The present invention relates to a resistance welding device capable of optimizing a welding condition with taking into account of various elements.
In a conventional resistance welding device, materials to be welded are overlapped, a portion to be welded is sandwiched between electrodes, a pressing force is applied to the portion, and a welding electric current is flowed between the electrodes. As the electrode, for example, a table-type electrode, a gun-type electrode or the like are used. As the tip of the gun-type electrode, various shapes of chips are used depending on the portion to be welded. An example of the resistance welding device is described in Patent Document 1.
The welding quality in the resistance welding device depends on a welding current flowing in the portion sandwiched between the electrodes, an energization time of the welding current, and a pressing force applied to a workpiece by the electrode for welding. In the following description, these are referred to as welding conditions. Since users have great variation of requirements to the welding quality, they adjust welding conditions at the trial production stage to obtain optimum values.
Patent Document 1: Japanese Patent Application publication No. 2019-150874
Patent Document 1: Japanese Patent Application publication No. HEI 7-178566
Patent Document 2: Japanese Patent Application publication No. HEI 9-029456
Patent Document 3: Japanese Patent Application publication No. HEI 11-047950
Patent Document 4: Japanese Patent Application publication No. 2005-128818
SUMMARY OF INVENTION
As described above, in order to obtain the optimum value of the welding conditions that meet the user's requirements, the user creates a large number of samples with varying welding conditions, measures the bond strength and nugget diameter, and then, performs an overall evaluation including appearance or the like. Even with skilled operators, it may take tens of hours to find the optimum value of the welding conditions. With inexperienced operators, it may take even more time, and then, the optimal value cannot be found in some cases. The above-mentioned Patent Document 1 provides an idea for solving such problems.
In the Patent Document 1 introduces an example of providing a database that outputs welding conditions such as a welding current and an energization time, when elements such as the kind and the thickness of the material to be welded and the type (shape) of the electrode are input. However, there are various kinds of elements for determining the welding condition. For example, welding can be performed for the material which has been plated or for the material which is made from overlapped multiple materials with different thicknesses. Considering the above cases, the number of combination of elements becomes enormous. As the result, the size of database becomes huge and the production cost is increased.
No matter how extensive the database is, the operation of obtaining of the optimum value by repeating trial manufactures while adjusting the welding condition is not omittable in order to obtain the welding quality required by the user of the welding device.
In view of the foregoing, it is an object of the invention to provide a resistance welding device capable of obtaining a welding condition as close as the optimum value which meets the needs of user while suppressing the expansion of a database.
The below configurations are means to solve the above problems.
A resistance welding device for flowing a welding current between electrodes which sandwiches a workpiece including a plurality of overlapped materials while applying a pressure to the workpiece, the resistance welding device including:
an input device from which a plurality of elements used to determine welding conditions including the welding current, an energization time, and a pressing force applied to the workpiece by the electrodes is input;
an element selecting device configured to select basic elements including a kind and a thickness of a material constituting the workpiece and a type of an electrode from among the plurality of elements input from the input device and perform searching in a first database, and configured to select an additional element other than the basic elements from among the plurality of elements input from the input device and perform searching in a second database;
an operating device configured to execute a correction operation process for applying a search result in a second database to an initial value of a welding condition searched in a first database, and configured to output welding conditions including the welding current, the energization time, and the pressing force;
a display device configured to display the welding condition output from the operating device; and
a power supply device configured to control a welding of a workpiece based on the welding condition output from the operating device,
wherein the first database stores data among which welding conditions including a welding current, an energization time, and a pressing force corresponding to the basic elements are searched and output, and
wherein the second database stores, in association with an additional element or a combination of additional elements, data including one or more trend formulas used to correct an initial value of a welding condition output from a first database based on a nature of the additional element.
The resistance welding device according to claim 1, wherein, when a welding is performed for a plurality of overlapped materials each having a different thickness, an input device receives a basic element including a thickness for each material,
The resistance welding device according to claim 1, wherein, when a welding which is divided into a plurality of times is performed for a plated material, a first database outputs a welding current, an energization time, and a cooling time between these weldings, for each time,
wherein an element selecting device performs searching in a second database with respect to an additional element for welding a plated material, and selects and outputs a trend formula used for a correction operation of a welding condition including a plated weight ratio to a reference value as a parameter, and
wherein the operation device executes a correction operation process for a first time of welding current and energization time and a second time of welding current and energization time, using a trend formula output from a second database, and outputs a welding condition including a welding current, an energization time, and pressing force.
The resistance welding device according to any one of claims 1 to 3, wherein the element selecting device performs searching in a first database and a second database with respect to a plurality type of elements,
wherein a means for specifying a relative ratio of a required welding quality to a welding quality having a standard value of a welding condition output from the operating device is provided,
wherein an element selecting device performs searching in a second database to output a trend formula, which is used for executing a correction operation of a welding condition, corresponding to a combination of a plurality type of additional elements,
wherein the operating device executes a correction operation process of a welding condition for a search result in a first database, using the trend formula, the relative ratio being a parameter of the trend formula, and outputs welding conditions including a welding current, an energization time, and a pressing force.
The resistance welding device according to any one of claims 1 to 4, wherein the input device includes an adjusting device to incrementally increase or decrease a welding condition displayed on the display device as a result of an operation process, by a limited amount within a pre-limited range to obtain a new welding condition.
The resistance welding device according to any one of claims 1 to 5, further including a third database storing a new welding condition obtained by the adjusting device.
The resistance welding device according to claim 6, wherein a second database and a third database configured to store a new trend formula obtained by back-calculating a parameter of a used trend formula based on a new welding condition obtained by the adjusting device.
A computer program for controlling a resistance welding machine to function a computer as the input device, the element selecting device, the operating device and the display device according to claim 1.
A recording medium storing the computer program according to claim 8 and readable by a computer.
It becomes possible to obtain a welding condition close to an optimum value while suppressing an expansion of the entire database, by correcting an initial value of a welding condition using a trend formula corresponding to a combination or the like of basic elements and additional elements, even when there exist various additional elements other than basic elements.
When plates with different thicknesses are overlapped and welded, it becomes possible to select an appropriate trend formula for correction and obtain a welding condition close to the optimum value by combining welding conditions for each thickness of the plates and specifying a thickness ratio as an additional element.
When a plated material is welded, for example, initial values of two times of the welding conditions and a cooling period between the two times of the welding are output from the first database. Then, the plating weight or the like is designated as the additional element. Thus, an appropriate trend formula for correction can be selected from the output of the second database. As the result, it become possible to obtain a welding condition close to the optimum value.
A ratio of the required welding quality relative to the welding quality obtained by using a standard value of a preset welding condition can be specified. With this configuration, it becomes possible to adjust the result of the correction operation process using a trend formula so that welding conditions close to the user's required conditions are always obtained. Therefore, the entire database can be collectively customized to a user-preferred property.
By gradually increasing or decreasing the welding condition in a pre-limited range and by a pre-limited width, it becomes possible to automatically indicate a procedure that is easy to reach the optimum value.
The optimized welding conditions obtained by adjusting with the adjusting device can be accumulated. The welding condition can be output based on the elements. Thus, it becomes possible to directly utilize the optimized welding condition from the next time. Further, it becomes possible to improve the welding conditions based on the previous results.
It becomes possible to obtain a new trend formula from the optimized welding condition obtained by adjustment with the adjusting device, and perform a calculation using this formula from the next time.
Hereinafter, embodiments of the present invention will be described in detail for each embodiment.
In the example shown in
As shown in
The display device 30 displays welding conditions 50 output from the operating device 42 on a display. The adjusting device 54 includes a button or the like for the user to adjust the obtained welding condition 50 in order to obtain a required welding quality. Of course, the input device 28, the display device 30, and the adjusting device 54 may be incorporated into independent panels or the like, respectively.
The power supply device 26 is provided with a known power supply circuit for supplying a welding current between the upper electrode 16 and the lower electrode 18. The power supply device 26 controls welding of the workpiece using the welding conditions 50 output from the operating device 42.
The element selecting device 36 and the operating device 42 are computer program modules for controlling the resistance welding device. Both of them execute operating processes for realizing functions described below, and they are not necessarily independent of each other and may be mixed. In other words, they may be integrated. The first database 38 and the second database 40 are stored in a storage device (not shown) incorporated in the resistance welding device. The storage device may be an external storage device connected via a network.
The input device 28 is a man-machine interface for inputting a plurality of elements for determining the welding conditions 50 including the welding current 44, the energization time 46, and the pressing force 48 applied to the workpiece by the electrodes. The screen as shown in this figure is displayed on the input device 28 of the resistance welding device.
In the example of this figure, the screen in which the input device 28, the display device 30, and the adjusting device 54 are integrated is shown. The portion where the welding current 44, the energization time 46, and the pressing force 48 are output and displayed corresponds to the display device 30. The portion where “adjustment upper limit (lower limit)” and “adjustment interval” are displayed is the adjusting device 54. The functions and operations of the adjusting device 54 and a relative value adjusting unit 66 for welding conditions shown in this screen will be described in detail in the later embodiments.
The plurality of elements include, in the example of this figure, a kind of material, a plate thickness (thickness), and an electrode type (type), a welding method (a table-type of electrode in the example of the figure), etc. In addition, the appearance and the strength of the product after welding can be specified. In this example, it is possible to specify “appearance is given priority.” “Scatter,” “dent,” and “distortion” affect the appearance. It is possible to specify which of these should be prioritized.
Here, the kind of material, the plate thickness, the electrode type, and the like are referred to as basic elements 32. Elements other than the basic elements 32 are referred to as additional elements 34. As will be described later, the additional elements 34 may include variety of things. The basic element 32 may include other elements specified with numerical values, properties, types, product names, or the like, which are capable of uniquely determining the welding condition 50.
Various elements corresponding to the basic elements 32 can exist. However, if the basic elements 32 are increased, the data size may also be increased in the structure of the first database 38. Therefore, as in this embodiment, it is most practical to use those three elements; the kind of material, the plate thickness (thickness), and the electrode type (type).
The element selecting device 36 (
The first database 38 stores data among which the welding current 44, the energization time 46, the pressing force 48, and the like corresponding to the basic element 32 are searched and output. When the kind of material, the plate thickness (thickness), and the electrode type are specified and input, the welding conditions 50 such as the welding current 44, the energization time 46, and pressing force 48 applied to the workpiece by the electrodes which are suitable to the welding are uniquely output as numerical values.
The structure of the first database 38 illustrated in
The additional element 34 may be singular or plural. The trend formula 52 to be output may also be singular or plural. When there is a plurality of additional elements 34, trend formulas corresponding to the combinations thereof are stored.
Coefficients 1 to 3 of the trend formula 52 shown in
When the additional element 34 is input to the input device 28, the corresponding trend formula 52 is output, and when the calculation is performed after determining parameters such as coefficients 1 to 3, a correction coefficient for correcting the output of the first database 38 can be obtained. Note that arbitrary variables in the trend formula such as coefficients 1 to 3 and correction rates are referred to as parameters.
In the examples shown in
The trend formulas 52 shown in
The trend formulas 52 shown in
(Correction ratio %) solves this problem. The difference between the standard value and the welding quality required by the user can be adjusted by specifying a relative ratio using the relative value adjusting unit 66 (
The operating device 42 (
Specifically, as shown in
In step S14, the operating device 42 obtains an initial value of the welding condition. In step S15, the element selecting device 36 selects the additional element 34. In step S16, the element selecting device 36 performs searching in the second database.
In step S17, the operating device 42 obtains a trend formula. In step S18, the correction value is calculated based on the obtained trend formula. In step S19, the initial value of the welding condition 50 is corrected based on the correction value. In step S20, the welding condition 50 is output and displayed on the display device 30. Further, the welding condition 50 is output to the power supply device 26 automatically or by user's operation.
As described above, when various additional elements 34 other than the basic element 32 exist, the welding condition 50 can be corrected by using the trend formula 52 corresponding to the additional element 34 or the combination of the additional elements 34. Therefore, the welding condition 50 closer to the optimum value can be obtained while suppressing the expansion of the entire database, particularly the first database 38.
As described above, by specifying prioritizing either “strength” or “appearance” with respect to the additional element 34, the welding conditions can be corrected according to the quality required for the welded product. Further, by using the function of the relative value adjusting unit 66, it is possible to collectively adjust the operation process results from various kinds of trend formulas for calculating the correction coefficients.
In performing spot welding, the upper workpiece 12 and the lower workpiece 14 are sandwiched by the upper electrode 16 and the lower electrode 18, a pressing force is applied to the sandwiched upper workpiece 12 and lower workpiece 14 by the electrodes, and a current of several thousands to several tens of thousands amperes (A) is flowed between the upper and lower electrodes. The welded material is melted by heat generated by its own resistance, causing an elliptical nugget 20 to be formed.
The contact resistance at the contact portion between the upper workpiece 12 and the lower workpiece 14 is larger than the resistance value of the material. The contact resistance at the center portion where the pressing force is applied by the electrodes becomes smaller than the contact resistance at the periphery, so that a current easily flows. Since the current density at the center portion increases, the material starts to melt from the center portion. The required shear strength after welding is related to the plate thickness. As the plate thickness increases, more strength is required. Therefore, the required nugget diameter also increases. That is, as the plate thickness increases, the volume to be melted increases and the energy required for welding also increases.
On the other hand, the upper electrode 16 and the lower electrode 18 are made of a copper alloy and are cooled by cooling water circulating inside of them so as not to be melted by welding heat. The upper workpiece 12 and the lower workpiece 14 usually have a measurable size. Therefore, although the central portion is melted by welding, the peripheral portion radiates heat through the electrodes or from the surface of the workpiece itself.
In an extreme case, even if an electric current is supplied for a long time at a low current value, the workpieces may not be melted at all and cannot be welded due to heat radiation from the electrodes and the workpiece itself. The volume of the portion to be melted to form the nugget 20 is correlated with the electrode tip area x (plate thickness of upper workpiece+plate thickness of lower workpiece).
The electric energy to be supplied is calculated using (square of welding current value x resistance x energization time), and heat is generated by this energy. If the welding current is lowered, it is necessary to lengthen the energization time. However, when the energization time is lengthened, the amount of heat radiation increases. Therefore, the welding current value must be set higher by that amount. When the pressing force is increased, the range in which the welding current flows through the material is expanded. As the result, the current density is lowered. In this case, it is necessary to increase the welding current or lengthen the energization time.
When the welding current is increased or the energization time is lengthened, the energy to be supplied is also increased. As the result, a phenomenon in which the molten material flies out (scattering occurs) from the periphery of the nugget 20 occurs. This may lead to decrease in welding strength, decrease in welding quality, and poor welding. As described above, if pressing force is increased, it is necessary to increase the welding current or to lengthen the energization time. In any case, multiple adjustments must be performed at the same time.
To what degree of the appearance and the strength the user requires is important. As described above, the adjustment becomes complicated, accordingly. The above trend formula contributes to output welding conditions that facilitate the adjustment. In the case of (a) and (b) in
That is, when two plates are welded, the required welding strength is generally determined by the thickness of the plate on the thin plate side. The upper limit of the shear strength of the welding portion is the strength of the base material. If the strength of the welded portion exceeds the strength of the base material, the portion around the nugget of base material breaks first in a manner for a plug to come out. Thus, when a thick plate and a thin plate are welded, the base material on the thin plate side breaks first.
(c) shows the case of a nearly flat electrode, and (d) shows the case of an electrode in which the tip of the electrode becomes narrower toward the thin plate side. The upper workpiece 12 is a thick plate and the lower workpiece 14 is a thin plate. The generation of the nugget 20 starts from the contact portion between the two plates and gradually shifts to the central portion of the two plates, whereby the nugget 20 is generated in the central portion.
When the nugget 20 is formed in the center portion, the nugget diameter contributing to the strength becomes small when viewed from the thin plate side. However, the welding strength is regulated on the thin plate side. Therefore, the required strength can be satisfied even when the nugget diameter becomes small.
Flat or nearly flat electrodes are used to improve the welding quality in appearance. There is no problem when the thicknesses of the two plates to be welded are close to each other. However, as the difference between those plate thicknesses increases, the nugget diameter contributing to the strength decreases, and it becomes difficult to obtain the required nugget diameter or welding strength.
Usually, the welding quality in appearance is required only on the outer surface of the product called an outer plate, not on both sides. The appearance of the opposite side is not required in many cases. In addition, in many cases, a thick plate is used as a workpiece constructing a framework to which strength is required, while a thin plate is used at the outside. It is preferable to use a flat electrode for the surface where the welding quality in the appearance is required, so that a dent is not left.
As shown in
Normally, welding can be performed based on the welding conditions on the thin plate side. However, when the plate thickness ratio is large, the values are far from proper values even if the welding conditions are adjusted based on those on the thin plate side. It is easy for an expert to make the adjustment based on experience, but it is not easy for a person with little experience to make the adjustment.
Further, in the welding of plates having large thickness difference, the welding condition is far from the condition on the thin plate side. If the welding condition of the thick plate side is adopted, excessive welding and scattering occurs, and proper welding cannot be performed. It is considered that the appropriate welding conditions when the difference in plate thickness is large tend to correlate with welding current, energization time, and plate thickness ratio based on the welding conditions on the thin plate side.
In the present invention, first, the basic element 32 of the upper workpiece 12 and the basic element 32 of the lower workpiece 14 are input from the input device 28 (
The initial values of the two sets of welding conditions 50 are corrected by, for example, any one of three kinds of trend formulas 52. The trend formula 1 is used to perform a correction based on the welding condition of the thin plate side. In this case, additional elements with respect to welding of different thicknesses of plates with the following thickness ratio can be specified.
Even if the electrode on the lower plate side is a plane electrode, the trend formulas may be different between (thickness of upper plate>thickness of lower plate) and (thickness of upper plate<thickness of lower plate). Therefore, it is necessary to provide the trend formula separately. Here, the case where (plate thickness of upper plate>plate thickness of lower plate) and the electrode on the lower plate side is a plane electrode will be described. Since the trend formula may be different depending on the kind of material to be welded, the shape of the workpiece, and the shape of the upper electrode, it is preferable to provide the trend formula for each of them.
For example, in the case of the kind of material: SPCC, the upper plate: 2.0 mm, the lower plate: 1.0 mm, and the lower plate side: a plane electrode (table-type), the following data is obtained by searching in the first database.
The upper plate (2.0 mm): “pressing force: 1.9 kN”, “welding current: 7.7 KA”, “energization time: 360 msec”
The lower plate (1.0 mm): “pressing force: 1.6 kN”, “welding current: 6.0 KA”, “energization time: 250 msec”
When the correction ratio is 100%, the following calculation is performed using the trend formula 2 in
Pressing force=(thin plate side pressing force+(thick plate side pressing force−thin plate side pressing force)×coefficient 1)×correction ratio %=1.6 kN+(1.9 kN−1.6 kN)×0.5×100%=1.75 kN
Welding current=(thin plate side welding current+(average welding current−thin plate side welding current)×coefficient 2)×correction ratio %=6.0 kA+(6.85 kA−6.0 kA)×1.05×100%=6.89 kA
Average welding current=(thin plate side welding current+thick plate side welding current)/2=(7.7 kA+6.0 kA)/2=6.85 kA
Energization time=(thin plate side energization time+(average energization time−thin plate side energization time)×coefficient 3)×correction ratio %=250 msec+(305 msec−250 msec)×0.5×100%=278 msec
Average energization time=(thin plate side energization time+thick plate side energization time)/2=(250 msec+360 msec)/2=305 msec
The welding conditions for the plated material differ depending on the type of plating and the plating weight (plating thickness). The plating has a lower melting point than the base material. Therefore, the plating layer 22 between the electrode and the workpiece melts in the initial stage when energization is started. Because of the pressing force applied by the electrodes, the molten plating layer 22 is pushed out and sticks around the electrodes.
That is, as shown in
If the plating layer 22 is thin, the amount of the plating layer 22 melting and clinging to the electrode in the initial stage of energization is small. Therefore, the welding condition is close to that of a non-plated material. However, the welding current is slightly higher and the energization time is slightly longer.
When the thickness of the plating layer 22 is increased, the welding cannot be performed under the condition close to that for welding without plating. In this case, a welding method called double energization is usually adopted. In the double energization, the plating layer 22 is melted by the first energization and the plating layer 22 sticks around the electrode. After a cooling time, the molten state of the plating layer 22 is returned to a solid state. Then, main energization is performed in the stable state. In some cases, energization can be performed three times or more.
Although the welding condition of the main energization is close to that of the non-plated material, the welding current becomes higher and the energization time longer since the plating layer 22 sticks around the electrodes. As the thickness of the plating layer 22 increases, the welding current becomes higher and the welding time becomes longer in order to move the plating layer 22 toward the circumference of the electrode at the initial stage. Similarly in the main energization, as the thickness of the plating layer 22 increases, the amount of the plating layer 22 sticking around the electrodes increases, so that the welding current becomes higher and the welding time longer.
As the thickness of the plating layer 22 increases, the variation in thickness tends to increase. The plating thickness 22 is managed with the plating weight (g/m2). In the case of a plated material with narrow plating thickness variation, energization is performed once. In the case of a plated material with wide plating thickness variation, energization is performed twice.
The first database is configured to perform similar outputting for any of single or double welding. That is, when the basic element 32 is input, two sets of welding time and welding current are output other than the pressing force of the electrodes.
The cooling time between the first welding and the second welding is also output. The initial pressurization time shown in (b) and (c) of
When just one welding is performed, “0” is output as the cooling time, the energization time 2, and the welding current 2. In the case of welding twice, actual numerical values are applied to cooling time, the energization time 2, and the welding current 2. In the case of welding twice, as shown in this figure, data is output from the first database such that the welding current 1 is supplied during the energization time 1 after the initial pressurization time, and then the welding current 2 is supplied during the energization time 2 after the cooling time to terminate the welding. The data output from the first database is corrected by the corresponding trend formula 52.
In the case of twice energization, the trend formula 52 in this figure is used. What is shown here is a trend formula in the case where the variation in plating thickness is wide. In this case, the welding of the plated plate corresponds to an additional element, and searching in the second database can be performed by specifying the plating weight as the additional element.
In the case of a plated material, the molten plating at the initial stage of energization sticks to the circumference of the electrode, and the current path expands. As the result, the current density decreases. The influence of sticking around the electrodes and the degree of decrease in the current density correlate with the plating weight.
The minimum value of the plating weight is set as the reference value, and the plating weight ratio to the reference value is set as a parameter. For example, when the plating weight 30 g/m2 is set as the reference value and the plating weight is 90 g/m2, the plating weight ratio=90/30=3 is set as a parameter. The following calculations can automatically output the characteristic welding conditions for plated materials.
In the case of Material: AAA and Reference plating weight: 30 g/m2
In the case of Plate thickness: 1.0 mm
In the case of Material plating weight: 90 g/m2, Plate thickness:
1.0 mm, Correction ratio: 100%, the weight ratio is set to 90/30=3.
Pressing force=2.0 kN×(1+(3−1)×0.03)×100%=2.12 kN
Welding Current 1=5.0 kA×(1+(3−1)×0.03)×100%=5.3 kA
Energization time 1=150 msec×(1+(3−1)×0.03)×100%=159 msec
Welding Current 2=7.5 kA×(1+(3−1)×0.07)×100%=8.6 kA
Energization time 2=250 msec×(1+(3−1)×0.07)×100%=285 msec
In some cases, the melting is terminated with a single energization. Although the trend formula of the single energization is not shown, the following formula is obtained. The formula corresponds to the first time in the above trend formula. However, the coefficients are different from those of the above trend formula.
Pressing force=Selected pressing force×(1+(weight ratio−1)×coefficient 1)×correction ratio %
Welding current 1=Selected welding current 1×(1+(Weight Ratio−1)×coefficient 2)×correction ratio %
Energization time 1=Selected energization time 1×(1+(weight ratio−1)×coefficient 3)×correction ratio %
After the welding condition 50 is output from the operating device 42, the welding condition can be adjusted by operating the screen shown in
The adjustment button 56 shown in
The adjustment interval 60 indicates a width that can be adjusted by a single click of the adjustment button 56, and an appropriate width is automatically set so that the user approaches the purpose little by little without passing through the target welding quality. The adjustment upper and lower limit release button 62 is a button for forcibly releasing the adjustment upper and lower limits. When the adjustment upper and lower limit release button 62 is used, adjustment beyond the adjustment range can be freely performed. When an optimum value is found by the adjustment, the result can be saved by clicking the data save button 64.
For example, the user determines whether or not the quality approaches the expected quality while increasing the value of the welding current. If the quality gets closer to the expected quality, the user performs adjustment by further increasing the value. If the quality becomes worse, the user performs adjustment by decreasing the value. It takes a lot of time to get closer to the desired quality by reducing the amount of adjustment little by little. If the adjustment amount is increased excessively, the optimum value may be passed or returned too much.
A skilled operator can reach the required welding condition with a small number of welding tests. However, a less experienced operator can take longer to reach the optimum value due to making too much adjustment at a time or inputting the incorrect condition. Such a problem can be solved by automatically setting the adjustment range 58 and the adjustment interval 60.
In the present invention, as described above, the adjustment amount is limited by providing the upper and lower limits of the reference adjustment range. Therefore, adjusting to a value far from the reference range by mistake is prevented.
For example, in the example shown in
Further, since a plurality of operations is required to switch the condition, the amount of one-time adjustment can be implicitly limited, and an appropriate adjustment can be performed. However, depending on the required welding quality, adjustment beyond the standard adjustment range may be necessary.
For example, if the welding strength is allowed to be fairly low (as long as it is attached), but the appearance such that the welded portion is invisible at all is required, adjustment beyond the standard range is necessary. In this case, the adjustment may be performed without any limitation on the adjustment range. When the adjustment upper and lower limit release button 62 (
For example, the energization time is adjusted from 200 msec to 210 msec, while the standard adjustment range is 170 msec to 230 msec.
When the adjustment button 56 (
If the kind and shape of material of the user's products (workpieces) are similar, the welding conditions are likely to be similar in many cases. Therefore, it is preferable to save a trend formula or the like associated with the result obtained by the adjustment by the user. In this embodiment, as shown in
For example, as shown in
If the combination of elements to be input has already been stored in the third database 41, the combination can be read out to confirm whether or not the adjustment work of the welding conditions is appropriate, and can be used immediately. In addition, even if further adjustment work is required, time to do such a work can be saved. Even if the welding conditions whose one element is coincident with the required element but another element is not coincident with the required element is stored in the third database 41, it is possible to save time by starting the adjustment work with the welding conditions.
On the other hand, the results stored in the third database 41 can also be used when the user requests welding conditions for different products in the future. In this case, if there is a combination of the same elements among the data stored in the third database 41, it becomes possible to generate new data by processing such as averaging, majority decision, using minimum value, using maximum value, etc. The new data is added to the first database 38 and the second database 40. As a result, when an element is input later to obtain a welding condition, a welding condition to provide results close to the welding quality required by the user is output.
If the welding quality (such as the strength and appearance) of the user's product (workpiece) is close to the welding quality expected by the manufacturer of the resistance welding device, the welding conditions output from the operation device can be used with minor adjustments. However, when the welding quality required by the user is special, a large adjustment is required.
The third database 41 is suitable for determining welding conditions for products that are always produced by the user or welding conditions for similar products. Further, by using the third database 41, new data can be added to the first database 38 and the second database 40.
In order to do that, a learning function of the contents of the third database 41 is provided. That is, the combinations of the same elements are extracted from the third database 41, and the initial values of the welding conditions and the parameters of the trend formula output when those elements are input are optimized. For example, those methods (averaging, majority decision, using minimum value, using maximum value) may be adopted.
For example, when the welding condition obtained by inputting the elements (the material kind: SPCC, the upper plate thickness: 1.0, the upper electrode: Φ16-8 R) is saved 10 times in a file, the average value is obtained for each item of the welding conditions from the 10 pieces of data, and they are aggregated into one piece of data. In the case of a majority decision, the value having the largest number may not be necessarily selected. For example, with respect to the energization time, the energization time is divided by 10 msec intervals, and the number of data included in each range of 10 to 19, . . . , 100 to 119, 120 to 129, . . . may be obtained. Then, the ranges in which the data-save has been performed many times are selected by majority decision. Thus, data can be aggregated into an average value of the ranges.
In addition, for example, the welding condition obtained by the operating process using the trend formula 52 output from the existing second database 40 is compared with the welding condition optimized by the user. Then, based on the result, a parameter of the trend formula 52 is reversely calculated, and is stored in the second database 40 as a new data. For example, in the case of the trend formula 52 for the correction of the pressing force shown in
For example, an operation screen shown in
In the above embodiment, the first database 38, the second database 40, and the third database 41 are provided independently for each other. However, common items exist in these databases. Therefore, the first database 38, the second database 40, and the third database 41 may be integrated into a single database in which all of items including the common items and the non-common items are mixed together. That is, it is important that the first database 38, the second database 40, and the third database 41 exits, having substantially same roles as the above-described roles.
The computer program and the database for controlling the device may be stored in storage devices such as servers connected through a network, in addition to various storage media mounted on the device itself.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-80906 | May 2020 | JP | national |