1. Field of the Invention
This application relates generally to repair of flange holes and, more particularly, to methods for repairing holes in flanges of gas turbine engine casings.
2. Description of Related Art
Because engine casing flanges are made to stringent dimensional requirements in terms of I.D. and O.D. dimensions, flatness and hole location, and materials/mechanical performance requirements, the heat input and during the repair and resultant distortion needs to be controlled to prevent flange distortion or a degradation in material microstructure around holes in the flange and mechanical performance.
Casing holes can become oversized in service due to wear or corrosion. Restoration of the inside diameter of small diameter holes is difficult to achieve with conventional fusion welding processes due to weld distortion and mechanical property degradation. One particular type of corrosion is corrosion pitting which has been found in gas turbine engine compressor casing flange bolt holes.
There is, thus, a need for resistance weld repair of casing flange holes that avoids fusion discontinuities and excessive distortion. There is also a need for a weld repair of casing flange holes that minimizes weld distortion while optimizing the microstructure in the repair area to enhance mechanical performance of the flange around the hole.
A method for repairing at least one degraded bolt hole in a metallic casing flange having first and second sides using resistance welding includes: a) reaming or cleaning and removing at least some corrosion on an inside and around the bolt hole to form a reamed hole; b) mounting the metallic casing flange so that the metallic casing flange floats relative to upper and lower electrodes of a welding machine; c) radially and axially clamping an area of the flange surrounding the reamed hole; d) placing upper and lower filler slugs in the reamed hole; e) placing the upper and lower electrodes against the upper and lower filler slugs and applying a welding current through the upper and lower electrodes while applying pressure forces to the upper and lower filler slugs with the upper and lower electrodes and resistively heating and melting the upper and lower filler slugs respectively to form a weldment; and f) the applying welding current includes pulsing the welding current on and off a first number of cycles.
The method may further include cooling to solidification or cooling to solidification and then in situ tempering a substantially liquid pool formed by the welding current under the pressure of the upper and lower electrodes.
The pulsing may be performed with progressively increasing amounts of current for successive ones of the first number of cycles. The in situ tempering may include applying a tempering current through the upper and lower electrodes and pulsing the tempering current on and off a second number of cycles wherein the tempering current is substantially lower than the welding current.
The pulsing of the welding may be immediately followed by the in situ tempering wherein the tempering current is held substantially constant during the second number of cycles and cooling and solidification of the substantially liquid pool occurs after the first number of cycles. A new bolt hole may be drilled in the weldment.
Boron may be placed between the upper and lower filler slugs and the flange before placing the upper and lower electrodes against the upper and lower filler slugs and applying the welding current.
The resistive heating and melting of the upper and lower filler slugs may be thermally controlled to avoid formation of retained austenite in the solidified liquid pool. The thermally controlling may include maintaining temperature of the substantially liquid pool below a peak temperature at which retained austenite forms in the solidified liquid pool. The upper and lower electrodes may be cooled with water and water temperature may be controlled.
Degraded bolt holes in a metallic flange of a metallic casing may also be repaired using resistance welding first reaming or cleaning and removing at least some corrosion on insides and around degraded bolt holes to form reamed holes and mounting the casing on a rotatable table of or associated with a resistance welding machine so that the metallic casing flange floats relative to upper and lower electrodes of a welding machine. Next, an area of the flange surrounding one of the reamed holes is radially and axially clamped and upper and lower filler slugs are placed in the reamed hole and the weldment is formed as explained above. Weldments are formed in each of the reamed holes using the rotatable table to position each of the reamed holes with respect to the upper and lower electrodes.
A welding arrangement for performing repairs of degraded bolt holes in a metallic flange of a metallic casing includes the casing mounted on a rotatable table of or associated with a resistance welding machine, the casing fixtured in a floating fixture mounted on the table so that the metallic casing flange of the casing floats relative to upper and lower electrodes of the welding machine, radial and axial clamps radially and axially clamping respectively an area of the flange surrounding a reamed hole, upper and lower filler slugs disposed in the reamed hole, upper and lower electrodes against the upper and lower filler slugs, the resistance welding machine operable for applying a welding current through the upper and lower electrodes while applying pressure forced P to the upper and lower filler slugs with the upper and lower electrodes, the resistance welding machine operable for resistively heating and melting the upper and lower filler slugs respectively to form a weldment, and the resistance welding machine operable for pulsing the welding current on and off a first number of cycles.
The resistance welding machine may be operable for cooling to solidification and then in situ tempering a substantially liquid pool formed by the welding current under pressure of the upper and lower electrodes. The resistance welding machine may be operable for progressively increasing amounts of current for successive ones of the first number of cycles. The radial and axial clamps may be mounted on a clamp fixture rotatably fixtured on the flange and rotatable about an axis of the table and the casing centerline.
The resistance welding machine may be operable for cooling to solidification and in situ tempering a substantially liquid pool formed by the welding current under the pressure of the upper and lower electrodes, and for progressively increasing amounts of current for successive ones of the first number of cycles, and for applying a tempering current through the upper and lower electrodes and pulsing the tempering current on and off a second number of cycles during the in situ tempering, and wherein the tempering current is substantially lower than the welding current.
The foregoing aspects and other features of the invention are explained in the following description, taken in connection with the accompanying drawings where:
Illustrated in
Illustrated in
Illustrated in
As further illustrated in
An area 56 of the flange 18 surrounding the reamed hole 33 is radially and axially clamped by radial and axial clamps 60, 62. The radial clamp 60 clamps inside and outside diameters ID, OD of the flange 18 with radially outwardly and inwardly clamping forces F1 and F2 respectively as illustrated in
The clamps constrain the flange to prevent edge bulge and out of plane warping of the flange 18 during welding. The radial and axial clamps 60, 62 are mounted on a clamp fixture 67 that is rotatably fixtured on the flange 18 and rotatable about the axis 55 of the table 52 and the casing centerline 12.
The consumable upper and lower filler slugs 38, 39 include cylindrical sections 37 attached to caps or retaining lips 40. The upper and lower filler slugs 38, 39 are made from the same metal as the casing flanges. The upper and lower filler slugs 38, 39 are placed in the reamed hole 33. Optionally, a coating or layer of Boron 46 may be disposed between the cylindrical sections 37 and the metal of the flange 18 and between the retaining lips 40 and the metal of the flange 18. As illustrated herein, the Boron 46 may be applied to contact surfaces 42 of first and second filler slugs 38, 39 that contact the metal of the flange 18 before the plugs are placed in the reamed hole. In the exemplary welding method illustrated herein, a layer of Boron about 0.0002 inches thick is used. The Boron suppresses the melting point of the metal of the plugs.
Resistance welding is then performed by applying welding current through the upper and lower electrodes 70, 72 to melt the upper and lower filler slugs 38, 39 respectively while applying a pressure force P with the electrodes to the upper and lower filler slugs 38, 39 to form the weldment in the reamed hole 33. The resistance welding is thermally controlled by thermally controlling the electrodes. Resistive heating of the upper and lower filler slugs 38, 39 and the a portion of the flange 18 around the reamed hole 33 produced by the welding current results in coalescence in a substantially liquid pool 73 (see
One thermal control method is controlling cooling water temperature of water used to cool the upper and lower electrodes 70, 72 during the resistance welding step. Electrical current passing through the upper and lower electrodes 70, 72 is pulsed during the resistance welding step. Pulse time (number of cycles, 1 second=60 cycles for US power supply) and cooling time between pulses are two parameters used to control pulsing the welding current on and off. Another thermal control method is controlling the welding current passing through the electrodes.
The amount of pressure applied with the electrodes to the upper and lower filler slugs 38, 39 is also controlled during the resistance welding step. Electrode material is important for good weld properties and a bimetallic material made of copper and tungsten (Cu—W) is an exemplary material suitable for the resistance welding step.
The resistance heating provided by the welding machine is controlled and limited by the temperature of the weld which is held to a peak temperature that avoids the formation of retained austenite in the corners of the weldment. The peak temperature is below the eutectoid temperature for the steel of the casing. Martensite is the desired microstructure of the weldment. The exemplary material used for the casing and flanges is M152 stainless steel having a peak temperature somewhere around its melting point which is about 2500 degrees Fahrenheit or higher. After welding, the weldment is heat treated or tempered by heating the weldment at a substantially lower temperature illustrated herein as in a range of about 1000-1200 degrees Fahrenheit.
T1 was measured by a first thermocouple located on the top side of the weld near an outer diameter of the upper electrode on the top side of the flange. Its location should have been at the outer edge of the heat affect zone and is not in the actual nugget, thus, indicating lower readings in the range of about 500 to 600 degrees Fahrenheit. T2 was measured by a second thermocouple located on the bottom side of the weld near an outer diameter of the lower electrode on the bottom side of the flange. Its location should have been at the outer edge of the heat affect zone and is not in the actual nugget or pool, thus, indicating lower readings in the range of about 500 to 600 degrees Fahrenheit. The differences in T1 and T2 are probably due to proximity of the thermocouples to the weld (these are hard to accurately align and still clamp the parts).
When Boron is applied to the contact surfaces 42 of first and second filler slugs 38, 39 instead of getting melting in center and growing a nugget at high welding current, a reduced welding current is used. The welding time is extended and the heat from the hotter center is conducted to the interface between the edge of the hole and the plug causing localized melting due to the presence of the boron which is a melting point suppressant. For example, the welding current may be reduced from about 18-20 kiloamperes (kA) to about 7-8 kiloamperes. As current continues to flow for a long period of time, boron diffuses into the base metal plug causing the locally melted area to solidify as the concentration of boron decreases.
Additionally excess material from the consumable upper and lower filler slugs 38, 39 and particularly the caps or retaining lips 40 may be removed after the welding and tempering. The excess material may be removed with a machine, such as a grinder, so that the first and second sides 30, 32 of the flange 18 are smooth and even. The new bolt hole may be then drilled or otherwise machined in the newly welded area so as to be consistent with the level of the adjoining flange material.
After the welding and in situ tempering is completed, the casing is placed in a furnace for a 6 hour long tempering cycle which is exemplary of a long term deep tempering either before or after the new bolt holes are drilled or machined into the flange. The nugget has already solidified and the microstructure has transformed to un-tempered martensite. The partial tempering of the martensite reduces the hardness in the weldment and prevents cold cracking while the part awaits other holes to be repaired. After the welding is completed, the casing is placed in a furnace for the 6 hour or long period tempering cycle.
The present invention has been described in an illustrative manner. It is to be understood that the terminology which has been used is intended to be in the nature of words of description rather than of limitation. While there have been described herein, what are considered to be preferred and exemplary embodiments of the present invention, other modifications of the invention shall be apparent to those skilled in the art from the teachings herein and, it is, therefore, desired to be secured in the appended claims all such modifications as fall within the true spirit and scope of the invention.
Accordingly, what is desired to be secured by Letters Patent of the United States is the invention as defined and differentiated in the following claims:
Number | Name | Date | Kind |
---|---|---|---|
1784015 | Lane et al. | Dec 1930 | A |
1933938 | Schnetzer | Nov 1933 | A |
2155412 | Eckman | Apr 1939 | A |
2394535 | Dawson | Feb 1946 | A |
2464981 | Leathers et al. | Mar 1949 | A |
2712585 | Domeny | Jul 1955 | A |
2859339 | Brady | Nov 1958 | A |
2908801 | Cresswell | Oct 1959 | A |
3265852 | Laws et al. | Aug 1966 | A |
3366773 | Edge et al. | Jan 1968 | A |
3453152 | Hill et al. | Jul 1969 | A |
3511963 | Chmiel | May 1970 | A |
3643057 | Becker | Feb 1972 | A |
3666912 | Anderson et al. | May 1972 | A |
3740820 | Tarves, Jr. | Jun 1973 | A |
3778583 | Becker | Dec 1973 | A |
3781511 | Rygiol | Dec 1973 | A |
4037073 | Becker | Jul 1977 | A |
4205221 | Meyer | May 1980 | A |
4414455 | Schneider et al. | Nov 1983 | A |
4519732 | Sutcliffe | May 1985 | A |
4564735 | Dufrenne | Jan 1986 | A |
4673122 | Dubey | Jun 1987 | A |
4953777 | Griffith et al. | Sep 1990 | A |
4994646 | Tabata et al. | Feb 1991 | A |
5021627 | Bersch et al. | Jun 1991 | A |
5066845 | Anderson | Nov 1991 | A |
5111570 | Baumgarten et al. | May 1992 | A |
5944922 | Kadoya et al. | Aug 1999 | A |
6107595 | Peterson | Aug 2000 | A |
6637986 | Powell | Oct 2003 | B2 |
7126076 | Workman et al. | Oct 2006 | B2 |
7126079 | Trewiler et al. | Oct 2006 | B2 |
7141754 | Workman et al. | Nov 2006 | B2 |
7244320 | Malley et al. | Jul 2007 | B2 |
7256368 | Artelsmair et al. | Aug 2007 | B2 |
7552855 | Vargas et al. | Jun 2009 | B2 |
7662244 | Yoshizawa et al. | Feb 2010 | B2 |
7802350 | Walker | Sep 2010 | B2 |
8230569 | Anantharaman et al. | Jul 2012 | B2 |
8367964 | Sullivan et al. | Feb 2013 | B2 |
20030038118 | Sun et al. | Feb 2003 | A1 |
20030222054 | Katou et al. | Dec 2003 | A1 |
20040169017 | Sakoda | Sep 2004 | A1 |
20050000947 | Sigler | Jan 2005 | A1 |
20050045597 | Wang et al. | Mar 2005 | A1 |
20050173492 | Workman et al. | Aug 2005 | A1 |
20050173493 | Workman et al. | Aug 2005 | A1 |
20050184031 | Sun et al. | Aug 2005 | A1 |
20060117562 | Subramanian et al. | Jun 2006 | A1 |
20070084906 | Vargas et al. | Apr 2007 | A1 |
20070175015 | Ainsworth | Aug 2007 | A1 |
20090083957 | Garrett | Apr 2009 | A1 |
20090250439 | Workman et al. | Oct 2009 | A1 |
20090250441 | Sullivan et al. | Oct 2009 | A1 |
20100024311 | Wambeke et al. | Feb 2010 | A1 |
20100032415 | Sullivan et al. | Feb 2010 | A1 |
20100158626 | Nakahata et al. | Jun 2010 | A1 |
20100178121 | Kondoh et al. | Jul 2010 | A1 |
20100183431 | Anantharaman et al. | Jul 2010 | A1 |
20100243614 | Bunting et al. | Sep 2010 | A1 |
20110073572 | Wang et al. | Mar 2011 | A1 |
20110076147 | Ganesh et al. | Mar 2011 | A1 |
20110272384 | Matsushita et al. | Nov 2011 | A1 |
Number | Date | Country |
---|---|---|
0470868 | Feb 1992 | EP |
63104788 | May 1988 | JP |
Entry |
---|
“Martensite and Retained Austenite” , George F. Vander Voort—Buehler Ltd., Lake Bluff, Ill., IndustrialHeating.com—Apr. 2009, beginning on p. 51. |
PCT Search Report and Written Opinion dated Nov. 5, 2012 from corresponding Application No. PCT/US2012/048501. |
Number | Date | Country | |
---|---|---|---|
20130032578 A1 | Feb 2013 | US |