Patent Application
20100292370
The present invention relates to rubber compositions containing functionalized nano transition metal oxide and/or sulfide material. In particular, the present invention relates to rubber compositions containing functionalized nano zinc oxide and/or nano zinc sulfide particles, their use as or in rubber components, especially after sulfur vulcanization, and methods to produce such rubber compositions.
Nanomaterials are materials with particles having a diameter from 1 to 100 nanometers. The use of such nanomaterials in rubber is known from U.S. Pat. No. 4,644,988 describing a tyre tread compound containing a styrene-butadiene copolymer rubber reinforced with carbon black with a particle size smaller than 20 nanometers. U.S. Pat. Nos. 6,121,346 and 6,225,397 disclose the use of silica fillers with primary particles having a particle size in the range of from 5 to 30 nanometers in a rubber also comprising zinc oxide in an amount of 2 phr to 5 phr.
A method to produce a nanoscaled zinc oxide with a mean particle diameter of from 5 nanometers to 10 nanometers starting from commercially available, comparatively cheap educts is described in DE 199 07 704 A1. These zinc oxide particles can be redispersed in water, organic solvents or mixtures with organic solvents or surface modifying substances in order to get a solution with a large extent of primary particles.
The increasing concern regarding the potential environmental and health effects of the release of zinc oxide (ZnO), which is also often accompanied by a release of cadmium, makes it desirable to reduce the ZnO content in rubber compositions, especially in rubber compositions used in the production of tyres, but also to retain the positive effects of ZnO in the curing/vulcanization process.
The present invention relates to rubber compositions containing functionalized nano transition metal oxide and/or sulfide particles, their use as or in rubber components, for example tyres, especially after sulfur vulcanization, and methods to produce such rubber compositions.
The term functionalized nano transition metal oxide and/or zinc particles refers to a material containing a transition metal, preferably Zn, and C, H, S, N and/or O. The base particle is hexagonal transition metal oxide or sulfide, for example ZnO or ZnS, of particle size less than 100 nm. The surface contains the presence of functionalized (end capped) groups, for example, of 2-mercaptobenzothiazole (MBT), zinc bis(2-mercaptobenzothiolate) and other zinc oxide-2 mercaptobenzothiazole complexes.
Other suitable end capping agents include bis-benzothiazole-2,2′-disulfide, N-oxydiethylene-2-benzothiazole-sulfenamide, N-oxydiethylenethiocarbomoyl-N-oxydiethylene sulfenamide, tetramethyl thiuram disulfide, tetramethyl thiuram monosulfide, tetraethyl thiuram disulfide, tetraethyl thiuram monosulfide, tetrabenzyl thiuram disulfide, tetrabenzyl thiuram monosulfide, tetrabutyl thiuram disulfide, tetrabutyl thiuram monosulfide, tetraisopropyl thiuram disulfide, tetraisopropyl thiuram monosulfide, N-cyclohexylthiophthalimide, N-cyclohexyl-2-benzothiazole sulfenamide, N-tert-butyl-2-benzothiazole sulfenamide, 4-morpholinyl-2-benzothiazole disulfide, dipentamethylene thiuram disulfide, dipentamethylene thiuram monosulfide, dipentamethylene thiuram tetrasulfide, 4,4′-dithiomorpholine, 2-mercaptotoluimidazole, ethylene thiourea, trimethylthiourea, 1,3-diethylethiourea and 1,3-dibutylthiourea.
The functionalized nano transition metal oxide or sulfide, for example ZnO or ZnS material can replace ZnO in rubber formulations in part or in full. The material can also be used in much lower loadings than ZnO and can act as an accelerator unlike ZnO which requires the presence of an accelerator. The material can act as a secondary accelerator in combination with known accelerators used in sulfur cures, for example 2-mercaptobenzothiazole (MBT). The material also significantly lowers cure scorch times at equivalent ZnO loadings.
According to a first aspect to the present invention there is disclosed a rubber composition containing a filler comprising at least one rubber containing olefinic unsaturation and functionalized nano transitional metal oxide and/or sulfide particles.
The rubber composition may be a sulfur-vulcanized rubber composition. The sulfur-vulcanized rubber composition may be prepared by heating the rubber composition according to the invention to a temperature of 100° C. or greater to 200° C. or less in the presence of a sulfur-vulcanizing agent.
According to a second aspect to the present invention there is provided a method of processing a rubber composition containing at least one rubber containing olefinic unsaturation with functionalized nano transition metal oxide and/or sulfide particles. The method of processing the rubber composition containing at least one rubber containing olefinic unsaturation and functionalized nano transition metal oxide and/or sulfide particles may include processing with a processing additive.
The term “phr” as used herein, and according to conventional practice, refers to “parts by weight of a respective material per 100 parts by weight of rubber, or elastomer.”
Preferably the rubber composition comprises less than 2 phr, preferably less than 1.9 phr, more preferably less than 1.8 phr, most preferably less than 1.7 phr of the functionalized nano transition metal oxide and/or sulfide particles. It will be appreciated that higher loadings may be used, although such higher loadings are counterintuitive to the aim of the present invention. The rubber composition may include greater than 0.1 phr, preferably greater than 0.2 phr, more preferably greater than 0.3 phr and most preferably greater than 0.5 phr of functionalized nano transition metal oxide and/or sulfide particles.
In a preferred aspect of this invention, the functionalized nano transition metal oxide and/or sulfide particles have a diameter of less than 100 nanometers.
The functionalized nano transition metal oxide and/or sulfide particles may be used to process sulfur-vulcanizable rubbers or elastomers containing olefinic unsaturation. The phrase “rubber or elastomer containing olefinic unsaturation” is intended to include both natural rubber and its various raw and reclaim forms as well as various synthetic rubbers, including but not limited to synthetic polyisoprene, polybutadiene and styrene butadiene rubber. In the description of this invention, the terms “rubber” and “elastomer” may be used interchangeably, unless otherwise prescribed. The terms “rubber composition”, “compounded rubber” and “rubber compound” are used interchangeably to refer to rubber which has been blended or mixed with various ingredients and materials and such terms are well known to those having skill in the rubber compounding art. Representative synthetic polymers are the homopolymerization products of butadiene and its homologues and derivatives, for example, methylbutadiene, dimethylbutadiene and pentadiene as well as copolymers such as those formed from butadiene or its homologues or derivatives with other unsaturated monomers. Specific examples of synthetic rubbers include neoprene (polychloroprene), polybutadiene (including cis 1,4-polybutadiene), polyisoprene (including cis 1,4-polyisoprene), butyl rubber, halobutyl rubber such as chlorobutyl rubber or bromobutyl rubber, styrene/isoprene/butadiene rubber, copolymers of 1,3-butadiene or isoprene with monomers such as styrene, acrylonitrile and methyl methacrylate, as well as ethylene/propylene terpolymers, also known as ethylene/propylene/diene monomer (EPDM), and in particular, ethylene/propylene/dicyclopentadiene terpolymers. Additional examples of rubbers which may be used include silicon-coupled and tin-coupled star-branched polymers. The preferred rubber or elastomers are polyisoprene, polybutadiene and SBR.
In one embodiment of the first aspect to the present invention, the rubber composition is preferably comprised of at least two of diene based rubbers. A combination of two or more rubbers is preferred such as cis 1,4-polyisoprene rubber (natural or synthetic, although natural is preferred), 3,4-polyisoprene rubber, styrene/isoprene/butadiene rubber, emulsion and solution polymerization derived styrene/butadiene rubbers, c is 1,4-polybutadiene rubbers and emulsion polymerization prepared butadiene/acrylonitrile copolymers. The 3,4-polyisoprene rubber (3,4-PI) is considered beneficial for a purpose of enhancing a tyre's traction when it is used in a tyre tread composition. The 3,4-PI, and use thereof, is more fully described in U.S. Pat. No. 5,087,668. The cis 1,4-polybutadiene rubber (BR) is considered to be beneficial for a purpose of enhancing a tyre tread's wear.
It is readily understood by those having skill in the art that the rubber composition can be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, sulfur donors, curing aids, such as accelerators, activators and retarders, and processing additives, such as oils, resins including tackifying resins and plasticizers, fillers, pigments, fatty acid, waxes, antioxidants and antiozonants and peptizing agents.
As known to those skilled in the art, depending on the intended use of the sulfur vulcanizable and sulfur-vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts. Representative examples of sulfur donors include elemental sulfur (free sulfur), an amine disulfide, polymeric polysulfide and sulfur olefin adducts. Preferably, the sulfur-vulcanizing agent is elemental sulfur. The sulfur-vulcanizing agent may be used in an amount ranging from 0.5 to 8 phr, with a range of from 1.5 to 6 phr being preferred. Typical amounts of tackifier resins, if used, comprise 0.5 to 10 phr, usually 1 to 5 phr. Typical amounts of processing aids comprise 1 phr to 50 phr. Such processing aids can include, for example, aromatic, naphthenic, and/or paraffinic processing oils. Typical amounts of antioxidants comprise 1 to 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in The Vanderbilt Rubber Handbook (1978), pages 344 to 346. Typical amounts of antiozonants comprise 1 to 5 phr. Typical amounts of fatty acids, if used, which can include stearic acid comprise 0.5 to 3 phr. Typical amounts of waxes comprise 1 to 5 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise 0.1 to 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide.
In one embodiment of the first aspect of the present invention, the rubber composition is sulfur-cured or vulcanized. Accelerators may be used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In the present invention, the functionalized nano transition metal oxide and/or sulfide can act as an accelerator rendering the addition of further accelerants redundant. In an alternative embodiment, a further single accelerator system (in addition to the nano transition metal oxide and/or sulfide) may be used, i.e. primary accelerator. The primary accelerator(s) may be used in total amounts ranging from 0.5 to 4, preferably 0.8 to 1.5, phr. In another embodiment, in addition to the functionalized nano transition metal oxide and/or sulfide, combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts, such as from 0.05 to 3 phr, in order to activate and to improve the properties of the vulcanizate. Vulcanization retarders might also be used. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound.
Vulcanization of the rubber composition of the present invention is preferably conducted at temperatures ranging from 110° C. to 200° C.
Any of the usual vulcanization processes may be used such as heating in a press or mold, heating with superheated steam or hot air or in a salt bath.
According to a third aspect to the present invention there is provided use of the rubber composition for various purposes. For example, rubber composition, preferably sulfur-vulcanized, may be in the form of a tyre, belt or hose. In case of a tyre, it can be used for various tyre components. Such tyres can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art. Preferably, the rubber composition is used in the tread of a tyre. As can be appreciated, the tyre may be a passenger tyre, aircraft tyre, truck tyre and the like. Preferably, the tyre is a passenger tyre. The tyre may also be a radial or bias, with a radial tyre being preferred.
According to the second-aspect to the present invention, functionalized nano transition metal oxide and/or sulfide particles are prepared according to the teaching of applicant's co-pending application ZA2006/04138 and these particles may be mixed with a processing additive like a wax, a fatty acid, a resin, or, preferably, an oil leading to a sol with dispersed functionalized nano transition metal oxide and/or sulfide particles therein. Then, this mixture is added to a prepared rubber composition containing the filler in the non-productive stage. The amount of transition metal oxide and/or sulfide in the mixture with the processing additive is such that the rubber composition comprises 0.1 to 1.0 phr, for example 0.8 phr, 0.6 phr or 0.4 phr, of transition metal oxide and/or sulfide after mixing. This process uses the possibility to redisperse nanoscaled transition metal oxide and/or sulfide particles prepared according to applicant's co-pending application in organic materials, for example, a usual processing additive in the rubber mixing art, and then to introduce the transition metal oxide and/or sulfide together with the processing additive into the prepared rubber composition preferably in the non-productive stage.
In summary, this process allows a considerable reduction of transition metal oxide and/or sulfide in the rubber composition, if desired, without negative impact on the following curing or vulcanization process due to the high dispersivity and high chemical activity of the nanoscaled transition metal oxide and/or sulfide particles. In addition, the inclusion of further accelerants can be avoided, if desired.
In an alternative embodiment to the second aspect of the present invention, functionalized nano transition metal oxide and/or sulfide particles are prepared according to the teaching of applicant's co-pending application ZA2006/04138 and then added to a master-batch including at least one polymer. The preparation of such a masterbatch is described in more detail in U.S. Pat. No. 6,555,606, the contents of which are included herein by reference. Preferably, the polymer is one of the polymers intended to be added to the rubber composition. This masterbatch is then mixed with a prepared rubber composition, preferably in the non-productive stage. The amount of transition metal oxide and/or sulfide in the master batch is such that the rubber composition comprises 0.1 to 1.0 phr, for example 0.8 phr, 0.6 phr or 0.4 phr, of transition metal oxide and/or sulfide after mixing.
Again, this process allows a considerable reduction of transition metal oxide and/or sulfide in the rubber composition, if desired, without negative impact on the following curing or vulcanization process due to the high dispersivity and chemical activity of the nanoscaled transition metal oxide and/or sulfide particles. In addition, the inclusion of further accelerants can be avoided, if desired.
The invention will now be described with reference to the following figures in which:
The invention will now be described with reference to the following non-limiting examples.
The following rubber compounds were prepared
Because the surface contains some 2-mercaptobenzothiazole, two further control compounds were prepared using normal zinc oxide. These contained some additional 2-mercaptobenzothiazole (MBT) or zinc bis(2-mercaptobenzothiazolate) (Zn2(mbt)4)
Below is a comparison of cure data. τ5 is the time taken for the change in torque (with respect to the minimum torque) to reach 5% of the difference in torque between minimum and maximum. τ95 is similar but for 95%.
Rate of cure is determined from the maximum slope of the torque time curve.
Of the samples, sample B displays the earliest onset and fastest rate of cure.
To better elucidate the effects of nano ZnO the curing temperature was lowered to 150° C. This lower temperature would display greater differences if any existed. The accelerator was also changed to N-cyclohexyl-2-benzothiazole sulfenamide (CBS)
Three samples were prepared
Sample G was expressly formulated to see if the properties of E could be mimicked with lower nano ZnO loadings.
It is apparent that at the same loadings, the MBT-capped nano ZnO significantly reduces the onset of curing. Reducing the ZnO loading by 90% to 0.1 phr produces a cure that has the same characteristics as 1.0 phr ZnO.
The cure behaviour can be summarized as
Rate of cure is determined from the maximum slope of the torque time curve
The data clearly shows that the onset of cure (τ5) is greatly reduced. Furthermore curing is complete with MBT-capped ZnO before curing has even begun using normal nano-ZnO. Sample G shows that reducing the zinc oxide loading 90% can still give the cure behaviour of normal zinc oxide. The rate of cure is slightly increased by the capped nano ZnO.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006/04137 | May 2006 | ZA | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB2007/051933 | 5/22/2007 | WO | 00 | 8/5/2010 |