Patent Grant
10137523
(1) Field of the Invention
The present invention relates to a resistance welding method for welding objects to be welded together such as an element wire having a plurality of coating layers and a metal piece and to a conductor unit, which is assembled by welding the objects together using the method.
(2) Description of the Related Art
In order to electrically and mechanically connect (a) an element wire as an object to be welded which includes: a core material coated with an electrically conductive metal on an outer surface thereof; and a plated layer consisting of metal, such as tin, which coats the coated core material, to (b) a metal plate as another object to be welded which includes: a base material consisting of an electrically conductive metal; and a plated layer consisting of metal, such as tin, which is laminated on an outer surface of the base material, so far, for example, brazing using solder is applied or, alternatively, one of the element wire and the metal plate is caulked to the other.
When the objects to be welded together are connected by using solder as described above, the solder reacts with the plated layer to form an intermetallic compound. Because the intermetallic compound generally has low mechanical strength, therefore, when the objects to be welded together are connected by using the solder, a welded part of the objects has low mechanical strength, causing a problem that the welded part of the objects tends to easily separate. This is a reason why such a method using solder is not suitable to connect an electric wire and a terminal fitting, which constitute a wiring harness to be mounted on a motor vehicle as a mobile unit.
On the other hand, in the method using the caulking described above, even when the object (to be welded) having the plated layer on an outer surface thereof is connected to the other object (to be welded), an electrical resistance between the objects tends to increase. Accordingly, the method using the caulking is also not suitable to connect an electric wire and a terminal fitting, which constitute a wiring harness to be mounted on a motor vehicle as a mobile unit.
It is therefore an objective of the present invention to solve the above problems and to provide a resistance welding method and a conductor unit assembled by welding the objects (to be welded) together using the resistance welding method, by which objects (to be welded together) can be connected without increasing the electrical resistance and with a sufficient mechanical strength, in particular, when the object having the plated layer on an outer surface thereof is being connected to the other object.
In order to attain the above objective, the present invention provides a resistance welding method of welding two objects together including the steps of:
clamping the two objects between a pair of electrodes; and
applying a welding current between the pair of the electrodes on a condition that the two objects are pressed to bring the two objects close to each other, so as to allow a contacting surface between the two objects to generate heat,
wherein one of the two objects includes a core member and a plated layer, which coats the core member and has a melting point lower than that of a metal constituting an outer surface of the core member,
wherein the two objects are clamped between the pair of the electrodes and the contacting surface are allowed to generate heat to melt the plated layer, so as to weld the outer surface of the core member of said one of the two objects and a base member of another of the two objects together, wherein at least the outer surface of the core member and the base member are made of respective metals, between which no intermetallic compound is formed.
With the construction described above, the contacting surface between the two objects is allowed to generate heat to melt the plated layer so as to remove the plated layer from between the outer surface of the core member and the base member. Therefore, the outer surface of the core member directly comes in contact with the base member. Therefore, the electrical resistance between the two objects can be prevented from increasing.
Further, because no intermetallic compound is formed between the outer surface of the core member and the base member, therefore the mechanical strength of the welded part between the outer surface of the core member and the base member can be prevented from deteriorating. That is, the two objects to be welded together can be joined together with sufficient mechanical strength.
The core member includes a core wire and a coating layer, which coats the core wire and constitutes the outer surface of the core member, the core wire being made of a material having a melting point higher than that of the coating layer,
wherein the coating layer is made of a metal which forms no intermetallic compound between the metal constituting the coating layer and the base member.
With the construction described above, the core wire does not melt upon welding the coating layer. Therefore, the mechanical strength of the core member can be secured upon the welding. That is, the core member can be prevented from being damaged upon the welding.
In order to attain the above objective, the present invention also provides a conductor unit assembled by means of a resistance welding method of welding two objects together including the steps of:
clamping the two objects between a pair of electrodes; and
applying a welding current between the pair of the electrodes on a condition that the two objects are pressed to bring the two objects close to each other, so as to allow a contacting surface between the two objects to generate heat,
wherein one of the two objects includes a core member and a plated layer, which coats the core member and has a melting point lower than that of a metal constituting an outer surface of the core member,
wherein the plated layer is removed from between the outer surface of the core member of said one of the two objects and a base member of another of the two objects, so that the outer surface of the core member and the base member are welded together,
wherein at least the outer surface of the core member and the base member are made of respective metals, between which no intermetallic compound is formed.
With the construction described above, the contacting surface between the two objects is allowed to generate heat to melt the plated layer so as to remove the plated layer from between the outer surface of the core member and the base member. Therefore, the outer surface of the core member directly comes in contact with the base member. Therefore, the electrical resistance between the two objects can be prevented from increasing.
Further, because no intermetallic compound is formed between the outer surface of the core member and the base member, therefore the mechanical strength of the welded part between the outer surface of the core member and the base member can be prevented from deteriorating. That is, the two objects to be welded together are joined together with sufficient mechanical strength.
In the following, exemplary embodiments of the present invention will be explained with reference to
As shown in,
The core wire 34 is made of metal or non-metal and formed as a long wire having a round shape in section. The core wire 34 is preferably made of a material having sufficient mechanical strength higher than that of the coating layer 35. The core wire 34 improves the mechanical strength of the core member 32. Of course, the core wire 34 may be made of a material having electrically conductive property or, alternatively, a material having no electrically conductive property. The core wire 34 is made of a material having a melting point higher than that of the coating layer 35. In an example shown in the figure, the core wire 34 is made of iron.
The coating layer 35 is made of a material (metal) having high electrical conductivity including an element such as copper, silver, gold, aluminum or magnesium. The coating layer 35 is made of a metal having a melting point higher than that of the plated layer 33 and lower than that of the core wire 34. The coating layer 35 coats an outer surface of the core wire 34 throughout the entire length of the core wire 34. A thickness of the coating layer 35 is constant in a circumferential direction and a longitudinal direction of the core wire 34. In an example shown in the figure, the coating layer 35 is made of copper and has a thickness of 30-40 μm. The coating layer 35 constitutes the outer surface of the core member 32.
The plated layer 33 is made of a metal, such as tin, zinc or solder, having a melting point lower than those of the metal constituting the core wire 34 and the metal constituting the coating layer 35. That is, the element wire 30 includes the core member 32 and the plated layer 33, which coats the core member and has a melting point lower than that of the metal constituting the outer surface (i.e. the coating layer 35) of the core member 32. The plated layer 33 coats the outer surface of the core member 32, that is, the coating layer 35 throughout the entire length of the core member 32. A thickness of the plated layer 33 is constant in the circumferential direction and in the longitudinal direction of the core member 32. In an example shown in the figure, the plated layer 33 is made of tin and has a thickness of 8 μm.
The element wire 30 described above has an outer diameter of about 0.8 mm.
The metal plate 31 as a whole is formed in a flat plate-shape. As shown in
The surface layer 37 is made of a metal, such as tin, having a melting point lower than those of the metal constituting the core wire 34, the metal constituting the coating layer 35 and the metal constituting the base member 36. That is, the metal plate 31 includes the base member 36 and the surface layers 37, which are laminated on both outer surfaces of the base member 36 and have a melting point lower than that of the metal constituting the base member 36. The surface layer 37 is laminated on the outer surface of the base member 36 with a constant thickness throughout the entire base member 36. In the example shown in the figure, the surface layer 37 is made of tin having a thickness of 0.8-1.5 μm.
The metal plate 31 having the structure described above has a thickness of about 0.8 mm.
As shown in
Here, (a) the coating layer 35 of the core member 32, i.e. the outer surface of the core member 32 of the element wire 30 and (b) the base member 36 of the metal plate 31 are made of metals, between which no intermetallic compound is formed when the coating layer 35 (i.e. the outer surface) of the core member 32 and the base member 36 are welded together by means of the resistance welding method. Preferably, (a) the coating layer 35 of the core member 32, i.e. the outer surface of the core member 32 of the element wire 30 and (b) the base member 36 of the metal plate 31 are made of the same metal.
The conductor unit 1 having the structure described above is obtained by welding the element wire 30 as one object (to be welded) and the metal plate 31 as another object (to be welded) together by using a resistance welding apparatus 2 (shown in
As shown in
As shown in
Each of the electrodes 15 and 16 is provided with a holder 17 and an electrode body 18. The electrode body 18 is formed in a bar-shape and attached to the holder 17. The holder 17 of one electrode 15 is fixed on the base plate 13, rising upward from the base plate 13. The electrode body 18 of the one electrode 15 is attached to the holder 17, rising upward along the vertical direction from the holder 17. Alternatively, the electrode body 18 of the one electrode 15 may extend along the horizontal direction from the holder 17.
The holder 17 of another electrode 16 is attached to a rod 20 (explained later) of the cylinder 6 in such a manner that the electrode body 18 of the one electrode 15 and the electrode body 18 of the other electrode 16 face each other along the vertical direction. The electrode body 18 of the other electrode 16 is attached to the holder 17, rising downward along the vertical direction from the holder 17. Alternatively, the electrode body 18 of the other electrode 16 may extend along the horizontal direction from the holder 17.
As for the pair of the electrodes 15 and 16, the electrode bodies 18 approach each other when the rod 20 of the cylinder 6 extends, while the electrode bodies 18 leave each other when the rod 20 of the cylinder 6 shrinks. That is, the electrode bodies 18 of the pair of the electrodes 15 and 16 approach and leave each other when the rod 20 of the cylinder 6 extends and shrinks, respectively.
As shown in
As shown in
As shown in
As shown in
As shown in
The control device 11 is a computer which includes a known RAM, ROM, CPU and so on. The control device 11 is connected to the cylinder 6, linear encoder 7, welding power supply 8, ammeter 9 and voltmeter 10 so as to control the whole of the resistance welding apparatus 2. When the element wire 30 and the metal plate 31 are clamped between the pair of the electrodes 15 and 16, the control device 11 permits the cylinder 6 to press the element wire 30 and the metal plate 31 with predetermined force in a direction in which the element wire 30 and the metal plate 31 approach each other.
Then, the control device 11 permits the welding power supply 8 to apply a welding current between the electrodes 15 and 16. Then, the control device 11 keeps a current value of the welding current being a predetermined value on the basis of a current value from the ammeter 9. The control device 11 resistance-welds the coating layer 35, i.e. the outer surface of the core member 32 and the base member 36 together with predetermined quality on the basis of a current value from the ammeter 9, a voltage value from the voltmeter 10 and a movement distance of the electrode 16 from the linear encoder 7, thereby assembling the conductor unit 1.
When the core member 32 of the element wire 30 and the base member 36 of the metal plate 31 are being resistance-welded, first, as shown in
Thereafter, the control device 11 permits the rod 20 of the cylinder 6 to extend so as to press the pair of the electrodes 15 and 16 with a desired load value (i.e. pressure) in a direction in which the electrodes 15 and 16 approach each other and then, permits the welding power supply 8 to apply a welding current between the pair of the electrodes 15 and 16. As a result, the welding current flows between the pair of the electrodes 15 and 16, so that a part of the outer surface of the surface layer 37 of the metal plate 31 and a part of the outer surface of the plated layer 33 of the element wire 30, which come in contact with each other, generate heat.
Thereby, the plated layer 33 and the surface layer 37, which are put between a part of the core member 32 and a part of the base member 36, which parts are clamped between the electrodes 15 and 16, melt. Because the pair of the electrodes 15 and 16 is pressed in the direction in which the electrodes 15 and 16 approach each other by the cylinder 6, therefore the electrodes 15 and 16 gradually approach each other, so that the molten plated layer 33 and the molten surface layer 37 are removed from between the part of the core member 32 and the part of the base member 36, which parts are clamped between the electrodes 15 and 16, and climb on the neighboring plated layer 33 and the neighboring surface layer 37. At that time, because the melting points of the core wire 34 of the core member 32, the coating layer 35 and the base member 36 are higher than those of the plated layer 33 and the surface layer 37, therefore the core wire 34 of the core member 32, the coating layer 35 and the base member 36 are not molten.
Then, as shown in
According to an exemplary embodiment described above, a part of the outer surface of the plated layer 33 and a part of the outer surface of the surface layer 37 as the contacting surface between the element wire 30 and the metal plate 31 are allowed to generate heat to melt the plated layer 33 so as to remove the plated layer 33 from between the coating layer 35 as the outer surface of the core member 32 and the base member 36 of the metal plate 31. Therefore, the coating layer 35 as the outer surface of the core member 32 directly comes in contact with the base member 36 of the metal plate 31. Therefore, the electrical resistance between the element wire 30 and the metal plate 31 can be prevented from increasing.
Further, because no intermetallic compound is formed between the coating layer 35 as the outer surface of the core member 32 and the base member 36 of the metal plate 31, therefore the mechanical strength of the welded part between the coating layer 35 as the outer surface of the core member 32 and the base member 36 of the metal plate 31 can be prevented from deteriorating. That is, the element wire 30 and the metal plate 31 can be joined together with sufficient mechanical strength. Accordingly, the element wire 30 and the metal plate 31 can be welded together in such a manner that the high mechanical strength and low electrical resistance sufficient enough to construct a wiring harness to be mounted on a motor vehicle as a mobile unit can be attained. That is, a conductor unit 1 suitable to construct a wiring harness to be mounted on a motor vehicle as a mobile unit can be obtained.
Because the core member 32 includes the core wire 34 having a melting point higher than that of the coating layer 35, therefore the core wire 34 does not melt upon welding the coating layer 35. Therefore, the mechanical strength of the core member 32 can be secured upon the welding. That is, the core member 32 can be prevented from being damaged upon the welding and therefore, the core member 32 can be welded to the metal plate 31 without being damaged.
Further, when a part of the outer surface of the plated layer 33 and a part of the outer surface of the surface layer 37 as the contacting surface between the element wire 30 and the metal plate 31 are allowed to generate heat, in addition to the plated layer 33, the surface layer 37 of the metal plates 31 is allowed to melt and removed from between the coating layer 35 as the outer surface of the core member 32 and the base member 36 of the metal plate 31. Therefore, the coating layer 35 as the outer surface of the core member 32 securely directly comes in contact with the base member 36 of the metal plate 31. Therefore, the electrical resistance between the element wire 30 and the metal plate 31 can be securely prevented from increasing.
In the exemplary embodiment described above, the core member 32 includes the core wire 34 and the coating layer 35. However, instead, in the present invention, the core member 32 may include a single layer, that is, only the core wire 34 is provided such that the outer surface of the core member 32 is made of metal having a melting point higher than that of the plated layer 33. Alternatively, the core member 32 may include more than two layers. In short, in the present invention, it is necessary to fulfill that at least the outer surface of the core member 32 is made of metal which does not form any intermetallic compound with the base member 36 of the metal plate 31.
In the exemplary embodiment described above, the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 are made of the same metal. However, instead, in the present invention, the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 may be made of respective metals different from each other provided that the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 do not form any intermetallic compound therebetween with the heat generated upon the resistance welding.
For example, one of the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 may be made of Cu, while another thereof may be made of Li, Mn, Ni, Pb, Pd, Pt or Ag. Alternatively, one of the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 may be made of Ag, while another thereof may be made of Au, Bi, Cu, Ge, Na, Ni, Pb, Pd, Si or Tl. Alternatively, one of the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 may be made of Au, while another thereof may be made of Ag, Ge, Pb, Si or Tl. Alternatively, one of the coating layer 35 (i.e., the outer surface) of the core member 32 and the base member 36 of the metal plate 31 may be made of Al, while another thereof may be made of Be, Bi, Ga, Ge, In, Si or Sn.
Further, in the present invention, the surface layer 37 may not be formed on the outer surface of the metal plate 31. The plated layer 33 and the surface layer 37 may be made of various metals other than tin. The other object to be welded may have various shapes other than the flat plate-shape.
The aforementioned exemplary embodiments are described to aid in understanding the present invention and variations may be made by one skilled in the art without departing from the spirit and scope of the present invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1695791 | Yunck | Dec 1928 | A |
| 2735163 | Brooks et al. | Feb 1956 | A |
| 2841546 | Robinson | Jul 1958 | A |
| 2880304 | Campbell | Mar 1959 | A |
| 2918722 | Kenmore | Dec 1959 | A |
| 3443053 | Luetzow | May 1969 | A |
| 3555240 | Gloor et al. | Jan 1971 | A |
| 3591754 | Baldwin, Jr. | Jul 1971 | A |
| 3592993 | Bennett | Jul 1971 | A |
| 3742588 | George | Jul 1973 | A |
| 3841127 | Pashak | Oct 1974 | A |
| 3992602 | Ashton | Nov 1976 | A |
| 4135075 | Heflin | Jan 1979 | A |
| 4203020 | Armbruster et al. | May 1980 | A |
| 4341939 | Briffod et al. | Jul 1982 | A |
| 4400608 | Wagatsuma et al. | Aug 1983 | A |
| 4650951 | Koga et al. | Mar 1987 | A |
| 4686153 | Tominaga et al. | Aug 1987 | A |
| 4717804 | Tomalin | Jan 1988 | A |
| 4740666 | Tomalin et al. | Apr 1988 | A |
| 4837416 | Yamamoto et al. | Jun 1989 | A |
| 4935594 | Groos et al. | Jun 1990 | A |
| 4968867 | Banzai et al. | Nov 1990 | A |
| 4988552 | Tomalin | Jan 1991 | A |
| 5231270 | Groos et al. | Jul 1993 | A |
| 5387774 | Boyer et al. | Feb 1995 | A |
| 5389761 | Kresse, Jr. | Feb 1995 | A |
| 5504296 | Sato et al. | Apr 1996 | A |
| 5587091 | Kawagoe et al. | Dec 1996 | A |
| 5688426 | Kirkwood et al. | Nov 1997 | A |
| 5762726 | Barthel et al. | Jun 1998 | A |
| 5928530 | Lacourcelle | Jul 1999 | A |
| 5961853 | Thornton | Oct 1999 | A |
| 6427904 | Groll | Aug 2002 | B1 |
| 6635843 | Takeda et al. | Oct 2003 | B1 |
| 6781081 | Groos et al. | Aug 2004 | B2 |
| 6794597 | Groos et al. | Sep 2004 | B2 |
| 6861609 | Sigler | Mar 2005 | B2 |
| 7041943 | Michelmann | May 2006 | B2 |
| 7126077 | Wang | Oct 2006 | B2 |
| 7723635 | Shin | May 2010 | B2 |
| 7969021 | Uno et al. | Jun 2011 | B2 |
| 8253062 | Forrest et al. | Aug 2012 | B2 |
| 8445807 | Hashizume et al. | May 2013 | B2 |
| 8546729 | Derda | Oct 2013 | B2 |
| 8597344 | Lundkvist et al. | Dec 2013 | B2 |
| 8853587 | Baumann et al. | Oct 2014 | B2 |
| 20030052113 | Saito et al. | Mar 2003 | A1 |
| 20050000947 | Sigler | Jan 2005 | A1 |
| 20050029234 | Lu et al. | Feb 2005 | A1 |
| 20050236373 | Hidaka | Oct 2005 | A1 |
| 20050247679 | Wang | Nov 2005 | A1 |
| 20060081563 | Ueda et al. | Apr 2006 | A1 |
| 20060219666 | Shin | Oct 2006 | A1 |
| 20080078749 | Sigler et al. | Apr 2008 | A1 |
| 20090025959 | Tomalin | Jan 2009 | A1 |
| 20110290531 | Baumann et al. | Dec 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 30 15 896 | Nov 1980 | DE |
| 195 14 687 | Oct 1995 | DE |
| 2 049 524 | Dec 1980 | GB |
| 06114563 | Apr 1994 | JP |
| 2008-137033 | Jun 2008 | JP |
| Entry |
|---|
| Pfeifer, L., “Technical knowledge of resistance welding,” Essen: Girardet, 1969, pp. 13-20. |
| German Office Action issued in corresponding German Patent Application No. 10 2008 020 582.6-34. |
| Number | Date | Country | |
|---|---|---|---|
| 20080156776 A1 | Jul 2008 | US |