The present invention relates to a steel cord for reinforcing rubber articles and a pneumatic tire (hereinafter, also simply referred to as “cord” or “tire”), and more particularly, to a steel cord for reinforcing rubber articles suitably used for a pneumatic radial tire for a heavy vehicle such as a transport vehicle or a construction machine, and a tire using the same.
Since a tire for a construction vehicle runs over rough ground surfaces, and at the same time, is subjected to a heavy load, a high tensile strength (breaking load) is required for steel cords used for reinforcing layer such as a carcass or a belt for a tire for the construction vehicle. Consequently, for such reinforcing layers, a steel cord with a so-called multi-twisted structure such as a 7×(3+9) structure or a 7×(3+9+15) structure in which a plurality of sheath strands are twisted around a core strand is generally used.
Further, since the tire for a construction vehicle frequently suffers a damage as a result of a heavy load while being in contact with a rough ground surface, such countermeasures have been taken, as use of a large diameter cord as a reinforcing cord, and use of a so-called high tensile strength steel to increase the tensile breaking force per unit area of the cord, so as to increase the tensile breaking strength in the axial direction of the cord.
However, a problem has been known with respect to a multi-twisted cord which is a plurality of twisted strands, that the cord strength is lower than the total of the strengths of the wires to such an extent as is unexplainable from the decrease attributable to the twist angle. To cope with the problem, for example, Patent Document 1 discloses a technique for avoiding premature breakage of a part of the wires to suppress the decrease of the strength in the axial direction of the cord.
Patent Document 2 discloses a technique for improving the cut resistant property of a steel cord for reinforcing rubber articles with a multi-twisted structure in which a plurality of sheath strands are twisted around a plurality of core strands placed in mutually parallel orientation, without increasing the rubber weight of a tire and without generating an early stage propagation of a crack between neighboring cords, by making the number of the core strands and the number of the sheath strand and the twist pitch of the sheath strands and the diameters of the sheath strands each satisfy a predetermined relation.
Further, Patent Document 3 discloses a technique for improving the cut resistant property of a steel cord with a multi-twisted structure in which sheath strands are twisted around core strands, without decreasing the strength of the axial direction of the cord, by making the ratio of the minimum diameter of the profile shape of the cord at the cross-section orthogonal to the cord axes to the maximum diameter thereof and the ratio of the diameter of the wire constituting the outermost layer of the sheath strand to the diameter of the sheath strand each in a predetermined range.
Patent Document 1: WO 01/034900 (claims or the like)
Patent Document 2: Japanese Unexamined Patent Application Publication No. 2002-339277 (claims or the like)
Patent Document 3: Japanese Unexamined Patent Application Publication No. 2006-22440 (claims or the like)
However, a conventional steel cord as a reinforcing member for a tire for a construction vehicle has not been very satisfactory under circumstances as described below. More particularly, belts, especially the innermost belt layer, of a tire for a construction vehicle forced to run on rough surfaces, is bent widely, when it treads on a relatively obtuse projection, and it has been often observed that a steel cord for reinforcement is led to premature cord breakage by a tensile force in the axial direction of the cord. Meanwhile, when the belts tread on a relatively sharply pointed projection, the belts are bent locally, and it has been often observed that cord breakage occurs by a shear force from the projection in a belt reinforcing layer closest to the tread surface.
From the above, for a steel cord to be used as a reinforcing material for a construction vehicle tire, both the tensile strength in the axial direction of the cord and the strength in the shearing direction are required. In case a belt layer is thick, when it is bent by treading on a projection, an inner side belt cord, namely located on an outer side of a bend, undergoes easily a tensile force which leads to the breaking elongation. Consequently, a belt layer is required to be as thin as possible.
Accordingly, an object of the present invention is to provide a steel cord for reinforcing a rubber article, which has an improved durability against so-called cuts, such as notches and perforations, which are generated in the case of treading on an obtusely or sharply pointed projection, without decreasing the strength in the axial direction of the cord, and without increasing the thickness in the radial direction, namely without increasing the weight of a tire, as well as a tire using the steel cord for reinforcing a rubber article as a reinforcing material, especially a construction vehicle tire.
In order to solve the above problems, the present inventors intensively studied to find out that the object can be attained by adopting the following constitution, thereby completing the present invention.
More particularly, a steel cord for reinforcing rubber articles according to the present invention with a multi-twisted structure formed by twisting a plurality of sheath strands formed by twisting a plurality of wires around a core strand formed by twisting a plurality of wires, and the core strand being constituted of an at least three-layer-twisted structure formed by twisting core filaments and sheath filaments,
is characterized in that the lowest tensile breaking strength of filament bs and the tensile breaking strength of steel cord Bc satisfy the relationship represented by the following formula:
bs/Bc×100≧0.65.
With respect to the steel cord for reinforcing rubber articles according to the present invention, it is preferable that the filament diameter of the thinnest filament of the filaments constituting the steel cord ds and the steel cord diameter Dc satisfy the relationship represented by the following formula:
ds/Dc×100≧5.70.
It is preferable that seven to nine sheath strands be twisted around the core strand.
Additionally, a pneumatic tire according to the present invention having a carcass comprising ply(s) of radially oriented cords, as well as at least four layers of belts each with arrayed cords, which are crossed between the laminated layers located on the outer side in the radial direction at a crown part of the carcass, is characterized in that, as a cord constituting at least two layers of the belts, the aforementioned steel cord for reinforcing rubber articles is used.
The present invention is particularly valuable for a tire for a construction vehicle.
According to the present invention, a steel cord for reinforcing rubber articles, which has an improved so-called durability against cuts in the case of treading on an obtusely or sharply pointed projection, as well as a tire, especially a tire for a construction vehicle can be attained, without decreasing the strength in the axial direction of the cord, and without increasing the weight of the tire.
Preferred embodiments of the present invention will be described specifically with reference to the drawings.
In the preferred example shown in
In the present invention, it is essential that the lowest tensile breaking strength of filament bs and the tensile breaking strength of steel cord Bc satisfy the relationship represented by the following formula:
bs/Bc×100≧0.65,
and preferably, by the following formula:
bs/Bc×100>0.70.
In case the tensile breaking strength bs and the tensile breaking strength Bc have the relationship represented by the following formula:
ti bs/Bc×100<0.65,
when the steel cord receives a shear force, the filaments result in premature breakage prior to the breakage of the steel cord, and consequently, it becomes hard to obtain the required resistance to shear force.
In the present invention, it is preferable that the filament diameter of the thinnest filament of the filaments constituting the steel cord with the multi-twisted structure ds and the steel cord diameter Dc satisfy the relationship represented by the following formula:
ds/Dc×100≧5.70,
and when the relationship represented by the following formula:
ds/Dc×100<5.70
is satisfied, it also becomes hard to obtain the required resistance to shear force.
Further, it is preferable that 7 to 9 sheath strands 2 be wound around a core strand 1. In case the number of the sheath strands 2 is 6 or less, it becomes hard to obtain a sufficient tensile strength with respect to the cord cross section. Meanwhile, in case the number of windings of the sheath strands 2 is 10 or more, the diameter of a filament constituting the core strand 1 needs to be made extremely large, so that the flexural rigidity of the steel cord becomes high, and the surface strain of the filaments increases when the steel cord is applied to a rubber article such as a tire, and it becomes hard to obtain sufficient resistance to fatigue.
Still further, it is preferable that line contact be realized in each of the core strand 1 and the sheath strand 2, and that in order to avoid a breakage due to stress concentration, a same direction twisted structure be applied.
Still further, in order to secure the strength of the rubber article, it is preferable to use a high tensile strength steel with the carbon content of 0.80 to 1.00% by mass for the wires used.
In the tire of the present invention, for the cords constituting at least two layers of the belts 24, steel cords for reinforcing rubber articles of the present invention are used. By this, an excellent durability against cuts can be attained, without decreasing the strength in the axial direction of the cord, and without increasing the weight of a tire. The present invention is particularly valuable when applied to a tire for a construction vehicle.
The present invention will be described below more specifically by way of Examples.
Steel cords of Conventional Example 1 (
The resistances to shear failure of these sample steel cords were evaluated by a Charpy impact tester. The results were expressed by indices based on the steel cord according to Conventional Example as 100. The higher value means the better resistance to shear failure.
The weights of the respective test tires were measured and the results were expressed by indices based on the tire according to Conventional Example 1 as 100. The larger value means the larger weight.
Respect test tires manufactured by way of trial in which the respective test cords were applied to the belts were seated on the standard rim according to the TRA standard (U.S.), and mounted on a construction vehicle, which traveled for 1000 hours. Thereafter the number of cuts having reached the belt layer was counted in the section equivalent to ⅕ of the circumferential length of each tire. The obtained results are shown in Table 1.
From the evaluation results shown in Table 1, it is found that each of the test steel cords of Examples 1 to 3 has an excellent resistance to shear failure as compared with the test steel cords of the Conventional Examples and Comparative Example. Accordingly, it was confirmed that, by the present invention, a tire for a construction vehicle whose cut resistant property was improved can be obtained.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-109845 | Apr 2009 | JP | national |
This application is a continuation of U.S. application Ser. No. 13/266,549, filed Oct. 27, 2011, which is a National Stage of International Application No. PCT/JP2010/057566, filed on Apr. 28, 2010, which claims priority from Japanese Patent Application No. 2009-109845, filed on Apr. 28, 2009, the contents of all of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13266549 | Oct 2011 | US |
| Child | 14182935 | US |