Patent Application
20210002758
The present invention relates to a roll-to-roll deposition apparatus and a roll-to-roll deposition method as a high-speed film deposition technology for a low-melting-point metal.
While paying out a film wound around a payout roller, an apparatus deposits metal on the film and then takes up the film through a take-up roller as a type of roll-to-roll deposition apparatus.
In the roll-to-roll deposition apparatus of this type, a metal deposition source is disposed on the way between the payout roller and the take-up roller, facing the film (e.g., see Patent Literature 1). When metal evaporating from the metal deposition source adheres to the film, the phase of the metal changes from gas to solid on the film, and the solid-state metal layer is formed on the film.
Patent Literature 1: WO2008/018297
However, if a metal layer is directly vapor-deposited on a travelling film, the film is susceptible to heat damage due to the latent heat. This latent heat becomes larger as the thickness of the metal layer vapor-deposited on the film becomes larger. Thus, the film becomes more susceptible to heat damage as the thickness of the film becomes larger.
In view of the above-mentioned circumstances, it is an object of the present invention to provide a roll-to-roll deposition apparatus and a roll-to-roll deposition method, by which a metal layer can be deposited as a film while reducing heat damage to the film.
In order to accomplish the above-mentioned object, a roll-to-roll deposition apparatus according to an embodiment of the present invention includes a vacuum chamber, a film travel mechanism, a lithium source, and a first roller.
The vacuum chamber is capable of maintaining a reduced-pressure state.
The film travel mechanism is capable of causing a film to travel inside the vacuum chamber.
The lithium source is capable of evaporating lithium inside the vacuum chamber. The first roller is disposed between a deposition surface of the film and the lithium source. The first roller has a transfer pattern that receives the lithium evaporated from the lithium source. The first roller transfers a pattern of a lithium layer corresponding to the transfer pattern to the deposition surface while rotating.
With such a roll-to-roll deposition apparatus, the molten lithium is received by the first roller having the transfer pattern, and the pattern of the lithium layer is indirectly transferred from the first roller to the deposition surface of the film. That is, the lithium layer is patterned onto the deposition surface of the film by vacuum deposition and application via the first roller. With this, heat damage to the film is reduced.
The roll-to-roll deposition apparatus may further include a second roller that faces the first roller with the film provided between the second roller and the first roller.
With such a roll-to-roll deposition apparatus, the first roller is held in contact with the second roller with the film provided between the first roller and the second roller. With this, the pattern of the lithium layer is more clearly transferred from the first roller to the deposition surface of the film.
In the roll-to-roll deposition apparatus, the lithium source may include a vapor deposition container and a doctor blade. The vapor deposition container stores the lithium and is disposed such that the lithium is vapor-deposited on the first roller. The doctor blade controls a thickness of the lithium supplied from the vapor deposition container to the first roller.
With such a roll-to-roll deposition apparatus, the thickness of the lithium supplied to the first roller from the vapor deposition container is reliably controlled by the doctor blade.
In the roll-to-roll deposition apparatus, the lithium source may include a third roller, a vapor deposition container, and a doctor blade. The third roller faces the first roller. The vapor deposition container stores the lithium and is disposed such that the lithium is vapor-deposited on the third roller. The molten surface of the lithium is held in contact with the third roller. The doctor blade controls a thickness of the lithium supplied from the vapor deposition container to the third roller.
With such a roll-to-roll deposition apparatus, the thickness of the lithium supplied to the first roller from the vapor deposition container is more reliably controlled by the doctor blade and the third roller.
In the roll-to-roll deposition apparatus, the lithium source may include a third roller, a fourth roller, and a vapor deposition container. The third roller faces the first roller. The fourth roller faces the third roller. The vapor deposition container stores the lithium and is disposed such that the lithium is deposited on the fourth roller.
With such a roll-to-roll deposition apparatus, the thickness of the lithium supplied to the first roller from the vapor deposition container is more reliably controlled by the third roller and the fourth roller. Further, due to the presence of the fourth roller, heat damage to the film is further reduced.
The roll-to-roll deposition apparatus may further include a pretreatment mechanism that cleans the deposition surface of the film, the pretreatment mechanism being placed upstream from the first roller.
With such a roll-to-roll deposition apparatus, the deposition surface of the film is cleaned before the pattern of the lithium layer is transferred from the first roller to the deposition surface of the film. With this, the adhesion force between the lithium layer and the film increases.
The roll-to-roll deposition apparatus may further include a protection layer-forming mechanism that forms a protection layer on a surface of the lithium layer, the protection layer-forming mechanism being placed downstream from the first roller.
With such a roll-to-roll deposition apparatus, the lithium layer is protected by the protection layer after the pattern of the lithium layer is transferred from the first roller to the deposition surface of the film.
The roll-to-roll deposition apparatus may further include a separator by which the protection layer-forming mechanism is isolated inside the vacuum chamber.
With such a roll-to-roll deposition apparatus, the protection layer-forming mechanism is isolated by the separator, and ingredients of the protection layer are barely mixed into the lithium layer.
Further, in order to accomplish the above-mentioned object, a roll-to-roll deposition method according to an embodiment of the present invention including causing a film to travel inside a vacuum chamber capable of maintaining a reduced-pressure state. Evaporated lithium is supplied to a first roller on which a transfer pattern is formed. A pattern of a lithium layer corresponding to the transfer pattern is held in contact with a deposition surface of the film to transfer the pattern of the lithium layer to the deposition surface while rotating the first roller.
With such a roll-to-roll deposition method, the vapor-deposited lithium is supplied to the first roller having the transfer pattern and the pattern of the lithium layer is indirectly transferred to the deposition surface of the film from the first roller. That is, the lithium layer is patterned on the deposition surface of the film by vacuum deposition and application. With this, heat damage to the film is reduced.
As described above, in accordance with the present invention, a metal layer can be deposited as a film while reducing heat damage to the film.
Hereinafter, embodiments of the present invention will be described with reference to the drawings. Some of the figures have X-, Y-, and Z-axis coordinates.
A roll-to-roll deposition apparatus 1 shown in
The first roller 11A is a tubular member containing metal such as stainless steel, iron, and aluminum. The first roller 11A is disposed between the film 60 and the lithium source 20. The first roller 11A faces a deposition surface 60d of the film 60. For example, a roller surface 11r of the first roller 11A is held in contact with the deposition surface 60d of the film 60. Further, a transfer pattern is formed on the roller surface 11r. The transfer pattern is, for example, a convex pattern such as a bank-shaped pattern and a hill-shaped pattern. Therefore, the first roller 11A can also be called plate cylinder in relief printing.
The first roller 11A is rotatable about its center axis. For example, a rotary drive mechanism that rotationally drives the first roller 11A may be provided outside the roll-to-roll deposition apparatus 1. Alternatively, the first roller 11A itself may include the rotary drive mechanism.
For example, with the film 60 traveling in an arrow-A direction, the first roller 11A made to face the film 60 is rotated in the clockwise direction. At this time, the movement velocity (tangential velocity) of the roller surface 11r is set to be equal to the travel velocity of the film 60, for example. With this, after a lithium pattern is formed on the roller surface 11r, this lithium pattern is transferred to the deposition surface 60d of the film 60 without position shift. Alternatively, the velocity at which this roller surface 11r moves may be set to be different from the travel velocity of the film 60 (lower or higher velocity). The film thickness or the like of the lithium 25 may be changed by utilizing this velocity difference.
Further, in this embodiment, a temperature control mechanism such as a temperature control medium circulation system is provided inside the first roller 11A. With this temperature control mechanism, control is performed as appropriate such that, for example, the temperature of the roller surface 11r can be equal to or higher than the melting point of lithium.
The second roller (back-up roller) 12 is a tubular member containing metal such as stainless steel, iron, and aluminum. The second roller 12 faces the first roller 11A with the film 60 provided between the second roller and the first roller 11A. A roller surface 12r of the second roller 12 is held in contact with a back surface of the film 60 (surface opposite to the deposition surface 60d). The transfer pattern is not formed on the roller surface 12r.
The second roller 12 is rotatable about its center axis. For example, the second roller 12 held in contact with the film 60 is rotated in the counter-clockwise direction due to the travel of the film 60. Alternatively, a rotary drive mechanism that rotationally drives the second roller 12 may be provided outside the roll-to-roll deposition apparatus 1. Alternatively, the second roller 12 itself may include the rotary drive mechanism. In this case, the second roller 12 is rotated by the rotary drive mechanism in the counter-clockwise direction.
Further, in this embodiment, a temperature control mechanism such as a temperature control medium circulation system may be provided inside the second roller 12. With this temperature control mechanism, control is performed as appropriate such that, for example, the temperature of the roller surface 12r can be smaller than the melting point of lithium.
The lithium source 20 includes a vapor deposition container 21, a doctor blade 22, and a third roller 23. The lithium source 20 is disposed facing the first roller 11A.
The vapor deposition container 21 stores molten lithium (Li) 25 in the form of a bulk, wire, or powder, for example. For example, during operation of the roll-to-roll deposition apparatus 1, the lithium 25 is heated and evaporated in the vapor deposition container 21 by using a technique such as resistance heating, induction heating, and electron beam heating. The film thickness of the lithium 25 may be adjusted by controlling the amount of evaporation by using those techniques.
The heating temperature of the lithium 25 is not particularly limited. Typically, the heating temperature of the lithium 25 is set to a temperature (e.g., 180° C. to 800° C.) equal to or higher than the melting point of the lithium. In a case where a natural film (Li2O or the like) is formed on the surface of the lithium, a target heating temperature is set such that only the lithium 25 can be evaporated (or distilled).
The third roller 23 is a tubular member, and is a so-called anilox roller. The first roller 11A is located between the third roller 23 and the second roller 12. For example, the third roller 23, the first roller 11A, and the second roller 12 are arranged in the stated order from the top to the bottom of the roll-to-roll deposition apparatus 1. The third roller 23 faces the first roller 11A. A roller surface 23r of the third roller 23 is formed of a layer (e.g., chromium (Cr) layer or ceramic layer) having a plurality of holes, for example.
The roller surface 23r of the third roller 23 is held in contact with the roller surface 11r of the first roller 11A. In addition, in the example of
The third roller 23 is rotatable about its center axis. For example, the third roller 23 held in contact with the first roller 11A is rotated in the counter-clockwise direction by rotation of the first roller 11A. Alternatively, a rotary drive mechanism that rotationally drives the third roller 23 may be provided outside the roll-to-roll deposition apparatus 1. Alternatively, the third roller 23 itself may include the rotary drive mechanism. In this case, the third roller 23 is rotated by the rotary drive mechanism in the counter-clockwise direction.
Further, in this embodiment, a distance control mechanism that changes a relative distance between the third roller 23 and the vapor deposition container 21 may be provided outside the roll-to-roll deposition apparatus 1. With this distance control mechanism, the amount of lithium 25 that adheres to the roller surface 23r can be changed.
When the third roller 23 rotates with the lithium 25 vapor-deposited on the third roller 23, the lithium 25 in the vapor deposition container 21 is upwardly moved via the roller surface 23r. With this, the vapor-deposited lithium 25 is supplied from the vapor deposition container 21 to the entire area of the roller surface 23r of the third roller 23. Further, in the roll-to-roll deposition apparatus 1, the doctor blade 22 is provided near the roller surface 23r of the third roller 23.
Due to the provision of the doctor blade 22, the thickness of the lithium 25 on the roller surface 23r is accurately adjusted. For example, the thickness of the lithium 25 on the roller surface 23r is adjusted to be substantially the same. With this, the supply amount of lithium 25 is constant on the first roller 11A supplied with the lithium 25 from the third roller 23.
Then, the lithium 25 on the roller surface 23r extends over the roller surface 11r of the first roller 11A held in contact with the lithium 25 on the roller surface 23r. In this manner, a constant amount of lithium 25 is supplied from the vapor deposition container 21 to the roller surface 11r of the first roller 11A via the third roller 23.
In this case, the supply amount of lithium 25 supplied to the roller surface 23r by the doctor blade 22 is constant. Therefore, the supply amount of lithium 25 supplied to the roller surface 11r of the first roller 11A is also constant. With this, the thickness of the lithium 25 on the roller surface 11r is the same in the entire circumference.
Further, in this embodiment, a temperature control mechanism such as a temperature control medium circulation system is provided inside the third roller 23. With this temperature control mechanism, control is performed as appropriate such that, for example, the temperature of the roller surface 23r can be equal to or higher than the melting point of lithium.
With this, adhesion of the evaporated lithium 25 to the roller surface 23r from the vapor deposition container 21 and supply of the molten lithium 25 to the first roller 11A in the third roller 23 are realized.
The film travel mechanism 30 includes a payout roller 31, a take-up roller 32, and guide rollers 33a, 33b, 33c, 33d, 33e, 33f, and 33g. A rotary drive mechanism that rotationally drives the payout roller 31 and the take-up roller 32 is provided outside the roll-to-roll deposition apparatus 1. Alternatively, each of the payout roller 31 and the take-up roller 32 may include the rotary drive mechanism.
Further, in this embodiment, temperature control mechanisms such as temperature control medium circulation systems may be provided inside the guide rollers 33a, 33b, 33c, 33d, 33e, 33f, 33g.
The film 60 is placed in the roll-to-roll deposition apparatus 1, nipped between the first roller 11A and the second roller 12. The deposition surface 60d of the film 60 faces the first roller 11A. The film 60 is wound around the payout roller 31 in advance and paid out from the payout roller 31.
The film 60 paid out from the payout roller 31 is traveling while being supported by the guide rollers 33a, 33b, and 33c, and is moved between the first roller 11A and the second roller 12 while changing the travel direction at each of the guide rollers 33a, 33b, and 33c.
In addition, the film 60 is traveling while being supported by the guide rollers 33d, 33e, 33f, and 33g, and continuously taken up by the take-up roller 32 while changing the travel direction at each of the guide rollers 33d, 33e, 33f, and 33g.
The film 60 is a long film cut at a predetermined width. The film 60 includes at least any of copper, aluminum, nickel, stainless steel, and resin. Regarding the resin, an OPP (oriented polypropylene) film, a PET (polyethylene terephthalate) film, or a PPS (polyphenylene sulfide) film is used, for example.
The pretreatment mechanism 40 is placed upstream from the first roller 11A. The pretreatment mechanism 40 cleans the deposition surface 60d of the film 60. For example, the pretreatment mechanism 40 is capable of generating plasma of inert gas (Ar, He, etc.), nitrogen (N2), oxygen (O2), and the like. When the deposition surface 60d of the film 60 is exposed to this plasma, an oil film, a natural oxidation film, and the like adhering to the deposition surface 60d are removed. With this, the adhesion force of the lithium layer formed on the deposition surface 60d increases.
The first roller 11A, the second roller 12, the lithium source 20, the film travel mechanism 30, the pretreatment mechanism 40, and the film 60 described above are stored in the vacuum chamber 70. The vacuum chamber 70 is capable of maintaining a reduced-pressure state. For example, the interior of the vacuum chamber 70 is maintained at a predetermined degree of vacuum at which vapor deposition of lithium is possible by the gas discharge mechanism 71 connected to a vacuum pumping system (not shown) such as a vacuum pump. With this, an environment where the dew point of lithium is lower than −30° C. (more favorably, lower than −50° C.) is easily formed, and the melting state of lithium can be stably kept inside the vacuum chamber 70. Reaction of lithium having a much higher reactivity is suppressed.
In evacuation of the vacuum chamber 70, the gas supply mechanism 72 may evacuate the vacuum chamber 70 after supplying at least any of gases such as dry air, inert gas (Ar, He, etc.), carbon dioxide (CO2), nitrogen, and the like as replacement gas. By introducing these gases into the vacuum chamber 70, reaction of lithium having a high reactivity is suppressed.
Further, in this embodiment, at least any of indium (In), zinc (Zn), tin (Sn), gallium (Ga), bismuth (Bi), natrium (Na), kalium (K), and alloy having a melting point of 400° C. or less may be stored in the vapor deposition container 21 in addition to lithium.
The vapor deposition container 21 is made of an austenitic stainless steel, for example.
[Operation of Roll-to-Roll Deposition Apparatus]
In the roll-to-roll deposition method according to the first embodiment, the film travel mechanism 30 causes the film 60 to travel inside the vacuum chamber 70 capable of maintaining a reduced-pressure state, for example (Step S10).
Next, the evaporated lithium 25 adheres to the third roller 23 from the lithium source 20 (vapor deposition container 21) (Step S20). The temperature control mechanism of the third roller 23 maintains the lithium 25 adhering to the third roller 23 in the melting state.
Next, the lithium 25 in the melting state on the third roller 23 is supplied to the first roller 11A on which the transfer pattern is formed (Step S30).
After that, the pattern of the lithium layer corresponding to the transfer pattern is transferred to the deposition surface by holding the pattern of the lithium layer corresponding to the transfer pattern in contact with the deposition surface 60d of the film 60 while rotating the first roller 11A (Step S40).
With such a roll-to-roll deposition method, the evaporated lithium 25 is supplied to the first roller 11A having the transfer pattern via the third roller 23, and the pattern of the lithium layer is transferred from the first roller 11A to the deposition surface 60d of the film 60.
That is, the lithium 25 (molten metal) is not directly vapor-deposited on the first roller 11A from the vapor deposition container 21 (tub). The lithium 25 (molten metal) is vapor-deposited on the third roller 23 once. Then, the lithium 25 (molten metal) is applied to the deposition surface 60d while maintaining the melting state through the temperature control mechanism of the third roller 23.
The lithium layer is patterned onto the deposition surface 60d of the film 60 by vacuum deposition and application. With this, heat damage to the film 60 is reduced.
A specific operation of the roll-to-roll deposition apparatus 1 will be described.
As shown in
Next, the liquid lithium 25 vapor-deposited on the third roller 23 from the vapor deposition container 21 is supplied onto the transfer pattern 11p of the first roller 11A.
For example, the vapor deposition container 21 is disposed below the third roller 23 such that the lithium 25 evaporated from the vapor deposition container 21 adheres to a part of the roller surface 23r of the third roller 23. In addition, the temperature of the roller surface 23r of the third roller 23 is adjusted to a lithium melting point (180° C.) or more by the temperature control mechanism. With this, the lithium 25 vapor-deposited on the third roller 23 is supplied to the first roller 11A with the lithium 25 molten on the roller surface 23r (by the third roller 23 rotating in the counter-clockwise direction). Further, the thickness of the lithium 25 on the roller surface 23r is accurately evenly adjusted by the doctor blade 22.
Next, the first roller 11A is rotated in the clockwise direction with the rotation of the third roller 23. In addition, the first roller 11A is held in contact with the third roller 23. With this, the transfer pattern 11p of the first roller 11A gets wet with the molten lithium 25, and the roller surface 11r receives the molten lithium 25 from the roller surface 23r. That is, the molten lithium 25 is formed on the transfer pattern 11p, and a pattern 25p of the lithium 25 corresponding to the transfer pattern 11p is formed on the roller surface 11r.
Here, the temperature of the roller surface 11r of the first roller 11A is controlled by the temperature control mechanism to be equal to or higher than the melting point (180° C.) of lithium. With this, also when the first roller 11A is rotated and the roller surface 11r is thus separated from the third roller 23, the lithium 25 is kept wet in the melting state on the transfer pattern 11p.
The film 60 is traveling between the first roller 11A and the second roller 12 with the rotation of the first roller 11A and the second roller 12. Here, the first roller 11A is held in contact with the deposition surface 60d of the film 60. With this, the pattern 25p is also held in contact with the deposition surface 60d of the film 60, and the pattern 25p is transferred from the transfer pattern 11p to the deposition surface 60d of the film 60.
After that, regarding the pattern 25p of the lithium 25 on the deposition surface 60d, the pattern 25p of the lithium layer is formed on the deposition surface 60d of the film 60 by the temperature control mechanisms of the guide rollers 33a, 33b, 33c, 33d, 33e, 33f, 33g, natural cooling, and the like. The thickness of the lithium layer formed on the deposition surface 60d is, for example, 0.5 μm or more and 50 μm or less. Note that the pattern 25p of the lithium layer may be formed on both sides of the film 60.
In this manner, in this embodiment, the lithium 25 evaporated from the vapor deposition container 21 adheres to the roller surface 23r of the third roller 23 including the temperature control mechanism for keeping the melting state. After that, the molten lithium 25 is received by the first roller 11A having the transfer pattern 11p.
After that, the pattern 25p of the lithium layer is transferred from the first roller 11A to the deposition surface 60d of the film 60.
As described above, in this embodiment, the lithium 25 indirectly transfers to the deposition surface 60d from the vapor deposition container 21 via the first roller 11A and the third roller 23.
In this embodiment, the lithium 25 (pattern 25p) is not directly supplied to the deposition surface 60d of the film 60 while changing from the gas phase state to the solid phase state. The lithium 25 (pattern 25p) is indirectly supplied to the deposition surface 60d of the film 60 through the liquid phase state (while changing the gas phase state the liquid phase state the solid phase state). With this, the latent heat applied to the film 60 from lithium is reduced and heat damage to the film 60 is greatly reduced. For example, even if relatively thick pattern of the lithium layer, which has a thickness of 0.5 μm or more and 50 μm or less, is formed on the deposition surface 60d of the film 60, heat damage to the film 60 is smaller.
Further, in this embodiment, the first roller 11A is provided with the transfer pattern 11p, and the lithium pattern 25p is formed on the film 60 from the first roller 11A directly. With this, it is unnecessary to use a dedicated mask for forming the lithium pattern on the film 60. With this, regular maintenance work of exchanging a mask to which lithium has adhered. In addition, it is unnecessary to use a complicated mechanism for taking up and paying out the mask together with the film 60 and a complicated mechanism for positioning the mask.
Further, in this embodiment, the lithium layer is patterned onto the film 60 in a reduced-pressure atmosphere. With this, the melting state of lithium can be stably maintained inside the vapor deposition container 21, and an environment where reaction of lithium having a much higher reactivity is suppressed is easily formed. Further, also if the lithium layer is patterned onto the film 60 in an inert gas atmosphere, reaction of lithium having a high reactivity is suppressed.
Further, in this embodiment, the film 60 is nipped by the first roller 11A and the second roller 12 from upper and lower sides and the transfer pattern 11p is transferred to the film 60 while the film 60 is moved in a horizontal direction. With this, the pattern 25p immediately after transferring to the film 60 is barely displaced in an in-plane direction of the film 60.
In a roll-to-roll deposition apparatus 2 shown in
The fourth roller 24 is a tubular member, and is a so-called fountain roller. The third roller 23 is located between the fourth roller 24 and the first roller 11A. A well-known material resistant to heat is employed for a roller surface 24r of the fourth roller 24. The roller surface 24r of the fourth roller 24 is, for example, made of metal. The roller surface 24r of the fourth roller 24 is held in contact with the roller surface 23r of the third roller 23.
In addition, in the example of
The fourth roller 24 is rotatable about its center axis. For example, the fourth roller 24 held in contact with the third roller 23 is rotated in the clockwise direction by rotation of the third roller 23. Alternatively, a rotary drive mechanism that rotationally drives the fourth roller 24 may be provided outside the roll-to-roll deposition apparatus 2. Alternatively, the fourth roller 24 itself may include the rotary drive mechanism. In this case, the fourth roller 24 is rotated by the rotary drive mechanism in the clockwise direction.
Further, in this embodiment, a distance control mechanism that changes a relative distance between the fourth roller 24 and the vapor deposition container 21 may be provided outside the roll-to-roll deposition apparatus 2. With this distance control mechanism, the amount of lithium 25 that adheres to the roller surface 24r of the fourth roller 24 can be changed.
When the fourth roller 24 is rotated with the lithium 25 vapor-deposited on the fourth roller 24, the lithium 25 in the vapor deposition container 21 is upwardly moved via the roller surface 24r. With this, the vapor-deposited lithium 25 is supplied from the vapor deposition container 21 to the entire area of the roller surface 24r of the fourth roller 24. In addition, the lithium 25 on the roller surface 24r extends over the roller surface 23r of the third roller 23 held in contact with the lithium 25 on the roller surface 24r.
In addition, the lithium 25 on the roller surface 23r extends over the roller surface 11r of the first roller 11A held in contact with the lithium 25 on the roller surface 23r. That is, the evaporated lithium 25 is supplied from the vapor deposition container 21 to the roller surface 11r of the first roller 11A via the fourth roller 24 and the third roller 23.
Here, the movement velocity of the roller surface 24r may be set to be different from the movement velocity of the roller surface 23r of the third roller 23 or may be set to be equal to the movement velocity of the roller surface 23r of the third roller 23. With this velocity control, the thickness of the lithium 25 on the roller surface 23r is accurately adjusted. For example, the thickness of the lithium 25 on the roller surface 23r is adjusted to be substantially the same (uniform). Note that the direction of rotation of the fourth roller 24 is not limited to the clockwise direction, and may be the counter-clockwise direction.
Further, in this embodiment, a temperature control mechanism such as a temperature control medium circulation system is provided inside the fourth roller 24. With this temperature control mechanism, control is performed as appropriate such that, for example, the temperature of the roller surface 24r can be equal to or higher than the melting point of lithium. Further, if the doctor blade 22 is provided near the roller surface 23r of the third roller 23, the thickness of the lithium 25 on the roller surface 23r is more accurately adjusted due to the provision of the doctor blade 22.
Also in the roll-to-roll deposition apparatus 2, the same actions and effects as the roll-to-roll deposition apparatus 1 can be provided. In particular, since the one roller (fourth roller 24) through which the lithium 25 passes is added, heat damage can be more reliably prevented in accordance with this embodiment.
A roll-to-roll deposition apparatus 3 shown in
The first roller 11B is a tubular member containing metal such as stainless steel, iron, and aluminum. The first roller 11B is disposed between the film 60 and the lithium source 20. A roller surface 11r of the first roller 11B faces the deposition surface 60d of the film 60. For example, the roller surface 11r is held in contact with the deposition surface 60d of the film 60.
In addition, in the example of
The transfer pattern is formed on the roller surface 11r. The transfer pattern is, for example, a concave pattern such as a groove-shaped pattern and a hole-shaped pattern. Therefore, the first roller 11B can also be called plate cylinder in intaglio.
The first roller 11B is rotatable about its center axis. For example, a rotary drive mechanism that rotationally drives the first roller 11B is provided outside the roll-to-roll deposition apparatus 3. Alternatively, the first roller 11B itself may include the rotary drive mechanism. For example, with the film 60 traveling in the arrow-A direction, the first roller 11B made to face the film 60 is rotated in the clockwise direction. At this time, the movement velocity of the roller surface 11r is set to be equal to the travel velocity of the film 60, for example. With this, after a lithium pattern is formed on the roller surface 11r, this lithium pattern is transferred to the deposition surface 60d of the film 60 without position shift.
Further, in this embodiment, a distance control mechanism that changes a relative distance between the first roller 11B and the vapor deposition container 21 may be provided outside the roll-to-roll deposition apparatus 3. Further, in this embodiment, a temperature control mechanism such as a temperature control medium circulation system is provided inside the first roller 11B. With this temperature control mechanism, the temperature of the roller surface 11r is controlled as appropriate.
When the first roller 11B is rotated with the lithium 25 vapor-deposited on the first roller 11B, the lithium 25 in the vapor deposition container 21 is upwardly moved via the roller surface 11r. With this, the lithium 25 evaporated from the vapor deposition container 21 is supplied to the entire area of the roller surface 11r of the first roller 11B.
Further, in the roll-to-roll deposition apparatus 3, the doctor blade 22 is provided near the roller surface 11r of the first roller 11B. Due to the provision of the doctor blade 22, the thickness of the lithium 25 in the transfer pattern is accurately adjusted. For example, the thickness of the lithium 25 in the transfer pattern is adjusted to be substantially the same (uniform).
As shown in
Next, the evaporated lithium 25 is supplied to the transfer pattern 11p of the first roller 11B from the lithium source 20. For example, the vapor deposition container 21 is disposed below the first roller 11B such that the lithium 25 evaporated from the vapor deposition container 21 adheres to a part of the roller surface 11r of the first roller 11B. In addition, the temperature of the roller surface 11r of the first roller 11B is adjusted to the lithium melting point or more by the temperature control mechanism.
With this, the lithium 25 vapor-deposited on the first roller 11B is kept wet with the lithium 25 molten on the roller surface 11r. Further, the thickness of the lithium 25 on the roller surface 11r is accurately adjusted by the doctor blade 22.
The film 60 is traveling between the first roller 11B and the second roller 12 with the rotation of the first roller 11B and the second roller 12. Here, the first roller 11B is held in contact with the deposition surface 60d of the film 60. With this, the pattern 25p is also held in contact with the deposition surface 60d of the film 60, and the pattern 25p is transferred from the transfer pattern 11p to the deposition surface 60d of the film 60.
After that, the pattern 25p of the lithium 25 on the deposition surface 60d is naturally cooled, and the pattern 25p of the lithium layer is formed on the deposition surface 60d of the film 60. After that, a protection layer is further formed on the deposition surface 60d by the protection layer-forming mechanism 50 to cover the pattern 25p of the lithium layer.
Also in the roll-to-roll deposition apparatus 3, the same actions and effects as the roll-to-roll deposition apparatus 1 can be provided. In addition, in the roll-to-roll deposition apparatus 3, the transfer pattern 11p formed on the first roller 11B is the concave pattern, and hence the molten lithium 25 is efficiently received in the concave pattern. With this, the pattern 25p of the lithium layer formed on the deposition surface 60d of the film 60 becomes clearer.
A roll-to-roll deposition apparatus 4 shown in
The protection layer-forming mechanism 50 is placed downstream from the first roller 11A. The protection layer-forming mechanism 50 is capable of forming the protection layer or the protection film on the surface of the lithium layer after the lithium layer is formed on the film 60 by the first roller 11A.
The protection layer-forming mechanism 50 includes a protection layer-forming portion 51A, a protection layer-forming portion 51B, a protection film-forming portion 52, a gas supply mechanism 57, and a separator 58. The protection film-forming portion 52 includes a payout roller 53, a protection film 54, and guide rollers 55, 56. Each of the protection layer-forming portion 51A, the protection layer-forming portion 51B, and the protection film-forming portion 52 can be independently driven, and at least one of the protection layer-forming portion 51A, the protection layer-forming portion 51B, and the protection film-forming portion 52 can be driven.
Further, the separator 58 isolates the protection layer-forming mechanism 50 inside the vacuum chamber 70. In the example of
The protection layer-forming portion 51A is capable of forming the protection layer on the deposition surface 60d of the film 60 by, for example, a film deposition technique such as sputtering, CVD (Chemical Vapor Deposition), vapor deposition. Further, by inputting elements such as silicon and aluminum from a deposition source of the protection layer-forming portion 51A into the deposition surface 60d of the film 60 while introducing gas such as oxygen, nitrogen, water, carbon monoxide, and carbon dioxide into a space 70s isolated from the gas supply mechanism 57 by the separator 58, a reaction product (protection layer) may be formed on the deposition surface 60d.
The protection layer-forming portion 51B is capable of forming the protection layer on the deposition surface 60d of the film 60 by, for example, plasma treatment or heat treatment. The protection layer may be formed on the surface of the lithium layer by, for example, introducing gas such as oxygen, nitrogen, water, carbon monoxide, and carbon dioxide into the space 70s isolated from the gas supply mechanism 57 by the separator 58 such that at least one of these gases reacts with the surface of the lithium layer. Further, in order to improve the reactivity of these gases, these gases may be transformed into plasma gases by a plasma generation means (not shown) added to the roll-to-roll deposition apparatus 4. Lithium oxide (Li2O), lithium nitride (Li3N), lithium carbonate (LiCOx), and the like are, for example, formed on the surface of the lithium layer by the protection layer-forming portion 51B.
Note that the roll-to-roll deposition apparatus 4 may include a gas discharge mechanism for discharging the gas inside the space 70s to prevent the gas inside the space 70s from leaking out of the space 70s. In this case, the pressure inside the space 70s is controlled to be lower than the pressure outside the space 70s. With this, for example, oxidation or the like of molten lithium stored in the vapor deposition container 21 is suppressed.
Further, the protection film-forming portion 52 is capable of bonding the protection film 54 to the deposition surface 60d of the film 60. For example, the protection film 54 is disposed facing the deposition surface 60d of the film 60. In addition, the protection film 54 is placed, nipped between the guide roller 33g and the guide roller 56.
The protection film 54 is wound around the payout roller 53 in advance and paid out from the payout roller 53. Supported by the guide roller 55, the protection film 54 paid out from the payout roller 53 is moved between the guide roller 33g and the guide roller 56. Then, the protection film 54 covers the deposition surface 60d of the film 60, and the protection film 54 is continuously taken up by the take-up roller 32 together with the film 60.
Hereinabove, the embodiments of the present invention have been described, though the present invention is not limited only to those embodiments. Various modifications can be made as a matter of course. For example, in the roll-to-roll deposition apparatus 1 to 3, the lithium source 20 may be a mechanism that supplies the lithium 25 evaporated from the vapor deposition container 21 to the first roller 11B, the third roller 23, or the fourth roller 24 via a nozzle, a shower, or the like.
The number of rollers provided between the film 60 and the vapor deposition container 21 is not limited thereto (1 to 3). Alternatively, four rollers may be provided between the film 60 and the vapor deposition container 21 in a manner that depends on purposes. Further, either one of the pretreatment mechanism 40 or the protection layer forming mechanism 50 or both the pretreatment mechanism 40 and the protection layer forming mechanism 50 may be selected.
Further, the vapor deposition rate (amount of vapor) can be controlled using the heating temperature of the lithium 25. Therefore, the doctor blade 22 may be omitted.
In addition, with the configuration in the first embodiment, the lithium 25 vapor-deposited on the third roller 23 is supplied to the first roller 11A with the lithium 25 molten on the roller surface, for example. Alternatively, a lithium film in the solid phase may be formed on the surface of the third roller and then the lithium film may be transferred to the deposition surface of the film via the surface of the first roller. In this case, a method of setting the adhesiveness of the surface of the third roller with the lithium film to be lower than the surface of the first roller and setting the adhesiveness of the surface of the first roller with the lithium film to be lower than the film deposition surface, for example, can be employed. In this case, the temperature of the surfaces of the first roller and the third roller are controlled to be a temperature lower than the melting point of the lithium by the temperature control mechanism.
1, 2, 3, 4 roll-to-roll deposition apparatus
11A, 11B first roller
11
r roller surface
11
p transfer pattern
12 second roller
12
r roller surface
20 lithium source
21 vapor deposition container
22 doctor blade
23 third roller
23
r roller surface
24 fourth roller
24
r roller surface
25 lithium
25
p pattern
30 film travel mechanism
31 payout roller
32 take-up roller
33
a, 33b, 33c, 33d, 33e, 33f, 33g guide roller
40 pretreatment mechanism
50 protection layer-forming mechanism
51A protection layer-forming portion
51B protection layer-forming portion
52 protection film-forming portion
53 payout roller
54 protection film
55, 56 guide roller
57 gas supply mechanism
58 separator
60 film
60
d deposition surface
70 vacuum chamber
70
s space
71 gas discharge mechanism
72 gas supply mechanism
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-104675 | May 2018 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2019/019504 | 5/16/2019 | WO | 00 |