The invention relates to a jewelry ring and a method for manufacturing the same.
Jewelry rings are crafted predominantly from the precious metals gold, platinum, palladium and alloys thereof, which are marked by their high resistance to corrosion, which also ensures a perfect surface of the metal over a very long period of time.
The disadvantage of such precious metal jewelry rings is, on the one hand, the high material costs and, on the other hand—as a result of the very high specific density of the metals used—their high absolute weight, in particular, in the case of wide, weighty embodiments, which may adversely affect the wearing comfort.
The invention seeks to remedy this. The object of the invention is to provide a jewelry ring and a method for manufacturing same, which overcomes these disadvantages, but at the same time maintains, or even improves, the high corrosion resistance, the optimal surface characteristics and the advantageous overall visual appearance of the jewelry ring.
The invention achieves the stated object with a jewelry ring as disclosed and claimed herein, and with a method for manufacturing the same as disclosed and claimed herein.
The advantages achieved by the invention are to be found essentially in that, thanks to the device according to the invention:
The density ρ1 of the precious metal substrate corresponds to the densities for the pure precious metals AU (19.3 g/cm3), platinum (21.4 g/cm3) or palladium (12.0 g/cm3), or of the standard alloys of these precious metals. The density ρ2 of the plastic adhesives lies typically in the range of 1.2 to 1.6 g/cm3, and the density ρ3 of the fibers lies typically in the range of 1.3 to 1.8 g/cm3, i.e., significantly lower than the density ρ1 of the precious metal substrate.
Additional advantageous embodiments of the invention may be commented on as follows:
The bundle of fibers is advantageously a so-called roving, the fibers of which have been twisted. In one embodiment, the bundle of fibers has one twist per 1-10 cm, preferably per 2-4 cm length of the bundle. The outer surface of the jewelry ring may have one or more indentations, in which the bundle is set. The depth of these indentations may lie in the range of 0.4 to 1.0 mm.
The sleeve-like or annular substrate may also have at least two sections having variously sized outer diameters, wherein the sections having the smaller outer diameters may be placed by means of the bundle essentially on the outer diameter of the section having the largest outer diameter.
The transparent plastic adhesive advantageously comprises an epoxy resin and the fibers are made of carbon.
In one particular embodiment, the number of windings is greater than 100, preferably greater than 150.
The carbon fibers preferably have a diameter in the range of 4.5-8 μm, preferably of 5.5-7 μm.
The length of the bundle may be at least 3 m, preferably at least 4 m. The length of the bundle may be at most 6 m, preferably at most 7 m.
In one particular embodiment, the bundle of carbon fibers has at least 500 individual fibers, preferably at least 800 individual fibers. The bundle of carbon fibers may have at most 1,200, preferably at most 1,500 individual fibers.
In one particular embodiment, the fibers are individually or doubly consolidated.
The indentations in the jewelry ring may have both a linear as well as a wavy design.
In one particular embodiment, insular regions that have the outer diameter of the section with the largest outer diameter may be left in the sections having a smaller outer diameter.
A method for manufacturing a jewelry ring according to the invention is characterized by the following method steps:
a) Wetting the bundle of fibers with the transparent plastic adhesive;
b) Fastening the start of the bundled treated with the plastic adhesive to the sleeve-like annular substrate;
c) Winding the bundle on the outer surface of the jewelry ring;
d) Pressing on the bundle wound on the jewelry ring;
e) Curing the plastic adhesive; and
f) Grinding off the peripheral-most fibers.
The plastic adhesive preferably comprises an epoxy resin mixed with a hardener, which contains, in particular, a Bisphenol A and/or Bishpenol F-based epoxy. The viscosity of the epoxy resin lies advantageously in the range of 350-450 mPa s at 25° C.
The hardener for the epoxy resin is preferably a cycloaliphatic amine. The viscosity of the hardener lies expediently in the range of 180-230 mPa s at 25° C.
The curing of the epoxy resin may typically take place at a temperature of 55-65° C. for a period of 2.5 to 3.5 hours.
The start of the bundle may be expediently fastened by a connection formed as a knot. The winding of the bundle advantageously takes place in a groove or indentation formed in the outer surface of the jewelry ring. The bundle is advantageously twisted about its longitudinal axis prior to being wound.
In one particular embodiment, the groove is roughened prior to fastening of the bundle, preferably by means of a grinding tool, as a result of which an improved bonding with the epoxy resin is obtained.
The winding in step c) of the method may take place by rotating the jewelry ring.
The pressing on in step d) of the method may advantageously take place by means of a heat shrinkable tubing which is caused to shrink when heated. The heat shrinkable tubing, once it is pressed on, may again be removed. The peripheral-most fibers may be expediently ground off on a lathe.
In one particular embodiment, the winding takes place in such a way that the bundle projects peripherally over the groove. This ensures that the groove is completely filled.
The winding in step c) of the method preferably takes place by hand. In this way, the carbon fibers may be fitted specifically to the shape of the ring and or wrapped around “islands”. The bundle may also be wound on the outer surface at an angle alpha>0° relative to the rotational direction of the ring. The bundle may also be wound on the outer surface in slalom-like fashion relative to the rotational direction of the ring.
In one particular embodiment, a circular ring-like disk, which has an outer diameter larger than the jewelry ring, may be temporarily fastened to one or both lateral surfaces. This measure prevents the bundle from being wound beyond the lateral surfaces of the ring.
The weight ratio between the precious metal forming the substrate and the carbon fibers may advantageously range in the area of 13:1 to 5:1.
The invention and refinements of the invention are explained in still greater detail below based on the partially schematic representations of multiple exemplary embodiments, in which:
The jewelry ring 1 depicted in
The fibers 9 are adhered to one another and to the groove 10 by means of a transparent epoxy resin adhesive. The peripheral-most fibers 9 are grounded off. The surface of the bundle 8 has a characteristic silk-like sheen.
Although, there are different embodiments of the invention, as described above, these are to be understood in the sense that the different features may be used both alone as well as in any arbitrary combination.
Thus, the invention is not limited simply to the aforementioned, particularly preferred embodiments.
| Number | Date | Country | Kind |
|---|---|---|---|
| 02908/12 | Dec 2012 | CH | national |
| 102013008188.2 | May 2013 | DE | national |
This application is a division of U.S. application Ser. No. 14/650,497, filed Jun. 8, 2015, which application is a U.S. national stage of PCT/CH2013/000206, filed Dec. 2, 2013, and claims priority to DE 10 2013 008 188.2, filed May 14, 2013 and CH 02908/12, filed Dec. 20, 2012.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14650497 | Jun 2015 | US |
| Child | 16038986 | US |