The present invention is directed to a rolling bearing having a composite polymer sheet attached thereto and to a method of manufacturing a rolling bearing having a composite polymer sheet attached thereto.
Many rotating mechanical apparatuses may include a rolling bearing that enables the relative rotation between a first component and a second component. For example, the first component may be a housing and the second component may be a rotating shaft, wherein an outer ring of the rolling bearing is fitted into the housing and/or an inner ring of the rolling bearing is fitted onto the shaft. Depending on the specific application, it can happen, either due to loads deforming the ring or by design, that one of these fits is a loose fit, which may lead to ring creep.
In some cases, this ring creep may induce a so-called ring creep wear damage. For example, if a steel outer ring is loosely fitted into an aluminum alloy housing, there is a chance that a ring creep of the outer ring induces ring creep wear damage on the aluminum alloy housing due to the relative motion (ring creep movement) between the outer ring and housing. In other words, the outer diameter surface of the outer ring and an inner surface of the housing are rubbed against each other so that wear occurs on the housing. When the wear of the housing increases, a backlash may occur at a rotation support part so that abnormal vibration is generated and the rotating mechanical apparatus is out of order. This may further lead to a loss of alignment which may cause undesired noise. Also, creep wear may cause debris and/or contaminants that may damage the bearing and/or parts of the mechanical apparatus such as gears which may lead to a shorter life of the bearing and/or the mechanical apparatus.
This ring creep movement may be prevented by interlocking or by a rubber O-ring. However, in practice, the interlocking mechanism and rubber O-ring are not a desired solution since it is difficult to realize and/or not reliable. Polymer coating of the rubbing surfaces using solid lubricants and pre-treatment by manganese-phosphating (MnPh) is an alternative solution to reduce the creep wear. So far, the coatings include antimony (Sb), which is regarded a toxic material to human health, and the necessary coating process is very complicated since it requires submerging a complete bearing into an acid liquid bath for the manganese-phosphating process and a thermal curing of the polymer coating.
It is therefore an aspect of the present disclosure to reduce creep wear damage.
In the following, a rolling bearing is provided which includes at least one outer ring, at least one inner ring, and at least one rolling element arranged between the at least one outer ring and the at least one inner ring. An outer surface of the at least one outer ring is configured to be fitted into a first component, such as a housing, and an inner surface of the inner ring is configured to be fitted to a second component, such as a shaft, wherein the first component and the second component are rotatable relative to one another.
The outer surface of the at least one outer ring may be the radial outer surface of the ring, such as the outer circumference surface of the outer ring. The inner surface of the at least one inner ring may be the radially inner surface of the ring, such as an inner bore of the inner ring. For example, the rolling bearing may be a ball bearing, a cylindrical roller bearing, a tapered roller bearing, and the like. Furthermore, the outer and/or inner ring may be made from a first material. The first material may be steel, particularly bearing steel. The first component and/or second component may be made from a second material that is different from bearing steel. In particular, the second material may be softer than the first material. For example, the second material may be aluminum, an aluminum alloy, or the like. Moreover, the roller bearing may be used in an electric motor, for example in an electric vehicle, or a pump.
In order to reduce creep wear and manufacturing costs, a polymer composite sheet layer (sometime referred to as a polymer composite sheet) is bonded on at least one of the outer surface of the outer ring and the inner surface of the inner ring using a bonding agent, wherein polymer composite sheet layer comprises at least one perfluoroalkyl and/or polyfluoroalkyl component (PFAS, perfluoroalkyl and polyfluoroalkyl substances). The perfluoroalkyl and/or polyfluoroalkyl component may be an organofluorine chemical compound that has at least one fluorine atom attached to an alkyl chain such as polytetrafluoroethylene (PTFE), fluroethylenepropylene (FEP), and/or perfluoroalkoxy (FPA). Such a polymer composite sheet layer can reduce the wear on the element that is fitted to the outer and/or inner ring such that abnormal vibrations and/or noise may be mitigated. Furthermore, the polymer composite sheet layer or liner may be cut to size before bonding the polymer composite sheet layer to the surface, which can reduce the manufacturing costs. In particular, a coating process can be omitted. Also, it may be possible to replace the polymer composite sheet layer if it is worn.
For example, the polymer composite sheet layer may be made of polytetrafluoroethylene (PTFE), fluroethylenepropylene (FEP), and/or perfluoroalkoxy (FPA). In particular, these compounds may exhibit self-lubrication and may have a high wear resistance. In addition, these compounds may be commercially available as sheet material which just has to be cut to size such that expensive coating processes can be omitted.
Furthermore, the polymer composite sheet layer may comprise a polytetrafluoroethylene (PTFE) polymer impregnated carrier, wherein the carrier is a glass and/or polyester carrier. Such a PTFE impregnated carrier has the advantage that it may have an increase durability, and/or may be commercially available as sheet material which just has to be cut to size such that expensive coating processes can be omitted.
Preferably, the polymer composite sheet layer comprises a polymer, and 1 to 50 wt %, preferable 5 to 20 wt % of at least one solid lubricant, wherein the polymer is fluroethylenepropylene (FEP), perfluoroalkoxy (FPA), polyether ether ketone (PEEK), polyphenylene sulfide (PPS), polyester (PET), polyurethane (TPU), polyethylene (PE), polypropylene (PP), polyimide (PI), and/or polyamideimide (PAI). For example, the solid lubricant may be polytetrafluoroethylene (PTFE). Due to the polytetrafluoroethylene (PTFE) which can act as a solid lubricant, the amount of wear on the outer and/or inner ring surface and/or the first and/or second element may be reduced which may also reduce the amount of debris. This may reduce damage of the bearing and/or parts of the mechanical apparatus such as gears which may lead to a longer life of the bearing and/or the mechanical apparatus.
The polymer composite sheet layer may have a thickness between 2 to 200 μm, preferably between 5 to 30 μm. When the layer thickness is smaller than 2 m, the polymer composite sheet layer may wear prematurely and the creep wear resistance may not last long. On the other hand, when the film thickness exceeds 200 m, the strength of the polymer composite sheet layer may be lowered, so that the polymer composite sheet layer may be peeled off. Thus, a layer thickness between 2 and 200 μm allows for an effective reduction of the creep wear, with a reduced risk that the polymer composite sheet layer is peeled off.
Preferably, the bonding agent is adhesive epoxy, or a cyanoacrylate glue. For example, the epoxy glue may be air-hardening, UV hardening and/or cure hardening.
Furthermore, the bonding agent may be applied as a bonding layer having a thickness less than 25 μm, preferably less than 5 μm. This allows for a secure bonding of the polymer composite sheet layer to the surface.
In addition or alternatively, the polymer composite sheet layer may be provided with an adhesive on one side, wherein the adhesive is an acrylic adhesive or a silicone. Thus, it may be possible to bond the polymer composite sheet layer to at least one of the outer surface of the outer ring and the inner surface of the inner ring without the need to apply the bonding agent in an extra bonding layer. This may reduce manufacturing costs.
Preferably, the outer surface of the outer ring and/or the inner surface of the inner ring has a surface roughness Ra of 0.5 to 10 μm, preferably 1 to 3 μm, before the polymer composite sheet layer is applied. This allows for an improved bonding of the polymer composite sheet layer on the outer surface of the outer ring and/or the inner surface of the inner ring. Preferably, a backside of the polymer composite sheet layer is pretreated using chemical etching and/or plasma etching. This may improve the bonding of the bonding agent to the polymer composite sheet layer.
Preferably, a friction coefficient of the polymer composite sheet in dry contact against an aluminum alloy is between 0.05 to 0.4. In particular, a lower friction coefficient may indicate a lower amount of creep wear.
According to a further preferred embodiment, the polymer composite sheet layer has a dielectric strength greater than 15 kV/mm and a dielectric constant or relative permittivity of lower than 4.
In case that the rolling bearing is employed in an electric motor, for example in an electric vehicle, it may happen that electric current runs through the bearing and/or that an electric voltage is applied over the rolling bearing. Due to current leakage through the bearing, a lubricant in the bearing and/or the bearing itself, particularly the metal surfaces of the bearing such as the raceways for the rolling elements, may be damaged. The damage may include an increase of surface roughness and/or noise and may damage the bearing function. By providing the outer surface of the outer ring and/or the inner surface of the inner ring with a polymer composite sheet layer that may have a dielectric strength greater than 15 kV/mm and a dielectric constant of lower than 4, the electric current passage intensity can be significantly reduced, for example by greater than 90%, and prolong the bearing service life. The relative high dielectric strength and low dielectric constant of the coating can reduce the current intensity and the bearing damage.
According to a further aspect of the disclosure a method for manufacturing a rolling bearing as mentioned above is provided. The method comprises: providing a polymer composite sheet layer, wherein polymer composite sheet layer comprising at least one perfluoroalkyl and/or polyfluoroalkyl component, applying a bonding agent on at least one of the outer surface of the outer ring and the inner surface of the inner ring and/or the polymer composite sheet layer, and bonding the polymer composite sheet layer to the at least one of the outer surface of the outer ring and the inner surface of the inner ring.
According to a further embodiment, the method further includes, before applying polymer composite sheet layer, preparing the at least one of the outer surface of the outer ring and the inner surface of the inner ring to have a surface roughness Ra of 0.5 to 10 μm, preferably Ra 1 to 3 μm. This allows for an improved bonding of the polymer composite sheet layer on the outer surface of the outer ring and/or the inner surface of the inner ring. Preferably, a backside of the polymer composite sheet layer is pretreated using chemical etching and/or plasma etching. This may improve the bonding of the bonding agent to the polymer composite sheet layer.
In the following, preferred embodiments of the invention are described in connection with the drawings, wherein the drawings are exemplarily only, and are not intended to limit the scope of protection. The scope of protection is defined by the accompanied claims, only.
In the following same or similar functioning elements are indicated with the same reference numerals.
A ball bearing is shown as an example of a rolling-element bearing in
The outer ring 1 and the inner ring 2 are made of metal, for example bearing steel. Further, the outer diameter surface 1b of the outer ring 1 is provided with a bonding layer 5 comprising a bonding agent, which bonds a polymer composite sheet layer 6 to the outer diameter surface 1b of the outer ring 1. The housing is made of aluminum or aluminum alloy (for example, aluminum die-cast material) for weight reduction, in many cases. Since the polymer composite sheet layer 6 of the present invention is softer than aluminum or aluminum alloy (for example, aluminum die-cast material), the housing is not damaged even though the outer diameter surface 1b of the outer ring and the housing may move with respect to each other.
The polymer composite sheet layer 6 comprises a polymer such as fluroethylenepropylene (FEP), perfluoroalkoxy (FPA), and/or polytetrafluoroethylene (PTFE). Additionally or alternatively, polymer composite sheet layer 6 comprising polyether ether ketone (PEEK), polyphenylene sulfide (PPS), polyester (PET), polyurethane (TPU), polyethylene (PE), polypropylene (PP), polyimide (PI), and/or polyamideimide (PAI) as well as at least one solid lubricant may be used.
If a solid lubricant is added to the polymer composite sheet layer 6, the solid lubricant is required to have lubrication performance and to be softer than a material of the housing, which in the present embodiment is aluminum or aluminum alloy. As the solid lubricant, polytetrafluoroethylene (PTFE) and/or molybdenum disulfide (MoS2) may be used. The content of the solid lubricant in the polymer composite sheet layer 6 may be between 1 and 50 wt %, preferable 5 to 20 wt %.
Alternatively, the polymer composite sheet layer is made of polytetrafluoroethylene (PTFE) and/or comprises a polytetrafluoroethylene (PTFE) polymer impregnated carrier, wherein the carrier is a glass and/or polyester carrier.
The polymer composite sheet layer 6 may be formed by an extruding method. For example, the raw materials for the polymer composite such as the used polymer or polymer mixture is dissolved (melted) and subsequently flow casted, using for example a drum cast. The obtained cast material is then forwardly and/or laterally stretched to the predetermined dimensions and finally rolled to obtain a roll of a polymer composite sheet material. This material can then be cut the needed size. Additives such as a solid lubricant may either be added at the beginning of the extruding method when the raw materials are dissolved (melted) and mixed and/or by using a coating method to coat the additives on the sheet material.
As the bonding agent an epoxy adhesive or a cyanoacrylate glue can be used. The bonding layer 5 has a thickness of less than 25 μm, preferably less than 5 μm, and can be applied directly on the outer diameter surface 1b of the outer ring. Alternatively, the polymer composite sheet layer 6 is provided with an adhesive on one side, wherein the adhesive is an acrylic adhesive or a silicone.
Before the polymer composite sheet layer 6 is applied to the outer ring 1, a surface of the outer ring 1 is machined to have a surface roughness Ra of 0.5 to 10 μm, preferably 1 to 3 μm. This allows for an improved bonding of the bonding layer 5 on the surface. Then, the polymer composite sheet layer 6 is applied to the bonding layer 5. Preferably, the polymer composite sheet layer 6 may be cut to size before the polymer composite sheet layer 6 is bonded to the outer ring 1.
The thickness of the polymer composite sheet layer 6 is between 2 to 200 μm. When the thickness of the polymer composite sheet layer 6 is smaller than 2 m, the polymer composite sheet layer 6 may wear prematurely and the creep wear resistance will not last long. On the other hand, when the thickness of the polymer composite sheet layer 6 exceeds 200 μm, the strength of the polymer composite sheet layer 6 is lowered, so that the polymer composite sheet layer 6 may be peeled off. The thickness of the polymer composite sheet layer 6 is more preferably 5 μm to 30 μm.
Alternatively, when the creep occurs in the inner ring and a shaft, the polymer composite sheet layer 6 may be bonded to the inner surface of the inner ring 2.
The present invention will be further described with reference to test examples. However, it should be noted that the present invention is not limited thereto.
In this test, the effects that are to be accomplished by the bonded film of the present invention was verified.
As shown in Table 1, as Example 1 a sheet material made of polytetrafluorethylene (PTFE) and polyester was used and as Example 2 sheet material made of fluoroethylenepropylene (FEP) was used.
For the test, a pin on disk test was performed, wherein a pin is moved with defined load and defined contact pressure over a disk for a predetermined amount of time. This allows to determine the wear depth as well as the average coefficient of friction. Two set were performed for the test, wherein in the first set a steel pin is moved over an aluminum disk and in the second set an aluminum pin is moved over a steel disk. In both sets, the steel component, namely the pin in the first set and the disk in the second set, were provided with a polymer composite sheet layer according to examples 1, and 2. Furthermore, uncoated reference samples were prepared as well. The polymer composite sheet layer was bonded to the workpiece with epoxy or cyanoacrylate. As reference samples, a coating containing a binder, molybdenum disulfide (MoS2) as a solid lubricant, as well as antimony according to the prior art as described for example in EP 3505783 A1 were used.
The steel pin had a diameter of 82 mm, and the aluminum pin had a diameter of 64 mm. The defined load was 20 N for the steel pin and 10 N for the aluminum pin, wherein the average contact pressure was 130 MPa for the steel pin, and 124 MPa for the aluminum pin. The results for the wear depth of the aluminum and the polymer composite sheet layer as well as the average coefficient of friction are shown in
It can be seen from
In summary, the described polymer composite sheet layer 6 can reduce the wear on an element which is fitted to the outer and/or inner ring, such as an aluminum housing, such that abnormal vibrations and/or noise may be mitigated. The described polymer composite sheet layer 6 has a low coefficient of friction which may allow to reduce the number of debris resulting in a longer life of the bearing and/or the mechanical apparatus.
Also, the polymer composite sheet layer 6 can be cut to size before being bonded on the metal surfaces of the outer and/or inner ring. The bonding agent can be applied as a bonding layer and/or on one side of the polymer composite sheet layer 6.
Representative, non-limiting examples of the present invention were described above in detail with reference to the attached drawings. This detailed description is merely intended to teach a person of skill in the art further details for practicing preferred aspects of the present teachings and is not intended to limit the scope of the invention. Furthermore, each of the additional features and teachings disclosed above may be utilized separately or in conjunction with other features and teachings to provide improved rolling bearings.
Moreover, combinations of features and steps disclosed in the above detailed description may not be necessary to practice the invention in the broadest sense, and are instead taught merely to particularly describe representative examples of the invention. Furthermore, various features of the above-described representative examples, as well as the various independent and dependent claims below, may be combined in ways that are not specifically and explicitly enumerated in order to provide additional useful embodiments of the present teachings.
All features disclosed in the description and/or the claims are intended to be disclosed separately and independently from each other for the purpose of original written disclosure, as well as for the purpose of restricting the claimed subject matter, independent of the compositions of the features in the embodiments and/or the claims. In addition, all value ranges or indications of groups of entities are intended to disclose every possible intermediate value or intermediate entity for the purpose of original written disclosure, as well as for the purpose of restricting the claimed subject matter.