Patent Application
20230257615
The invention relates to a rheology-modifying diurethane compound. The invention also provides an aqueous composition comprising a diurethane compound according to the invention and a method for controlling the viscosity of an aqueous composition using the diurethane compound according to the invention.
In general, for aqueous coating compositions, and in particular for aqueous paint or varnish compositions, it is necessary to control the viscosity both for low or medium shear gradients and for high shear gradients. Indeed, during its preparation, storage, application or drying, a paint formulation is subjected to numerous stresses requiring particularly complex rheological properties.
When paint is stored, the pigment particles tend to settle by gravity. Stabilising the dispersion of these pigment particles therefore requires a paint formulation with high viscosity at very low shear gradients corresponding to the limiting velocity of the particles. Paint uptake is the amount of paint taken up by an application tool such as, for example, a paintbrush, a brush or a roller. If the tool takes up a large amount of paint when dipped into and removed from the can, it will not need to be dipped as often. Paint uptake increases as the viscosity increases. The calculation of the equivalent shear gradient is a function of the paint flow velocity for a particular thickness of paint on the tool. The paint formulation should therefore also have a high viscosity at low or medium shear gradients.
Moreover, the paint must have a high filling property so that, when applied to a substrate, a thick coat of paint is deposited at each stroke. A high filling property therefore makes it possible to obtain a thicker wet film with each stroke of the tool. The paint formulation must therefore have a high viscosity at high shear gradients.
High viscosity at high shear gradients will also reduce or eliminate the risk of splattering or dripping when the paint is being applied.
Reduced viscosity at low or medium shear gradients will also result in a neat, taut appearance after the paint has been applied, particularly a single-coat paint, to a substrate which will then have a very even surface finish with no bumps or indentations. The final visual appearance of the dry coat is thus greatly improved.
Furthermore, once the paint has been applied to a surface, especially a vertical surface, it should not run. The paint formulation thus needs to have a high viscosity at low and medium shear gradients.
Lastly, once the paint has been applied to a surface, it should have a high levelling capacity. The paint formulation must then have a reduced viscosity at low and medium shear gradients.
Document EP0761780 discloses thickening and heat-resistant diurethane compounds.
Document EP1908807 discloses aqueous metal paint compositions that may comprise a diurethane compound. Document JP2009001687 discloses industrial paint emulsions that may comprise a diurethane compound. Document FR2113316 discloses diurethane compounds for textile printing pulp.
HEUR (hydrophobically modified ethoxylated urethane)-type compounds are known as rheology-modifying agents.
However, the known HEUR-type compounds do not always make it possible to provide a satisfactory solution. In particular, the rheology-modifying compounds of the prior art do not always allow for effective viscosity control or do not always achieve a satisfactory improvement in the compromise between Stormer viscosity (measured at low or medium shear gradients and expressed in KUs) and ICI viscosity (measured at high or very high shear gradients and expressed in s−1). In particular, the known rheology-modifying compounds do not always make it possible to increase the ICI viscosity/Stormer viscosity ratio.
There is therefore a need for improved rheology-modifying agents. The diurethane compound according to the invention makes it possible to provide a solution to all or part of the problems of the rheology-modifying agents in the prior art.
The invention thus provides a diurethane compound T prepared by reacting:
Essentially according to the invention, the diurethane compound T is prepared from at least one compound (a) comprising two isocyanate groups and from a compound (b) capable of reacting with these isocyanate groups and comprising a saturated, unsaturated or aromatic hydrocarbon chain combined with a polyalkoxylated chain. Preferably according to the invention, this reagent compound (b) is a monohydroxylated compound.
Preferably according to the invention, the condensation of compounds (a) and (b) is carried out in the presence of a catalyst. This catalyst can be chosen among an amine, preferably 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU), a derivative of a metal chosen among Al, Bi, Sn, Hg, Pb, Mn, Zn, Zr, Ti. Traces of water may also participate in the catalysis of the reaction. As examples of metal derivatives, a derivative is preferably chosen among dibutyl bismuth dilaurate, dibutyl bismuth diacetate, dibutyl bismuth oxide, bismuth carboxylate, dibutyltin dilaurate, dibutyltin diacetate, dibutyltin oxide, a mercury derivative, a lead derivative, zinc salts, manganese salts, a compound comprising chelated zirconium, a compound comprising chelated aluminium. The preferred metal derivative is chosen among a Bi derivative, an Sn derivative and a Ti derivative.
Preferably according to the invention, the reaction uses a single compound (a) or the reaction uses two or three different compounds (a).
According to the invention, the polyisocyanate compound (a) comprises on average two isocyanate groups. Generally, the polyisocyanate compound (a) comprises on average 2±10 mol % isocyanate groups. According to the invention, the diisocyanate compounds are symmetric diisocyanate compounds or asymmetric diisocyanate compounds. The symmetric diisocyanate compounds comprise two isocyanate groups that have the same reactivity. The asymmetric diisocyanate compounds comprise two isocyanate groups that have different reactivities.
Preferably according to the invention, the compound (a) is chosen among:
Preferably according to the invention, the compound (a) is chosen among IPDI, HDI, H12MDI and combinations thereof.
According to the invention, the monoalcohols are compounds comprising a single hydroxyl (OH) group that is terminal. According to the invention, the polyethoxylated monoalcohols are compounds comprising a hydrocarbon chain that comprises several ethoxylated groups and a terminal hydroxyl (OH) group. According to the invention, the polyethoxylated monoalcohols are compounds of formula R-(LO)n-H in which R represents a hydrocarbon chain, n represents the number of polyethoxylations and L, identical or different, independently represents a straight alkylene group comprising 2 carbon atoms. According to the invention, the number of carbon atoms defining monoalcohols (b1) to (b3) therefore corresponds to the number of carbon atoms in the R groups.
According to the invention, the polyethoxylated monoalcohols comprise from 100 to 500 ethoxylated groups, preferably from 100 to 400 ethoxylated groups or from 100 to 200 ethoxylated groups. According to the invention, the ethoxylated groups are oxyethylene groups (—CH2CH2O). Preferably according to the invention, the monoalcohols (b1) comprise strictly fewer than 200 oxyethylene groups or strictly fewer than 180 oxyethylene groups or fewer than 170 oxyethylene groups. Also preferably according to the invention, the monoalcohols (b2) comprise strictly fewer than 200 oxyethylene groups or strictly fewer than 180 oxyethylene groups.
Essentially according to the invention, the compound T is a compound comprising ethoxylated groups. Preferentially according to the invention, the compound T has a degree of polyethoxylation comprised between 105 and 500 or between 100 and 502 or between 105 and 502 or between 100 and 400 or between 105 and 400. The degree of polyethoxylation defines the number of ethoxylated groups comprised in this compound. Preferably according to the invention, the compound (b) is such that:
In addition to a diurethane compound T, the invention also relates to a method for preparing this compound.
Thus, the invention provides a method for preparing a diurethane compound T by reacting:
Preferably according to the invention for the preparation method according to the invention, the condensation of compounds (a) and (b) is carried out in the presence of a catalyst. More preferably, the reaction is catalysed using an amine, preferably using 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU), or at least one derivative of a metal chosen among Al, Bi, Sn, Hg, Pb, Mn, Zn, Zr, Ti. Traces of water may also participate in the catalysis of the reaction. As examples of metal derivatives, a derivative is preferably chosen among dibutyl bismuth dilaurate, dibutyl bismuth diacetate, dibutyl bismuth oxide, bismuth carboxylate, dibutyltin dilaurate, dibutyltin diacetate, dibutyltin oxide, a mercury derivative, a lead derivative, zinc salts, manganese salts, a compound comprising chelated zirconium, a compound comprising chelated aluminium. The preferred metal derivative is chosen among a Bi derivative, an Sn derivative and a Ti derivative.
Advantageously according to the invention, the condensation of compounds (a) and (b) is carried out in an organic solvent. The preferred organic solvents are solvents that are non-reactant with the isocyanate groups of compound (a), in particular the solvents chosen among the hydrocarbon solvents (particularly C8 to C30 petroleum cuts), the aromatic solvents (particularly toluene and its derivatives) and combinations thereof. More preferably according to the invention, condensation is carried out directly with the different reagents or is carried out in toluene.
At the end of the preparation of the compound T according to the invention, a solution of the compound in an organic solvent is obtained. Such a solution can be used directly. Also according to the invention, the organic solvent can be separated and the compound T dried. Such a compound T according to the invention, which is dried, can then be used in solid form, for example in powder or pellet form.
In addition to the diurethane compound T and a method for preparing this compound, the invention also relates to an aqueous composition comprising at least one diurethane compound T according to the invention. The invention also relates to an aqueous composition comprising at least one diurethane compound T prepared according to the preparation method according to the invention.
Advantageously, the diurethane compound according to the invention is a compound that is hydrophilic in nature. It can be formulated in an aqueous medium.
The aqueous composition according to the invention may also comprise at least one additive, in particular an additive chosen among:
The invention also provides an aqueous formulation that can be used in many technical fields. The aqueous formulation according to the invention comprises at least one composition according to the invention and may comprise at least one organic or mineral pigment or organic, organo-metallic or mineral particles, for example calcium carbonate, talc, kaolin, mica, silicates, silica, metal oxides, in particular titanium dioxide, iron oxides.
The aqueous formulation according to the invention can also comprise at least one agent chosen among a particle-spacer agent, a dispersing agent, a stabilising steric agent, an electrostatic stabilising agent, an opacifying agent, a solvent, a coalescing agent, an anti-foaming agent, a preservative agent, a biocide, a spreading agent, a thickening agent, a film-forming copolymer and mixtures thereof.
Depending on the particular diurethane compound or the additives that it comprises, the formulation according to the invention can be used in many technical fields. Thus, the formulation according to the invention can be a coating formulation. Preferably, the formulation according to the invention is an ink formulation, an adhesive formulation, a varnish formulation, a paint formulation, for example a decorative paint or an industrial paint. Preferably, the formulation according to the invention is a paint formulation. The invention also provides a concentrated aqueous pigment pulp comprising at least one diurethane compound T according to the invention or at least one diurethane compound T prepared according to the preparation method according to the invention and at least one coloured organic or mineral pigment.
The diurethane compound according to the invention has properties that make it possible to use it to modify or control the rheology of the medium comprising it. Thus, the invention also provides a method for controlling the viscosity of an aqueous composition.
This viscosity control method according to the invention comprises the addition of at least one diurethane compound according to the invention to an aqueous composition. This viscosity control method may also include the addition of at least one diurethane compound prepared according to the preparation method according to the invention.
Preferably, the viscosity control method according to the invention is carried out using an aqueous composition according to the invention. Also preferably, the viscosity control method according to the invention is carried out using an aqueous formulation according to the invention.
The particular, advantageous or preferred characteristics of the diurethane compound T according to the invention define aqueous compositions according to the invention, formulations according to the invention, pigment pulp and viscosity control methods which are also particular, advantageous or preferred. The following examples illustrate the various aspects of the invention.
In a 3 L glass reactor equipped with mechanical stirring, a vacuum pump, a nitrogen inlet and heated by means of a double jacket in which oil circulates, 451.2 g of ethoxylated dodecanol are introduced with 140 mol of ethylene oxide (MM=6,355 Da) that is heated to 90° C. in an inert atmosphere. This product is dehydrated.
Under stirring and in an inert atmosphere, 5.97 g of HDI (MM=168.2 g/mol) are then added in one hour in the presence of 200 ppm of dibutyltin dilaurate catalyst. When the addition is complete, the reaction mixture is left to stir for 60 minutes at 90° C.±1° C. Then, the absence of isocyanate is checked by back titration. 1 g is collected from the reaction medium to which an excess of dibutylamine (1 mol, for example) is added, which reacts with any isocyanate groups that may be present in the medium. Any unreacted dibutylamine is then assayed with hydrochloric acid (1 N, for example). The number of isocyanate groups present in the reaction medium can then be deduced. If this number is not zero, the reaction is continued for 15-minute periods until the reaction is completed. When the level reaches zero, the compound T1 obtained is formulated in water to which are added 1,000 ppm of a biocide (Biopol SMV Chemipol) and 1,000 ppm of an anti-foaming agent (Tego 1488 Evonik). A composition 1 is obtained consisting of 20% by mass of compound T1 according to the invention and 80% by mass of water.
In a 3 L glass reactor equipped with mechanical stirring, a vacuum pump, a nitrogen inlet and heated by means of a double jacket in which oil circulates, 448.7 g of ethoxylated dodecanol are introduced with 140 mol of ethylene oxide (MM=6,355 Da) that is heated to 90° C. in an inert atmosphere. This product is dehydrated.
Under stirring and in an inert atmosphere, 7.85 g of IPDI (MM=222.3 g/mol) are then added in one hour in the presence of 200 ppm of bismuth carboxylate catalyst. When the addition is complete, the reaction mixture is left to stir for 60 minutes at 90° C.±1° C. As described in Example 1-1, the absence of isocyanate is checked by back titration. If this number is not zero, the reaction is continued for 15-minute periods until the reaction is completed. When the level reaches zero, the compound T2 obtained is formulated in water to which are added 1,000 ppm of a biocide (Biopol SMV Chemipol) and 1,000 ppm of an anti-foaming agent (Tego 1488 Evonik). A composition 2 is obtained consisting of 20% by mass of compound T2 according to the invention and 80% by mass of water.
In a 3 L glass reactor equipped with mechanical stirring, a vacuum pump, a nitrogen inlet and heated by means of a double jacket in which oil circulates, 449.3 g of ethoxylated dodecanol are introduced with 140 mol of ethylene oxide (MM=6,355 Da) that is heated to 90° C. in an inert atmosphere. This product is dehydrated.
Under stirring and in an inert atmosphere, 9.27 g of H12MDI (MM=262.3 g/mol) are then added in one hour in the presence of 200 ppm of bismuth carboxylate catalyst. When the addition is complete, the reaction mixture is left to stir for 60 minutes at 90° C. +1° C. As described in Example 1-1, the absence of isocyanate is checked by back titration. If this number is not zero, the reaction is continued for 15-minute periods until the reaction is completed. When the level reaches zero, the compound T3 obtained is formulated in water to which are added 1,000 ppm of a biocide (Biopol SMV Chemipol) and 1,000 ppm of an anti-foaming agent (Tego 1488 Evonik). A composition 3 is obtained consisting of 20% by mass of compound T3 according to the invention and 80% by mass of water.
In a 3 L glass reactor equipped with mechanical stirring, a vacuum pump, a nitrogen inlet and heated by means of a double jacket in which oil circulates, 449.3 g of ethoxylated octadecanol are introduced with 132 mol of ethylene oxide (mean MM=6,078 Da) that is heated to 90° C. in an inert atmosphere. This product is dehydrated.
Under stirring and in an inert atmosphere, 6.23 g of HDI (MM=168.2 g/mol) are then added in one hour in the presence of 200 ppm of bismuth carboxylate catalyst. When the addition is complete, the reaction mixture is left to stir for 60 minutes at 90° C.±1° C. As described in Example 1-1, the absence of isocyanate is checked by back titration. If this number is not zero, the reaction is continued for 15-minute periods until the reaction is completed. When the level reaches zero, the compound T4 obtained is formulated using a surfactant compound such as ethoxylated alcohol (ethoxylated hexanol with five ethylene oxide equivalents) in water to which are added 1,000 ppm of a biocide (Biopol SMV Chemipol) and 1,000 ppm of an anti-foaming agent (Tego 1488 Evonik). A composition 4 is obtained consisting of 20% by mass of compound T4 according to the invention, 15% of surfactant and 65% by mass of water.
Paint formulations F1 to F3 according to the invention are prepared respectively from aqueous compositions 1 to 3 of diurethane compounds Ti to T3 according to the invention. All of the ingredients and proportions (% by mass) used are listed in Table 1.
For the paint formulations according to the invention, the Brookfield viscosity, measured at 25° C. and at 10 rpm and 100 rpm (μBk10 and μBk100 in mPa·s) was determined 24 hours after their preparation using a Brookfield DV-1 viscometer with RVT spindles. The properties of the paint formulations are listed in Table 2.
The diurethane compounds according to the invention are highly effective in obtaining excellent low and medium shear gradient viscosities for paint compositions.
For the paint formulations according to the invention, the Cone Plan viscosity or ICI viscosity, measured at high shear gradient (μI in mPa·s), and the Stormer viscosity, measured at medium shear gradient (μS in Krebs Units or KUs), were determined 24 hours after the preparation of the formulations and at room temperature, using the reference module. The properties of the paint formulations are listed in Table 3.
The diurethane compounds according to the invention make it possible to prepare paint formulations with particularly well-controlled viscosities. In particular, the μ
| Number | Date | Country | Kind |
|---|---|---|---|
| FR2007888 | Jul 2020 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2021/000080 | 7/26/2021 | WO |