Claims
- 1. A tire which is comprised of a generally toroidal-shaped carcass with an outer circumferential tread, two spaced beads, an innerliner, at least one ply extending from bead to bead and sidewalls extending radially from and connecting said tread to said beads, wherein said innerliner is comprised of a sulfur cured rubber composition which is comprised of about 5 phr to about 50 phr of cyclized polyisoprene and about 50 phr to about 95 phr of at least one other rubbery polymer selected from the group consisting of natural rubber and halobutyl rubber.
- 2. A sulfur cured rubber composition which is comprised of (a) about 5 to about 50 parts by weight cyclized polyisoprene; (b) about 10 to about 70 parts by weight cis 1,4-polyisoprene rubber; and (c) about 5 to about 60 parts by weight of at least one other rubber selected from the group consisting of solution polymerization formed styrene/butadiene copolymer rubber having a styrene/butadiene ratio in the range of about 5/95 to about 30/70, emulsion polymerization formed styrene/butadiene copolymer rubber having a styrene/butadiene ratio in the range of about 10/90 to about 60/40, cis 1,4-polybutadiene rubber, isoprene/butadiene copolymer rubber having an isoprene/butadiene ratio in a range of about 30/70 to about 70/30, styrene/isoprene copolymer rubber having a styrene/isoprene ratio in a range of about 10/90 to about 35/65, and styrene/isoprene/butadiene terpolymer rubber.
- 3. A sulfur cured rubber composition as specified in claim 2 wherein said sulfur cured rubber composition is in the form of a tire tread.
- 4. A sulfur cured rubber composition as specified in claim 2 wherein the cyclized polyisoprene is present at a level which is within the range of about 5 phr to about 35 phr, wherein the cis-1,4-polyisoprene is present at a level which is within the range of about 20 phr to about 60 phr, and wherein the other rubber is present at a level which is within the range of about 10 phr to about 50 phr.
- 5. A sulfur cured rubber composition as specified in claim 2 wherein the cyclized polyisoprene is present at a level which is within the range of about 5 phr to about 20 phr, wherein the cis-1,4-polyisoprene is present at a level which is within the range of about 40 phr to about 60 phr, and wherein the other rubber is present at a level which is within the range of about 30 phr to about 40 phr.
- 6. A tire as specified in claim 1 wherein the cyclized polyisoprene is present at a level which is within the range of about 25 percent to about 50, and wherein the other rubbery polymer is present at a level which is within the range of about 50 phr to about 75 phr.
- 7. A tire as specified in claim 6 wherein the other rubbery polymer is natural rubber.
- 8. A tire as specified in claim 6 wherein the other rubbery polymer is a halobutyl rubber.
- 9. A tire as specified in claim 1 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 25 percent to about 90 percent.
- 10. A tire as specified in claim 1 wherein said cyclized polyisoprene has a level of cyclization that is within the range of about 35 percent to about 70 percent.
- 11. A tire as specified in claim 1 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 40 percent to about 60 percent.
- 12. A tire as specified in claim 1 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 45 percent to 55 percent.
- 13. A sulfur cured rubber composition as specified in claim 2 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 25 percent to about 90 percent.
- 14. A sulfur cured rubber composition as specified in claim 2 wherein said cyclized polyisoprene has a level of cyclization that is within the range of about 35 percent to about 70 percent.
- 15. A sulfur cured rubber composition as specified in claim 2 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 40 percent to about 60 percent.
- 16. A sulfur cured rubber composition as specified in claim 2 wherein said cyclized polyisoprene has a level of cyclization that is within the range of 45 percent to 55 percent.
Parent Case Info
[0001] This is a Divisional of application Ser. No. 09/473,011, filed on Dec. 28, 1999, presently.
Divisions (1)
|
Number |
Date |
Country |
Parent |
09473011 |
Dec 1999 |
US |
Child |
09824610 |
Apr 2001 |
US |