Information
-
Patent Grant
-
4814084
-
Patent Number
4,814,084
-
Date Filed
Thursday, September 1, 198836 years ago
-
Date Issued
Tuesday, March 21, 198935 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
-
CPC
-
US Classifications
Field of Search
US
- 210 50029
- 210 5003
- 210 50031
- 210 50032
- 264 41
- 264 48
- 264 86
-
International Classifications
-
Abstract
There is provided a method of manufacturing cellulose membranes with pore radii less than 30.times.10.sup.-10 m, suitable for reverse osmosis applications. The method comprises dissolving a cellulosic material in a DMSO/PF solvent at a temperature about 125.degree. C. for about 90 min., cooling and casting the solution at room temperature, evaporating the solvent at a temperature of 140.degree.-180.degree. C. and gelling the resulting membrane in a protic solvent, e.g. ethanol or water.
Description
This invention relates to reverse osmosis membranes and particularly to a method of manufacturing such membranes of cellulose or cellulosic material.
BACKGROUND OF THE INVENTION
Reverse osmosis (RO) membranes are widely used in the separation of water from various aqueous solutions, for instance for water desalination. Such membranes have been made for example from cellulose acetate. The processes for the preparation of such membranes are described in Loeb et al. U.S. Pat. Nos. 3,133,132 and 3,133,137, in Cannon U.S. Pat. No. 3,460,683 and in MacDonald et al. U.S. Pat. No. 3,842,515. The processes involve generally: preparation of a suitable casting solution, casting the solution onto a substrate, evaporation of the solvent and gelling the cast in a gelling medium. The casting solutions used in the processes referred to hereinabove generally contain acetone.
It has also been known for a number of years to manufacture membranes by regenerating cellulose from cellulose acetate or from cellulose nitrate.
While cellulose acetate membranes are useful, cellulose membranes have a distinct advantage over the former. The advantage is in their higher mechanical strength and lower affinity to organic solute compounds in aqueous solutions. Thus, cellulose membranes are less susceptible to fouling by organic contaminants. The relatively small affinity to organic compounds also enables celulosic membranes to withstand the environment of nonaqueous solvents.
It is also known that membranes may be obtained from cellulose by dissolving a cellulose-containing material in dimethyl sulfoxide (DMSO) and paraformaldehyde (PF). These two compounds appear to be excellent and nondegrading solvents of cellulose when applied in certain proportions. The formation of methylol cellulose is reported to be crucial to the dissolution mechanism. The DMSO/PF solvent system is capable of dissolving a variety of cellulosic materials with weight average degrees of polymerization ranging from 16 to over 8000.
Seymour and Johnson, Journal of Applied Polymer Science, Vol. 20, 3425 (1976), have attempted to prepare cellulose solutions in the DMSO/PF solvent with concentrations up to 10%. The temperature of dissolution in these experiments was 65.degree. to 80.degree. C., and it was found that complete cellulose solution was only achieved with cellulose concentration about 0.5%. The molar ratio of paraformaldehyde to cellulose was about 10:1. Such mixtures of cellulose and PF in dimethyl sulfoxide produced homogeneous solutions or gels from which cellulose was precipitated by adding dioxane, alcohol or water. However, precipitation in water or ethanol, wet spinning in water or alcohol as well as solvent evaporation resulted in brittle films and weak fibers.
(a) dissolving cellulose (or cellulosic material) in a dimethyl sulfoxide/paraformaldehyde solvent to form a casting solution containing
(i) 12-15 wt % cellulose,
(ii) 70-76 wt % dimethyl sulfoxide, and
(iii) 12-15 wt % paraformaldehyde at an elevated temperature while formaldehyde gas is evolved and until a transparent casting solution is formed,
(b) cooling the casting solution to about room temperature,
(c) casting the cooled solution at about room temperature,
(d) evaporating the solvent from the cast solution at a temperature in the range 140.degree.-180.degree. C., and
(e) gelling the cast solution in a gelling medium comprising at least one liquid selected from the group consisting of water, an alcohol having carbon atoms in the range 1 to 4, acetone and methyl ethyl ketone at a temperature of 0.degree.-30.degree. C.
Preferably, the temperature of evaporation is about 170.degree. to 175.degree. C. The gelling medium must be a protic solvent to achieve a satisfactory gellation.
Following the work of Seymour and Johnson, Doshi and Webb reported a relation between the concentration of cellulose in the casting solution (or in the gel) and the pore sizes of the membranes obtained thereby (Proceedings of 1983 International Dissolving and Specialty Pulps Conference, Boston, April 5-8, 1983, TAPPI Press, Atlantic, Ga., 41 (1983)). The membranes obtained by Doshi and Webb had pore sizes of ca. 750.times.10.sup.-10 m (750 .ANG.).
Uragami et al. (Sep. Sci. and Tech., 17(2), 307 (1982) obtained casting solutions based on the dissolution method of Seymour and Johnson with cellulose concentrations below 9 wt. %, wherein the solvent was evaporated below 110.degree. C.
For certain reverse osmosis applications such as water desalination, it is desirable to obtain membranes of pore radii smaller than 30.times.10.sup.-10 m. Such membranes can be produced from cellulose acetate but have not thus far been obtained from cellulose. Such need exists in view of the advantages of cellulosic membranes as explained above.
STATEMENT OF INVENTION
According to the present invention, an improved method is provided for manufacturing reverse osmosis membranes of cellulose or cellulosic material. The method comprises the steps of:
DETAILED DESCRIPTION OF THE INVENTION
A number of tests were conducted to verify the invention and establish the range of parameters leading to acceptable membranes. A typical experimental procedure is described below.
Known weights of cellulose powder (Baker), paraformaldehyde powder and DMSO (Fisher) totalling ca. 200 g were slurried at room temperature in a closed 500 ml flask. The flask was placed in a paraffin oil temperature bath and was fitted with an air cooled condenser. The bath temperature was slowly raised to 125.degree..+-.2.degree. C. while the slurry was vigorously stirred. As the oil bath temperature exceeded 105.degree. C., gas bubbles were observed in the agitated slurry, presumably caused by the decomposition of PF to formaldehyde gas. The slurry was opaque prior to the formation of bubbles but after 30 minutes it became clearer. The solution was held at 125.degree. C. for 90 minutes while vigorous stirring continued. The flask was then sealed from the atmosphere and cooled to room temperature. The solution was transparent but contained gas bubbles and residual PF particles.
It was pressure filtered and left to stand overnight whereby the solid residue and the bubbles were removed.
The membranes were made by casting the solution as a thin film at room temperature onto smooth glass sheets edged with a polyvinyl chloride tape to control the film thickness. The glass plate was immediately placed in a preheated oven at a controlled temperature to evaporate the DMSO solvent. After the evaporation, the glass plate was immediately placed in a gelling solution. The membranes produced were translucent and were typically 0.17 mm in thickness.
The preferable range of evaporation temperature is 170.degree.-180.degree. C., with an optimum about 175.degree. C.
It is advantageous to ensure that the slurry contains no water as water interferes, according to some literature references, with the dissolution of cellulose. In these experiments, cellulose was stored in a desiccator under vacuum before slurrying. For some cellulosic materials having originally a pH significantly different from 7, it may be necessary to bring the pH to neutral e.g. by washing the material with distilled water.
Casting solution compositions and the preparation details for respective membranes are shown in Table I. Where the gelation medium was an organic solvent (membrane No. I and III), the samples were subsequently placed in ice cold water for cellulose regeneration.
TABLE I______________________________________Film Casting DetailsMembrane No. I II III IV______________________________________Composition of castingsolution, wt. %Cellulose 12.3 13.4 13.6 14.3DMSO 75.4 73.2 72.8 71.4paraformaldehyde 12.3 13.4 13.6 14.3Film casting conditionsTemperature of casting room room room roomsolutionSolvent evaporation 175 160 152 142temperature, .degree.C.Solvent evaporation 10 10 10 10time, min.Gelation medium.sup.a EtOH water i-PrOH waterGelation temperature, .degree.C. room room room room______________________________________ .sup.a Gelation period 100 min.
Reverse osmosis experiments were conducted on the membranes obtained by the above-described procedure. The pore radii of the membranes were found to be less than 30.times.10.sup.-10 m. In these experiments, the effective membrane surface was 13.2 cm.sup.2. The membranes were operated at 1724 kPag (ca. 250 psig). The inorganic solute concentrations were determined by electroconductivity measurement.
The results of the reverse osmosis experiments are shown in Table II.
TABLE II______________________________________Reverse Osmosis Experimental ResultsMem- Feed Pure water.sup.a Product.sup.a Solutebrane conc., permeation rate, separ-no. Solute molal g/h g/h ation %______________________________________I NaCl 0.001 6.05 5.62 76.4I NaF 0.004 6.05 5.70 68.6I Na.sub.2 SO.sub.4 0.004 6.05 5.30 87.1I Na.sub.2 HPO.sub.4 0.009 6.05 6.02 88.9I Na.sub.2 SO.sub.4 0.001 6.05 6.02 95.5I t-Butanol 0.001 6.05 5.84 47.7I l-Octanol 0.0005 6.05 5.92 63.7I Sucrose 0.0007 6.05 5.81 69.5I Anisole 0.0001 6.05 5.89 84.3I Phenol 0.0004 6.05 5.87 23.7I Benzene 0.0001 6.05 5.97 85.6I t-Butyl 0.0002 6.05 5.64 83.6 i-Propyl etherI PEG-1000.sup.b 52.8.sup.c 6.05 5.68 77.3I PEG-6000.sup.b 58.1.sup.c 6.05 6.05 96.6II MgSO.sub.4 0.015 7.50 7.10 58.7II sucrose 0.0008 7.50 7.36 43.7III RbCl 0.003 6.24 6.13 62.6III NaF 0.004 6.24 6.04 65.6IV MgSO.sub.4 0.015 7.14 6.87 59.1IV sucrose 0.0008 7.14 7.01 42.7______________________________________ .sup.a effective membrane surface is 13.2 cm.sup.2 .sup.b polyethylene glycol .sup.c ppm
It is apparent that the improved method of the invention provides conditions for preparing good reverse osmosis membranes capable of yielding significant separation for a variety of inorganic and organic solutes. While the above examples give an indication as to the expected performance of the membranes obtained by the method of the invention, it will be appreciated that some testing work may be necessary to select optimum membrane preparation conditions for a specific reverse osmosis application, the conditions being within the scope of the invention as defined by the appended claims.
Claims
- 1. A method of manufacturing a reverse osmosis membrane of cellulosic material, comprising the steps of:
- (a) dissolving the cellulosic material in a dimethyl sulfoxide/paraformaldehyde solvent to form a casting solution containing
- (i) 12-15 wt % cellulose,
- (ii) 70-76 wt % dimethyl sulfoxide, and
- (iii) 12-15 wt % paraformaldehyde at an elevated temperature while formaldehyde gas is evolved and until a transparent casting solution is formed,
- (b) cooling the casting solution to about room temperature,
- (c) casting the cooled solution at about room temperature,
- (d) evaporating the solvent from the cast solution at a temperature in the range 140.degree.-180.degree. C., and
- (e) gelling the cast solution in a gelling medium comprising at least one liquid selected from the group consisting of water, an alcohol having carbon atoms in the range 1 to 4, acetone and methyl ethyl ketone at a temperature of 0.degree.-30.degree. C.
- 2. The method of claim 1 where the cellulosic material is dissolved at a temperature of 125.degree..+-.2.degree. C.
- 3. The method of claim 2 wherein the solvent evaporation temperature is 170.degree.-180.degree. C.
- 4. The method of claim 1 wherein the solvent evaporation temperature is 170.degree.-180.degree. C.
- 5. A cellulose membrane obtained by the steps of
- (a) dissolving the cellulosic material in a dimethyl sulfoxide/paraformaldehyde solvent to form a casting solution containing
- (i) 12-15 wt % cellulose,
- (ii) 70-76 wt % dimethyl sulfoxide, and
- (iii) 12-15 wt % paraformaldehyde at an elevated temperature while formaldehyde gas is evolved and until a transparent casting solution is formed,
- (b) cooling the casting solution to about room temperature,
- (c) casting the cooled solution at about room temperature,
- (d) evaporating the solvent from the cast solution at a temperature in the range 140.degree.-180.degree. C., and
- (e) gelling the cast solution in a gelling medium comprising at least one liquid selected from the group consisting of water, an alcohol having carbon atoms in the range 1 to 4, acetone and methyl ethyl ketone at a temperature of 0.degree.-30.degree. C.
- 6. The membrane of claim 5 having pore radii below 30.times.10.sup.-10 m.
Priority Claims (1)
Number |
Date |
Country |
Kind |
548640 |
Oct 1987 |
CAX |
|
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4323627 |
Joh |
Apr 1982 |
|