 2004 | A1 |
| 20050274504 | Torigoe | Dec 2005 | A1 |
| 20060168812 | Insalaco | Aug 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 58-75584 | Jun 1981 | JP |
| 57-183494 | Nov 1982 | JP |
| 61-11594 | Jan 1986 | JP |
| 2002-225138 | Aug 2002 | JP |
| 3488470 | Jan 2004 | JP |
| 2004-108644 | Apr 2004 | JP |
| 2004-226056 | Aug 2004 | JP |
| 2006-200816 | Aug 2006 | JP |
| WO 9728953 | Aug 1997 | WO |
| Entry |
|---|
| Office Action for corresponding Japanese Patent Application No. 2008-132990, dated Dec. 11, 2012. |
| International Search Report-PCT/JP2008/054878 dated Jun. 2, 2009. |
| Number | Date | Country | |
|---|---|---|---|
| 20100276133 A1 | Nov 2010 | US |