The present invention relates generally to systems and methods for repairing water leaks in concrete substrates, such as in walls and floors.
Concrete is widely used to form building structures such as walls and floors. When these concrete building structures are below grade, they are susceptible to water infiltration. Water seeks to penetrate via a path of least resistance, so cracks in the concrete wall or floor provide an easy path for water to penetrate and reach the interior space of the structure.
Attempts have been made to patch cracks in concrete with mortar or the like, but the patch material is difficult to apply due to the presence of water in the location to be patched. Thus, the patch is susceptible to failure.
Other known solutions are to drill holes in the concrete substrate and inject mud, concrete or a chemical grout under pressure in order to cause the material to flow behind the substrate and hopefully seal the crack(s). One injected chemical grout attempted is a room-temperature flowable polymer rubber gel with the brand name TURBOSEAL. This material is composed of approximately 78% solids, so it will flow at room temperature. These methods have had some measure of success, but there is a continuing need to find even better solutions to seal concrete cracks.
The present invention provides a method and system for sealing cracks in concrete substrates such as walls and floors. A plurality of holes are drilled through the concrete substrate, with at least one hole on each opposing side of the crack. Then a polymer rubber gel that is thick enough that it does not flow at room temperature (e.g. comprising 99% solids) is heated in a tank to an elevated temperature (e.g. 120-200° F.). Next, the heated polymer rubber gel is pumped in the heated state through one of the holes in the concrete. The pumping continues until the polymer rubber gel is observed exiting a second drilled hole that is spaced apart from the injecting hole. The polymer rubber gel rapidly cools and solidifies, thereby forming a waterproofing membrane that seals the crack(s).
The disclosure includes a method of providing a restorative waterproofing membrane to a distal side of a concrete substrate that includes a crack through the substrate from a proximal side to the distal side. The method includes forming a first hole through the concrete substrate from the proximal side that communicates with the distal side. A second hole is formed through the concrete substrate from the proximal side that communicates with the distal side. The second hole is laterally displaced from the first hole along the proximal side such that the crack lies between the first hole and the second hole. An injection valve is coupled to the first hole. A distal end of a heated hose is coupled to the injection valve. A proximal end of the heated hose is coupled to a heated hopper. The heated hopper includes a pump. A polymer rubber gel material is introduced into the heated hopper. The temperature of the polymer rubber gel in the hopper is elevated until the polymer rubber gel material can flow under pressure through the heated hose. The polymer rubber gel material is pumped at the elevated temperature through the injection valve until the polymer rubber gel material can be observed exiting the second hole.
The disclosure also includes a process for repairing a water leak through a concrete substrate. The method includes forming a first hole through the concrete substrate from the proximal side that communicates with the distal side. A second hole is formed through the concrete substrate from the proximal side that communicates with the distal side. The second hole is laterally displaced from the first hole. A polymer rubber gel material is pumped at an elevated temperature through the first hole until the polymer rubber gel material can be observed exiting the second hole. The polymer rubber gel is sufficiently viscous that the polymer rubber gel cannot be pumped when at room temperature.
The disclosure further includes a system for repairing a water leak through a concrete substrate. The system includes an injection valve, a polymer rubber gel material that comprises 99% solids, a heated tank configured to heat the polymer rubber gel material to a temperature range of 120-200° F., a pump coupled to the heated hopper and a heated delivery hose coupled to the hopper. An end of the heated delivery hose is configured to couple to an end of the injection valve.
The above summary is not intended to limit the scope of the invention, or describe each embodiment, aspect, implementation, feature or advantage of the invention. The detailed technology and preferred embodiments for the subject invention are described in the following paragraphs accompanying the appended drawings for people skilled in this field to well appreciate the features of the claimed invention. It is understood that the features mentioned hereinbefore and those to be commented on hereinafter may be used not only in the specified combinations, but also in other combinations or in isolation, without departing from the scope of the present invention.
While the invention is amenable to various modifications and alternative forms, specifics thereof have been shown by way of example in the drawings and will be described in detail. It should be understood, however, that the intention is not to limit the invention to the particular example embodiments described. On the contrary, the invention is to cover all modifications, equivalents, and alternatives falling within the scope of the invention as defined by the appended claims.
In the following descriptions, the present invention will be explained with reference to various exemplary embodiments. Nevertheless, these embodiments are not intended to limit the present invention to any specific example, environment, application, or particular implementation described herein. Therefore, descriptions of these example embodiments are only provided for purpose of illustration rather than to limit the present invention.
Referring to
The concrete wall substrate 100 shown in
The present system and method can be applied to repair one or more cracks in the concrete wall 100 or the membrane can be established prophylactically to guard against leakage through future cracks that may form in the concrete wall 100.
Another way that a concrete wall 100 can fail and leak is where the protective layer(s) between the wall and the soil are compromised. For example, between the concrete substrate 100 and the soil 102 is a sandwich of a protective layer 104 and waterproofing material 106. If the waterproofing sandwich 104, 106 is compromised or is inadequate to prevent water passage from the soil to the concrete substrate 100, there is a substantial chance that water will penetrate through the concrete wall 100. The penetration will be even worse where the concrete wall 100 is cracked as the water will attempt to escape into the interior through the crack(s).
In order to remedy the water intrusion, a series or array of holes 101 are drilled through the concrete wall 100 as shown in
As shown in
The chemical grout in one embodiment can be a polymer rubber gel material 108. In particular, it is preferred that the polymer rubber gel comprises a sufficient solids percentage such that it is not flowable at room temperature. Most preferably, the polymer rubber gel comprises 99% solids.
Polymer rubber gel is a non-curing rubber emulsion with adhesive and cohesive physical characteristics. Polymer rubber gel never completely cures and remains in a flexible state. Since it never cures, it is capable of self-healing under application of hydrostatic pressure. Also, due to Polymer rubber gel's responsiveness to substrate movement and vibration, it makes for an excellent substance to repair cracks in concrete and/or separations in waterproofing layers.
In contrast, other chemical grouts cure and crack, leading to renewed water intrusion. The non-curing property of polymer rubber gel can weather the constant stress of thermal expansion/contraction, seismic activity and vibration that might be experienced in a wide variety of applications. The polymer rubber gel layer 108 also provides for creation of a seamless or continuous layer. Thus, there are no seams or gaps where water can easily penetrate.
Not all polymer rubber gels are the same. For example, different gels have widely differing amounts of solids in their content. Thus, any two given gels will have very different material properties. The higher the solids content, the more viscous the polymer rubber gel material will be at room temperature.
To achieve flowability (and injectability) at room temperature, a relatively thin gel such as TURBOSEAL has been conventionally used. TURBOSEAL polymer rubber gel is approximately 78% solids and can flow at room temperature. This allows the gel to be injected at typical room temperature and up to about 90° F. But such gel cannot be heated to an elevated temperature without the gel breaking down. As a result, only a modest waterproofing membrane can be formed behind the concrete wall 100. Also, the room temperature flowability means that the injected polymer rubber gel material can migrate over time, which may cause the water leakage to reoccur.
In contrast, the present invention utilizes a polymer rubber gel with a much higher solids content than TURBOSEAL polymer rubber gel and the like. The preferred gel material is not flowable at room temperature (e.g. 99% solids). That also means it is not injectable at room temperature.
One example polymer rubber gel can have the physical properties noted in the following Table 1:
In order to address the need for the preferred polymer rubber gel material to be flowable in order to be injected, the invention includes heating of the polymer rubber gel to an elevated temperature range of 120-200° F. and most preferably 150-200° F. The preferred polymer rubber gel does not break down because it is almost entirely solids.
The heating of the polymer rubber gel can be accomplished by providing a heated hopper 114 or tank where the solid blocks of gel material are deposited after removing them from their packaging. The hopper 114 then heats the solid blocks to lower the viscosity of the polymer rubber gel, which allows it to flow.
A heated hose 116 is coupled to the hopper 114 to be a conduit between the hopper 114 and the injection valve 110. The heated hose 116 helps maintain the elevated temperature of the polymer rubber gel until it reaches the point of injection because the polymer rubber gel will quickly cool upon injection.
An injection pump 118 is provided to the hopper 114 to pressurize the flow of heated polymer rubber gel from the hopper 114 and through the hose 116 so that the polymer rubber gel can be injected through the valve 110 with pressure. The flow of the heated polymer rubber gel can be regulated by operation of the injection valve 110.
Arrows are provided in
In use, the injection valve 110 is inserted into a first hole 101 on a first side of a crack. The hose 116 is attached to the injection valve 110. The heated polymer rubber gel is pumped under pressure through the injection valve which causes the polymer rubber gel to flow along the back side of the concrete wall 100. Once the polymer rubber gel begins to exit the second hole in the concrete wall located on an opposite side of the crack, the injection valve is closed to stop the material flow. This process can be repeated for additional spaced-apart holes until a desired restorative membrane is formed behind the wall (soil side).
After injection, the polymer rubber gel material 108 flows for a short time until it cools back to ambient temperature, which effectively solidifies the polymer rubber gel so that it cannot flow or migrate further. This solidification property at room temperature provides a far stronger water barrier and seal as compared to use of the room temperature flowable gel material. Moreover, the higher solids content of the invention combined with heating allows for better spreading and filling of cracks since the heated polymer rubber gel is less viscous at the elevated temperature as compared to the prior art polymer rubber gel at room temperature. Thus, a stronger final sealing effect can be achieved as compared to the use of room temperature flowable gel material. The increased flowability due to elevated material temperatures of the invention also makes for a quicker restoration process because the heated gel material flows quicker than the room temperature flowable gel material. The self-healing ability of the polymer rubber gel of the invention and its non-migration characteristics can also provide a permanent repair in many applications.
A waterproofing method can include injecting the heated polymer rubber gel material in more than one hole 101 separately, or simultaneously. The number of injection holes or sites employed depends on the size of the area needing to receive the restorative waterproofing membrane.
While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiments, it will be apparent to those of ordinary skill in the art that the invention is not to be limited to the disclosed embodiments. It will be readily apparent to those of ordinary skill in the art that many modifications and equivalent arrangements can be made thereof without departing from the spirit and scope of the present disclosure, such scope to be accorded the broadest interpretation of the appended claims so as to encompass all equivalent structures and products. Moreover, features or aspects of various example embodiments may be mixed and matched (even if such combination is not explicitly described herein) without departing from the scope of the invention.
This application claims the priority benefit of U.S. Provisional Application No. 62/159,207 filed on May 8, 2015, which is hereby incorporated herein by reference in its entirety.