This invention relates to roofing materials with increased wind uplift resistance and methods of making such roofing materials. The roofing materials include a sealant attachment zone with surfacing media. Roofing materials, such as shingles, that include this sealant attachment zone exhibit superior properties of, for example, increased wind uplift resistance, as compared to roofing materials without such a sealant attachment zone.
Typically, roofing materials, such as, e.g., shingles, are based upon a fiberglass or felt mat that is coated and impregnated with an asphalt-based composition that is subsequently coated with granules. Generally, these roofing materials further include a sealant that is applied at one or more locations on a backing during the time of manufacturing. During this application step, the sealant is generally in the form of a molten asphaltic sealant. When the sealant cools into a solid form after manufacturing and during installation of the roofing material, the sealant is generally placed into contact with a granulated surface of another previously installed roofing material where adhesion between the roofing materials will later be activated by solar heat. In this case, the sealant usually adheres to the granulated surface first, once the sealant is thermally activated by solar heat. The presence of granules on the previously installed roofing material's surface, however, can interfere with the sealant forming a strong cohesive bond. As a result, wind uplift resistance can be limited due to the fact that the sealant will be attaching to the granulated surface first, and the presence of granules on the previously installed roofing material's surface can interfere with the sealant from making direct surface-to-surface contact (e.g., asphalt-to-asphalt contact).
There is therefore a need for a roofing material having a sealant attachment zone that comprises surfacing media that promotes the ability of sealants, such as, e.g., asphaltic sealants, to make better contact between overlying roofing materials and previously installed roofing materials to thus form a strong bond, and thereby increase wind uplift resistance of the roofing materials.
One embodiment of this invention pertains to a roofing material comprising (a) a front surface, (b) a back surface, and (c) a sealant attachment zone disposed on at least the front surface of the roofing material, the sealant attachment zone including surfacing media that comprise at least one of mineral particles, polymeric particles, and combinations thereof. The sealant attachment zone has an average surface coverage with the surfacing media of 30% to 70%. The roofing material exhibits an increased wind uplift resistance, as measured according to ASTM D6381, as compared to a roofing material without a sealant attachment zone having said average surface coverage with the surfacing media of 30% to 70%.
In one embodiment, the sealant attachment zone has an average surface coverage with the surfacing media of 40% to 70%.
In one embodiment, the sealant attachment zone has an average surface coverage with the surfacing media of 40% to 60%.
In one embodiment, the surfacing media comprise mineral particles that include at least one of slag fines, granule fines, sands, limestone fines, calcium carbonate, slate fines, and combinations thereof.
In some embodiments, the surfacing media comprise polymeric particles that include at least one of rubber particles, linear low-density polyethylene (LLDPE) particles, styrene-butadiene-styrene (SBS) powders, particles having a polar functional group that is selected from the group consisting of an alcohol, a carboxyl, a phenolic, an amine, and a thiol, and combinations thereof.
In one embodiment, the surfacing media have a particle size distribution of 16 to 270 US mesh. In some embodiments, the surfacing media have a particle size distribution of 16 to 100 US mesh.
In one embodiment, the surfacing media have a mean particle size of 100 to 250 microns. In some embodiments, the surfacing media have a mean particle size of 200 to 250 microns.
In some embodiments, the sealant attachment zone comprises (i) a first region having a percentage of surface coverage of the surfacing media that is less than the average surface coverage, and (ii) a second region having a percentage of surface coverage of the surfacing media that is greater than the average surface coverage.
In one embodiment, the roofing material exhibits a decreased surface tack temperature (° F.) as compared to a roofing material without the sealant attachment zone.
In one embodiment, the roofing material is a roofing shingle.
In one embodiment, the surfacing media further comprise a tackifier, an encapsulated adhesion promoter, magnetic powder, and combinations thereof. In some embodiments, the surfacing media further comprise ferrous metal powder.
Another embodiment of this invention pertains to a method of preparing a roofing material. The method comprises (a) obtaining a substrate, (b) obtaining surfacing media that comprise at least one of mineral particles, polymeric particles, and combinations thereof, and (c) applying the surfacing media to a surface of the substrate to form a roofing material having a sealant attachment zone with an average surface coverage of the surfacing media of 30% to 70%. The roofing material exhibits an increased wind uplift resistance, as measured according to ASTM D6381, as compared to a roofing material without a sealant attachment zone having said average surface coverage of the surfacing media of 30% to 70%.
In one embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 70%.
In one embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%.
In one embodiment, the method further includes heating the surfacing media prior to applying the surfacing media to the surface of the substrate.
In one embodiment, the applying the surfacing media to the surface of the substrate is conducted by controlling an amount of the surfacing media applied to the surface of the substrate. In some embodiments, the controlling the amount of the surfacing media applied to the surface of the substrate is conducted by forming (i) a first region of the sealant attachment zone that has a percentage of surface coverage of the surfacing media that is less than the average surface coverage, and (ii) a second region of the sealant attachment zone that has a percentage of surface coverage of the surfacing media that is greater than the average surface coverage.
In one embodiment, the surfacing media comprise mineral particles that include at least one of slag fines, granule fines, sands, limestone fines, calcium carbonate, slate fines, and combinations thereof.
In some embodiments, the surfacing media comprise polymeric particles that include at least one of rubber particles, linear low-density polyethylene (LLDPE) particles, styrene-butadiene-styrene (SBS) powders, particles having a polar functional group that is selected from the group consisting of an alcohol, a carboxyl, a phenolic, an amine, and a thiol, and combinations thereof.
In one embodiment, the surfacing media have a particle size distribution of 16 to 270 US mesh. In some embodiments, the surfacing media have a particle size distribution of 16 to 100 US mesh.
In one embodiment, the surfacing media have a mean particle size of 100 to 250 microns. In some embodiments, the surfacing media have a mean particle size of 200 to 250 microns.
In one embodiment, the roofing material exhibits a decreased surface tack temperature (° F.) as compared to a roofing material without the sealant attachment zone.
In one embodiment, the roofing material is a roofing shingle.
In one embodiment, the surfacing media further comprise a tackifier, an encapsulated adhesion promoter, magnetic powder, and combinations thereof. In some embodiments, the surfacing media further comprise ferrous metal powder.
For a more complete understanding of the invention and the advantages thereof, reference is made to the following descriptions, taken in conjunction with the accompanying figures, in which:
Among those benefits and improvements that have been disclosed, other objects and advantages of this disclosure will become apparent from the following description taken in conjunction with the accompanying figures. Detailed embodiments of the present disclosure are disclosed herein; however, it is to be understood that the disclosed embodiments are merely illustrative of the disclosure that may be embodied in various forms. In addition, each of the examples given regarding the various embodiments of the disclosure are intended to be illustrative, and not restrictive.
Throughout the specification and claims, the following terms take the meanings explicitly associated herein, unless the context clearly dictates otherwise. The phrases “in one embodiment,” “in an embodiment,” and “in some embodiments” as used herein do not necessarily refer to the same embodiment(s), though they may. Furthermore, the phrases “in another embodiment” and “in some other embodiments” as used herein do not necessarily refer to a different embodiment, although they may. All embodiments of the disclosure are intended to be combinable without departing from the scope or spirit of the disclosure.
As used herein, the term “based on” is not exclusive and allows for being based on additional factors not described, unless the context clearly dictates otherwise. In addition, throughout the specification, the meaning of “a,” “an,” and “the” include plural references. The meaning of “in” includes “in” and “on.”
As used herein, terms such as “comprising” “including,” and “having” do not limit the scope of a specific claim to the materials or steps recited by the claim.
As used herein, terms such as “consisting of” and “composed of” limit the scope of a specific claim to the materials and steps recited by the claim.
All prior patents, publications, and test methods referenced herein are incorporated by reference in their entireties.
One embodiment of this invention pertains to a roofing material comprising (a) a front surface, (b) a back surface, and (c) a sealant attachment zone disposed on at least the front surface of the roofing material, the sealant attachment zone including surfacing media that comprise at least one of mineral particles, polymeric particles, and combinations thereof. The sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%. The roofing material exhibits an increased wind uplift resistance, as measured according to ASTM D6381, as compared to a roofing material without a sealant attachment zone having said average surface coverage of the surfacing media of 30% to 70%.
The roofing material 100 of the embodiment of
In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 55%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 50%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 45%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 40%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 35%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 55%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 50%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 45%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 35% to 40%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 55%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 50%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 45%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 55%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 45% to 50%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 50% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 50% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 50% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 50% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 50% to 55%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 55% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 55% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 55% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 55% to 60%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 60% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 60% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 60% to 65%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 65% to 75%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 65% to 70%. In an embodiment, the sealant attachment zone has an average surface coverage of the surfacing media of 70% to 75%.
In an embodiment, the surfacing media comprise mineral particles that include at least one of slag fines, granule fines, sands, limestone fines, calcium carbonate, slate fines, and combinations thereof. In some embodiments, the surfacing media comprise various minerals and/or materials extracted from a quarry, including, for example, various types of granite, basalt, clay, coal, gypsum, limestone, marble, quartz, rhyolite, sandstone, quartz, among others, as well as combinations thereof.
In some embodiments, the surfacing media comprise polymeric particles that include at least one of rubber particles, linear low-density polyethylene (LLDPE) particles, styrene-butadiene-styrene (SBS) powders, particles having a polar functional group that is selected from the group consisting of an alcohol, a carboxyl, a phenolic, an amine, and a thiol, and combinations thereof. In some embodiments, the surfacing media comprise activated rubber particles from reclaimed tire. In some embodiments, the surfacing media comprise recycled asphalt, such as, e.g., recycled asphaltic shingles. According to one embodiment, the surfacing media have a high affinity for a sealant, including, e.g., an asphaltic sealant.
In an embodiment, the surfacing media comprise glass.
In an embodiment, the surfacing media comprise nickel, copper, iron, titanium, and/or zinc, as well as any other metal, and combinations thereof.
In an embodiment, the surfacing media further includes granules. In some embodiments, the surfacing media is free of granules.
In an embodiment, the surfacing media have a particle size distribution of 16 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 50 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 40 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 30 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 25 US mesh. In an embodiment, the surfacing media have a particle size distribution of 16 to 20 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 50 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 40 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 30 US mesh. In an embodiment, the surfacing media have a particle size distribution of 20 to 25 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 50 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 40 US mesh. In an embodiment, the surfacing media have a particle size distribution of 25 to 30 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 50 US mesh. In an embodiment, the surfacing media have a particle size distribution of 30 to 40 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 40 to 50 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 50 to 75 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 75 to 100 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 100 to 125 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 125 to 150 US mesh. In an embodiment, the surfacing media have a particle size distribution of 150 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 150 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 150 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 150 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 150 to 175 US mesh. In an embodiment, the surfacing media have a particle size distribution of 175 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 175 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 175 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 175 to 200 US mesh. In an embodiment, the surfacing media have a particle size distribution of 200 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 200 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 200 to 225 US mesh. In an embodiment, the surfacing media have a particle size distribution of 225 to 270 US mesh. In an embodiment, the surfacing media have a particle size distribution of 225 to 250 US mesh. In an embodiment, the surfacing media have a particle size distribution of 250 to 270 US mesh.
In an embodiment, the surfacing media have a mean particle size of 100 to 250 microns. In an embodiment, the surfacing media have a mean particle size of 100 to 225 microns. In an embodiment, the surfacing media have a mean particle size of 100 to 200 microns. In an embodiment, the surfacing media have a mean particle size of 100 to 175 microns. In an embodiment, the surfacing media have a mean particle size of 100 to 150 microns. In an embodiment, the surfacing media have a mean particle size of 100 to 125 microns. In an embodiment, the surfacing media have a mean particle size of 125 to 250 microns. In an embodiment, the surfacing media have a mean particle size of 125 to 225 microns. In an embodiment, the surfacing media have a mean particle size of 125 to 200 microns. In an embodiment, the surfacing media have a mean particle size of 125 to 175 microns. In an embodiment, the surfacing media have a mean particle size of 125 to 150 microns. In an embodiment, the surfacing media have a mean particle size of 150 to 250 microns. In an embodiment, the surfacing media have a mean particle size of 150 to 225 microns. In an embodiment, the surfacing media have a mean particle size of 150 to 200 microns. In an embodiment, the surfacing media have a mean particle size of 150 to 175 microns. In an embodiment, the surfacing media have a mean particle size of 175 to 250 microns. In an embodiment, the surfacing media have a mean particle size of 175 to 225 microns. In an embodiment, the surfacing media have a mean particle size of 175 to 200 microns. In an embodiment, the surfacing media have a mean particle size of 200 to 250 microns. In an embodiment, the surfacing media have a mean particle size of 200 to 225 microns. In an embodiment, the surfacing media have a mean particle size of 225 to 250 microns.
In an embodiment, the sealant attachment zone comprises (i) a first region having a percentage of surface coverage of the surfacing media that is less than the average surface coverage, and (ii) a second region having a percentage of surface coverage of the surfacing media that is greater than the average surface coverage.
In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 10% to 25% and (ii) a second region having a surface coverage of the surfacing media of 75% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 15% to 25% and (ii) a second region having a surface coverage of the surfacing media of 75% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 20% to 25% and (ii) a second region having a surface coverage of the surfacing media of 75% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 10% to 25% and (ii) a second region having a surface coverage of the surfacing media of 80% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 10% to 25% and (ii) a second region having a surface coverage of the surfacing media of 85% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 10% to 25% and (ii) a second region having a surface coverage of the surfacing media of 90% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 30% to 70%, with (i) a first region having a surface coverage of the surfacing media of 10% to 25% and (ii) a second region having a surface coverage of the surfacing media of 95% to 100%.
In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 70% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 15% to 30% and (ii) a second region having a surface coverage of the surfacing media of 70% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 20% to 30% and (ii) a second region having a surface coverage of the surfacing media of 70% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 25% to 30% and (ii) a second region having a surface coverage of the surfacing media of 70% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 75% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 80% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 85% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 90% to 100%. In some embodiments, the sealant attachment zone has an average surface coverage of the surfacing media of 40% to 60%, with (i) a first region having a surface coverage of the surfacing media of 10% to 30% and (ii) a second region having a surface coverage of the surfacing media of 95% to 100%.
In an embodiment, the roofing material exhibits a decreased surface tack temperature (° F.) as compared to a roofing material without the sealant attachment zone. According to this embodiment, the sealant attachment zone and/or surfacing media promote low temperature adhesion, which can thus enhance bonding and/or low temperature wind resistance when the roofing materials are installed at cold temperatures.
In an embodiment, the roofing material is a roofing shingle. According to one embodiment, the roofing shingle is one of (i) a single layer shingle or (ii) a laminated shingle having two or more layers.
Other ingredients and/or additives may also be added to the surfacing media to further modify their properties. In an embodiment, the surfacing media further comprise a tackifier, an encapsulated adhesion promoter, magnetic powder, and combinations thereof. In an embodiment, the encapsulated adhesion promoter can increase the chemical affinity to a sealant material upon contact and/or provide time release benefits over a prolonged period of time to enhance sealant strength, as the roofing material (e.g., shingle) is exposed to an outdoor environment. In some embodiments, the surfacing media further comprise ferrous metal powder. According to one embodiment, magnetic powder is applied to one surface (e.g., the back surface or underside) of the roofing material, while ferrous metal powder (or another material that attracts to the magnetic powder) is applied to the opposite surface (e.g., the front surface or top side) of the roofing material, to thereby attract to magnetic powder that is applied to an overlying roofing material and thus improve the bonding between the overlying and the previously installed roofing materials.
Another embodiment of this invention pertains to a method of preparing a roofing material. The method comprises (a) obtaining a substrate, (b) obtaining surfacing media that comprise at least one of mineral particles, polymeric particles, and combinations thereof, and (c) applying the surfacing media to a surface of the substrate to form a roofing material having a sealant attachment zone with an average surface coverage of the surfacing media of 30% to 70%. The roofing material exhibits an increased wind uplift resistance, as measured according to ASTM D6381, as compared to a roofing material without a sealant attachment zone having said average surface coverage of the surfacing media of 30% to 70%.
In an embodiment, the substrate comprises one of a fiberglass mat or a polyester mat. In an embodiment, the substrate comprises one of a fiberglass mat, a polyester mat, a scrim, a coated scrim, or a combination thereof. In an embodiment, the substrate comprises a fiberglass mat, a polyester mat, a scrim, a coated scrim, and/or other synthetic or natural scrims. In some embodiments, the substrate or mat includes nano-fibrillated cellulose fibers.
In an embodiment, the method further comprises heating the surfacing media prior to applying the surfacing media to the surface of the substrate. According to one embodiment, such heating of the surfacing media prior to applying the surfacing media to the surface of the substrate can increase adhesion of the surfacing media to the substrate, which thereby promotes or improves the wind uplift resistance.
In an embodiment, the applying the surfacing media to the surface of the substrate is conducted by controlling an amount of the surfacing media applied to the surface of the substrate.
Embodiments of the invention provide roofing materials with a sealant attachment zone that exhibit increased wind uplift resistance, as measured according to ASTM D6381 (see, e.g.,
Specific embodiments of the invention will now be demonstrated by reference to the following examples. It should be understood that these examples are disclosed by way of illustrating the invention and should not be taken in any way to limit the scope of the present invention.
A commercially available laminate shingle (Timberline HD, available from GAF, Tuscaloosa, Ala.) was produced having an upper surface covered with roofing granules (#11 grade available from SGI, Hagerstown, Md.) and a sealant material (available from Craftco Co., Chandler, Ariz.), which was applied to a sand backing during manufacturing. When the produced shingle was tested for wind uplift resistance, following the ASTM D6381 test method, the shingle averaged a wind uplift resistance of 19.61 lbs. The roofing granules had a mean particle size of 1190 microns, with a particle size distribution of between US mesh #12 to US mesh #40. The resulting shingle had a surface coverage of about 84% to 89%, which was determined by using an image analysis method using a Keyence VHX-5000 microscope and a height level threshold method.
The same type of shingle was made, as discussed above, but with the introduction of a sealant attachment zone having coal slag fines (available from MineralTech LLC, Highlands, Tex.) as the surfacing media to replace the roofing granules. The resulting inventive shingle was found to have an average wind uplift resistance of 37.74 lbs, according to ASTM D6381. Thus, this prepared shingle with a sealant attachment zone exhibited a 92% increase in the wind uplift resistance as compared to that of the previously prepared shingle having no sealant attachment zone. The analysis showed that the coal slag fines had a particle size distribution of between US mesh #30 to US mesh #270, with a mean particle size of 210 microns, and a mean surface coverage of 67%, as determined by an image analysis method using a Keyence VHX-5000 microscope and a height level threshold method.
The effect of surfacing media on wind uplift performance and related process flexibility was studied by varying the percentage or amount of surface coverage of the surfacing media over a shingle surface, such that the desirable range for both wind uplift performance and shingle processability could be determined. This was done by depositing surfacing media over a molten asphalt coating reinforced by a fiberglass mat on a moving conveyor (see, e.g.,
The effect of the surfacing media on wind uplift performance was determined by measuring the mechanical uplift resistance using the ASTM D6381 test method. For shingle process flexibility, the effect of surface tackiness was determined by measuring the tack temperature (° F.) using a tackimeter (Model D.D.W. from E. J. Cady & Co.). This tack temperature (° F.) provides an assessment of the amount of surfacing media that is needed in order to avoid the shingle fabric from sticking to the rolls during shingle manufacturing, particularly during hot summer days when it is difficult to cool off the web.
Table 1 provides the results of the shingles with the sealant attachment zone having varying amounts of surface coverage and their resulting mechanical uplift strength. The data also include the case of a shingle with no surfacing media (i.e., 0% surface coverage of the surfacing media), or a bare asphalt coating, as a comparative or control case.
As shown in Table 1 above, the data illustrates a non-linear trend. This is further shown in
This example clearly demonstrated that there is an optimal range for the amount of surfacing media such that a desirable surface coverage can be obtained for enhancing the wind uplift performance, while maintaining good manufacturability of the asphalt coated web. In this case study, the desirable surface coverage range was found to be between about 30% and 70%, with improved results between about 40% and 60%.
Although the invention has been described in certain specific exemplary embodiments, many additional modifications and variations would be apparent to those skilled in the art in light of this disclosure. It is, therefore, to be understood that this invention may be practiced otherwise than as specifically described. Thus, the exemplary embodiments of the invention should be considered in all respects to be illustrative and not restrictive, and the scope of the invention to be determined by any claims supportable by this application and the equivalents thereof, rather than by the foregoing description.