The present invention relates to a reversible permeability measuring device, and more particularly, to a reversible permeability measuring device for measuring magnetic characteristics and magnetic flux change in a specimen, as one of a plurality of non-destructive methods for evaluating mechanical properties.
Since mechanical properties of structural steel, turbine rotor steel, or the like, are associated with magnetic characteristics, the mechanical properties are evaluated by non-destructively measuring magnetic characteristics.
A coil used for a magnetic characteristic measuring device for measuring the magnetic characteristics is largely classified into a surface type probe measuring the change in a magnetic flux generated from a specimen by vertically disposing a coil on a surface of a specimen to be measured and an encircling type probe winding a coil around a round bar or a flake type specimen The former is used to measure Barkhausen noise (BN) or harmonics and the latter is used to measure a magnetic hysteresis curve in addition to the BN or the harmonics. Among others, the former is usefully used for the magnetic evaluation of a non-destructively operated material.
An example of the reversible permeability measuring device was disclosed in paper “Nondestructive evaluation of aged 1Cr-1Mo-0.25V steel by harmonic analysis of induced voltage” (JMMM, Volume 231, 2001. 3) published in Journal of Magnetism and Magnetic Materials by the inventors.
The paper defines the correlation capable of measuring Vickers hardness, yield strength, and tensile strength, all of which are mechanical properties of artificially deteriorated 1Cr-1Mo-0.225V steel, non-destructively measuring reversible permeability that is a primary harmonic of an AC magnetic field with the surface type probe, and inferring mechanical properties with a coercive force that is ½ of a peak interval of reversible magnetic permeability.
A system of measuring reversible permeability with the surface type probe used in the paper was shown in
The surface type probe is manufactured by winding a pick up coil to a yoke and then, winding an AC driving coil and a DC driving coil thereto. Meanwhile, a direct current is applied by power-amplifying a function generated from an I/O acquisition board with a power amplifier and an AC magnetic field applies a function generated from a function generator. The reversible permeability induced to the pick up coil is measured by a lock-in amplifier using a frequency of the AC magnetic field as a reference signal and values read by a shunt and the lock-in amplifier are measured through an input side of the I/O acquisition board and are then processed as data in a computer.
The magnetic characteristic measuring device having the above-mentioned structure uses a manner that obtains current from the voltage measured in the shunt to indirectly calculate a magnetic field H through the following Equation 1.
(n: winding number per unit length, i: current obtained in shunt, and 1: average magnetic path)
As represented by Equation 1, when the magnetic field H is calculated, it is calculated by an indirect calculation scheme, such that the measured value of the reversible permeability is inaccurate and the reliability of deterioration evaluation on materials is degraded.
The correlation capable of inferring the mechanical properties with a coercive force that is ½ of a peak interval of reversible magnetic permeability (PIRMP) using the magnetic characteristic measuring device having the above-mentioned structure is obtained, as shown in
In this case, the measurement of the coercive force that is ½ of the peak interval of reversible magnetic permeability (PIRMP) is made as shown in a graph of
An object of the present invention is to provide a reversible permeability measuring device capable of more accurately evaluating deterioration of a material by directly measuring magnetic field on a surface of a specimen.
In one general aspect, a reversible permeability measuring device includes: a surface type probe 10 including a DC driving coil 11 wound to an outermost side and applying DC magnetic field, an AC driving coil 12 wound to the inner side of the DC driving coil 11 and applying AC perturbing magnetic field to the applied DC magnetic field, a pick up coil 13 wound to the inner side of the AC driving coil 12 and picking up the induced AC perturbing magnetic field, and a yoke 14 to which the coils 11, 12, and 13 are wound and spacing a specimen 1 from the coils 11, 12, and 13; a magnetic potentiometer 20 provided in the inner side of the surface type probe 10 and detecting magnetic field induced from the surface of the specimen 1; an AC function generator 30 applying an AC magnetic field function to the AC driving coil 12; a lock-in amplifier 40 measuring reversible permeability induced to the pick up coil 13 by using the frequency of the applied AC perturbing magnetic field as a reference signal; a fluxmeter 50 measuring the magnetic field induced from the surface of the specimen 1, which is detected from the magnetic potentiometer 20; an I/O acquisition board 60 applying a DC magnetic field function to the DC driving coil 11, applying the AC magnetic field to the AC driving coil 12, and being applied with the magnetic field induced from the surface of the specimen measured in the fluxmeter 50; a power amplifier 70 applying power in a function applied from the I/O acquisition board 60 to the DC driving coil 11; and a microcomputer 80 directly calculating the reversible permeability induced to the pick up coil 13 input to the I/O acquisition board 60 and the magnetic field generated from the surface of the specimen 1 measured in the fluxmeter 50.
The magnetic potentiometer 20 may be provided in the inner side of the yoke 14.
The present invention improves the problem in that the measured value of the magnetic field is inaccurate and the reliability of deterioration evaluation on materials is degraded, due to the magnetic field H calculated by the indirect calculation manner. That is, the present invention directly measures the magnetic field generated on the surface of the specimen by using the magnetic potentiometer and the fluxmeter, thereby making it possible to more accurately evaluate the deterioration of the material.
The above and other objects, features and advantages of the present invention will become apparent from the following description of preferred embodiments given in conjunction with the accompanying drawings, in which:
Hereinafter, a reversible permeability measuring device according to the present invention will be described with reference to the accompanying drawings.
As shown, the reversible permeability measuring device according to the present invention is configured to include a surface type probe 10 including a DC driving coil 11, an AC driving coil 12, a pick up coil 13, and a yoke 14 wound with the coils 11, 12, and 13; a magnetic potentiometer 20 detecting magnetic field induced from the surface of the specimen 1; an AC function generator 30 applying an AC magnetic field function to the AC driving coil 12; a lock-in amplifier 40 measuring reversible permeability of a specimen induced to the AC driving coil 12; a fluxmeter 50 measuring the magnetic field induced from the surface of the specimen 1; an I/O acquisition board 60 applying the reversible permeability of the specimen induced to the AC driving coil 12 and being applied with the magnetic field induced from the surface of the specimen 1 measured in the fluxmeter 50; a power amplifier 70 applying power to the DC driving coil 11; and a microcomputer 80 directly calculating the reversible permeability of the specimen induced to the pick up coil 13 and the magnetic field induced from the surface of the specimen 1 measured in the fluxmeter 50.
The surface type probe 10 is configured to include the DC driving coil 11, the AC driving coil 12, the pick up coil 13, and the yoke 14 wound with the coils 11, 12, and 13, wherein the pick up coil 13, the AC driving coil 12, and the DC driving coil 11 are sequentially wound from the inner side of the yoke 14.
The DC driving coil 11 is wound to the outermost side of the yoke 14 and applies the DC magnetic field. In this case, the applied DC magnetic field is applied through the power amplifier 70 in the DC magnetic field function applied from the I/O acquisition board.
The AC driving coil 12 is wound to the inner side of the DC driving coil 11 and serves to induce the AC perturbing magnetic field to the applied DC magnetic field.
The pick up coil 13 is wound to the inner side of the AC driving coil 12 and detects the DC magnetic field and the reversible permeability of the specimen induced by the AC perturbing magnetic field by the lock-in amplifier 40 using the frequency of the AC perturbing magnetic field as the reference signal.
The yoke 14 is wound with the coils 11, 12, and 13 and spaces the specimen 1 from the coils 11, 12, and 13.
The magnetic potentiometer 20 is provided in the inner side of the surface type probe 10 and serves to detect the magnetic field induced from the surface of the specimen 1. In this case, the magnetic potentiometer 20 may be provided in the inner side of the yoke 14.
The function generator 30 serves to apply the AC magnetic field function to the AC driving coil 12. The DC magnetic field applied from the DC driving coil 11 applies the AC magnetic field from the AC function generator 30 to induce the AC perturbing magnetic field.
The lock-in amplifier serves to measure the reversible permeability of the specimen induced to the pick up coil 13 using the frequency of the AC magnetic field function as the reference signal.
The fluxmeter 50 serves to directly measure the magnetic field induced from the surface of the specimen 1 detected from the magnetic potentiometer 20. Therefore, when the magnetic field H generated from the surface of the specimen is calculated, the related art calculates the magnetic field generated from the surface of the specimen through the indirect calculation manner rather than through the direct calculation manner, while the present invention directly measures the magnetic field generated from the surface of the specimen, thereby making it possible to obtain the accurate measured values and improve the reliability of deterioration evaluation on materials.
The I/O acquisition board 60 applies the DC magnetic field function to the DC driving coil 11 and applies the reversible permeability induced to the pick up coil 13 and the reversible permeability induced from the surface of the specimen 1 measured in the fluxmeter 50.
The power amplifier 70 serves to apply power in the function applied from the I/O acquisition board 60 to the DC driving coil 11.
The microcomputer 80 directly calculates the reversible permeability induced to the pick up coil 13, which is input to the I/O acquisition board 60, and the magnetic field induced from the surface of the specimen 1 measured in the fluxmeter 50.
As shown, it can be appreciated that the graph has result values of the left and right symmetrical structure. As such, as the graph has the left and right symmetrical structure, the coercive force that is ½ of the peak interval of reversible magnetic permeability (PIRMP) can be more accurately measured and the mechanical properties can be more accurately inferred.
The present invention improves the problem in that the measured value of the magnetic field is inaccurate and the reliability of deterioration evaluation on materials is degraded, due to the magnetic field H calculated by the indirect calculation manner. That is, the present invention directly measures the magnetic field generated on the surface of the specimen by using the magnetic potentiometer and the fluxmeter, thereby making it possible to more accurately evaluate the deterioration of the material.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2008-0063810 | Jul 2008 | KR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/KR2009/003573 | 7/1/2009 | WO | 00 | 12/29/2010 |