Patent Grant
7669331
The following disclosure is based on German Patent Application No. 10 2004 019 306.1 filed on Apr. 15, 2004, which is herewith incorporated into this application by explicit reference.
The invention relates to a roll or calender roll, as well as to a method for the manufacture of a roll.
In construction and process engineering use is frequently made of treatment devices such as punches or punch surfaces, presses or rotary rolls, which have a multilayer structure. Such a multilayer structure can be desired in order to achieve particular strength characteristics or behaviour. Cases can also arise in which already existing treatment devices have to be modified or reconstructed, for example provided with new surfaces. Difficulties more particularly arise if on an already existing covering or substructure a further layer structure has to be applied, whose mechanical characteristics do not necessarily bring about harmony or which cause difficulties.
One example is constituted by calender rolls, which have a covering as the top layer and which is made from a paper or textile material. There are in particular calender rolls, whose covering comprises a plurality of textile material or cotton fabric sheets, which are engaged on a metal core and strongly compressed in the axial direction. These rolls form a covering or surface having a certain elasticity and which is relatively favourable and in the case of wear can be dressed to a certain extent in order to once again obtain a uniform, smooth surface. In order to be able to use existing rolls for the formation of a new covering or layer system, attempts have been made to slide a precisely matching metal cylinder onto the textile layer and then apply thereto a layer of plastic or rubber for example. However, the problem arises that the diameter of the metal tube must precisely match the roll diameter, because otherwise mechanical problems arise.
The problem of the invention is to provide a roll and a method for the manufacture of the roll making it possible to avoid the problems of the prior art and which in particular enable in an inexpensive and technically advantageous manner to apply a further layer structure to existing treatment devices.
This problem is solved by a roll having a hard substructure and a covering several centimeters thick of a material in the form of paper or textile material on the substructure. The covering includes a plurality of individual, thin layers, which are compressed or pressed together along an axial direction of the roll such that outer edges of the sheets form a surface of the roll, the surface of the roll being structured with grooves or depressions, liquid plastic applied as an adhesive to said structuring, and a stabilizing fibrous material layer applied to the liquid plastic, wherein the fibrous material layer is impregnated with liquid plastic and the covering is built up from sheets, the sheets being engaged on the substructure in a direction perpendicular to the axial direction of the roll and stacked one on another along the axial direction has been inserted. The problem is also solved by a method for the manufacture of such a roll. Advantageous and preferred developments of the invention form the subject matter of the claims and are explained in greater detail hereinafter. By express reference the wording of the claims is made into part of the content of the present description. Features concerning the technical design, as well as the treatment device, together with the method in part apply to both and are only explained once hereinafter. These explanations relate both to the treatment device and to the method.
According to the invention a treatment device has a hard substructure to which is applied a covering of paper or textile material having a certain thickness, more particularly several centimeters. The covering comprises a plurality of individual, thin paper or textile material layers. The latter are compressed or pressed together to give a certain dimensional stability. This paper or textile material covering undergoes surface structuring. To it is applied plastic, particularly a liquid plastic, which has the effect of an adhesive and also provides a mechanical connection, particularly for load transfer purposes. In turn to it is applied a fibrous material stabilizing layer. The latter is also impregnated with plastic, which cures and together with the fibrous material forms a stable, fibre-reinforced layer.
Thus, through the plastic and fibrous material is formed an intermediate layer, which in turn has an adequate strength. As a result of the structuring of the surface of the covering below the same it is once again ensured that the plastic deeply penetrates the paper or textile material and at least impregnates a portion thereof. This brings about a particularly good adhesion in addition to the actual structuring and also leads to a good mechanical connection, particularly for load transfer. Particularly in the case of paper or textile material as a result of structuring the surface can be opened, so that liquid plastic or adhesive can penetrate. As a result of the following stabilizing layer with fibrous material firstly a relatively smooth surface of the treatment device is again provided, so that the structuring is compensated and secondly a stable layer results from the composite of fibrous material and plastic or adhesive.
With particular preference the treatment device is a roll, particularly a calender roll, or this is used so that a new treatment device can be produced with the described method. After finishing as a calender roll, such a roll can form a rolling mill with a metal counterroll, for example for smoothing paper surfaces. Onto the previously described stabilizing layer a cover layer can be applied for this purpose and is advantageously made from plastic or rubber. It can have a thickness of a few millimeters to a few centimeters and can be adapted as regards its hardness and other properties to the intended use.
An advantageous textile material is cotton. More particularly the textile material comprises a cotton fabric, such as is used for jeans and the like. This permits a relatively favourable availability. Further possibilities are the provision of pieces of wool or synthetic fibres in the textile material, for example under the trade name Nomex.
A substructure of the treatment device or roll is preferably metallic in order to ensure an adequate strength. In particularly preferred manner it is a solid or hollow metal core, which in the case of a roll also forms the rotation axis.
Paper or textile material sheets can be applied to a substructure or in the case of a roll can be engaged on a roll core and in this way form the covering, being compressed or pressed together for this purpose. In the case of a roll this is advantageously brought about by tightening means at the ends, which can be nuts to be screwed on, for example.
The structuring of the surface of the covering can have grooves, for example, which can have a variable depth as a function of the covering thickness and other requirements. The depth can be between 3 and 20 mm, for example somewhat under 10 mm. It is considered advantageous to provide a uniform, unitary structuring, i.e. only having grooves. The latter can all be equidistant and are advantageously closely juxtaposed. As a result of a directly interconnecting application of the grooves, there is a very large number of these per surface unit and consequently there is a considerable adhesion-improving effect. This also improves the mechanical connection with respect to the load transfer. Thus, mechanical loads can be better transferred from the outer layer to the roll core.
In the case of a roll, preferably a surface structuring is such that it only runs in the rotation direction with no or only a limited longitudinal component, mainly in the axial direction of the roll. Otherwise in the case of rotating rolls, from a pressure along the nip line of a calender rolling mill a force and motion action of the top covering with deflection in the longitudinal direction of the axis could be brought about and this is obviously to be avoided. Thus, grooves run substantially or advantageously exclusively in the rotation direction in the form of closed, circular grooves. It is also possible to provide a groove in the form of a screw thread. As a result the indicated characteristics are still achieved, but not in quite such a satisfactory manner.
Another possibility for a surface structuring, which in certain circumstances can be provided in addition to the aforementioned elongated grooves is constituted by advantageously conical holes or depressions, which should be uniformly distributed. It is also advantageous and favourable from the manufacturing standpoint for them to have roughly the same size. They can be applied to rotating rolls by drills or arbors and in certain circumstances by laser beams.
The plastic or adhesive can be a resin, such as a synthetic resin, for example, or epoxy resin. A plastic can advantageously be a thermosetting plastic.
The fibrous material is advantageously constituted by very stable reinforcing fibres. They are with particular advantage applied in the form of rovings, that is a continuous fibre bundle. A fibrous material is preferably selected from the following group: glass, carbon, aramid or boron fibres.
The application of the fibrous material to a roll as the treatment device can take place by rotating the roll and winding on the fibrous material. On winding on the fibrous material it must be ensured that it is compressed and the fibres are applied uniformly and in closely juxtaposed manner. In a first pass it is possible to fill the grooves or depressions for obtaining a planar surface and then a further fibrous material layer can be applied. Alternatively and in a single pass the fibrous material can be applied in the desired thickness. It is considered advantageous if the fibrous material is applied already impregnated with liquid plastic or adhesive. Following the hardening of the plastic or adhesive a further covering can either be directly applied or firstly the surface is smoothed, for example abraded. The top covering can be constituted by a polymer material, for example rubber or plastic.
Embodiments of the invention are described in greater detail hereinafter relative to the attached drawings, wherein show:
For the treatment according to the invention, using a cutting tool 21 and in accordance with a conventional turning process, the surface 19 or sheets 13 are treated, so as to cut in grooves 23. The grooves 23 are precisely parallel, directly follow on to one another and always equidistantly spaced run precisely in the circumferential direction on roll 11.
It is clear from the larger scale reproduction of groove structures in
On carefully working the surface 19 of roll 11 using cutting tool 21, the outer edges of the individual sheets 13 do not become ragged and are instead cut relatively smooth. This means that they can be worked in the same way as a solid material. However, as a result of the working, the surface or overall surface formed of the directly following on outer edges of the sheets 13 acquire a structure which is opened from the outside or which is accessible for liquid, as will be explained hereinafter.
To the far right in
In the first step according to
In the third step in
In the fifth step the entire roll 11 is covered with a layer of fibrous material 35 impregnated with synthetic resin 30. This application of the layer or the production of the layer is to take place in such a way that the surface is already to some extent uniform and flat, either as a result of winding or subsequent working.
According to the next or sixth step, onto the completely cured fibre-reinforced synthetic resin material layer is applied a further polymer material covering 37, for example of rubber or plastic, as a function of the intended use. This, however, corresponds to the known method. With regards to this functional polymer material layer 37, as a result of the stable, intermediate, fibrous material layer 35, the roll behaves in a neutral manner and its characteristics are no longer influenced or characterized by the underlying structure of paper sheets 13. As a result of the improved mechanical connection it is better possible to transfer loads from the surface to the underlying roll 11.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2004 019 306 | Apr 2004 | DE | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 1884104 | Moore et al. | Oct 1932 | A |
| 3646651 | McGaughey et al. | Mar 1972 | A |
| 4368568 | Watanabe | Jan 1983 | A |
| 4475275 | Edwards | Oct 1984 | A |
| 4503769 | Andersen | Mar 1985 | A |
| 4604778 | Edwards | Aug 1986 | A |
| 4866826 | Koide | Sep 1989 | A |
| 5091027 | Watanabe | Feb 1992 | A |
| 5097596 | Hoogesteger et al. | Mar 1992 | A |
| 5307563 | Svenka | May 1994 | A |
| 5601920 | Paasonen et al. | Feb 1997 | A |
| 5766120 | Schmitz | Jun 1998 | A |
| 5780131 | Paasonen et al. | Jul 1998 | A |
| 5952017 | Nishida et al. | Sep 1999 | A |
| 5958533 | Paasonen et al. | Sep 1999 | A |
| 6375602 | Jones | Apr 2002 | B1 |
| 6409645 | Paasonen et al. | Jun 2002 | B1 |
| 6432031 | Paasonen et al. | Aug 2002 | B1 |
| 6514369 | Shieh | Feb 2003 | B1 |
| 6776744 | Shieh | Aug 2004 | B1 |
| 6793754 | Shieh | Sep 2004 | B1 |
| 6896647 | Karger et al. | May 2005 | B1 |
| 7051554 | Hart | May 2006 | B2 |
| 20020189749 | Shieh | Dec 2002 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20050233880 A1 | Oct 2005 | US |