Field of the Invention
The invention is based on a roll, in particular for use in a machine for producing and/or finishing a fibrous web such as a paper, board or tissue web, including a roll shell having at least some sections formed of a metal material and a coating formed thereon.
Rolls of this type are present in a multiplicity of positions and with a multiplicity of functions in the aforementioned machines. For example, rolls having soft covering layers are suitable for pressing and dewatering the fibrous web, rolls with hard surfaces, in particular including those with a heating device, are primarily used for calendering and drying.
The last-named rolls were earlier often produced from granite and ground with high quality. More recent concepts provided steel rolls, which were likewise polished. Since these rolls all have various disadvantages, such as, for example, the high weight in the case of granite rolls or the susceptibility to corrosion in the case of steel rolls, novel methods for coating roll bodies made of steel or of composite materials have become widespread over time, said methods forming a metallic, ceramic or cermet sprayed layer by means of methods such as HVOF or flame spraying on the roll body. Rolls of this type have been known for a relatively long time and form the current prior art, for example in the case of central press rolls, drying cylinders and guide rolls.
The thermal coating process provides for powder or wires to be melted by means of the input of thermal energy and accelerated kinetically onto the roll core to be coated. The properties and possibilities of the spraying processes are substantially given by the ratio of the kinetic to the thermal energy.
A roll having a coating made of a metal oxide is known, for example from EP 0 870 867 B1. There, a description is given of a roll for a paper machine, board machine or a finishing machine, having a ceramic layer with a thickness of 100 to 2000 μm which is applied to the surface of the roll, the roughness Ra of the outer surface of the roll being 0.2 to 2.0 μm and preferably 0.4 to 1.5 μm. The ceramic layer has 50 to 95% and preferably 55 to 80% of Cr2O3 and 3 to 50% and preferably 20 to 45% of TiO2 and possibly other metal oxides.
The known methods and the metallic, ceramic or cermet coatings that can be produced thereby are afflicted with various disadvantages.
Firstly, as a result of the sole input of energy into the material to be applied and a cooling rate of up to 106 K/s, only a mechanical connection or bonding of the raw material on the roll core occurs. In order to configure this bonding as effectively as possible, careful preparatory surface treatment such as sandblasting and the like is necessary, which is complicated and time-consuming.
Secondly, the coating structure, depending on the material and/or production process, is sealed porous as far as open porosity. The porosity can lead to an increased tendency to corrosion and to adhesion problems. Accordingly, the surface of the sprayed layer must be filled, for example by means of final sealing, with a polymer.
Furthermore, thermal spraying is not an economical or an ecological method, because of the poor application efficiency of the powder with regard to the microns per pass and the percentage of powder remaining on the roll.
It is accordingly an object of the invention to specify a roll the coating of which, with regard to the adhesion thereof to the roll core and the corrosion resistance thereof, satisfies the requirements which are placed by paper, board or tissue machines with regard to temperatures, moisture and loading by chemicals.
The object is achieved by a roll for use in a machine for producing and/or further processing a fibrous web such as a paper, board or tissue web, including a roll shell having at least some sections formed of a metal material and a coating formed thereon.
According to the invention, provision is made for there to be a coating which is made of a metallic, ceramic and/or a cermet material, or for at least some sections of said coating to comprise one of said materials, an alloy region being formed between the roll shell and the coating.
Further advantageous refinement variants and aspects of the invention emerge from the sub-claims.
Provision can preferably be made for the alloy region to have a thickness of 0.5 to 3%, preferably of 1%, of the layer thickness of the coating.
According to an advantageous aspect of the invention in the alloy region there can be a metallurgical connection between the material and the material of the roll shell.
The coating can preferably be produced by using an inductive device, a plasma gun or a laser.
The material can advantageously be present in powder form, in rod form or as wire.
According to advantageous aspects of the invention, the coating can have at least one layer which is produced by a single pass, or preferably a plurality of layers which are produced by a plurality of passes.
The invention will be described in more detail below with reference to the drawings, without restricting the generality. In the figures:
In
The basic task of a roll coating, depending on the position in the paper, board or tissue machine, can extend from “only wear-resistant” as far as “only corrosion-resistant”. The common factor in all positions, however, is a requirement for good adhesion of the roll coating to the roll core. The disadvantages listed further above can be ameliorated by improved adhesion of the coating to the roll core to the extent that the attachment of the coating material is not based on purely mechanical bonding but on a metallurgical bond.
By means of this “true” adhesion, which must be present only in a range from 0.5 to 3% of the layer thickness, an increase in the adhesive tensile strength by up to 80% as compared with a thermal sprayed layer can be achieved. Depending on the position, this increase in the adhesion primarily provides an increased running time, in the area of safety in the event of fabric tears and other, also local, overloads.
In combination with the improved adhesion with a reduced porosity of the coating, the corrosion resistance can additionally be increased as compared with a conventional thermal sprayed layer.
If
As explained further above, the sprayed layer 2 can at least partly consist of metallic, ceramic or cermet materials. The attachment of the materials to the roll shell 3 is carried out only by mechanical or form-fitting bonding of the molten particles to the material of the appropriately prepared roll shell 3. The interface 4 formed in this way has no significant extent, viewed in the radial direction. The adhesion is thus limited. In particular in the event of corrosion by water migrating underneath and in the event of point-like mechanical overloads, such as, for example, during the passage of a foreign body through a nip between two rolls 1, it is therefore necessary to take account of the fact that some areas of the sprayed layer 2 will be detached from the roll shell 3. This can lead to endangering the operating personnel and to damaging following machine parts.
By comparison, in the same view as
Here, it is sufficient if an alloy region 6 makes up about 0.1 to 3%, preferably 1%, of the layer thickness of the coating 5 that is to be built up.
This is to be judged as positive in view of the likewise known method of application welding. Firstly, the alloy region 6 is smaller, so that finer processing of the materials is possible, which improves the surface quality of the coating 5 and reduces subsequent operations.
Secondly, the coating 5 produced by the laser cladding is normally produced in several passes, an alloy region likewise being produced again between the layers of the individual passes, since each time the region lying underneath is melted again and forms an alloy with the further layer lying thereon. This results in turn in adhesion and corrosion resistance which are increased.
The structure of a coating 5 on a roll 1 is illustrated in a highly schematic view in
Here, the roll 1 is supported such that it can rotate and is driven suitably, so that it rotates underneath an application device 7 that can preferably be displaced axially along the roll 1. As a result, the entire surface of the roll 1 can be coated in a continuous spiral line in at least one or more passes. However, it is also possible to apply the coating 5 in another way, for example in radial rings or axial stripes. The application device 7 substantially comprises a material feed 8 and an energy source 9, into which the usually powdery material is put.
Conceivable as the energy source 9 are inductive and plasma-generating devices and lasers of various types such as CO2 lasers, HDPL (high-power diode lasers) or DDL (direct diode lasers). Building up a coating 5 by means of laser cladding constitutes the technologically most easily implemented variant.
A great economic advantage of the method is to be seen in the high deposition efficiency as compared with thermal coatings, with an increased layer thickness per pass (μm/pass).
Number | Date | Country | Kind |
---|---|---|---|
10 2013 208 254 | May 2013 | DE | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/EP2014/054651 | 3/11/2014 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2014/180588 | 11/13/2014 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
3526939 | Nikkanen | Sep 1970 | A |
4015100 | Gnanamuthu | Mar 1977 | A |
4064608 | Jaeger | Dec 1977 | A |
4323756 | Brown | Apr 1982 | A |
4484959 | Boucher | Nov 1984 | A |
4609577 | Long | Sep 1986 | A |
4733446 | Kuroki | Mar 1988 | A |
4748736 | Miihkinen | Jun 1988 | A |
4772773 | Hashimoto | Sep 1988 | A |
4847112 | Halleux | Jul 1989 | A |
4856161 | Miihkinen | Aug 1989 | A |
4942059 | Wilson | Jul 1990 | A |
4989306 | Leino et al. | Feb 1991 | A |
5111567 | Leino et al. | May 1992 | A |
5235747 | Leino | Aug 1993 | A |
5308409 | Kamimura | May 1994 | A |
5766378 | Horn | Jun 1998 | A |
5967959 | Niemi et al. | Oct 1999 | A |
6127644 | Singh | Oct 2000 | A |
6200248 | Vestola et al. | Mar 2001 | B1 |
6843866 | Brenner | Jan 2005 | B2 |
20010024723 | Vestola et al. | Sep 2001 | A1 |
20060054079 | Withey | Mar 2006 | A1 |
Number | Date | Country |
---|---|---|
1037371 | Nov 1989 | CN |
1435531 | Aug 2003 | CN |
2744188 | Apr 1978 | DE |
3621154 | Mar 1987 | DE |
3725892 | Feb 1989 | DE |
0278942 | Aug 1988 | EP |
0425454 | May 1991 | EP |
0425464 | May 1991 | EP |
0870867 | Oct 1998 | EP |
0870868 | Oct 1998 | EP |
Number | Date | Country | |
---|---|---|---|
20160130756 A1 | May 2016 | US |