Patent Application
20230416502
The present invention relates to diene rubber compounds which can be recycled, to processes for their preparation, and their use in the manufacture of vehicle tires and vehicle tire components. In particular, it relates to the use of the compounds to produce tire treads.
More specifically, the invention relates to modified silica for use as a reinforcing filler in diene rubber compounds. The surface of silica is chemically modified by covalent linkage of cationic moieties which are capable of forming a reversible cation-π interaction with the polymeric chains of the diene rubber. This reversible interaction advantageously improves the recyclability of the rubber compounds whilst improving their mechanical performance.
Diene rubbers, such as natural rubber, isoprene rubber and butadiene rubber, comprise repeat units derived from diolefins having a conjugated carbon-carbon double bond. The properties of synthetic diene rubbers can be specifically tailored by copolymerisation of diolefin monomers with other monomers and they are used in a wide range of applications.
Styrene-butadiene rubber (referred to herein as “SBR”) is one example of a butadiene rubber produced by polymerisation of styrene and butadiene. The ratio of styrene to butadiene influences the properties of the polymer and various types of SBR find use in the automotive industry, particularly as components of car tires such as tire treads. When used in the manufacture of tire treads, SBR is typically cross-linked using the sulfur vulcanisation system. Its mechanical properties are improved using various reinforcing fillers, such as silica and carbon black. Carbon black was the first material in common use as a filler, but more recently silica has largely replaced the traditional use of carbon black in SBR-based compounds. The use of silica fillers improves rubber properties such as lowering rolling resistance and improving traction, particularly on wet surfaces. Other diene rubbers, including butadiene rubber (BR), natural rubber (NR), isoprene rubber (IR), epoxidised natural rubber (ENR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR), isobutylene-isoprene rubber (IIR), styrene-isoprene-butadiene rubber (SIBR) and ethylene-propylene-diene rubber (EPDM) are also commonly used to produce components in the automotive industry. As with SBR-based compounds, the mechanical properties of rubber compounds made from any diene rubber may similarly be improved by the incorporation of reinforcing fillers such as silica.
Dispersion of any reinforcing filler and the filler-rubber interaction are key when preparing high performance rubber compounds having the required mechanical properties. The presence of polar silanol groups on the surface of silica makes it acidic and moisture adsorbing which can lead to its aggregation and thus poor dispersion in the rubber matrix, causing high compound viscosity and loss of reinforcing properties. Various treatments of silica have been proposed to tailor its surface chemistry, such as the use of silanes as surface modifiers or “compatibilising agents”. Silane coupling agents, such as bis(3-triethoxysilylpropyl)tetrasulfide (TESPT) and bis(3-triethoxysilylpropyl)disulfide (TESPD), are also used to form covalent bonds between silica and diene rubber chains, for example chains of SBR. These improve filler dispersion in the diene rubber matrix and strengthen the interaction between silica and rubber to reinforce the rubber compounds.
Vehicle tires have a limited lifespan due to general wear and tear, and degradation of the tire tread, etc. and can present a significant problem as a waste material. They take up valuable space in landfill sites and do not generally biodegrade. There is therefore an ongoing need to improve the sustainability of rubber compounds used in the manufacture of tires. The ability to recycle such materials for use as a secondary raw material which can be mixed with other new raw materials is the subject of much research. One of the most difficult types of tire material to recycle is diene rubber filled with silica, such as SBR-silica, due to the existence of strong covalent bonds between the rubber chains and the silica filler formed by silane coupling agents. In order to recycle such materials, it is necessary to break the covalent bonds since any remaining covalent bonds inhibit flow, compatibility, and can co-cross link when the recycled materials are mixed with other new polymers. That makes recycling difficult and generally uneconomical.
There are two types of covalent bond present in conventional diene rubbers which are reinforced with silica, such as SBR-silica compounds. One is the sulfur cross-links which arise from the sulfur vulcanisation system used to harden the rubber.
The other is the coupling between the diene rubber chains and silica via the use of silane coupling agents such as those described above. It is these covalent interactions which severely restrict the re-use of rubbers, such as SBR-silica compounds, as raw materials due to the large amount of energy required to break the covalent bonds.
Although silica-containing diene rubber compounds, such as SBR-silica compounds, have become preferred for use in the manufacture of passenger car tires, there is thus a need for alternative fillers for rubber compounding which can maintain, or improve, tire performance properties whilst improving their recyclability.
The inventors now propose a modified silica filler which can form a reversible interaction with the rubber chains in a diene rubber compound. It is proposed that this modified silica can effectively replace covalent silane coupling in conventional diene rubber-silica compounds thereby enabling the compounds to be recycled more readily whilst still retaining their desired mechanical properties. Specifically, the inventors propose chemical modification of the silica surface by covalent attachment of a cationic moiety which is capable of forming a reversible cation-π interaction with the polymeric diene rubber. The silica filler can be “pre-modified” by attachment of the cationic moiety to its surface before it is dispersed in the diene rubber matrix. Alternatively, it can effectively be modified in-situ as part of the compounding process to produce the diene rubber-silica compound.
Ionic liquids such as 1-allyl-3-methyl-imidazolium chloride (AMI) have been proposed for use in natural rubber compounds (see, for example Zhang et al., J. Appl. Polym. Sci. 134: 44478, 2017) to strengthen the interaction between silica and natural rubber. However, the interaction between silica and the ionic liquid is a weak non-covalent hydrogen bond which has been suggested to restrict the performance of the rubber-silica compounds. More recently, Qian et al. (Polymer Composites 40: 1740, 2018) introduced both AMI and TESPT into SBR-silica compounds. They concluded that the use of multiple interactions of cation-π interaction, hydrogen bonding and covalent bonds between silica and the SBR chains was required to achieve the required dispersion as well as mechanical properties of the rubber compounds.
In contrast to earlier work involving the use of ionic liquids, the inventors propose the use of functionalised silica in which the surface of the silica is modified by strong covalent bonding to a cationic species. This has several important advantages over the use of ionic liquids and, in particular, compared to the use of AMI. When using AMI, for example, the presence of chloride ions is highly undesirable since these increase the risk of degradation and thus premature aging of the rubber compounds. The presence of a weak hydrogen bond between the ionic liquid and the silica surface is also highly susceptible to exchange with water molecules present in the silica, especially at its surface. That runs the risk of water adsorption on the surface of the silica which can lead to aggregation of the silica and poor dispersion in the rubber matrix. In Qian et al. the proposal to use TESPT in addition to AMI to provide the desired multiple interactions between silica and the SBR chains also involves covalent bonding between the silica and rubber chains. That can result in a loss of elasticity of the material whilst also resulting in a material which cannot readily be recycled.
The present invention thus solves the problems relating to known silica-rubber compounds by providing chemically modified silica fillers which not only retain the key performance characteristics of the rubber products, but which enhance their recyclability.
In one aspect the invention thus provides a diene rubber-silica compound comprising a diene rubber matrix having dispersed therein a silica filler, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety which forms a cation-π interaction with the diene rubber matrix.
In another aspect, the invention provides a process for producing a diene rubber-silica compound as herein described, said process comprising the step of dispersing a silica filler in a diene rubber matrix, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with the diene rubber matrix.
In another aspect, the invention provides a vulcanizable rubber composition comprising a diene rubber matrix having dispersed therein a silica filler, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety which forms a cation-π interaction with the diene rubber matrix.
In another aspect, the invention provides a vulcanized rubber compound obtained by, directly obtained by, or obtainable by cross-linking a vulcanizable rubber composition as herein described.
In another aspect, the invention provides a process for producing a vulcanised diene rubber-silica compound, said process comprising the steps of introducing a silica filler into a diene rubber matrix whereby to produce a vulcanizable rubber compound; and subjecting said vulcanizable rubber compound to vulcanization by heating to a predetermined temperature and for a predetermined time, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with the diene rubber matrix.
In another aspect, the invention provides the use of a diene rubber-silica compound as herein described as a component of a vehicle tire or in the manufacture of a component of a vehicle tire.
In another aspect, the invention provides a vehicle tire component made from a diene rubber-silica compound as herein described.
In another aspect, the invention provides a vehicle tire comprising a vehicle tire component as herein described.
In another aspect, the invention provides a method of recycling a diene rubber-silica compound as herein described, said method comprising the step of de-vulcanising said compound; and optionally recovering the diene rubber.
In another aspect, the invention provides a silica filler which is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with a diene rubber.
In another aspect, the invention provides a process for producing a silica filler as herein described, said process comprising the step of chemically modifying silica by covalently attachment of a cationic moiety capable of forming a cation-π interaction with a diene rubber.
In one aspect the invention relates to a diene rubber-silica compound comprising a diene rubber matrix having dispersed therein a silica filler, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety which forms a cation-π interaction with the diene rubber matrix.
Unless otherwise specified, the terms “rubber compound” and “rubber composition” are used interchangeably herein and refer to a rubber which is blended or mixed (i.e. compounded) with various components or materials. A “diene rubber-silica compound” refers to a diene rubber which is mixed with a silica filler.
The invention relates to rubber compounds and rubber compositions both in the raw state (i.e. before curing or vulcanisation) and in the cured or vulcanised state, i.e. after cross-linking or vulcanisation.
As used herein, the term “diene rubber” refers to a rubber comprising repeat units derived from at least one conjugated diolefin monomer. It includes homopolymers and copolymers having one or more additional units derived from monomers copolymerisable with the diolefin monomer(s). The repeat units have a carbon-carbon double bond which may be present in the backbone and/or in a side-chain of the polymer. A diene rubber may be natural or synthetic. Non-limiting examples of diene rubbers include butadiene rubber (BR), natural rubber (NR), isoprene rubber (IR), epoxidized natural rubber (ENR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR), isobutylene-isoprene rubber (IIR), styrene-butadiene rubber (SBR), styrene-isoprene-butadiene rubber (SIBR) and ethylene-propylene-diene rubber (EPDM).
In one embodiment, the diene rubber for use in the invention contains repeat units derived from butadiene. Examples of such rubbers include, but are not limited to, styrene butadiene rubber (SBR) and butadiene rubber (BR). In one set of embodiments, the diene rubber for use in the invention is SBR.
The term “cation-π interaction” as used herein refers to a non-covalent interaction between a cation and an electron-rich π system. The cation-π interaction which is described herein involves the interaction between a cationic moiety which forms part of the silica filler and at least one type of electron-rich π system in the diene rubber polymer. The electron-rich π system may be provided by the π bond which forms part of a carbon-carbon double bond present in the diene rubber polymer.
The carbon-carbon double bond may form part of the backbone of the polymer or it may be present in a side-chain or in a terminal group. An electron-rich π system may also be associated with other substituent groups present in the diene rubber, for example any aromatic (e.g. phenyl) or heteroaromatic group which may be present in the backbone of the polymer or as part of a side-chain. Alternatively, or in addition, the cation-π interaction which is described herein may thus also involve the interaction between the cationic moiety which is provided on the silica filler and an electron-rich π system of an aromatic or heteroaromatic group present in the polymer, for example a phenyl ring in the case where the diene rubber is SBR. As will be understood, multiple cation-π interactions may be involved, for example where the cationic moiety provided on the silica filler contains a plurality of cationic groups.
It is intended that the primary interaction between the modified silica and diene rubber matrix in the rubber compounds herein described is a cation-π interaction. Other interactions between the silica and diene rubber matrix may be present, including both covalent and other non-covalent interactions. However, the presence of any additional covalent interactions should be minimised to achieve the desired aim of recyclability of the rubber compounds. In one embodiment, there will be a substantial absence of any covalent interactions between the silica and the diene rubber chains, such as those arising from the presence of conventional coupling agents such as bifunctional silanes. By “substantial absence” is meant that the extent of covalent bonding between the silica and diene rubber chains is less than 1 mol of covalent linkages per 1 mol of diene rubber, preferably less than 0.5 mol per 1 mol, e.g. less than 0.3 mol per 1 mol. It may be understood that the rubber compounds will be substantially free from (e.g. free from) any coupling agents which covalently bind the silica to the diene rubber. Other reversible non-covalent interactions which may be present between the silica and the diene rubber chains can include any of the following and combinations thereof: electrostatic, π-π bonding, van der Waals forces, hydrogen bonding and hydrophobic effects. In one embodiment, however, the only interaction will be a cation-π interaction as herein described.
The term “silica filler” as used herein refers to particulate silica. Any known type of particulate silica capable of reinforcing a diene rubber matrix may be used in the invention. As will be understood, known silica materials typically contain a proportion of other components (e.g. as impurities), but the main component will be silicon dioxide, i.e. SiO2. The content of silicon dioxide will generally be at least 90 wt. %, preferably at least 95 wt. %, e.g. at least 97 wt. %.
Silica materials for use in the invention are well known in the art and include, in particular, precipitated silica (an amorphous form of silica), pyrogenic (fumed) silica, wet silica (hydrous silicic acid), dry silica (silicic anhydride), calcium silicate and aluminium silicate. A single silica or combination of two or more types of silica may be used. The silica is used in the form of discrete particles, i.e. as a granulate which is highly dispersible. It may be monodisperse in size and uniform in shape. Alternatively, it may be provided in the form of branched or linear clusters. Precipitated silica is preferred in view of its ability to impart to tread compounds excellent rolling resistance and wet traction. Silica for use in the invention may have a specific surface area (e.g. nitrogen-specific absorption surface area) in the range of from 50 to 350 cm2/g, preferably from 80 to 280 cm2/g, for example from 120 to 230 cm2/g. The average particle size of the silica may range from about 5 nm to about 50 nm, preferably from about 8 nm to about 35 nm, e.g. from about 10 nm to about 28 nm. Commercial grades of silica for use in the invention are widely available from suppliers such as Evonik (Germany) and include, for example, Ultrasil® 7000 GR and Ultrasil® VN3.
Silica for use in the invention is surface-modified by covalent linkage to at least one cationic moiety capable of forming a cation-π interaction with the diene rubber matrix. As herein described, the silica may be “pre-modified” to carry the cationic moiety or it may be modified in-situ. The silica may be surface-modified in this way with a plurality of cationic moieties. Where more than one cationic moiety is present, these may be the same or different. Typically, however, where a plurality of cationic moieties are present these will be the same chemical entity.
In some embodiments, the silica surface may also be modified by attachment of one or more additional functional groups. Such functional groups may be non-polar or polar in nature and suitable groups may readily be selected by those skilled in the art. The silica may, for example, be surface-treated to decrease the filler-filler interaction during compounding and thus to improve its dispersibility in the rubber matrix. Compatibilising agents (also known as “covering agents”) suitable for this purpose are well known in the art and include, but are not limited to, monofunctional silanes such as hexadecyltrimethoxysilane or propyltriethoxysilane. Other non-polar species which may be attached to the surface of the silica particles include aromatic groups and saturated aliphatic hydrocarbons. In some embodiments, the silica surface may be functionalised with one or more polar functional groups such as those containing amine or carboxyl groups.
In one embodiment, the silica for use in the invention will only be modified with one or more cationic moieties as herein described, i.e. no other types of functional group will be bound to its surface.
Each cationic moiety which is attached to the silica surface will contain at least one cationic group. By “cationic group” is meant any group having a positive charge. The positive charge should be permanent. As will be understood, each cationic group will be associated with a counter anion of equal and opposite charge in order to balance the overall charge. The cationic group may be an inorganic cation or an organic cation, but typically it will be an organic cation.
In some cases, each cationic moiety may contain more than one cationic group. Where more than one cationic group is present these may be the same or different but typically they will be the same. Typically, the cationic moiety will contain a single cationic group which is capable of forming the intended cation-π interaction with the diene rubber matrix.
The positive charge of any cationic group may be localised on a single atom present in the group, or it may be associated with a group of atoms, for example a group of atoms which together form a ring structure such as an aromatic or heteroaromatic ring in which the positive charge is delocalised over more than one atom.
It is envisaged that a range of cationic moieties may be employed in the invention and suitable moieties can readily be selected by those skilled in the art having in mind its intended function. For example, it will be understood that any cationic moiety should not have any adverse impact on any of the remaining components of the rubber compound as herein described, or in respect of the rubber compound itself or its physical and mechanical properties. Similar considerations apply in respect of the selection of any anionic counter-ions.
Suitable examples of cationic moieties for use in the invention include, but are not limited to, organic groups containing at least one of the following cationic groups: a quaternary ammonium, a tertiary sulfonium, a quaternary phosphonium, a protonated or alkylated heterocyclic group, a diazonium ion and a guanidinium ion.
In one embodiment, the cationic moiety will include only one of these types of cationic groups. Examples of cationic heterocyclic groups include, for example, pyridinium, pyrrolium, pyrimidinium, quinolinium and imidazolium ions.
The cationic moiety is attached to the surface of the silica via at least one covalent bond, i.e. it is covalently bound. In one embodiment, it may be attached by more than one covalent bond, for example by two covalent bonds. However, typically it will be attached by a single covalent bond.
The cationic moiety can be directly attached to the surface of the silica. By directly attached it is meant via a direct covalent bond. Conveniently, however, the cationic moiety may be attached to the silica surface via a suitable linking group. This linking group should form a covalent bond to the silica surface and to the cationic moiety thereby serving to link the two entities. Due to the nature of the surface of silica which carries a plurality of silanol groups, the cationic moiety or the linking group which carries the cationic moiety, will generally be bound to the silica via a siloxane linkage.
Where the cationic moiety is linked to the silica surface via a linking group, it will be understood that the precise nature of the linking group is not critical provided it is capable of covalently linking the cationic moiety to the surface of the silica. As will be appreciated, the linking group should not include any components which will impact the performance of the rubber compound, for example any groups that may adversely interact with the diene rubber matrix. Suitable linking groups may readily be selected by those skilled in the art having in mind their intended function.
Typically, the linking group will be an organic group having a backbone chain containing up to 16 atoms, preferably up to 12 atoms, for example from 2 to 8 atoms, between its point of attachment to the silica surface and to the selected cationic moiety. It may, for example, contain up to 12 carbon atoms, for example from 2 to 8 carbon atoms. Linking groups may be linear or branched and they may carry one or more substituent groups.
The linking group may, for example, be represented by:
In one set of embodiments, each R in formula (I) or formula (II) is independently selected from —OH, C1-3 alkoxy and C1-3alkyl. For example, each R may independently be selected from —OH, C1-2 alkoxy and C1-2 alkyl. Typically, all R groups may be —OH.
In one set of embodiments, group Z in formula (I) and formula (II) may be an optionally substituted C1-12 alkylene, preferably C1-3 alkylene, for example C1-6 alkylene. Optional substituents include, for example, —OH and —NR″2 (where each R″ is independently H or C1-6 alkyl, preferably H).
In one set of embodiments, group Z in formula (I) and formula (II) may be an optionally substituted C1-12 alkylene, preferably C1-3 alkylene, for example C1-6 alkylene, optionally interrupted by one or more —O— atoms, for example by one or two —O— atoms. Optional substituents include, for example, —OH and —NR″2 (where each R″ is independently H or C1-6 alkyl, preferably H).
In one embodiment, the linking group may be represented by any of the following structures:
In one embodiment, m is 3.
In one embodiment, a is 3 and b is 1.
Specific examples of linking groups include, but are not limited to, the following:
Examples of cationic moieties which may be covalently linked to the silica surface, optionally via any of the linking groups herein described, include the following:
The term “alkyl” as used herein refers to a monovalent saturated, linear or branched, hydrocarbon chain. It may be substituted or unsubstituted. Where more than one substituent group is present, these may be the same or different. Examples of alkyl groups include, but are not limited to, methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, neo pentyl, n-hexyl, etc. An alkyl group preferably contains from 1-6 carbon atoms, e.g. 1-4 carbon atoms.
The term “alkoxy” as used herein refers to an —O-alkyl group, wherein alkyl is as defined herein. Examples of alkoxy groups include, but are not limited to, methoxy, ethoxy, propyloxy, etc. Unless otherwise specified, any alkoxy group may be substituted in one or more positions with a suitable substituent. Where more than one substituent group is present, these may be the same or different.
The term “cycloalkyl” as used herein refers to a monovalent saturated cyclic carbon system. It may be substituted or unsubstituted. Where more than one substituent group is present, these may be the same or different. Examples of cycloalkyl groups include, but are not limited to, cyclopropyl, cyclobutyl, cyclopentyl and cyclohexyl.
The term “alkylene” as used herein refers to a saturated, linear or branched divalent carbon chain. Examples of alkylene groups include, but are not limited to, methylene (—CH2—), ethylene (—CH2CH2—), propylene (—CH2CH2CH2—), etc. Unless otherwise specified, any alkylene group may be substituted in one or more positions with a suitable substituent. Where more than one substituent group is present, these may be the same or different.
The term “alkenyl” as used herein refers to a monovalent, substituted or unsubstituted hydrocarbon chain and includes, but is not limited to, straight and branched chains having 2 to 12 carbon atoms and containing at least one carbon-carbon double bond. It may be substituted or unsubstituted. Where more than one substituent group is present, these may be the same or different.
The term “alkynyl” as used herein refers to a monovalent, substituted or unsubstituted hydrocarbon chain and includes, but is not limited to, straight and branched chains having 2 to 12 carbon atoms and containing at least one carbon-carbon triple bond. It may be substituted or unsubstituted. Where more than one substituent group is present, these may be the same or different.
As used herein, the term “aryl” is intended to cover aromatic, carbocyclic ring systems. Such ring systems may be monocyclic or polycyclic (e.g. bicyclic) and contain at least one unsaturated aromatic ring. Where these contain polycyclic rings, these may be fused or bridged. Preferably such systems contain from 6-20 carbon atoms, preferably from 6 to 14 carbon atoms, e.g. either 6 or 10 carbon atoms. Examples of such groups include phenyl, 1-napthyl and 2-napthyl. A preferred aryl group is phenyl. Unless stated otherwise, any “aryl” group may be substituted by one or more substituents, which may be identical or different.
As used herein, the term “heteroaryl” is intended to cover heterocyclic aromatic groups. Such groups may be monocyclic or bicyclic and contain at least one unsaturated heteroaromatic ring system. Where these are monocyclic, these comprise 5- or 6-membered rings containing at least one heteroatom selected from nitrogen, oxygen and sulphur and contain sufficient conjugated bonds to form an aromatic system. Where these are bicyclic, these may be fused with a carbocyclic or heterocyclic ring and may contain from 9-11 ring atoms. Examples of heteroaryl groups include thiophene, thienyl, pyridyl, thiazolyl, furyl, pyrrolyl, triazolyl, imidazolyl, oxadiazolyl, oxazolyl, pyrazolyl, imidazolonyl, oxazolonyl, thiazolonyl, tetrazolyl, thiadiazolyl, benzimidazolyl, benzooxazolyl, benzofuryl, indolyl, isoindolyl, pyridonyl, pyridazinyl, pyrimidinyl, imidazopyridyl, oxazopyridyl, thiazolopyridyl, imidazopyridazinyl, oxazolopyridazinyl, thiazolopyridazinyl and purinyl. Unless stated otherwise, any “heteroaryl” may be substituted by one or more substituents, which may be identical or different.
In one embodiment, R1, R2, R3 and R4 are each independently selected from H, optionally substituted C1-12 alkyl, optionally substituted aryl (e.g. phenyl), and optionally substituted heteroaryl (e.g. pyridine). In one embodiment, R1, R2, R3 and R4 are each independently selected from H, optionally substituted C1-12 alkyl and optionally substituted phenyl. In another embodiment, R1, R2, R3 and R4 are each independently selected from C1-10 alkyl, preferably C1-3 alkyl, for example methyl, ethyl, propyl and octyl. In one embodiment, one or more of R1, R2, R3 and R4 are unsubstituted phenyl.
In one embodiment, the cationic moiety which is covalently linked to the silica surface, optionally via a linking group such as any of those as herein defined, has the following structure:
In one embodiment of formula (III), R1, R2 and R3 are each independently selected from unsubstituted C1-12 alkyl, e.g. unsubstituted C1-3 alkyl. For example, these may be independently selected from methyl (“Me”), ethyl (“Et”) and octyl.
Specific examples of structures of formula (III) include:
Where any of the groups herein described are substituted, any substituents may be the same or different and may be selected from any of the following: C1-3 alkyl (e.g. —CH3), C1-3alkoxy (e.g. —OCH3), and —NR62 (wherein each R6 is independently H or C1-6 alkyl, preferably C1-3 alkyl, e.g. —CH3).
In one embodiment, the cationic moiety which is covalently linked to the silica surface is selected from one of the following structures:
The surface-modified silica as herein described can be prepared using methods known in the art. The precise method used will depend on the nature of the linking group (if present) and the cationic group or groups but can readily be selected by those skilled in the art. Typically a compound which is capable of forming a covalent bond both to the surface of the silica and to the selected cationic moiety may be used and which will form the linking group as herein defined. For example, the method may involve reaction between silica, a compound capable of forming the linking group and a compound which either contains the selected cationic moiety, or which is capable of forming the selected cationic moiety as a result of the reaction. Where the selected cationic moiety is a quaternary ammonium group, for example, this can conveniently be formed by the reaction of a tertiary amine.
Formation of the surface-modified silica may be carried out in stepwise fashion, for example in which the linking group is initially covalently linked to the surface of the silica followed by reaction with a compound containing the cationic moiety (or a compound capable of forming the cationic moiety). Alternatively, the linking group may initially be covalently linked to the cationic moiety (or compound capable of forming the cationic moiety) followed by covalent linkage to the silica. Typically, however, the surface-modified silica will be formed in a single one-step reaction involving all reactants. An example of such a reaction is schematically illustrated in
In cases where the compound for reaction already contains the selected cationic moiety, the nature of the counter anion can be appropriately selected. In some cases, however, the cationic moiety and hence its counter anion will form in-situ and will be determined by the nature of the compound which forms the linking group. It may be necessary or desirable in some cases, therefore, to exchange the counter-ion which is generated in-situ with an alternative counter-ion which is more favourable for use in the context of a rubber compound. This may be the case, for example, where the counter-ion that is generated in-situ is a halide ion (e.g. chloride, bromide or iodide) whose presence may increase the risk of aging or degradation of the rubber matrix.
In some cases, the method for preparation of the surface-modified silica may therefore include an additional step involving replacement of the counter-ion. Counter-ion exchange will readily occur in the presence of a more favourable anion and suitable methods to achieve this are well known in the art. Any suitable source of an alternative counter-ion may be used, for example an alkali or alkaline earth metal salt. A suitable counterion is thiocyanate which may be provided by sodium thiocyanate, for example. Suitable reaction conditions for counter-ion exchange may readily be selected by those skilled in the art.
Certain silanes which contain a positively charged group (i.e. a suitable cationic moiety) are commercially available. These may be reacted directly with the silica to produce the surface-modified silica as herein described. Where appropriate, any less favourable counterions present in any commercially available silane, such as halide ions (e.g. chloride), can be exchanged with a more favourable counterion for use in the context of a rubber compound (e.g. a thiocyanate counterion). This can be achieved using any method known in the art, for example by reaction with sodium thiocyanate and removal of the resulting sodium halide salt (e.g. by crystallisation). Typically, counterion exchange may be carried out prior to reaction of the silane with the silica. Silanes containing quaternary ammonium groups are available from suppliers such as Gelest, Inc., for example N-trimethoxysilylpropyl-N,N,N-trimethylammonium chloride or octadecyldimethyl(3-trimethoxysilylpropyl) ammonium chloride.
An example of a method for preparation of a modified-silica for use in the invention is shown in the scheme below:
Following the reaction to form the surface-modified silica, any ungrafted material may be removed using conventional methods, such as by washing with a suitable solvent, or by Soxhlet extraction in water. If necessary, any residual solvent can be removed, for example by drying at elevated temperature.
Following preparation of the surface-modified silica, FTIR analysis can be used to determine the success of the reaction as described in the examples. If appropriate, the yield of modified silica can be determined by methods known in the art such as thermogravimetric analysis (TGA).
The methods described above relate to the preparation of a “pre-modified” silica for subsequent incorporation into the rubber to produce the desired diene rubber-silica compound. An alternative to these methods is to prepare the surface-modified silica in situ. In such methods, the components required to form the surface-modified silica are added to the rubber during compounding. In addition to the silica, these components will include a compound which either contains the selected cationic moiety or which is capable of forming the selected cationic moiety in situ and, optionally, a compound capable of forming the desired linking group.
For example, an amine (capable of forming a positively charged quaternary ammonium ion), a silane (capable of reaction to form a linking group) and silica may be added together to the rubber.
The surface-modified silica herein described and methods for its preparation form further aspects of the invention.
In another aspect, the invention thus provides a silica filler which is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with a diene rubber.
In another aspect, the invention provides a process for producing a silica filler as herein described, said process comprising the step of chemically modifying silica by covalently attachment of a cationic moiety capable of forming a cation-π interaction with a diene rubber.
The surface-modified silica which is herein described acts as a reinforcing filler in the diene rubber matrix. The term “diene rubber matrix” refers to an elastomeric matrix which comprises a diene rubber.
Any known diene rubber can be used in the invention and those skilled in the art can readily select a suitable rubber having in mind the intended use of the silica-diene rubber compound. Diene rubbers are well known in the art and include both natural and synthetic rubbers. Non-limiting examples of such rubbers include butadiene rubber (BR), natural rubber (NR), isoprene rubber (IR), epoxidized natural rubber (ENR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR), isobutylene-isoprene rubber (IIR), styrene-butadiene rubber (SBR), styrene-isoprene-butadiene rubber (SIBR) and ethylene-propylene-diene rubber (EPDM).
Diene rubbers can be modified with one or more functional groups and any such functionalised diene rubbers may be used in the invention. Where the diene rubber is functionalised, any of its polymer backbone, terminal groups and/or side chains may be bound to one or more functional groups. These functional groups may be incorporated into the polymer material during its production or, alternatively, they may be subsequently grafted onto the polymer. The type and position of any functional groups varies in different rubber grades known in the art. The choice of any functionalised rubber will depend on the intended use of the rubber compounds herein described. Examples of functionalised diene rubbers include those which carry one or more reactive groups (e.g. alkoxysilyl groups) and/or one or more interacting groups (e.g. amino groups). Interacting groups such as amino groups may, for example, form hydrogen bonds within the rubber matrix. In one embodiment, the diene rubber for use in the invention is unfunctionalised.
In one set of embodiments, the diene rubber for use in the invention is one suitable for use in the production of a rubber compound which can be used as a tire component, such as a tire tread. The diene rubber to be used in the invention may, for example, be functionalised or unfunctionalised styrene butadiene rubber (SBR). Unfunctionalised SBR is particularly preferred.
Styrene-butadiene rubber is well known in the art. The term “styrene-butadiene rubber” or “SBR” as used herein is intended to refer generally to any synthetic rubber made by polymerisation of styrene and butadiene monomers. It thus refers to any styrene-butadiene copolymer and is intended to include both functionalised and non-functionalised SBR. SBR is commonly used in the tire industry and can be made by well-known methods, such as by co-polymerisation of the corresponding monomers in emulsion, suspension or in solution. Styrene and butadiene monomers may be selected in suitable ratios according to the intended use and properties of the rubber compound. For example, styrene may be present in an amount of up to 80 wt. %, more typically up to about 45 wt. % for rubber tire tread compounds (wt. % based on the total weight of the comonomers). The diene component will generally be present in an amount of at least 50 wt. %. Tread compounds are required to have good viscoelastic properties due to their road contact when in use, as well as properties such as rolling resistance and traction on wet surfaces. Suitable amounts of styrene to achieve such properties are well known in the tire industry and may readily be selected by those skilled in the art.
The selected diene rubber can be used as 100 parts of the rubber in the compounds herein described, or it may be blended with any conventionally employed elastomer for rubber compounding or blends thereof, including both natural and synthetic rubbers. Blends of different diene rubbers may be used. Rubbers suitable for use in any blend are well known to those skilled in the art and include natural rubber, synthetic polyisoprene rubber, styrene-isoprene rubber, styrene-butadiene rubber, styrene-isoprene-butadiene rubber, butadiene-isoprene rubber, polybutadiene, butyl rubber, neoprene, acrylonitrile-butadiene rubber (NBR), silicone rubber, fluoroelastomers, ethylene acrylic rubber, ethylene-propylene rubber, ethylene-propylene terpolymer (EPDM), ethylene vinyl acetate copolymer, epichlorohydrin rubber, chlorinated polyethylene-propylene rubbers, chlorosulfonated polyethylene rubber, hydrogenated nitrile rubber, and tetrafluoroethylene-propylene rubber. The ratio of any polymer blends can be selected according to need, for example based on the viscoelastic properties of the rubber compound. Those skilled in the art can readily determine which elastomers may be appropriate and their relative amounts to provide a desired viscoelastic property range.
In a preferred embodiment, the selected diene rubber for use in the invention will be SBR. This may be used alone or as a blend with any of the other rubbers mentioned herein. Binary and ternary blends are preferred. In one set of embodiments, SBR may be used in combination with butadiene rubber and/or natural rubber. When used in combination with butadiene rubber the amount of SBR in the blend may range from 50 to 90% by weight (based on the total weight of the blend), preferably from 60 to 80% by weight, e.g. about 70% by weight. A binary blend of SBR:butadiene rubber in which the components are present in a 70:30 weight ratio is particularly preferred. Ternary blends including SBR, butadiene and natural rubber can also be used in the invention. In such blends, the SBR will generally form the major component and will be present in an amount ranging from 40 to 80% by weight (based on the total weight of the blend), preferably from 50 to 70% by weight, e.g. about 60% by weight. The butadiene and natural rubber components may each be present in an amount ranging from 10 to 30% by weight (based on the total weight of the blend), e.g. about 20% by weight. An SBR:butadiene:natural rubber blend in which the components are present in a 60:20:20 weight ratio may, for example, be used.
Commercially available sources of synthetic rubber such as SBR include Arlanxeo, Germany. A non-limiting example of a styrene butadiene rubber for use in the invention is Buna VSL 3038-2 HM (Arlanxeo, Germany).
The chemically modified silica can be blended with a diene rubber, and any other rubber materials as desired, to provide the rubber compounds according to the invention.
Methods for the preparation of the diene rubber-silica compounds herein described form a further aspect of the invention. In another aspect, the invention thus provides a process for producing a diene rubber-silica compound as herein described, said process comprising the step of dispersing a silica filler in a diene rubber matrix, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with the diene rubber matrix.
Diene rubber-silica compounds in which the modified silica herein described is dispersed in a rubber matrix can be made using methods known in the art in the manufacture of rubber compounds, such as compounding with other components including silanes, processing aids, curing systems, anti-degradants, pigments, additional fillers, compatibilising agents for the fillers, fibres, resins, etc. Those skilled in the art can readily select a combination of vulcanizable rubber compounds for subsequent mixing and vulcanization according to the specific rubber product which is desired.
For example, in addition to the diene rubber matrix and chemically modified silica filler herein described, a vulcanizable composition may contain processing aids (e.g. oils), activators (e.g. zinc oxide, stearic acid, etc.), sulfur or sulfur-donating compounds, accelerators, anti-degradants (e.g. anti-oxidants, anti-ozonants, etc.), pigments, additional fillers, and compatibilising agents. Zinc oxide and stearic acid function as activators in the vulcanisation process by shortening the vulcanisation time and impact the length and number of cross-links in the rubber matrix that forms during curing or vulcanisation. Depending on the intended use of the sulfur-vulcanized material, these additives can be selected and used in the conventional amounts.
The amount of chemically modified silica to be mixed into the rubber compound can be selected based on the desired physical properties of the resulting compound and may depend on the presence or absence of any other fillers, for example. Suitable amounts can readily be determined by those skilled in the art but may, for example, range from about 20 to about 150 phr, preferably from about 50 to about 100 phr, e.g. from about 60 to about 90 phr (where “phr” is parts per hundred parts of the rubber).
Additional reinforcing fillers such as carbon black, carbon nanotubes, short carbon, polyamide, polyester, natural fibres, calcium carbonate, clay, alumina, aluminosilicates, etc. or any mixtures of these may also be present. However, typically the only filler present in the compositions will be the chemically modified silica herein described.
Processing aids improve the processability of the compositions and include oils, such as mineral oils, vegetable oils, synthetic oils, or any mixtures thereof. These may be used in an amount of from about 5 to 75 phr, preferably from about 10 to 50 phr. Typical processing aids include oils, such as aromatic oils. Examples of such oils include Treated Distillate Aromatic Extract (TDAE), Residual Aromatic Extract (RAE), Mild Extract Solvate (MES), and bio-based oil seed derivatives.
Zinc oxide may be used in an amount of from about 1 to about 10 phr, preferably from about 2 to about 5 phr, more preferably from about 2 to about 3 phr. Stearic acid may be used in an amount of from about 1 to about 5 phr, preferably from about 2 to about 3 phr.
Sulfur may be used in an amount effective to achieve a satisfactory cure of the composition. It may, for example, range from about 1 to about 10 phr, preferably from about 1 to about 5 phr, e.g. from about 1 to about 3 phr.
Accelerators may be may be used in an amount of from about 1 to about 5 phr, preferably from about 1 to about 3 phr. Accelerators include thiazoles, dithiocarbamates, thiurams, guanidines, and sulphonamides. Examples of suitable accelerators include N-tertiary butyl benzothiazyle sulphonamide (TBBS), N-cyclohexyl-2-benzothiazole sulfenamide (CBS), diphenyl guanidine (DPG), 2-mercaptobenzothiazole (MBT) and tetrabenzilthiuram disulphide (TBZTD).
Compatibilising agents may be used to reduce the formation of silica aggregates during compounding and may be present in an amount of from about 0 to about 5 phr, preferably from about 1 to about 3 phr. In one embodiment, no additional compatibilising agents are present. Many compatibilizing agents are known for use in combining silica and rubber. The silica-based compatibilizing agents include silanes such as alkylalkoxy silanes, e.g. hexadecyltrimethoxy silane, octyltriethoxy silane and hexyltrimethoxy silane.
Coupling agents which function to covalently link the silica to the SBR matrix may be present, though for reasons herein described it is generally preferred that these are absent. If present, these should be provided in low amounts. The appropriate amount of any coupling agent can be determined by those skilled in the art having in mind factors such as its molecular weight, the number of functional groups it contains and its reactivity. Most coupling agents may be used in an isomolar amount based on the amount of silica. When using bis(triethoxysilylpropyl) tetrasulfide as a coupling agent, this may be provided in an amount of from about 0.6 to about 4.8 phr per 80 phr silica, preferably from 1.2 to 3.2 phr per 80 phr silica. Examples of coupling agents include bifunctional silanes such as bis(3-triethoxysilylpropyl)tetrasulfide (TESPT), bis(3-triethoxysilylpropyl)disulfide (TESPD) and 3-octanoylthio-1-propyltriethoxysilane. In one embodiment, no additional coupling agents are present.
The rubber compounds may be prepared by methods known in the art and will involve mixing (i.e. compounding) of the rubber, the chemically modified silica filler and any other components herein described to produce a rubber compound for subsequent vulcanization.
Mixing of the components will usually be carried out in stages in which the components may be added. Multi-step mixing processes are generally preferred to optimise dispersion of the silica filler and may involve the use of more than one mixer, for example different mixers arranged in series. For example, in the case of mixing a tire tread compound, the mixing process may involve an initial mixing stage in which a masterbatch is produced, followed by one or more additional non-productive mixing stages, and finally a productive mixing stage in which the curative agents (i.e. sulfur or sulfur-donating agents and accelerator(s)) are added. Mixers which may be used are well known in the art and include, for example, an open mill or a Banbury type mixer having tangential or intermeshing rotors.
Typically, the rubber, silica filler, processing aids, zinc oxide, stearic acid, anti-degradants (e.g. anti-oxidants, anti-ozonants), pigments, additional fillers, compatibilising agents, and coupling agents (where present) are mixed to produce the initial masterbatch. This initial masterbatch may be followed by another masterbatch in which additional fillers and additives are added, or by a non-productive mixing stage in which no additional components are added. Any non-productive mixing stage may be used to further disperse the components (e.g. fillers) within the rubber, or to decrease the viscosity of the mixed rubber compound.
During mixing, the temperature is kept below a predetermined level to avoid premature cross-linking of the composition. Typically, the temperature may be kept below 150° C., preferably below 140° C. In producing the initial masterbatch, mixing may for example be carried out a temperature of from about 80 to about 110° C., e.g. about 100° C. In the non-productive mixing stage the temperature may be raised, for example up to about 150° C., e.g. about 130° C. Where in-situ silanisation of the silica is performed during the mixing procedure, the use of temperatures at the higher end of this range may be necessary for the reaction to occur. Similarly, if any additional compatibilising agents are added during mixing, it may be necessary to carry out mixing at higher temperatures to ensure that these react with the silica surface. Mixing times may vary but can readily be determined by those skilled in the art based on the composition of the mixture and the type of mixer used. Generally a mixing time of at least 1 minute, preferably between 2 and 30 minutes, should be sufficient to obtain the desired homogenous composition.
A final mixing stage involves the addition of curatives, including accelerator(s), anti-degradants. The temperature for this mixing stage will generally be lower, for example in the range of from about 40 to about 60° C., e.g. about 50° C. This final mix may also be followed by a further non-productive mixing stage in which no additional components are added.
The most appropriate type of mixing can readily be selected to achieve a vulcanizable rubber compound. Mixing speeds may readily be determined, but may for example range from a speed of from about 20 to about 100 rpm, e.g. from about 30 to about 80 rpm, preferably about 50 rpm.
The vulcanizable rubber compound may be provided as an uncured (so-called “green”) tire component for final vulcanisation that cures the composition. Curing to cross-link the rubber components may be carried out by known methods. In the tire industry, for example, an uncured rubber (so-called “green body”) is produced followed by curing in a press mold which concurrently cross-links the rubber components and molds the components into a final tire. Vulcanisation cures the rubber by cross-linking, principally via sulfur cross-links. Vulcanisation methods are well known. Appropriate vulcanisation conditions typically include heating to a temperature in the range from 120 to 200° C. for a duration of from 5 to 180 mins.
The following scheme illustrates the formation of one type of cation-π interaction between a cationic moiety present on a surface-modified silica and SBR chains during compounding:
Vulcanizable rubber compositions form a further aspect of the invention. In another aspect, the invention thus provides a vulcanizable rubber composition comprising a diene rubber matrix having dispersed therein a silica filler, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety which forms a cation-π interaction with the diene rubber matrix.
Vulcanised rubber compounds obtained by, directly obtained by, or obtainable by cross-linking any vulcanizable rubber composition as herein described are also part of the invention.
Methods of producing a vulcanised rubber compound also form part of the invention. In another aspect, the invention thus provides a process for producing a vulcanised diene rubber-silica compound, said process comprising the steps of introducing a silica filler into a diene rubber matrix whereby to produce a vulcanizable rubber compound; and subjecting said vulcanizable rubber compound to vulcanization by heating to a predetermined temperature and for a predetermined time, wherein said silica filler is surface-modified by covalent attachment of a cationic moiety capable of forming a cation-π interaction with the diene rubber matrix.
The rubber compounds herein described find particular use in the manufacture of vehicle tires, in particular in the manufacture of tire components such as tire treads. Tire treads may be used for tires for any vehicle, but they find particular use in the manufacture of tire treads for motor cars. Other uses for the rubber compounds include as vibration dampers, sidewall rubbers, inner liner rubbers, bead filler rubbers, body ply rubbers, skim shock rubbers and tread rubbers.
In another aspect, the invention thus provides the use of a diene rubber-silica compound as herein described as a component of a vehicle tire or in the manufacture of a component of a vehicle tire.
In another aspect the invention provides a vehicle tire component, such as a tire tread, made from a diene rubber-silica compound as herein described. A vehicle tire comprising the vehicle tire component also forms part of the invention.
The assembly of the components of a tire and production methods are well known in the art. Assembly of the “green” tire is followed by compression molding in a suitable mold in which vulcanisation produces the final tire.
The rubber compounds according to the invention may also be used for non-tire applications, such as in the manufacture of hoses and seals.
In the present invention, the replacement of conventional fillers with the chemically modified silica filler results in a rubber compound having excellent physical properties, as well as acceptable wet traction and rolling resistance for use as tire tread rubber compounds. In the tire industry, various tests of the rubber compound are used as predictors of cured tire properties. These include the following:
The Payne effect:
This provides an indication of the extent of the filler network and may be measured using a Rubber Process Analyzer.
Mechanical properties, such as tensile strength, elongation at break and reinforcement index:
ASTM D412 standard using universal testing machine Zwick Z05 (Zwick, Germany) operated with crosshead speed of 500 mm/min.
Percent rebound at 60° C. is a predictor of rolling resistance of the tread compound.
An increased percent rebound at 60° C., when compared to a control compound, is indicative of lower rolling resistance. Rebound may be measured using a Zwick 5109 (Zwick, Germany) according to ISO 8307.
Hardness, Shore A may be measured using a universal hardness tester (Zwick, Germany) according to DIN 53505.
Dynamic Mechanical Properties:
These may be measured using a Gabo-Netzsch Eplexor at a frequency of 10 Hz, with a dynamic strain of 1% below 0° C. and 3% at room temperature. The loss factor (tangent δ, or tan δ) at 0° C. is an indicator of wet traction. An increase in tan δ at 0° C., when compared to a control compound, correlates with an improvement in wet traction of the tread compound. tan δ at 60° C. is an indicator of rolling resistance. A lower result, when compared to a control compound, is indicative of decreased rolling resistance.
The diene rubber-silica compounds herein described may be recycled using methods known in the art. Recycling involves de-vulcanisation of the rubber. During recycling the rubber compounds will usually be cut and shredded into finely divided form. The presence of the reversible cation-π interaction between the chemically-modified silica filler and diene rubber chains permits the rubber compound to be further treated whereby to break the reversible bonds without the need for any harsh treatment conditions. For example, methods such as mild chemical, thermophysical or biological treatment may be used. Following the removal of impurities, the rubber may be combined with one or more additional polymer components and converted into a new polymer material.
In a further aspect, the invention thus provides a method of recycling a diene rubber-silica compound as herein described, said method comprising the step of de-vulcanising said compound; and optionally recovering the diene rubber.
The method of recycling may involve the step of shearing the compound whereby to form a finely divided rubber composition which can then be subjected to devulcanisation. Shearing of the diene rubber-silica compound may be achieved using any known method, such as grinding. Once ground into finely divided form, de-vulcanisation can be carried out in order to reclaim the rubber. Methods for de-vulcanisation include physical processes (e.g. mechanical, thermo-mechanical, microwave and ultrasonic) or chemical processes (e.g. the use of radical scavengers, nucleophilic additives, catalyst systems or chemical probes). Thermal de-vulcanisation may be carried out at a temperature of from 180 to 300° C. Thermo-chemical de-vulcanisation can be achieved by using a de-vulcanisation aid (e.g. a disulphide such as diphenylsulfide, dibutylsulfide or di(2-aminophenyl)disulfide) and the use of temperatures of from 180 to 300° C.
Once recovered, the diene rubber can be blended with original virgin diene rubber and/or other additional polymer components and used to produce a new polymer material.
The invention is illustrated further by way of the following non-limiting Examples and the accompanying figures, in which:
Testing Procedures:
1. Payne Effect
Payne effect was measured using a Rubber Process Analyzer, RPA elite (TA instruments) with strain sweeps from 0.1% to 100% for cured samples and for uncured samples, at a frequency of 1.6 Hz and a temperature of 60° C. The cured samples were vulcanized beforehand inside the equipment chamber according to the vulcanization conditions at 160° C.
2. Modulus, Tensile Strength and Elongation at Break
Modulus, tensile strength (Stress at Maximum Strain) and elongation at break were measured using a universal testing machine Zwick Z05 (Zwick, Germany) operated with a crosshead speed of 500 mm/min according to ASTM D412. Modulus (100% (M100)) and 300% (M300)), tensile strength (Ts) and elongation at break (Eb) were calculated according to the calculations in ASTM D412. The reinforcement index was determined as the ratio of M300 to M100.
3. Rebound
Rebound, the resilience of a rubber sample based on the ratio of returned to delivered energy, was measured according to ISO 8307 using a testing machine Zwick 5109 (Zwick, Germany). Percentage rebound was calculated according to ISO 8307.
4. Hardness, Shore A
Shore A hardness was measured according to DIN 53505 using a universal hardness tester (Zwick, Germany).
5. Loss and Storage Modulus, and Loss Factor (Tan δ)
Dynamic mechanical measurement of the vulcanized samples was carried out using a Gabo-Netzsch Eplexor. Measurements were performed with a frequency of 10 Hz, a dynamic strain of 1% below 0° C. and 3% at room temperature (RT). The change in the strain at RT was investigated due to softening of the rubber at higher temperatures which can generate noise in the measurements.
6. Mechanical Properties at High Temperature
Mechanical properties of the compounds at 100° C. were measured by a universal testing machine Zwick Z010 (Zwick, Germany) operated with a crosshead speed of 500 mm/min and with a limit strain of 330%. The tests were performed in a temperature chamber at 100° C. Measurements of the dynamic properties of the vulcanized compounds before and after cycling the samples in the tensile machine were carried out on a Gabo-Netzsch Eplexor. Measurements were performed with a frequency of 10 Hz, a dynamic strain of 1% below 0° C. and 3% at room temperature (RT). The change in the strain at RT was investigated due to softening of the rubber at higher temperatures which can generate noise in the measurements. The cycling of the samples was performed in a universal testing machine Zwick Z010 (Zwick, Germany) operated with a crosshead speed of 500 mm/min and with a limit strain of 200%. All samples were cycled 5 times at 100° C.
Preparation of Rubber Compounds:
Rubber compounds for tire tread applications were prepared using a non-functionalised solution styrene butadiene rubber (SSBR) as the polymer matrix and pre-modified silica as the filler.
Materials:
Silica Modification:
Chemical modification of the silica (ULTRASIL® 7000 GR) was performed by reaction with a halogen silane (3-bromopropyltrimethoxysilane) and a tertiary amine in a two-step reaction. Three different tertiary amines were studied: N,N-dimethyloctylamine, N,N-dimethylethylamine, and N,N-trimethylamine.
Step 1: Preparation of Modified Silica:
Silica (ULTRASIL® 7000 GR), 3-bromopropyltrimethoxysilane and the tertiary amine were reacted to form the modified silica. The amount of 3-bromopropyltrimethoxysilane was 15% of the mass of the silica. The molar ratio between the 3-bromopropyltrimethoxysilane and the different amines was established at 1:5. The reaction was performed for 24 hours at 55° C. using toluene as the solvent.
Step 2: Elimination of the Bromine Formed in Step 1:
Sodium thiocyanate was used to eliminate the bromine present in the modified silica. The reaction between the modified silica and sodium thiocyanate was carried out for 24 hours at 80° C. using water as the solvent.
The resulting modified silica was analysed by Fourier Transform Infrared Spectroscopy (FTIR) using the DRIFTS (diffuse reflectance infrared Fourier transform spectrometry) cell. Chemical modification of the silica was confirmed for all samples by the presence of a band at a ˜2965 cm−1 (corresponding to the symmetric and asymmetric stretching of —CH2— groups) and a band at ˜1480 cm−1 (corresponding to —CH3 groups) (see
The yield of the reactions was measured by Thermogravimetric Analysis (TGA) using a TA 550 device from TA Instruments operating under a nitrogen and air atmosphere with a heating rate of 20° C./min from room temperature to 800° C. The obtained yields were 13% for the reaction with N,N-dimethyloctylamine, 1.5% for the reaction with N,N-dimethylethylamine and 2% for the reaction with N,N-trimethylamine. TGA curves of the unmodified and modified silica produced using the different tertiary amines are shown in
In order to confirm that bromine was not present in the modified silica, X-Ray photoelectron spectroscopy (XPS) was performed using a Quantera SXM (scanning XPS microprobe) from Physical Electronics. The data analysis was made using the software Compass for XPS control, Multipak v.9.8.0.19 for data reduction. The presence of nitrogen in the samples confirmed the chemical modification of the silica with the tertiary amines (see
Preparation of Rubber Compounds According to the Invention:
Rubber compounds (SSBR/modified silica) in accordance with the invention were prepared in an internal mixer (Brabender Plasticorder 350S, Duisburg, Germany) with a fill factor of 0.7, initial temperature of 100° C. and rotor speed of 50 rpm. Samples were prepared according to the formulation in Table 2 and in accordance with the mixing procedure in Table 3. Each rubber compound was prepared in two different versions, i.e. with and without the addition of a cornpatibilising agent (hexadecyltrimethoxysilane). The addition of the compatibilising agent during the mixing process decreases the filler-filler interaction during compounding.
Details of the final rubber compounds according to the invention are set out in Table 4 below.
Preparation of Reference Rubber Compounds:
The results obtained from the SSBR/modified silica rubber compounds were compared to three reference rubber compounds, details of which are shown in Table 5.
The reference compounds were prepared according to the formulation shown in Table 6 and in accordance with the mixing procedure used for the compounds according to the invention shown in Table 3 (in which the silane is “TESPD or the compatibilising agent”, as appropriate).
Testing of Rubber Compounds:
Results for the measured Payne effect are shown in Table 7 and
The results show that for the unvulcanised and vulcanised Payne effect the compounds 2b and 3b according to the invention show a lower Payne effect than the reference compounds. This indicates a reduction in the filler network.
Results for the mechanical properties of the vulcanised compounds are shown in Table 8 and
The mechanical properties show that the compounds 2b and 2c have a higher reinforcement index than the Reference 1 and Reference 2 compounds and slightly inferior than the Reference 3 compound. The tensile strength is inferior in all compounds compared to the Reference compounds and the elongation at break is slightly superior. The values for all compounds according to the invention are considered acceptable with respect to the reference compounds.
The rebound properties of the compounds and hardness are shown in Table 9. The rebound results show that Compound 2a and 2b present higher values than the Reference compounds. With respect to hardness all compounds according to the invention except for Compound 1a showed lower values than the Reference compounds (see Table 9).
Results of the dynamic mechanical measurement of the vulcanized samples are set out in Table 10 and
Analysis of the loss factor (tan δ) as a function of the temperature of the compounds according to the invention shows that Compound 2b has lower values of tan δ at 60° C. (indicating better rolling resistance) compared to Reference 1 and Reference 2, but is similar to Reference 3. Compound 2b presents higher values of tan δ at 0° C. and a higher maximum of tan δ (indicating better wet grip) than all reference samples. The values for all compounds according to the invention are considered acceptable with respect to the reference compounds.
The re-connectivity of the new bonds created with the silica modification according to the invention was analysed by studying the mechanical response of the compounds at high temperatures and analysing the change in dynamic properties after submitting the compounds to a cycling (fatigue test). The results are set out in
1Ts values are for the reference compounds only. For the compounds according to the invention the results are for the Stress at 330% (maximum extension in the heating chamber).
The results of the mechanical properties measured at 100° C. show that the compounds according to the invention present better resistance to high temperature. All the reference samples were broken before reaching the limit strain established for the experiment (330% strain). However, in the case of the compounds according to the invention, the samples did not break during the experiment indicating that the new bonds created with the silica modification are able to re-connect and consequently resist the tests at high temperatures. The tensile strength and the modulus at 100% are inferior in all compounds according to the invention compared to the references.
Results of the dynamic mechanical measurement of the vulcanized compounds before and after cycling in the tensile machine are set out in Table 12.
Compound 2b showed smaller changes in its dynamic properties after being submitted to 5 cycles at 100° C. until 200% strain than reference compound 3.
The invention has been described with reference to exemplary embodiments. Modifications and alterations are considered to form part of the invention to the extent that they are within the scope of the disclosure and appended claims. The scope of the disclosure should be determined with reference to the claims and is considered to include equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20209132.8 | Nov 2020 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2021/082542 | 11/22/2021 | WO |